Recent Advances of Cobalt-Based Electrocatalysts for Oxygen Electrode Reactions and Hydrogen Evolution Reaction

This review summarizes recent progress in the development of cobalt-based catalytic centers as the most potentially useful alternatives to noble metal-based electrocatalysts (Pt-, Ir-, and Ru-based) towards the oxygen reduction reaction (ORR), oxygen evolution reaction (OER), and hydrogen evolution reaction (HER) in acid and alkaline media. A series of cobalt-based high-performance electrocatalysts have been designed and synthesized including cobalt oxides/chalcogenides, Co–Nx/C, Co-layered double hydroxides (LDH), and Co–metal-organic frameworks (MOFs). The strategies of controllable synthesis, the structural properties, ligand effect, defects, oxygen vacancies, and support materials are thoroughly discussed as a function of the electrocatalytic performance of cobalt-based electrocatalysts. Finally, prospects for the design of novel, efficient cobalt-based materials, for large-scale application and opportunities, are encouraged.


Introduction
Considering the continuous decrease of fossil fuels and deteriorated environments, it is of great importance and urgency to explore abundant, eco-friendly and renewable energy sources.Many energy conversion and storage technologies, e.g., proton exchange membrane fuel cells (PEMFCs, in which the free energy of a chemical reaction is directly converted into electrical energy), water electrolyzers (WEs, where oxygen and hydrogen from water are produced), unitized regenerative cells (URCs, a system comprising an electrolyzer and a fuel cell), due to their high efficiency and friendly environments, have been extensively developed [1,2].To some extent, electrochemical processes play an essential role in these systems, for example, the oxygen reduction reaction (ORR) and hydrogen oxidation reaction (HOR) occurring on the cathode and anode of a H 2 -O 2 fuel cell, whereas the oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) are, respectively, the anodic and cathodic reactions in an electrolyzer [3][4][5].Platinum-based materials perform efficiently the HOR with much less Pt mass loading (0.05 mg cm −2 ) at the anode [6].The complex oxygen electrode reactions (oxygen reduction reaction and oxygen evolution reaction), which involve various elementary steps, are kinetically intrinsic sluggish reactions, and primarily catalyzed by precious metal centers, e.g., Pt, Ir, Ru.The limited resources and high cost of these precious metals are an unavoidably obstacle for widespread commercial applications [7].Therefore, it is of increasing interest to reduce the usage of precious metals, or completely replace precious metals with abundant, cheap and highly active ones.In the past few years, various kinds of novel non-precious metal nanomaterials have been explored as alternatives to precious metal-based electrocatalysts, including strongly coupled transition metals (oxides, phosphides, chalcogenides, hydroxides, double perovskites, and so on) [8][9][10][11][12][13][14], nanocarbon hybrids [15], and free-metal carbon-based materials [7,16].
In this review, we stress this novel cobalt-based material (CoCat) associated with some electrochemical processes, e.g., ORR, OER and HER in acid and alkaline electrolytes from the surface electrochemistry perspective.All these carbons supported cobalt-centered catalysts are organized into several categories, namely, cobalt oxides, cobalt chalcogenides (selenides, sulfides), Co-LDH, Co-MOFs, and Co-N x /C, see Figure 1.In what follows, we firstly illustrate the basic reaction mechanism of ORR, OER and HER, then summarize recent progress in the development of cobalt-based electrocatalysts towards ORR, OER, HER.For the Co-centered electrocatalysts, particular attention is paid to the design, synthesis strategies, and electrocatalytic performance.Finally, we further discuss the challenges ahead in designing novel, highly efficient cobalt-based electrocatalysts for large-scale applications and opportunities.complex oxygen electrode reactions (oxygen reduction reaction and oxygen evolution reaction), which involve various elementary steps, are kinetically intrinsic sluggish reactions, and primarily catalyzed by precious metal centers, e.g., Pt, Ir, Ru.The limited resources and high cost of these precious metals are an unavoidably obstacle for widespread commercial applications [7].Therefore, it is of increasing interest to reduce the usage of precious metals, or completely replace precious metals with abundant, cheap and highly active ones.In the past few years, various kinds of novel non-precious metal nanomaterials have been explored as alternatives to precious metal-based electrocatalysts, including strongly coupled transition metals (oxides, phosphides, chalcogenides, hydroxides, double perovskites, and so on) [8][9][10][11][12][13][14], nanocarbon hybrids [15], and free-metal carbonbased materials [7,16].
In this review, we stress this novel cobalt-based material (CoCat) associated with some electrochemical processes, e.g., ORR, OER and HER in acid and alkaline electrolytes from the surface electrochemistry perspective.All these carbons supported cobalt-centered catalysts are organized into several categories, namely, cobalt oxides, cobalt chalcogenides (selenides, sulfides), Co-LDH, Co-MOFs, and Co-Nx/C, see Figure 1.In what follows, we firstly illustrate the basic reaction mechanism of ORR, OER and HER, then summarize recent progress in the development of cobaltbased electrocatalysts towards ORR, OER, HER.For the Co-centered electrocatalysts, particular attention is paid to the design, synthesis strategies, and electrocatalytic performance.Finally, we further discuss the challenges ahead in designing novel, highly efficient cobalt-based electrocatalysts for large-scale applications and opportunities.

Mechanism of ORR
The oxygen reduction reaction is the cathodic electrode reaction.The ORR electrochemical properties can be evaluated from rotating disc electrode (RDE) measurements (namely, the onset potential (E onset ), half-wave potential (E 1/2 ), overpotential (η), and diffusion-limiting current density (j L )).The ORR electrochemical reactions, in acid and alkaline medium, are shown below.The adsorbed molecular oxygen is reduced by a "direct" four-electron charge transfer process or reduced to water (acid medium) or OH − (alkaline medium) via the formation of HO 2 − and H 2 O 2 intermediates with the consumption of two electrons [41].In acid condition, oxygen can be reduced to water with a standard thermodynamic potential at 1.229 V vs. SHE (Standard Hydrogen Electrode) for the four-electron pathway (Equation ( 1)); while in the alkaline medium, hydroxide is produced with a standard thermodynamic potential at 0.401 V vs. SHE in the four-electron reaction (Equation ( 4)).
The charge-transfer reaction depends on the electrolyte nature and the surface properties of the catalytic centers.Even for Pt, considered as the best ORR catalyst, a substantial cathodic overpotential of 300 mV [41] is observed in acid electrolyte.Clearly, a selectivity for the four-e − reduction pathway is highly desirable to improve the electrocatalytic ORR efficiency.Acid medium: or Alkaline medium: or O 2 + H 2 O + 2e − → (HO 2 ) − + OH − , ( (HO 2 ) − + H 2 O + 2e − → 3OH − , (6)

Bond Ionicity or Covalency of S, Se, Te
In transition metals (TM) chalcogenides, the increase of covalency is obtained when d-state of TM interact with p-state of chalcogenides take place in MX 2 compounds (e.g., M: Co; X: S, Se).The hybridization degree of chalcogenides p-state with d-state of TM favors the metal-metal interaction.Moreover, metal cluster chalcogenides catalysts, Ru 2 Mo 4 X 8 (Chevrel phase), where X: Se-and S-based, have motivated a strong interest since Alonso-Vante and Tributsch [42] in 1986 reported the comparable ORR activity of Ru 2 Mo 4 Se 8 to that of Pt in H 2 SO 4 [43][44][45][46].In binary metal clusters (e.g., Ru) coordinated with X, they proposed that the activity of Ru x X y catalysts depends on the chalcogen, and increases according to: Ru x S y < Ru x Te y < Ru x Se y ~Mo x Ru y Se z in acid solution [47].The structure analysis from the EXAFS (Extended X-ray Absorption Fine Structure) data suggested that that the variation of the chalcogen nature led to a change in its amount in the first co-ordination sphere of ruthenium.The latter apparently affected the strength of ruthenium interaction with oxygen, which is evidenced by significant differences observed in the Ru/O distances.For Ru x S y clusters, the high co-ordination number of Ru to sulfur resulted in blocking the ruthenium active sites towards adsorption of molecular oxygen, which showed lowest ORR catalytic activity.In this respect, the coordinating strength of S, Se, Te on Ru chalcogenides was demonstrated (ligand effect).This is in contrast to cobalt dichalcogenides compound (CoX 2 ) demonstrated by Behret et al. [48] that reported a trend of ORR activity basically followed the sequence: M x S y > M x Se y > M x Te y .In addition, the activity was also related to the catalytic centers with Co.Both theoretical and experimental results confirmed that Co-selenides are less active than its sulfides by ~0.2 V [49].The considerable decrease in activity was observed when S was partly or totally substituted by O, Se, and Te, probably attributed to the geometric and electrostatic conditions in spinel structures.It was claimed that the selenium and tellurium with higher atomic radii give a weaker electrostatic repulsion to the reduction product (O 2− ) and also to the intermediate reduction products.Therefore, the reaction products on the surface of seleno-and tellurospinels were not as easily desorbed as those on thiospinels [48].
Furthermore, a series of transition metal chalcogenides were reported by Behret et al. [48] consisting of the anionic substitution (S, Se and Te), and the cationic substitution (Fe, Co, Ni).These primary results disclosed a trend for ORR electrochemical performance with the metal cations as follows: Co > Ni > Fe, and for the chalcogenide anions: S > Se > Te.They found that Co-S and Co-NiS systems possessed very high catalytic activity in acidic medium.They declaimed that better catalytic activity may be caused by the minimal energy difference between the oxygen 2p orbital and the highest occupied d orbital of sulfides [50].CoS was, apparently, the most promising ORR non-precious metal catalyst in alkaline media.Besides, Co 9 S 8 was predicted to have similar ORR activity with that of Pt via a four-electron ORR pathway in acidic solution [51].Zhu et al. [52] developed a simple and scalable route to synthesize 3D hybrid nanocatalyst-the Co 9 S 8 incorporated in N-, S-doped porous carbon exhibited an excellent catalytic activity, superior long-term stability, and good tolerance against methanol.Recently, Dai et al. [19], for the first time, designed and prepared the etched and doped Co 9 S 8 /graphene hybrid as an advanced bifunctional oxygen electrode reactions catalyst.

Crystal Structure and Particle Size Effect
The different crystal structures with the same chemical composition led to the different ORR catalytic activity.For instance, CoSe 2 has two common crystal structures: cubic (pyrite-type), and orthorhombic marcasite-type.Alonso-Vante and Feng [53,54] discovered that the orthorhombic CoSe 2 was obtained after a heat treatment of 250-300 • C. The cubic CoSe 2 phase was obtained at high temperature (400-430 • C).The latter showed a higher ORR activity by 30 mV in 0.5 M H 2 SO 4 .Wu et al. [55] prepared cubic Co 9 S 8 particles surrounded by nitrogen-doped graphene sheets for the ORR in alkaline medium with an improved ORR activity and stability comparable to Pt/C.Similarly, cobalt sulfides with different chemical compositions and crystal structures, namely, Co 1-x S, CoS (hexagonal phase) [56], CoS 2 , Co 9 S 8 and Co 3 S 4 (cubic phase) [56], are the most promising type of chalcogenides for the ORR.As an illustration, Dai et al. [18] obtained the Co 2 S/RGO with an average particle size of ca.50 nm and Co 1-x S/RGO with an average particle size of 10-20 nm.The latter displayed a better ORR activity in terms of the onset potential of ca.0.8 V vs. RHE (Reversible Hydrogen Electrode) in 0.5 M H 2 SO 4 .The authors noticed that the ORR performance depends on the particle size and on the crystal structure.
Generally, the mass activity (MA, activity mass −1 ) of a catalyst is defined as the current normalized by the noble metal loading or catalyst loading as measured at a specific electrode potential.In order to increase MA, some strategies can be adopted, i.e., increasing the specific surface area of the catalysts by decreasing the particle size [57].The particle size effect on the specific activity of catalysts has been attributed to different factors, such as, the structural sensitivity, i.e., the dependence of surface geometry, the electronic state, and the metal-support interaction [58].Moreover, the particle size of the catalysts on the oxygen reduction reaction can be influenced by the adsorption of oxygen during the reaction, which is mainly associated with the fraction of active sites on the surface of the catalysts.Wang et al. [59] demonstrated that the Pd 3 Co alloy had a slightly smaller lattice spacing than that of Pd, and thus a further shifting to larger size was expected due to the stronger lattice-induced compression.The 3-fold enhancement in the specific activity of Pd 3 Co could be attributed to the nanosized-, and lattice mismatch-induced contraction in (111) facets, based on the DFT (density Functional Theory) calculation using a nanoparticle model.Feng et al. [46] developed cubic CoS 2 nanocatalysts with different particle size from 30 nm to 80 nm by adjusting the initial Co 2+ concentration in the presence of hexa-decylcetyl-trimethylammonium (CTAB), and further demonstrated that the ORR activity depends on the average particle size, see Figure 2. The ORR activity remained similar to the particle size from 30 nm to 50 nm, and then significantly decreased with size from 50 nm to 80 nm.The CoS 2 catalyst with an average particle size of 30.7 nm demonstrated an excellent electrocatalytic performance with an onset potential (E onset ) of 0.94 V vs. RHE, a half-wave potential of 0.71 V vs. RHE, and high tolerance in methanol-containing 0.1 M KOH.Such a trend was also found for 20 wt% Co 3 S 4 /C nanoparticles and 20 wt% CoSe 2 /C [60].The particle size can be approximately adjusted within a certain range by controlling the initial feeding concentrations, which has strong effect on the crystal nucleation and crystal growth.
Catalysts 2018, 8, x FOR PEER REVIEW 5 of 43 could be attributed to the nanosized-, and lattice mismatch-induced contraction in (111) facets, based on the DFT (density Functional Theory) calculation using a nanoparticle model.Feng et al. [46] developed cubic CoS2 nanocatalysts with different particle size from 30 nm to 80 nm by adjusting the initial Co 2+ concentration in the presence of hexa-decylcetyl-trimethylammonium (CTAB), and further demonstrated that the ORR activity depends on the average particle size, see Figure 2. The ORR activity remained similar to the particle size from 30 nm to 50 nm, and then significantly decreased with size from 50 nm to 80 nm.The CoS2 catalyst with an average particle size of 30.7 nm demonstrated an excellent electrocatalytic performance with an onset potential (Eonset) of 0.94 V vs. RHE, a half-wave potential of 0.71 V vs. RHE, and high tolerance in methanol-containing 0.1 M KOH.Such a trend was also found for 20 wt% Co3S4/C nanoparticles and 20 wt% CoSe2/C [60].The particle size can be approximately adjusted within a certain range by controlling the initial feeding concentrations, which has strong effect on the crystal nucleation and crystal growth.

