Inﬂuence of Ce 3+ on the Structural, Morphological, Magnetic, Photocatalytic and Antibacterial Properties of Spinel MnFe 2 O 4 Nanocrystallites Prepared by the Combustion Route

: The present work describes the effect of Ce 3+ ion doping on the structural, morphological, and magnetic properties of spinel manganese ferrite (MnFe 2 O 4 ) nanocrystallites (NCs) using various instrument techniques. Rare earth element (REE) Cerium (Ce 3+ ) doped MnFe 2 O 4 NCs were prepared by a simple microwave combustion technique. In the present scenario, ferrites are widely used for photocatalytic dye degradation and antibacterial applications. Aiming to achieve this, we prepared Ce 3+ doped MnFe 2 O 4 NCs by microwave combustion method and urea as burning agent and the obtained powder samples were characterized by powder X-ray diffraction (XRD), Fourier transform infrared (FT-IR), high resolution scanning electron microscope (HR-SEM), high resolution transmission electron microscope (HR-TEM) and vibration sample magnetometer (VSM) techniques. The pure spinel phase formation was conﬁrmed by XRD analysis. FTIR spectra show two prominent absorption bands under 1000 cm − 1 , which conﬁrms the formation of the spinel structure. HR-SEM and HR-TEM pictures demonstrated a sphere-shaped blue (MB) and the sample MnCe 0.3 Fe 1.7 O 4 NCs showed superb photocatalytic performance (91.53%) compared to other samples. The antibacterial activities of Gram-positive S. aureus , B. subtilis and Gram-negative K. pneumonia and E. coli were investigated using pure and Ce 3+ substituted MnFe 2 O 4 NCs and a higher activity for MnCe 0.3 Fe 1.7 O 4 NCs than other samples was observed, which indicated that they can be used in biomedical applications.


Introduction
Spinel ferrites (AFe 2 O 4 , where A = Ni, Cu, Mg and Zn, etc.) are a well-known family of scientific materials and have been well studied owing to their unique magnetic properties, as they are endowed with high electrical resistivity [1][2][3][4][5]. The excellent properties of spinel ferrites are well utilized in modern technological applications. Ferrites often have a spinel structure with the formula AB 2 O 4 , where A and B are various metal cations, with iron being the most common (Fe). Spinel ferrites typically adopt FCC oxides (O 2− ) with A cations reside in one-eighth of the tetrahedral holes and B cations reside in half of the octahedral holes, i.e., instead of the normal spinel structure, ferrite crystals have the inverse spinel structure: B cations occupy (one-eighth of the tetrahedral holes, A cations occupy one-fourth of the octahedral sites, and B cations occupy the remaining one-fourth octahedral sites. Spinel ferrites with a mixed structure can also be possible with the for- 4 , where δ represents the degree of inversion [6][7][8][9][10]. Additionally, ferrites are hard and brittle, contain iron, are generally grey or black, and are polycrystalline materials. They can be magnetized or drawn to a magnet since they are ferrimagnetic. Conflicting with other ferromagnetic materials, most of the ferrites are insulating materials, making them ideal for transformers to defeat eddy currents for applications such as magnetic cores [11][12][13][14][15]. Spinel ferrites have vast applications in the present technological world. The main applications are precursors for ferro-fluids, radio, magnetic guided drug-delivery agents, telecommunication, biomedicine, magnetic storage, gas sensor, television, microwave, military devices, microwave absorbers, satellite communication, humidity sensors and magnetic storage [16,17]. Among them, manganese ferrite (MnFe 2 O 4 ) is an important material with good chemical stability, moderate magnetization, high sensitivity, band gap of~2.0 eV, and high electrical resistivity, and it is widely used in the transformer core, gas sensor, anode materials, photocatalysis, microwave absorber, and magnetic hyperthermia applications [18]. MnFe 2 O 4 nanoparticles exhibit a spinel cubic structure. Manganese ferrite (MnFe 2 O 4 ) is a kind of lenient magnetic material among different ferrites with little saturation magnetization (Ms) and coercivity (Hc). They are used for sensing gases and temperature, and for catalytic applications. MnFe 2 O 4 nanoparticles have been shown to be superparamagnetic or ferrimagnetic depending on its size. MnFe 2 O 4 nanoparticles with a size smaller than 15 nm behave as a superparamagnetic material and those above 15 nm behave as ferrimagnetic materials. The oxygen atoms in ferrites surround the metal ions, resulting in a super exchange interaction between the A-and B-sublattices, which disturbs the ferrites' magnetic properties [19]. These interesting properties motivated us to choose MnFe 2 O 4 magnetic nanoparticles for the present study.
The bulk MnFe 2 O 4 crystallizes mostly in a normal spinel structure with interstitial sites, such as A-and B-sites. Among the two sites, the manganese ions occupy the A-sites, whereas the iron ions occupy the B-sites [20]. Compared with the bulk form, nanocrystalline ferrites exhibit unusual behaviors, such as metastable cation distribution, super paramagnetism, enhanced coercivity and improved electrical resistivity [21]. Hence, the preparation and performance evolution of nanocrystalline ferrites attract increasing scientific attention. Additionally, the surface area and crystallite size of the ferrites are leads to the properties of the materials. It is reported that the replacement of Fe by other elements, such as Ce, La, Al, etc., occupies the B sites and modifies the magnetic and electrical properties of MnFe 2 O 4 [22].
The great effort made by previous studies demonstrates that the substitution of Ce for Fe in MgFe 2 O 4 effectively tunes the size of the crystallites, enhances the magnetization, and alters the electrical properties [23]. Since the preparation method plays a dominant role in deciding the size of the crystallites and its properties, in the present work we intend to synthesize nanocrystalline MnCe x Fe 2−x O 4 ferrites using a microwave combustion method, which is not reported in earlier literature surveys. The present method is practically efficient, due to the short reaction time and a relatively low temperature of processing.
In recent years, many physical and chemical methods have been used to synthesize nanosized ferrites. Because their composition and microstructure influence their structural, magnetic, and electrical properties, they are vastly reliant on the preparation method and conditions. R. Foroutan et al. reported the adsorption properties of montmorillonite (MMT) using graphene oxide (GO) and CoFe 2 O 4 magnetic nanoparticles for methyl violet (MV) removal. They observed that the MMT/GO/CoFe 2 O 4 magnetic composite demonstrates the high adsorption capacity and suitable reusability toward MV removal from aqueous media [24]. M. M. Boushehrian et al. reported a new nanocomposite of kaolin/copper iron oxide (CuFe 2 O 4 ), which were used to remove cationic dyes of methylene blue (MB) and methyl violet (MV) from an aqueous media in a batch system. They observed that, under the optimal conditions, the removal efficiency of MB and MV dyes using a kaolin/CuFe 2 O 4 nanocomposite was obtained with values of 98.64% and 99.25%, respectively, which show the highest removal ever achieved for MB and MV [25]. Additionally, the elimination of methyl violet dye (MVD) and Nile blue dye (NBD) from a water solution using a CNT/MgO/CuFe 2 O 4 magnetic composite powder produced by co-precipitation was investigated. The magnetic composite powder could be used several times in the adsorption process of MVD and NBD without a significant reduction in removal efficiency. The results showed that the CNT/MgO/CuFe 2 O 4 magnetic composite powder can be successfully used in textile wastewater treatment [26].
R. Foroutan et al. reported activated carbon oak wood (ACOW600) and modified activated carbon using ZnO (ACOW600/ZnO) and Fe 3 O 4 (ACOW600/ZnO/Fe 3 O 4 ) nanoparticles were used to remove methyl violet 2B dye (MV2B) from aqueous solutions. Textile wastewater was significantly treated by ACOW600, ACOW600/ZnO, and ACOW600/ZnO/Fe 3 O 4 adsorbents. The recycling of the adsorbents was demonstrated that the investigated adsorbents could be re-utilized many times in the MV2B removal process [27]. Additionally, a new nanocomposite, clinoptilolite (CLT)/Starch/CoFe 2 O 4 , was synthesized using the co-precipitation method. The prepared magnetic composite powder was utilized for the decontamination of methylene blue dye (MBD), methyl violet dye (MVD), and crystal violet dye (CVD) from water media. The maximum adsorption capacity of CVD, MBD, and MVD to the desired composite was determined as 32.84 mg·g −1 , 31.81 mg·g −1 , and 31.15 mg·g −1 , respectively. Finally, the ad(de)sorption experiments' results showed that the synthesized nanocomposite adsorbent has an excellent ability to adsorb cationic dyes after several consecutive cycles [28].
Among all the spinel ferrite systems, rare earth element (REE) doped MnFe 2 O 4 are soft materials called ferromagnetic materials. Furthermore, these materials have attractive magnetic properties, such as large M s , low H c , moderate M r , remarkable Y-K angle, high initial permeability, high electrical resistivity, and low energy loss. REE doped MnFe 2 O 4 NPs are widely used in scientific applications, such as spintronic systems and data transfer circuits as magnetic wave absorbers, converters, and inductor cores [29]. The concentration of Ce 3+ in the host material is expected to enhance structure properties. By incorporating different cations into the crystal structure, it is possible to tune the catalytic response of MnFe 2 O 4 nanoparticles. Due to the higher spin-orbit pairing in their 4f electrons, REE ions with massive ionic radii experience strong magnetostriction, magnetic moments, and magneto-crystalline anisotropy at low temperatures [30][31][32]. Replacing trivalent iron with REE ions at the Fe site improves dielectric, structural, optical, sensing and magnetic  [33][34][35].
Ceramics, polymers, and organic compounds can be used to make photocatalytic materials. Photocatalytic materials with low hysteresis and high stability are improving their efficiency and are reusable [36]. In terms of high mechanical strength, mechanical and chemical stability, low cost and operability in a wide range of catalyst are found to be a better alternative to all other nanocatalytic materials [37,38]. To the best of our knowledge, only a limited number of articles discussed the influence of cerium ions on the morphology, crystal structure, and magnetic properties of MnFe 2 O 4 NCs. In the present work, for the first time, we investigate the structural, morphological, and photocatalytic properties of Ce 3+ doped MnFe 2 O 4 NCs and the obtained results are reported in detail. , and urea was used as the fuel. Here, urea acted as fuel, whereas the precursors of metal nitrates (manganese, ferric and cerium nitrates) functioned as oxidizers. The chemicals were brought from SD fine (India) and were of systematic grade and utilized as usual. For pure manganese ferrite, the precursors of manganese nitrate and ferric nitrate were mixed by a continuing molar ratio 1:2 and dissolved in double distilled water. Urea was added to the main achieved solutions and agitated for 1 h and the final obtained homogeneous substances were transported to a silica crucible and were placed in a microwave oven (SAMSUNG, Noida, India), utilized as the mechanism of treatment. The microwave oven power was set as 900 W for 10 min (2.54 GHz). Under the influence of microwave energy (ME), the solutions were subjected to the following procedures: steaming, vaporization, desiccation, and finally decomposition; this caused the progression of the reaction gas and an explosion took place, which ground the speedy flame feathery construction of pure MnFe 2 O 4 . Similarly for the preparation of Ce 3+ doped MnFe 2 O 4 NCs, cerium nitrate was added by a stoichiometry ratio. Additionally

Characteri Zation Techniques
Powder X-ray (Model Rigaku Ultima III, Tokyo, Japan) was used to authorize the phase formation by employing CuKα energy (ń= 1.5406 Å) and within 2θ series of 20-80 • . The morphological and elemental analysis was recorded using scanning electron microscope accompanied by FEI Quanta FEG 200 (Hillsboro, OR, USA). The transmission electron micrographs were carried out by Philips-TEM (CM20, Brussels, Belgium). Perkin Elmer spectrophotometer (Spectrum RX1, Los Altos, CA, USA) was utilized to log the FTIR spectra. Lake Shore (Model7404, Westerville, OH, USA) vibration sample magnetometer (VSM) equipped with 3 magnets is used to perform magnetization measurements at RT.

Photocatalytic Evaluation
The photocatalytic performances of MnFe 2 O 4 , MnCe 0.1 Fe 1.9 O 4 , MnCe 0.3 Fe 1.7 O 4 and MnCe 0.5 Fe 1.5 O 4 NCs were examined under a visible light (Xenon lamp 300 W; ń > 400 nm) treatment. The photocatalytic activity was analyzed at RT. Exactly 100 mg of the nanocatalyst was distributed in 100 mL of methylene blue (MB) (10 mg/L), which was reserved in a quartz glass photocatalytic reactor. Before irradiation, the aliquot was stirred 30 min in dark conditions and it was ensured that the catalyst equilibrium of adsorption-desorption was reached between the dye and photocatalyst. The degradation efficiency was examined using UV absorption readings, which lead to govern the dye absorptions at a certain   (442) indicate that the cubic spinel phase is present. The XRD analysis shows the formation of a single-phase spinel structure having Fd-3m space group [39]. The lattice parameter increases with dopant concentration, reaching the limit of 8.388 Å as shown in Table 1. Scherrer's formula was used to measure the average crystallite size of the as synthesized samples between 22 and 24 nm in size. The values of lattice parameter and crystallite size are shown in Table 1.

Structural Analysis
where d hkl is the inter-atomic space consistent to h, k, and l planes (Miller indices), respectively, and a is the lattice constant. Lattice parameter 'a' resembles the spinel cubic structure ( Figure 2    where dhkl is the inter-atomic space consistent to h, k, and l planes (Miller indices), respectively, and a is the lattice constant. Lattice parameter 'a' resembles the spinel cubic structure ( Figure 2). The lattice parameter 'a' value was calculated for MnFe2O4 and Ce doped MnFe2O4 NCs and it was found to be 8.348 Å and 8.388 Å, respectively [40]. The increase of 'a' is due to doping of larger ionic size Ce ions (0.92 Å) in place of the lower ionic size Fe cations (0.67 Å), which obeys Vegard's law [41][42][43]. The particle size (D) was obtained by employing the Williamson-Hall (W-H) plot, as shown in Equation (2): where k is the constant and strain associated with samples signified by ε. The W-H plot is 4sinθ/λ vs. βcosθ/λ, wherever the interrupt (k/D) is used to control the actual D. by the Scherer method. The variance is, chiefly, due to participation of the strain module in the plot of the W-H route. It can be perceived that, with the increase in Ce ions (x), the L size shrinks, whereas an escalation in the 'a' can also be detected.
where k is the constant and strain associated with samples signified by ε. The W-H plot is 4sinθ/λ vs. βcosθ/λ, wherever the interrupt (k/D) is used to control the actual D. The W-H plot for MnFe2O4 and Ce doped MnFe2O4 NCs is represented in Figure 3 and the D size attained by the W-H plot method is greater when compared with the L size obtained by the Scherer method. The variance is, chiefly, due to participation of the strain module in the plot of the W-H route. It can be perceived that, with the increase in Ce ions (x), the L size shrinks, whereas an escalation in the 'a' can also be detected.

Fourier Transform Infrared (FT-IR) Spectral Analysis
To

HR-SEM Analysis
The study of the surface morphology of spinel MnFe2O4 and the morphology of the Ce doped MnFe2O4 NCs was achieved with the aid of HR-SEM analysis. The obtained SEM pictures of MnFe2O4 ( Figure 5a) and Ce doped MnFe2O4 NCs (Figure 5b,c), respectively, demonstrated a sphere-shaped morphology and also exposed a combination and agglomeration of grains. An agglomerated and sphere-shaped morphology was noticed, which is mostly due to the magnetic characteristics of the samples [47,48]. The surface of Ce doped MnFe2O4 ferrites shows the agglomerated coalescence behavior. Furthermore, it can be seen that the Ce substitution in MnFe2O4 NCs influence the surface morphology of nanocrystalline MnCexFe2−xO4 NCs.   (Figure 5b,c), respectively, demonstrated a sphere-shaped morphology and also exposed a combination and agglomeration of grains. An agglomerated and sphere-shaped morphology was noticed, which is mostly due to the magnetic characteristics of the samples [47,48]. The surface of Ce doped MnFe 2 O 4 ferrites shows the agglomerated coalescence behavior. Furthermore, it can be seen that the Ce substitution in MnFe 2 O 4 NCs influence the surface morphology of nanocrystalline MnCe x Fe 2−x O 4 NCs.

HR-TEM Analysis
To find additional confirmation on the nano-scaled samples, an HR-TEM study was performed and is shown in Figure 6a,b. In order to investigate the particle size and shape and nanostructure, the HR-TEM analysis was executed for MnFe 2 O 4 NCs (Figure 6a

HR-TEM Analysis
To find additional confirmation on the nano-scaled samples, an HR-TEM study was performed and is shown in Figure 6a,b. In order to investigate the particle size and shape and nanostructure, the HR-TEM analysis was executed for MnFe2O4 NCs (Figure 6a) and MnCe0.3Fe1.7O4 NCs (Figure 6b). HR-TEM photographs of the samples clearly show spherical-shaped particles in the manner of nanostructures. Crystallographic clarifications were performed by SAED patterns of MnCexFe2−xO4 NCs (x = 0.3) as shown in Figure 6c. A regular of significant Debye rings agreeing to the planes hkl; 311, 400, 511, and 440 of the MnFe2O4 cubic crystal structure indexed a test of the purity and crystallinity of the products. The Debye rings appeared incessant and diffused, and they also had an evidently visible agreement with good crystallinity, which show additional leaflets that demonstrate that the products are very much in the nano regime and well-developed nanoparticles. The images demonstrate that the spherical-shaped MnCexFe2−xO4 NCs are aggregated and differences were observed among the surface of the samples.

Magnetization Analysis
The magnetic properties of the synthesized magnetic nanoparticles were studied using a vibrating sample magnetometer (VSM) at RT. The magnetic parameters of MnFe2O4 and Ce doped MnFe2O4 NCs were undertaken at the field of −15kOe to +15kOe by VSM

Magnetization Analysis
The magnetic properties of the synthesized magnetic nanoparticles were studied using a vibrating sample magnetometer (VSM) at RT. The magnetic parameters of MnFe 2 O 4 and Ce doped MnFe 2 O 4 NCs were undertaken at the field of −15kOe to +15kOe by VSM techniques and the obtained results of magnetization (M) vs. external field (H) plots are shown in Figure 7. The M s , H c , and M r were also determined and are shown in Table 2 [49,50]. The increasing trend in M s , H c , and M r was described on the basis of cerium substitution for prescribed nanoferrites and this fluctuation in values is due to the ionic size and electronic structure of Ce 3+ [53,54]. The PCD efficiency rates of C/C 0 (%) vs. time for MB are shown in Figure 8. The photocatalytic constancy of the blank solution under visible light treatment was calculated in the nonappearance of MnFe 2 O 4 and Ce doped MnFe 2 O 4 NCs over 120 min, resulting in a PCD efficiency of 5.85%. The PCD efficiency of the MB solution using MnCe 0.3 Fe 1.7 O 4 NCs showed a higher degradation percentage (91.53%) than other samples (Table 3).

Kinetic Studies
The photocatalytic degradation (PCD) kinetic rate value of MB dye, PCD study of MnFe2O4 and Ce doped MnFe2O4 NCs and can be signified by the pseudo-first-order equation: −ln(Ct/C0) = kabs(t) where Ct = concentration of MB at different time (t); C0 is the initial dye attentiveness; and kabs is the pseudo-first-order rate constant (Figure 9). It should be noted that MnCe0.3Fe1.7O4 possesses a higher rate constant than other compositions [55,56]. Hence, spinel MnCe0.3Fe1.7O4 NCs is the optimal attentiveness to enhance the PCD of MB. The rate constant kabs value of MB from the experimental data are given in Table 4.

Kinetic Studies
The photocatalytic degradation (PCD) kinetic rate value of MB dye, PCD study of MnFe 2 O 4 and Ce doped MnFe 2 O 4 NCs and can be signified by the pseudo-first-order equation: where Ct = concentration of MB at different time (t); C 0 is the initial dye attentiveness; and k abs is the pseudo-first-order rate constant (Figure 9). It should be noted that MnCe 0.3 Fe 1.7 O 4 possesses a higher rate constant than other compositions [55,56]. Hence, spinel MnCe 0.3 Fe 1.7 O 4 NCs is the optimal attentiveness to enhance the PCD of MB. The rate constant k abs value of MB from the experimental data are given in Table 4.
PEER REVIEW 14 of 20

Photocatalytic Degradation Mechanism
Based on the above outcomes, PCD mechanism for MB degradation by Ce doped MnFe2O4 NCs is shown in Figure 10. When passing through the visible light on the nanocatalysts surface, the electrons, e -, become excited from the valence band (VB) to the conduction band (CB), along with producing h + in VB. The CB excited electrons of MnFe2O4 NCs become combined cerium and electron-hole (e-h) pair recombination rates become lower, hence the PCD process improves [57][58][59][60]. The CB electron becomes combined with a dissolved oxygen molecule to form anions of peroxide radicals (•O2 − ) and similarly created •OH, owing to the reaction amongst h + and OH− ions. MB decomposes into a simpler − Figure 9. Pseudo-first-order kinetic plot for MB dye degradation using spinel MnCe x Fe 2−x O 4 (x = 0.0, 0.1, 0.3 and 0.5) NCs.

Photocatalytic Degradation Mechanism
Based on the above outcomes, PCD mechanism for MB degradation by Ce doped MnFe 2 O 4 NCs is shown in Figure 10. When passing through the visible light on the nano-catalysts surface, the electrons, e -, become excited from the valence band (VB) to the conduction band (CB), along with producing h + in VB. The CB excited electrons of MnFe 2 O 4 NCs become combined cerium and electron-hole (e-h) pair recombination rates become lower, hence the PCD process improves [57][58][59][60] Figure 10. Photo-degradation (PCD) mechanism of MB dye using spinel Ce:MnFe2O4 NCs.

Antibacterial Studies
The antibacterial action of MnFe2O4 and Ce doped MnFe2O4 NCs ( Figure 11) were inspected by the Gram-positive B. subtilis and S. aureus, and Gram-negative K. pneumonia and E. coli, which are bacterial strains, correspondingly. It was supposed that there is no region of inhibition found over the control (Figure 11). The antibacterial activity showed that all samples have a positive response in killing bacterial strains. The different concentrations of the samples were used to determine the optimized concentration at which bacterial growth stopped. The measured values of radial diameters of ZOI at varying concentrations are presented in Table 5. The zones of inhibition elucidate that the increase in the concentration of Ce ions leads to a bigger zone of inhibition. The trend was followed: the increasing concentration eventually stops the process of replication and ceases the growth of bacteria. A higher activity can be seen in MnCexFe2−xO4 (x = 0.3) NCs compared to the doped and undoped samples. The enhanced antibacterial activity can be defined as the exposure of positively charged ions, such as Ce 3+ , Fe 3+ , and Mn 2+ , which charged bacterial membrane and distorted membrane integrity and can impair electrostatic interaction, leading to the crossing of membrane barriers, thus disrupting the electron transport chain,

Antibacterial Studies
The antibacterial action of MnFe 2 O 4 and Ce doped MnFe 2 O 4 NCs ( Figure 11) were inspected by the Gram-positive B. subtilis and S. aureus, and Gram-negative K. pneumonia and E. coli, which are bacterial strains, correspondingly. It was supposed that there is no region of inhibition found over the control (Figure 11). The antibacterial activity showed that all samples have a positive response in killing bacterial strains. The different concentrations of the samples were used to determine the optimized concentration at which bacterial growth stopped. The measured values of radial diameters of ZOI at varying concentrations are presented in Table 5. The zones of inhibition elucidate that the increase in the concentration of Ce ions leads to a bigger zone of inhibition. The trend was followed: the increasing concentration eventually stops the process of replication and ceases the growth of bacteria. A higher activity can be seen in MnCe x Fe 2−x O 4 (x = 0.3) NCs compared to the doped and undoped samples. The enhanced antibacterial activity can be defined as the exposure of positively charged ions, such as Ce 3+ , Fe 3+ , and Mn 2+ , which charged bacterial membrane and distorted membrane integrity and can impair electrostatic interaction, leading to the crossing of membrane barriers, thus disrupting the electron transport chain, and causing cell death. The major element that has played a central role is the ROS species •OH and •O 2− , and they were higher in MnCe x Fe 2−x O 4 (x = 0.0, 0.1, 0.3 and 0.5) NCs and the highest in the case of MnCe x Fe 2−x O 4 (x = 0.3) NCs (evident from photocatalysis). These species have unpaired electrons and can generate oxidative stress and cytotoxicity in the cellular environment. Further, they can start a series of reactions, such as DNA damage, enzyme protein peroxidation, and membrane lipid peroxidation, and inhibit the functioning of the electron's transport mechanism [61,62]. Furthermore, a better attentiveness of Ce ions replacement impact improved antibacterial activity than the smaller Ce exchanged MnFe 2 O 4 NCs. The smaller grain size and developed surface area with bulk ratio of the products show an exciting atmosphere in antibacterial activity [63,64].

Conclusions
Spinel MnCexFe2−xO4 NCs were synthesized using manganese nitrate, ferric nitrate and cerium nitrate, and urea was used as the fuel. In this paper, urea acted as fuel, wherea the precursors of metal nitrates (manganese, ferric and cerium nitrates) functioned as ox idizers. The spinel cubic structure of the sample was confirmed by XRD patterns. Becaus of lattice distortion, the average crystallite size (nm) shrinks as the concentration of Ce 3 rises. Since the particle size decreases as the concentration of Ce 3+ increases, the PCD effi ciency increases. As a result, these samples could be used to develop photocatalytic ma terials in the future. According to the VSM analysis, the pure and Ce 3+ doped MnFe2O

Conclusions
Spinel MnCe x Fe 2−x O 4 NCs were synthesized using manganese nitrate, ferric nitrate, and cerium nitrate, and urea was used as the fuel. In this paper, urea acted as fuel, whereas the precursors of metal nitrates (manganese, ferric and cerium nitrates) functioned as oxidizers. The spinel cubic structure of the sample was confirmed by XRD patterns. Because of lattice distortion, the average crystallite size (nm) shrinks as the concentration of Ce 3+ rises. Since the particle size decreases as the concentration of Ce 3+ increases, the PCD efficiency increases. As a result, these samples could be used to develop photocatalytic materials in the future. According to the VSM analysis, the pure and Ce 3+ doped MnFe 2 O 4 NCs shows ferromagnetic behaviour. The photodegradation results exhibited that MnFe 2 O 4 and Ce doped MnFe 2 O 4 NCs have the higher potential to degrade methylene blue (MB) and the sample MnCe 0.3 Fe 1.7 O 4 NCs has shown superb photocatalytic performance (91.53%) than other samples. The antibacterial activities of Gram-positive S. aureus and B. subtilis, and Gram-negative K. pneumonia and E. coli were investigated using undoped and Ce 3+ substituted MnFe 2 O 4 NCs, and observed a higher activity, which indicated that they can be used in biomedical applications. Additionally, a higher antibacterial activity of Ce 3+ doped MnFe 2 O 4 NCs was observed.