Fine-Tuning Synthesis and Characterization of Mono-Sized H-Beta Zeolite-Supported Palladium-Iridium Nanoparticles and Application in the Selective Hydrogenation of Acetylene

In this research, a mono-sized Beta zeolite support synthesized by the solvothermal method was used in the selective acetylene to ethylene hydrogenation reaction with minimum coke build up on the catalyst surface. Tetrapropylammonium hydroxide (TPAOH), tetrapropylammonium bromide (TPABr), n-butylamine, and morpholine were used as structure direct agents (SDA) in the support to obtain various shapes. The characterization results show that although the Si/(Al + SDA) ratio has no effect on the phase purity of support, it has a remarkable effect on porosity, crystal size, shape, and structure of micropores. After comparing characterization results, the developed support, based on TPAOH, was selected and modified by different metals (Ce, Ir, Ag, and Pd) using the incipient wetness co-impregnation method. Since there is an interaction between selectivity and conversion, the optimum metal content in the synthesized catalysts and reaction condition were determined to achieve the desired acetylene conversion and ethylene selectivity. The physicochemical transformation of the developed optimum catalysts was determined using different techniques. Based on the characterization and cata-test results, the catalyst which contains 0.29% Ir and 0.08% Pd presents a better performance and higher stability compared to the other catalysts due to the moderate size and mono layer dispersion of the metals on the support. The experimental results show that acetylene conversion and ethylene selectivity approach 97% and 92% at 55 ◦C, respectively.


Introduction
In the previous few decades, synthetic micro/meso-porous materials have played a significant role in addressing social subjects such as the extra effective utilization of reproducible resources or fossils, to meet more accurate environmental standards [1][2][3].Zeolite supported catalysts, that are classified as nanostructured catalysts, have a considerable surface-to-volume ratio which favorably affects their catalytic activity [4,5].Zeolite supported catalysts, that are synthesized by various methods such as solvothermal treatment, hydrothermal treatment, etc. [2,[6][7][8][9], have broad industrial utilization in a wide variety of processes such as, aromatization and oligomerization of light olefins, alkylation reactions, catalytic cracking, and optoelectronic devices [10][11][12][13].Among the synthesized zeolites, zeolite Beta is a famous substance which has 12-loop crossovers channels with a pore size distribution of around <2 nm [14].Nevertheless, micro pore size distribution of the Beta zeolite is considered as a barrier for the transformation of molecules [15].The pore size of microporous zeolites can be modified by various techniques including ion exchange [16], zeolites external surface modification, and framework control using structure direct agents (SDA) [17,18].
For the first time, in 1992, Kresge et al. prepared a big-channel zeolite by using quats (NR4+ that R is an aryl or alkyl group like the methyl groups, benzyl groups, methylene chains, ammonium groups and heterocyclic amines [19]) as SDA without transformation restrictions [20].Using this SDA, shapeless silica and/or aluminosilicate substances were obtained instead of zeolite crystal-like materials.Regardless of their shapeless skeleton, the products had mono-sized pore distribution of about 2-50 nm which was higher than the obtained pore size distribution for zeolites up to that time.In addition, the shape and the diameter of the mesoporous zeolites were controllable through tuning type and concentration of the SDA suspensions.From that time onwards, by using SDA suspensions for pore tuning, different substances with various mesoporous morphologies have been made.However, under synthesis circumstances, the meso-zeotype substances have less stability than the zeolite crystal-like which is due to the shapeless quiddity of their SDAs.In addition, poor acid sites of the shapeless SDAs have limited their application in catalytic processes in which potent Brønsted acidity of mesoporous is needed [21].To overcome these problems, many efforts have been made to prepare large pore substances with zeolite specifications.A considerable number of researches have been reported on zeolite synthesis and development [22].For example, Ryoo et al. prepared C 38 H 82 N 2 Br 2 as SDA for initial load and by using this SDA, the scientists prepared mesosheet zeolite of only 2.5 nm width.This SDA acted as an organic surfactant while the tails of numerous SDAs were aggregated to make a suspension [23,24].Na et al. and Kim et al. described that the mesosheet zeolite made by several templates (such as zeolite Beta (*BEA), Linde Type A(LTA), and Linde Type l(LTL)that are synthesized with binary SDA surfactant) not only had a considerable conversion in the methanol to hydrocarbons process, but they also had a good lifetime [25].Wadlinger et al. synthesized Beta zeolite with *BEA morphology by using N,N,N-triethylethanaminium (TEA) SDA [26].Moreover, the TEA+, benzyl(2-hydroxy-1-methyl-2-phenylethyl)dimethylammonium bromide, methylphenyl carbinol, etc. were used as SDAs in Beta zeolite preparation for increasing hydrophobicity [27].According to the literature, hydrophobicity of Beta zeolite increased when methylcyclohexane, toluene, and water solvents and/or a mixture of these were used [28].
Catalysts with moderate pore size distribution, which are promising selective catalysts, can be obtained by adding a metal precursor to micro/meso-porous supports [29].The presence of microporous channels favorably affects the mass transfer and diffusion of guest molecules.This is why Beta zeolite has a considerable stability and catalytic activity [30].
Selective hydrogenation of acetylene to ethylene is a challenging issue which not only is important in academia but is also critical in the chemical industry [31,32].In the academic world, acetylene hydrogenation is considered as a model for selective hydrogenation reactions.As for the industrial world, this reaction is mostly used to purify the ethylene stream which is the product of naphtha cracking.When this purified stream is used for polyethylene production, it yields more alkene which enhances the profitability and eliminates undesired alkyne [32].Selective acetylene hydrogenation has been reviewed thoroughly in other publications [32,33].For instance, Benavidez et al. deposited Pd nanoparticles on carbon, alumina, and magnesia.These nanoparticles were about 0.5-1.0nm and they were produced by solution phase alcohol reduction of Pd(OAc) 2 [34,35].It is safe to say that most of the industrially used catalysts are egg-shell catalysts with minor loads of Pd (<0.1 wt%) where the active component is alloyed with Ag, Cu, Ir, Au, etc. which acts as a structural diluent [32].Addition of another metal, which is better to have for high hydrogenolysis activity, may increase the sintering resistance of Pd [36].The ring opening tendency of Ir (through dicarbene mechanism) is stronger than for other noble metals and is famous for its extraordinary hydrogenolysis activity [37][38][39].Iridium has a noticeable oxidation/reduction potential, therefore, in acidic media (Ir3þ/Ir 1.16 V), it is electrochemically stable.This is why Ir is a suitable candidate for improving the surface electronic structure of Pd alloys and the stability of Pt-based catalysts which is of paramount importance for further increasing their catalytic activity [39][40][41].As introduced by Exxon (1970s), Ir forms a part of the reforming Pt-Ir catalysts with higher activity than monometallic Pt which was used commercially previously [37].You et al. studied Ir decorated PdCu alloy and the obtained ternary Ir-PdCu/C catalyst had a higher oxygen reduction reaction (ORR) activity [42].In addition, Ham et al. showed that Pd-Ir-Co alloy catalyst had higher ORR activity and durability than the bimetallic Pd 3 Co alloy [39].According to their studies, chemical composition plays a key role in tuning the electrocatalytic properties of Pd alloy catalysts [39].Jin et al. showed that Pd-Ag alloys considerably improve the selectivity of the catalyst but need catalyst activation by high temperature reduction in hydrogen [43].Han et al. assessed a new procedure for introducing Ag to Pd/TiO 2 catalysts using sequential photo-deposition [44].
Wang and Song [45,46] selected K, La, and Cu as promoters for the Pd or Au catalysts in acetylene hydrogenation.Higher catalytic activity was exhibited, and the lifetime was improved greatly [47].Zhang et al. [48,49] synthesized a series of Au-La/SAC, Au-Co/SAC catalysts and found that the additives Co(III), Co(II), and La(III) could greatly inhibit coke deposition and sintering of the catalyst surface to improve the activity and long-term stability of the catalysts.However, there are several examples of non-palladium catalysts proposed for selective alkyne hydrogenation including Ni-Zn alloy [50], the ternary Cu-Ni-Fe system [51], and CeO 2 [52] as well as monometallic Au [53,54], Ag [55], and Cu [56] catalysts.They demonstrate very high ethylene selectivity but require elevated temperatures to provide high acetylene conversion and are therefore strongly limited for commercial use.On the contrary, in spite of the high activity, selectivity, and stability of supported monometallic palladium catalysts, they are not sufficient, especially at high acetylene conversions, so the second metal (e.g., Ag, Cu) is introduced to improve catalytic performance [33,57].It hinders palladium hydride formation and decreases the number of adjacent Pd sites responsible for multiplet adsorption leading to over-hydrogenation of acetylene to ethane and its oligomerization to higher hydrocarbons (green oil) [57,58].The Pd-Ag bimetallic catalysts have been found to be most efficient and are successfully employed on an industrial scale [59].Also, a Pd-based catalyst supported Y zeolite was studied by Wang et al. [60] and it was found that acetylene conversion and selectivity were about 95% and more than 90%, respectively.Although the catalyst displayed favorable catalytic activity for acetylene conversion and selectivity, it became easily deactivated as the reaction time exceeded 140 min [47].In the event in this article a palladium-based catalyst supported Beta zeolite hardly deactivated as the reaction time exceeded 15 h and acetylene conversion and selectivity were about 97% and more than 92%, respectively, showing that this specification of catalysts here is higher than the previous research up to this time.
A summarized scheme of the reaction is demonstrated in Figure 1.At lower temperatures of interest, the influence of dehydrogenation and decomposition paths on the overall activity and selectivity over pure Pd is negligible, consequently these paths are neglected [32,43,61,62].Generally, hydrogenation (through which ethylene/ethane is produced) and oligomerization (through which 1,3-butadiene and larger hydrocarbons are produced) are the existing reaction pathways that compete with each other [32].Oligomerization pathway is highly relevant given that oligomers are the precursor for 'green oil' production that generally brings about deactivation of the catalyst as a result of hydrocarbon accumulation on the surface of the catalyst.Therefore, the catalyst which avoids oligomer production is considered as the ideal catalyst for hydrogenation of acetylene which is a big challenge with Pd based catalysts.It is more realistic to choose catalysts that decrease the production of 1,3-butadiene (small k3 in Figure 1) or larger oligomers which eventually bring about deactivation (small k4 in Figure 1).In order for a catalyst to selectively hydrogenate acetylene, it is imperative to maximize the rate of ethylene formation (large k1 in Figure 1) whilst minimizing over hydrogenation (k2 in Figure 1) [32].
In this work, we synthesized unique and mono-sized mesoporous spherical Beta zeolite by a facile solvothermal method and we also successfully synthesized and modified PdM/H-Beta-based (M = Ag, Ce, and Ir) catalysts by an incipient wetness co-impregnation method.Different SDA such as tetrapropylammonium hydroxide (TPAOH), tetrapropylammonium bromide (TPABr), morpholine, and n-butylamine were added via a solvothermal procedure to modify the shape, specific surface area, pore size distribution, acidity, and stability of Beta-based catalysts.Finally, PdM/H-Beta-based catalysts were characterized with high-resolution transmission electron microscopy (HRTEM), X-ray powder diffraction (XRD), thermogravimetric analysis-differential thermogravimetry (TGA-DTG), N 2 -adsorption/desorption, pore size distribution (PSD), Fourier-transform infrared spectroscopy (FTIR), UV-Visible, inductivity couple plasma-optical emission spectrometry (ICP-OES), dynamic light scattering (DLS), temperature programmed desorption (TPD), stability, and zeta potential.They were used in the selective hydrogenation of acetylene to ethylene at different gas hour space velocity (GHSV), reaction temperature, and hydrogen to acetylene ratio (R) to investigate the acetylene conversion, ethylene selectivity, and yield of the process.

