A Novel Electrochemical Sensing Platform for the Sensitive Detection and Degradation Monitoring of Methylene Blue

: Methylene blue is a toxic dye that is extensively used as a colorant in textile industries. Industrial efﬂuent containing methylene blue, when drained into water bodies without proper treatment, poses a serious threat to aquatic and human lives. In order to protect the biocycle, various methods have been established to detect and remove hazardous dyes from aqueous systems. Electrochemical methods are preferred, owing to their characteristic features of simplicity, portability, potential selectivity, cost effectiveness, and rapid responsiveness. Based on these considerations, an electrochemical sensor consisting of amino-group-functionalized, multi-walled carbon nanotubes (NH 2 - f MWCNTs) immobilized on a glassy carbon electrode (GCE) was developed for the sensitive detection of methylene blue in aqueous solutions. The performance of the designed sensor was ana-lyzed by electrochemical impedance spectroscopy, cyclic voltammetry, and square wave voltammetry. The developed sensing tool demonstrated promising features of sensitivity, selectivity, stability, fast responsiveness, and the ability to work with a very small volume of the analyte, i.e., in microliters, for analysis. Amino groups rich in electrons provide a negative charge to multi-walled carbon nanotubes, which signiