Controllable Fabrication of Heterogeneous p-TiO 2 QDs @ gC 3 N 4 p-n Junction for Efficient Photocatalysis

Photocatalytic technology has been considered to be an ideal approach to solve the energy and environmental crises, and TiO2 is regarded as the most promising photocatalyst. Compared with bare TiO2, TiO2 based p-n heterojunction exhibits a much better performance in charge separation, light absorption and photocatalytic activity. Herein, we developed an efficient method to prepare p-type TiO2 quantum dots (QDs) and decorated graphitic carbonitrile (g-C3N4) nanocomposites, while the composition and structure of the TiO2@g-C3N4 were analyzed by X-ray diffraction, Fourier transform infrared spectroscopy ,thermogravimetric analysis, transmission electron microscopy, X-ray photoelectron spectroscopy and UV-visible diffuse reflectance spectroscopy characterizations. The characterization results reveal the surface decorated TiO2 quantum dots is decomposed by titanium glycerolate, which exhibits p-type conductivity. The presence of p-n heterojunction over interface is confirmed, and photoluminescence results indicate a better performance in transfer and separation of photo-generated charge carriers than pure semiconductors and type-II heterojunction. Moreover, the synergy of p-n heterojunction over interface, strong interface interaction, and quantum-size effect significantly contributes to the promoted performance of TiO2 QDs@g-C3N4 composites. As a result, the as-fabricated TiO2 QDs@gC3N4 composite with a p/n mass ratio of 0.15 exhibits improved photo-reactivity of 4.3-fold and 5.4fold compared to pure g-C3N4 in degradation of organic pollutant under full solar spectrum and visible light irradiation, respectively.


Introduction
With the increasing concerns regarding the global environmental and energy-related crises over the past decades, photocatalytic technology has been considered to be an effective approach since the foundation of Fujishima-Honda effect in 1972 [1,2].The key for an efficient photocatalytic process lies in the design and construction of highly active photocatalyst, which requires a wide light absorption edge, fast transfer and separation of photo-generated charge carriers, and quick surface redox reaction [3][4][5][6][7].TiO2 is regarded as the most promising photocatalyst due to the advantages such as earth abundance, low price, excellent thermal and chemical stability, and being environmentally friendly [8,9].Unfortunately, the broad band gap (i.e.3.2 eV for anatase) means TiO2 can only be excited by ultraviolet (UV) light, which is less than 5% in the solar spectrum.Meanwhile, the fast charge recombination rate in single TiO2 also results in a low quantum efficiency.Therefore, it is an urgently necessary to promote the light absorption and charge separation efficiency of TiO2 to meet the requirements of industrial applications [10,11].
Recently, many researchers have focused on the modification of TiO2 towards an improved photocatalytic performance, including for: morphology modulation [12][13][14], metal or nonmetal doping [15][16][17][18], defect engineering [19][20][21][22], and fabrication of hetero/homojunction [2,[23][24][25][26][27].In our previous reports, we found that the introduction of titanium vacancies into TiO2 will widen the valence band, which controls the mobility of holes inherently and thus increase charge separation efficiency.Moreover, the introduction of metal vacancies can alter TiO2 from an n-type semiconductor to a p-type semiconductor [28].Pan et-al.modified p-type TiO2 with n-type TiO2 quantum dots (QDs) to construct p-n homojunction, and the resulted p-n homojunction exhibits significantly high photo-activity compared with pure type TiO2, which is attributed to the formation of large electronic field over the interface [29].Moreover, besides the influence of p-n homojunction, quantum sized TiO2 can also enhance the charge separation due to the quantum size effect [13,[30][31][32].However, in these reports, both the titanium defected TiO2 and TiO2 QDs still absorb only UV light, which limits their applications under sunlight.