BET and DLS Characterization
Beta-based catalysts (Beta as support, 0.08%Pd1.9%Ag/H-Beta(i),0.08%Pd2.9%Ce/H-Beta(i),and 0.08%Pd0.29%Ir/H-Beta(i)as optimum catalysts) were characterized with N2 adsorption-desorption isotherms, PSD patterns, and DLS pictures.Table S1 shows the different Beta-based catalyst synthesis conditions in which the PSD and specific surface area are changed with the SDA and tetraethylorthosilicate (TEOS) values.The Si/(Al + SDA) ratio is 28.57, 19.05, 20.68, 13.18, 11.95 for Beta(0), Beta(i), Beta(ii), Beta(iii), and Beta(iv)-based catalysts, respectively and TPAOH is selected as the best SDA because this sample has a very high surface area, excellent acidity, standardized morphology, and the nanoparticles are moderate and mono sized.According to the Table S1 and Figure S2, by increasing the Si/(Al + SDA) ratio, the PSD value increases but the Brunauer-Emmett-Teller (BET) value increases at first to the maximum value and then decreases.This demonstrates that augmenting TPAOH results in a moderate pore size distribution in the supports, and the micro porosity of samples could be easily adjusted by adding various amounts of SDA.The highest specific surface area is obtained over Beta-zeolite with TPAOH as SDA which has a moderate particle size and micropore volume.Table S2 and Table 1 show the synthesis conditions of different catalysts and optimized catalysts with textural properties, respectively.BET specific area, average PSD curves of optimum supports and effect of Si/(Al + SDA) on the BET and PSD of optimum supported are depicted in Figure 2a-c.The isotherm of Beta-based catalyst (Figure 2a) demonstrates an International Union of Pure and Applied Chemistry (IUPAC) kind I and IV treatment, which is usual for microporous substances, and no mesoporous appears in Beta(0) PSD patterns, because of the presence of a slightly enhanced absorption at higher pressures.Additionally, the isotherm of Beta(i, ii, iii, and iv)-based catalysts shows mesoporous channels and no microporous appears in their PSD patterns (Figure 2b).This gives growth to a remarkable internal and external specific area, eventually over 1474.78 m 2 g −1 with a PSD final amount of about 1.5 nm for Beta(0).The non-appearance of a pronounced hysteresis curl in the BET Beta(0)-based patterns brings about a comparatively high amount of S micro and as a result there is a rise in exterior specific area partnership compared to interior crystalline microporosity [63].It also proposes the existence of some slit-like intercrystalline voids which are due to the agglomeration of crystals.Specific surface area and PSD value for other Beta(i, ii, iii, iv)-based catalysts that are synthesized with different SDA are shown in Table S2 and Table 1. Figure 2c shows that with an increase in the Si/(Al + SDA) ratio when TPAOH is used as SDA, PSD and BET increase but BET increases to a maximum surface area then decreases.At the optimum Si/(Al + SDA) ratio, this is 19.05,PSD and BET set at 10.3 nm and 1358.3 m 2 g −1 , respectively.For other SDAs, with a decrease in Si/(Al + SDA) ratio, PSD peaks at 20.68 (ii), 13.18 (iii), 11.95 (iv), are reported in Figure S1 and Table 2.The Beta-zeolite with n-butylamine and morpholine supports contains lower BET and a very wide PSD compared to the Beta-based catalysts with TPAOH and TPABr as SDA.For Beta(iv) and Beta(iii), a large adsorption is observed at high relative pressure which is attributed to N 2 -adsorption in the interparticle voids.These results are attributed to the attendance of low crystallinity and α-quartz phase through the Beta-based catalyst with n-butylamine and morpholine.
The H-Beta(i)-based catalyst shows higher textural specifications compared to the other supports which means that the introduction of SDA (such as TPAOH) can strongly modify the textual specifications of the supports and catalysts.Therewith, the decrease in the textural specifications of the catalysts could be ascribed to a little incorporation of chelating agents.As shown in Figure S2, all samples display kind IV patterns with H 3 kind hysteresis curl because a high amount of alumina and/or silica is integrated into the support's structure.The moderate and mono sized PSD patterns are obtained from the patterns of all samples, especially in 0.08%Pd 0.29%Ir/H-Beta(i).Figure S3 depicts DLS catalysts under optimum synthesis conditions and the results are demonstrated in Table 2. Figure S3 shows that the crystal sizes of the different catalysts over optimum support are around 10-30 nm and the crystal sizes of 0.08%Pd0.29%Ir/H-Beta(i)catalyst were mono and narrow sized compared to other catalysts.a : Determined by Inductively Coupled Plasma (ICP) analysis; b : Calculated by BET method; c : Mesopore volume and diameter calculated using the BJH method; d : The total pore volume was obtained at a relative pressure of 0.98 by Horvath and Kawazoe (HK) model; e : Calculated using t-plot method; f : Determined by DLS analysis.

TEM and FESEM Characterization
The effect of Si/(Al + SDA) parameter on the Beta morphology of Beta-zeolite is also investigated.The obtained results show that a change in the type of SDA brings about a change in shapes.Figure 3 shows that all of the Beta-zeolite samples display orderly shapes.As Si/(Al + SDA) is reduced in the synthesis procedure, the shapes of the mesoporous Beta-zeolites become more standard.With modifying the Si/(Al + SDA) value for the four different SDA, four various shapes are formed.SDA also plays a significant role in the synthesis of the supports and catalysts.A large amount of Beta-zeolite with TPAOH, as the SDA, exhibits a spherical shape that is useful for diminishing diffusion restrictions with the average crystal size of ~12 nm (DLS patterns are depicted in Figure S4).Hydrophobicity, size, and the geometric figure of SDAs impress their filling and directing styles.Hence, the morphology and particle direction change with SDA alteration [24].According to Figure 3, Beta-zeolite precursor with TPABr as the SDA has a clews like shape and the average sizes of crystals are about ~18 nm.Beta-zeolite precursor with morpholine as the SDA has approximately a stretched nanowire shape with nonhomogeneous average sizes of ~40 nm and Beta-zeolite precursor with n-butylamine as the SDA has gear wheel shape with average crystal size of ~67 nm (DLS patterns are demonstrated in Figure S4).These types of zeolite pictures have not been presented in the literature.These results show that the shape of all of the supports depends on the Si/(Al + SDA) parameter.Researches have shown that the selective hydrogenation of acetylene is structure sensitive [64].
The crystal size distribution of bimetallic PdIr, PdCe and PdAg nanoparticles has an excellent influence on their catalytic efficiency which is shown in Figure 4 and Figure S5.According to Figure S5, the distribution of Pd, Ir, Ce, and Ag metals on the Beta(ii, iii, iv)-based catalysts are much poorer than the Beta(i)-based catalysts (Figure 4) and this result can be explained based on the SDA effects on the supports reported in Section 2.1.Also, the performance of the Beta(i, ii, iii, iv)-based catalysts investigated in the selective hydrogenation of acetylene are reported in Section 2.8.The Cata-test shows that selectivity and conversion of Beta(i)-based catalysts are much higher than the Beta(i, ii, iii, iv)-based catalysts.Therefore, it can be concluded that the Beta(i)-based catalysts are a better support than the Beta(ii, iii, iv)-based catalysts and the denoted optimum support with dispersity of Pd, Ir, Ce and Ag metals in this support is shown in Figure 4.
Figure 4 shows the TEM pattern of the optimum H-Beta(i)-based catalyst.According to Figure 4, Pd and Ir metals have a very good dispersity and TEM images confirm the DLS, BET, and PSD results.Figure 4 shows that Pd and Ir metals have mono and narrow sized particles in the H-Beta(i)-based catalyst but Ag and Ce metals have poorer dispersity compared to Ir metal.It is clearly observed from the Energy Dispersive Spectrometer (EDS) patterns, shown in Figure S6, that the as-acquired supported Pd, Ir, Ce, and Ag catalysts contain Pd, Ir, Ag, Ce, Al, Si, and O.No additional amorphous silica or crystalline phase was observed [66].With an increase in the Si/(Al + SDA) parameter, the severity of diffraction peaks increases which shows growth of particle sizes and reduction of specific surface area.The XRD analyses of the optimum catalysts are shown in Figure 5b.It can be seen that all of the optimum samples have potent peaks at 2θ = 33.8• , 48.6 • , and 69.3 • , which are probably relative to the characteristic peaks of alumina or silica.

XRD Patterns
The relatively feeble diffraction peaks at 6.6 and 20.2 are indexed as the specific peaks of Beta-zeolite nanoparticles as formerly explained (Figure 5a).Afterward, the XRD analysis of all of the optimum samples exhibits no clear Pd, Ag, Ce, and Ir oxide diffraction peaks which denotes the absence of bulk crystalline Pd, Ag, Ce, and Ir oxides on the support.Finally, the XRD analysis (Figure 5b) of catalysts shows that the Beta-based catalyst structure remains pure and no Pd peak is observed, as reported in the literature.