Synthesis and Support Effect
Cobalt selenides have received extensive attention for their ORR activity [61,62].This electrocatalyst deposited on highly conductive supporting material is very important to enhance the electrocatalytic performance.The ideal supporting materials for catalytic centers have high surface area, high electrical conductivity, and high chemical stability [63].Taking advantage of the high surface area of amorphous carbon, Feng et al. [62] synthetized via a surfactant-free way the CoSe2 orthorhombic-phase nanoparticle supported onto XC-72 Vulcan with a promising ORR performance in acid media.Zhou et al. [64] developed supported CoSe2 nanostructures by a hydrothermal approach using the increased disordered domains of carbon nanotubes (CNTs) derived from a MOF with excellent ORR performance in 0.1 M KOH with a Tafel slope of 45 mV dec −1 , onset potential of ca.0.8 V vs. RHE, and a long-term stability.Although a relative success was obtained, the major drawback of the hybrid catalysts is the weak interaction between the catalytic centers and the support

Synthesis and Support Effect
Cobalt selenides have received extensive attention for their ORR activity [61,62].This electrocatalyst deposited on highly conductive supporting material is very important to enhance the electrocatalytic performance.The ideal supporting materials for catalytic centers have high surface area, high electrical conductivity, and high chemical stability [63].Taking advantage of the high surface area of amorphous carbon, Feng et al. [62] synthetized via a surfactant-free way the CoSe 2 orthorhombic-phase nanoparticle supported onto XC-72 Vulcan with a promising ORR performance in acid media.Zhou et al. [64] developed supported CoSe 2 nanostructures by a hydrothermal approach using the increased disordered domains of carbon nanotubes (CNTs) derived from a MOF with excellent ORR performance in 0.1 M KOH with a Tafel slope of 45 mV dec −1 , onset potential of ca.0.8 V vs. RHE, and a long-term stability.Although a relative success was obtained, the major drawback of the hybrid catalysts is the weak interaction between the catalytic centers and the support leading to low activity and stability.The formation of interfacial bonds between the catalytic center and the support favors the adsorption properties, therefore, enhancing the kinetics toward the electrocatalytic reaction [65].The catalytic-support interaction may weaken the adsorption events, and then decrease the energy barriers for the reaction.This phenomenon, known as strong metal-support interaction (SMSI) is an important ingredient to tailor, and tune highly active and stable catalyst centers.Unni et al. [66] fabricated high-surface area N-doped carbon nanohorns (NCNH) supported cubic-phase CoSe 2 via a simple NaBH 4 -chemical reduction process of CoCl 2 and SeO 2 , Figure 3a,b.The CoSe 2 /NCNH demonstrated considerable ORR activity in alkaline medium, cf. Figure 3c,d, as a result of the electronic structure modification of chalcogenide (CoSe 2 ) centers throughout its interaction with NCNH via the nitrogen moieties, Figure 3e.
Catalysts 2018, 8, x FOR PEER REVIEW 6 of 43 leading to low activity and stability.The formation of interfacial bonds between the catalytic center and the support favors the adsorption properties, therefore, enhancing the kinetics toward the electrocatalytic reaction [65].The catalytic-support interaction may weaken the adsorption events, and then decrease the energy barriers for the reaction.This phenomenon, known as strong metalsupport interaction (SMSI) is an important ingredient to tailor, and tune highly active and stable catalyst centers.Unni et al. [66] fabricated high-surface area N-doped carbon nanohorns (NCNH) supported cubic-phase CoSe2 via a simple NaBH4-chemical reduction process of CoCl2 and SeO2, Figure 3a,b.The CoSe2/NCNH demonstrated considerable ORR activity in alkaline medium, cf. Figure 3c,d, as a result of the electronic structure modification of chalcogenide (CoSe2) centers throughout its interaction with NCNH via the nitrogen moieties, Figure 3e.Similarly, García-Rosado et al. [67] prepared a series of N-doped reduced graphene oxide (N-RGO) as supports for hexagonal cobalt selenide (CoSe) by a NaBH4-assisted chemical reduction, Figure 4.The carbon support after the surface reduction supplied more available active and anchor sites due to the increase in the pore size and surface area.The ORR performance is concomitant with the properties of the supports.The graphitic and pyridinic nitrogen moieties of N-RGO acted as electrochemical active sites for the ORR in alkaline media.Similarly, García-Rosado et al. [67] prepared a series of N-doped reduced graphene oxide (N-RGO) as supports for hexagonal cobalt selenide (CoSe) by a NaBH 4 -assisted chemical reduction, Figure 4.The carbon support after the surface reduction supplied more available active and anchor sites due to the increase in the pore size and surface area.The ORR performance is concomitant with the properties of the supports.The graphitic and pyridinic nitrogen moieties of N-RGO acted as electrochemical active sites for the ORR in alkaline media.
Additionally, Pan et al. [68] used porous g-C 3 N 4 as a template and a N-source to successfully synthesize mesoporous S-, and N-co-doped carbon matrix coupled with Co@Co 9 S 8 nanoparticles, cf. Figure 5. Herein, the g-C 3 N 4 carbon matrixes not only enhance the conductivity, but also suppress the aggregation phenomenon during the electrochemical reactions.Besides, the strong coupling between Co@Co 9 S 8 and N-, S-carbon promoted significantly the ORR electrocatalytic performance with a more positive half-wave potential and lower Tafel slope value, as compared with the commercial Pt/C catalyst.
Similarly, García-Rosado et al. [67] prepared a series of N-doped reduced graphene oxide (N-RGO) as supports for hexagonal cobalt selenide (CoSe) by a NaBH4-assisted chemical reduction, Figure 4.The carbon support after the surface reduction supplied more available active and anchor sites due to the increase in the pore size and surface area.The ORR performance is concomitant with the properties of the supports.The graphitic and pyridinic nitrogen moieties of N-RGO acted as electrochemical active sites for the ORR in alkaline media.Additionally, Pan et al. [68] used porous g-C3N4 as a template and a N-source to successfully synthesize mesoporous S-, and N-co-doped carbon matrix coupled with Co@Co9S8 nanoparticles, cf. Figure 5. Herein, the g-C3N4 carbon matrixes not only enhance the conductivity, but also suppress the aggregation phenomenon during the electrochemical reactions.Besides, the strong coupling between Co@Co9S8 and N-, S-carbon promoted significantly the ORR electrocatalytic performance with a more positive half-wave potential and lower Tafel slope value, as compared with the commercial Pt/C catalyst.

Oxygen Reduction on Metal-Organic Frameworks (MOFs) Catalysts
MOFs and their derivatives have also been used as efficient precursors and self-sacrificing templates because of their well-tunable physical and chemical properties.Benefiting from the unique

Oxygen Reduction on Metal-Organic Frameworks (MOFs) Catalysts
MOFs and their derivatives have also been used as efficient precursors and self-sacrificing templates because of their well-tunable physical and chemical properties.Benefiting from the unique properties of MOF, such as, large surface area, tailoring porosity, and easy functionalization with other heteroatoms or metal/metal oxides, various carbon-based nanomaterials (as support) have been prepared.Based on organic ligands and cobalt metal centers, MOFs compounds possess special superiority to prepare various cobalt-based functionalized carbon nanomaterials, including heteroatom-doped porous carbons, and metal/metal oxide decorated porous carbons, via thermal decomposition under controlled atmospheres.For instance, Lou et al. [69] used ZIF-67 as a template and thioacetamide as a sulfur source to prepare a double-shelled Co-C@Co 9 S 8 nanocages electrocatalyst for the ORR.By adjusting the reaction time, the amorphous CoS nanocages (a-CoS NCs) and ZIF-67@a-CoS yolk-shelled hollow nanostructures were fabricated.The Co 9 S 8 shells, served as a nanoreactor, effectively prevented the Co-C active centers from aggregation, Figure 6a.Interestingly, the unique Co-C hollow cages significantly shortened the diffusion pathway of the electrolyte, and thus promoted the electrocatalytic activity, durability, and tolerant to methanol toward the ORR of Co-C@Co 9 S 8 catalyst.In Figure 6b-e, the onset potential remarkably reached 0.96 V vs. RHE with a limiting current of 4.5 mA cm −2 and a four-electron transfer route with OH − production in alkaline media.Additionally, a simple and efficient method to produce homogeneously dispersed cobalt sulfide/N-, S-co-doped porous carbon electrocatalysts, using ZIF-67 as precursor and template, was reported by Xia et al. [70].Due to a unique core-shell structure, high porosity, homogeneous dispersion of active components together with N-, and S-doping effects, the electrocatalyst not only showed an excellent electrocatalytic activity towards ORR with a high onset potential (ca.−0.04 V compared with −0.02 V for the benchmark Pt/C catalyst), but also revealed a superior stability (92%) compared with the commercial Pt/C catalyst (74%) in ORR.
Table 1 summarizes some transition metal chalcogenides as ORR catalysts investigated so far.One can conclude that: (1) Co-based chalcogenides are promising catalysts for the ORR in alkaline media; (2) the carbon support having a pore morphological structure, and hetero-atom doping plays a key role to promote the ORR performance of Co-based chalcogenides.Additionally, a simple and efficient method to produce homogeneously dispersed cobalt sulfide/N-, S-co-doped porous carbon electrocatalysts, using ZIF-67 as precursor and template, was reported by Xia et al. [70].Due to a unique core-shell structure, high porosity, homogeneous dispersion of active components together with N-, and S-doping effects, the electrocatalyst not only showed an excellent electrocatalytic activity towards ORR with a high onset potential (ca.−0.04 V compared with −0.02 V for the benchmark Pt/C catalyst), but also revealed a superior stability (92%) compared with the commercial Pt/C catalyst (74%) in ORR.
Table 1 summarizes some transition metal chalcogenides as ORR catalysts investigated so far.One can conclude that: (1) Co-based chalcogenides are promising catalysts for the ORR in alkaline media; (2) the carbon support having a pore morphological structure, and hetero-atom doping plays a key role to promote the ORR performance of Co-based chalcogenides.