Graphic carbon nitride (g-C3N4) is a promising metal-free photocatalyst in the field of H2 production, organic pollutant degradation, CO2 reduction, and artificial photosynthesize due to the suitable band structure (2.7~2.8 eV), excellent chemical and thermal stability [33][34][35][36][37]. Usually, g-C3N4 is synthesized by thermal condensation of melamine, urea or other triazine derivatives, but the resultant product exhibits an irregular 2D aggregation structure, leading to a lower surface area and electrical conductivity, as well as an increased charge carrier recombination [38,39].Both theoretical and experimental results suggest that nanosheet structured g-C3N4 will exhibit a larger surface area and lower charge transfer resistance, so the exfoliation of bulk g-C3N4 into nanosheets has been regarded as an effective approach to promote the photocatalytic performance of g-C3N4 [40,41].Wang et-al.applied a liquid exfoliation method on bulk g-C3N4 to prepare layer g-C3N4, and the charge transfer resistance decreased by 75% according to the electrochemical impedance spectroscopy (EIS) results, indicating a lower charge recombination [42].Cheng et-al.conducted an exfoliation treatment on bulk g-C3N4 using a simple thermal oxidation etch method, and g-C3N4 nanosheets with layer thickness of 2 nm and surface area of 306 m 2 /g were obtained.Compared with bulk g-C3N4, the charge carrier life in the as-prepared g-C3N4 nanosheets is prolonged because of the quantum confinement effect [43].Li and coworkers also reported the synthesizing of 6-9 atomic thick g-C3N4 nanosheets by a thermal exfoliation approach, the photocatalytic degradation rate is 2.9 times higher than that of bulk g-C3N4 [44].Therefore, the exfoliation of bulk g-C3N4 to nanosheets can effectively increase the surface area, and thus improve charge transfer and separation.
Construction of heterojunction is an effective approach to improve the photocatalytic performance by combining both the advantage of two semiconductors, and the electronic field will enhance the charge transfer and separation across the interface.Type II heterojunction with staggered band alignment is the most widely studied structure.Jiang et-al.placed 5.5 nm sized TiO2 on g-C3N4 nanosheets.Due to the formation of type-II heterojunction, the resultant composites exhibited a Rhodamine B (RhB) degradation rate of 2.5-fold compared to pure g-C3N4 [25].However, this is due to the fact that the work function of the same types semiconductor is closed to each other, which limits the driving force in type-II heterojunction.Instead, with different conductivity types semiconductor contacts, p-n heterojunction will be formed and the difference of the work function is large enough to realize a more efficient charge carrier separation [26,29].For example, Wang et-al.reported that Cu2O/TiO2 p-n junction exhibits a much better photoelectrochemical activity than that of pure TiO2 and pure Cu2O [27].
In this work, based on the improvement of our previous work [26,28,29], nanosized titanium glycerolate (TiGly), precursors of p-type TiO2 quantum dots, were successfully synthesized and insitu deposited on the surface of g-C3N4, TiO2@g-C3N4 nanosheet p-n heterojunctions were then obtained after calcination in air.This p-n junction can achieve the function of killing three birds with one stone: p-type TiO2 QDs for promoted charge separation, g-C3N4 nanosheets for lower charge resistance and p-n junction for enhanced charge transfer over interface.Therefore, compared with pure g-C3N4 and TiO2/g-C3N4 type-II heterojunction, TiO2 QDs@g-C3N4 p-n heterojunctions exhibit promoted electron-hole separation efficiency and excellent photocatalytic performance in degradation of organic pollutant and hydrogen evolution.

Results and Discussion
The synthesizing process of bulk g-C3N4 and TiO2@g-C3N4 p-n heterojunctions were diagrammatically presented in Scheme 1.Consistent with the literature reported, melamine was calcined in air at 550 °C and then bulk g-C3N4 were obtained.Previously, we have demonstrated that titanium glycerolate (TiGly) is the precursor of p-type TiO2, the organic groups will be gradually removed after calcination, and titanium vacancies (VTi) will be introduced into TiO2 during the conjunction process of the remaining Ti-O-Ti parallel lattice chains.Herein, in order to fabricate TiO2@g-C3N4 p-n heterojunction, bulk g-C3N4 is synthesized firstly, and then TiGly nanoparticles were in-situ deposited on the surface of g-C3N4 and labeled as TGC-x according to the added g-C3N4.
