A review of photocatalytic water purification with metal organic frameworks

This review analyzes the preparation and characterization of metal organic frameworks (MOFs) and their application as photocatalysts for water purification. The study begins by highlighting the problem of water scarcity and the different solutions for purification, including photocatalysis with semiconductors such as MOFs. It also describes the different methodologies that can be used for the synthesis of MOFs, paying attention to the purification and activation steps. The characterization of MOFs and the different approaches that can be followed to learn on the photocatalytic processes are also detailed. Finally, the work reviews literature focused on the degradation of contaminants from water using MOF-based photocatalysts under light irradiation.

The availability of quality water is a major problem in the current societies.Water needs have increased annually, from 1990s, almost 1% according to the continuous growth of the worldwide population, consumption patterns and economic development [1,2].It is noteworthy that this is a both hemispheres issue, affecting regions such as Southern Europe, Western South America, Southern Africa and countries like China or Mexico [3].By 2025, global water demand for the most water-intensive activities, agriculture and energy production, is expected to increase about 60% and 80%, respectively.Besides this, the world population prospects establish a population growth in the range of the 22-32% by 2050.
However, the surface water availability remains almost invariable and the quality of this water is being deteriorated because of the continuous release of chemicals to environment, mainly nutrients due to the intensification of the agricultural production [4][5][6].In this sense, pesticides such as herbicides, insecticides and fungicides are also well-known water pollutants [7].Moreover, the group of emerging contaminants (ECs) includes the wide range of personal care products, pharmaceuticals, cyanotoxins, steroids and hormones, plasticizers, caffeine, detergents, fragrances, etc. [6,8].ECs are compounds appeared in the last decades, detected in low concentrations in the water streams and without a proper regulation in most cases, resulting a risk for human health, environment and also economic activities [9,10].All those water pollutants can be introduced to the environment by multiple pathways, among which are industries disposal, hospital effluents, domestic wastewater, sewage treatment plants (STPs) and water treatment plants (WTPs) [11].For all previous reasons, international agreements as the United Nations 2030 Agenda for Sustainable Development establish specific targets for improving the water quality management.In this sense, wastewater treatment is a crucial step inside the water cycle.Further investigation for the improvement of the technologies for wastewater treatments may suppose a great deal of opportunities, especially in the new context of circular economy [6,12].
The treatment and purification of wastewater consist in the removal of the contaminants by the combination of physical, biological and/or chemical processes.In the case of physical methods, gravity as natural force (such as for sedimentation) or barriers such as membranes or filters are commonly used for separating and concentrating the pollutant.In this field, technologies like ultraor nanofiltration are able to remove macromolecules and biological matter, while inorganic ions can be separated by reverse osmosis.However, those processes are characterized by high power consumption, increasing operational costs [13].The biological treatment of wastewater mainly includes the use of biological activated sludge for promoting the biochemical degradation routes of the different pollutants.This technology presents lower operational costs compared to physical and chemical operations, but it also has larger time requirements.Furthermore, some of the aforementioned ECs may present bioaccumulation [14,15] and persistence or inhibitory effects over the bacterial microorganisms of the activated sludge [16], drastically reducing the effectivity of the biological process.Finally, chemical processes allow removing heavy metals by alkaline precipitation and disinfection by using UV radiation.Besides this, a family of high-power oxidant technologies, known as advanced oxidation processes (AOPs), have been deeply investigated in the last decades.These processes enable the degradation of refractory organic compounds by the in-situ generation of reactive oxygen species (ROS), mainly hydroxyl radicals ( • OH).AOPs can implement iron/H2O2 (Fenton processes), O3 (ozonation), electric power (electrochemical oxidation), UV or solar radiation (heterogeneous photocatalysis), or their combination [17,18].
Among AOPs used for water purification, heterogeneous photocatalysis highlights for the treatment of hazardous metal ions and the total abatement of organic pollutants [19][20][21][22][23].This technology has the advantages of using O2 as main reactive and the possibility of operating at mild conditions (ambient temperature and pressure).In heterogeneous photocatalysis, the ROS are generated after a charges separation caused by the irradiation of a semiconductor (photocatalyst) [24,25].The photocatalyst, as semiconductor material, is defined by two separated energy bands: the highest energy band with electrons (known as valence band, VB) and the lowest energy band without electrons (called conduction band, CB).The energetic barrier between aforementioned bands receives the name of band gap energy (Eg) [26].In this way, as represented in Figure 1, when a photocatalyst is irradiated and receives an energy equal or higher to its band gap energy, an electron (e -) is promoted from the valence band (generating a hole, h + , in the VB) to the conduction band.Immediately, these photogenerated charges can recombine, releasing the excitation energy as heat; or can migrate to the surface of the semiconductor and generate the ROS.In the latter case, hydroxyl radicals ( • OH) can be obtained by the oxidation of water molecules performed by the h + ; while superoxide radical anions (O2 •-) can be produced by the reduction of adsorbed oxygen.Moreover, superoxide radical anions can be further oxidized to hydroperoxyl radicals (HO2 •-) by protonation.These oxidant species, coupled to direct oxidation by h + , are able to mineralize the pollutant; this is, to perform the oxidation of the entire organic matter to CO2 and H2O.However, besides the recombination of the pair e -/h + , other reactions can reduce the effectivity of the global process: combination of HO2 •-, producing H2O2; or protonation of • OH, resulting in the formation of water [27][28][29].
The increasing attention paid in the research field of the photocatalysis for water purification has resulted in the design and development of a wide variety of photocatalysts and their modifications.Table 1 gathers some of the most investigated (and some other novel) semiconductor materials for the photocatalytic purification of wastewater.Thus, further investigation is necessary for outstanding the real behavior of these materials in diverse contexts: i.e., different water matrix or the degradation of emerging contaminants in real wastewaters.In addition to this, the stability of the material is a recurring issue.For example, metal sulfides might present low photochemical stability under irradiation, resulting in their dissolution; while corrosion in aqueous media is other major drawback for some semiconductor materials [30].This is not the case for titanium dioxide (TiO2), the most used and researched photocatalyst.TiO2 has been utilized for both air and water purification [31,32].This semiconductor is characterized by high activity in photocatalysis, besides high chemical stability and low biological toxicity [33,34].However, the use of TiO2 powder has the main disadvantages of low porosity, poor adsorption and the difficult management for its recovery.Moreover, the principal photocatalytic phase of TiO2, anatase, can be only activated by UV radiation due to its high band gap energy (3.2 eV, corresponding to  ≤ 387 nm).This fact supposes an important drawback inside the current trend of using solar energy (in which UV only represent the 5% of the total electromagnetic spectrum) for photocatalytic applications [29,35].For these reasons, TiO2 modifications, by means of morphological (e.g., supporting on activated carbon or graphene, immobilized over fibers, forming heterojunctions with other materials) and electronic (e.g., doping with heteroatoms, metal deposition, combination with other semiconductors, sensitization with dyes) approaches, have been frequent researching lines in photocatalysis.In any case, the synthesis of a TiO2-based photocatalyst for real wastewater purification using not only UV light (and using visible and solar light) is still a challenging frontier for the upcoming years.Simultaneously, during this last two decades, another type of materials has received special attention photocatalysis, regarding the broad range of possibilities that the interaction between metal clusters and organic linkers may present.This is the case of metal organic frameworks (MOFs), whose crystalline structure provides a robust and well-defined network and also a high development of the surface area [52].These characteristics, coupled with the wide number of different available linkers and metal clusters for their synthesis, allow obtaining semiconductor materials with redshifted absorption in the electromagnetic spectrum and suitable open porosity and very low framework density [53][54][55].In this sense, three different approaches will be suitable for obtaining MOFs with photocatalytic activity [30]: i) encapsulating chromophores in the internal structure (MOFs would act as a passive cage for reactions); ii) promoting e -/h + separation in the metal cluster (as it occurs in metal oxides); or iii) synthesizing MOFs using organic linkers with absorption bands displaced to the visible region in the spectrum, so promoted electrons can move to the metallic cluster, avoiding charges recombination.Therefore, the use of MOFs for the photocatalytic treatment of pollutants in water is an interesting strategy for water purification.The photodegradation of water contaminants with MOFs has been studied from the early 2000s [56], and it continues to nowadays [57].Since that, a wide range of chemical and structural modifications has been applied to enhance the photoresponse of MOFs.The aim of this work is to review the latest progress in the synthesis, characterization and application of MOFs for the photocatalytic purification of water.

Metal organic frameworks (MOFs)
Metal organic frameworks (MOFs) are a class of porous materials with modular structure.This allows a very wide structural diversity and the possibility of synthesizing materials with tailored properties for specific applications such as, gas storage, drug delivery, separation processes, catalysis, light harvesting and energy conversion, sensing and so on.MOFs are formed by the assembly of two components: cluster or metal ion nodes, also called secondary building units (SBUs), and organic linkers between the SBUs, usually given rise to crystalline structures with significant porous texture development [58].As example, Figure 2 represents the SBU (metal node) and organic linker used for the synthesis of two well-known MOFs, namely MOF-5 and HKUST-1.The combination of these structures results in a huge number of possibilities, and therefore of different MOFs with tailored properties.Figure 3 represents the different MOFs obtained using the same SBU and different organic linkers.As can be observed, diverse pore shapes can be obtained, depending on the linker.The organic linkers are generally polytopic linkers as carboxylates, phosphonates, sulphates, azole and heterocyclic compounds [60].Some of the most representative SBUs and organic linkers used for the formulation of MOFs are depicted in Figure 4.The first reference to metal organic frameworks was reported by Yaghi et al. [61] who synthesized MOF-5 in 1995.Since then, a large number of these materials have been analyzed in the literature and grouped under different denominations.For example, UIO-based MOFs, like UIO-66, are from Universitetet i Oslo, MIL are from Materials of Institute Lavoisier or ZIF-based MOFs referred to Zeolite Imidazolate Framework, among others.Figure 3. Different MOFs obtained using the same SBU and different organic linkers (reproduced from ref. [62]).
One of the most studied applications of MOFs is gas adsorption and storage due to their, in some cases, extremely high porosity, with surface areas higher than 6000 m 2 •g -1 .In the case of hydrogen storage, materials with low volume and with fast adsorption kinetics at relative low pressure and at ambient temperature are needed.Recent reviews [63,64] about hydrogen storage on MOFs have appeared since the first study reported by Rosi et al. in 2003 [65].CO2 capture and storage technology has been investigated to mitigate its effect as greenhouse gas [66,67].Methane storage, as main component of natural gas, has also been a relevant issue.In this sense, MOFs have been considered as promising candidates due to their high and tuneable porosity and easily immobilized functional sites [68].Not only gas storage, but also gas separation applications with MOFs have been widely studied in literature.In these sense, the adsorption of toxic gases, such as CO, NH3 or sulphur and nitrogen dioxides has been the main purpose in different studies [69,70].
Multifunctional MOF-based materials, such as magnetic sensors or low-dimensional magnetic materials can be included in the applications due to their magnetic properties of some MOFs.These properties are ferromagnetic, antiferromagnetic, ferrimagnetic, frustration and canting [63].Moreover, MOF luminosity has been developed with different designs by combining metal ions, organic linkers or guest molecules.Thus, sensing devices can be prepared for selective ion monitoring, stress-induced chemical detection, anisotropic photoluminescence probes and/or the presence of guest/solvent molecules [63].
By other side, development of a controllable drug delivery system is required to enhance the therapeutic efficacy.MOFs, compared to traditional porous materials, possess predominance of large surface areas, tunable pore size and shape, adjustable composition and functionalized pore surface, which enable them unique advantages for promising applications in adsorption and release of therapeutic agents [63,71].In this sense, the use of zirconium-based MOFs for drug delivery and biomedicine applications has been recently reviewed due to the their optimal stability towards hydrolysis and post-synthetic modifications with low toxicity [72].

Figure 4.
Inorganic secondary building units (A) and organic linkers (B) commonly used in MOF synthesis (reproduced with permission from ref. [73]).
Photocatalytic applications of MOFs have also been widely analysed due to their semiconductor properties [74].Many studies are focused on the photocatalytic degradation of organic pollutants, mainly dyes, and the photoreduction of heavy metals, both in water solutions.In these applications, it is crucial to assure the stability of MOF in water for large periods of time and wide pH ranges [75].Other pollutants coming from agricultural (pesticides, veterinary drugs), industrial (nitrobenzene) or municipal (personal care or pharmaceutical products) waste streams can be removed or degraded using MOFs [76].

Synthesis of MOFs.
Figure 5 summarizes the different approaches and synthesis conditions commonly used for MOF preparation reported in the literature [77].The conventional method is usually performed in liquid-phase by mixing organic ligands, metal SBU and a solvent for a certain time.The product of the reaction is filtered and dried by evaporation to obtain a purified MOF [78].The most used method for the synthesis of MOFs is hydrothermal/solvothermal synthesis via conventional electrical heating at controlled temperature.Generally, high-boiling organic solvents, such as dimethyl formamide, diethyl formamide, acetonitrile, acetone, ethanol or methanol, are used in solvothermal reactions.To avoid the problems related to the different solubility of the initial reagents, mixtures of solvents can be used.Solvothermal synthesis can be performed at different temperatures.At the lower temperatures, glass vials can be used, while at temperatures higher than 130 ºC the synthesis is generally performed in small volume Teflon-lined autoclaves [79].Hydrothermal synthesis of MOFs constitutes a more environmental friendly approach that substitutes the use of organic solvents for water [80].Nevertheless, these syntheses usually require long reaction times for an optimal crystallization, in order to accelerate the crystallization and obtain more uniform crystals with lower size, other alternative synthesis routes have been researched, such as microwave-assisted, electrochemical, sonochemical, mechanochemical and spray-drying synthesis.These methods try to synthesize MOFs in a shortened time and with higher quality.The choice of the solvent is crucial in liquid-phase reactions and is based on different characteristics as redox potential, reactivity, solubility or stability, among others.The nature of the solvent also determines the thermodynamic and activation energy of the reaction.Besides liquid-phase, some studies have focused on MOF synthesis by solid-state synthesis.
Figure 5. Different approaches and synthesis conditions commonly used for MOF preparation (reproduced from ref. [77]).
The slow evaporation synthesis does not need any external energy supply.However, the advantage of using room temperature results in significantly longer synthesis times than other methods.In this synthesis, the initial solution is progressively concentrated by the slow evaporation of the solvent.In some cases, the process uses a mixture of solvents to increase the solubility of the reagents and accelerate the process by the faster evaporation of low-boiling solvents [81].Microwave-assisted synthesis provides a very rapid method for the synthesis of MOFs [82,83].Besides to the lower synthesis times in relation with solvothermal method, microwave heating can also result in higher crystallinity, porous texture development, particle size reduction, and better morphology control.Microwave-assisted synthesis is based on the interaction between electromagnetic waves and mobile electric charges, such as polar solvent molecules or ions in the solution.In sonochemical synthesis the reagents undergo chemical change due to the application of intensive ultrasonic radiation (20 kHz-10 MHz).Ultrasound produces chemical and/or physical transformations by cavitation, which involves the formation and growth of small bubbles in the liquid phase.The collapse of these bubbles creates local hot spots of a short lifetime with high temperature and pressure, which generate homogeneous nucleation centres and reduce the crystallization time compared with conventional solvothermal methods [84][85][86].The mechanochemical method is based on mechanical agitation and collision between substances.It has advantage of a solvent-free procedure, resulting in less energy (because no heating is necessary), high efficiency and simple process [87,88].In liquid-assisted grinding (LAG), a small amount of solvent is added into a solid reaction mixture to facilitate the grinding [89].Electrochemical synthesis does not require metal salts in the solution and offers continuous production of MOFs, which constitutes a main advantage in an industrial process [90].Furthermore, this method allows the direct synthesis of thin films of MOFs over a surface at mild temperatures, reducing the effects of film cracking observed with other methods.The most studied electrosynthesis method is anodic dissolution, which uses an electrode as the source of metal ions.The electrode is located in a solution with the organic linker and often with an electrolyte.Upon applying an appropriate voltage or current, the metal dissolves and the metal ions required for the MOF formation are released near the electrode surface.The metal ions then immediately react with the linkers present in the solution and the MOF is formed close to the electrode surface.Thus, unlike the other synthesis methods, the metal ion is not supplied by a salt precursor but by the oxidation of the electrode.
Other methods, less analyzed, include spray-drying synthesis, diffusion methods or ionothermal synthesis.The spray-drying method consists in the atomization of a solution containing the MOF precursors into a spray of microdroplets using a two-fluid nozzle.The inner nozzle injects the solution and the outlet compresses gas.The droplets are therefore surrounded by the gas at a controlled temperature.The evaporation of the solvent increases the precursor concentrations at the surface, until the critical concentration for reaction is reached, and the crystallization begins [91,92].The diffusion methods can be divided into gas phase, liquid phase or gel diffusion.In these methods the reaction rate is controlled by the diffusion of one of the reagents.In gas phase diffusion, a volatile organic ligand solution is used as a solvent, while in liquid phase diffusion both metal ions and organic ligands are dissolved in immiscible solvents [93].To carry out the gel diffusion, the formation of MOF crystals comes from the mixture of the metal ions solution and the organic ligand disperse in a gel substance [94].The synthesis of MOFs by the diffusion method is often conducted under a mild reaction conditions, but it requires long reaction times.The ionothermal method uses an ionic liquid as structural template, charge balance group or reaction medium.Thereby, this method provides a pure ionic environment.The physicochemical properties of MOFs can be controlled by changing the composition of the ionic liquid.Employing an ionic liquid has benefits such as a good thermal stability, lower melting point and wider liquid range [95].
The synthesis of MOFs usually requires final steps of purification and/or activation.Purification consists in the removal of impurities, such as metal oxides, recrystallized linker or dense hybrid compounds, not occluded inside the pores.This can be carried out by sieving or based on the densities of the synthesized products.Nevertheless, most often impurities are removed by solvent treatment at elevated temperatures.Activation entails the removal of guest molecules from the pores.Various techniques are used to get the activation of MOFs, such as vacuum drying, solvent exchange or supercritical drying.In some cases, the heating of the MOF under vacuum can be enough to assure the activation.However, it also occurs that after vacuum drying lower surface areas than expected are obtained.This behaviour can be ascribed to the framework collapse due to the high surface tension and capillary forces produced by the liquid to gas-phase transformation of the trapped solvent molecules, especially if the solvent has a high boiling point and/or high surface tension.To avoid this problem the solvent can be exchanged with a lower boiling point/lower-surface tension solvent prior to heating under vacuum.For the exchange, the MOF should be soaked in the new solvent during enough time to assure the complete solvent exchange.The soaking time can be from a few hours to several days (nuclear magnetic resonance spectroscopy can be used to assure the complete solvent exchange).Afterwards, the MOF will be activated at a temperature above the boiling point of the new solvent but below the decomposition temperature of the framework.If conventional solvent exchange is unsuccessful, activation can be achieved by exchange with supercritical carbon dioxide (scCO2), which avoids the liquid to gas-phase transformation.Prior to use scCO2, the MOF should be exchanged with a solvent miscible with CO2, such as ethanol or methanol.With this last technique, activation is achieved even if the MOF has a quite breakable structure [96].A new technique has been recently reported to activate different MOFs with UV-vis lamp [97].The localized light-to-heat conversion produced in the MOF crystals upon irradiation enables a very fast solvent removal, thereby significantly reducing the activation time to 30 min and suppressing the need for time-consuming solvent exchange procedures and vacuum conditions.It is necessary to highlight that during all steps that are necessary for the purification and activation, the integrity of the framework must be verified, since high temperature can result in the collapse of the structure of the MOF or even in side chemical reactions that can alter the surface chemistry and properties of the final material.In order to know if the purification/activation steps are correctly performed, it is usually convenient to compare the experimental measured surface areas with those calculated by computational modelling or previously reported in other studies.If the experimental surface area is similar to the computationally derived, the activation procedure seems wellperformed.If the experimental area is significantly lower than the theoretical one, this is indicative of a collapse of the frameworks or an incomplete solvent removal.

Modification of MOFs
The performance of MOFs in different applications can be improved by modifying their chemical groups or other components.In the case of photocatalytic applications, some of the MOFs show relatively high band gap values and therefore, they can only harvest UV light, which limits their application.The different strategies to enhance photocatalytic activity of MOFs include: (i) Functionalization; (ii) Deposition of metal nanoparticles; (iii) Combination with semiconductors in different types of heterostructures, and (iv) Sensitization with dyes.
Functionalization of MOFs can be achieved by two different approaches.The first is based on the synthesis of the functionalized MOF using an organic linker containing the desired functional groups.This approach avoids the modification of an already synthesized MOF.However, this procedure has some limitations and might not be easily generalized because either the groups could interfere with the formation of the desired material or the properties (thermal stability, solubility) of the functionalized linker might not be compatible with the synthetic conditions.The more complex are the functions to be introduced, the more difficult is the synthesis by self-assembly because of their reactivity towards the metallic precursors [98].A clear example of this methodology is the inclusion of amine groups by replacing terephthalic acid by 2-aminoterephthalic acid as organic linker in the synthesis of MIL-125(Ti) MOF to obtain NH2-MIL-125(Ti).This change in the organic linker resulted in a much higher photocatalytic activity of the resulting MOF [99].The second functionalization approach is post-synthetic modification (PSM), consisting in the functionalization of a previously synthesized MOF.The main difficulty with post-synthetic modification is to not distort the structure of the starting material during the process.Different routes have been developed to access postfunctionalized MOFs based on different chemical interactions while keeping the same native structure [100].PSMs can be divided in four different categories as summarized in Figure 6, namely covalent PSM, which is produced by the covalent modification of the organic linker; dative PSM, involving the coordination of a metal centre to a linker with vacant coordination site; inorganic PSM, which is produced by the modification of the SBUs; and ionic PSM, as result of the exchange of a counter-ion in a cationic or anionic MOF.For covalent or dative PSM, the MOF normally needs to have a reactive group present on a linker.This group is often referred to as a 'tag', which is defined as a group or functionality that is stable and non-structure-defining during MOF formation, but that can be transformed by a post-synthetic modification [101].Different covalent transformations have been successfully carried out in the literature to modify preassembled MOFs.These transformations include varied chemical reactions, such as amide coupling, imine condensation, urea formation, salicylaldehyde condensation, N-alkylation, click reactions, bromination and protonation.Many of these transformation reactions have been implemented in amino-functionalized MOFs, due to the higher reactivity of the amino functional group.It should be mentioned that most PSM reactions involve the increase of the size and complexity of the functional groups into the pores.However, it is also possible to make this group smaller, simultaneously unmasking a protected functional group.This class of reactions has been termed post-synthetic deprotection (PSD) [103] and can achieved by thermolysis and photolysis reactions.Dative PSM reactions can be divided into two types: those in which the metal coordinates to a neutral site of the organic ligand, and those in which coordination occurs by the deprotonation of the ligand such as the conversion of hydroxyl groups into alkoxides (incorporating metal centres).Inorganic PSM can be included in a wider functionalization category, namely post-synthetic exchange (PSE), which includes the modification/substitution of the SBU (inorganic PSM) or of the organic linker.Inorganic PSM reactions include transmetalation at inorganic nodes, oxidation and reduction of the framework metal centres or substitution of metal centres.On the other hand, PSE by substitution of framework ligands includes solvent-assisted linker exchange (SALE) and solventassisted linker incorporation (SALI).Finally, ionic MOFs are those in which the framework has a cationic or anionic charge, with counter-ions present in the pores to balance these charges.Many ionic MOFs can undergo post-synthetic ion-exchange processes (ionic PSM) during which the cations or anions initially present in the pores are substituted for others.
There are other possible MOF transformations that can be viewed as post-synthetic modifications, including the formation of nanoparticles within the porosity of the MOF (deposition of metal nanoparticles).In recent years, metal nanoparticles (NPs) have gained popularity because of their application in heterogeneous catalysis.Different methods have been developed to load metals nanoparticles in MOFs, such as incipient wetness impregnation or double solvents method, based on the use of a hydrophilic and a hydrophobic solvent [104].Generally, these processes require the use of strong reducing agents like NaBH4 or H2, to obtain the desired metal NPs, which compromises the stability of the framework.Recently, photoreduction has been used for the reduction of the metal nanoparticles with promising results [105].
Dye-sensitization is considered a mature way of enhancing the visible light harvesting.In 1991, it appeared in a report to create a solar cell from dye-sensitized colloidal TiO2 films for first time [106].Since then, some studies have analysed the post-modification of MOFs by sensitization with dyes.For instance, sensitization of Pt@UiO-66 with Rhodamine B or UiO-66 with Erythrosin (ErB) enhanced the photocatalitic activity under visible-light for H2 production [107,108].Similarly, Qin and co-workers utilized a dye photosensitizer to get ZIF-67 as a co-catalyst for photochemical CO2 reduction [109].
Finally, combination of MOF with semiconductors can show great advantages compared with pure MOFs due to the synergetic effect.For example, MOF heterostructures combined with typical semiconductors (e.g., ZnO, TiO2 and graphene) have been demonstrated to exhibit exciting catalytic abilities, also with great changes in luminescence and adsorption properties.In the case of photocatalysis, the construction of heterostructures can reduce the recombination, improve light absorption and show better charge separation, as will be described in detail in Section 6.

Characterization of MOFs
The resulting MOFs prepared by different methodologies should be further characterized with diverse physicochemical techniques for determining their properties.From the point of view of water treatment by photocatalysis, it is also important to know its structural and textural properties, studying its homogeneity, while determining its electronic and light absorption properties and, of course, its stability in water.The techniques more useful for the characterization of MOFs are: Powder X-ray diffraction (PXRD) PXRD is widely used to determine the structural parameters and crystallinity of the MOFs.The structural identification can be performed by comparing the diffractogram of the synthesized MOF with a previous one reported in literature or a simulated pattern generated by single crystal X-ray and included in a database, or through the use of computational modeling [110].With this technique is possible to identify the crystalline structure, different polymorphic forms, distinguish between amorphous and crystalline material and estimate its crystallinity percentage.Once the crystalline structure of the MOF is identified, it is possible to determine the crystallographic parameters, such as unit cell size, lattice parameters, and crystallite size.The formers can be refined from diffraction data by different methodologies that assume a mathematical adjustment, such as the non-linear least squares method [111].Once the diffraction peaks are identified, the crystallite size is calculated using the Scherrer's equation usually with the most intense no-overlapped peak [112]: being D the crystallite size, K a size factor (values among 0.84-0.98depending on the equipment), β the full width at half maximum height of the peak (FWHM), and θ the Bragg angle for the peak identified in the diffraction pattern.
This characterization technique is extensively used by researchers working on MOFs because it allows understanding the crystallization of a MOF, but also serves to verify the creation of a new MOF or heterojunction or composite [113].In photocatalytic applications, the stability of the MOF is also determined by XRD technique.The used-MOF is recovered from the medium after reaction, washed and dried.Thus, its diffraction pattern is recorded and compared with the pristine MOF, checking the possible differences and thus determining if the structure of the MOF is stable [114].
Unlike X-ray diffraction, there are other techniques based on the absorption of X-rays that are less used in the characterization of MOFs, mainly because they require the use of complex synchrotron radiation installations.Extended X-ray absorption fine structure (EXAFS or XAFS) is an oscillatory modulation in the X-ray absorption coefficient on the high-energy side of an absorption edge, which analyses the types and numbers of atoms in the local environment of the absorbing atom and accurate absorber-neighbor distances [115].On the other hand, X-ray absorption near-edge structure (XANES) gives information about the energy band width, the valence state and the bond angles [116].

Nitrogen adsorption-desorption at -196 ºC
This technique is commonly used in MOFs characterization because it allows determining the textural parameters such as surface areas, pore volumes, average pore size and pore size distributions.This approach studies the N2 adsorption over the surface of a solid at the boiling temperature of liquid nitrogen, resulting in an adsorption isotherm.The shape of the isotherm provides information about the homogeneity of the solid [117].In 1985, the International Union of Pure and Applied Chemistry (IUPAC) classified the physisorption isotherms into six types [118].However, Thommes et al. [119] refined the original IUPAC classifications of physisorption isotherms, where Type I and IV isotherm were divided in I(a), I(b), IV(a) and IV(b), respectively.The same happens with the types of hysteresis loops.IUPAC classification identified four different loops and Thommes et al. [119] recently found two more types, resulting in six types of hysteresis loops related to the underlying adsorption mechanism and pore structure.To get useful information, the MOF must be properly vacuum drying and heating before N2 adsorption/desorption isotherm.However, in some cases, this pre-treatment reduces the surface areas due to framework collapse [110,120].This collapse could often be related to the capillary forces and the high surface stress that occurred in the interphase between the gas and the confined molecules of the solvent [121].
In general, MOFs are solids with high surface areas (>2000 m 2 •g -1 ) and porosity, being the majority microporous materials describing type I isotherms.The most common approach used to calculate the surface area of MOFs is the Brunauer-Emmett-Teller (BET) method [122], which permits the comparison with other porous materials.However, special attention must be paid with highly porous 3D MOF frameworks, since the BET model was designed for flat surfaces and may not correctly describe the MOFs adsorption data [123].The presence of microporous is usually determined by the t-plot method, which compares the adsorption isotherm data of a porous sample and of a nonporous material [124].Analogous to the BET modelling, the pore volume and pore size distribution can be extracted from the N2 adsorption isotherm, although it must be cautious when using the mathematical models.The density functional theory, commonly named DFT model [125], is widely used for analyzing the pore size distributions of MOFs in the range of meso-and micropores, while Barrett-Joyner-Halenda (BJH) method is only used for mesopores and Horwath-Kawazoe (HK) for micropores [124,126].Of course, the accurate fit of the experimental data depends on the available equipment, mainly for the micropores analysis that requires adsorption data at very low relative pressures, and the porosity of MOFs.For instance, if the studied MOF has flexible pores or they are randomly ordered, the DFT approach is questionable because it assumes that the pores are rigid and of a well-defined shape [127].
Ultraviolet-visible diffuse reflectance spectroscopy (UV-vis DRS) UV-vis DRS is frequently used in the characterization of photocatalysts because provides information about the optical properties and allows knowing the wavelength range in which the semiconductor absorb the light.By this technique, an absorption spectrum is recorded in the UVvisible wavelength range, usually from 190 to 900 nm, appearing the absorption band.MOFs are a very interesting type of semiconductor because depending on its composition, they can behave as an inorganic semiconductor, organic or both.When an inorganic semiconductor is excited by light with enough energy, the electrons are able to move from the valance band (VB) to the conduction band (CB), leaving a hole in the VB.The mechanism follows by organic semiconductors are very similar, but the electronic transitions are among the highest occupied molecular orbital (HOMO) and the lowest unoccupied molecular orbital (LUMO) of an organic compound.Since MOFs are organometallic compounds constitutes of metal oxo-clusters and organic linkers, when they are excited by light of an appropriate energy, the e -transitions can occur between the VB and CB of the metal oxo-cluster and/or between the HOMO and LUMO of the organic linker [128].Thus, the absorption spectrum can be formed by several bands depending on which constituent promotes electronic transitions.An interesting example of the UV-vis characterization was reported by Horiuchi et al. [129] comparing the light absorption of MIL-125 and NH2-MIL-125.MIL-125 showed an absorption band below 350 nm, due to the e -transitions in the Ti-oxo-cluster, while the NH2-MIL-125 showed a broad band up to 500 nm with two peaks, associated to electronic transitions in both the Ti-oxo-clusters and the NH2-linkers.
UV-vis DRS is also a useful tool to determine the band gap energy (Eg) of a semiconductor.For this purpose, the Tauc Plot approximation is usually employed [130,131].This model determines the Eg by the equation: where α, h, ν, Eg, and A are the absorption coefficient, Planck constant, radiation frequency, band gap and a constant, respectively.The value of n depends on the semiconductor type, being ½ for direct semiconductors and 2 for indirect ones.From this equation, it is possible to build a plot of (αhv) 1/n vs hv, called Tauc Plot [130].For a direct band gap semiconductor, the plot with n = 1/2 shows a linear Tauc region just above the optical absorption edge, while indirect band gap materials show the Tauc region on the n = 2 plot.Extrapolation of this line to the photon energy axis yields the semiconductor band gap-a key indicator of its light harvesting efficiency under solar illumination.Figure 7 depictes an example of the UV-vis absorption spectra and the respective Tauc plots for a variety of modified-MIL-125(Ti) MOFs [132].It can be seen that these MOFs have an absorption band up to 460 nm, shifting the absorption to the visible region and yielding direct semiconductors with band gap values close to 2.85 eV.These values are lower than the characteristic band gap of TiO2 semiconductor (3.2 eV) usually used in photocatalytic applications.

Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) SEM technique is routinely used for MOFs characterization. It generates high-resolution 2D
images that display the shape of the material and its spatial variations, revealing information about the external morphology, dispersion, and mixture of phases.The porous structure that characterizes MOFs gives rise to particles of curious shapes, such as cubes, bars, rhombohedra, and so on, yielding a varied morphology (see an example in Figure 8).Depending on the SEM equipment used and the insulating nature of some MOFs, the SEM characterization can require a previous pretreatment by coating the surface with a conductive material, usually gold [123].To avoid this drawback, researchers have access to Field Emission Scanning Electron Microscope (FESEM).This equipment works with a field emission gun that provides extremely focused electron beams, which enhances the spatial resolution working at low potentials.This characteristic reduces the charging effect on insulating materials and, even, avoid the damage that the electron beam can induce in some sensitive MOFs.On the other hand, TEM has been widely applied to determine the grain size, particle size, and crystallographic data, such as plane indices and dislocations.Different software programs can be used to analyze the microscopy images (e.g.ImageJ, Cell Profiler).With those tools, it is possible to determine the particle size, measuring different particles and creating a histogram, and the spacing between crystallographic planes.This technique is very useful for the characterization of MOFs modified by the incorporation of nanoparticles (NPs), because the collected images provides data about the size and dispersion of those NPs [133].These microscopies can be coupled with Energy Dispersive Spectroscopy (EDS) or Energy Dispersive X-ray Analysis (EDX or EDAX) that allows determining the elemental quantitative and qualitative composition of MOF.As an example, Gao et al. [134] synthesized Fe-MOFs that were characterized by Field Emission SEM (FE-SEM) and Highresolution TEM (HRTEM), observing uniform spindle-like shape and an uniform microstructure and lattice structure (Figure 8).The chemical composition was studied by EDX yielding mapping results of each element that allows knowing the homogeneity of the synthesized MOF.
Thermogravimetric Analysis (TGA) TGA measures the mass loss of a material as a function of temperature in a controlled atmosphere.This technique is useful to determine the thermal stability of the MOF and to estimate its solvent-accessible pore volume.The MOF decomposition varies depending of the carrier gas (N2, air or O2) used for the TGA.In a common study, the TGA curve represents the weight loss of the MOF (%) versus temperature.This plot usually depicts a first loss of mass in the 40-110 ºC range that corresponds to the removal of the solvent molecules, and a second loss between 300-600 ºC that is usually assumed to the structural modification of the MOF framework, yielding the corresponding metal-oxides.It must be borne in mind that this weight loss does not have to be due to a structural change, so it is necessary to complement this study with an analysis by XRD at variable temperature to check the change of structure [123].

Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES)
ICP-OES is an elemental analysis technique that uses the emission spectra of a sample to identify, and quantify the present elements [135].ICP-OES can detect most elements at very low concentrations, so it is used to know the purity of the MOFs and the relationship between the elements that form it [123].However, this technique requires that the sample be digested (dissolved) prior to analysis.The complete dissolution of MOFs is not always so easy, requiring treatments with HNO3, H2SO4 followed by H2O2 or even HF digestions.These procedures difficult the ICP-OES analysis, because it is necessary to ensure that the dissolution is complete [123].Due to this inconvenience, other technologies are sought that allow knowing the elementary analysis.Wavelength Dispersive X-ray Fluorescence (WDXRF), for instance, is a novel technique used for elemental analysis applications.In WDXRF, all elements are excited simultaneously yielding each one a characteristic radiation emission that is detected by a detector.This technique can be used directly in solid materials, avoiding the complex dissolution of the solid required by ICP-OES.

Aqueous Stability Testing
MOFs must be stable in aqueous solution to efficiently carry out the photocatalytic reactions for water purification; hence it has a significant importance testing the aqueous stability of these materials.Usually, MOFs have basic or acidic functional groups on their structure, so it has to be measured the pH of the water before adding the MOF and after it is removed.Even, it can be interested to determine the zeta potential of the MOF, which corresponds to the surface charge at the interface between the MOF surface and the water medium.A simple way to assess the stability in water of MOFs is to expose the material to an aqueous solution at known pH.Then, after a certain time, the MOF is filtered, washed and dried.The stability yield can be known by comparing the mass recovered with the initial mass [123].However, this comparison requires first a control of the structure and porosity, measuring the XRD and the N2 adsorption isotherm before and after water testing.Another option for understanding the aqueous stability is to measure the water adsorption isotherms by introducing a set partial pressure of water vapor into the MOF under vacuum [114].As stated before, the majority of MOFs are microporous materials, which gas adsorption followed the expected type I isotherm.The shape of the respective adsorption isotherm provided details on the strength and type of interaction between the water molecule and the MOF surface.These analyses must be accompanied by XRD characterization.Thus, although most MOFs display water adsorption isotherms similar to those reported by other porous materials (e.g.zeolites or carbon materials), there are several MOFs that exhibit an interesting adsorption behavior as a consequence of their framework flexibility.MOFs of type MIL-53 are a clear example of this behavior, in which the water adsorption produces a reversible structural transition from its large pore form to its narrow pore form, accompanying by a large reduction in their pore volume [114].Nonetheless, for those applications in which MOFs must be used in aqueous phase, the best way to check the MOF stability is by immersion and stirring under the specific aqueous conditions followed by the XRD, BET and mass loss analysis after sample filtration.
Photoluminescence (PL) Spectroscopy PL provides information about the electronic properties of semiconductors.In this spectroscopy, the material is directly excited by a light proceeding from a xenon lamp.The material absorbed the radiation, but the excess energy not adsorbed is dissipated by the material through the emission of light, known as photoluminescence.The energy emitted as light in semiconductors is related to the band gap energy, i.e. the energetic difference between the CB and VB, but also with the presence of localized defect levels.In this way, photoluminescence supplies information about oxygen vacancies, structural defects, and recombination of photogenerated charges.It is noteworthy that the intensity of the spectrum gives information about the number of recombination centers present in the MOF.Higher photocurrent response usually indicates a more efficient separation of the photogenerated charges and longer lifetime of the charge carriers [136].As an example, Sofi et al. [137] studies the photoluminescence response of pristine HKUST-1 and Ag/Ag3PO4/HKUST-1 heterostructure to investigate the recombination of photogenerated charge carriers.Authors attributed the decreasing of the intensity in the heterostructure to the reduction of the electron-hole recombination due to the effective separation of photoinduced charge carriers.Thus, highlights that this technique together with the UV-vis characterization are very useful to understand the photocatalytic activity of the MOFs.

Photocatalytic reactors
There are many diverse and heterogeneous configurations of photocatalytic reactors devoted to water treatment processes.The most common classification divides photocatalytic reactors into (i) reactors with the photocatalyst suspended in the solution, and (ii) those with the photocatalyst immobilized on a fixed support [27,138].The former one needs an additional separation step for the recovery and recirculation of the photocatalysts' particles.In contrast, the latter allows operating in a real continuous mode.The literature contains many different photocatalytic reactor configurations that could be sorted by this classification.

Slurry reactors
Slurry reactors have been widely employed in many studies probably due to their simplicity of use.Furthermore, this configuration is valid for all the types of light sources, i.e.UV, visible or solar.In these reactors, the solid photocatalyst is suspended in the aqueous solution by air bubbling or mechanical stirring.They can be externally irradiated or include submerged lamps and can operate in batch or continuous mode.Besides to their simplicity, this type of reactor has other remarkable advantages including a very high exposed surface area of photocatalyst and low mass-transfer limitations.In contrast their main disadvantages are the problems of light penetration due to the opacity and the recovery of the fine powder photocatalysts from the liquid phase.The powder photocatalysts can be separated using filtration systems or settling tanks, which allow a continuous operation mode.

Photocatalytic membrane reactor (PMR)
Photocatalytic membrane reactors combine in a single set up the photocatalytic reactor and the filtration stage [139].A membrane is used with two different purposes, to serve as photocatalyst support forming an active photocatalytic layer and/or to be used for separation and recirculation of the photocatalytic particles [140].In the case of the immobilization of the photocatalysts on the membrane, the irradiated surface area is very considerably reduced and the regeneration of the photocatalysts implies the replacement of the whole membrane [141].To overcome these disadvantages, slurry PMRs can be used.In these reactors, the photocatalysts particles are suspended in the aqueous phase, like in slurry reactors, and the membrane is used for the recovery/confinement of the photocatalysts particles [142,143].

Annular Photoreactor
In annular photoreactors water solution is confined between two concentric cylinders.Usually, the inner cylinder accommodates the light lamp, which is refrigerated with flowing air, although these reactors could be also externally irradiated [144].This configuration provides a symmetrical irradiation and allows multiple possibilities for the positioning of the photocatalyst particles.The photocatalysts could be suspended in the solution, like in slurry reactors, or immobilized on supports located in the space between both cylinders or in the internal wall of the external cylinder.
Many other reactor configurations are described in the technical literature, including microreactors, rotating annular reactors, closed-loop reactors, among many others [27,145,146].It is also worth-mentioning the utilization of photoreactors with parabolic deflectors to enhance the incidence of light and increase the photocatalytic activity, especially in solar photocatalytic applications [147].

Parameters affecting the photocatalytic behavior
Besides to the reactor configuration, the photocatalytic activity is highly dependent on the different operational parameters.The effect of some of these parameters on the photocatalytic degradation are briefly discussed below.

Photocatalyst loading
Usually, the increment of the amount of photocatalysts results in an increase of the photocatalytic activity, more or less accentuated depending on the reactor configuration and reaction conditions.This is due to the higher light absorption and therefore to the higher generation of the reactive radicals responsible of the degradation of the pollutants.However, there is a saturation effect and beyond this point it is observed a decrease of the photocatalytic with increasing photocatalysis loading.This behavior is usually attributed to the light blocking produced by the increase of the turbidity of the water due to the high number of suspended particles of the photocatalyst.pH pH is one of the most decisive parameters affecting the overall behavior of the photocatalytic reaction.pH affects not only the surface charge of the photocatalytic particles, but also their selfaggregation.The analysis of the pH impact is usually performed based on the pH of point of zero charge (pHPZC) of the photocatalyst.So that, at pH values near pHPZC, the interaction between the solved pollutants and the photocatalyst's surface is very little due to the absence of significant electrostatic forces.However, when the pH of the solution is lower than pHPZC, the photocatalyst surface becomes positively charged and therefore it exerted an electrostatic attraction towards negatively charged compounds.This can intensify the adsorption on the photocatalyst and consequently increase the possibility of degradation of the pollutant.Finally, if the pH is higher than the pHPZC, the surface of the photocatalyst will be charged negatively and therefore it repulses anion compounds.
Besides to the electrostatic effect between the surface of the photocatalyst and the dissolved pollutants, pH can also affect significantly the interaction between the particles of the photocatalysts themselves.At pH values near the pHPZC of the photocatalyst, aggregation of the photocatalyst particles is observed resulting in photocatalyst sedimentation [148].

Temperature
The effect of the temperature on the photocatalytic activity in water purification processes has been extensively analyzed in the literature.It is generally accepted that the increase of the reaction temperature favors the recombination of charges and disfavor the adsorption of the pollutants on the surface on the photocatalysts [149].Furthermore, the increase of the reaction temperature can also result in a decrease of the oxygen adsorbed, with a detrimental effect in the photocatalytic activity as explained below.

Dissolved oxygen
Dissolved oxygen plays a crucial role in the framework of photocatalytic degradation of pollutants in water.Oxygen is involved in the generation of reactive oxygen species (ROS), which are the main responsible of the pollutant degradation by oxidation reactions.Furthermore, dissolved oxygen also guarantees enough electron scavengers to avoid recombination effects, stabilize radical intermediates and is directly involved in some of the intermediate photocatalytic reactions [150].The amount of dissolved oxygen can be approximated by the Henry's Law at the reaction conditions.The increment of the temperature of the aqueous medium produces a reduction of the dissolved oxygen concentration.

Contaminant initial concentration
The initial concentration of the contaminant has also significant effect on the kinetics of the photocatalytic degradation reaction.A significant increase in the contaminant concentration results in slower photodegradation rates mainly due to (i) the surface of the photocatalyst can be saturated by the adsorbed molecules of the contaminant and (ii) a decrease of the photonic efficiency [151].

Light wavelength
The light wavelength can show a very significant effect on the photocatalytic degradation depending on the photocatalyst characteristics.Nowadays, the studies can be classified according to the light wavelength in UV, visible or solar irradiation.The band gap value of the photocatalyst allows estimating the wavelength of the irradiated light that can activate it.For instance, TiO2 in anatase phase has a band gap value of around 3.2 eV, and it can be activated with a light wavelength of λ < 380 nm.In contrast, other semiconductor with lower band gaps, such as some types of MOFs, can be activated with lights of higher wavelengths, including visible or solar radiation that cover a wide range of wavelengths.

Light intensity
In water applications, it is generally accepted that relatively high light intensity values are needed to obtain a proper photocatalytic reaction rate.This is due to the needing of a minimum number of photons to activate the surface of the photocatalyst.Initial studies confirmed a linear relationship between contaminant conversion and incident radiant lux [152].However, later it was demonstrated a different relation between reaction rate and light intensity changes.With increasing light intensity, the linear dependency between reaction rate and radiant flux changes from linear (r = k•Ф) to a square root (r = k•Ф 0.5 ) and finally to zero order (r = k).This behavior can be explained by the saturation of the photocatalyst surface.

Kinetics and modelling
Most of the studies reported in the literature fitted their experimental results to simplified Langmuir-Hinshelwood models.The kinetic mechanisms should consider the contaminant and the oxygen molecules.However, oxygen is usually in great excess in the reaction media and therefore its concentration can be considered constant during the whole reaction.The photocatalytic reaction can be described by a first-order reaction following the expression: where r is the reaction rate, Cads(t) is the amount of contaminant adsorbed on the photocatalyst at time t and k is the rate constant.Considering that the adsorption-desorption equilibrium follows a Langmuir isotherm, the previous equation can be written as: being KL the Langmuir constant and C(t) the concentration of the contaminant in the solution at time t.Generally, photocatalytic degradations are performed with low concentrations of the contaminant, therefore KL•C(t) << 1, and the equation can be simplified to: where kapp is the product of k and KL known as apparent rate constant.The integration of this equation between 0 and t, results in: being C0 and Ct the contaminant concentrations in the solution at times 0 and t, respectively.The representation of ln(C0/Ct) versus reaction time, t, allows obtaining the value of the apparent rate constant from the slope of the line adjusting the experimental data.

Water purification by photocatalysis using MOFs
Their outstanding properties and their versatility make MOFs ideal candidates for photocatalytic applications.One hot topic in photocatalysis is water purification to remove diverse pollutants, including heavy metals, nitrates, priority pollutants or emerging pollutants, and inactivate different pathogens.The use of MOFs in this application is subject to their photochemical response but also to their stability in water.They must maintain their structural and textural properties at the same time as their photocatalytic activity after successive uses.The literature reports several strategies to develop photoactive materials based on MOFs, which have been classified in three groups depending on the photocatalytic mechanism and can be seen in Figure 9 [153][154][155].The first approach exploits the semiconductor dots properties of the metal clusters, which act as dispersed nanosemiconductors isolated by the organic linkers.This approach results in type I MOFs that can be more efficient than conventional semiconductors because: i) their high porosity, that favors the presence of the pollutant close to the semiconductor dots and the photogenerated charges; ii) their high density of photoactive dots; iii) the organic linker can also absorb light, acting as antennae and thus increasing the photoresponse of the catalyst [153].Type II MOFs are synthesized using organic linkers with photoresponse, such as dye-based linkers, that are separated by the metal clusters.The linkers act as antennas absorbing the light and transferring the photogenerated charges to the metal clusters, described as linker-metal cluster charge-transfer mechanism (LCCT) [128].Finally, type III MOFs is the simplest approach in which the MOFs are used as a porous matrix and the photoactive species are encapsulated within its porous structure.While the promising photochemical properties of MOFs were described from the end of nineteens, their application in water purification began a decade later.The main drawback of these materials was their stability in water.As an example, Alvaro et al. [156] reported in 2007 the photodegradation of phenol in water using the MOF-5, but its instability was further reported by Hausdorf et al. [157] who observed its structural modification depended of the water environment.It was not until 2013 when Laurier et al. [158] described the photocatalytic activity of several Fe-MOFs (MIL-88B, MIL-100 and MIL-101, all based on Fe3-μ3-oxo clusters) for the degradation of Rhodamine 6G under visible light (550 nm).Although the dye degradation was not complete, these MOFs were more active than the conventional TiO2 and their crystallinity was reasonably maintained after reaction.Since then, several works have been published regarding the use of MOFs in water treatment.Among the most studied MOFs stand out ZIF-8, UiO-66(Zr) and MIL-125(Ti) [159], whose photocatalytic mechanism corresponds to type II, and MIL-101, MIL-53 and MIL-88B (all Fe-based type I MOFs) in which the light is used by the Fe-O cluster so as the photogenerated electron is transferred to Fe 3+ from O 2- [128,160].Moreover, the literature shows additional strategies to promote the photocatalytic activity of MOFs in order to enlarge their visible light absorption, thus favoring their behavior under solar light.
One approach consists in functionalizing the organic linker to shift its photoresponse to higher wavelengths.Shi et al. [161] synthesized several amine-functionalized Fe-MOFs (NH2-MIL-88B, NH2-MIL-53 and NH2-MIL-101) with high stability and activity for the photoreduction of Cr(VI) in water under visible light.Authors concluded that the incorporation of an amine group in the organic linker enhanced the activity of the MOFs because both the NH2-linker and the Fe-cluster were excited under visible light.Authors proposed a mechanism based on a dual excitation, shown in Figure 10, that promotes the electron transfer and reduces the recombination of charges.Other strategy used in the design of more efficient photocatalysts is to support metal nanoparticles on MOFs.A recent example was reported by Liang et al. [162].Authors loaded Pd NPs on MIL-100(Fe) leading to active photocatalysts for the photodegradation under visible light of three PPCPs (Pharmaceuticals and Personal Care Products), theophylline, ibuprofen and bisphenol A. It was concluded that Pd NPs minimized the recombination of photogenerated electron-hole pairs, improving the photocatalytic performance.Another effective plan of action is to combine MOFs with other semiconductors achieving interesting and promising heterojunctions.In this approach the porous network of the MOF can favor the dispersion of the other semiconductor, yielding to more active centers [128].For instance, Mosleh and Rahimi [163] analyzed recently the photodegradation of abamectin pesticide using Cu2(OH)PO4-HKUST-1 through the sonophotocatalytic technique.The MOF showed a band gap value of 2.59 eV and an almost complete degradation of the pesticide.A great development has been performed on synthesizing MOFs and modifying MOFs, using the methodologies described in Section 3, in order to look for a next generation of photocatalysts more active and stable.Since literature summarized a certain diversity of MOFs for water treatment by photocatalysis, the following subsections have been stablished paying particular attention to the nature of the pollutant, mainly dyes, heavy metals, priority and emerging pollutants.Moreover, since the research in photocatalysis tends to the use of solar light as energy source, we have focused the attention on those works that use visible and solar light for water treatment, leaving in the background the previous works dedicated to the use of UV radiation.Finally, a subsection has been included in which stability and recyclability of these promising photocatalysts are studied.

