Influence of Temperature and Plastic Strain on Deformation Mechanisms and Kink Band Formation in Homogenized HfNbTaTiZr

Due to its outstanding ductility over a large temperature range, equiatomic HfNbTaTiZr is well-suited for investigating the influence of temperature and plastic strain on deformation mechanisms in concentrated, body centered cubic solid solutions. For this purpose, compression tests in a temperature range from 77 up to 1073 K were performed and terminated at varying plastic strains for comparison of plastic deformation behavior. The microstructure and chemical homogeneity of a homogenized HfNbTaTiZr ingot were evaluated on different length scales. The compression tests reveal that test temperature significantly influences yield strength as well as work hardening behavior. Electron backscatter diffraction aids in shedding light on the acting deformation mechanisms at various temperatures and strains. It is revealed that kink band formation contributes to plastic deformation only in a certain temperature range. Additionally, the kink band misorientation angle distribution significantly differs at varying plastic strains.


Introduction
Metals and alloys usually deform plastically by (uniform) dislocation slip or by deformation twinning if diffusion-based processes (at elevated temperatures) are excluded. In body centered cubic (bcc) metals and alloys, pencil glide occurs in {011}, {132} and {121} 1 2 111 slip systems, whereas twinning is found in a {112} 1 6 111 -type system [1,2]. Additionally, localized deformation mechanisms can be active in metals and alloys, such as the formation of kink bands. Kink band formation was firstly described by Orowan [3] as a mechanism that can be neither assigned to uniform dislocation slip nor to deformation twinning. Kink bands form by highly localized dislocation-mediated rotation of one crystal/crystallite segment by a certain misorientation angle with respect to the non-kinked segment. The misorientation angle of the kinked region does not necessarily possess an obvious crystallographic relationship to the undeformed crystal [3]. This property unambiguously distinguishes kink bands from deformation twins [3]. The rotation axes depend on the crystal structure of the metals and alloys. In general, a certain rotation axis is located within the slip plane in operation and is perpendicular to the corresponding slip direction [4]. For bcc metals and alloys with 111 slip directions and potential {011}, {132} and {121} slip planes, rotation axes are therefore expected to be of 211 -, 514 -and 101 -type, respectively [5].