Particle Size Effect and Chemical Composition
Different particle size also influences the electrocatalytic active surface.For example, Feng's group [76] synthesized a series of Co 3 O 4 /N-RGO composites with different particle size by controlling Co 2+ initial feeding concentrations, and carefully investigated the particle size effect of Co 3 O 4 nanoparticles on the bifunctional oxygen electrocatalytic performance.The Co 3 O 4 /N-RGO with the smallest particle size of 12.2 nm revealed the best bifunctional oxygen activity (ORR and OER) with lower ∆E = 0.75 V (∆E = E OER , j@10 mA cm −2 − E ORR , j@−3 mA cm −2 ) (E OER , j@10 mA cm −2 , the potential at a current density of 10 mA cm −2 for OER; E ORR , j@−3 mA cm −2 , the potential at a current density of −3 mA cm −2 for ORR) than other larger particle sized samples.Sun and co-workers [77] investigated, on the other hand, the impact of the CoO particle size on the ORR activity via a combined controllable hydrolysis and thermal treatment process.The promoted ORR current and the increased content of HO 2 − produced over the smallest CoO particles benefited from the increase of the interface between carbon support and CoO nanoparticles (NPs).Thus, the interface between carbon and CoO NPs could be identified as the most active site.
Besides the control of particles' size, fine-tuning of the chemical composition (e.g., Co 3+ /Co 2+ ratio) was an effective strategy to boost the electrocatalytic activity of cobalt oxide catalysts.Liu et al. [78] proposed an interesting approach to enhance the electrocatalytic activity of Co 3 O 4 nanosheets through the modulation of the inner oxygen vacancy concentration, and the Co 3+ /Co 2+ ratio.Based on the synergistic effect of the fashioned 2D nanosheets, the presence of oxygen vacancies, and the Co 3+ /Co 2+ ratio, the catalyst showed a much lower overpotential towards ORR and OER for Li-O 2 batteries.Furthermore, Zhao's group [79] reported that the ORR catalytic activity of the prepared catalysts is sensitive to the number and activity of surface-exposed Co 3+ ions that could be tailored by the morphology of cobalt oxides.

Support Effect
Cobalt oxide (Co 3 O 4 and CoO) nanoparticles are recognized as a class of non-precious catalysts with high activity, stability and durability in alkaline solution.For example, Co 3 O 4 /graphene hybrids had a remarkable ORR performance comparable to that of commercial Pt/C in alkaline, which was attributed to the synergistic catalyst-support coupling [25]; as for graphene supported 3D "sheet-on-sheet" interleaved Co 3 O 4 nanosheets (Co-S/G), the strong electron transport and charge transfer from graphene to Co 3 O 4 nanosheets significantly enhanced the ORR electrocatalytic properties of Co-S/G [80].
Bao et al. [81] proposed that the excessive ascorbic acid (AA) could form abundant negative functional groups on the surface of 3D graphene aerogel (3DG, Figure 7a), with Co 2+ ions uniformly anchored on 3DG by electrostatic or coordination interaction.The hollow Co 3 O 4 /3DG was synthesized by a direct oxidation of C@Co/3DG precursor through the Kirkendall effect, Figure 7b.The prepared Co 3 O 4 /3DG (22 wt% Co 3 O 4 ) electrocatalyst showed a positive onset potential of 0.82 V vs. RHE, and a limiting current density of 5.12 mA cm −2 (1600 rpm), Figure 7c.The rotating ring disk electrode (RRDE) method further confirmed a charge transfer pathway close to 4-electron with a production of hydrogen peroxide (HO 2 − ) of 4.27%to 14.2% in Figure 7d.
Catalysts 2018, 8, x FOR PEER REVIEW 10 of 43 Bao et al. [81] proposed that the excessive ascorbic acid (AA) could form abundant negative functional groups on the surface of 3D graphene aerogel (3DG, Figure 7a), with Co 2+ ions uniformly anchored on 3DG by electrostatic or coordination interaction.The hollow Co3O4/3DG was synthesized by a direct oxidation of C@Co/3DG precursor through the Kirkendall effect, Figure 7b.The prepared Co3O4/3DG (22 wt% Co3O4) electrocatalyst showed a positive onset potential of 0.82 V vs. RHE, and a limiting current density of 5.12 mA cm −2 (1600 rpm), Figure 7c.The rotating ring disk electrode (RRDE) method further confirmed a charge transfer pathway close to 4-electron with a production of hydrogen peroxide (HO2 − ) of 4.27%to 14.2% in Figure 7d.Wang et al. [82] developed a supramolecular gel-assisted method to manufacture N-doped carbon shell coated Co@CoO nanoparticles on carbon Vulcan XC-72 (Co@CoO@N-C/C) for ORR.Herein, melamine not only acted as a chelating agent interacting with Co 2+ , but also as a nitrogen source to dope at high-temperature pyrolysis treatment.Due to the synergistic effect, the doubleshelled Co@CoO@N-C/C nanoparticles displayed the excellent ORR performance with Eonset = 0.92 V vs. RHE and E1/2 = 0.81 V vs. RHE, comparable with the commercial Pt/C in 0.1 M KOH.

Synthesis Strategy
Layered double hydroxides (LDHs), a class of two-dimensional (2D) layered material, consist of host sheets with divalent (M II ) and trivalent (M III ) metal cations coordinated to hydroxide anions, and the guest anions in the interlayer regions.This kind of structure has attracted interest in various energy conversion systems [31].Generally, hydroxides have a good affinity to aqueous electrolytes and their layered structures offer an enlarged surface area and improved dispersion degree based on the confinement effect.This latter property favors the accessibility of catalytic sites.Nevertheless, the positively charged host sheets in LDHs favor the oxygen adsorption and its oxygen reduction.Currently, Co-containing LDHs, as ORR catalysts, have been the object of intense research [83][84][85].For instance, Li et al. [85] investigated the interaction of LDHs with RGO toward the ORR via a fourelectron transfer pathway and found that the Co 2+ in the LDHs, as active sites, catalyzed the disproportionation of the peroxide species to form H2O and O2.Additionally, the RGO support increased the electrical conductivity.
Apart from the direct preparation of the LDHs precursor, the materials derived from LDHs, after thermal treatment, showed similar promising electrocatalytic activity in alkaline solution.For example, Co3Mn-CO3-LDH/RGO precursor was calcined to produce reduced graphene oxide supported Co-Mn oxides under nitrogen atmosphere with enhanced catalytic performance (Eonset = 0.95 V vs. RHE, E1/2 = 0.76 V vs. RHE, and jlimit = 4.2 mA cm −2 at 0.2 V vs. RHE, 1600 rpm) [84].Similarly, Co3O4/Co2MnO4 composites, resulting from CoMn-LDHs precursor, displayed excellent bifunctional activities for ORR and OER with ΔE = 1.09V. Wang et al. [82] developed a supramolecular gel-assisted method to manufacture N-doped carbon shell coated Co@CoO nanoparticles on carbon Vulcan XC-72 (Co@CoO@N-C/C) for ORR.Herein, melamine not only acted as a chelating agent interacting with Co 2+ , but also as a nitrogen source to dope at high-temperature pyrolysis treatment.Due to the synergistic effect, the double-shelled Co@CoO@N-C/C nanoparticles displayed the excellent ORR performance with E onset = 0.92 V vs. RHE and E 1/2 = 0.81 V vs. RHE, comparable with the commercial Pt/C in 0.1 M KOH.

Synthesis Strategy
Layered double hydroxides (LDHs), a class of two-dimensional (2D) layered material, consist of host sheets with divalent (M II ) and trivalent (M III ) metal cations coordinated to hydroxide anions, and the guest anions in the interlayer regions.This kind of structure has attracted interest in various energy conversion systems [31].Generally, hydroxides have a good affinity to aqueous electrolytes and their layered structures offer an enlarged surface area and improved dispersion degree based on the confinement effect.This latter property favors the accessibility of catalytic sites.Nevertheless, the positively charged host sheets in LDHs favor the oxygen adsorption and its oxygen reduction.Currently, Co-containing LDHs, as ORR catalysts, have been the object of intense research [83][84][85].For instance, Li et al. [85] investigated the interaction of LDHs with RGO toward the ORR via a four-electron transfer pathway and found that the Co 2+ in the LDHs, as active sites, catalyzed the disproportionation of the peroxide species to form H 2 O and O 2 .Additionally, the RGO support increased the electrical conductivity.
Apart from the direct preparation of the LDHs precursor, the materials derived from LDHs, after thermal treatment, showed similar promising electrocatalytic activity in alkaline solution.For example, Co 3 Mn-CO 3 -LDH/RGO precursor was calcined to produce reduced graphene oxide supported Co-Mn oxides under nitrogen atmosphere with enhanced catalytic performance (E onset = 0.95 V vs. RHE, E 1/2 = 0.76 V vs. RHE, and j limit = 4.2 mA cm −2 at 0.2 V vs. RHE, 1600 rpm) [84].Similarly, Co 3 O 4 /Co 2 MnO 4 composites, resulting from CoMn-LDHs precursor, displayed excellent bifunctional activities for ORR and OER with ∆E = 1.09V.
Herein, the activity of the material was attributed to the large specific surface area and well-dispersed heterogeneous structure [83].Xu et al. [86], on the other hand, fabricated a Co/CoO/CoFe 2 O 4 as ORR electrocatalyst based on the utilization of CoFe-LDHs as precursor by separate nucleation and aging steps (SNAS).The same group later reported Co@N-CNTs obtained by calcination of melamine/CoAl-LDH mixture, cf.Herein, the activity of the material was attributed to the large specific surface area and welldispersed heterogeneous structure [83].Xu et al. [86], on the other hand, fabricated a Co/CoO/CoFe2O4 as ORR electrocatalyst based on the utilization of CoFe-LDHs as precursor by separate nucleation and aging steps (SNAS).The same group later reported Co@N-CNTs obtained by calcination of melamine/CoAl-LDH mixture, cf.

Co-Nx Active center
Besides the aforementioned Co-based electrocatalysts, Co-Nx/C has also been considered as another potential candidate to substitute Pt for ORR.In 1964, Jasinski [87] for the first time found that cobalt-phthalocyanine (CoPc) activated the ORR process in alkaline electrolyte.However, the catalytic sites in macrocyclic cathode catalysts for ORR are still controversial.Apropos Co-Nx/C catalysts, various type of active sites were proposed, including Co-N4/C and Co-N2/C [88][89][90][91][92], NxCy [93], pyridinic N [91,94], and graphitic N [95,96].For example, Kiefer et al. [97] explained the origin and mechanism of ORR on Co-Nx (x = 2, 4) based on self-assembled carbon supported electrocatalysts in alkaline and acidic media via first-principle DFT calculations.The graphitic Co-N4 defect was energetically more favorable than the graphitic Co-N2 defects, and the former was predicted to be the dominant in-plane graphitic defect in Co-Nx/C electrocatalysts.
Nevertheless, Li et al. [98] believed that the dominant reactive sites for cobalt single atoms (Co-SAs) in Co-SAs/N-C could be postulated as Co-N4 and Co-N2 moieties, and Co-N2 species had a stronger interaction with peroxide than Co-N4, promoting the ORR four-electron reduction process.Tang et al. [99] considered that both of Co-Nx and pyri-N species were very important and their coupling effect (Co-pyri-N) was of paramount importance in the high electrocatalytic activity due to the high lying HOMO energy levels.Besides, Liao et al. [100] proposed that doped transition metals could act, on one hand, as a catalyst for the formation of stable active sites in the pyrolysis process, and on the other hand, the residual metal compounds could serve as active sites.In fact, the ORR catalytic performance improvement of transition metals might be the result of joint effects: (i) the overall N content/active N content; (ii) metal residue; and (iii) the surface area and pore structures.Metal-free carbon structure was originally suggested as active sites by Wiesener [101].Yet, Masa et al. [102] argued for the concept of a metal-free catalyst.Indeed, truly metal-free nitrogen-doped carbon demonstrated much lower ORR activity and reduced O2 through a two-electron pathway in acidic solution, so that undetectable metal residues may play a crucial role for the ORR.Besides the aforementioned Co-based electrocatalysts, Co-N x /C has also been considered as another potential candidate to substitute Pt for ORR.In 1964, Jasinski [87] for the first time found that cobalt-phthalocyanine (CoPc) activated the ORR process in alkaline electrolyte.However, the catalytic sites in macrocyclic cathode catalysts for ORR are still controversial.Apropos Co-N x /C catalysts, various type of active sites were proposed, including Co-N 4 /C and Co-N 2 /C [88][89][90][91][92], N x C y [93], pyridinic N [91,94], and graphitic N [95,96].For example, Kiefer et al. [97] explained the origin and mechanism of ORR on Co-N x (x = 2, 4) based on self-assembled carbon supported electrocatalysts in alkaline and acidic media via first-principle DFT calculations.The graphitic Co-N 4 defect was energetically more favorable than the graphitic Co-N 2 defects, and the former was predicted to be the dominant in-plane graphitic defect in Co-N x /C electrocatalysts.
Nevertheless, Li et al. [98] believed that the dominant reactive sites for cobalt single atoms (Co-SAs) in Co-SAs/N-C could be postulated as Co-N 4 and Co-N 2 moieties, and Co-N 2 species had a stronger interaction with peroxide than Co-N 4 , promoting the ORR four-electron reduction process.Tang et al. [99] considered that both of Co-N x and pyri-N species were very important and their coupling effect (Co-pyri-N) was of paramount importance in the high electrocatalytic activity due to the high lying HOMO energy levels.Besides, Liao et al. [100] proposed that doped transition metals could act, on one hand, as a catalyst for the formation of stable active sites in the pyrolysis process, and on the other hand, the residual metal compounds could serve as active sites.In fact, the ORR catalytic performance improvement of transition metals might be the result of joint effects: (i) the overall N content/active N content; (ii) metal residue; and (iii) the surface area and pore structures.Metal-free carbon structure was originally suggested as active sites by Wiesener [101].Yet, Masa et al. [102] argued for the concept of a metal-free catalyst.Indeed, truly metal-free nitrogen-doped carbon demonstrated much lower ORR activity and reduced O 2 through a two-electron pathway in acidic solution, so that undetectable metal residues may play a crucial role for the ORR.

Co-N x Synthesis Strategy
Generally, the electrocatalytic activity and stability of Co-N x /C, or nitrogen-modified carbon supports (NCSs) or templates materials, basically rely on the morphology, pore structure, dispersion of the active sites, and nitrogen species, which are up to the crucial synthetic route.Traditional methods involving the pyrolysis of carbon-supported cobalt N 4 -macrocycles, e.g., phthalocyanine (Pc), tetra-azaannulene (TAA), tetra-phenylpophyrin (TPP) and tetra-methoxyphenlyporphyrin (TMPP), at temperatures between 550 • C and 800 • C preserved or created Co-N x active sites, although the macrocyclic structure of the complex was partially or completely destroyed [103][104][105][106]. Above 800 • C, the metal-nitrogen species are known to decompose with a concomitant decrease in the ORR performance.For example, Popov et al. [107] found, via EXAFS, that the content of Co-N species decreased when the heat treatment exceeded 800 • C. Yet, Dodelet's group [108] proposed that Co metal and/or CoPc fragments containing Co could be responsible for the catalytic activity of CoPc/XC-72 pyrolyzed at 600 or 700 • C, a treatment where the maximum of the electrocatalytic activity was obtained [109].Jahnke et al. [110] improved the stability as well as the electrochemical activity of transition metal porphyrins deposited on carbon support by a pyrolytic treatment step in the range of 450 to 900 • C, in an inert atmosphere.Qiao et al. [35] synthesized carbon-supported cobalt catalysts, namely, Py-CoPc/C, heat-treated at 600-900 • C, and investigated its heat-treatment effect onto the ORR activity in alkaline electrolyte.The catalysts that annealed at 700 • C exhibited the best activity towards ORR in 0.1 M KOH.Such a phenomenon was related with Co-N x /C, pyridinic-N and graphitic-N active sites.Shan et al. [111] fabricated novel mesoporous Co-N x -C, by a nanocasting-pyrolysis method, using Co-phenanthroline as the only precursor, permitting that abundant Co-N x moieties remained embedded in the graphitic framework during pyrolysis.
Recently, most Co-N x /C catalysts were fabricated by pyrolysis treatment of Co salts mixed with carbon support and nitrogen-rich precursor [100].Zelenay et al. [88] used polyaniline (PANI) as a nitrogen source for high-temperature synthesis of catalysts incorporating iron or cobalt centers.The most active catalysts: FeCo/N/C, showed a very positive onset potential of ~0.93 V with a long-term stability test of 700 h at a fuel cell voltage of 0.4 V in 0.5 M H 2 SO 4 .Zhang et al. [112] demonstrated the direct utilization of the intrinsic structural defects in nanocarbon to generate atomically dispersed Co-N x -C active sites via defect engineering.The as-obtained Co/N/O tri-doped graphene mesh (denoted as NGM-Co) were prepared via the carbonization of a mechanical mixture of gelatinized amylopectin, melamine, cobalt nitrate, and in situ generated Mg(OH) 2 nanoflakes.The remarkable bifunctional electroactivity for ORR and OER in alkaline medium of NGM-Co catalyst was ascribed to Co-N x -C moieties, nitrogen-doping, oxygen functional groups, and topological defects.Miao et al. [113] reported a noble-free Co-N-C catalyst, derived from cobalt-phenanthroline complexes on CMK-3 under heat-treatment.By careful examination of the Co-N-C catalyst with sub-Ångström-resolution aberration-corrected scanning transmission electron microscopy (HAADF-STEM), the authors suggested that the Co single atoms bonded to N within the graphitic sheets served as the active sites.Wang's group [114] developed a new type of Co-N/C catalysts that contained two forms of active components, namely, coordinating cobalt moieties (CoC x N y or CoN x ) and Co nanoparticles encapsulated in mesoporous N-doped carbon hollow spheres (Co-N-mC) by pyrolyzing the polystyrene@polydopamine-Co (PS/PDA-Co) precursor.The Co-N-mC catalysts revealed striking ORR performance, comparable with commercial Pt/C, with onset potential of 0.94 V vs. RHE, half-wave potential of 0.851 V vs. RHE, and a Tafel slope of 45 mV dec −1 in 0.1 M KOH.Similarly, Tsiakaras et al. [115] designed and fabricated a 3D hollow carbon spheres (HCS) with co-doping of cobalt and nitrogen, using dopamine and poly-methyl-methacrylate (PMMA) as a template and a vacuum-assisted impregnation method, Figure 9a.The Co-N@HCS catalyst with a large specific surface area (347.3 m 2 g −1 ) displayed excellent catalytic activity for both ORR and OER with a ∆E (∆E = E OER , j@10 mA cm −2 − E 1/2, ORR ) of 0.856 V, much lower than those of the N@HCS (1.233 V) and the benchmark Pt/C catalysts (1.044 V).Besides, more recently, some new synthesis strategies have been proposed to precisely control and fabricate the Co-Nx catalytic materials, under the confinement effect, with well-engineered nanostructure derived from metal-organic framework precursors (MOFs).The Co-Nx/C catalysts synthesized by a simple pyrolysis of MOF precursor, inherited the large surface area and satisfactory porosity of MOFs, which led to dense active sites on the surface of materials.Feng's group [28] fabricated the Co/CoNx/N-CNT/C electrocatalysts by heat treatment of MOF (Co-mela-BDC) at different temperatures under N2 atmosphere.The Co/CoNx/N-CNT/C catalyst obtained at 800 °C contained N-doped carbon nanotubes, which were generated by the catalysis of cobalt species.Owing to the synergistic effect between Co-Nx-C and NCNTs, the Co/CoNx/N-CNT/C composite boosted the much higher ORR performance.Aijaz et al. [116] reported highly active bifunctional electrocatalysts for oxygen electrodes containing core-shell Co@Co3O4 nanoparticles embedded in CNT-grafted N-doped carbon-polyhedra from the pyrolysis of ZIF-67, involved in the sequential reduction and oxidation steps.The use of ZIF-67, as sacrificial precursor, was advantageous to build a core-shell nanostructured polyhedral with large surface area, and high dispersion of Co-Nx and Co3O4-Nx active sites.Furthermore, Zheng et al. [117] developed a bimetal (Cu and Co) embedded N-doped carbon framework, using the in situ growth of ZIF-67 polyhedrons on Cu(OH)2 nanowires, followed by pyrolysis treatment, Figure 10.The pyrolytic decomposition proceeded successively for Cu(OH)2 and ZIF-67, and thus the hierarchical porosity of ZIF-67 enabled the confinement of Cu nanocrystals and particles' size.The authors proposed that the existence of Cu ions not only provided extra active sites, but also led to an increased nitrogen content in the carbon frameworks via Cu-N coordination, optimized porous structure and large specific surface area, favorable to enhance the ORR electrocatalytic activity, Figure 10b.The CuCo@NC material showed an outstanding ORR activity, with much more positive Eonset = 0.96 V and E1/2 = 0.88 V, comparable to commercial 30% Pt/C (1.04 V and 0.84 V, for Eonset, and E1/2, respectively).Besides, more recently, some new synthesis strategies have been proposed to precisely control and fabricate the Co-N x catalytic materials, under the confinement effect, with well-engineered nanostructure derived from metal-organic framework precursors (MOFs).The Co-N x /C catalysts synthesized by a simple pyrolysis of MOF precursor, inherited the large surface area and satisfactory porosity of MOFs, which led to dense active sites on the surface of materials.Feng's group [28] fabricated the Co/CoN x /N-CNT/C electrocatalysts by heat treatment of MOF (Co-mela-BDC) at different temperatures under N 2 atmosphere.The Co/CoN x /N-CNT/C catalyst obtained at 800 • C contained N-doped carbon nanotubes, which were generated by the catalysis of cobalt species.Owing to the synergistic effect between Co-N x -C and NCNTs, the Co/CoN x /N-CNT/C composite boosted the much higher ORR performance.Aijaz et al. [116] reported highly active bifunctional electrocatalysts for oxygen electrodes containing core-shell Co@Co 3 O 4 nanoparticles embedded in CNT-grafted N-doped carbon-polyhedra from the pyrolysis of ZIF-67, involved in the sequential reduction and oxidation steps.The use of ZIF-67, as sacrificial precursor, was advantageous to build a core-shell nanostructured polyhedral with large surface area, and high dispersion of Co-N x and Co 3 O 4 -N x active sites.Furthermore, Zheng et al. [117] developed a bimetal (Cu and Co) embedded N-doped carbon framework, using the in situ growth of ZIF-67 polyhedrons on Cu(OH) 2 nanowires, followed by pyrolysis treatment, Figure 10.The pyrolytic decomposition proceeded successively for Cu(OH) 2 and ZIF-67, and thus the hierarchical porosity of ZIF-67 enabled the confinement of Cu nanocrystals and particles' size.The authors proposed that the existence of Cu ions not only provided extra active sites, but also led to an increased nitrogen content in the carbon frameworks via Cu-N coordination, optimized porous structure and large specific surface area, favorable to enhance the ORR electrocatalytic activity, Figure 10b.The CuCo@NC material showed an outstanding ORR activity, with much more positive E onset = 0.96 V and E 1/2 = 0.88 V, comparable to commercial 30% Pt/C (1.04 V and 0.84 V, for E onset , and E 1/2 , respectively).
extra active sites, but also led to an increased nitrogen content in the carbon frameworks via Cu-N coordination, optimized porous structure and large specific surface area, favorable to enhance the ORR electrocatalytic activity, Figure 10b.The CuCo@NC material showed an outstanding ORR activity, with much more positive Eonset = 0.96 V and E1/2 = 0.88 V, comparable to commercial 30% Pt/C (1.04 V and 0.84 V, for Eonset, and E1/2, respectively).Because of some interesting properties, such as, tunable chemical composition, permanent porosity, and a high thermal/chemical stability, the porous covalent networks (PCNs), also known as covalent organic frameworks (COFs), are chemical precursors of interest for electrocatalysis.In this context, Bu et al. [118] proved that the porphyrinic conjugated network PCN-FeCo/C, a carbonized product of heterometalloporphyrinic PCN-FeCo at 800 • C, showed a spectacular ORR activity and electrochemical stability in alkaline and acid electrolytes, Figure 11.The PCN-FeCo/C electrode displayed a very positive onset potential (1.00 V vs. RHE), and a half-wave potential of 0.85 V vs. RHE comparable to that of Pt/C (0.84 V vs. RHE) in 0.1 M KOH.Again, the binary PCN-FeCo/C catalyst was found to give the highest activity, i.e., the most positive E onset = 0.90 V vs. RHE, and E 1/2 = 0.76 V vs. RHE in 0.1 M HClO 4 solution.The prominent performance of PCN-FeCo/C was attributed to the high homogeneity of active components derived from ordered distribution of Fe and Co covalent network, i.e., a generated hierarchical porosity.displayed a very positive onset potential (1.00 V vs. RHE), and a half-wave potential of 0.85 V vs. RHE comparable to that of Pt/C (0.84 V vs. RHE) in 0.1 M KOH.Again, the binary PCN-FeCo/C catalyst was found to give the highest activity, i.e., the most positive Eonset = 0.90 V vs. RHE, and E1/2 = 0.76 V vs. RHE in 0.1 M HClO4 solution.The prominent performance of PCN-FeCo/C was attributed to the high homogeneity of active components derived from ordered distribution of Fe and Co covalent network, i.e., a generated hierarchical porosity.

Mechanistic Approach of OER
OER kinetics are also a multi-electron charge transfer process in acid and alkaline media.The kinetic parameters such as overpotential (η), exchange current density (i), Tafel slope (b), turnover frequency (TOF), and so on, are employed to evaluate the OER performance of electrocatalytic materials.Particularly, the overpotential at a current density of 10 mA cm −2 is a crucial criterion to examine the OER performance (indicated as η @10 ).These parameters play a key role for obtaining an insight into the mechanism of this electrocatalytic process.In general, the electrochemical reaction that occurs at the anode (OER) in acid, and alkaline electrolytes are: Alkaline medium: Various research groups have proposed possible OER mechanisms in acid (Equations ( 9)-( 13)) and alkaline medium (Equations ( 14)-( 18)).Most of the proposed mechanisms involve MOH and MO intermediates.The diagram in Figure 12 displays two different routes to form oxygen from a MO intermediate.One, the green route, via the direct combination of 2MO to produce O 2(g) (Equation ( 11)), and that involving the generation of the MOOH intermediate (Equations ( 12) and ( 17)) which subsequently decomposes, black route, to O 2(g) (Equations ( 13) and ( 18)).During the heterogeneous OER process, all the bonding interactions (M-O) within the intermediates (MOH, MO and MOOH) are crucial to determining the overall electrocatalytic performance.
Acid  Until now, the Ni-and Co-based materials (both free support and supported on, e.g., carbon) have been intensively investigated as promising non-precious OER electrocatalysts.The catalysts derived from cobalt metal centers can activate the OER in alkaline medium rather than in acid medium.Particularly for CoOx and CoOOH, the nature of their OER activities, stabilities in alkaline solution and OER mechanism have been thoroughly investigated [131][132][133].For example, Mattioli group [131] provided insightful information into the pathways towards oxygen evolution of a cobaltbased catalyst (CoCat) by performing ab initio DFT + U molecular dynamics calculations of cluster models in water solution.The reaction pathways of CoCat were proposed as follows: (1) the fast H + mobility at the CoCat/water interface is responsible for an optimal distribution of terminal Co(III)- Until now, the Ni-and Co-based materials (both free support and supported on, e.g., carbon) have been intensively investigated as promising non-precious OER electrocatalysts.The catalysts derived from cobalt metal centers can activate the OER in alkaline medium rather than in acid medium.Particularly for CoO x and CoOOH, the nature of their OER activities, stabilities in alkaline solution and OER mechanism have been thoroughly investigated [131][132][133].For example, Mattioli group [131] provided insightful information into the pathways towards oxygen evolution of a cobalt-based catalyst (CoCat) by performing ab initio DFT + U molecular dynamics calculations of cluster models in water solution.The reaction pathways of CoCat were proposed as follows: (1) the fast H + mobility at the CoCat/water interface is responsible for an optimal distribution of terminal Co(III)-OH groups, as sites of injected holes.These sites are preferred in the case of complete cubane units; (2) the oxygen evolution process starts with the release of a proton from one of such terminal Co-OH sites, a process favored by the proton-acceptor species in solution, leading to the formation of a Co(IV)=O • oxyl radical; (3) the coupling of Co=O radicals with germinal (i.e., bonded to the same Co atom) Co-OH or Co-µO-Co groups to form hydroperoxo and peroxo intermediates.

Synthesis Strategy
One of the attractive electrocatalysts surface engineering strategies, e.g., etching and edging, could greatly improve the catalytic performance.Dai et al. [19], for the first time, developed an novel bifunctional oxygen electrode catalysts by using NH 3 -plasma to simultaneously etch and dope the cobalt sulfides-graphene hybrid (N-Co 9 S 8 /G).NH 3 -plasma treatment, not only could induce the N doping into both Co 9 S 8 and graphene to enhance the activity, but also realized etching on the surface to expose more active sites for electrocatalysis.The N-Co 9 S 8 /G catalyst exhibited a low onset potential at ca. 1.51 V vs. RHE and a small Tafel slope of 82.7 mV dec −1 .Notably, the required overpotential of N-Co 9 S 8 /G catalyst to reach the current density of 10 mA cm −2 was only 0.409 V in 0.1 M KOH.Additionally, Xie's group [134] proposed that reducing the thickness of bulk CoSe 2 into the atomic scale, rather than doping or hybridizing, was inclined to form a great deal of exposed active sites e.g., V Co " vacancies, which could effectively catalyze the OER process evidenced by the positron annihilation spectrometry, XAFS (X-ray Absorption Fine Structure) spectra and DFT calculations.The ultrathin CoSe 2 nanosheets with rich V Co " vacancies manifested an OER overpotential of 0.32 V at 10 mA cm −2 in alkaline electrolyte (pH = 13) much less than that of the bulk CoSe 2 .

Support Effect
Clear evidence of the strong metal-support interaction (SMSI) was given by Gao et al. [135] with synthesized CoSe 2 nanobelts on N-doped reduced graphene oxide (RGO) sheets.This system showed an exceptional OER activity and stability in alkaline environment, with a Tafel slope of 40 mV dec −1 and η @10 (the overpotential required to achieve the current density of 10 mA cm −2 ) of 0.366 V.The authors concluded that the high performance is dependent on the interaction between N-doped carbon domains and CoSe 2 nanobelts.Similarly, Liao et al. [121] embedded Co 1-x S hollow nanospheres in N and S co-doped graphene holes to create an efficient bifunctional catalysts (Co 1-x S/N-S-G) with hierarchical meso-macroporous structures for ORR and OER.The Co 1-x S/N-S-G material with a large specific surface area (390.6 m 2 g −1 ), showed a small overpotential of 371 mV for 10 mA cm −2 in 0.1 KOH, and the ∆E value is 0.706 V, which was much smaller than those of many reported non-precious metal catalysts.The investigated results demonstrated that the excellent bifunctional performance was mainly attributed to a synergistic effect of the multiple active sites consisting of Co 1-x S, N and S dopants, and possible Co-N-C sites.Interestingly, Guo et al. [136] used CoSe 2 nanosheets as support to grow Co 2 B at room temperature.The resulting Co 2 B/CoSe 2 hybrid catalysts showed η @10 values for OER and HER in alkaline of 0.32 V, and 0.30 V, respectively.Apparently, CoSe 2 nanosheets supplied nucleation sites for Co 2 B, as well as high electrical conductivity that promoted a high stability through water splitting reactions in alkaline medium.

Mechanism of Cobalt Oxides
Cobalt (II) commonly undergoes the oxidation (Co II → Co III ) under an anodic potential prior to the OER in an aqueous solution, forming a layered oxidic cobalt species [137,138].Some researchers pointed out that Co IV species were generated on the outermost surface of the electrode [137,139].So that the catalytic site formed on the Co 3 O 4 electrode was the quasi-reversible redox couple Co III /Co IV that accelerated the one-step or two-step OER [131,133,140,141].In order to investigate the role of the peroxo process in the oxygen evolution reaction, Fu et al. [142]

Chemical Composition
As mentioned above, the electrocatalytic performance of Co3O4 nanoparticles mainly depends on the surface area, the oxidation charge of the cobalt atoms, and the oxygen vacancies.Hence, a reasonable tuning of the surface electronic states of undoped Co3O4 can provide more electrochemically active sites to favor the OER.The preparation of mesoporous Co3O4 nanowires (Co3O4 NWs) by Zheng et al. [143], through a facile NaBH4 reduction method led to seven-fold activity enhancement of OER, as compared to pristine Co3O4, Figure 14.As shown in Figure 14a, the peak current density observed in the cyclic voltammetry curves increased dramatically, after the chemical reduction process, signifying the existence of more active sites as a result of the oxygen vacancies, confirmed by DFT calculations.The increased Co 4+ /Co 3+ redox peaks (1.4-1.5 V) was ascribed to the formation of [Co 4+ -O] intermediate, involved in the turnover-limiting chemical step of oxygen evolution.The onset potential of the reduced Co3O4 NWs was ca.1.52 V vs. RHE, i.e., ca.50 mV and 100 mV more negative than pristine Co3O4 NWs and Pt/C catalyst, respectively, Figure 14b.Besides reduction post-treatment, Xia et al. [144] fabricated 3D ordered mesoporous cubic Co3O4 implementing hard-templating strategies.X-ray photoelectron spectroscopy (XPS) analysis revealed that the molar surface ratio Co III+ /Co II+ of ordered mesoporous Co3O4 was much lower than that of bulk-Co, suggesting more surface oxygen vacancies on the former, which benefited the adsorption

Synthesis Strategy
The synthesis of graphene-Co3O4 (G-Co3O4) composite having a unique sandwich-architecture was reported by Zhao et al. [145].The large amount of tiny Co3O4 nanocrystals, uniformly dispersed on both sides of graphene sheets, allowed for a favorable electron transfer kinetics.The onset potential of G-Co3O4 was 0.406 V vs. Ag/AgCl in 1 M KOH, and 0.858 V vs. Ag/AgCl in neutral phosphate buffer solution (PBS).The overpotential at a current density of 10 mA cm −2 (η@10) was 313 mV in 1 M KOH, and 498 mV in PBS, respectively.Kim et al. [146], on the other hand, used dextrose as chemical source to obtain mesoporous carbon, and urea together with CoCl2•6H2O in a hydrothermal treatment to obtain carbon-cobalt oxide-nanorods (C-Co3O4-NRs).This latter provided an overpotential at a current density of 10 mA cm −2 (η@10) of 415 mV, a value much lower than that of carbon free Co3O4 nanorods.The OER activity of the C-Co3O4-NRs electrode was significantly increased with a low onset potential of 356 mV and Tafel slope of 53 mV dec −1 .
Additionally, materials with high conductivity and mobility, e.g., Co foil, Ni foam and carbon fiber paper, were employed as support grown on non-precious metal electrocatalysts to facilitate the electrolyte diffusion, drive off the as-formed gas bubbles from the electrode surface during the oxygen evolution process, favoring the kinetics, and the chemical stability.In this connection, a simple and reasonable method to synthesize self-supported Co3O4 nanocrystal/carbon fiber paper via thermal decomposition of the [Co(NH3)n] 2+ -oleic acid complex and subsequent spray deposition was done by Fu et al. [147].The Co3O4 NCs with a loading of 0.35 mg cm −2 showed a current density of

Synthesis Strategy
The synthesis of graphene-Co 3 O 4 (G-Co 3 O 4 ) composite having a unique sandwich-architecture was reported by Zhao et al. [145].The large amount of tiny Co 3 O 4 nanocrystals, uniformly dispersed on both sides of graphene sheets, allowed for a favorable electron transfer kinetics.The onset potential of G-Co 3 O 4 was 0.406 V vs. Ag/AgCl in 1 M KOH, and 0.858 V vs. Ag/AgCl in neutral phosphate buffer solution (PBS).The overpotential at a current density of 10 mA cm −2 (η @10 ) was 313 mV in 1 M KOH, and 498 mV in PBS, respectively.Kim et al. [146], on the other hand, used dextrose as chemical source to obtain mesoporous carbon, and urea together with CoCl 2 •6H 2 O in a hydrothermal treatment to obtain carbon-cobalt oxide-nanorods (C-Co 3 O 4 -NRs).This latter provided an overpotential at a current density of 10 mA cm −2 (η @10 ) of 415 mV, a value much lower than that of carbon free Co 3 O 4 nanorods.The OER activity of the C-Co 3 O 4 -NRs electrode was significantly increased with a low onset potential of 356 mV and Tafel slope of 53 mV dec −1 .
Additionally, materials with high conductivity and mobility, e.g., Co foil, Ni foam and carbon fiber paper, were employed as support grown on non-precious metal electrocatalysts to facilitate the electrolyte diffusion, drive off the as-formed gas bubbles from the electrode surface during the oxygen evolution process, favoring the kinetics, and the chemical stability.In this connection, a simple and reasonable method to synthesize self-supported Co 3 O 4 nanocrystal/carbon fiber paper via thermal decomposition of the [Co(NH 3 ) n ] 2+ -oleic acid complex and subsequent spray deposition was done by Fu et al. [147].The Co 3 O 4 NCs with a loading of 0.35 mg cm −2 showed a current density of 16.5 mA cm −2 at η @10 of 350 mV in 1 M KOH.With the same perspective, Wei et al. [148] reported the synthesis of Co

Oxygen Evolution on Cobalt-Based Layered Double-Hydroxides Catalysts
The use of LDH materials for OER has been recently promoted, see Table 2. Cobalt-containing LDHs composed of edge-sharing octahedral MO6 layers, which are OER active sites, were successfully synthesized and showed an unusual catalytic activity and stability [149][150][151].Li et al. [15] presented a strategy for a direct nucleation and growth of CoMn-LDH material on modified multiwall carbon nanotubes (MWCNTs) with three-dimensional hierarchical configuration.This approach afforded an intimate chemical and electrical coupling between LDH nanoplates and carbon materials, to allow for a rapid electron charge transfer from the active sites to the support.By tuning Co/Mn ratio, the Co5Mn-LDH/MWCNT activated the reaction at a low overpotential of η@10 ~300 mV in 1 M KOH.Ren et al. [152] designed and synthesized randomly cross-linked CoNi-LDH/CoO via an in situ reduction and interface-directed assembly in air.Owing to the orbital hybridization between metal 3d and O 2p orbitals, and electron transfer between metal atoms through Ni-O-Co,