After calcination in air, g-C3N4 was exfoliated and TiGly nanoparticles were decomposed to p-type TiO2 QDs (labeled as PTC-x).The sharp peak at about 27.4° in the X-ray diffraction (XRD) pattern of TGC-x (Figure 1a) can be attributed to the periodic accumulation of layers of conjugated aromatic systems in bulk g-C3N4 [45].In the sample TGC-20 and TGC-40, a weak peak appearing at about 10.2°, which is the characteristic peaks corresponding to TiGly [28], indicating the presence of TiGly nanoparticles.As for TGC-60, the content of TiGly is too low to be detected.After being calcined at 470 °C for 1 h, TiGly nanoparticles will be decomposed into anatase ptype TiO2.As shown in Figure 1b, no diffraction peaks of TiGly can be observed, only anatase TiO2 (JCPDS No. 21-1272) and g-C3N4 (JCPDS No. 87-1526) can be observed in PTC-x, with no other visible phases or impurities.Notably, the full-width at half maxima (FWHM) of peaks at 25.3° corresponding to (101) planes of p-type TiO2 nanoparticles is broadened from 0.57 to 0.65 compared with bulk p-TiO2, so the average particle size of the TiO2 nanoparticles is smaller than the bulk p-TiO2 according to Scherer Equation.The same phenomenon can also be observed in bulk g-C3N4 and g-C3N4 nanosheets, the peak at 27.4° corresponding to (002) plane of g-C3N4 nanosheets is broadened and drastically weakened from PTC-60 to PTC-20, which is due to the decreased thickness of nanosheets during the thermal exfoliation process [39].Moreover, we also calculated the lattice constant of the p-type TiO2 nanoparticles based on XRD patterns, the results indicate that a = b = 3.793 Å, slightly larger than normal anatase TiO2 (a = b = 3.785 Å for JCPDS No. 21-1272), whereas the c axis shrinks from 9.514 Å to 9.488 Å, which is identical with that of titanium defected TiO2 [28].
Thermogravimetric (TG) tests were conducted to quantify the relative content of TiO2 QDs in the as-prepared samples.As shown in Figure 2, the weight loss of the samples below 80 °C is due to the removal of surface absorbed water, whereas the weight loss between 80 °C and 400 °C is attributed to the decomposition of titanium glycerolate as shown in Equation (1) [28,29].Since bulk g-C3N4 exhibits almost no weight loss in this range, the weight loss of TGC-x can all assigned to the decomposition of TiGly.As shown in Figure 2, the weight loss is 20.03%, 9.77% and 7.98% for TGC-20, TGC-40 and TGC-60, respectively.Therefore, according to Equations ( 2) and ( 3), the mass content of TiGly in TGC-x can be calculated as 43.7%, 21.3% and 17.4%, respectively, corresponding to a ptype TiO2 QDs mass content of 29.6%, 12.8% and 10.2% in PTC-20, PTC-40 and PTC-60, respectively.Additionally, there is a sight weight increase after 80 °C for all the samples, which may be due to the impurity in the sample gas used in TG tests, but this deviation will not affect the calculated QDs content in the samples.TiGly (Ti3(C3H4O3)4) + 14O2→3Ti1-xO2 + 12CO2 + 10H2O (1) Among these figures: yTG is the calculated content of TiGly , %; Ws is the weight loss of TGC-x, %; WTG is the weight loss of pure TiGly, %; mTiO2 is the calculated mass of TiO2 in unit mass of PTC-x, g; mg-C3N4 is the calculated mass of g-C3N4 in unit mass of PTC-x, g; yTiO2 is the calculated mass content of ptype TiO2 QDs in PTC-x, %. High resolution transmission electron microscopy (HRTEM) analyses were conducted to reveal the morphology and composition of the samples.Unlike the densely packed bulk g-C3N4 reported in literatures [39], the as-prepared g-C3N4 exhibits a nanosheet structure, the edges are curled and rough due to the minimizing surface energy (Figure 3a), which provides a lower resistance pathway for charge transfer.As shown in Figure 3b-d, the light contrast nanosheets are g-C3N4 nanosheets whereas the dark contrast are the p-type TiO2 nanoparticles decomposed from TiGly. Figure 3e shows the lattice fingers of 0.35 nm and 0.48 nm in the dark contrast, corresponding to the (101) and (002) planes of anatase TiO2, which reveal the exposure of (010) facet of anatase, consistent with the XRD results [31].The typical size of TiO2 nanoparticles is 4-5 nm according to the particle size distribution result shown in the inset of Figure 3e, which is accordance with the characteristic size of quantum confinement effect.It is noteworthy that when the p-type TiO2 QDs are in-situ grown on the surface of g-C3N4, there is a strong interaction that exists between them so that the TiO2 QDs cannot be peeled off even after a 30 min ultra-sonication process.Moreover, the strong interaction implies an obvious interface heterojunction between TiO2 QDs and g-C3N4, which will enhance the transfer of photo generated electrons and holes [25].In addition, in agreement with the TG results, the relative content of TiO2 QDs decreases from PTC-20 to PTC-60.In order to further investigate the composition and interaction between p-type TiO2 QDs and g-C3N4 in the as-prepared composites, Fourier transform infrared spectroscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS) characterizations were conducted.As shown in Figure 4a, for the TGC-x, there are three characteristic bands corresponding to g-C3N4, namely the broad peaks located at 3000-3400 cm −1 assigned to the stretching of N-H bonds, the strong peaks at 1250-1650 cm −1 due to the stretching vibration of C=N heterocycles and C-N bonds, and the band around 808 cm −1 related to the ring vibration of s-triazine [45][46][47][48].Moreover, besides the above three peaks, another three peaks related to TiGly appearing in TGC-x, the peaks located at around 1000-1150 cm −1 were attributed to the alcoholic Ti-O-C stretching mode, the apparent peak at 611 cm −1 was indexed to the stretching mode of Ti-O bonds, and the bands located at 2855-2927 cm −1 were assigned to the glycerol C-H stretching vibration [49].Besides, the broad peak over 3000-3600 cm −1 was attributed to the presence of physically adsorbed water and glycerol O-H stretching mode.Therefore, by combining with the XRD, TG and FT-IR results, it is proved that the as-prepared TGC-x samples is composed by TiGly and g-C3N4.Upon calcination, the major FT-IR peaks of g-C3N4 almost all remained in PTC-x samples (Figure 4b).However, the bands assigned to C-H and O-H in TiGly disappeared, while only the stretching band of Ti-O remained, indicating the transformation of TiGly to TiO2, further confirming the formation of TiO2 QDs@g-C3N4 heterojunction.Moreover, with the decrement of g-C3N4 content from PTC-60 to PTC-20, the intensity of s-triazine ring vibration 808 cm −1 also decreases, which is in agreement with the above TG results.It is noteworthy that the stretching vibration of Ti-O-Ti shifted significantly towards a lower wavenumber in PTC-x composites, suggesting a strong interaction exists between p-TiO2 QDs and g-C3N4 [25], which is in favor of charge transfer across the interface and thus promotes the photocatalytic performance of the heterojunction.
XPS spectrum were recorded to study the status of the C, N, Ti and O elements in the composites.Figure 5a shows the C1s XPS spectra of the samples, there are two main peaks located at 284.8 eV and 288.5 eV, respectively.The peak located at higher binding energy is attributed to the sp3-bonded C of N-C=N2 in g-C3N4, and the peak located at 284.8 eV is due to the surface contaminated carbon during XPS test and sp2-hybridized carbon atoms presented in graphic domains [29].In the N1s XPS spectra (Figure 5b), a asymmetric profiles can be observed in all the samples, with a main peak at 401 eV and a shoulder peak at lower binding energy, the main peak is due to the sp2-hybridized nitrogen (C-N-C), while the shoulder peak is usually attributed to amino functional groups with a hydrogen atom (C-NH) and sp3-hybridized nitrogen (N-[C]3) [25,39].For the Ti 2p XPS spectra of the PTC-x (Figure 5c), the binding energy of Ti 2p3/2 and Ti 2p1/2 are observed at 458.9 eV and 464.4 eV, respectively, suggests the existence of TiO2 in the samples.Notably, compared with the Ti 2p binding energy of 458.4 eV in n-type TiO2 [29], the Ti 2p binding energy in the as-prepared samples shifted towards a higher binding energy, indicating the existence of titanium vacancies (VTi) and p-type properties of the TiO2 QDs [28].The O1s XPS spectrum were shown