Materials and Methods
Equiatomic HfNbTaTiZr was synthesized by arc melting in an AM/0.5 device (Edmund Bühler GmbH, Bodelshausen, Germany) from elemental granules of Hf, Nb, Ta, Ti, and Zr with purities higher than 99.8% in all cases. The melting process was performed in Ar atmosphere using a water-cooled Cu crucible. The HfNbTaTiZr ingot was re-melted five times to ensure uniform element distribution. Prior to each melting step, the disc-shaped specimen was flipped, and a Zr lump was melted to getter residual O within the process chamber. The alloy composition, estimated by means of inductively coupled plasma optical emission spectrometry (ICP-OES), is presented in Table 1. In order to obtain a chemically homogeneous microstructure, the ingot was homogenized in a tube furnace (Carbolite Gero GmbH and Co. KG, Neuhausen, Germany) at a temperature of 1473 K for 24 h under flowing Ar gas and subsequently furnacecooled. The mean value and standard deviation of O concentration in the homogenized state was determined by means of hot gas carrier extraction, averaging three measurements.
For crystal structure and phase analysis, a Bruker D8 Discover X-ray diffraction (XRD) device equipped with a LynxEye XE line detector was used in a 2Θ range of 10 up to 140 • and a step size of 0.03 • while rotating the sample at a speed of 0.5 s −1 . The Bragg-Brentano experiment was performed using a Cu Kα radiation source at 40 kV and 40 mA and 2.5 • Soller slits on both, beam and detector side. Further microstructural investigations in terms of electron channeling contrast imaging (ECC) and energy-dispersive X-ray spectroscopy (EDX) were performed using an Apreo scanning electron microscope (SEM; Thermo Fisher Scientific Inc., Waltham, USA). For attaining ECC, the SEM was operated at an acceleration voltage of 15 kV, a beam current of 3.2 nA, and an aperture size of 32 µm. For EDX mapping, an Octane Elite system by EDAX (AMETEK Inc., Berwyn, USA) was used at an acceleration voltage of 25 kV, a step size of 3 µm, a dwell time of 100 µs, and a total number of 20 frames. A Strata dual beam device (Thermo Fisher Scientific Inc., Waltham, USA) was used to prepare tip-shaped specimens for atom probe tomography (APT). A LEAP 4000X HR atom probe (Cameca SAS, Gennevilliers, France) was used in pulsed laser mode for the analysis. Laser pulses had a repetition rate of 125 kHz with a pulse energy of 50 pJ. The detection rate was set to 0.3% fraction of pulses, leading to ion detection. The reconstruction and analysis of the APT experiment were conducted with the IVAS 3.6.14 software of Cameca SAS. Terminated, displacement-controlled compression tests were conducted in a temperature range of 77 up to 298 K as well as in a range of 873 up to 1073 K on a MTS25 testing device equipped with a CryoVac He gas continuous flow cryostat and a Zwick Z100 universal testing device equipped with a Maytec resistance furnace, respectively. The term "terminated" means that the compressions tests were purposely stopped at desired plastic strains. The strain was measured using extensometers to avoid discrepancies by finite machine compliance. The cuboidal samples with (3 · 3 · 4.5) mm 3 in dimensions were loaded with an initial strain rate of 10 −3 s −1 . In order to avoid barreling during compression tests, the samples were lubricated using BN spray films. Plastic deformation behavior was investigated by evaluating engineering stress; load with respect to the initial cross-section area of the compression sample, with respect to engineering strain; the difference in height with respect to initial sample height in stress-strain curves to ensure immediate comparison to literature data [9,11].
For the investigation of deformation mechanisms, EBSD on longitudinal sections of deformed samples was performed using a Auriga 60 dual beam microscope (Carl Zeiss AG; Oberkochen, Germany) equipped with an EDAX DigiView (AMETEK Inc., Berwyn, USA) EBSD system. Data were acquired on an area of (2100 · 2100) µm 2 in size at a step size of 5 µm for an overview, whereas regions of interests (ROI) were scanned at a step size of 0.8 µm. EBSD data of the bcc phase was handled with the Matlab tool MTex [20]. Intensity is plotted in a logarithmic scale for better visibility of low-intensity peaks. (b) electron channeling contrast imaging (ECC) micrograph and elemental energy-dispersive X-ray spectroscopy (EDX) maps of the same area.