Oxygen Evolution on Cobalt-Based Layered Double-Hydroxides Catalysts
The use of LDH materials for OER has been recently promoted, see Table 2. Cobalt-containing LDHs composed of edge-sharing octahedral MO 6 layers, which are OER active sites, were successfully synthesized and showed an unusual catalytic activity and stability [149][150][151].Li et al. [15] presented a strategy for a direct nucleation and growth of CoMn-LDH material on modified multiwall carbon nanotubes (MWCNTs) with three-dimensional hierarchical configuration.This approach afforded an intimate chemical and electrical coupling between LDH nanoplates and carbon materials, to allow for a rapid electron charge transfer from the active sites to the support.By tuning Co/Mn ratio, the Co 5 Mn-LDH/MWCNT activated the reaction at a low overpotential of η @10 ~300 mV in 1 M KOH.Ren et al. [152] designed and synthesized randomly cross-linked CoNi-LDH/CoO via an in situ reduction and interface-directed assembly in air.Owing to the orbital hybridization between metal 3d and O 2p orbitals, and electron transfer between metal atoms through Ni-O-Co, some Co and Ni atoms in the CoNi LDH underwent a high +3 valence.For transition metals, highly oxidized redox couples, e.g., Co 4+/3+ and Ni 4+/3+ were considered as active centers for OER [153].
The specific activity of the material for the target reaction is usually highly dependent on the chemical composition and electronic structure.The higher conductivity induced by modifying the electronic structure of Co is applicable for the electrochemical catalysis, such as de-lithiated hexagonal LiCo 2 for OER, and spinel LiCo 2 for ORR [153].For the OER, a small amount of Fe doping was effective for enhancing the OER activities of Ni hydroxides or oxides, possibly due to the enhanced structure disorder and conductivity.Inspired by this, Sun et al. [154] systematically investigated the ORR and OER activities of ternary NiCoFe-LDHs and observed that a peroxidation treatment of NiCoFe-LDHs led to obtain o-NiCoFe-LDHs that significantly enhanced the corresponding bifunctional performance of (ORR/OER), as shown in Figure 16a.The XPS results and Zeta potential measurements evidenced that Co 2+ was partially oxidized to a higher Co 3+ state, while negligible chemical state change of Ni and Fe elements was observed in o-NiCoFe-LDHs.The partial conversion of Co 2+ to Co 3+ state stimulated the charge transfer to the catalyst surface, which could lead to the enhancement of the conductivity.In the Figure 16b, in 6 M KOH medium, the o-NiCoFe-LDHs afforded a high ORR current density of −20 mA cm −2 at a required potential of 0.65 V vs. RHE.Moreover, there was a negligible ORR current density degradation of o-NiCoFe-LDHs for 40 h.The higher conductivity induced from the higher valence state of Co, might enhance the electrophilicity of the adsorbed O and thus facilitating the reaction of an OH − anion with an adsorbed O atom on the catalytic active sites to form adsorbed -OOH species, which was considered as the rate-limiting step for OER [138,155].It is fascinating to design and build a bifunctional oxygen electrode catalyst based on the combination of highly OER-active Ni-Fe hydroxides or oxides, and highly ORR-active Co, Fe-based compounds.Feng's group [33] designed and obtained a bifunctional electrocatalyst based on NiFeOx/Co-Ny-C by a simple calcination of Ni2Fe-CoPcTs-LDH precursor based on the intercalation of cobalt phthalocyanine tetrasulfonate (CoPcTs) into Ni2Fe-LDHs under N2 atmosphere at 600 °C.Moreover, the surface area of lamellar architecture materials can be further enlarged by swelling and exfoliating into individually single layers by mechanical, chemical or electrochemical means [156][157][158][159].The exfoliated single-layered nanosheets revealed significantly higher oxygen evolution activity than the corresponding bulk LDH in alkaline conditions.Hu et al. [159] inferred that the higher OER activities of exfoliated LDHs (CoCo, NiCo, and NiFe-LDH) were mainly attributed to the increase in the number of active edge sites and to higher electronic conductivity.Analogously, Jin et al. [160] selected NiCo LDH as a representative material to demonstrate the concept of the amplified influence of exfoliation using a newly developed high-temperature high-pressure hydrothermal continuous flow reactor (HCFR), see Figure 17.The major findings were presented as follows: (1) the utilized HCFR technology effectively maintain the supersaturation to control the morphology and size of the product; (2) the exfoliation not only resulted in thinner layers with reduced size, but it was also caused by a change in the electronic structure; (3) the increase in the number of edge sites to activate OER; and (4) the increase in the electrochemical active surface area (ECSA) upon the exfoliation was not the only important factor that led to the enhanced OER performance.This work provided a general strategy to enhance the electrocatalytic performance of layered materials by chemical exfoliation.Moreover, the surface area of lamellar architecture materials can be further enlarged by swelling and exfoliating into individually single layers by mechanical, chemical or electrochemical means [156][157][158][159].The exfoliated single-layered nanosheets revealed significantly higher oxygen evolution activity than the corresponding bulk LDH in alkaline conditions.Hu et al. [159] inferred that the higher OER activities of exfoliated LDHs (CoCo, NiCo, and NiFe-LDH) were mainly attributed to the increase in the number of active edge sites and to higher electronic conductivity.Analogously, Jin et al. [160] selected NiCo LDH as a representative material to demonstrate the concept of the amplified influence of exfoliation using a newly developed high-temperature high-pressure hydrothermal continuous flow reactor (HCFR), see Figure 17.The major findings were presented as follows: (1) the utilized HCFR technology effectively maintain the supersaturation to control the morphology and size of the product; (2) the exfoliation not only resulted in thinner layers with reduced size, but it was also caused by a change in the electronic structure; (3) the increase in the number of edge sites to activate OER; and (4) the increase in the electrochemical active surface area (ECSA) upon the exfoliation was not the only important factor that led to the enhanced OER performance.This work provided a general strategy to enhance the electrocatalytic performance of layered materials by chemical exfoliation.

Cobalt-Based Bifunctional Catalysts in Assembled Unitized Regenerative Fuel Cells
Bifunctional oxygen electrode catalysts play a vital role in the development of unitized regenerative fuel cells (URFCs).URFC, a compact energy storage and conversion device, can simultaneously work in a fuel cell mode to produce electricity, and as a water electrolyzer mode to store off-peak electricity in the form of hydrogen.In this closed-loop system, the essential component is the desired bifunctional oxygen electrode catalysts with high catalytic activity, long-term durability, and strongly resistance to anodic corrosion.To date, several previous studies have reported cobalt-based materials as promising bifunctional ORR/OER electrocatalysts for a URFC system [161].Scott's group used cobalt-based ORR catalysts as the cathodes and demonstrated high and stable power density performance (>200 mW cm −2 ) in alkaline anion exchange membrane fuel cells (AAEMFCs) [162].They further [163] modified the ORR and OER electrode with Cu 0.6 Mn 0.3 Co 2.1 O 4 catalyst for regenerative H 2 -O 2 fuel cell.In water electrolyzer mode, the onset voltage for water electrolysis (deionized water as electrolyte) was ca.1.55 V.At 100 mA cm −2 , the voltages of fuel cell mode and electrolyzer mode were 0.58 V and 1.82 V, respectively, indicating that the fuel cell to electrolyzer voltage ratio was ca.31.87%.However, the current densities in both modes were much lower than those cells with KOH as electrolyte, probably because of the large electrolytic resistance.
Xu et al. [161] measured the performance of a unitized regenerative anion exchange membrane fuel cells (UR-AEMFCs), using a bifunctional ORR/OER catalysts, Co 3 O 4 /oCNT, (oCNT stands for oxidized CNTs) on the oxygen electrode.The obtained performance in fuel cell mode was basically consistent with the result in half-cell mode, while the electrolyzer performance was poor.Likewise, 0.1 M KOH solution in the cell, significantly improved the performance of electrolysis.
Our group designed a self-assembly laminar flow unitized regenerative micro-cell (LFURMC) without gas separator, which was provided with Pt/C as the hydrogen catalyst, bifunctional oxygen NiFeOx/CoNy-C catalyst and 3 M KOH electrolyte [33].In the fuel cell mode, Figure 18, the NiFeO x /CoN y -C electrode showed the maximum power density of 56 mW cm −2 , which was very close to that of Pt/C (63 mW cm −2 ) and IrO x /C (58 mW cm −2 ); in the electrolyzer mode, the maximum electrical power consumed on NiFeO x /CoN y -C (237 mW cm −2 ), was more than three times that on Pt/C (73 mW cm −2 ).Moreover, the calculated round-trip efficiency (RTE) of NiFeO x /CoN y -C catalyst nearly held a level of ca.52% during three cycles, evaluating a super reversibility of the NiFeO x /CoN y -C electrode.
NiFeOx/CoNy-C electrode showed the maximum power density of 56 mW cm −2 , which was very close to that of Pt/C (63 mW cm −2 ) and IrOx/C (58 mW cm −2 ); in the electrolyzer mode, the maximum electrical power consumed on NiFeOx/CoNy-C (237 mW cm −2 ), was more than three times that on Pt/C (73 mW cm −2 ).Moreover, the calculated round-trip efficiency (RTE) of NiFeOx/CoNy-C catalyst nearly held a level of ca.52% during three cycles, evaluating a super reversibility of the NiFeOx/CoNy-C electrode.

Mechanism of HER
The hydrogen evolution reaction (HER) is the half-reaction carried out at the cathode of an electrolyzer, in which protons (acidic environment) or water molecules (alkaline environment) are reduced, accompanied by the subsequent evolution of gaseous hydrogen through the water splitting process.The overall HER proceeds as follow (in all cases, any catalytic site is denoted as "*"): Acid medium: Alkaline medium: The standard potentials (E • ) are different due to the nature of the active ions in the reaction.As we can expect, the HER as any electrochemical reaction possesses a certain activation energy barrier to promote the reaction, usually denoted as overpotential η.Therefore, the HER usually demands the assistance of electrocatalytic materials to lower η, and consequently to increase the reaction rate and efficiency.The mechanisms to achieve the HER can be Volmer-Heyrovsky or Volmer-Tafel.In acid medium, the HER proceeds according to the following steps: i.
A hydrogen atom adsorption, which is the result of the combination of a proton and an electron on the electrode surface (proton discharge) is the Volmer reaction: * + H + + e − * H ad (21) ii.
The adsorbed hydrogen atom interacting with a proton and an electron leads to an electrochemical desorption.This reaction is the Heyrovsky reaction: * H ad + H + + e − H 2 + * iii.
The coupling of the two adsorbed hydrogen atoms leads to a dissociative desorption of hydrogen, the Tafel reaction: In alkaline electrolyte, due to the OH − abundance, the HER proceeds according to the following steps.For the Volmer reaction, the molecular water couples with an electron, leading in an adsorbed hydrogen atom at the electrode surface: i.
For the Heyrovsky reaction, the adsorbed hydrogen atom combines with molecular water and an electron, allowing the electrochemical desorption of hydrogen: ii.
The Tafel reaction is similar to that of the acidic medium.
In acid and alkaline media, for the HER, the hydrogen adsorption starts via the Volmer reaction, Equations (21) or (24).The successive hydrogen desorption can proceed via the Heyrovsky reaction, Equations (22) or (25) or the dissociative desorption via the Tafel reaction, Equation (23).On the other hand, the HER can be proposed by the Tafel slope, as derived from the HER polarization curves.The Tafel slope analysis represents the intrinsic nature of the electrocatalytic material, and the empirical magnitude of the Tafel slope can provide information to distinguish the mechanism.For a Tafel rate determining step (RDS), the slope is 30 mV dec −1 , whereas for Heyrovsky and Volmer RDS, slopes are 40, and 120 mV dec −1 , respectively.
The HER mechanism on Co-based catalysts follows the Volmer-Heyrovsky mechanism, where normally the Heyrovsky step is the RDS in acid medium [164,165]; whereas the Volmer step is considered the RDS in alkaline medium [165].

Synthesis Strategy
Co-based catalysts are potential materials for the HER.Considerable research efforts were devoted to synthesizing cobalt chalcogenides as catalysts for HER.Those dichalcogenides are in the pyrite/marcasite phase.The metal atoms are octahedrally coordinated to adjacent S/Se atoms.Kong et al. [164] claimed that CoSe 2 possessed one of the best HER performance among the first raw transition-metal chalcogenides, because of the partially filled e g band of CoSe 2 .With this knowledge, Liu et al. [166] developed CoSe 2 nanowire arrays on carbon cloth (CoSe 2 NW/CC) through a facile two-step hydrothermal preparative strategy.The hydrogen evolution reaction performance was tested in 0.5 M H 2 SO 4 .Current densities of 10 and 100 mA cm −2 at overpotentials of 130 and 164 mV were maintained for at least 48 h.The excellent HER activity and durability for CoSe 2 NW/CC were explained as follows.(1) The nanoarray allows for the exposure of more active sites; (2) The direct growth of CoSe 2 on CC offers intimate contact, good mechanical adhesion and excellent electrical connection between them; and (3) The absence of polymer binder for catalyst immobilization.
Vertical-aligned graphene nanoribbons (VA-GNRs) were used as a support for cobalt carbide nanocrystals, e.g., Co 3 C/VA-GNRs by Fan et al. [119].The HER performance in acid medium revealed a Tafel slope of 57 mV dec −1 and η @10 of ca.0.125 V. Zhang et al. [167] synthesized by a hydrothermal procedure polymorphic CoSe 2 supported onto graphite with promising HER performance, Figure 19.These authors observed that the optimized calcination temperature of CoSe x was 300 • C.This treatment allowed the change of a mixed orthorhombic to cubic phase of CoSe 2 .The polymorphic CoSe 2 catalytic center showed higher HER performance compared to CoSe x , cubic CoSe 2 and CoSe synthesized under the same conditions.The high performance observed in polymorphic CoSe 2 was attributed to the enhanced chemisorption of H atoms onto the mixed-phase in the Tafel step.

Crystal Structure and Nanostrcuture
Tuning the crystal structure and surface morphology, a catalytic center can enhance its performance for electrochemical energy conversion devices.For example, the combined effect of morphology and phase of CoSe 2 was studied by Li et al. [168].These authors fashioned CoSe 2 nanotubes with orthorhombic-(o-CoSe 2 ) and cubic-phases (c-CoSe 2 ) by a facile precursor transformation method, Figure 20a.In the synthetic process, the crystal structure and surface morphology of CoSe 2 were adjusted by the calcination temperature.Benefiting from the advantageous tubular structure, including the functional shells and well-defined interior voids, CoSe 2 nanotubes showed a clear HER performance in alkaline medium.Interestingly, the authors observed that the orthorhombic phase (o-CoSe 2 ) possessed the highest HER performance in terms of lowest onset overpotential (~54 mV) and smallest Tafel slope (~65.9 mV decade −1 ) in alkaline medium, see Figure 20b,c.Another approach where the morphology effect towards the HER was observed were given by CoSe 2 nanoparticles [21], nanowires [166,169], interwoven [170], nanocomposites [171], hollow microspheres [172], and nanosheets [173].On the other hand, the construction of the ultra-thin two-dimensional (2D) nanostructure have become an promising approach to tailor novel high active electrocatalytic centers, due to the confined charge interaction in the planar dimension with minimum interlayer interaction (which in fact hinders the electrical conductivity), thus improving catalytic properties [174].An ultrathin 2D structure with abundant low-coordinated surface atoms offers adequate active sites for hydrogen evolution reactions.Liu group [175], prepared the Mn 0.05 Co 0.95 Se 2 ultrathin nanosheets with 1.2 nm thickness by usual liquid exfoliation of homogeneous Mn doped CoSe 2 /DETA hybrid nanosheets.The subtle distortion of atomic arrangement was induced after the incorporation of Mn 2+ into CoSe 2 , which boosted the exposure of more active edge Se sites, optimizing the HER activity.Since the chalcogenide atoms at the edges of pyrite catalyst have been verified to be HER active sites analogous to MoS 2 , the authors proposed that the edge Se sites in the CoSe 2 probably were responsible for HER as the active sites.The Mn-doped CoSe 2 ultrathin nanosheets displayed outstanding HER performance, with a low overpotential of 174 mV, and a Tafel slope of 36 mV dec −1 .

Hydrogen Evolution on MOFs Catalysts
Regarding derived-MOF electrocatalysts, the porous ZIF-9 was used as a cobalt source and sacrificial template to synthesize CoS 2 , see Figure 21a [176].The ZIF-9 presented very weak HER electrocatalytic performance, the benzimidazole ligands of ZIF-9 were substituted by S ions after adding sulfur sources in the appropriate mention of 200 • C and 1 atm hydrothermal temperature and pressure, the resulting CoS 2 had excellent HER activity.The introduction of graphene to further enhance the conductivity of the material, and improve the dispersion of cobalt disulfide, on RGO (CoS 2 /RGO) was necessary.In Figure 21b, the HER performance of the material with an overpotential of 180 mV at 10 mA cm −2 was smaller than those of ZIF-9, and ZIF-9/RGO.The Tafel slope of CoS 2 /RGO was 75 mV decade −1 .This slope was near that obtained on Pt/C electrode.Zhang et al. [177] synthesized the core-shell structure Co/Co 9 S 8 anchored onto S-, N-co-doped porous graphene sheet (Co/Co 9 S 8 @SNGS).They employed thiophene-2,5-dicarboxylate (Tdc), and 4,4-bipyridine (Bpy) organic ligands assembled Co-based metal-organic frameworks in situ grown on graphene oxide sheets.The S-containing Tdc, and the N-containing Bpy did not only trigger the growth of Co-MOF nanocrystals but also fixed the S/N atomic ratio of 1:2.4 on graphene oxide sheets.After pyrolysis of Co-MOF at 1000 • C the catalyst showed high bifunctional catalytic activities for the OER, and HER in 0.1 M KOH electrolyte, with an overpotential of 290 mV for OER at a current density of 10 mA cm −2 , and 350 mV for HER at a current density of 20 mA cm −2 .
Besides the cobalt sulfide, cobalt selenide could also be synthesized using MOFs.CoSe 2 nanoparticles embedded in defective carbon nanotubes (CoSe 2 @DC) was produced by carbonoxidation-selenization procedure of Co-based MOFs [64], Figure 22.The pre-oxidation treatment was a crucial step in introducing an increasing number of defects into carbon nanotubes, which promoted the reaction between Co@Carbon and selenium.The authors associated the enhanced HER performance to the induced carbon-surface defect density, which favored the diffusion of Se atoms through Co atoms, and made the best use of the exposed active surface area.Lin et al. [178]   Table 3 summarizes the relevant contributions regarding the HER Co-based catalysts, wherein it is possible to highlight that these catalysts present considerable performance in acid and in alkaline media.One can stress some remarkable parameters regarding the HER electrocatalytic performance, namely, (1) among non-precious catalysts, Co-based catalytic centers are one potential candidate to replace Pt-based electrodes for the water-splitting cathodic reaction, their high activity and stability; (2) since cobalt selenides catalytic centers boost the HER in acidic and in alkaline media, the chemical coordination of Co with sulfides and phosphides showed considerable performance in acid media; (3) the crystalline structure, due to the exposed active sites and electronic properties are crystalline-phase dependent; (4) the surface morphology can expose active sites; (5) the electrical coupling with conductive supports; in as much as the coupling of Co-based catalytic centers with high surface area and high electrical conductive supports modulate the dispersion of the catalytic centers and the interfacial charge-transfer.Doped carbon supports (mainly N-doped graphitic surfaces) could modify the electronic structure of the anchored catalytic centers; and (6) the synthesis route and metal source; e.g., MOFs, could provide hybrid materials which combine the surface properties of the porous carbon network and the catalytic properties of Co domains.Those parts are critical points to be considered in tailoring HER advanced materials.Table 3 summarizes the relevant contributions regarding the HER Co-based catalysts, wherein it is possible to highlight that these catalysts present considerable performance in acid and in alkaline media.One can stress some remarkable parameters regarding the HER electrocatalytic performance, properties which can be achieved by the rational design of materials, such as a large specific surface area, ultrathin/atomic level thickness, optimized porous structure for the exposure of active sites, high conductivity, and a high uniform dispersion, the Co-based nanomaterials will continue to open new avenues to further enhance electrocatalytic activity and stability.Among these Co-based catalysts, due to the coexistence of the diverse active sites including doping via nitrogen, Co-N x /C derived from LDH, MOF and other precursor used as templates were considered to substitute Pt, Ru, and Ir-based catalysts in acidic and alkaline medium.Last but not least, in-depth studies and interdisciplinary cooperation are still urgently required.Therefore, the design and development of cobalt-based electrocatalysts should be concentrated on the following aspects in the future: (1) understanding the fundamental reaction mechanisms of ORR, OER and HER by virtue of theoretical prediction and simulation; (2) probing and identifying the ideal active sites, and then integrating the different types of active sites to develop the so-called bifunctional oxygen electrode electrocatalysts or bifunctional HER-OER electrocatalysts; (3) gaining insights into the active sites involved such as metal species, oxygen vacancies, and topological defects, by using various advanced characterization techniques, e.g., X-ray absorption near edge structure spectroscopy (XANES), sub-Ångström-resolution aberration-corrected scanning transmission electron microscopy (HAADF-STEM), and in situ Raman; (4) developing simple and low-cost approaches to synthesize the catalysts with satisfactory activity and stability is expected to achieve the mass-production and high quality required for large-scale applications.

Figure 1 .
Figure 1.Schematic organization of the cobalt-based catalysts (CoCat) including layered double hydroxides, chalcogenides, oxides, M-N x /C and metal organic framework with some major applications.

Figure 2 .
Figure 2. (a-d) High-resolution transmission electron microscope (HRTEM) images of CoS 2 -0 (without addition of hexa-decylcetyl-trimethylammonium (CTAB)), CoS 2 -1, -2, and -3 nanoparticles with the initial Co 2+ concentrations from 0.025 M to 0.075 M in the presence of 0.5 mM CTAB; (e) rotating disc electrode (RDE) curves of the four CoS 2 samples in O 2 -saturated 0.1 KOH at 1600 rpm at a scan rate of 5 mV s −1 (cathodic sweep) at room temperature.The catalyst loading was 0.1 mg cm −2 ; (f) half-wave potential (E 1/2 ) and OCP (Open Circuit Potential) extracted from Tafel plots as a function of the average CoS 2 particle size.Reproduced from [46], Copyright © Royal Society of Chemistry, 2013.

Catalysts 2018, 8 ,
x FOR PEER REVIEW 8 of 43 properties of MOF, such as, large surface area, tailoring porosity, and easy functionalization with other heteroatoms or metal/metal oxides, various carbon-based nanomaterials (as support) have been prepared.Based on organic ligands and cobalt metal centers, MOFs compounds possess special superiority to prepare various cobalt-based functionalized carbon nanomaterials, including heteroatom-doped porous carbons, and metal/metal oxide decorated porous carbons, via thermal decomposition under controlled atmospheres.For instance, Lou et al.[69] used ZIF-67 as a template and thioacetamide as a sulfur source to prepare a double-shelled Co-C@Co9S8 nanocages electrocatalyst for the ORR.By adjusting the reaction time, the amorphous CoS nanocages (a-CoS NCs) and ZIF-67@a-CoS yolk-shelled hollow nanostructures were fabricated.The Co9S8 shells, served as a nanoreactor, effectively prevented the Co-C active centers from aggregation, Figure6a.Interestingly, the unique Co-C hollow cages significantly shortened the diffusion pathway of the electrolyte, and thus promoted the electrocatalytic activity, durability, and tolerant to methanol toward the ORR of Co-C@Co9S8 catalyst.In Figure6b-e, the onset potential remarkably reached 0.96 V vs. RHE with a limiting current of 4.5 mA cm −2 and a four-electron transfer route with OH − production in alkaline media.
prepared a series of surface-tuned Co 3 O 4 nanoparticles with different morphologies (cubic (Co 3 O 4 -NC/NGr-9h), blunt-edged cubic (Co 3 O 4 -BC/NGr-12h), and rough edged spherical (Co 3 O 4 -SP/NGr-24h)) dispersed on nitrogen-doped graphene (NGr) electrocatalysts for ORR by varying the reaction time.The transformations of the morphologies of Co 3 O 4 could be assigned to the transformation of the higher to the lower surface energy crystal plane structure, which was expected to obtain the mixed facets of the exposed Co-oxide crystals.Among them, the NGr supported spherical Co 3 O 4 (Co 3 O 4 -SP) nanoparticles (Co 3 O 4 -SP/NGr-24h) with the highest roughness factor and increased surface area exhibited the best activity in alkaline medium, and attributed to: (1) homogenous dispersion of Co 3 O 4 nanoparticles on NGr support; (2) NGr served as nucleation sites, efficiently controlling the growth kinetics of Co 3 O 4 nanoparticles; and (3) a strong synergistic interaction between the active sites and the support.
Figure 8 [32].Here, the CoAl-LDH precursor operated as: (i) catalyst for carbonization and formation of N-CNTs; (ii) detacher of active Co nanoparticles from the Co component in the host sheet; (iii) enabler for the growth of long N-CNTs with the aid of the confinement effect of non-active Al 2 O 3 matrix formed.Catalysts 2018, 8, x FOR PEER REVIEW 11 of 43 Figure 8 [32].Here, the CoAl-LDH precursor operated as: (i) catalyst for carbonization and formation of N-CNTs; (ii) detacher of active Co nanoparticles from the Co component in the host sheet; (iii) enabler for the growth of long N-CNTs with the aid of the confinement effect of non-active Al2O3 matrix formed.

Catalysts 2018, 8 , 43 Figure 9 .
Figure 9. (a) The schematic chemical synthesis route of Co-N@HCS catalyst; (b) the LSV curves within ORR (cathodic sweep) and OER (anodic sweep) potential window of Co-N@HCS, N@HCS and Pt/C catalysts in O2-saturated 0.1 KOH at a rotation speed of 1600 rpm with a mass loading of 0.3 mg cm −2 .Inset: the comparison of the ΔE values.Reproduced from [115], Copyright © Elsevier, 2017.

Figure 9 .
Figure 9. (a) The schematic chemical synthesis route of Co-N@HCS catalyst; (b) the LSV curves within ORR (cathodic sweep) and OER (anodic sweep) potential window of Co-N@HCS, N@HCS and Pt/C catalysts in O 2 -saturated 0.1 KOH at a rotation speed of 1600 rpm with a mass loading of 0.3 mg cm −2 .Inset: the comparison of the ∆E values.Reproduced from [115], Copyright © Elsevier, 2017.

Figure 10 .Figure 10 .
Figure 10.(a) The chemical synthesis route of Co-N@HCS catalyst; (b) ORR current-potential characteristics on (Cu and Co) embedded N-doped carbon materials in O2-saturated 0.1 M KOH Figure 10.(a) The chemical synthesis route of Co-N@HCS catalyst; (b) ORR current-potential characteristics on (Cu and Co) embedded N-doped carbon materials in O 2 -saturated 0.1 M KOH solution at a scan rate of 10 mV s −1 and rotation speed of 1600 rpm (cathodic sweep) at room temperature (25 ± 1 • C).The catalyst loadings of all samples were 0.182 mg cm −2 .Reproduced from [117], Copyright © Wiley, 2017.

Figure 12 .
Figure 12.The oxygen evolution reaction (OER) mechanism in acid (blue line) and alkaline (red line) medium.Two reaction routes of oxygen evolution take place: (1) black line indicates that the process involves the formation of a peroxide (M-OOH) intermediate; (2) green line indicates that the direct reaction of two adjacent oxo (M-O) intermediates to produce molecular oxygen.Reproduced from [4], Copyright © Royal Society of Chemistry, 2017.

Figure 12 .
Figure 12.The oxygen evolution reaction (OER) mechanism in acid (blue line) and alkaline (red line) medium.Two reaction routes of oxygen evolution take place: (1) black line indicates that the process involves the formation of a peroxide (M-OOH) intermediate; (2) green line indicates that the direct reaction of two adjacent oxo (M-O) intermediates to produce molecular oxygen.Reproduced from [4], Copyright © Royal Society of Chemistry, 2017.

Figure 14 .
Figure 14.(a) Cyclic voltammograms of reduced Co 3 O 4 , and pristine Co 3 O 4 NWs deposited on glassy carbon electrodes in O 2 -saturated 1 M KOH at 5 mV s −1 ; (b) water oxidation current-potential characteristic of reduced Co 3 O 4 NWs (red curve), pristine Co 3 O 4 NWs (blue curve), IrO x (brown curve) and Pt/C (black curve) in O 2 -saturated 1 M KOH at a scan rate 5 mV s −1 at 1600 rpm (anodic sweep) at 25 ± 1 • C with iR-compensation.The catalyst mass loadings in all cases was 0.136 mg cm −2 ; The bottom panel shows the ins situ chemical reduction via NaBH 4 to form oxygen vacancies in Co 3 O 4 NWs.Reproduced from [143], Copyright © Wiley, 2014.
3 O 4 nanorods array on Co foil (Co 3 O 4 NA/CF) oxygen-evolving catalyst using the so-called in situ self-standing method, Figure 15a.The 1D Co 3 O 4 NA/CF OER material only needed η = 308 mV to drive a geometrical current density of 15 mA cm −2 in 1 M KOH, exceeding the value reported so far on Co 3 O 4 -based electrocatalysts.The electrocatalyst delivered an excellent long-term durability of 22 h, and a turnover frequency of 0.646 mol O 2 s −1 at η = 410 mV in Figure 15b.The suggested OER high activity of Co 3 O 4 NA/CF was thought to be the formation of Co III (in an octahedral environment) on CoOOH as a result of Co 3 O 4 oxidation.The surface Co III -containing octahedral forms Co III -OH, which was further oxidized to form the active catalytic center: Co IV -O for OER.A further coupling of Co IV -O with neighboring species formed hydroperoxo (Co IV -OOH) to peroxo (Co IV -OO) species, leading to the release of O 2 and initial Co III , see scheme in Figure 15c.Catalysts 2018, 8, x FOR PEER REVIEW 21 of 43 308 mV to drive a geometrical current density of 15 mA cm −2 in 1 M KOH, exceeding the value reported so far on Co3O4-based electrocatalysts.The electrocatalyst delivered an excellent long-term durability of 22 h, and a turnover frequency of 0.646 mol O2 s −1 at η = 410 mV in Figure 15b.The suggested OER high activity of Co3O4 NA/CF was thought to be the formation of Co III (in an octahedral environment) on CoOOH as a result of Co3O4 oxidation.The surface Co III -containing octahedral forms Co III -OH, which was further oxidized to form the active catalytic center: Co IV -O for OER.A further coupling of Co IV -O with neighboring species formed hydroperoxo (Co IV -OOH) to peroxo (Co IV -OO) species, leading to the release of O2 and initial Co III , see scheme in Figure 15c.

Catalysts 2018, 8 ,
x FOR PEER REVIEW 22 of 43 electronic structure of Co is applicable for the electrochemical catalysis, such as de-lithiated hexagonal LiCo2 for OER, and spinel LiCo2 for ORR[153].For the OER, a small amount of Fe doping was effective for enhancing the OER activities of Ni hydroxides or oxides, possibly due to the enhanced structure disorder and conductivity.Inspired by this, Sun et al.[154] systematically investigated the ORR and OER activities of ternary NiCoFe-LDHs and observed that a peroxidation treatment of NiCoFe-LDHs led to obtain o-NiCoFe-LDHs that significantly enhanced the corresponding bifunctional performance of (ORR/OER), as shown in Figure16a.The XPS results and Zeta potential measurements evidenced that Co 2+ was partially oxidized to a higher Co 3+ state, while negligible chemical state change of Ni and Fe elements was observed in o-NiCoFe-LDHs.The partial conversion of Co 2+ to Co 3+ state stimulated the charge transfer to the catalyst surface, which could lead to the enhancement of the conductivity.In the Figure16b, in 6 M KOH medium, the o-NiCoFe-LDHs afforded a high ORR current density of −20 mA cm −2 at a required potential of 0.65 V vs. RHE.Moreover, there was a negligible ORR current density degradation of o-NiCoFe-LDHs for 40 h.The higher conductivity induced from the higher valence state of Co, might enhance the electrophilicity of the adsorbed O and thus facilitating the reaction of an OH − anion with an adsorbed O atom on the catalytic active sites to form adsorbed -OOH species, which was considered as the rate-limiting step for OER[138,155].

Figure 16 .
Figure 16.(a) Schematic chemical synthesis route and crystal structure of peroxidized ternary LDH bifunctional catalyst; (b) The global polarization curves of various catalysts loaded onto Teflontreated carbon fiber paper (T-CFP) in O2-saturated 6 M KOH electrolyte with a scan rate of 1 mV s −1 , the mass-loading of 1 mg cm −2 without iR-compensation; (c) ORR (cathodic sweep) and OER (anodic sweep) stability measurements of o-NiCoFe-LDH/Y-CFP electrode in O2-saturated 6 M KOH electrolyte with a constant potential, the mass-loading of 1 mg cm −2 .Reproduced from [154], Copyright © Wiley, 2015.

Figure 16 .
Figure 16.(a) Schematic chemical synthesis route and crystal structure of peroxidized ternary LDH bifunctional catalyst; (b) The global polarization curves of various catalysts loaded onto Teflon-treated carbon fiber paper (T-CFP) in O 2 -saturated 6 M KOH electrolyte with a scan rate of 1 mV s −1 , the mass-loading of 1 mg cm −2 without iR-compensation; (c) ORR (cathodic sweep) and OER (anodic sweep) stability measurements of o-NiCoFe-LDH/Y-CFP electrode in O 2 -saturated 6 M KOH electrolyte with a constant potential, the mass-loading of 1 mg cm −2 .Reproduced from [154], Copyright © Wiley, 2015.
NiFe2O4).Particularly, the CoPcTs-intercalated structure and Ni2Fe-LDH host sheet significantly enhanced the immobilization of CoPcTs and improved the dispersion degree of catalytic sites, respectively.

Figure 18 .
Figure 18.Alkaline laminar flow unitized regenerative micro-cell (LFURMC) experiment.(a) Current-potential of the material as anode (electrolyzer mode) and cathode (fuel cell mode).inset: The geometric activities comparison of three LFURMC; (b) the cell voltage and power density curves of the fuel cell with platinum as the hydrogen catalyst, and NiFeO x /CoN y -C, 20 wt% Pt/C and 20 wt% IrO x /C cathode catalysts; (c) the cell voltage and power density curves of the electrolyzer with platinum as the hydrogen catalyst, and NiFeO x /CoN y -C, 20 wt% Pt/C and 20 wt% IrO x /C cathode catalysts; (d) Stability tests of LFURMC based on the NiFeO x /CoN y -C catalyst (three runs), inset: round-trip-efficiency (RTE) for the three cycles.All measurements were conducted at room temperature (25 • C).Remark: no Ohmic-drop correction was made for all determinations.Reproduced from [33], Copyright © Elsevier, 2017.

Figure 20 .
Figure 20.(a) Synthesis route of CoSe2 nanotubes; (b) iR-corrected HER polarization curves (cathodic sweep) of o-CoSe2, c-CoSe2, Co3Se4 NTs, Pt/C and Co3Se4 nanoparticles (NPs) catalysts at a scan rate of 5 mV s −1 in 1 M KOH solution; and (c) Tafel slopes analysis of all the catalysts.The mass loading of

Figure 20 .
Figure 20.(a) Synthesis route of CoSe 2 nanotubes; (b) iR-corrected HER polarization curves (cathodic sweep) of o-CoSe 2 , c-CoSe 2 , Co 3 Se 4 NTs, Pt/C and Co 3 Se 4 nanoparticles (NPs) catalysts at a scan rate of 5 mV s −1 in 1 M KOH solution; and (c) Tafel slopes analysis of all the catalysts.The mass loading of the catalyst was ~0.283 mg cm −2 .Reproduced from [168], Copyright © Royal Society of Chemistry, 2017.

43 Figure 21 .
Figure 21.(a) Schematic illustration of the synthesis of CoS2/RGO; and (b) HER polarization curves (cathodic sweep) collected on different catalysts with mass loading of 0.285 mg cm −2 in 0.5 M H2SO4 acidic solution at a scan rate of 5 mV s −1 at room temperature.Reproduced from [176], Copyright © Elsevier, 2017.

Figure 21 .
Figure 21.(a) Schematic illustration of the synthesis of CoS 2 /RGO; and (b) HER polarization curves (cathodic sweep) collected on different catalysts with mass loading of 0.285 mg cm −2 in 0.5 M H 2 SO 4 acidic solution at a scan rate of 5 mV s −1 at room temperature.Reproduced from [176], Copyright © Elsevier, 2017.

Figure 21 .
Figure 21.(a) Schematic illustration of the synthesis of CoS2/RGO; and (b) HER polarization curves (cathodic sweep) collected on different catalysts with mass loading of 0.285 mg cm −2 in 0.5 M H2SO4 acidic solution at a scan rate of 5 mV s −1 at room temperature.Reproduced from [176], Copyright © Elsevier, 2017.

Table 1 .
Selected Co-based catalyst for the oxygen reduction reaction.