in Figure 6, there is only one symmetrical peak at around 532.7 eV appearing in pure g-C3N4, which is attributed to the loosely bonded oxygen species on the surface (O2, H2O or OH groups), no peaks corresponding to C-O and N-C-O appeared at 531.4 eV, indicating that no O doping process occurred in g-C3N4 during the calcination process [38].As for the TiO2@g-C3N4 composites, the O1s peaks split into two peaks located at 532.7 eV and 529.8 eV, respectively.The lower binding energy is assigned to the oxygen anions (O 2− ) in the crystal lattice of anatase [28], and the concentration of TiO2 QDs is proportional to the intensity of this peak.As shown in Figure 6b-d, from PTC-20 to PTC-60, the intensity of this peak becomes obviously weak, confirming the gradually decreased content of TiO2 QDs in the composites.These results are in good agreement with the TEM, TG and FT-IR results, indicating that the composites are composed of g-C3N4 and p-type TiO2 QDs, and that the content of TiO2 QDs decreases from PTC-20 to PTC-60.The light absorption properties of the as-prepared samples were characterized by UV-visible diffuse reflection spectrum (UV-vis DRS).As illustrated in Figure 7a, pure g-C3N4 can absorb light from UV region to visible light up to 465 nm, while p-type TiO2 only absorb UV light up to 400 nm.As for the TiO2 QDs@g-C3N4 composites, there is a remarkable absorption edge extension to the visible region compared with single TiO2 [39].Moreover, with the increasing content of g-C3N4 form PTC-20 to PTC-60, the optical absorption edge of p-n heterojunction shifts towards a longer wavelength, indicating a stronger light absorption in the visible light region, which is beneficial for the improvement of photocatalytic performance.Meanwhile, the quantum-size effect of the p-type TiO2 QDs is illustrated by VB XPS spectra.As shown in Figure 7b, a blue shift of VB edge is observed in the as-prepared heterojunctions due to the existence of TiO2 nanoparticles, and this tendency becomes more and more obvious with the increment of TiO2, confirming the quantum dots nature of the surface decorated p-type TiO2 nanoparticles [31].As mentioned above, we have demonstrated that the surface deposited TiO2 QDs is abundant in titanium vacancies, while both experimental and density functional theoretical (DFT) results have indicated that metal defected TiO2 is p-type semiconductor [28].In general, g-C3N4 exhibits n-type conductivity, therefore, p-n heterojunctions will be formed across the interface, which can afford a large electrical filed and more efficient charge separation.Therefore, according to the band gap and valence band (VB) position of pure g-C3N4 and TiO2, the band alignment of the p-n heterojunction (PTC-40) is diagrammed in Scheme 2. Both TiO2 and g-C3N4 can be excited under λ > 365 nm, charge redistribution process will occur to equilibrate the Fermi level (Ef) due to the large difference of Ef between p-type TiO2 and n-type g-C3N4, the consequence is that the photogenerated electrons migrate to the conduction band (CB) of TiO2 and holes to the g-C3N4 VB.However, only g-C3N4 can be excited under visible light irradiation (λ > 400 nm), and the photogenerated electrons will still transfer to the CB of TiO2, while the holes tend to keep stay in the VB of g-C3N4.In both cases, an efficient electronhole spatial separation can be realized and the lifetime of charge carriers can also be prolonged, these separated electrons can react with O2 or H2O to form reactive oxygen species (•O2 − ) or H2, while the holes will oxidize an organic pollutant or sacrificial agent directly.In addition, the presence of metal vacancies will enlarge the width of VB, which controls the mobility of holes inherently [28], and thus the synergy influence of metal vacancies, quantum confinement effect, and nanosheet structure can effectively promote the charge transfer and separation across the interface.Scheme 2. Schematic illustration of TiO2 QDs@g-C3N4 p-n heterojunction and the pathway for electron-hole transfer and separation over the junction under simulated solar irradiation (λ > 365 nm) and visible light irradiation (λ > 400 nm).