FT-IR Spectroscopy
The Beta-based catalysts that are prepared with different SDAs were investigated by FT-IR analysis, as shown in Figure 6.The wavelength is near to 458 cm −1 because of the existence of AlO 4 and SiO 4 intramural, a triangular pyramid module (Figure 6a).The wavelength of about 520 cm −1 confirms that the Beta-mesoporous is generated by 5-membered rings.The severity ratio of the wavelength which is about 520 cm −1 and 458 cm −1 , is defined as FTIR crystallinity, which increases in the following order: Beta(i) > Beta(ii) > Beta(iii) > Beta(iv).The SDA presence can be identified through the feeble H-C stretching sorption wavelength at about 2850-2950 cm −1 (Figure 6b).The absorption intensity at ~3653 and 3765 cm −1 is dedicated to the Al-O-H-Si and Si-O-H vibration [67].The combination of the obtained results with BET, PSD, DLS, FTIR, and XRD characterizations patterns shows that Beta with TPAOH as SDA is a support with mono sized crystals and moderate pores.

Surfac Acidity Meassurment
Pyridine is usually used as the probe molecule to evaluate the amount of Lewis (L) and Brønsted (B) acidic sites because of its specific interaction with different kinds of acid sites [68].The acidities of the optimum samples were considered by means of the pyridine IR spectra on absorbing pyridine and later desorbing at temperatures of 200  As mentioned in the references [69,70], the bands near ~1608 cm −1 and 1449 cm −1 are attributed to the potent L-acid sites, and the bands at about 1640 and 1545 cm −1 are attributed to the B acid sites [71].While the wavelength near 1575 cm −1 is attributed to the weak L sites, the wavelength near about 1489 cm −1 is dedicated to both L and B sites.As shown schematically in Figure 7a, all of the catalysts supported with H-Beta(i) show a wavelength at about 1545 cm −1 which is related to the B acid sites.The wavelengths appearing at about 1449 and 1608 cm −1 are attributed to L bound acid sites [72].Furthermore, the generic wavelength presenting at about 1489 cm −1 is attributed to the combination of L and B acid sites.The data on acid strength site distribution in the different catalysts is listed in Table 3.These results are obtained from the adsorption IR analysis collected from the optimum samples.As depicted in Figure 7a, after pyridine desorption at 200 • C, B and L acid sites of the 0.08%Pd 0.29%Ir/H-Beta(i) catalyst are considerably higher than those of the other supported catalysts.Furthermore, the acid strength distributions of 0.08%Pd 1.9%Ag/H-Beta(i) and 0.08%Pd 2.9%Ce/H-Beta(i) catalysts are approximately alike.There is a minor percentage of weak B acid sites in the catalysts due to the presence of H-kind Beta-precursor in the Beta(i) support.The existence of a minor percentage of B acid sites is due to the addition of a small percentage of Al species in the catalysts.After degassing at 350 • C (Figure 7b), no B acid site was identified in the samples.The percent of moderate and potent L and B is as follow: 0.08%Pd 0.29%Ir/H-Beta(i) > 0.08% Pd 2.9%Ce/H-Beta(i) > 0.08%Pd 1.9% Ag/H-Beta(i).

UV-Visible Spectroscopy Specification
The scattering of Pd, Ce, Ag, and Ir oxide molecules on the supports was characterized by Ultra Violet (UV) spectrophotometer.The UV absorption analyses of various catalysts with different amounts of crystalline metals are shown in Figure 8. UV spectroscopy in the range of 200-800 nm displays the polymerization states and the nature of the chemical forms of Pd oxide on the surface of the catalysts.The sorption wavelengths related to LMCT (ligand-to-metal charge transfer) O 2− → Pd 2+ are detectable in the 200-390 nm range [73].The precise location of the wavelengths reflects the native symmetry of Pd 2+ affiliated with their agglomeration and coordination environments states [74].In this analysis, the absorption bands in the range of ~260-290 and 290-360 nm, that show isolated tetrahedral and octahedral Pd species, respectively, are detected in all of the catalysts.Also, 0.08%Pd0.29%Ir/H-Beta(i) is well shown in Figure 8 which illustrates an increase in the ratio of scattered tetrahedral and octahedral Pd molecules after modification owing to TPAOH.The key wavelengths in the visible zone are detected at about 538, 572, and 615 nm which are because of the incorporation of the triangular pyramid of Ag(II), Ir(III), and Ce(III) into the support.Nevertheless, the peak intensities are moderately weak in 0.08%Pd 0.29%Ir/H-Beta(i) (see Figure 8).This phenomenon may be due to the presence of Ir 3+ molecules which have lower polymerization than the other metals.The UV-Vis analysis results suggest that the specification of the active phase (Pd) and promoter (Ir) shows superior scattering on the surfaces of Beta when TPAOH is added through the synthesis procedure.

Zeta (ξ) Potentiail Analysis
The structure of the substances is one of the key factors that affect the reciprocal action between the active site precursor solution and support of the specific surface.It can be explained using the below mechanisms: (1) ligand-exchange, (2) ion-exchange, and (3) electrostatic interaction.The electrostatic reciprocal action depends on the pH of the solution and supports charge.The ξ potential technic has provided beneficial data according to the material charge in support and catalyst preparation [75].Figure 9a,b show the results of ξ potential measurements carried out using different supports and catalysts.All of the supports and catalysts are presented with NaNO 3 and de-agglomerated in an ultrasonic probe with high energy for about 1 h.As shown in Figure 9a, the point of zero charges (PZCs) for H-Beta(i) is at pH ~8.3, for H-Beta(ii) is at pH ~8.92, for H-Beta(iii) is at pH ~10 and for H-Beta(iv) is at pH ~10.2.In other words, the surface charge of H-Beta(i), H-Beta(ii), H-Beta(iii), and H-Beta(iv) is positive below pH ~8.3, 8.92, 10, and 10.2, respectively, and becomes negative above these values.It is important to note that for a special substance, the amount of the ξ as a function of pH depends on many parameters, e.g., the electrolyte concentration, whether the material is solid or porous, the measurement method, and the presence of impurities or additives.Generally, ξ at high amounts of pH should be significantly higher than that at pH ranges near the PZCs.This might be due to an increase in the electrolyte concentration and/or a partial dissolution of the special substance during the titration to lower or higher pH values.The pH values for all of the support and catalyst emulsions were ~>6.5 before starting the titration.The PZCs for the micro/mesoporous structure do not significantly differ from the corresponding solid structures since all of the nanoparticles with zero charge are motionless in the applied electric field.Figure 9b displays the same type of measurements which are performed using the optimum catalysts.These measurements were carried out without de-agglomeration and sodium nitrate addition.As Figure 9 depicts, the PZCs for 0.08%Pd0.29%Ir/H-Beta(i),0.08%Pd2.9%Ce/H-Beta(i),0.08%Pd 1.9%Ag/H-Beta(i) are at pH ~9.4,9.52, and 9.55, respectively.For these samples (Figure 9b), all of the patterns (ξ = f(pH)) present the same shape, and cross together at the isoelectric point.For 0.08%Pd 0.29%Ir/H-Beta(i), one PZC is reported (Figure 9b).This diversity is perhaps due to the attendance of various frameworks of alumina silica and/or the presence of PdIr in this catalyst.The diversity among the potential surface charges shows that the sorption of Pd and Ir solution types are monotonous.For other catalysts, one peak is detectable as is demonstrated in Figure 9b.As mentioned in other researches, by increasing the electrostatic attraction in the metal complex with a permeating precursor, mono sized and smaller metal particles appear in the catalyst [75].Furthermore, Pd complex which is adsorbed in the precursor has a more monotonous size distribution on the surface of 0.08%Pd 0.29%Ir/H-Beta(i) microporous compared to 0.08%Pd 2.9%Ce/H-Beta(i), and 0.08%Pd 1.9%Ag/H-Beta(i) catalysts.The ξ distribution of surfaces change by changing the support, metal active phase, and promoter.The amount of metalliferous solution that can be adsorbed by the catalysts depends on the value of the surface charge of the catalyst [76].So, various amounts of Pd adsorption complex lead to the formation of various Pd active sites on the synthesized catalysts.

