Proton Exchange Membrane Fuel Cell Reversal : A Review

The H2/air-fed proton exchange membrane fuel cell (PEMFC) has two major problems: cost and durability, which obstruct its pathway to commercialization. Cell reversal, which would create irreversible damage to the fuel cell and shorten its lifespan, is caused by reactant starvation, load change, low catalyst performance, and so on. This paper will summarize the causes, consequences, and mitigation strategies of cell reversal of PEMFC in detail. A description of potential change in the anode and cathode and the differences between local starvation and overall starvation are reviewed, which gives a framework for comprehending the origins of cell reversal. According to the root factor of cell starvation, i.e., fuel cells do not satisfy the requirements of electrons and protons of normal anode and cathode chemical reactions, we will introduce specific methods to mitigate or prevent fuel cell damage caused by cell reversal in the view of system management strategies and component material modifications. Based on a comprehensive understanding of cell reversal, it is beneficial to operate a fuel cell stack and extend its lifetime.


Introduction
At present, the proton exchange membrane fuel cell is the most promising energy system used in commercialized electric vehicles; it has the following advantages: low-temperature operation (50-100 • C), high power density (40%-60%), nearly zero pollutants compared to conventional internal combustion gasoline vehicles, simple structure, and so on [1,2].However, during the PEMFC technological development, there are two primary barriers to commercialization-durability and cost [3].
Cell polarity reversal occurs frequently in standard fuel cell operating conditions.In such a condition, there is some irreversible damage to fuel cell stack material, including flow field plate, membrane electrode assembly (MEA), and other constructional elements, which seriously affects the durability of PEMFC.There are two principal approaches to solving this problem.The first is a system control strategy whereby specially designed software would monitor anode and cathode outlet exhaust gas composition, cell voltage, and local density variation response.The software would then regulate fuel/air stoichiometry, cell temperature, current density, water management, and any other operating parameters to minimize fuel cell reversal damage [4][5][6].Although the system control strategy can be an effective and efficient method to extend a fuel cell's lifespan, it would require a peripheral sensor to monitor and feedback information, and even to regulate the system parameters for steady operation.In fact, it does not take long for cell reversal damage to occur.The extra equipment involved would not only increase system complexity and decrease cost efficiency, but also cannot address cell reversal in time.Therefore, there is a second more direct strategy, system hardware material modification.Because all forms of cell reversal damage eventually lead to system material degradation, optimized materials would minimize cell reversal and improve fuel cell durability in nature.This paper presents the causes, types of damage, and improvement approaches related to cell reversal in a fuel cell.

PEMFC Cell Reversal Description
In a single fuel cell or fuel cell stack system, electrode potential drives chemical reactions, including hydrogen oxidation reaction (HOR), oxygen reduction reaction (ORR), carbon corrosion, and water electrolysis.In normal operations, there are excess hydrogen and air supplied to the anode and cathode, respectively.HOR and ORR take place in the anode and cathode, respectively, to produce sufficient amounts of electrons and protons.Nevertheless, there are many extreme operations or conditions, such as insufficient supply of reactant [5][6][7], low catalyst performance, uneven gas distribution, drastic current load change, and startup or shutdown operations [8], which would result in potential change.In PEMFC cell reversal, the experiment polarity curve shows that the anode potential increases and the cathode potential decreases, narrowing the electric potential difference and even reversing for several seconds.The fuel cell stack cannot work normally anymore and will consume energy instead of supplying energy.As a result, hydrogen and oxygen would be present in the wrong electrode components of fuel cell, which induces a corresponding potential change.In each cavity, all kinds of matter spontaneously recombine and react with each other to make the system right.However, because of the wrong initial conditions, the result cannot match what the fuel cell should be.
As shown in Figure 1, the fuel cell was subjected to cell reversal test experiment (hydrogen starvation).Figure 1 illustrates the time-dependent change in the anode and cathode potentials versus RHE in hydrogen starvation.The cell terminal voltage quickly changed to a negative voltage, from 1.0 to −2.0 V [6].This will be discussed in more detail in Section 3.1.1.2004) [42][43][44][45][46][47][48][49] ard hydrogen electrode by a H 2 SO 4 as used as shown in Fig. 1.For this ousing made from PTFE, the cell B, t collectors were made from titanium.electrode was filled with 1 M H 2 SO 4 iton ® gasket is located between eleceous solution.The standard hydrogen ted to the membrane at the periphery M H 2 SO 4 aqueous solution as shown [16].

by TEM, EDX, and XPS
emoved from the MEA for preparation d carbon paper was peeled from both he cross-section of the MEA sample xy impregnation and ultramicrotome mond knife.Samples for the TEM obtly supported on a copper mesh with The TEM observation was performed 00F electron microscope at an accel-kV.The particle size distribution mearmed on digital images using the ime Image-Pro.The TEM was equipped ice for analysis of the elemental comze region.MEA sample was also characterized g a field emission scanning electron M-6700FA, Jeol) equipped with EDX r elemental analysis of the MEAs.rements, a small piece removed from paper on both sides was placed on the easurements of the catalyst layer were IMADZU ESCA-3400.Since reprothe catalyst layer from the membrane is shown in Fig. 2. In addition, this figure shows the time-dependent change of the anode and cathode potentials versus RHE.It was observed that the cell terminal voltage rapidly dropped to the negative voltage and the MEA changes polarity due to cell reversal as soon as the experiment started.After this initial rapid drop, the cell terminal voltage showed a steady decrease with time.Cell reversal occurred when the anode potential increased and became more positive than the cathode potential.The anode potential quickly increased to near 1.5 V.This result indicates that the anode potential increased until water electrolysis occurs as soon as the experiment started since the anode was starved of fuel [9].
Fig. 3 shows I-V curves of the cell after different experimental periods during the cell reversal test using the cell In the case of air starvation, there is another type of cell reversal detected in currency to voltage (I-V) image.In Figure 2, we can see that cell voltage decreased rapidly to become negative when the cell reversal experiment started (air starvation).After the initial drop, the anode potential, cathode potential, and cell voltage all reached constant values but remained near zero [5].
Fig. 3 shows I2V curves of the cell after different experimental periods during the cell-reversal test using cell A. These curves were measured when enough air, 300 cc=min, was supplied.An increase in the experimental time lowered the original performance of the cell.The internal resistance did not show an obvious change with the experimental time.With pure hydrogen fuel, the anode overpotential can usually be considered to be almost negligible [20].Therefore, this degradation may be attributed to the deterioration of oxygen reduction performance of the cathode catalyst.
In situ cyclic voltammetry is useful for assessing the electrochemically active surface area of the MEA catalyst layer.This method was used to compare the electrochemically active surface area of the fuel cell cathodes.Fig. 4 shows the cyclic voltammograms before and after the cell-reversal experiments.The effect of cell reversal on hydrogen adsorption and desorption is shown.The hydrogen adsorption and desorption area, the electrochemically active surface area of the cathode, decreased during the cell-reversal experiments.First, we showed that the process of the cyclic voltammetry measurement itself did not contribute to the hydrogen adsorption and desorption features.Therefore, these findings mean that the electrochemically active surface area decreased with the duration of the cell-reversal experiment.The time dependency of the electrochemically active surface area derived from the hydrogen desorption area is shown in Fig. 5.The electrochemically active surface area decreased with time and was saturated at a decrease of approximately 46% at 120 min of cell reversal, as shown in Fig. 5 (solid line b).However, this change cannot be attributed solely to cell reversal.The electrochemically active surface area of MEA decreases to some extent upon normal fuel cell operation at the same current density with adequate air supply.The time dependency of the electrochemically active surface of MEA in normal cell operation is also shown in Fig. 5 (dashed line a).Such a decrease in the electrochemically active surface of platinum can usually be seen in new MEA at an early stage of cell operation.However, this figure suggests that the decrease in the electrochemically active surface area in cell-reversal experiment is much greater than in normal operation.
A TEM analysis was performed on the cathode catalyst layer of the MEA.Fig. 6 shows TEM images of the sample at the air outlet region, location B, before and after the cell-reversal experiment for 120 min.In the sample before the experiment, the smallest detected particles have a size of 1.0-2.0nm, as can be seen in the image (Fig. 6a).However, these smallest particles disappeared and particles grew in the image of the sample after the cell-reversal experiment, as seen in Fig. 6b.Fig. 7 shows the particle size distribution for cathode catalysts determined from the TEM images.The average particle size increased from 2:81 nm, the value before experiment, not only  Fuel starvation results in a markedly different level of cell reversal compared to air starvation.Cell terminal voltage is much larger with low fuel feed compared to low air feed.The damage to material under low potential is less serious than the high potential caused by hydrogen starvation.From this point, we can understand that the damage of fuel starvation could be caused by gas supply and flow field diffusion.In view of keeping reactant diffusion steady, and considering gas diffusion layer design, flow field design, and membrane gas permeation, the assembly of different layers should attract more attention.In the meantime, how to eliminate interface effect is also a point to be researched.Steadier system operation conditions will mean a longer lifetime.

ARTICLE IN PRESS
Due to the carbon corrosion in cell reversal, polarity curve, gas chromatography (GC) and differential electrochemical mass spectrometry (DEMS) can be the main in situ measurements to analyze the extent of carbon corrosion, the exhaust gas compositions, and the anode or cathode outlet contents [9][10][11].These techniques can realize online detection of carbon dioxide generated by carbon corrosion.After cell reversal, energy dispersive X-ray analysis (EDX), transmission electron microscopy (TEM) [6], scanning electron microscopy (SEM), X-ray diffraction (XRD), electrochemical impedance spectrum (EIS), inductively coupled plasma (ICP), and Raman Spectroscopy are the main means used to characterize the status of the catalyst layer (CL), catalyst nanoparticles sintering, and carbon corrosion extent [10,[12][13][14][15].These methods analyze CL morphology, catalyst distribution, elemental content, atomic structure, and impedance, respectively.
In a fuel cell reversal system experiment, there is a three-step protocol to test and categorize the electrode's reversal tolerance [16].The point of this protocol is to build fuel starvation by replacing H 2 content with humidified N 2 to measure the performance of MEA after cell reversal.Specifically, Step 1, MEA should be in the condition of cell reversal for a long time, with a period of H 2 supply.Step 2, MEA is in the cycle between cell reversal and normal H 2 supply every 30 s. Step 3, MEA would be in cell reversal until the cell potential is −2.0 V.In the whole test procedure, the anode outlet air would be measured for the concentration of CO 2 and O 2 .
To simulate and design cell reversal experiment, sub-stoichiometric reactant feeding is the first step.Then, regulating the fuel and air ratio should take a more important place for cell reversal data image.The data collection should include I-V image, different electrode potential of time-dependent like Figures 1 and 2, localized current and potential change across the electrode plane, and so on.

Causes of Cell Reversal
The main cause of cell polarity reversal is that the fuel cell cannot satisfy the requisition of the electron and proton from the normal anode and cathode chemical reactions [17].This key factor occurs in some improper or nonstandard operations, such as fuel and air sub-stoichiometric feeding, rapid load change, low catalyst performance, control module failure, and so on.During a sudden load change or incorrect operation, such as start-up or artificial reasons, fuel and oxidant starvation would occur.Li et al. [18] found that the cell performance loss was induced by the rapidly changing load frequencies resulting in catalyst particles' growth and agglomeration in the anode.This is a typical example where the mass transfer rate cannot match the load change rate.
In the fuel cell stack or galvanostatic operation of a single cell, other cells with sufficient reactant or the single cell system would electrolyze the sick cell for the specified electron and proton or location of saturated fuel supply electrolyze sub-saturated area.There are three key points to define the sick fuel cell: (1) low electrode performance; (2) low fuel supply; (3) low air or oxygen supply.By filling the current requirements, the sick cell would be self-abandoned to conduct some different reaction under high potential, like carbon oxidation, water oxidation in an anode, or hydrogen evolution in a cathode [17].Hydrogen evolution occurs in the cathode catalyst layer, close to the proton exchange membrane; hydrogen re-oxidization is in the other part of the cathode catalyst layer; and ORR occurs between the cathode catalyst layer and the cathode gas diffusion layer.
Sanyo Electronics previously studied the performance degradation of fuel cell caused by fuel starvation [19].Then, Kim et al. [20] researched the effect of stoichiometry on the dynamic behavior of a PEMFC during load change, and found a vacuum effect in fuel starvation.Hydrogen utilization was significant to overshoot or undershoot behaviors.Taniguchi et al. [6] designed an experiment using a single cell to simulate cell reversal in a stack.
An abrupt change in oxygen demand at the cathode, like start-up operation, load change, or water management failure, would induce air starvation.Rao et al. [21] developed a distributed dynamic model including three layers (the gas flow channel, the diffusion layer, and the reaction layer) in a cathode to discuss the problem of gas starvation.There are many reports about current distribution and degradation caused by air starvation [5,22,23].In these papers, current distribution is relevant to matter diffusion.The different reactant combinations in different layers have various reactant reaction modules.Due to reaction spontaneity and external drive, electron transfer and high potential occur at the same time.
All of the experiments reported above show that reactant starvation would change anode or cathode reaction conditions and lead to abnormal chemical reactions in high potential.These reasons would complicate the situation of the electrode surface.The following section will discuss in detail the specific situation, causes, and effects in view of a PEMFC anode and cathode.