Photodegradation of dyes
Dye effluents are usually discharged from different industries such as textile, rubber, paper, leather, plastics, cosmetic and printing.Their presence in water is responsible of important damages to aquatic organisms and humans by mutagenic and carcinogenic effects.Most of dyes are stable and non-biodegradable due to their chemical structure characterized by a large aromatic degree.Thus, their removal by conventional biological technologies turns out inefficient.In this scenario, photocatalysis appeared as a promising technology for the removal of organic dyes from wastewater.Moreover, numerous MOFs have been tested as photocatalysts for the degradation of dyes, which has been summarized in several reviews [164][165][166][167][168].However, most of articles are just focused on the removal of commercial dyes in synthetic waters instead of real dyestuffs water.Methylene blue (MB), Methyl orange (MO) and Rhodamine B (RhB) have been with difference the most used dyes as target pollutants, mainly because they are easy to analyze.Many examples can be found in the review reported by Wu et al. [164] where it stands out that around 60% of the articles used UV light, while 30% used visible irradiation and only 5% utilized sunlight as energy source.This issue is mainly due to the lower conversion rates achieved by pure MOFs when using solar light, even in some cases additional oxidant (such as H2O2 or persulfate) is needed to favor the degradation rate.Table 2 appointed some relevant examples of pure MOFs used for dyes degradation classified according to the type of radiation employed.Table 2. Relevant examples of MOFs for dyes degradation, along with the dye target and the light used. 1 R6G= rhodamine 6G; AO7= acid orange 7; CR= congo red; EBT= eriochrome black T; MG= malachite green.

MOFs
Among MOFs used under UV light stands out several Cd(II)-imidazole MOFs reported by Liu et al. [170].Their study for the MB and MO degradation demonstrated that the Cd(II) complexes formed with the linkers were excited by UV light, generating the photogenerated charges required for dyes degradation.In a posterior work, Zhang et al. [171] tested other Cd(II)-imidazole MOFs for MO degradation and demonstrated that the adequate band gap was not the only factor that controlled the activity, had to take into account other factors such as its efficiency in the transference and separation of charges.Zn(II)-imidazolate MOF, named ZIF-8, also revealed a high activity for the MB degradation under UV light due to the excitation of the Zn-complexes [172].Regarding the types of MOFs described before, it has been reported that the ligand of Ag(I)-tetrazole MOFs was relevant in the design of active photocatalysts for the R6G degradation [173].Using ligands with more delocalized  electrons (such as ethylenediamine and 5,5'-tetrazolate) favored the linker-metal cluster charge-transfer mechanism (LCCT) resulting in higher degradation rates.
Nevertheless, it is noteworthy that the technological application of photocatalysis tends to the use of solar light as energy source.For this reason, many researchers are currently working on the design of MOFs with the aim to enhance their activity under visible light.Different Fe-based MOFs have been tested for the photodegradation of dyes under visible light [186].Among them, MIL-88B (based on terephtalate linkers) showed higher activity for the R6G degradation than others MIL-100 and MIL-101 MOFs, which was associated to the visible light absorption of the Fe-oxo-clusters that formed the structure (being a type-I MOF) [158].However, regarding the degradation rates, none of these Fe-based MOFs achieved full conversion values of the dye.Similar behavior has been reported by different authors when MIL-53 was used as photocatalyst under visible light.Although it absorbed the light in the visible region because its low band gap, it only managed to degrade 40% of RhB after 6 h of reaction [176] and only 3% of MB after 1 h [177].Something similar occurred using MIL-88A as photocatalyst.The degradation of MB only achieved 40% of conversion, requiring the incorporation of H2O2 as oxidant to achieve 100% conversion [178].
Since titanium dioxide is by far the most used photocatalyst, several researchers have focused on the preparation of Ti-MOFs.NTU-99 has been described as an efficient catalyst, achieving complete degradation of RhB and MB in short times (20-80 min) and maintaining its activity after successive reaction cycles [179].Although MIL-125 showed activity for other photocatalytic applications (CO2 transformation and/or water splitting) its effectiveness in water purification is not so interesting [167,187,188].For instance, under UV light the MB conversion reached was 96% after 6 h, but it should be noted that only by adsorption 90% of MB was removed from the solution (without light), so its photocatalytic activity is quite low [175].More interesting is the design of MOFs with activity under solar light.In this sense, UiO-66(Ti) was successfully synthesized from UiO-66(Zr) MOF, reaching more than 80% of MB degradation under simulated sunlight [185].Its activity was related to the light absorption by the tianium-oxo-clusters, which results in the generation of superoxide and hydroxyl radicals able to oxidize the dye.
The choice of adequate metal clusters is an important issue during the design of active MOFs.It has been described that the d-d spin allowed transition proper of some metals can shift the absorption of the MOF to the visible region.Nevertheless, the ligands also play an important role in the photocatalytic activity for dyes degradation [165].N,O-donor and N-containing ligands are often selected for the synthesis of stable and functional MOFs.Using N,O-donor ligands results in the formation of chromophore blocks that provide - transitions by light absorption.This property induces the shift of the absorption band to higher wavelengths, allowing taking more advantage of the radiation for the degradation of dyes [180].N-donor ligands are selected because they have lone electron pairs in their structure that can be faster transferred to the metal clusters [181].Based on these N-ligands, it has been studied the modification of known MOFs by introducing -NH2 in the ligand [99,159,165].Its incorporation usually results in the reduction of the band gap, extending the light absorption to the visible region.This behavior is ascribed to the conjugated  electron transition from the amine-ligand to the metal-clusters.Nevertheless, in some cases, although the NH2-MOFs had narrow band gaps, their photocatalytic activity did not stand out.In different works it has been concluded that it is not only important to generate electrons and holes, but to keep them separate avoiding the recombination [158,189].
As has been said so far, the activity of MOFs in terms of dye conversion values is quite limited, mainly for their application under solar light.In addition, the stability of these MOFs in aqueous solutions is also an important drawback.For these reasons, different modifications are currently under study with a double aim to enhance the activity under solar light (achieving higher conversion rates) and the stability in aqueous solutions.Although in the literature there is a wide range of examples, this review focuses the attention on those modifications designed for the use of solar radiation.These modifications are similar to those made over other semiconductors that can be divided in: metal doping, metal nanoparticles decoration and combination with free-metal semiconductors [159,164,165].The following subsections collect information on this.

Metal doping
The partial substitution of metal center of MOFs can enhance the photocatalytic activity under visible light, similar to what happens with other semiconductors [190].The substitution of the pristine metal by other one yields the introduction of new energy levels resulting in metal-to-metal charge transfers.These new assemblies are expected to improve the photocatalytic activity of the pristine MOF.Wang et al. [185] demonstrated that the replacement of Zr by Ti in UiO-66 was an effective way to increase the MB conversion rate under solar light.The Ti incorporation narrows the band gap of UiO-66 and enhances the absorption properties, attributed mainly to the electron donor properties of Ti.Other interesting example was reported by Li et al. [191] by the susbtituion of Zn by Ni in ZIF-8, resulting in a new MOF denoted as BIT-11.This MOF achieved the complete disappearance of MB in less than 30 min under visible light.This behavior was adscribed to the photogenerated electrons of Ni atoms that have a variable valence.This MOF is also interesting because its structure changes slightly in water.Water molecules induced a chemical de-coordination resulting in an stable fourcoordinated Ni clusters denoted as BIT-11b.
The NH2-MIL-125 has been also modified by metal doping to enhance the MB photodegradation under simulated sunlight [192].Cr (III) and Ag(I) were used as dopants resulting in doped-MOFs that reached the total degradation of MB.Chromium was able to induce the formation of structural defects at the same time that incorporates new energy levels where the photogenerated electrons can migrate.By other side, silver atoms can act as electrons traps reducing the recombination processes and herby enhancing the photocatalytic activity.It is also noteworthy the stability of Ag-MIL-125 which maintained its activity even after five cycles of use.

Metal nanoparticles decoration
Different researchers have demonstrated that the incorporation of noble metal nanoparticles over the surface of the MOF improved its photocatalytic performance [159,165].Nevertheless, most of those works study other photocatalytic applications, mainly hydrogen production, so there have not been published many articles related to the degradation of dyes.Liang et al. [133] reported an interesting work comparing effectiveness based on deposited metal.Pt, Pd and Ag were loaded over MIL-100 applied in the methyl orange (MO) degradation upon visible light.Although all metals enhanced the activity, Pt@MIL-100 showed the highest conversion values, reaching complete degradation after 40 min.It was also remarkable the stability of these M@MIL-100 that maintained the activity after 5 cycles of utilization and did not show any structural change.Pt@MIL-100 clearly exhibited the highest photocurrent density compared with the other modified-MOFs, which showed that Pt was more effective in keeping the charges separated and avoiding the electron-hole recombination.Authors also detailed the mechanism that can be seen in Figure 11.

Heterostructures combining different components
Compared to other strategies, an interesting solution is to assemble different semiconductors to construct novel heterostructures with improved activity under visible and solar light.The bibliography gathers different possibilities of combination, but it is necessary to emphasize that the objectives in all of them are to favor the absorption of visible light, to generate the charges and, perhaps most importantly, to keep them separated [159,164].Without forgetting, of course, the requirement that these heterostructures must be stable and maintain their activity after successive uses.Some examples of these strategies are listed in Table 3. MOF combination with metal oxides commonly used in photocatalysis has been an interesting way to create novel photocatalysts.It is possible to find some examples combining the conventional TiO2 and ZnO oxides with different MOFs, but most of those heterostructures have been just proved under UV light [159].An interesting heterojunction was recently reported combining TiO2 nanosheets with MIL-100(Fe), but its photocatalytic performance under visible light requires the addition of H2O2 as oxidant to increase the amount of radicals responsible of the MB oxidation [193].Something similar occurs by combining Fe-based MOF with iron oxides.They required the addition of H2O2, thus converting in a photoFenton like process.Beside this, Feng et al. [194] constructed recently a magnetic modified MOF based on Fe2O3/MIL-53(Fe).Although the best photocatalyst was not able to degrade completely the MB tested, the reusability of the photocatalysts was very interesting because it can be recovered from aqueous solution by a magnet thanks to the paramagnetic properties provided by the inclusion of Fe2O3.Bismuth based materials are other typical class of semiconductor studied that have attracted widely attention as visible-light-driven photocatalysts because of their narrow band gap.Bi2WO6 was assembled on UiO-66(Zr) for the removal of RhB under visible lights.The data demonstrated the high activity of these composites that depended on the Bi:Zr ratio used during the synthesis.RhB was totally degraded after 3 h of reaction due to the formation of O2 •-and h + as main active species [196].Further, same authors were also able to synthesize several BiOBr/UiO-66 composites that were more efficient than Bi2WO6/UiO-66, achieving total elimination of RhB in just 15 min under visible light [199].The activity of this composite was also attributed to the generation of active O2 •-and h + species.More recently, Bi2MoO6 was coupled to UiO-66 yielding novel photocatalysts with a similar photocatalytic activity than Bi2WO6/UiO-66 for the removal of RhB under visible light [197].It is noteworthy that all these heterostructures were better than the pristine UiO-66, which just achieved RhB conversion values close to 40%.The combination of MOFs with bismuth compounds improves the photocatalytic activity because favors the separation of charges, inhibiting the recombination and thus generating more radical species [200].
Several silver-based materials have been also used as component to promote the photocatalytic activity for dyes degradation.Ag2CO3 was combined with UiO-66(Zr) yielding high RhB degradation rates [201].The results showed the existence of an interaction between the Ag2CO3 and the UiO-66, which benefited the structural stability of composite and its photocatalytic performance.Same authors also fabricated a similar heterostructure with AgI and UiO-66 achieving analogous performance for RhB degradation [202].
g-C3N4 is a metal-free semiconductor with a low band gap (2.70 eV) that can absorb visible light, so it has a great potential for photocatalytic applications.Its coupling with different MOFs has been considered by researches for dyes removal.g-C3N4/MIL-125 heterostructure was created some years ago by hydrothermal synthesis, studying the optimal ratio among both components.The photocatalytic data showed that just incorporating 7% of g-C3N4 was possible to increase the degradation rate to double [204].The stability of this heterostructure was also remarkable, showing the same RhB reduction after 5 recycles.The photocatalytic performance was ascribed to the electron transfer in the metal-oxo-clusters, the light absorption by g-C3N4 and the intimate contact among both semiconductors that favors the charges separation [205].
Graphene materials have been also proved as a component to create novel heterojunctions with different MOFs for water treatment by photocatalysis.Reduced graphene oxide (rGO) and graphene oxide (GO) have been selected because their textural and conductive properties (see examples in Table 3).rGO/NH2-MIL-125 turns out to be an interesting example [207].Authors described the high photocatalytic performance of this heterojunction for MG degradation, but also demonstrated that the incorporation of rGO affected the crystallization of the MOF.Both NH2-MIL-125 and rGO are rich structures that when combined generate strong interactions that produce the twisting of the Tioxo-clusters and distort the NH2-MIL-125 structure.When designing heterojunctions, it is also important to take into account the relationship between both components.This issue was also studied in this work, showing that rGO amounts higher to 20% diminished the activity because a redundant relationship between both semiconductors occurred, that caused weakness in the movement of electrons.
Continuing with the idea of achieving a more efficient use of solar energy, due to the increasing environmental and energy concerns, the synthesis of ternary and hybrid systems has received great attention.These systems integrate different components (more than 2) in order to take advantage of the synergy between different heterojunctions.Table 4 summarizes some representative examples, recently reported, highlighting Z-schemes systems based on plasmonic structures.Most of them use silver nanoparticles and other silver compounds to enhance the photocatalytic activity.The superior activity of these ternary systems was usually attributed to the synergistic effects from surface plasmon resonance (SPR) of silver compounds and the sequential transfer of charges via the known Z-scheme mechanism, resulting in an efficient separation of electron-hole pairs [137].Nevertheless, in some cases the stability of these hybrids is not strong enough.For instance, Ag/AgCl/MIL-53 exhibited high photocatalytic activity for the removal of different dyes, but its efficiency decreased after several recycles [210]. 1 RhB= rhodamine B; MB= methylene blue; PBS= ponceau BS.

Photoreduction of heavy metals
Regarding the water pollution, heavy metals turn out to be toxic pollutants whose removal is one of the challenges of many researches.Different heavy metals have been detected in surface water and industrial wastewater, being lead, mercury, cadmium, arsenic and chromium the most representative.These compounds cause acute toxicity on humans and aquatic organisms [216,217].A recent review reports the use of MOFs for the removal of heavy metals from water, but it is curious that the vast majority are dedicated to elimination by adsorption [218].There is a small number of works that try to convert these toxic species into others of lower toxicity.Among them stands out the reduction of Cr(VI) by photocatalysis.The removal of Cr(VI) is one of the objectives in environmental remediation due to the increasing use of chromium compounds in various industries, such as metal plating and tanneries.Table 5 summarizes some representative examples used for chromium reduction under visible light, including some pristine and modified-MOFs.Initially Fe-based MOFs, such as MIL-53 or MIL-100, were tested for reducing Cr(VI), although not too many were able to achieve high conversion rates at short times (among 1 and 2 h) [218].The continuous investigations on MOFs has allowed advancing in the development of more efficient photocatalysts.Thus, MIL-68(Fe) prepared by solvothermal methodology showed high activity under visible light in a wide pH range [219].100% conversion rate was obtained in just 5 min at pH=3.Higher pH values result in the same conversion rate but requires greater times, e.g. 60 min are required at pH=6.The amine functionalization of different MOFs was also tested by different authors [161,220].Shi et al. [161] prepared different amine-Fe-based-MOFs and observed that the amine effect depends on the pristine MOF structure.Thus, while NH2-MIL-88 and NH2-MIL-101 achieved complete Cr(VI) reduction among 40-60 min, NH2-MIL-53 only managed to reduce 10% of Cr(VI).Authors assumed that the high performance of those NH2-MIL(Fe) is because the incorporation of NH2 in the linker promotes the transfer of charges between the organic linker and the iron cluster and enhances the light absorption.These NH2-MIL(Fe) also exhibited high stability in the reaction medium, maintaining their performance after successive reuses.
Regarding the modified-MOFs, the strategies followed so far to modify MOFs are the same as those described above in section 6.1, mainly metal NPs decoration and heterostructures creation.The M@MIL-100 system described before for MO degradation was also tested for Cr(VI) reduction, demonstrating once again the activity of these modified-MOFs [133].All of them reached complete reduction of Cr(VI) to Cr(III) in very short times, even Pt@MIL-100 only needed 8 min, being even stable when reused in successive occasions.Different heterostructures have also been tested in the reduction of chromium by photocatalysis.Heterojunctions with g-C3N4 are attracting great attention, as occurred for dyes degradation, because the contact between both semiconductors inhibits the recombination process.In a recent work, g-C3N4/MIL-153(Fe) was successfully prepared demonstrating high conversion rates for the reduction of Cr(VI).The study revealed that the activity was not only favored by the inhibition of recombination but also because the contact improved charges mobility thanks to the good conductive properties of g-C3N4 [222].Analogous performance was obtained when MIL-53(Fe) was assembling with reduced graphene oxide (rGO), which was to minimize the charges recombination [223].The promoter effect of rGO has been also observed during the Cr(VI) reduction with rGO/UiO-66-NH2.In this case, rGO acts as electron trapper extending the average life time of electron-hole pairs [136].
At this stands, it is noteworthy that contrary to what happens with other semiconductors, MOFs have not been tested almost for the reduction of heavy metals other than Cr(VI).Even, the use of solar light has not been considered enough in photoreduction processes instead of what happens with the degradation of dyes.Therefore, there are still many opportunities for research in this field to apply MOFs to heavy metals remediation.

Photodegradation of priority pollutants
Different chemical pollutants were included by the Environmental Protection Agency (EPA, USA) in a list because of their toxicity and their presence in urban areas and wastewater systems [224].They were known as priority pollutants, including polycyclic aromatic hydrocarbons, pesticides, volatile organic compounds, chlorobenzenes, phthalates and alkylphenols.Their toxicity was related to their carcinogenic and mutagenic effect on organisms and humans, aggrieved by their persistence in the environment.
Among them, phenol and related phenolic-compounds have been extensively studied as target contaminants in many technologies focused on water purification.Their degradation pathways are known in detail, which allows establishing a reliable comparison between various photocatalysts.Nevertheless, not too many MOFs have been tested for phenol degradation, probably because the conversion rates achieved were not so high.For instance, Alvaro et al. [225] compared some time ago the activity of MOF-5 with TiO2 and ZnO semiconductors for phenol degradation under UV light.Although, the activity per metal atom was somewhat superior, the conversion rate per gram of catalyst was considerably inferior.Even, posterior studies demonstrated the instability of MOF-5 in water systems [218].More recently, Surib et al. [226] intercalated several metal ions (Ag + , Fe 3+ , and Zn 2+ ) into the porous framework of a Cd-MOF by ion-exchange, yielding a new series of photocatalysts used for the removal of 2-chlorophenol under direct daylight illumination.All tested modified-MOFs were more active than the common TiO2, although the intercalated with Fe 3+ achieved the highest conversion value, 93% after 5 h of reaction.Authors explained that this activity was due to the new energy levels triggered between the bands of Cd-MOF by the metal ion.These new levels reduced the band gap enhancing the light absorption.Despite these results, the use of MOFs in the degradation of priority pollutants is still untapped.

Photodegradation of emerging pollutants
Emerging pollutants have raised concerns in water treatment because they are found in wastewater in low concentrations due to the continued use by humans.The discharge regulations of these compounds are not completely or not at all regulated, which can result in real hazards to the human health and environment.Among the emerging pollutants, it is possible to find pharmaceuticals, personal care products, plasticizers and pesticides, among others [227].The degradation of emerging pollutants requires highly efficient photocatalysts, capable of absorbing visible radiation, generating the necessary charges and keeping them separate for the creation of radicals that oxidize contaminants, since these pollutants present a chemical structure that is more difficult to oxidize than dyes.Despite research into the design of MOFs with photocatalytic activity, until now there are few works dedicated to the removal of emerging pollutants and most are focused on Fe-based MOFs.Among Fe-MOFs, MIL-53, MIL-101 and MIL-100 were used for the removal of tetracycline in water solutions.MIL-101 was with difference the most active, attributed to its structure, reaching 100% disappearance of the compound [57].However, it highlights that 60% of the tetracycline elimination was due to the adsorption process, only 40% was removed by photocatalysis.Although there were no data about the detection of byproducts, the study about the radical mechanism demonstrated that O2 •-, h + and • OH were involved in the tetracycline degradation.The MIL-100 and its derivative Pd@MIL-100 have been also evaluated in the degradation of various pharmaceuticals and personal care products (PPCPs), theophylline, ibuprofen and bisphenol A [162].However, their activity was quite limited and required the incorporation of additional oxidants, such as H2O2, to achieve conversions greater than 60%, becoming a photo-fenton type process.
Better results have been recently achieved by Huang et al. [228] with a novel Ag/AgCl@MIL-88A(Fe) composite.This composite reached total removal of ibuprofen under visible light after 3 h of reaction, but more interesting is the high degree of mineralization, achieving in that time a TOC reduction of 90%.The stability of this composite is also remarkable.It maintains the activity after 4 recycles and keeps its structure, without negligible leaching of Fe and Ag after those 4 cycles.Authors even studied the degradation pathway and concluded that h + , e -and O2 •-played important roles on the photocatalytic degradation.The performance of this composite is due to a synergistic effect between the plasmon resonance of Ag NPs, the light absorption of both MOF and AgCl, and the charges separation due to the interconnection among the three components (Figure 12).Fun et al. [229] prepared a Ag/AgCl@ZIF-8 MOF to eliminate acetaminophen under visible light irradiation.Interesting works have been recently reported focused on the degradation of tetracycline antibiotic.Wang et al. [230] developed a core-shell In2S3/MIL-125(Ti) heterostructure capable of degrading 60% tetracycline after 60 min upon visible light.This result is very interesting considering that the tetracyline oxidation is more difficult than that of dyes.However, compared to other conventional photocatalysts, the mineralization rate was quite low.Only 17% of tetracycline was transformed on CO2 and H2O.Even, the stability of this heterostructure was not high enough, the conversion rate decreased to 45% after 3 successive cycles.Higher rates were obtained for the tetracycline photodegradation upon sunlight by using a novel g-C3N4/ZIF-8 heterostructure [231].Total disappearance was exhibited after 60 min of reaction, although there are no data about the mineralization of the antibiotic.The mechanism proposed that ZIF-8 absorbs the light yielding photogenerated electrons that are further transferred to the g-C3N4.These electrons react with the O2 present in the medium generating O2 •-radicals that are involved in the tetracycline oxidation.At the same time, the holes generated in the ZIF-8 can also interact with the target molecules.As occurred in other heterojunctions, the synergistic effect between both components promotes the separation of charges and inhibits the undesired recombination process.

Stability and reusability of MOFs during water purification by photocatalysis
Unfortunately, MOFs have relatively inferior stability than other photocatalysts such as those based on TiO2, CdS, BiVO4, g-C3N4, and their heterojunctions.Their instability can be mainly related to the self-dissolution of some components into the aqueous reaction medium, and some irreversible reaction of metal clusters and/or the organic linkers with some component (reactant, products or byproducts) of the water medium [153,166,167].The main factor controlling the stability of MOFs in water is the strength of the metal-ligand bonds, although crystallinity, metal-ligand coordination geometry and porosity must be also considered [114,232].The methodologies commonly used to study the stability of MOFs are the characterization of the recovered used-MOF after the reaction, mainly studying the surface morphology and crystalline structure, the metal leaching analysis, and the reusability tests.It must take into account that one of the main aims in terms of environmental protection is to avoid the leaching of transition metals into the reaction solutions.Reusability is also a very relevant criterion for the use of MOFs.The main reasons stablished for the reduction of the photocatalytic activity after several cycles of use were: i) the inevitable dissolution of some MOF's components during the photocatalytic reaction, and ii) the deactivation of the MOF surface due to the adsorption of some reactant or product [155].Regarding the stability and reusability, some MOFs and MOF-based composites have been demonstrated to exhibit reasonable stability and reusability for catalytic removal of water contaminants.
As it has been mentioned before, MIL-53(Fe) has been one of the most studied MOF in photocatalysis.However, some works reveals that its photocatalytic activity decreased significantly after reutilization for degrading several dyes under visible light.Feng et al. [194] showed that the conversion rate for MB degradation with MIL-53(Fe) decreased from 90% to 30% after only 3 cycles of use.Worse results were obtained by Araya et al. [233] with this MOF, whose photocatalytic performance disappeared after 5 cycles during RhB degradation.In this case, the instability was due to the iron leaching on the reaction medium.However, both works reported interesting solutions to avoid the MIL-53(Fe) instability based on combining the MIL-53(Fe) with other components.The degradation of MB was enhanced by synthesizing a magnetic Fe2O3-MIL-53 composite, maintaining a 60% conversion rate after 3 cycles [194], while more than 90% was kept for RhB removal by using a novel hybrid material Amberlite-MIL-53 combining the MOF with a resin [233].
In addition, many efforts are currently focused on the development of multicomponent MOFs, also called MOFs-hybrid materials or MOFs-composites, looking for a synergistic effect that enhances the stability and reusability, the photocatalytic activity and a better use of the visible light.However, as it has been affirmed before, the majority of the researches have been focused on the photodegradation of dyes.The application of MOFs on degrading other pollutants is an important aim to be pursued in future investigations, shifting for instance to the removal of inorganic species, emerging pollutants or, even, pathogens from water, focusing the attention on the use of solar light as energy source.

Conclusion and outlooks
MOFs are a relatively novel class of porous inorganic-organic materials with repetitive structure from unit cell composed by organic linkers and clusters or metal nodes (SBUs).The combination of these components allows synthesizing MOFs with tailored properties for specific applications such as photocatalytic degradation of pollutants from water.In order to much wider application of MOFs for photocatalytic water purification process a deeper understanding of the structural parameters controlling their activity is needed.Furthermore, most of the studies performed up to date are focused in the degradation of dyes using UV light as energy source.A more complete analysis of the degradation of other compounds is advisable, including the photocatalytic degradation of emerging contaminants and reduction of heavy metals.
For real application two aspect must be improved.First, the synthesis conditions should allow obtaining higher amounts of MOFs in continuous operation, solvothermal processes are limited by the slow reaction rates, and at a lower cost.And second, the stability of MOFs in water should be assured.With the achievement of these requirements, MOFs can become a real alternative with promising future for the removal of different pollutants present in water by photocatalysis. Photocatalyst

Figure 1 .
Figure 1.Schematic representation of reactive oxidant species generation and contaminant oxidation after the irradiation of a photocatalyst in aqueous solution.

Figure 2 .
Figure 2. SBUs (metal node) and organic linkers used for the synthesis of MOF-5 and HKUST-1.Yellow and blue spheres represent the free spaces in the framework and have no chemical meaning (reproduced from ref. [59]).

Figure 6 .
Figure 6.Post-functionalization strategies for MOFs modification (reproduced with permission Reproduced by permission of The Royal Society of Chemistry [102]).

Figure 9 .
Figure 9. Illustration of the types of MOF developed for photocatalytic applications (reproduced with permission from ref. [153]).

Figure 10 .
Figure 10.Scheme of the dual excitation mechanism proposed by Shi et al. for the photoreduction of Cr(VI) with NH2-Fe-MOFs (reproduced from ref. [161]).

Figure 11 .
Figure11.Scheme of the mechanism proposed for the MO photodegradation with several M@MIL-100 (M=Pt, Pd, Ag) under visible light (reproduced with permission from ref.[133]).

Table 1 .
Different types of photocatalysts used for the removal of pollutants in water.

Table 3 .
Heterostructures based on MOFs for dyes degradation under visible and solar light.

Table 4 .
Ternary and hybrid systems for dyes removal under visible and solar light.

Table 5 .
Relevant MOFs and modified-MOFs used for Cr(VI) reduction under visible light.