Catalytic Performance in the Selective Hydrogenation of Acetylene
The process mechanism proposes that rapid discharging of the process outlets from the reactor bed results in higher production of products such as ethylene.Rapid discharge of the products could be attained by exerting microporous materials via narrow particle sizes and introducing good mass transfer.Narrow sizes of particles with a superior specific area decrease the diffusion path lengths and increase the surface active sites, which displayed great catalytic efficiency [77].In an acetylene hydrogenation process, the conversion of catalysts is not the unique imperative factor.In a chain process of the kind, acetylene → ethylene → ethane, the ethylene selectivity is also important [78].Acetylene conversion, yield and selectivity in the hydrogenation of acetylene are measured at 1000-6000 h −1 GHSV and 35-65 • C temperature over the total catalysts (0.08%Pd 0.29%Ir/H-Beta(i), 0.08%Pd2.9%Ce/H-Beta(i),0.08%Pd1.9%Ag/H-Beta(i),0.08%Pd0.29%Ir/H-Beta(ii),0.08%Pd2.9%Ce/H-Beta(ii),0.08%Pd1.9%Ag/H-Beta(ii),0.08%Pd0.29%Ir/H-Beta(iii),0.08%Pd2.9%Ce/H-Beta(iii), 0.08%Pd1.9%Ag/H-Beta(iii),0.08%Pd0.29%Ir/H-Beta(iv),0.08%Pd2.9%Ce/H-Beta(iv), 0.08%Pd1.9%Ag/H-Beta(iv))with various R, including 1/1, 3/1 and 5/1 (R = 1, 3 and 5), after reduction at 150 • C. The results of the acetylene hydrogenation process show that 0.08%Pd0.29%Ir/H-Beta(i)catalyst at R = 3, p = 20 bar and GHSV = 4030 h −1 , has the best performance, as displayed in Figure 10 and Figures S7-S21.According to Figures S7-S21, it can be concluded that 0.08%Pd0.29%Ir/H-Beta(i)catalyst has the best performance of the catalysts and is explained below.S21 show the acetylene conversion, ethylene selectivity, and yield with different R. At first, the conversion of acetylene increases with an increase in the process temperature and the selectivity of ethylene and then decreases.The 0.08%Pd 0.29%Ir/H-Beta(i) catalyst has the highest conversion because it has the biggest valency for dissociation and/or activation of hydrogen.In detail, at R of 1, the acetylene activity (conversion) of 0.08%Pd 0.29%Ir/H-Beta(i) catalyst at 35 • C is 5%, and reaches 55% when the reaction temperature increases to 65 • C (Figure S7).The 0.08%Pd 2.9%Ce/H-Beta(i) catalyst has only 3% conversion at 35 • C but when the temperature reaches 65 • C, it has the same conversion as 0.08%Pd0.29%Ir/H-Beta(i)(about 40%) (Figure S8).For 0.08%Pd1.9%Ag/H-Beta(i)catalyst, the highest conversion of acetylene is about 36% at 65 • C, which is the lowest at the same temperature (Figure S9).Also, according to Figures S13-S21 for other catalysts at different R, conversion is as below: at R of 1, the acetylene activity (conversion) of 0.08%Pd0.29%Ir/H-Beta(ii),0.08%Pd0.29%Ir/H-Beta(iii),0.08%Pd0.29%Ir/H-Beta(iv)catalysts at 35 • C are 4%, 1.23%, 1%, and reaches to 49%, 40%, 33%, respectively, when the reaction temperature increases to 65 • C (Figures S13a, S16a, S19a).The 0.08%Pd2.9%Ce/H-Beta(ii),0.08%Pd2.9%Ce/H-Beta(iii),0.08%Pd2.9%Ce/H-Beta(iv)catalysts have only 1.8%, 2.3%, 1% conversion, respectively, at 35 • C but when the temperature reaches 65 • C, they have the same conversion as 0.08%Pd0.29%Ir/H-Beta(i)(about 40%) (Figures S14a, S17a, S20a).For 0.08%Pd1.9%Ag/H-Beta(ii),0.08%Pd1.9%Ag/H-Beta(iii),0.08%Pd1.9%Ag/H-Beta(iv)catalysts, the highest conversion of acetylene is about 45%, 49%, 41%, respectively, at 65 • C, which is the lowest at the same temperature (Figures S15a, S18a, S21a).With the increase of R to 3, the conversion increases quickly and reaches about 99% at 65 • C. Similarly, with R of 5, the conversion of acetylene over 0.08%Pd0.29%Ir/H-Beta(i)increases even faster and reaches nearly 100% at 55 • C. The difference in the activity of the catalysts that have been tested in the hydrogenation of the acetylene process is related to the shape and particle size distribution of active component, specific surface area, and the interplay of Pd and other metals with supports in the catalysts, which will be discussed in the characterization section.The catalysts 0.08%Pd2.9%Ce/H-Beta(i)and 0.08%Pd1.9%Ag/H-Beta(i),0.08%Pd0.29%Ir/H-Beta(ii),0.08%Pd2.9%Ce/H-Beta(ii),0.08%Pd1.9%Ag/H-Beta(ii), 0.08%Pd0.29%Ir/H-Beta(iii),0.08%Pd2.9%Ce/H-Beta(iii), 0.08%Pd1.9%Ag/H-Beta(iii),0.08%Pd0.29%Ir/H-Beta(iv),0.08%Pd2.9%Ce/H-Beta(iv),0.08%Pd1.9%Ag/H-Beta(iv)have the lowest conversion, selectivity and yield owing to the lake of special acidity, and mono and narrow sized crystals during synthesis.As displayed in Figure 10 and Figures S7-S21, the selectivity toward ethylene over the different catalysts decreased in the order of 0.08%Pd 0.29%Ir/H-Beta(i) > 0.08%Pd2.9%Ce/H-Beta(i)> 0.08%Pd1.9%Ag/H-Beta(i),0.08%Pd0.29%Ir/H-Beta(ii)> 0.08%Pd2.9%Ce/H-Beta(ii) > 0.08%Pd1.9%Ag/H-Beta(ii),0.08%Pd0.29%Ir/H-Beta(iii)> 0.08%Pd2.9%Ce/H-Beta(iii)> 0.08%Pd1.9%Ag/H-Beta(iii),0.08%Pd0.29%Ir/H-Beta(iv)> 0.08%Pd2.9%Ce/H-Beta(iv)> 0.08%Pd1.9%Ag/H-Beta(iv).As expected, by increasing the temperature of the bed reactor to 65 • C to the maximum acetylene conversions, optimum yield and high selectivity are achieved at the same GHSV.The 0.08%Pd0.29%Ir/H-Beta(i)catalyst at first displays perfect conversions of acetylene with excellent selectivity to ethylene at 55 • C. It should be noted that, since ethylene is produced as an in-between substance in the selective acetylene hydrogenation process, when the conversion of acetylene is near to 100%, the ethylene selectivity decreases significantly [79].When the temperature of reaction changes from 35 to 65 • C, the selectivity over 