The facilitated charge separation by the p-n heterojunction was confirmed by photoluminescence (PL) spectra.As shown in Figure 8, pure g-C3N4 has an emission peak around 450 nm, whereas p-TiO2 exhibits a signal at around 400nm, which is due to the band-band transition, namely the energy corresponding to the emission is close to the excitation energy of g-C3N4 and TiO2, respectively [25,29].The PL intensity of PTC-x is much lower than pure p-type TiO2 and g-C3N4, indicating a promoted electron-hole separation by the p-n heterojunction.Notably, PTC-40 exhibits the lowest PL intensity among the samples, suggesting a higher charge separation efficiency and a better photocatalytic performance, which also indicates that there exists an approximate p/n ratio between the p-type TiO2 and n-type g-C3N4 in the heterojunction.Photocatalytic degradation of organic pollutants and photocatalytic water splitting were conducted to evaluate the performance of as-prepared TiO2@g-C3N4 p-n heterojunctions.Figure 9a shows the photodegradation rate of the samples based on pseudo-first-order reaction mode.Under simulated sunlight irradiation (λ > 365nm), the degradation rate of MO for PTC-40 with a TiO2 (p) to g-C3N4 (n) mass ratio of 0.15 is 0.52 min −1 •g −1 , which is the highest among the PTC-x and is 4.3-fold higher than that of pure g-C3N4.Moreover, we also tested the photoactivity with a cut-off filter of λ > 400 nm to evaluate the visible light photocatalytic performance, the reaction rate exhibits the same trends with that under simulated solar spectrum (Figure 9b), and the reaction rate for MO degradation of PTC-40 is 0.125 min −1 •g −1 , 5.4-fold higher than pure g-C3N4.This result confirms that p-n heterojunction exhibits a better photocatalytic performance than single photocatalyst and that the as-prepared TiO2@g-C3N4 is active under visible light.The photocatalytic H2 evolution reaction rate is shown in Figure 10a, the H2 release rate for g-C3N4, PTC-20, PTC-40 and PTC-60 is 186 μmol respectively.It is clearly that the H2 evolution rate of PTC-40 is the fastest, which is 5.8-fold of pure g-C3N4, 1.5-fold of PTC-20 and 1.3-fold of PTC-60.Combining with the PL results and photoactivity, we can get the conclusion that PTC-40 has the most efficient electron-hole separation, and thus exhibits the best photocatalytic performance among the as-fabricated samples.Meanwhile, this phenomenon also indicates that a suitable p/n ratio is required to construct the best p-n heterojunction.In comparison, we also loaded n-type TiO2 QDs on the surface of g-C3N4 to construct a type-II heterojunction and found that the promotion in photoactivity is far from that by p-n heterojunction (1.44-fold vs. 5.8-fold in H2 evolution), illustrating that p-n heterojunctions are more effective in accelerating photogenerated charge carrier separation and promoting the photocatalytic performance.

Materials
Ethanol, glycerol, melamine and methyl orange (MO) were all purchased from Tianjin Jiangtian Fine Chemical Research Institute.Titanium butoxide (C16H36O4Ti, TBOT), triethanolamine (TEOA) and phenol were purchased from J&K chemical.Milli-Q ultra-pure water with a resistivity larger than 18.2 MΩ•cm was used in all experiments.All the chemicals were reagent grade and used as received.

Preparation of Bulk g-C3N4
Bulk g-C3N4 was synthesized by thermal annealing melamine under air atmosphere.Typically, 5 g of melamine was put into an airtight crucible, then the crucible was placed into a muffle furnace and calcined at 550 °C for 4 h with a ramping rate of 5 °C/min.After being cooled down to room temperature naturally, the obtained yellow powder is bulk g-C3N4.

Preparation of TiO2 QDs@g-C3N4 p-n Heterojunction
As shown in Scheme 1, for the fabrication of TiO2 QDs@g-C3N4 p-n heterojunction, x (x = 20, 40, 60) mg g-C3N4 was dispersed in 148 ml ethanol and sonicated for one hour.After that, 5 mL glycerol was added into the solution.After being stirred for another 20 min, 400 μL TBOT was dropwised into the solution and then titanium glycerolate (TiGly) was in-situ grown on the surface of g-C3N4, the solution was stirred at room temperature for 16 h.The resulted powders (labeled as TGC-x) were washed with water and absolute ethanol for several times, and dried at 70 °C overnight.After calcination of TGC-x in air at 470 °C for 1 h, TiO2 QDs@g-C3N4 p-n heterojunctions were obtained and labeled as PTC-x (x = 20, 40, 60).As a reference, n-type TiO2 QDs deposited g-C3N4 was synthesized with the same procedure (x = 40 mg) except that glycerol was replaced by 233 μL NH3•H2O for the purpose of triggering the nucleation of TiO2 on g-C3N4 as previously reported (the reference sample was labeled as NTC-40) [29].

3.4.Characterization of Photocatalysts
The calcination temperature for the decomposition of titanium glycerolate and the content of TiO2 was determined by thermogravimetric analysis (TGA Q500, TA Instruments, DE, USA) with air gas flow at 50 mL/min in a range of 30-500 o C (5 °C/min).In order to obtain the composition of the samples, Fourier transform infrared spectroscopy (FT-IR, Bruker Tensor-27 spectrum, Bavaria, Germany) was conducted before and after calcination, the FT-IR spectra were acquired in the range of 400-4000 cm -1 with a resolution of 1 cm -1 .