Microstructural and Chemical Analysis
In order to evaluate elemental distribution within the bcc phase, APT was performed on the region from within a grain. The microstructure, which is shown in the tip reconstruction (Figure 2a), did not indicate any segregation or precipitation at first view. The chemical homogeneity by APT analysis could be quantified by a sample volume independent correlation factor which describes the deviation between the ideal, binomial, and the experimental element distribution [21].
values of all elements within the entire APT tip were determined (Table 2) and are in the range of 5.1 • 10 −2 (Hf) up to 24.7 • 10 −2 (Ta). The parameter has already been used for quantifying the chemical homogeneity of other HEAs, such as of non-equiatomic FeMnNiCoCr [22], quaternary NbTaTiV [23] and quinary, equiatomic AuCuNiPdPt [24]. Moody et al. [21] emphasize that varies with the number of elements and their concentrations. Hence, the values from this work were only compared with those of AuCuNiPdPt, reported by Thiel et al. [24].
is between 4 • 10 −2 (Cu, Ni) and 7 • 10 −2 (Pt) [24]. Four of five elements of the alloy from this work showed higher and, thus, higher tendency for clustering [21], which might arise from segregation. APT experiments of this work and of [24] were conducted on the exact same APT device. Hence, a -variation by differing experimental procedures can be excluded. In order to reveal slight chemical fluctuations within the tip-shaped sample caused by segregation, the isoconcentration surfaces of each element were systematically investigated. In fact, when highlighting the 14 at.% isoconcentration surfaces of Ta, it is demonstrated that Ta segregates on a nm scale (black arrows Figure 2b). In order to quantify the magnitude of the fluctuations within the segregated regions, elemental concentration profiles in a representative volume (red frame from In order to evaluate elemental distribution within the bcc phase, APT was performed on the region from within a grain. The microstructure, which is shown in the tip reconstruction (Figure 2a), did not indicate any segregation or precipitation at first view. The chemical homogeneity by APT analysis could be quantified by a sample volume independent correlation factor µ which describes the deviation between the ideal, binomial, and the experimental element distribution [21]. µ values of all elements within the entire APT tip were determined ( Table 2) and are in the range of 5.1 · 10 −2 (Hf) up to 24.7 · 10 −2 (Ta). The parameter µ has already been used for quantifying the chemical homogeneity of other HEAs, such as of non-equiatomic FeMnNiCoCr [22], quaternary NbTaTiV [23] and quinary, equiatomic AuCuNiPdPt [24]. Moody et al. [21] emphasize that µ varies with the number of elements and their concentrations. Hence, the µ values from this work were only compared with those of AuCuNiPdPt, reported by Thiel et al. [24]. µ is between 4 · 10 −2 (Cu, Ni) and 7 · 10 −2 (Pt) [24]. Four of five elements of the alloy from this work showed higher µ and, thus, higher tendency for clustering [21], which might arise from segregation. APT experiments of this work and of [24] were conducted on the exact same APT device. Hence, a µ-variation by differing experimental procedures can be excluded. In order to reveal slight chemical fluctuations within the tip-shaped sample caused by segregation, the isoconcentration surfaces of each element were systematically investigated. In fact, when highlighting the 14 at.% isoconcentration surfaces of Ta, it is demonstrated that Ta segregates on a nm scale (black arrows Figure 2b). In order to quantify the magnitude of the fluctuations within the segregated regions, elemental concentration profiles in a representative volume (red frame from Figure 2b) were acquired. The concentration profiles across several sequences of segregations clarify that the fluctuations are highest for Ta and Zr ( Figure 2c) and remain within ±4 at.%. It can be additionally observed, that Ta enriched regions are depleted in Zr and vice versa, highlighted in Figure 2c. Nb is preferentially located in the Ta-enriched regions and Hf in the Zr-enriched regions whereas Ti does not prefer one of the two observed regions (not shown here; concentration profiles of Nb, Hf and Ti are provided in the Supplementary Materials). Segregations of a similar nature can be seen at the µm level in the as-cast state of HfNbTaTiZr [25]. The concentration profile of O did not indicate preferences of this element to be located in one of the two regions. level in the as-cast state of HfNbTaTiZr [25]. The concentration profile of O did not indicate preferences of this element to be located in one of the two regions.