0.08%Pd 0.29%Ir/H-Beta(i) catalyst increases and then decreases steadily, from almost 100% (at R = 1) to about −1% (at R = 5).Nevertheless, the selectivity over the other catalyst decreases sharply when the temperature reaches 45 • C and then it faces a reduction to about −40% at 65 • C (in Figures S7-S21).The preferable ethylene selectivity of 0.08%Pd 0.29%Ir/H-Beta(i) catalyst could be owing to the strong synergistic trace of bimetallic PdIr with supports including electronic and geometric effects.As for 0.08%Pd 2.9%Ce/H-Beta(i) catalyst, with an increase in the temperature, the ethylene selectivity decreases rapidly from 90% (at R = 1) to only −10% (at R = 5).As 0.08%Pd2.9%Ce/H-Beta(i)catalyst characterization confirms, poor ethylene selectivity of the 0.08%Pd2.9%Ce/H-Beta(i)catalyst is due to the different nature of the Ce compared to Ir metal on the Beta-based catalyst.Due to the nature of supports, the shape and particle size distribution of active phases and promoters also have a decisive role in the conversion and selectivity.Commonly, an increase in the particle size distribution leads to a reduction of ethylene selectivity and the support effect overwhelms the effect of particle size distribution [54].Furthermore, because the ethylene selectivity decreases sharply when the conversion of acetylene approached 100%, it is necessary to survey the selectivity of ethylene at a fixed acetylene conversion over different catalysts.The selective acetylene conversion over 0.08%Pd2.9%Ce/H-Beta(i)and 0.08%Pd1.9%Ag/H-Beta(i)are significantly lower than that over 0.08%Pd0.29%Ir/H-Beta(i)catalysts, which is due to the agglomeration of metal nanoparticles during the synthesis.The observed increase in the selectivity of ethylene over 0.08%Pd1.9%Ag/H-Beta(i)catalyst after exchanging Ag with Ce metal indicates that 0.08%Pd2.9%Ce/H-Beta(i) is better than 0.08%Pd1.9%Ag/H-Beta(i)and 0.08%Pd0.29%Ir/H-Beta(i) is the best catalysts for this purpose.Figures S7-S12 show that the selectivities of 0.08%Pd0.29%Ir/H-Beta(i),0.08%Pd2.9%Ce/H-Beta(i),and 0.08%Pd1.9%Ag/H-Beta(i)catalysts are 88%, 70%, and 55%, respectively, at R = 3 and reaction temperature of 55 • C, indicating that the bimetallic PdIr catalyst has a better ethylene selectivity than PdCe and PdAg bimetallic catalysts.As shown in Figures S7-S12, the yield percentage of ethylene in acetylene hydrogenation increases gradually with temperature and maximizes at ~55% at 65 • C when the R ratio is 1 and increases rapidly with temperature, reaching to ~84% at 60 • C when R is 3. Nevertheless, with R of 5, the yield percentage drops to negative values at a temperature increase to 55 • C, which is not favorable even though the activity of acetylene is very desirable.The results suggest that the performance of 0.08%Pd0.29%Ir/H-Beta(i)for acetylene hydrogenation is the best with R ratio of 3. It is challenging to obtain high yield of acetylene hydrogenation in large excess of ethylene with industrial Pd catalysts.As for the supported Pd catalysts, promoters are necessary to improve the ethylene selectivity [80].The addition of Ce, Ag or Ir to Pd modifies the geometrical and electronic properties and enhances the ethylene selectivity.It also should be mentioned that the obtained catalyst with Pd nanoparticles have higher selectivity than catalysts reported in the literature (PdTi/SiO 2 (37.5%),Pd/ZnAl 2 O 3 (64%), and Pd/SiO 2 (20%) catalysts synthesized by solvothermal methods at a similar conversion 100, 102).Nevertheless, the selectivity is improved by modifying the conversion species, and the maximum ethylene selectivity (≥88%) at 95% acetylene conversion was obtained by this procedure.The deactivation behavior of the catalysts varies extremely with the crystallite size distribution and support structure.Crystals with a narrow size distribution and moderate micropores retained their conversion longer.Finally, it can be concluded from the FTIR analysis and cata-test that 0.08%Pd0.29%Ir/H-Beta(i)heterogeneous catalyst provided high catalytic activity with low loading level (0.08 wt%), because the Lewis acid catalyst was grafted on the surface of the nanocomposites [81].
There also is a reduction in the undesired oligomerization of alkenes which is followed by the sedimentation of carbonaceous substance.Therefore, the 0.08%Pd0.29%Ir/H-Beta(i)catalyst has the highest selectivity, yield, activity, and stability in the hydrogenation of acetylene process.This conclusion is also confirmed in the literature which summarized that moderate crystallites showed the best catalytic performance.An optimized R is obtained over mesoporous 0.08%Pd0.29%Ir/H-Beta(i)catalysts, which was ascribed to the optimum Si/(Al + SDA) ratios and low diffusion obstacle that facilitate the transport of ethylene products out of the catalyst before they are finally converted to other products [82,83].Figure 11 shows that with increasing GHSV from 1000 to 6000 h −1 at T = 55 • C and p = 20 bar over 0.08%Pd0.29%Ir/H-Beta(i)catalyst, acetylene conversion decreases from about 95% to 90% and at GHSV = 4030 h −1 the ethylene selectivity reaches the maximum (about 88%).
At lower GHSV, where acetylene remains on the catalyst bed for a longer time, hydrogenation of acetylene process occurred, and the selectivity of the products such as ethylene increase.With an increase in GHSV, ethylene forms mainly through hydrogenation of the acetylene process at maximum selectivity.With a further increase in GHSV, acetylene remains on the catalyst bed for a shorter time.Therefore, a reduction appears in the conversion.