PEMFC Anode
Compared to air starvation, complete hydrogen starvation will induce high potential to lead to carbon corrosion.Generally speaking, its impact on fuel cell is more far-reaching and thorough.So we pay more attention to cell reversal caused by hydrogen starvation.
In normal operations, excess hydrogen and air are supplied to the anode and cathode, respectively, whereby hydrogen and air distribution in the two compartments meet the mass transportation requirement.However, local fuel starvation induced by heterogeneous fuel distribution and complete fuel starvation in the whole anode have different effects in the whole anode.These two hydrogen-deficient conditions are similar but the damage to the fuel cell is completely different, and in fact heterogeneous fuel distribution cannot cause cell reversal but current reversal [24].Local fuel starvation, or partial hydrogen coverage, damages the air electrode and induces oxygen migration across the membrane from the cathode [25,26].There are two mathematical guides to help us distinguish between and get a clear picture of these two situations by demonstrating electron diffusion and gas flow.
Complete hydrogen starvation: Equation ( 1) depicts the practical status of fuel cell operations in the whole fuel starvation.In this equation, N is the molar flow of hydrogen, I is the practical current, and F is Faraday's constant.Without enough hydrogen to support the required current, the cell has to oxidize other cell system materials such as water and carbon at the fuel electrode to produce electrons and protons.Obviously, the fuel cell must be a single cell during galvanostatic operation or in a fuel cell stack where other cells have excess hydrogen supply.
Partial hydrogen coverage: Equation ( 2) shows the local hydrogen starvation.Here, A is the active area and I lim is the limiting current density on active area.According to the equation, enough hydrogen is fed to the anode to satisfy the necessary current, but the fuel distribution is uneven in the gas distribution layer (GDL).Finally, the partial electrode area is not fed with adequate fuel.Oxygen in the cathode is permitted to migrate to the anode across the membrane to form the potential in some fuel-deficit areas to produce electrons, resulting in the average current value being higher than the limiting current.Some active areas have the same cell potential difference as a normal fuel cell, about 0.8 V. Nevertheless, other negative regions' cell potential is lower than 0.8 V but more than 0. This potential difference between the anode and cathode can be due to partial pressure discrepancy.So this situation cannot induce cell reversal but it will cause current reversal.Patterson and Darling studied the damage caused by local fuel starvation to the cathode catalyst [27].The experiment showed that the situation of local fuel starvation is not similar to cell reversal caused by fuel starvation.
Only when the low hydrogen stoichiometry is less than 1 can the fuel cell polarity be reversed in the condition of a single-cell galvanostatic operation or a fuel cell stack where other cells have excess hydrogen supply.Obviously, all mechanisms and consequences of local fuel starvation would also occur at some location of the CL during overall fuel complete starvation [15].In fact, the relationship between local fuel starvation and complete hydrogen starvation is just a qualitative change induced by a different hydrogen degree.
Different fuel flow fed to the anode provokes different phenomena on its electrode surface.Fuel starvation induced uneven currency diffusion, which had an increasing trend in the anode inlet and a decreasing trend in the outlet [4]; hydrogen oxidation reaction and water oxidation occurred at different regions of the electrode simultaneously.Due to the lack of hydrogen supply, which cannot satisfy the fuel cell system's electron requirements, the fuel cell system would spontaneously increase the anode potential as a result of an abnormal reaction or cell performance degradation, such as water oxidation, carbon corrosion, and so on, to obtain extra electrons [28].In a galvanostatic operation or fuel cell stack, it will decompose the electrode material or the sick cell, like an electrolytic cell.
Therefore, in this condition, oxygen is simultaneously reduced in the cathode while oxygen is produced in the anode.The final consequence is that oxygen is pumped from cathode to anode while water moves in the opposite direction.The cell is similar to an "oxygen pump".We can use GC to test the anode production online [23].The electrode half reactions and the overall reaction are listed below: Water oxidation is the initial main reaction in a fuel cell, caused by fuel complete starvation in the anode.While the cell reversal experiment proceeds, the cell voltage becomes more and more negative.
In Figure 1, we can see that the anode potential could be more than 1.5 V and the cathode is about 0.85 V at the first decreased stage.So the cell voltage is less than −0.65 V.At the next stage, the anode potential would become so high that carbon could be corroded gradually, especially with a platinum (Pt)-based catalyst, which would promote carbon corrosion.Finally, the cell voltage would get close to −2.0 V until the fuel cell cannot function.
According to Equations ( 3), (10), and (11), corrosion in the anode, water oxidation, and carbon would produce heat to dehydrate the anode ionomer and membrane electrolyte.When the cell voltage reaches −2.0 V, the membrane would be completely degraded by dielectric breakdown [16].We can judge which cell reversal strategy is best based on the time it takes the cell to reach −2.0 V in order to avoid cell reversal causing irreversible damage.The better strategy should have a longer time to reach −2.0 V of cell potential.
Aside from the cell polarity change, local current density and temperature also have special distribution across the CL in cell reversal.Zhang and his team analyzed dynamically the local current densities and temperatures in proton exchange membrane fuel cells during reactant starvations [7].The dynamic variations of local current densities with cell voltage and local temperatures during hydrogen starvation are studied.In this experiment, the hydrogen flow rate was held at 50 NmL•min −1 (equal to average current density of 450 mA•cm −2 ).In the average current controlled operation, it was set to increase from 440 to 470 mA•cm −2 to mimic fuel starvation.We can see that at the initial stage in this experiment, about 10 to 20 s, carbon corrosion is less than water oxidation, as indicated by a relatively stable current density variation.Then the local current densities began to diverge.The closer the location is to the anode inlet, the larger the current density.The outlet area had the completely opposite case.The local temperature variation was similar to local current density.Without a stable −0.2 V cell voltage during fuel starvation [16,29], current density and temperature would be so divergent that the MEA would fail.The temperature and current density show a relatively clear picture to explain the electrode reaction.
In addition, cell reversal caused by hydrogen starvation would induce an abnormal oxidation reduction reaction at the electrode surface plane.There are different situations in different hydrogen feeding stoichiometry.
Akira Taniguchi et al. discussed and analyzed electrocatalyst degradation in PEMFC caused by cell reversal during fuel starvation [6].The ruthenium dissolution occurred in the anode catalyst layer and the outlet had more severe degradation.There was also surface activity area loss in the cathode.The standard potential of transition metal couple is smaller than the electrode surface potential.Hence, some transition metal dissolution and redeposition are likely to occur.This is why the catalyst particle size becomes bigger than before cell reversal.In fuel starvation, the anode reaction is complex, involving hydrogen oxidation, water oxidation, carbon corrosion, and oxygen reduction.All of these reactions involve proton and electron transfer, which promote potential difference across the electrode plane.Reaction correspondence cannot be executed across the anode plane.It would simply get worse and worse until the system is dead.
Liang et al. focused their attention on a single cell under different degrees of fuel starvation [30].They measured some electric parameters, such as cell voltage, current distribution, cathode and anode potentials, local interfacial potentials between anode and membrane, and so on, by means of a specially constructed segmented fuel cell.Experimental results showed that the current distribution was extremely uneven during fuel cell reversal, due to starvation or high local interfacial potential near the anode outlet.Hydrogen and water were oxidized at different areas of the anode.Anode carbon corrosion was proven to occur by monitoring its outlet's CO 2 concentration.Figure 3 shows that the anode potential became higher and higher with the decrease of hydrogen stoichiometry, and water oxidation gradually took on an important role in the current contribution.Simultaneously, carbon corrosion was more and more serious than before.The comparison between cell reversal voltage and anode potential under different hydrogen conditions is shown in Table 1.Different hydrogen stoichiometry creates different terminal cell potential.affected by the fuel cell test device.Taniguchi's test result was not steady even 300 s after the experiment started, as compared to Liang's.It involves support material, test device design, sealing, and so on.They also proposed that the hydrogen stoichiometry would shift the position of the lowest current [31].With a comparatively high hydrogen feed, the position of the lowest current was closer to the anode outlet, where the fuel feed would encounter the gas drawn back from the outlet manifold and fuel starvation first occurred.The inadequate hydrogen supplied and "vacuum effect" would mix in the fuel cell.In this situation, researchers could analyze the area of fuel starvation in the anode according to the hydrogen stoichiometry to design a catalyst layer of anisotropy to avoid or mitigate the fuel starvation caused by inadequate fuel feed.

PEMFC Cathode
When the real-time current exceeds the limiting current for ORR, air starvation occurs.In this case, the cathode voltage approaches the potential of reversible hydrogen due to the existence of hydrogen evolution.The potential of the cell is slightly negative in this condition, which is smaller than the hydrogen starvation.At this comparatively low potential value, it is hard to corrode carbon material.
In the PEMFC cathode, oxidation supply and the obstruction of gas channels caused by water flooding or freezing are the main causes of cell reversal.The causes also include control system failure and incorrect operation.Water flooding or ice would block the access of the reactant gases to the  With the change of cell voltage over time, fuel cell system would begin to search reaction balance.In the anode, a compromise between hydrogen oxidation, water oxidation, and carbon corrosion move anode reaction from chaos to relative balance.Hydrogen stoichiometry has a different influence on the anode when it is lower than its satisfied supply.However, the experimental result is also affected by the fuel cell test device.Taniguchi's test result was not steady even 300 s after the experiment started, as compared to Liang's.It involves support material, test device design, sealing, and so on.
They also proposed that the hydrogen stoichiometry would shift the position of the lowest current [31].With a comparatively high hydrogen feed, the position of the lowest current was closer to the anode outlet, where the fuel feed would encounter the gas drawn back from the outlet manifold and fuel starvation first occurred.The inadequate hydrogen supplied and "vacuum effect" would mix in the fuel cell.In this situation, researchers could analyze the area of fuel starvation in the anode according to the hydrogen stoichiometry to design a catalyst layer of anisotropy to avoid or mitigate the fuel starvation caused by inadequate fuel feed.

PEMFC Cathode
When the real-time current exceeds the limiting current for ORR, air starvation occurs.In this case, the cathode voltage approaches the potential of reversible hydrogen due to the existence of hydrogen evolution.The potential of the cell is slightly negative in this condition, which is smaller than the hydrogen starvation.At this comparatively low potential value, it is hard to corrode carbon material.
In the PEMFC cathode, oxidation supply and the obstruction of gas channels caused by water flooding or freezing are the main causes of cell reversal.The causes also include control system failure and incorrect operation.Water flooding or ice would block the access of the reactant gases to the electrocatalyst surface and result in a slower mass transport rate compared to the oxygen reduction reaction and a relative absence of cathode reactant.There are three ways for the PEMFC cathode to generate excess water, i.e., humidified hydrogen and air to optimize the interaction between the interface and reactant, the reaction product in the cathode, and water migrating across the membrane by electro-osmotic drag with protons [5].
Combined with Figure 2, it is evident that the final cell voltage in cell reversal caused by air starvation was close to −0.1 V, which is much lower than the fuel starvation including anode and cathode voltage.Because potential is the driving force of electrochemical reaction, with high potential it is easier to realize carbon corrosion, catalyst metal dissolution, and sinter.Fuel starvation at the PEMFC anode results in irreversible damage to the PEMFC after several minutes under higher potential and is more critical than improper gas supply or distribution at the cathode [15].
When oxidation starvation happens, protons and electrons produced in the anode enter into the cathode.Simultaneously, hydrogen is consumed in the anode and produced in the cathode.Protons act as a "hydrogen pump" [23].The electrode half reactions and the overall reaction are listed below: Cathode: Overall: Regarding air starvation, researchers have focused on its causes, its dynamic characteristics across the anode plane, and the relationships between air feed and fuel cell degradation.Tüber et al. focused on the water flooding phenomenon at the fuel cell cathode caused by an accumulation of H 2 O [32].They analyzed the effect of air flow, humidity, temperature, and flow-field type on flooding.
Zhang et al. also detected the dynamic characteristics of local current densities and temperatures in proton exchange membrane fuel cells during air starvation under current controlled and voltage controlled operation [7].Their experimental results were obtained at different times and relative positions.This paper demonstrated that the local temperature changes followed the local current density changes during experimental operation.It is similar with hydrogen starvation.Due to reactant starvation, anode and cathode chemical reactions cannot follow normal operations.It refers that a mixture of gas evolution, reactant oxidation, and reduction reaction occur in anode or cathode.According to different reactions' energy change, there must be a relationship between electrode temperature and current density.
Taniguchi et al. researched degradation in PEMFC caused by cell reversal during air starvation [5].They detected catalyst samples by means of cell reversal experiment and analyzed electrochemical performance, such as electrochemical surface area (ECSA) and current-potential character, using TEM images to illustrate that the size of catalyst particles increased, agglomerated, and recrystallized.Obviously, this degradation effect caused by air starvation was smaller than fuel starvation.It is shown in Figure 4 that ECSA shrinks as a function of time.In high electrode potential, it is easier to make catalyst particles dissolve and agglomerate.Similarly, it also will impact fuel cell durability and performance.Improving catalyst electrode surface diffusion is a feasible method to mitigate its sinter.
by operation under cell reversal but also by normal operation.The average particle size reached 4.16 nm at the air inlet region, location A, and 4.83 nm at the air outlet region, location B, with cell reversal.On the other hand, the average particle sizes for a normally operated cell were 2.92 nm at the air inlet region and 2.84 nm at the air outlet region.The results in these figures suggest that the particle size after cell-reversal experiment was much larger than that after normal operation.The smallest particles with a size below 2.0 nm disappeared in the sample at the air inlet region after the cell-reversal experiment, as seen in Fig. 7a.In the image of the sample at the air outlet region, even the particles with a size of 2.0-2.5 nm disappeared, as can be seen in Fig. 7b.The average particle size of cell reversal at the air outlet region was greater than that at the air inlet region.This phenomenon was not seen in normally operated MEA.These results mean that degradation is more severe in the region starved of oxygen.A loss of platinum surface area through sintering or recrystallization within the porous cathode has been proposed to be the reason for the decrease in activity in low temperature fuel cells [8,21].Such catalyst degradation can occur through the surface migration of platinum and platinum   Natarajan et al. researched the relationship between cell temperature, anode and cathode gas streams humidity, and oxidant flow rate and current density distribution in a single-channel PEM fuel cell using a segmented collector setup [33].The relationship between various oxidant flow rates and current densities in segment downstream was studied specifically.However, this setup also had its limitations in that this result did not include data from when the test temperature is over 55 • C. A local current density map at various test conditions is an accurate experimental measurement.With this method, we can analyze and understand the chemical reaction situation at the local electrode surface and the layer interface.

Consequences of Cell Reversal
There are some specific situations in anode and cathode above.Then, we put more attention on fuel starvation due to the permanent damage caused to the fuel cell.Hydrogen and air starvation are the main factors in cell reversal.Compared to air starvation, anode potential is increasing in fuel starvation.Once anode potential rises over 0.207 V, or further to over 1.23 V with fuel consumption, water electrolysis and carbon oxidation would occur at the anode to provide the protons and electrons required for the load and the ORR at the cathode [16].
There are some other reactions happening under higher potential, like carbon reacting with water [34].
Anode : As an indispensable component of the fuel cell system, carbon supports tend to corrode with water to produce CO 2 at high potential [28].Thanks to a large number of micropores, catalyst particles can be physically segregated by carbon supports to prevent particle sintering and catalyst dissolution, which can improve catalyst particles' specific surface area [35,36].On the other hand, under cell reversal conditions, the advantages presented above would be reversed due to the degradation of the catalyst layer structure.Without integrated carbon support structure, three degradation effects would occur: (1) Pt particle agglomeration and particle growth; (2) Pt loss and redistribution; and (3) poisonous effects caused by contaminants [13].Due to the inherent tendency of catalyst nanoparticles to agglomerate to reduce the surface energy, without the limit of support carbon it would promote deterioration of catalyst performance.Low catalyst performance would inhibit electron and proton production for the anode.With the low chemical reaction rate, the anode would only seize carbon and water as reactant material for ORR.This creates a vicious cycle that leads to fuel cell degradation and obsolescence.In the end, the fuel cell would be in a dynamic balance for several chemical reactions on the cathode and anode plane or interface.
However, in air starvation conditions, because of the lower anode and cathode potential, 0.05 V at anode and 0.85 or 0.05 V at cathode (localized ORR and HOR, respectively), carbon corrosion is unlikely to occur [24].Instead, the mixture of oxygen and hydrogen may damage the fuel cell, due to the large hydrogen explosion ranging from 4% to 75.6% that is likely to occur at room temperature in a narrow and airtight space.Elsewhere, with the reduction of water and high cell voltage, the membrane would be completely degraded and broken apart.Air starvation does not have a direct or serious effect on electrodes compared to fuel starvation.

Mitigation Strategies
In the case of cell reversal, there are many approaches to attenuate or solve this question, such as system management and material modification.This review will discuss two ways to summarize cell reversal failures.System strategies mainly monitor operation parameters and feed it back by adjusting gas flow and load change, and controlling gas humidity and system temperature.Because the system management method should consider material features, we mainly pay attention to the role of electrode material and catalyst layer design.The quality and design of fuel cell installation are key to solving fuel cell system failure.Thus, in terms of materials, we focus on three parts: high performance catalysts, carbon support materials, and water oxidation reaction.Because the damage caused by air starvation is less than that caused by fuel starvation, we focus on the design and structure of the anode CL.For the cathode, researchers [37] adjusted the porosity of GDL to improve gas diffusion and changed the supported material to optimize the transformation of oxygen and water.

System Management Strategies
System management mitigates catalyst degradation by regulating fuel cell system operation parameters such as pressures, cell temperature, humidity levels, and current density [38].With auxiliary equipment, researchers can detect reverse cell potential by monitoring cell voltages of individual cells or groups of cells in the stack [39].Combined with current density distribution and temperature distribution detected by electrode segmentation technology [40], researchers can also understand the situation of cell starvation specifically.Furthermore, by setting an alarm value on the monitored cell voltage, the system can adjust operation parameters such as reactant flow rate, operation load, and water management data, and so on to avoid cell reversal or system halt situations.For instance, a sensor in the cell test system activates a switch that plays the role of removing the stack load the instant the sensor detects a precipitous loss of voltage [41].
Vahidi et al. proposed a fast-responding auxiliary power source to prevent oxygen starvation in a fuel cell during rapid current transitions [42].In the oxidation starvation experiment of increasing stack power, the reactant starvation was less than 1% in the hybrid installation.An image of the hybrid installation follows.In the schematic, a capacitor was used to provide deficit current when the power sensor gives a signal.With capabilities of model predictive control, it can mitigate cell reversal damage in air starvation.However, it is transitory for fuel starvation to make carbon corrosion.This auxiliary installation cannot support adequate current in fuel starvation.

System Material Modification
Compared to the system management strategy, the design and composition of a fuel cell structure are more important, especially in terms of preventing cell reversal.While there are additional accessory costs, improving corrosion resistance naturally increases the fuel cell lifespan.Due to the high potential, slow reaction rate, and reactant transfer rate, which cannot meet current density in fuel cell stacks and in galvanostatic operations, researchers focused on the three aspects previously discussed-catalyst, carbon material, and water oxidation reaction.
Specifically, there are four approaches used to attenuate performance degradation and extend fuel cell lifespan [11,15,37].
Water oxidation catalysts to promote water oxidation instead of carbon corrosion; 4.
Increasing anode gas humidity.

High-Performance Catalyst
Low-performance catalysts would induce low anode and cathode reaction rates without sufficient protons and electrons supported in cell stacks and galvanostatic operations.However, in normal operation, Pt-based catalysts could meet the requirements of HOR and ORR due to their excellent catalyst performance [43].
Catalyst dissolution and agglomeration would occur via carbon support material corrosion [44], Pt loss [13,45], and surface energy reduction during standard fuel cell operations.Generally, the dissolution of Pt in the anode was more stable than in the cathode because of the electrode potential; the Pt particles' dissolution follows Equations ( 12) and ( 13) into Pt 2+ , and the standard equilibrium potential is +0.88 V vs. RHE [46].However, in cell reversal, the potential polarity is changed so that catalyst metals have high ORR potential with carbon support corrosion.
Pt-based catalyst dissolution is more common during cell reversal in the anode.According to the metal couple potential, different catalyst metal dissolution and redeposition occur.Furthermore, the catalyst particle size becomes bigger as a result of the electrochemical surface area decreasing.Then, it also would induce activity degradation and the potential would grow higher and higher.Obviously, this is another vicious cycle.
High durability and catalyst activity are the keys to solving this problem.Pt-alloy catalysts have better activity and stability compared to traditional Pt/C catalysts, like Pt-Co and Pt-Cr-Ni [47].The different alloy elements and the larger size of catalyst particles show excellent properties [48].With high catalyst activity to decrease ORR or HOR activity energy, the basic electrode reaction rate can occur even in poor operating conditions such as bad fuel or air transfer operation.As to the durability, the non-noble metals in the Pt alloy catalysts are more sensitive to the ionomer phase by XRD analysis.These non-noble metals can partially lose to induce (111) Pt skin to increase catalyst activity [49].It indirectly improves fuel cell catalyst durability.
Various kinds of alloy metals have already proved to be capable in a fuel cell operating environment, including Co, Cr, Fe, Ni, and V. Due to its advantage of stability, researchers paid more attention to Pt-Co/C recently [50,51].Adzic et al. [52] showed that the durability of Pt-based catalyst could be improved with the addition of gold (Au) clusters.The above reports showed that the Pt alloy could not only use a second metal to replace unavailable Pt to reduce costs, but also could use other metals to stabilize the Pt skin and frame structure to increase its lifespan.However, in cell reversal, catalyst performance only adds brilliance to its present splendor.Its root is reactant supply and material corrosion resistance.

Carbon Support Material
As to material corrosion resistance, carbon is commonly used in PEMFC as a catalyst support, in GDLs, and as a bipolar-plate material [24].Carbon support has many basic features, such as high specific surface area, good electrical conductivity, and chemical stability in a fuel cell system [53].The stronger the interaction between carbon material and catalyst particles is, the better the performance of catalyst particles that is not prone to sinter is [36].However, carbon oxidation reaction (COR) has a direct relationship with electrocatalytic material stability, and thermodynamically the reaction would happen at the cathode, because the reaction oxidation potential is 0.207 V (vs.RHE at T = 298 K).In the case of cell reversal, high potential in both the anode and cathode could electrolyze carbon material.Furthermore, with the existence of Pt-based catalyst, carbon corrosion would be easier [10,54].
Different kinds of carbon material have an impact on corrosion resistance.As a new carbon material, graphene has special optical, chemical, and mechanical properties.Due to its high surface area, high conductivity, and unique graphitized basal plane structure, it has potential to serve as a fuel cell catalyst support material to overcome the problem of corrosion [55].Considering the strong interaction between graphene and nanoparticles with functional groups, it is hard for Pt-based catalyst nanoparticles to dissolve or sinter [56].Graphene increases a Pt-based catalyst metal's dissolution potential.Guo and Sun developed a facile solution-phase self-assembly method to deposit FePt NPs on a graphene surface [43].This experiment mainly shows that graphene as a carbon support could have an effect on carbon corrosion in harsh conditions.Although graphene has influence on improving catalyst activity and durability, easily stacking between graphene sheets, the effects of surface functional groups should be intensively investigated.
Generally, graphitic content is a point to be researched.Luis Castanheira and coworkers proposed that the structure of carbon material, including high-surface area carbon (HSAC), Vulcan XC72, or reinforced-graphite (RG) with identical Pt (40 wt %), was the key to carbon corrosion caused by the hydrogen/air interface [10].Results showed that there were 60% and 80% ECSA loss for Pt/Vulcan and Pt/HSAC, respectively.However, Pt/RG only had 25%.Compared to other disorganized carbon material, graphitic carbon is more robust against carbon corrosion.
Similarly, Artyushkova et al. [57,58] found a relationship between carbon material structure and chemical parameters.Good electrochemical activity of ORR but poor activity of COR were seen with high amounts of graphite carbon, small specific surface area, less carbon surface oxides, and many large-sized pores.In fact, it is a contradiction that graphite carbon has less surface deficit, which makes it resistant to corrosion, and has weak interaction with catalyst particles.ORR and COR should be in balance only if we consider carbon material surface factor.Carbon material surface structure and function can be a method of improving this situation.This paper [58] introduced the relationship between different carbon material structural features, corrosion resistance, and hydrophobicity or hydrophilicity.According to this relationship, we have a path to manufacture and synthesize ideal carbon material.
Carbon surface porosity plays a role in corrosion resistance and wettability.Wlodarczyk [59] suggested that carbon could show good corrosion resistance with a porosity value in excess of 10%, because its wettability decreased with the value of porosity.
Apart from graphene, other carbon materials have also attracted researchers' attention.Oh et al. [60] focused on the performance of various carbon support materials including carbon black [44,61], carbon nanofiber [62,63], and carbon nanocage [64].The electrochemical data about Pt-based catalyst supported by these three different types of carbon materials before and after corrosion are shown in Figure 5 and Table 2 [60].Among these carbon materials, the amorphous carbon black was more susceptible to corrosion compared to carbon nanofiber (CNF) and carbon nanocage (CNC).In addition, CNC exhibited better performance than CNF in carbon corrosion resistance and preventing Pt particle aggregation, because of the balance between hydrophobicity and surface roughness [60].Different three-dimensional carbon materials also lend corrosion resistance and physical segregation.
By combining these two points-carbon surface and spatial structure, we can design the desired carbon material structure to optimize a fuel cell.V with reference to the anode was applied to the cathode of fuel cell for 30 min and the amounts of CO 2 produced from the cathode of fuel cell were monitored as a function of time using on-line mass spectrometry.During the corrosion test, the cathode of the fuel cell becomes the anode of the externally powered cell, exhibiting carbon corrosion.On the other hand, the anode of the fuel cell behaves as a counter electrode as well as a reference electrode.Dispersion of the carbon support in a two-phase water/hexane (1:1) mixture was used to explore hydrophobicity.One milligram of each carbon support was wetted with 10 mL water and dispersed in a sonication bath for 1 min.Next, an equal volume of hexane was added.Mixtures were swiftly hand-agitated and observed.The Pt sintering effect of each carbon support was investigated under half-cell conditions using 0.5 M H 2 SO 4 as electrolyte.Catalysts were sprayed onto 4 cm 2 Au plates with 0.8 mg cm −2 of Pt.Next, CV was performed in the range of 0.0-0.8V to minimize carbon corrosion with a sweep rate of 50 mV s −1 for up to 4,000 cycles.Changes in Pt active surface area were determined by CV measurements in the range 0.0-1.2V with a 5 mV s −1 sweep rate at the 500th, 1000th, 2000th, 3000th, and 4000th cycles.Active surface areas were calculated from the CV hydrogen adsorption peaks.
X-ray photoelectron spectroscopy (XPS) was used to inspect functional groups on carbon surfaces, and both X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HR-TEM) were performed to examine the graphitic structure of carbon supports and to measure Pt particle sizes.ICP-AES analysis was carried out to estimate the Pt loading over the carbon support.

Results and discussion
Fig. 2 shows XRD patterns of three different carbon supports.Diffraction peak at 2Â = 26 • reflecting carbon graphitic structure is observed with CNF and CNC.However, no such peak was present in the CB spectrum indicating that CB is amorphous structure.The degree of graphitization and Brunauer-Emmett-Teller (BET) surface area of three different carbon supports were summarized in Table 1.To evaluate the degree of graphitization, crystallite thickness (L c values) and interlayer spacing (d 0 0 2 values) were calculated using the Scherrer formula and Bragg's law, respectively.Higher L c value of (0 0 2) peak and lower d 0 0 2 number imply higher graphitization [21][22][23].When different carbon supports were compared, CNF showed the lowest d 0 0 2 value of 0.3356 nm, close to that of pure graphite (0.3354 nm) [23].CNF also yielded a higher L c value than did the other two carbon supports.Thus, it can be concluded that CNF has the highest degree of graphitization among the three carbon supports tested.However, CNF showed the smallest BET surface area.
HR-TEM images are presented in Fig. 3. Fig. 3a shows an image of CB which exhibit a particle size of 30-50 nm.Fig. 3c displays CNF, showing well-aligned platelet-type graphitic layers with diameters of 50-200 nm.Fig. 3e shows that CNCs with caged carbon particles with hollow interiors surrounded by walls composed of a few graphitic layers.Pt was deposited onto each type of carbon support.HR-TEM images of Pt-bearing supports are also shown in Fig. 3. Pt particle size on the CNF support appeared larger than on CB and   There are some specific examples to show various kinds of carbon material durability performance.Vinod et al. made an effort to test graphite carbon support [65].In the accelerated stress test (AST), graphite Pt/C catalyst had better carbon corrosion resistance relative to the untreated carbon sample.They tested ECSA, cell performance, charge transfer resistance by CV, cell polarization, and resistance, respectively.In the PEMFC cathode, graphite Pt/C catalyst electrical performance deteriorated by 10% after 70 h AST compared to 77% of untreated carbon support, as shown in Figure 6 [65].
Zhao et al. evaluated the change in nanostructure through the various heat treatments of carbon materials and their durability for the startup/shutdown operation of PEFC [66].This paper had a similar result in that great catalyst support should have a high graphitization degree and good interaction with the catalyst.It gave an optimum heat treatment temperature of 1600 • C for best durability.
Generally, carbon material corrosion is caused by high electrode potential, which induces a reaction between carbon material and water.Carbon material surface defects are the most influential factor in corrosion.The purpose of carbon material graphite is to reduce surface defects for a more compact surface.Different types of carbon materials, like CNT, CNC, graphene, and so on, due to their unique surface structures, have different properties that have yet to be fully investigated.To achieve good ORR activity and carbon corrosion resistance, one must consider the balance between the graphitic level, the amount of surface oxide, surface roughness, pore size, and hydrophobicity.With the consideration of the important relationship among catalyst layer effective properties, ORR performance, and durability, it would prove useful to set design rules to produce and optimize the structure carbon material and MEA in order to satisfy various kinds of fuel cell operation conditions.There are some specific examples to show various kinds of carbon material durability performance.Vinod et al. made an effort to test graphite carbon support [65].In the accelerated stress test (AST), graphite Pt/C catalyst had better carbon corrosion resistance relative to the untreated carbon sample.They tested ECSA, cell performance, charge transfer resistance by CV, cell polarization, and resistance, respectively.In the PEMFC cathode, graphite Pt/C catalyst electrical performance deteriorated by 10% after 70 h AST compared to 77% of untreated carbon support, as shown in Figure 6 [65].Zhao et al. evaluated the change in nanostructure through the various heat treatments of carbon materials and their durability for the startup/shutdown operation of PEFC [66].This paper had a similar result in that great catalyst support should have a high graphitization degree and good interaction with the catalyst.It gave an optimum heat treatment temperature of 1600 °C for best durability.
Generally, carbon material corrosion is caused by high electrode potential, which induces a reaction between carbon material and water.Carbon material surface defects are the most influential factor in corrosion.The purpose of carbon material graphite is to reduce surface defects for a more compact surface.Different types of carbon materials, like CNT, CNC, graphene, and so on, due to their unique surface structures, have different properties that have yet to be fully investigated.To achieve good ORR activity and carbon corrosion resistance, one must consider the balance between the graphitic level, the amount of surface oxide, surface roughness, pore size, and hydrophobicity.With the consideration of the important relationship among catalyst layer effective properties, ORR performance, and durability, it would prove useful to set design rules to produce and optimize the structure carbon material and MEA in order to satisfy various kinds of fuel cell operation conditions.

Water Oxidation Reaction
In fuel cell reversal, water oxidation occurs in combination with carbon corrosion among abnormal reactions.Like the sacrificial anode preventing metal corrosion, water oxidation would occur more prevalently to minimize carbon oxidation.Some papers [11,37] also propose that the promotion of water oxidation over carbon through anode structure and component modification would mitigate the catalyst degradation.Obviously, there are two kinds of approaches to promoting chemical reaction: (1) increasing the amount of reactant and (2) reducing water oxidation reaction's activation energy.In Equations ( 9) and ( 10), we can see that reducing the water oxidation reaction's over-potential and increasing its kinetic rate instead of the protons and electrons produced by carbon corrosion can protect the fuel cell system.These two methods are reported in detail as follows.

Water Oxidation Catalyst
Catalysts can increase or decrease reaction activity energy to promote chemical reactions in directions we expect.Adding catalysts to boost water oxidation and reduce carbon corrosion would be an effective method of decreasing cell reversal.
Ralph et al. [16] added 20 wt % RuO 2 to 20% Pt and 10% Ru catalysts supported on Vulcan XC 72R with PTFE.The time to achieve −2.0 V increased from 22 to 32 min.As Table 3 shows, three water oxidation catalysts, RuO 2 , RuO 2 -TiO 2 , and RuO 2 -IrO 2 , had different effects on cell reversal with the increasing reactivity RuO 2 -IrO 2 > RuO 2 -TiO 2 > RuO 2 .Ralph and coworkers made a series of investigations into electrochemical catalyst loading for water oxidation both unsupported and supported on various kinds of carbon materials.In the three-step protocol presented above, it is easy to recognize the performance of electrochemical catalysts according to the time it takes to get −2.0V of cell potential, as listed in Table 3.The time to get to −2.0 V can partially demonstrate the effect of a water oxidation catalyst.Combined with CV, TEM, or SEM imaging before and after cell reversal experiment, we can analyze the morphology of carbon support and catalyst particles generally.
Jang et al. [67] studied the effect of water oxidation catalyst added into cathode to weaken carbon corrosion.In Figure 7, compared with commercialized Pt/C catalyst, the electrochemical carbon corrosion decreased by 76% with 2 wt % IrO 2 (0.016 mg•cm −2 ) under 1.6 V (vs.NHE) and 70 • C. CO 2 monitoring showed that the water oxidation catalyst had the effect of mitigating carbon corrosion.Carbon dioxide is produced by carbon corrosion in a fuel cell.The decrease of carbon dioxide production means the amount of COR is reducing.Theoretically, a water oxidation catalyst could also be used in anodes to decrease carbon corrosion.
Jang et al. [68] also studied the performance of IrO 2 and IrO 2 /C mixed with Pt/C on cathode durability during fuel starvation.In an accelerated fuel starvation test, with varying amounts of IrO 2 (2.5, 5, 10, or 20 wt %), the peak power densities of the cell cathode catalyst were decreased by 10.21%, 6.52%, 2.93%, and almost 0, respectively.This shows that IrO 2 plays an important role in maintaining cell performance under extreme operation conditions.However, due to the screening effect, IrO 2 particles in the cathode surface mixed with the commercial Pt/C would reduce the activity of the Pt-based catalyst.Therefore, IrO 2 /C was chosen as the mixture of cathode catalyst.As a water electrolysis catalyst, with the IrO 2 /C increasing, the durability of the fuel cell became better and better due to the rapid decomposition of water molecules.According to the screening effect and catalyst durability, 10 wt % IrO 2 /C with Pt/C catalyst is a better choice.
In the case of water oxidation, the most important points are the design of catalyst layers mixed between Pt-based catalysts and water oxidation catalysts.Some papers [16,67,68] proposed that the water oxidation catalyst has a positive effect on water electrolysis over and above carbon corrosion and the degradation of carbon support material.It is obvious that water oxidation catalyst improves the cell reversal tolerance with increasing effect (RuO 2 -IrO 2 > RuO 2 -TiO 2 > RuO 2 ).corrosion decreased by 76% with 2 wt % IrO2 (0.016 mg•cm −2 ) under 1.6 V (vs.NHE) and 70 °C.CO2 monitoring showed that the water oxidation catalyst had the effect of mitigating carbon corrosion.Carbon dioxide is produced by carbon corrosion in a fuel cell.The decrease of carbon dioxide production means the amount of COR is reducing.Theoretically, a water oxidation catalyst could also be used in anodes to decrease carbon corrosion.

Control Humidity and Holding Water Volume
Enhancing water retention is another way to promote water oxidation over carbon corrosion, due to the increase of reactant resources.However, humidity has a negative relationship with fuel cell performance in some ranges.More does not mean better.Some patents and papers [42,69,70] focused on cell reversal prevention over its performance and lifetime mitigation due to its irreversible damage.Therefore, a hydrophobic agent is a way to hold more water in the anode when cell reversal occurs induced by fuel starvation, which is always used in the gas diffusion layer to improve reactant gas diffusion and water management [71].
Ralph et al. [16] changed the water supply at the anode in their fuel cell reversal mimic experiment [72], in which the anode was fed with humidified N 2 and the cathode fed with O 2 .When the cell current was set at 120 A, the current density was 0.5 A•cm −2 and the cell potential was more than −1.0 V (when the cell potential is less than −2.0 V, the polymer membrane can be completely degraded by dielectric breakdown).This experiment demonstrated that water supply played an important role in sustaining the cell potential and preventing MEA deterioration.
Besides increasing fuel humidity, the other method is to add hydrophobic materials into the catalyst layer, like PTFE.It could slow down the rate of water and increase the water contact angle by keeping water in the anode without shrinking the contact area between the catalyst layer and the membrane.Due to its key role in water retention, it is hoped that a hydrophobic agent would promote water oxidation reactions to solve the issues caused by cell reversal, resulting in less carbon component oxidation [16].As Figure 8 depicted, Ralph et al. [16] put four Ballard cell stacks under cell reversal condition.When the cell potential got to −2.0 V, the one added PTFE was increased to 22 from 3 min, which is the time the standard anode took.Numerous research papers have studied the effect of hydrophobic agent content and species, including polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), and fluorinated ethylene propylene (FEP), in GDL on the performance of fuel cells [73][74][75].Given their excellent characteristics, hydrophobic agents can be used in the anode catalyst layer to hold more water.

Conclusions
Fuel starvation, inadequate air supply, water flooding, load change, low catalyst performance, etc. can induce cell reversal when the current rate exceeds the limiting mass transfer rate.Because these factors cannot produce sufficient electron and proton feeds to match current stack requirements and achieve current value balance, the fuel cell voltage could reverse and some other abnormal chemical reactions might occur to make up for the deficit.In these abnormal operating conditions, there is irreversible damage to the PEMFC system, including carbon support corrosion, catalyst and sinter agglomeration, and membrane degradation.In fact, gross fuel starvation is different from localized fuel starvation in terms of causes, carbon corrosion area, cell voltage, and current phenomena.Generally, cell reversal caused by overall fuel starvation is more critical than in a cathode and is induced by improper gas supply, flooding, and any other factors that obstruct the flow field and catalyst layer; therefore, the design of the anode catalyst layer and the catalytic performance have drawn more attention to cell reversal.Due to the existence of hydrogen in cathodes or oxygen in anodes, cell reversal can cause permanent damage to a fuel cell.
To solve this problem or mitigate the harm to fuel cells, two approaches have been used in recent years.First is the system management strategy, where auxiliary monitoring equipment is used to determine necessary adjustments to operation parameters to avoid cell reversal, such as adding reactant flow rate, change operation load, water management, and so on.The second is system material modification to resist cell reversal.Specifically, there are three approaches to attenuate performance loss and extend fuel cell lifespan.Researchers have placed attention on highperformance catalysts, carbon support materials, and water oxidation reactions.In addition, heatresistant membranes also attract more attention for their ability to reduce water flooding in a cathode, but they would decrease the proton transfer rate and catalyst efficiency.
Obviously, there are still several problems in need of further study, such as (1) understanding the effects of different types of carbon materials' surface forms and structure; (2) developing a novel Numerous research papers have studied the effect of hydrophobic agent content and species, including polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), and fluorinated ethylene propylene (FEP), in GDL on the performance of fuel cells [73][74][75].Given their excellent characteristics, hydrophobic agents can be used in the anode catalyst layer to hold more water.

Conclusions
Fuel starvation, inadequate air supply, water flooding, load change, low catalyst performance, etc. can induce cell reversal when the current rate exceeds the limiting mass transfer rate.Because these factors cannot produce sufficient electron and proton feeds to match current stack requirements and achieve current value balance, the fuel cell voltage could reverse and some other abnormal chemical reactions might occur to make up for the deficit.In these abnormal operating conditions, there is irreversible damage to the PEMFC system, including carbon support corrosion, catalyst and sinter agglomeration, and membrane degradation.In fact, gross fuel starvation is different from localized fuel starvation in terms of causes, carbon corrosion area, cell voltage, and current phenomena.Generally, cell reversal caused by overall fuel starvation is more critical than in a cathode and is induced by improper gas supply, flooding, and any other factors that obstruct the flow field and catalyst layer; therefore, the design of the anode catalyst layer and the catalytic performance have drawn more attention to cell reversal.Due to the existence of hydrogen in cathodes or oxygen in anodes, cell reversal can cause permanent damage to a fuel cell.
To solve this problem or mitigate the harm to fuel cells, two approaches have been used in recent years.First is the system management strategy, where auxiliary monitoring equipment is used to determine necessary adjustments to operation parameters to avoid cell reversal, such as adding reactant flow rate, change operation load, water management, and so on.The second is system material modification to resist cell reversal.Specifically, there are three approaches to attenuate performance loss and extend fuel cell lifespan.Researchers have placed attention on high-performance catalysts, carbon support materials, and water oxidation reactions.In addition, heat-resistant membranes also attract more attention for their ability to reduce water flooding in a cathode, but they would decrease the proton transfer rate and catalyst efficiency.
Obviously, there are still several problems in need of further study, such as (1) understanding the effects of different types of carbon materials' surface forms and structure; (2) developing a novel catalyst layer assembly including a high-performance catalyst, corrosion-resistant carbon material, a water oxidation catalyst, and hydrophobic agents; and (3) distinguishing the specific electrode reaction caused by the phenomenon of hydrogen pump and oxygen pump.Compared to a fuel cell system of water and heat management, this is simpler and more critical to catalyst layer design, and would make system management more efficient by diminishing several controlling limitations.

Fig. 2 .
Fig. 2. The time-dependent changes of the anode and cathode potential during the cell reversal experiment.

Figure 1 .
Figure 1.Anode and cathode potential change experienced cell reversal caused by hydrogen starvation.Reproduced with permission from [6].Copyright Elsevier, 2004.

Fig. 2 -Fig. 3 -
Fig. 2 -Time-dependent changes in the anode and cathode potential during the cell-reversal experiment.

Figure 2 .
Figure 2. Anode and cathode potential change in cell reversal caused by oxygen starvation.Reproduced with permission from [5].Copyright Elsevier, 2008.

Fig. 4 -Fig. 5 -
Fig. 4 -Change in the electrochemically active surface by a cell-reversal experiment: (a) before experiment, (b) after experiment for 5 min, (c) after experiment for 10 min and (d) after experiment for 120 min.

Fig. 6 -
Fig. 6 -TEM images of the cathode catalyst: (a) before and (b) after the cell-reversal experiment for 120 min.

Figure 4 .
Figure 4. Change in the electrochemically active surface by a cell-reversal experiment: (a) before experiment; (b) after 5 min of experiment; (c) after 10 min of experiment; and (d) after 120 min of experiment.Reproduced with permission from [5].Copyright Elsevier, 2008.

Figure 6 .
Figure 6.Steady-state performance curves for PEFCs with (a) Pt/Non-GrC and (b) Pt/GrC cathodes prior to AST and after 50 or 70 h of AST with H 2 -O 2 at 60 • C. Reproduced with permission from [65].Copyright WILEY-VCH, 2011.

Figure 8 .
Figure 8.The effect of anode catalyst layer structure and composition in Ballard four-cell stack tests.Reproduced with permission from [16], Copyright ECS, 2006.The anode contains 20 wt % Pt and 10 wt % Ru supported on Vulcan XC72R at an electrode loading rate of ca.0.3 mg•Pt•cm −2 with the water oxidation electrocatalyst added at a loading rate of ca.0.1 mg•Ru•cm −2 .

Figure 8 .
Figure 8.The effect of anode catalyst layer structure and composition in Ballard four-cell stack tests.Reproduced with permission from [16].Copyright ECS, 2006.The anode contains 20 wt % Pt and 10 wt % Ru supported on Vulcan XC72R at an electrode loading rate of ca.0.3 mg•Pt•cm −2 with the water oxidation electrocatalyst added at a loading rate of ca.0.1 mg•Ru•cm −2 .

Table 1 .
Different times for cell reversal in different hydrogen stoichiometry.

Table 1 .
Different times for cell reversal in different hydrogen stoichiometry.

Table 1
The degree of graphitization and BET surface area of different carbon supports.

Table 2 .
Changes in different types of carbon materials' electrical data before and after corrosion experiments.

Table 3 .
[16]catalysts effect in anodes on the cell reversal tolerance in Step 3 of the protocol.Reproduced with permission from[16].Copyright ECS, 2006.