All the samples were characterized with an X-ray diffractometer (XRD-6100, Shimadzu, Kyoto, Japan) to determine the crystalline properties.The X-ray diffractometer was equipped with a Cu Kα radiation at 40 kV and 30 mA at a scanning rate of 5°/min.The diffraction patterns were determined over 2 theta range of 5 o -90 o with a resolution of 2 o /min.To obtain the average size of the crystalline size, Scherrer equation was used (D=0.9λ/βcosθ),whereas the lattice constants was calculated according to Bragg equation of 2dhklsinθ=λ, where λ is the applied wavelength, θ is the Bragg angle and β is the FWHM value.
The chemical states of the as-prepared samples were characterized by X-ray photoelectron spectroscopy (PHI-1600, ULVAC-PHI, Kanagawa, Japan) with Al Kα radiation, and the binding energy was calibrated by the C1s peak (284.8 eV) of the contamination carbon.High resolution transmission electron microscopy (HRTEM) analysis was carried out using a Tecnai G 2 F-20 transmission electron microscope (FEI, OR, USA) with a field-emission gun operation at 200 kV.
The band gap and the light absorption properties of the samples were determined with a UVvis diffuse reflectance spectrum (U-3010, Hitachi Ltd., Lbarakiken, Japan ) with a 60 mm diameter integrating sphere using BaSO4 as the reflectance sample.Steady-state photoluminescence spectra (PL) spectra were measured by a Fluorolog3-21 (Horiba JobinYvon, NJ, USA) with the excitation light at 325 nm.

Photocatalytic Degradation and Hydrogen Evolution
Photodegradation of organic pollutants (phenol and MO) was conducted in an opening quartz chamber (150 mL) vertically irradiated by a 300 W high-pressure xenon lamp (PLS-SXE300, Beijing Perfect Light Co. Ltd., Beijing, China) located on the upper position.The irradiation area was about 20 cm 2 .The light density was measured using a radiometer (Photoelectric Instrument Factory, Beijing Normal University, Model UV-A, Beijing, China), and the results indicate that the light density at 365 nm and 400 nm was 34.7 mW/cm 2 and 32.5 mW/cm 2 , respectively.Reaction conditions included the following: a temperature of 25 °C, solution volume of 100 mL, C0 (phenol) of 400 μmol•L -1 ; C0 (MO) of 120 μmol•L -1 ; photocatalyst of 0.1 g•L -1 .Prior to the reaction, the suspension was stirred without irradiation for 20 minutes to achieve an adsorption equilibrium.Samples were withdrawn, centrifuged and analyzed using a U-3010 UV-vis spectrometer.
Photocatalytic hydrogen production was carried out in a Pyrex top-irradiation reaction vessel connected to closed glass gas system.10 mg catalyst dispersed in 120 mL aqueous solution containing TEOA (30 vol.%).The temperature of reaction solution was maintained at 0 °C.The resultant hydrogen was analyzed using an off-line gas chromatography (Bruker 450-GC, CA, USA) equipped with a thermal conductive detector (TCD), 5 Å molecular sieve column, and N2 as carrier gas.

Conclusions
In this work, p-TiO2 QDs@g-C3N4 p-n heterojunctions were fabricated by in-situ decorating titanium-defected TiO2 QDs on the surface of g-C3N4, in which TiO2 QDs bring up p-type conductivity and g-C3N4 affords for n-type conductivity.The as-prepared p-n heterojunction exhibits higher charge separation efficiency and photocatalytic performance in H2 evolution reaction and degradation of organic pollutant than pure g-C3N4 and TiO2/g-C3N4 type-II heterojunction under both UV-light and visible light irradiation, which can be ascribed to the synergy of a large electrical field over interface, a strong interface interaction, and the quantum confinement effect.In all the samples, PTC-40 with a p/n mass ratio of 0.15 exhibits the best photocatalytic performance.This work demonstrates that the construction of p-n heterojunction is an effective pathway to accelerate the electron-hole separation that is the key for a highly efficient photocatalyst.

Figure 9 .
Figure 9. Pseudo-first-order reaction rate in degradation of methyl orange (MO) and phenol under: (a) full solar spectrum and (b) visible light (λ > 400 nm).

Figure 10 .
Figure 10.(a) Time course of hydrogen evolution and (b) hydrogen generation rate of the samples.