Stability
Stability is another significant parameter in catalyst evaluation.Time-on-stream analysis of the 0.08%Pd0.29%Ir/H-Beta(i)catalysts (reduced at 150 • C) in selective hydrogenation of acetylene was performed at 55 • C and 20 bar for up to 15 h, as shown in Figure 12.The activity of 0.08%Pt0.29%Ir/H-Beta(i)catalyst maintains the highest level during the initial 13 h and after 15 h, slowly decreases to 92%.This stable conversion of 0.08%Pd0.29%Ir/H-Beta(i)catalyst could be attributed to low carbon deposition and preferable structure stability.

TPD-C 2 H 2 and TPD-C 2 H 4
Figure 13 shows that in the 0.08%Pd0.29%Ir/H-Beta(i)catalyst, an increase in the temperature of acetylene desorption leads to an increase in the acetylene activity and a reduction in the temperature of ethylene desorption brings a rise in ethylene selectivity.Note that in this process, large amounts of ethylene compete with acetylene.Also, the comparative adsorption between C 2 H 2 and C 2 H 4 is evaluated by the change in Temperature programmed desorption (TPD) temperature that meaningfully modified the C 2 H 2 conversion.Furthermore, according to TPD characterization at low temperatures, 0.08%Pd0.29%Ir/H-Beta(i)catalyst has a better conversion than 0.08%Pd2.9%Ce/H-Beta(i)and 0.08%Pd1.9%Ag/H-Beta(i)catalysts, as is depicted in Figure 10a.

Coke Analysis
To investigate fresh and used (after 15 h stability reaction) catalysts, the carbonaceous pattern was analyzed with Thermal Gravity Analysis-derivative thermogravimetry (TGA-DTG) characterization, which is shown in Figure 14.According to this Figure, the mass loss of 0.08%Pd0.29%Ir/H-Beta(i)-freshcatalyst is negligible (≤1.05%) until about 400 • C. In addition, quantities of carbonaceous types for 0.08%Pd0.29%Ir/H-Beta(i)-used catalyst are very considerable compared to that for the fresh catalyst (the amount of weight loss for the used catalyst is about 8.5% after the catalyst is reduced at 150 • C).DTG patterns show that carbonaceous types on the used-catalyst are reduced at 150 • C and may be omitted at lower temperature near 275 • C. The results of characterization, specially TGA-DTG, show that after reduction of 0.08%Pd0.29%Ir/H-Beta(i)catalyst at 150 • C, there is a minor amount of carbon deposit.Consequently, 0.08%Pd0.29%Ir/H-Beta(i)catalyst, that is reduced at 150 • C, not only is selective and active, but is also stable for acetylene hydrogenation.

Synthesis of H-Beta-Based Catalyst
The Beta-zeolite micro/mesoporous solution was synthesized with a molar ratio of a SiO 2 :b Al 2 O 3 :c Na 2 O:d SDA:e solvent and a, b, c, d, and e parameters were modified during synthesis.To synthesis the support, 70 mM of NaAlO 2 solution was mixed with 95 mM of NaOH solution with slow stirring, then 2 M of TEOS and specified amount of SDA (TPAOH(i) or TPABr(ii) or orpholine(iii) or n-butylamine(iv)) solution was added dropwise into the above mixture precursor with vigorous stirring.The solution was stirred with a hot plate magnetic stirrer for 20 h at 303 K, then it was heated at about 130-170 • C in a PTFE-lined autoclave for 50 h.The Beta-zeolite precursor was accumulated by vacuum filtration, dried at ambient temperature, and calcined with 3 • C/min ratio at about 550 • C for 9 h with static air to remove the templates.
H-type support of Beta-based catalyst was obtained 1-4 times ion-exchanged with a 0.5-2 M NH 4 NO 3 aqueous solution at 110 • C for 4 h with vigorous stirring.After that, the aqueous solution was filtered with a vacuum pump and calcined with 3 • C/min ratio at about 550 • C for 9 h.The resulting supports were denoted as H-Beta(0), H-Beta(i), H-Beta(ii), H-Beta(iii), and H-Beta(iv), and H-Beta(0) was synthesized without using SDA.The amount of Si/(Al + SDA) ratio for different Beta-based catalysts is reported in Table S1 in the electronic supplementary information (ESI) file and an optimum value of Si/(Al + SDA) is reported in Table 2.

