Selective Synthesis of a Gasoline Fraction from CO and H 2 on a Co-SiO 2 /ZSM-5/Al 2 O 3 Catalyst

: This article reports on a simple method for producing high-octane gasoline from CO and H 2 on a Co-Al 2 O 3 /SiO 2 /HZSM-5/Al 2 O 3 hybrid catalyst. In the selected pressure range (0.5, 1.0, and 2.0 MPa), it was found that a decrease in pressure and an increase in temperature contribute to an increase in the content of branched hydrocarbons. The optimal technological parameters of the process were determined to ensure high selectivity and productivity for C 5 –C 10 hydrocarbons: pressure—1.0 MPa, ratio H 2 /CO = 2, gas space velocity—1000 h − 1 , temperature—250 ◦ C. The selectivity for the gasoline fraction is 65.2%, and the ratio of branched to linear hydrocarbons (iso/n index) is 2.3. Under the speciﬁed technological conditions, an experimental batch of gasoline fraction (1000 cm 3 ) was produced at the pilot plant during 400 h of continuous operation. The main physicochemical and operational parameters of the experimental gasoline fraction of hydrocarbons have been determined. The octane number determined by the research method according to GOST R 52947-2019 is 78.5 units.


Introduction
Recently, there has been a growing interest in technologies for the industrial production of liquid hydrocarbons, in particular, synthetic gasoline, from non-oil raw materials (natural gases, coal, biomass) [1][2][3].The first industrial-scale production of synthetic gasoline using the Fischer-Tropsch (FT) method was mastered at Ruhrchemie in Germany during the Second World War [4].The gasoline fraction of hydrocarbons synthesized at the plants was mainly represented by linear paraffins and olefins and had a low octane number, about 40-50 units.The technology was multi-stage and very costly and, in the future, could not compete with motor fuels produced from natural oil [5].
Currently, large-scale production of synthetic hydrocarbons based on the synthesis of FT makes it possible to obtain a low-octane gasoline fraction (naphtha), which is sent for further processing or used as a feedstock for petrochemicals, solvents, etc.It is possible to obtain high-octane gasoline from CO and H 2 using MTG technology (methanol to gasoline), involving the synthesis of methanol, on which dimethyl ether is based, followed by the conversion of the latter into hydrocarbons.MTG technology is a three-Mobil process [6], two-TIGAS process [7], or one-stage technological process [8].The main products of this technology are hydrocarbons of the gasoline fraction, which consist mainly of aromatic, branched paraffin and cycloparaffin hydrocarbons [9,10].The octane number of the gasoline fraction obtained by these processes can reach 90 units.mainly of aromatic, branched paraffin and cycloparaffin hydrocarbons [9,10].The octane number of the gasoline fraction obtained by these processes can reach 90 units.
In the synthesis of hydrocarbons using the FT method on zeolite-containing catalysts, the selectivity for the gasoline fraction, depending on the synthesis conditions, varies from 60 to 90% [11][12][13][14][15][16][17][18].At the same time, it is important that the synthesis products contain a significant proportion of iso-alkanes, which have high antiknock properties.For example, in a commercial catalyst developed by Chevron, the selectivity for the fraction C5-C20 is 71.8%, but the content of iso-alkanes in the synthesis products is not indicated [19].
Previously, we developed a bifunctional cobalt catalyst for the synthesis of FT for the direct production of liquid hydrocarbons from synthesis gas [20,21].On this catalyst at a pressure of 1.0-2.0MPa, light synthetic oil is obtained, consisting of gasoline and diesel fractions.The purpose of this work is to search for synthesis conditions under which the gasoline fraction obtained on this catalyst is enriched in iso-alkanes, which have high antiknock properties.

Results and Discussion
An XRD study of the catalyst (Figure 1) showed that the catalyst contains phases of Co3O4 oxides (reflexes in the range 2θ ≈ 10°-55°), ZSM-5 zeolite (reflexes in the range of angles 2θ ≈ 2°-12°), Al2O3 (reflexes at 2θ ≈ 20.3°, 29.5°, and 52.0°) formed during the heat treatment of boehmite, and SiO2, which is X-ray amorphous.The particle size of Co3O4 was determined using the Debye-Scherrer equation, which was then used to determine the size of metallic cobalt d(Co 0 ), the size of which was 8 nm.It was determined using TEM that cobalt particles 3-13 nm in size were present on the catalyst surface (Figure 2); the average size was 8 ± 2 nm (Table 1).It was determined using TEM that cobalt particles 3-13 nm in size were present on the catalyst surface (Figure 2); the average size was 8 ± 2 nm (Table 1).
The study of morphology using SEM (Figure 3) confirmed the heterogeneity of the state of the catalyst surface.It was found that silicon, aluminum, and oxygen atoms were more uniformly distributed over the catalyst surface, while cobalt atoms were localized fragmentarily.
According to the BJH data (Figure 4), the maximum pore-size distribution in the region of 1.5-2.5 nm corresponds to the H-ZSM-5 zeolite, and the maximum at 5 nm corresponds to the Co-Al 2 O 3 /SiO 2 catalyst.In the region of 6-15 nm, the catalyst has a maximum because of the presence of a binder in its composition.The study of morphology using SEM (Figure 3) confirmed the heterogeneity of the state of the catalyst surface.It was found that silicon, aluminum, and oxygen atoms were more uniformly distributed over the catalyst surface, while cobalt atoms were localized fragmentarily.According to the BJH data (Figure 4), the maximum pore-size distribution in the region of 1.5-2.5 nm corresponds to the H-ZSM-5 zeolite, and the maximum at 5 nm corresponds to the Co-Al2O3/SiO2 catalyst.In the region of 6-15 nm, the catalyst has a maximum because of the presence of a binder in its composition.The study of morphology using SEM (Figure 3) confirmed the heterogeneity of the state of the catalyst surface.It was found that silicon, aluminum, and oxygen atoms were more uniformly distributed over the catalyst surface, while cobalt atoms were localized fragmentarily.According to the BJH data (Figure 4), the maximum pore-size distribution in the region of 1.5-2.5 nm corresponds to the H-ZSM-5 zeolite, and the maximum at 5 nm corresponds to the Co-Al2O3/SiO2 catalyst.In the region of 6-15 nm, the catalyst has a maximum because of the presence of a binder in its composition.The specific surface area of the catalyst according to BET was 245 m 2 /g and was mainly determined by the presence of a zeolite and a cobalt-containing component (Co-Al 2 O 3 /SiO 2 ) in the catalyst.The share of micropores was 5% of the total pore volume.
According to the results of the TPR H 2 (Figure 5), the reduction of the cobalt-containing component of the bifunctional catalyst proceeds sequentially according to the schemes Co 3 O 4 → CoO and CoO → Co 0 , which confirms the presence of two stages of reduction [22].The ratio of peak areas of hydrogen absorption required for the reduction of Co 3+ oxides to Co 0 differs from the theoretically expected calculated value and is 2.70.The absence of a large H 2 absorption peak in the high-temperature region indicates that cobalt does not form difficult-to-reduce compounds with zeolite or boehmite.The specific surface area of the catalyst according to BET was 245 m 2 /g and was mainly determined by the presence of a zeolite and a cobalt-containing component (Co-Al2O3/SiO2) in the catalyst.The share of micropores was 5% of the total pore volume.According to the results of the TPR H2 (Figure 5), the reduction of the cobaltcontaining component of the bifunctional catalyst proceeds sequentially according to the schemes Co3O4 → CoO and CoO → Cо 0 , which confirms the presence of two stages of reduction [22].The ratio of peak areas of hydrogen absorption required for the reduction of Co 3+ oxides to Co 0 differs from the theoretically expected calculated value and is 2.70.The absence of a large H2 absorption peak in the high-temperature region indicates that cobalt does not form difficult-to-reduce compounds with zeolite or boehmite.
When studying the acidity of the catalyst according to the NH3 TPD data, it was found that the amount of ammonia desorbed in the temperature range of 100-250 °C ("weak" centers), 250-400 °C ("medium" centers), and 400-550 °C ("strong" centers) is 70 µmol NH3/g, 31 µmol NH3/g, and 5 µmol NH3/g, respectively.Like the HZSM-5 zeolite, the catalyst based on it has a relatively high Bronsted acidity.In order to select the optimal process mode and optimize the consumption coefficients of reagents for the pilot plant, the process conditions (temperature, pressure) were previously determined at the laboratory plant, under which the performance of the bifunctional cobalt FT synthesis catalyst and the selectivity for the gasoline fraction would be maximum.The criterion for the search for optimal process conditions was the presence in the synthesis products of a large number of isomeric hydrocarbon structures (high iso/n) in the synthesis products, which provide high antiknock characteristics of the gasoline fraction.
Zeolite-containing FT synthesis catalysts mainly operate in the temperature range of 230-250 °C [23][24][25][26] since, under these conditions, secondary processes of transformations of synthesized hydrocarbons on the zeolite-containing component begin to actively proceed [27].In this study, we varied the temperature in the range of 240-250 °C.The effect of pressure was studied in the range of 0.5-2.0MPa under the conditions: GHSV = 1000 h -1 , H2/CO ratio = 2, temperatures of 240 °C and 250 °C, and the volume of catalyst loading into the reactor of 10 cm 3 .The results of these studies are given in Table 2.When studying the acidity of the catalyst according to the NH 3 TPD data, it was found that the amount of ammonia desorbed in the temperature range of 100-250 • C ("weak" centers), 250-400 • C ("medium" centers), and 400-550 • C ("strong" centers) is 70 µmol NH 3 /g, 31 µmol NH 3 /g, and 5 µmol NH 3 /g, respectively.Like the HZSM-5 zeolite, the catalyst based on it has a relatively high Bronsted acidity.
In order to select the optimal process mode and optimize the consumption coefficients of reagents for the pilot plant, the process conditions (temperature, pressure) were previously determined at the laboratory plant, under which the performance of the bifunctional cobalt FT synthesis catalyst and the selectivity for the gasoline fraction would be maximum.The criterion for the search for optimal process conditions was the presence in the synthesis products of a large number of isomeric hydrocarbon structures (high iso/n) in the synthesis products, which provide high antiknock characteristics of the gasoline fraction.
Zeolite-containing FT synthesis catalysts mainly operate in the temperature range of 230-250 • C [23][24][25][26] since, under these conditions, secondary processes of transformations of synthesized hydrocarbons on the zeolite-containing component begin to actively proceed [27].In this study, we varied the temperature in the range of 240-250 • C. The effect of pressure was studied in the range of 0.5-2.0MPa under the conditions: GHSV = 1000 h −1 , H 2 /CO ratio = 2, temperatures of 240 • C and 250 • C, and the volume of catalyst loading into the reactor of 10 cm 3 .The results of these studies are given in Table 2.A comparative analysis of the catalytic characteristics showed that with decreasing pressure, the selectivity of the catalyst for hydrocarbons in the gasoline fraction, as well as the iso/n and o/n indicators, increases.It has been established that with the technological parameters of synthesis P = 1.0 MPa, T = 250 • C, GHSV = 1000 h −1 , and the ratio H 2 /CO = 2, selectivity and productivity for C 5 -C 10 are 73.3% and 83.2 kg/(m 3 cat h), respectively.Under these conditions, a significant proportion (iso/n = 3.64) of isomeric hydrocarbon structures is formed (see Table 2), which helps increase the octane number of gasoline and improve its quality characteristics.Therefore, it is advisable to produce synthetic gasoline at a pilot plant with the specified technological parameters.
Table 3 presents the average results of the hydrocarbon synthesis process at the pilot plant, obtained over 400 h of operation.During this time period, five samples of hydrocarbons were taken, which, upon completion of the synthesis, were combined into one and used to determine the average characteristics of the fuel.Table 3. Averaged catalytic characteristics of a bifunctional cobalt catalyst for FT synthesis in a pilot plant at GHSV = 1000 h −1 , P = 1.0 MPa, T = 247-250 • C, H 2 /CO ratio = 2.

Sample
No. With an increase in the time interval of catalyst operation, the degree of CO conversion decreased, and by the end of the experiment, it decreased by ~12% from the initial values (78.3%).The dynamics of changes in CO conversion over a time interval of 400 h is clearly shown in Figure 6.With an increase in the time interval of catalyst operation, the degree of CO conversion decreased, and by the end of the experiment, it decreased by ~12% from the initial values (78.3%).The dynamics of changes in CO conversion over a time interval of 400 h is clearly shown in Figure 6.The productivity of the process over the entire period of catalyst operation decreased from 113.8 to 69.6 kg/(m 3 cat h), and, as a result, the production of gaseous products (CH 4 , C 2 -C 4 , CO 2 ) increased.The calculated average productivity of the process for the combined sample of hydrocarbons was 86.0 kg/(m 3 cat h); that is, it decreased by 24% from the initial value.The largest decrease in productivity (by 32%) was recorded in the initial period (~100 h) of catalyst operation.

Working
One of the factors reducing the activity can be local temperature overheating in the catalytic layer.However, temperature measurements along the height of the catalytic layer (see Figure 7) for the entire period of operation of the bifunctional cobalt catalyst for FT synthesis showed that the largest temperature gradient of 3-4 • C was observed in the initial 10 h of catalyst operation.Subsequently, it stabilized and did not exceed 2-3 • C, which indicates a sufficiently high stability of the catalyst.The main reasons for catalyst deactivation can be the agglomeration of active metal nanoparticles, as well as carburization (hydrocarbons, amorphous, and graphitized carbon) of the active catalyst surface during operation [20].
Catalysts 2023, 13, x 7 of 16 The productivity of the process over the entire period of catalyst operation decreased from 113.8 to 69.6 kg/(m 3 cat h), and, as a result, the production of gaseous products (CH4, C2-C4, CO2) increased.The calculated average productivity of the process for the combined sample of hydrocarbons was 86.0 kg/(m 3 cat h); that is, it decreased by 24% from the initial value.The largest decrease in productivity (by 32%) was recorded in the initial period (~100 h) of catalyst operation.
One of the factors reducing the activity can be local temperature overheating in the catalytic layer.However, temperature measurements along the height of the catalytic layer (see Figure 7) for the entire period of operation of the bifunctional cobalt catalyst for FT synthesis showed that the largest temperature gradient of 3-4 °C was observed in the initial 10 h of catalyst operation.Subsequently, it stabilized and did not exceed 2-3 °C, which indicates a sufficiently high stability of the catalyst.The main reasons for catalyst deactivation can be the agglomeration of active metal nanoparticles, as well as carburization (hydrocarbons, amorphous, and graphitized carbon) of the active catalyst surface during operation [20].Group analysis of C5+ products synthesized on a pilot catalytic plant showed that the average sample of hydrocarbons contains a high number of isomeric compounds; the iso/n index corresponds to a value of 2.3.The o/p index indicating the presence of unsaturated hydrocarbons in the fuel composition was 1.14 (Table 4).The molecular weight distribution diagram shows that these are predominantly branched alkenes contained in Group analysis of C 5+ products synthesized on a pilot catalytic plant showed that the average sample of hydrocarbons contains a high number of isomeric compounds; the iso/n index corresponds to a value of 2.3.The o/p index indicating the presence of unsaturated hydrocarbons in the fuel composition was 1.14 (Table 4).The molecular weight distribution diagram shows that these are predominantly branched alkenes contained in the C 5 -C 10 gasoline fraction (Figure 8).Fuel characteristics can be significantly improved, in particular, to increase the octane properties of the fuel and reduce the content of alkenes.One of the ways to improve the performance of motor fuel is its hydro-treatment.This can be achieved by introducing promoters-hydrogenating components-into the composition of a polyfunctional catalyst [28].Content, % wt.The results of a study of a number of basic physicochemical and oper indicators of a synthesized experimental batch of gasoline fraction of hydrocarb presented in Table 5.The results of a study of a number of basic physicochemical and operational indicators of a synthesized experimental batch of gasoline fraction of hydrocarbons are presented in Table 5.The octane number of the experimental gasoline fraction of hydrocarbons, determined by the research method (GOST P 52947-2019), is 78.5, which is 13.5 units lower than the minimum requirement in force by GOST.However, the obtained synthetic gasoline fraction has an octane number higher compared to the octane number of straight-run gasoline (59), hydrocracked gasoline (68), and coking gasoline (63) [29].

Number of carbon atoms
The density of the experimental gasoline fraction of hydrocarbons is also somewhat lower.However, the lower density of synthetic fuel, in comparison with gasoline obtained from petroleum feedstock, is due to the complete absence of aromatic hydrocarbons, which significantly improves its environmental performance.
As a rule, the calorific value of commercial gasoline is almost the same for different grades and varies within 43-44 MJ/kg [30].The net calorific value of the obtained synthetic gasoline fuel is 43.78 MJ/kg, which is not inferior in terms of the calorific value of commercial petroleum gasoline.
An important indicator characterizing its chemical stability is the iodine number, which is determined based on the content of unsaturated compounds.The iodine number of gasoline fuel is 11.8, which corresponds to the calculated mass fraction of unsaturated hydrocarbons of 53.03 wt.%.Note that a certain proportion of unsaturated hydrocarbons, based on capillary gas-liquid chromato-mass spectrometry in the gasoline fraction of hydrocarbons, is 53.3 wt.%.However, the content of olefins significantly exceeds the requirements of the regulation.It is possible to reduce the number of olefins via light hydrogenation or, for example, the process of methoxylation to obtain esters with high antiknock resistance [31].
Fischer-Tropsch synthesis over a commercial zeolite-containing catalyst from Chevron was reported by C. Kibby et al. [19].The developed catalyst produced C 5 -C 20 hydrocarbons with a selectivity of 75.6%.Chuang Xing et al. [11] reported on the synthesis of zeolitecontaining catalysts based on Co/SiO 2 + ZSM-5; the content of the gasoline fraction was 41.5%.In our catalyst, which was tested in a pilot reactor for almost 400 h, a larger gasoline fraction of 63.5% formed.The octane number was determined as 87 units in [11]; in our work, the octane number was determined on a single-piston unit and was 78.5 (Table 6).Deactivation during the Fischer-Tropsch synthesis can be due to the phenomena of active site poisoning, formation of surface carbon and carbidization, formation of mixed compounds and re-oxidation of the metal, sintering of particles, etc.
To understand the causes of deactivation, after the reaction, we took samples of the catalyst at different heights: the top, middle, and bottom of the reactor.The selected samples were characterized with XRD using synchrotron radiation.The XRD results are shown in Figure 9.The diffraction pattern for all samples, regardless of the height of the catalyst layer, is of the same type: there are diffraction reflections of metallic cobalt and its oxide, aluminum oxide, and ZSM-5 zeolite.Based on XRD data, it was established that in the course of synthesis, there is no formation of hard-to-recover metal-carrier compounds and no significant oxidation of metallic cobalt.In turn, the estimated average size of crystallites of metallic cobalt is 12 nm, while the particle size of the catalyst before synthesis is 8 nm.Thus, one of the reasons for reducing the activity of the catalyst is the coarsening of particles of metallic cobalt (sintering).

Catalyst Preparation
A bifunctional cobalt catalyst for the synthesis of FT was obtained by mixing and The diffraction pattern for all samples, regardless of the height of the catalyst layer, is of the same type: there are diffraction reflections of metallic cobalt and its oxide, aluminum oxide, and ZSM-5 zeolite.Based on XRD data, it was established that in the course of synthesis, there is no formation of hard-to-recover metal-carrier compounds and no significant oxidation of metallic cobalt.In turn, the estimated average size of crystallites of metallic cobalt is 12 nm, while the particle size of the catalyst before synthesis is 8 nm.Thus, one of the reasons for reducing the activity of the catalyst is the coarsening of particles of metallic cobalt (sintering).

Catalyst Preparation
A bifunctional cobalt catalyst for the synthesis of FT was obtained by mixing and molding powders of a cobalt-containing component, ZSM-5 zeolite in the H-form, and a binder, boehmite.The cobalt catalyst Co-Al 2 O 3 /SiO 2 was used for the selective synthesis of long-chain hydrocarbons (20.0 Co and 1.0 Al 2 O 3 wt.%)with a silica gel carrier KSKG (OOO Salavat Catalyst Plant, Salavat, Russia) [22], and zeolite HZSM-5 was used as the acid component.with a SiO 2 /Al 2 O 3 molar ratio of 40.5 (OOO Ishimbay Specialized Chemical Plant of Catalysts, Ishimbay, Russia) [21,32] and binder boehmite Al(OH)O (Sasol, TH 80).
The catalyst was prepared by mixing the following powders (fraction <0.1 mm) in wt.%: catalyst Co-Al 2 O 3 /SiO 2 -35, HZSM-5-30, boehmite-35 [20,21,23,32].To plasticize the boehmite binder, an aqueous-alcoholic solution of triethylene glycol and nitric acid was used (the nitric acid solution was prepared by adding 1-2 mL of nitric acid with a concentration of 65 wt.% in 90-100 mL of distilled water per 100 g of a mixture of powders; triethylene glycol was introduced based on the volume ratio nitric acid:triethylene glycol in a mixture of 1:3).The catalyst granules were molded by extrusion.The mold was dried for 24 h at room temperature, 4-6 h at 80-100 • C, and 2-4 h at 100-150 • C and calcined for 5 h at 500 • C. To obtain an experimental batch of synthetic gasoline in a pilot plant, an enlarged laboratory batch of a bifunctional cobalt catalyst for the synthesis of FT with a volume of 500 cm 3 was produced.

Catalyst Characterization
The phase composition of the reduced catalyst was determined with X-ray diffraction using the equipment of the European Synchrotron Radiation Center (ESRF, Grenoble, France) in the 2θ angle range from 5 • to 55 • with a radiation wavelength λ = 0.7121 Å.The determination of the qualitative phase composition was performed using PDF-2 [33] in the Crystallographica software package (Version 3,1,0,2 with RDB support).The diffraction patterns of the catalysts were processed using the FullProf program.
XRD was performed with precision X-ray diffraction using synchrotron radiation at the X-ray diffraction analysis station of the Kurchatov Research Center.The diffraction pattern was taken at a radiation wavelength of 0.074 nm using the "transmission" geometry and registration of scattered radiation with a Rayonix SX165 two-coordinate detector, LaB6 standard (NIST SRM 660a) [20].The beam size on the sample was 400 µm.The catalyst sample was placed in a 300 µm cryostat and rotated around a horizontal axis during the measurement, which allowed the diffraction patterns to be averaged according to sample orientations.
Based on the XRD data of the catalyst in the oxide form, the average particle size of Co 3 O 4 (d(Co 3 O 4 ), nm) was determined using the Debye-Scherrer equation [34]: where d(Co 3 O 4 ) is the average particle size (nm); K is the dimensionless particle shape factor (K = 0.89); λ is the wavelength of X-ray radiation (nm); θ is the Bragg angle (rad); β is the reflection width at half height (rad).
There is a formula that calculates, based on the average particle size of Co 3 O 4 (d(Co 3 O 4 ), nm), using the Debye-Scherrer equation to determine the size of Co 0 particles [35]: where d(Co 3 O 4 ) is the average particle size of Co 3 O 4 calculated using the Debye-Scherrer equation.
The particle size of the cobalt catalysts was determined through transmission electron microscopy (TEM) using a Tecnai G2 Spirit BioTWIN (FEI, Boston, MA, USA) with an accelerating voltage of 120 kV.The catalyst sample was preliminarily reduced with a nitrogen-hydrogen mixture (5% H 2 + 95% N 2 ) during linear heating from room temperature to 500 • C for 1 h.
The average size of cobalt crystallites (d av (Co 0 ), nm) was calculated using the following formula [36]: where n i is the number of particles with diameter d i .
The standard deviation was determined by the following formula [36]: The size distribution of metal particles was obtained from measurements of ~200 particles from several micrographs taken at different locations on the grid.
The microstructure of the catalyst surface was studied through scanning electron microscopy (SEM) on a JSM-6490LV microscope (JEOL, Osaka, Japan) at an accelerating voltage of 30 kV, which was equipped with an INCA Penta FET 3 energy dispersive detector (Oxford Instruments, Wycombe, UK).
The study of the parameters of the porous structure of zeolite samples was carried out via nitrogen adsorption-desorption using a Nova 1200e instrument (Quantachrome, Boynton Beach, FL, USA).The value of the specific surface obtained with the BET method (Brunauer-Emmett-Teller) was calculated at a relative partial gas pressure P/P 0 = 0.20.The pore volume was determined using the BJH method at a relative partial pressure P/P 0 = 0.95; the pore-size distribution was calculated from the BJH desorption curve (Barrett-Joyner-Halenda)' the volume of micropores in the presence of mesopores was measured using the t-method (de Boer and Lippens).The samples were preliminarily subjected to vacuum treatment for 5 h at a temperature of 350 • C.
The process of reduction of surface phases and structures on the catalyst surface was studied via temperature-programmed reduction with hydrogen (TPR H 2 ) using a Micromeritics ChemiSorb 2750 analyzer (Micromeritics, Norcross, GA, USA) equipped with a thermal conductivity detector.TPR H 2 was carried out under the following conditions: catalyst weighed 0.10 g; gas mixture containing 10% hydrogen and 90% nitrogen; flow rate of 20 mL/min; temperature range of 20-800 • C; and heating rate of 20 • C/min.Before TPR H 2 , the catalyst was kept in a helium flow (20 mL/min) for 1 h at a temperature of 200 • C to remove moisture and adsorbed gases.
The catalysts were studied via temperature-programmed ammonia desorption (NH 3 TPD) on a Quantachrome Autosorb analyzer (Quantachrome, USA).Before adsorption, the samples were degassed in a helium flow at 600 • C for 5 h and purged to remove physically adsorbed ammonia.Ammonia was adsorbed at a temperature of 100 • C in a stream of an ammonia-helium mixture (10% NH 3 by volume) for 2 h.Desorption was carried out in the temperature range of 100-600 • C with linear heating at a rate of 10 • C/min; the carrier gas was helium.
Ex situ magnetic measurements of samples were carried out on a LakeShore VSM 7404 (LakeShore Cryotronics, Westerville, OH, USA) magnetometer.Metallic cobalt is ferromagnetic at room temperature, whereas CoO is paramagnetic, so its magnetic moment can be neglected compared to the magnetic moment of the metal.Cobalt carbide is also ferromagnetic, but its magnetic susceptibility [37] is an order of magnitude lower compared to metallic cobalt [38], so it could be neglected as well.Thus, neglecting the magnetization of non-metallic cobalt phases, the fraction of metallic cobalt in total loaded cobalt in the sample Co 0 /Co tot , i.e., the cobalt extent of reduction (EOR), can be estimated from the following relation: where M s is the measured saturation magnetization of a catalyst sample (emu), σ is the specific magnetic susceptibility for bulk cobalt (164 emu/g) 2 , and m is the cobalt mass contained in the sample (g).

Catalyst Characterization
The study of the influence of technological parameters in order to select the optimal technological mode for determining the maximum selectivity and productivity for the gasoline fraction was carried out on a laboratory installation in a flow mode in a tubular reactor (inner diameter 16 mm) with a stationary bed of a pre-reduced catalyst using synthesis gas with a ratio of H 2 /CO = 2 at pressures of 0.5, 1.0, and 2.0 MPa, gas hourly space velocity (GHSV) = 1000 h −1 , and temperature of 240-250 • C in a continuous mode for 50-100 h.The catalyst was preliminarily reduced with hydrogen for 3 h at 400 • C and GHSV 3000 h −1 ; the degree of reduction of cobalt was 60%.
The production of a batch of gasoline fraction in a volume of at least 1 L was carried out on a pilot plant with a tubular reactor 1500 mm high.The pilot plant and its technological scheme are shown in Figure 10.The unit consists of a reagent preparation unit, a hydrocarbon synthesis reactor unit, and a reaction product cooling unit.H2 and CO gases are supplied from cylinders 1 and 13 installed outdoors.Control over the level of gas consumption is carried out using the Bronkhorst gas flow regulators of the EL-FLOW series in automatic mode.The reactor block for hydrocarbon synthesis includes a reactor 20 1500 mm high and 16 mm in diameter, equipped with a cooling jacket and a coaxial pocket for a thermocouple, and a steam collector 21.The volume of catalyst loaded into the reactor is 100 cm 3 (fraction 1-2 mm mixed with 100 cm 3 1-2 mm quartz).
The temperature in the catalytic zone is controlled by removing excess reaction heat due to the phase transition of water to steam in the cooling jacket or, in case of a lack of heat, by heating the water in the jacket using a heating furnace and a Thermodat 38 temperature controller.The parameters (T, P) of boiling water in the jacket are set by the pressure regulator 26.The pressure in the plant and the reactor is controlled by pressure gauge 9 and electronic pressure sensors 11 and 33.The reaction product cooling unit is a set of air-cooled separators 27 and 30 and a water cooler 29.
Before starting the catalytic tests, the catalyst was reduced in a hydrogen flow for 3 h at a temperature of 400 °C and a GHSV of 3000 h −1 .Activation of the samples with synthesis gas with a ratio of H2/CO = 2 and catalytic tests were carried out at a pressure of 1.0 −1 The unit consists of a reagent preparation unit, a hydrocarbon synthesis reactor unit, and a reaction product cooling unit.H 2 and CO gases are supplied from cylinders 1 and 13 installed outdoors.Control over the level of gas consumption is carried out using the Bronkhorst gas flow regulators of the EL-FLOW series in automatic mode.The reactor block for hydrocarbon synthesis includes a reactor 20 1500 mm high and 16 mm in diameter, equipped with a cooling jacket and a coaxial pocket for a thermocouple, and a steam collector 21.The volume of catalyst loaded into the reactor is 100 cm 3 (fraction 1-2 mm mixed with 100 cm 3 1-2 mm quartz).
The temperature in the catalytic zone is controlled by removing excess reaction heat due to the phase transition of water to steam in the cooling jacket or, in case of a lack of heat, by heating the water in the jacket using a heating furnace and a Thermodat 38 temperature controller.The parameters (T, P) of boiling water in the jacket are set by the pressure regulator 26.The pressure in the plant and the reactor is controlled by pressure gauge 9 and electronic pressure sensors 11 and 33.The reaction product cooling unit is a set of air-cooled separators 27 and 30 and a water cooler 29.
Before starting the catalytic tests, the catalyst was reduced in a hydrogen flow for 3 h at a temperature of 400 • C and a GHSV of 3000 h −1 .Activation of the samples with synthesis gas with a ratio of H 2 /CO = 2 and catalytic tests were carried out at a pressure of 1.0 MPa and GHSV of 1000 h −1 , raising the temperature from 180 • C to the specified test temperature at a rate of 2.5 • C h −1 .
The production of an experimental batch of hydrocarbons of the gasoline fraction was carried out in a continuous mode of operation for 400 h.As collectors 27 and 30 were filled, the synthesis products (liquid C 5+ hydrocarbons and water) were drained and subjected to separation, fractionation, and analysis.Since in the course of long-term testing, there is a partial loss of the hydrotreating function of the catalyst, accompanied by a decrease in the content of isomeric structures (iso-alkanes, iso-alkenes) that affect the quality and performance characteristics of the fuel, all hydrocarbon samples taken over 400 h of operation were combined and used to determine the average characteristics of the fuel.
In parallel with the production of synthetic hydrocarbons, the temperature was controlled along the height of the catalytic layer and, if necessary, corrected.The average temperature in the catalytic bed was maintained in the range of 247-250 • C, which ensured a CO conversion of at least 70%.
The composition of the initial gas and gaseous synthesis products was analyzed using a Kristall 5000 gas chromatograph (Khromatek, Russia) equipped with a thermal conductivity detector and two columns (Haysep R active phase and NaX molecular sieves).The analysis mode is temperature-programmable with a heating rate of 8 • C/min.
The condensed synthesis products were separated via distillation at atmospheric pressure, separating fuel fractions with a boiling point: gasoline-up to 180 • C, diesel-180-330 • C, distillation residue-above 330 • C. The composition of C 5+ hydrocarbons was determined using an Agilent 7890A chromato-mass spectrometer (Agilent Technologies, Santa Clara, CA, USA) equipped with an MSD 5975C detector and an HP-5MS capillary column.

Conclusions
The conducted studies on the variation of technological parameters in the synthesis of FT on a bifunctional catalyst made it possible to identify the conditions under which the largest amount of gasoline fraction with the content of isomeric hydrocarbons is formed (pressure 1.0 MPa, temperature 250 • C, GHSV = 1000 h −1 ).Under these conditions, an experimental batch of gasoline fraction was produced at the pilot plant; its main properties were analyzed according to GOST.The resulting synthetic fraction of gasoline fuel in some parameters differs significantly from the requirements of GOST 51105-2020 for petroleum gasoline.There are no aromatic hydrocarbons and benzene in the synthetic fraction, which improves its environmental characteristics but reduces its operational characteristics-octane number and density.According to the content of olefins, the synthetic gasoline fraction is close to catalytically cracked gasoline.
Thus, gasoline fuel obtained through the fractionation of synthetic oil certainly has good environmental characteristics, but in terms of performance, it does not meet the requirements of the current standards for petroleum gasoline.The use of synthetic gasoline may become possible by compounding it, for example, with distillates from secondary oil refining processes at refineries.At the same time, C 1 -C 4 hydrocarbon gases, which are available in excess at refineries, can become raw materials for producing synthetic gasoline.
Another possible option for bringing synthetic gasoline to the requirements of GOST is its secondary processing, for example, light hydrogenation, catalytic reforming, and methoxylation processes.However, this requires additional research on the selection of catalysts and process modes.

Figure 1 .
Figure 1.X-ray diffraction pattern of the catalyst in the oxide form.

Figure 1 .
Figure 1.X-ray diffraction pattern of the catalyst in the oxide form.

Figure 2 .
Figure 2. TEM micrograph of the reduced catalyst and histogram of cobalt particle size distribution.

Figure 3 .
Figure 3. SEM micrographs of the catalyst in the oxide form.

Figure 2 .
Figure 2. TEM micrograph of the reduced catalyst and histogram of cobalt particle size distribution.

Figure 2 .
Figure 2. TEM micrograph of the reduced catalyst and histogram of cobalt particle size distribution.

Figure 3 .
Figure 3. SEM micrographs of the catalyst in the oxide form.

Figure 3 .
Figure 3. SEM micrographs of the catalyst in the oxide form.

Figure 5 .
Figure 5. Curve of temperature-programmed hydrogen reduction (TPR H 2 ) of the catalyst.

Figure 7 .
Figure 7. Temperature distribution along the height of the layer of a bifunctional cobalt catalyst for the synthesis of an FT catalyst for 400 h of operation.

Figure 7 .
Figure 7. Temperature distribution along the height of the layer of a bifunctional cobalt catalyst for the synthesis of an FT catalyst for 400 h of operation.

Figure 8 .
Figure 8.Molecular weight distribution of hydrocarbons in the average sample of C5+ hydro

Figure 8 .
Figure 8.Molecular weight distribution of hydrocarbons in the average sample of C 5+ hydrocarbons.

Table 1 .
Physicochemical properties of the catalyst.

of the Porous Structure Co 0 Particle Size, nm S BET , m 2 /g S EXT , m 2 /g V micro , cm 3 /g V Σ , cm 3 /g XRD TEM
Note: S BET -BET specific surface area; S EXT -external specific surface; V micro -specific volume of micropores; V Σ -total pore volume.Catalysts 2023, 13, x 3 of 16

Table 1 .
Physicochemical properties of the catalyst.

Table 2 .
Dependence of the activity and selectivity of the bifunctional cobalt catalyst for FT synthesis on pressure and temperature (GHSV = 1000 h -1 , H2/CO ratio = 2).

Table 2 .
Dependence of the activity and selectivity of the bifunctional cobalt catalyst for FT synthesis on pressure and temperature (GHSV = 1000 h −1 , H 2 /CO ratio = 2).
Note: iso/n is the ratio of hydrocarbons of isostructure to hydrocarbons of normal structure; o/p is the ratio of alkenes to alkanes (olefins to paraffins).

Table 4 .
Group composition of the synthesis products of the average sample of C 5+ hydrocarbons synthesized at the pilot plant.

Table 5 .
Physicochemical and operational parameters of the experimental gasoline fra hydrocarbons.

Table 5 .
Physicochemical and operational parameters of the experimental gasoline fraction of hydrocarbons.
Note: "-" means that the corresponding parameters are not regulated.

Table 6 .
Comparison of commercial vs. synthesized catalysts.