Plastic Deformation Behavior
In order to investigate plastic deformation behavior and active deformation mechanisms of homogenized HfNbTaTiZr, compression tests in a temperature range of T = 77 up to 1073 K were terminated at varying plastic strains ε pl,stop . The stress measured at test termination is defined as σ stop . The corresponding stress-strain curves and characteristic values are presented in Figure 3 and Table 3, respectively. The RT yield strength was determined from three compression tests (Figure 3 left) and was σ 0.2 = (1150 ± 40) MPa which is significantly higher than that observed by Senkov et al. [9]. It is likely, the interstitially dissolved O contributes to the additional strengthening of the bcc solid solution. Additionally, the processing routes from the work of [9] and from this work differ from each other. The hereby arising variations of microstructure and grain size might influence strength, too. In a temperature range of 77 up to 298 K, σ 0.2 significantly decreased with increasing test temperature (Figure 3 center). This behavior of σ 0.2 is typical for the temperature regime I in bcc metals and alloys [26]. This means that screw dislocation motion governing yield strength is thermally activated at these test temperatures [13]. Hence, the knee temperature of as-homogenized HfNbTaTiZr was obviously higher than 298 K. The stress-strain curves of tests at 77, 150, and 298 K all exhibited a similar work hardening rate during plastic deformation. Consequently, one may assume that the dominant, active deformation mechanisms do not change. It additionally confirms that all three test temperatures are located in temperature regime I. At 873 and 1073 K, yield strength is similar (being σ 0.2 = 481 and 461 MPa, respectively; see Figure 3 right) which might be explained by athermal strength at temperature regime II. However, at least the test temperature of 1073 K was located in temperature regime III due to following reasons: (i) At 873 K, the stress-strain curve continuously increases during plastic deformation; however, it flattens with increasing strain, whereas at 1073 K, even a strain-softening behavior was observed after reaching a stress maximum at a plastic strain ε pl = 1.6%. Taking a solidus temperature of 2155 K [27] for HbNbTaTiZr, the homologous temperatures T hom of each of tests was T 873 hom = 0.41 and T 1073 hom = 0.50, respectively. At these temperatures, apart from thermally activated cross-slip of screw dislocations, climb of edge dislocations can contribute to dynamic recovery during plastic deformation which would indicate these two tests to be located in temperature regime III [28]. At high temperatures, microstructural changes as well as damage of the sample can lead to a stress decrease, too. However, microstructural analysis of the deformed sample did not indicate any of these causes (not shown here). (ii) Senkov et al. [11] revealed a significant strain rate dependence of yield strength at 1073 K, proving that at this test temperature, the region of temperature and strain rate-independent strength has already been exceeded.  Table 3.
The RT deformation mechanisms of HfNbTaTiZr after compression to , = 9.8% were investigated by analyzing the corresponding EBSD results. The inverse pole figure (IPF) map of the deformed microstructure, with respect to compression direction (CD), of the deformed microstructure qualitatively exhibited an above average number of grains in red and blue colors (for color code, please see IPF in the inset of Figure 4a). Uniform plastic deformation could be observed by continuously changing orientations within the individual grains and grain flattening perpendicular to the loading axis. Within some grains, abrupt orientation changes were observed in terms of needle-shaped and lenticular features. These features are known to be kink bands, as already revealed by Zherebtsov et al. [8]. A significant number of kink bands were found at angles close to 45° with respect to load direction. It is reasonable that maximum shear stress under uniaxial nominal loading conditions caused severe localization of dislocation slip necessary to form kink bands. Hence, some slip systems are preferentially activated and become kink bands. The appearance and properties of kink bands will be discussed in the subsequent section. To further analyze the present deformation mechanism, the orientation distribution of the IPF map with respect to CD is presented as a color map within an IPF in Figure 4b.  [29]. The same fiber texture after plastic deformation was also found for another refractory HEA, namely the bcc concentrated solid solution NbMoCrTiAl [30]. Stress-strain curves of terminated compression tests at constant test temperature (left), comparable plastic strain ε pl,stop (center) and comparable yield strength σ 0.2 (right). Yield strength σ 0.2 , plastic strain ε pl,stop and stress σ stop at test termination are pointed out in Table 3. The RT deformation mechanisms of HfNbTaTiZr after compression to ε pl,stop = 9.8% were investigated by analyzing the corresponding EBSD results. The inverse pole figure (IPF) map of the deformed microstructure, with respect to compression direction (CD), of the deformed microstructure qualitatively exhibited an above average number of grains in red and blue colors (for color code, please see IPF in the inset of Figure 4a). Uniform plastic deformation could be observed by continuously changing orientations within the individual grains and grain flattening perpendicular to the loading axis. Within some grains, abrupt orientation changes were observed in terms of needle-shaped and lenticular features. These features are known to be kink bands, as already revealed by Zherebtsov et al. [8]. A significant number of kink bands were found at angles close to 45 • with respect to load direction. It is reasonable that maximum shear stress under uniaxial nominal loading conditions caused severe localization of dislocation slip necessary to form kink bands. Hence, some slip systems are preferentially activated and become kink bands. The appearance and properties of kink bands will be discussed in the subsequent section. To further analyze the present deformation mechanism, the orientation distribution of the IPF map with respect to CD is presented as a color map within an IPF in Figure 4b.  [29]. The same fiber texture after plastic deformation was also found for another refractory HEA, namely the bcc concentrated solid solution NbMoCrTiAl [30].

Appearance and Properties of Kink Bands
The kink bands which form during plastic deformation at RT (298 K), Figure 4a, were analyzed in detail as follows. Firstly, a ROI that contained kink bands was chosen from the overview map, highlighted by the red rectangle in Figure 4a. The orientation map of this ROI is presented in Figure 5a (top). Needle-shaped kink bands that adjoin a grain boundary as well as lenticular bands within the adjacent grain were observed. Note that the presented orientation map only revealed a two-dimensional section of the deformed sample. Hence, the observed kink bands could possess varying morphologies if other sections or sample orientations of the deformed sample were analyzed. The local  Figure 5a (bottom). The KAM map reveals a significant misorientation at the kink band boundaries only. Hence, the crystallographic orientation within the kink bands themselves does not change significantly. These results support the misorientation line profiles across kink bands determined for the quaternary derivative HfNb 0.7 TiZr, provided by Wang et al. [5]. Additionally, the misorientation angles for different kink bands as well as the misorientation angle along the boundary of an individual kink varied, revealed by the varying shades of red color in the KAM map. For visualization and quantification of the misorientation angle at the boundary along with each individual kink band, the kink band with the highest KAM was selected for further analysis (red polygonal frame in Figure 5a, bottom). The color-coded misorientation angle along the kink band boundary (Figure 5b) revealed misorientation angles between 3 and 25 • . The relative frequency distribution of these angles (bin size of 2 • ) of this kink band is plotted in Figure 5c. It exhibited a frequency maximum at 22.2 • and a full width at half maximum (FWHM) of 4.6 • when fitting the misorientation angles by a Bi-Gaussian fit function. Since the misorientation angle distribution is asymmetrical, a Bi-Gaussian function that allows two different values for half widths at half maximum (HWHM) was chosen. The quality of the Bi-Gaussian fit can be expressed by the adjusted R-squared R 2 adj = 0.83. The deviation from the maximum value of unity was explained by the non-steady increase of frequency in the low misorientation angle range. The fit quality also depends significantly on the selected bin size. As an example, R 2 adj increases to 0.96 for a bin size of 3 • instead of 2 • . However, for comparability of misorientation data with other deformation conditions, bin size was kept constant at 2 • . The orientation distribution (Figure 5d) of rotation axes within the ROI as depicted in the IPF map of Figure 5b reveals a maximum in the [211]-direction. It was, therefore, found that a single slip for kink band formation occurred on the resulting {011} slip plane. This result expands experimental findings from [5,31] where 101 rotation axes were experimentally observed for kink band formation on HfNbTaTiZr and HfNb 0.7 TiZr.
For comparing kink band properties at various deformation conditions, the following steps were carried out: first, the KAM overview map of a section with (2100 · 2100) µm 2 of a deformed sample was plotted to reveal kink bands with the highest misorientation angles by systematically adjusting the threshold and upper limit of KAM. Second, a ROI was selected that comprised the kink band with the highest misorientation angles (all selected ROIs are presented in the Supplementary Materials). Third, the relative frequency distribution of misorientation angles was plotted in order to determine the frequency maximum by fitting the data by a Bi-Gaussian function. The misorientation angle at frequency maximum and the FWHM, which is the sum of both HWHM, were used as characteristic values for kink band properties. It should be emphasized that the present evaluation routine is not regarded as a standardized method. Kink band properties can vary when other sections of the deformed sample are investigated. Additionally, different characteristic values might be defined to evaluate kink band properties. The characteristic values of kink band misorientation angle distribution are presented in Table 4.

Appearance and Properties of Kink Bands
The kink bands which form during plastic deformation at RT (298 K), Figure 4a, were analyzed in detail as follows. Firstly, a ROI that contained kink bands was chosen from the overview map, highlighted by the red rectangle in Figure 4a. The orientation map of this ROI is presented in Figure 5a (top). Needle-shaped kink bands that adjoin a grain boundary as well as lenticular bands within the adjacent grain were observed. Note that the presented orientation map only revealed a two-dimensional section of the deformed sample. Hence, the observed kink bands could possess varying morphologies if other sections or sample orientations of the deformed sample were analyzed. The local misorientation within the ROI can be visualized by the kernel average misfit (KAM) as depicted in Figure 5a (bottom). The KAM map reveals a significant misorientation at the kink band boundaries only. Hence, the crystallographic orientation within the kink bands themselves does not change significantly. These results support the misorientation line profiles across kink bands determined for the quaternary derivative HfNb0.7TiZr, provided by Wang et al. [5]. Additionally, the misorientation angles for different kink bands as well as the misorientation angle along the boundary of an individual kink varied, revealed by the varying shades of red color in the KAM map. For visualization and quantification of the misorientation angle at the boundary along with each individual kink band, the kink band with the highest KAM was selected for further analysis (red polygonal frame in Figure 5a, bottom). The color-coded misorientation angle along the kink band boundary (Figure 5b) revealed misorientation angles between 3 and 25°. The relative frequency distribution of these angles (bin size of 2°) of this kink Kink band properties of RT compression tests with varying plastic strains ε pl,stop = 1.9%, 9.8%, and 14.3% are presented in Figure 6 (top). It is observed that the misorientation angle at frequency maximum significantly increases with increasing ε pl,stop . There is no overlap of frequency distribution in the range of FWHM. This result supports the findings by Zherebtsov et al. [8], who found an increase of misorientation angle for increasing plastic strains in the range of 15% to 40%. It was concluded that kink band properties qualitatively correlate with plastic strain and, thus, with strain hardening. Additionally, the maximum value of relative frequency decreased with increasing ε pl,stop as a result of a larger range of misorientation seen in the kink band. The influence of test temperature on misorientation angle distribution is depicted in Figure 6 (bottom). The plastic strains at test termination ε pl,stop (77 K) = 10.4%, ε pl,stop (150 K) = 10.0%, and ε pl,stop (298 K) = 9.8% were within a tolerance of ∆ε pl,stop = 0.6%. It is assumed that the plastic strain conditions should be comparable. The misorientation angle at maximum frequency for 77, 150, and 298 K were 25.8 • , 24.4 • , and 22.2 • , respectively and, therefore, exhibited a maximum difference of 3.6 • . As observed in the previous part, work hardening behaviors at 873 and 1073 K significantly differ from each other, although their yield strengths were similar. The consequences of kink band formation are discussed in this section. A parameter that indicates dislocation-mediated plasticity is the aspect ratio, which, in this work, was defined as the ratio of the grain size parallel and the one perpendicular to CD. An aspect ratio of unity, therefore, indicated equiaxed grains. On the one hand, the sample deformed at 873 K (Figure 7a) exhibited an aspect ratio of 0.67, which was derived from grain flattening perpendicular to the loading axis, which is explained by pencil glide being the main active deformation mechanism. At this test temperature, kink bands were observed ( Figure  7a). On the other hand, the aspect ratio of the grains in the sample deformed at 1073 K (Figure 7b) was 0.97. Diffusion-based grain boundary sliding might contribute to plastic deformation, as already observed by Senkov et al. [11], leading to almost equiaxed grains. Additionally, plastic deformation by the already discussed combination of favored Figure 6. Relative frequency distribution of misorientation angles (2 • bins, presented by histograms) and Bi-Gaussian fit (line diagrams) of respective data set. Influence of plastic strain ε pl,stop on kink band properties in HfNbTaTiZr, deformed at 298 K: 1.9% vs. 9.8% vs. 14.3% (top) and influence of test temperature T on misorientation angle distribution at comparable plastic strains ε pl,stop : 77 vs. 150 vs. 298 K (bottom).
As observed in the previous part, work hardening behaviors at 873 and 1073 K significantly differ from each other, although their yield strengths were similar. The consequences of kink band formation are discussed in this section. A parameter that indicates dislocationmediated plasticity is the aspect ratio, which, in this work, was defined as the ratio of the grain size parallel and the one perpendicular to CD. An aspect ratio of unity, therefore, indicated equiaxed grains. On the one hand, the sample deformed at 873 K (Figure 7a) exhibited an aspect ratio of 0.67, which was derived from grain flattening perpendicular to the loading axis, which is explained by pencil glide being the main active deformation mechanism. At this test temperature, kink bands were observed (Figure 7a). On the other hand, the aspect ratio of the grains in the sample deformed at 1073 K (Figure 7b) was 0.97. Diffusion-based grain boundary sliding might contribute to plastic deformation, as already observed by Senkov et al. [11], leading to almost equiaxed grains. Additionally, plastic deformation by the already discussed combination of favored cross-slip of screw dislocations and climb of edge dislocations is active. These thermally activated deformation mechanisms that become more dominant with increasing test temperature counteract to conventional pencil glide as observed in temperature regime I and, thus, suppress kink band formation. We, therefore, conclude that kink band formation does not depend on yield strength, but on strain hardening behavior, at these temperatures. temperature counteract to conventional pencil glide as observed in temperature regime I and, thus, suppress kink band formation. We, therefore, conclude that kink band formation does not depend on yield strength, but on strain hardening behavior, at these temperatures.

Conclusions
In equiatomic HfNbTaTiZr, kink band formation as a localized deformation mechanism was revealed in a temperature range from 77 up to 873 K. At room temperature, kink bands could already be observed at low plastic strains of 1.9%. The maximum frequency of misorientation angle distribution significantly increased with increasing plastic strain in a strain range of 1.9% up to 14.3%. Although mechanical twinning and phase formation were identified as deformation mechanisms in addition to pencil glide at 77 K [31], the kink band properties at this test temperature were comparable to the ones at RT determined from the same strain conditions. This leads to the conclusion that at 77 K, dislocation slip still dominates plastic deformation. At 1073 K, dislocation slip is superimposed by favored cross-slip and edge dislocation climb leading to enhanced dynamic recovery as indicated by the corresponding stress-strain curve. Accompanied by grain boundary sliding, kink band formation as the deformation mechanism was not active at this test temperature. Additional results are summarized in the following:

•
In the homogenized state, segregation on the nanometer scale could be revealed by an isoconcentration surface analysis of the APT tip reconstruction only. In general, it is hence recommended to apply isoconcentration surface analysis for evaluating the homogeneity of HfNbTaTiZr and concentrated solid solutions. The autocorrelation factor can be used as an indicator for segregation.

•
Kernel average misorientation analysis is suited to detect kink bands from EBSD data.

•
The misorientation angle distribution along an individual kink band was fitted by a Bi-Gaussian peak function. The angle of maximum frequency and the FWHM can be used to characterize the kink band properties.

Conclusions
In equiatomic HfNbTaTiZr, kink band formation as a localized deformation mechanism was revealed in a temperature range from 77 up to 873 K. At room temperature, kink bands could already be observed at low plastic strains of 1.9%. The maximum frequency of misorientation angle distribution significantly increased with increasing plastic strain in a strain range of 1.9% up to 14.3%. Although mechanical twinning and ω phase formation were identified as deformation mechanisms in addition to pencil glide at 77 K [31], the kink band properties at this test temperature were comparable to the ones at RT determined from the same strain conditions. This leads to the conclusion that at 77 K, dislocation slip still dominates plastic deformation. At 1073 K, dislocation slip is superimposed by favored cross-slip and edge dislocation climb leading to enhanced dynamic recovery as indicated by the corresponding stress-strain curve. Accompanied by grain boundary sliding, kink band formation as the deformation mechanism was not active at this test temperature. Additional results are summarized in the following:

•
In the homogenized state, segregation on the nanometer scale could be revealed by an isoconcentration surface analysis of the APT tip reconstruction only. In general, it is hence recommended to apply isoconcentration surface analysis for evaluating the homogeneity of HfNbTaTiZr and concentrated solid solutions. The autocorrelation factor µ can be used as an indicator for segregation.

•
Kernel average misorientation analysis is suited to detect kink bands from EBSD data.

•
The misorientation angle distribution along an individual kink band was fitted by a Bi-Gaussian peak function. The angle of maximum frequency and the FWHM can be used to characterize the kink band properties.