Synthesis of Different Catalysts by the Incipient Wetness Co-Impregnation Method
Using a common and facile procedure, we mixed a certain amount of 0.01 M PdCl 2 and 0.2 M HCl, and then we diluted it with DW to obtain H 2 PdCl 4 .All of the samples were synthesized subsequently with the incipient wetness co-impregnation method.0.01-0.1 wt% of Pd, 1-3 wt% of Ag, 1-3 wt% of Ce and 0.1-0.4wt% of Ir were co-impregnated on H-Beta(i, ii, iii, iv)-based catalysts with H 2 PdCl 4 , AgNO 3 , Ce(NO 3 ) 3 •6H 2 O, and IrCl 3 •H 2 O solutions, respectively.Among the four supports that were synthesized, H-Beta(i) was the best support and its characterizations and cata-tests are reported in Section 2. The samples were dried at 100 • C for 9 h and calcined with 3 • C/min ratio at 550 • C for 9 h to obtain the catalysts.The obtained catalysts are reported in Table S2 (for H-Beta(i) support) and the optimum loading of Pd, Ag, Ce, Ir metals (evaluated with ICP analysis) and textural properties of optimum catalysts (evaluated with N 2 -adsorption/desorption, PSD and DLS analysis) are reported in Table 3.The optimum catalysts were denoted as 0.08%Pd1.9%Ag/H-Beta(i),0.08%Pd2.9%Ce/H-Beta(i),and 0.08%Pd0.29%Ir/H-Beta(i).
Crystal size distribution and surface charge (zeta potential) of catalysts were measured with particle size analysis (SZ-100 nanoparticle series instruments) which was performed by DLS (HORIBA, Beijing, China).
XRD patterns were characterized on a Shimadzu XRD-6000 powder diffraction by using Ni-filtered Cu Ka radiation (λ = 0.154056 nm) at 200 mA and 40 kV in the 2θ ranges of 3-90 • with a scan velocity of 4 • min −1 (HORIBA, Beijing, China).
N 2 -adsorption/desorption analyses of supports and catalysts were conducted at 77 K after out gassing the samples at 110 • C for 12 h with a Micromeritics Tristar II 2020 analyzer.The BET procedure was used to calculate the internal and external surface areas (m 2 /g) of the samples using adsorption information in a relative pressure of ~0.05 to 0.2.The PSD was derived from the desorption data of N 2 physisorption analysis applying the Barrett-Joyner-Halenda (BJH) procedure.The entire volumes of micro, meso, and macro-pores V t were estimated by the Horvath and Kawazoe (HK) model (HORIBA, Beijing, China).
The UV-Vis spectrophotometer recorded at the wavelength of about 100-900 nm via a Hitachi UV-Vis (U-4100) instrument.
FTIR absorbance spectra (JEOL Ltd., Shanghai, China) were performed on a FTS-3000 spectrophotometer with wave numbers in the range of 4000 to 400 cm.Two mg of the samples which was mixed with 200 mg of dry KBr was used to prepare the transparent discs.
FTIR spectroscopy (with pyridine as a probe molecule) was used to determine the type and strength of acid sites.All samples were prepared as self-supporting wafers (ca.8-12 mg/cm 2 ) and activated overnight at 350 • C under vacuum prior to pyridine adsorption at 200 • C and at 3 torr.After 20 min of adsorption, the probe molecule was desorbed during 20 min and the corresponding spectrum was recorded with a resolution of 4 cm −1 by using a Nicolet spectrometer equipped with a mercury cadmium telluride (MCT) detector cooled with liquid N 2 .All measured spectra were normalized to 10 mg/cm 2 wafers.Furthermore, different desorption temperatures (200 and 350 • C) were assayed in order to assess the strength of the acid sites, using a desorption time of 20 min at every temperature.The quantity of acid sites was determined using the following bands and absorption coefficients: pyridine Py H+ band at 1545 cm −1 (ε = 1.67 cm/µmol) and pyridine PyL bands at 1461 + 1454 cm −1 (ε = 2.2 cm/µmol) [84].
The weight loss of the fresh and used samples was determined using a TA Q500 thermogravimetric analyzer (JEOL, Beijing, China).The temperature was increased from room temperature to 450 • C at a heating rate of 20 • C min −1 .DTG analysis results of the catalysts were also obtained.
TPD measurements were performed on an AutoChem II 2920 equipped with a quadrupole mass spectrometer (JEOL, Beijing, China).The samples were loaded in the U-tube reactor, followed by reduction at 250 • C for 1 h.After cooling to room temperature, the sample was subjected to acetylene or ethylene adsorption for 1 h, and then purged with He for 30 min.The temperature was increased to 400 • C with a heating rate of 10 • C min −1 .
The metal content was analyzed by an ICP-OES (Optima 3000 DV, Perkin Elmer, EUA, Beijing, China).ICP/OES was carried out using a Varian Vista-MPX CCD Simultaneous ICP/OES device, the used Pd-standard was 10,000 ppm Pd in 5% HNO 3 .Potential Pd leaching into the reaction mixture was also analyzed by ICP/OES analysis.For this purpose, samples were taken through a syringe filter (Whatman Puradisc 4, 4 mm diameter, 0.45 lm, PTFE) during standard heterogeneous Suzuki-Miyaura reactions (reaction temperature: 115 • C), the solvent was evaporated, and the residue was dissolved n HNO 3 .The analysis of these samples with ICP/OES showed that the Pd concentration in the reaction solution was less than the detection limit (i.e., 50 ppb), which corresponds to less than 0.11% of the starting Pd-amount.The same result was obtained when the complete reaction mixture of a standard heterogeneous Suzuki-Miyaura reaction was filtered, the solvent was evaporated, and the residue was dissolved in HNO 3 .Both findings indicate that virtually no Pd leaches from the surface into the solution.The microactivity-reactor was placed inside a hot box (304 stainless steel) insulated with heating capability to 220 • C. A thermocouple with K type encrusted with a 1.5 mm thickness and Inconel covering was placed horizontally via up to down of the micro-activity reactor and was in straight connection with the fixed bed.This scheme permits the analysis of process conditions with answer times of only milliseconds.After passing the streams through a check valve, the reactant inlet streams (H 2 reactant, mixed gas, N 2 carrier gas) were fed into the microactivity-reactor through HI-TEC mass flow controllers by Bronkhorst.To investigate the catalysts using a facile procedure, all of the samples were analyzed for the acetylene hydrogenation process with excess ethylene.Catalyst and quartz sand were packed in a cylindrical microactivity reactor.The packed bed catalyst was reduced in high purity H 2 (99.999%) with GHSV 500 h −1 and N 2 carrier (99.999%) at 150 • C for about 7-9 h and then underwent purging with N 2 carrier before beginning the heating process and switching the reaction to the process condition.Afterward, the furnace of the reactor was fixed for 1 h before being increased to the subsequent process temperature.Table 4 shows the gaseous reactants, that were prepared from the domestic Jam Petrochemical Company (JPC), and H 2 , which were used to obtain different R (1-5), and were fed into the reactor at a GHSV of 1000-6000 h −1 at 35-65 • C and 10-22 bar.The investigation of the mixture product of the microactivity-reactor was done via a GC device (Horiba, Hiroshima, Japan) by a 0.32 mm (i.d.) × 30 m × 1.50 m GS-CARBONPLOT capillary (17A) column working at about ~75

Conclusions
In this research, we successfully synthesized a unique type of Beta zeolite as support with an incipient wetness co-impregnation-solvothermal method.The supports with different shapes such as spherical seed, like clews, stretched nanowire, and gear wheel-shaped were synthesized by adding different values of TPAOH, TPABr, morpholine, and n-butylamine as SDAs while the obtained supports with TPAOH had a standard geometry and less mass transfer limitation.The values of Si/(Al + SDA), surface area, pore size, and crystal size in Beta zeolite supports were modified and the optimum values for TPAOH supports were 19.05, 1358.3 m 2 •g −1 , 10.3 nm and 12 nm, respectively.FTIR patterns showed that the Beta-based catalyst was the most active support in the acetylene hydrogenation process.The optimized weight percentages for Pd, Ir, Ce, and Ag were 0.08%, 0.29%, 2.9%, and 1.9%, respectively.TEM analysis showed that Pd and Ir bi-metals were very mono sized and mono dispersed on the support surfaces.Cata-tests showed that 0.08%Pd0.29%Ir/H-Beta(i)catalysts have an optimum acetylene conversion (about ~97%), high selectivity (near ~92%), and maximum yield (about ~99%) at optimum GHSV and reaction temperature which were 4030 h −1 and 55 • C, respectively.Stability tests displayed that 0.08%Pd0.29%Ir/H-Beta(i)catalysts were stabilized after 15 h.TGA-DTG analysis demonstrated that after reduction at 150 • C, the optimum catalysts had insignificant carbonaceous spaces.

Figure 5 .
Figure 5. (a) X-ray powder diffraction (XRD) patterns of the parent Beta zeolite with different SDA; (b) XRD patterns of the corresponding optimum catalysts.
• C and 350 • C. Various intensities are detected in the zone of 1800-1300 cm −1 , as shown in Figure 7a,b.

Figure 13 .
Figure 13.Temperature programmed desorption (TPD) pattern of acetylene and ethylene desorption on optimum catalysts.

Figure 15 .
Figure 15.Schematic flow diagram of the fixed-bed tubular microflow reactor.MFC: mass flow controller.

Table 2 .
Textural properties and optimum metal loading of the H-Beta(i)-based catalysts.

Table 3 .
Amounts of Lewis (L) and Brønsted (B) acid sites determined by Fourier-transform infrared spectroscopy (FTIR) of pyridine adsorption for various catalysts.

Table 4 .
Specification of inlet stream.
• C and an Flame Ionization Detector (FID) indicator.The calculations of conversion, yield, and selectivity are defined as follows: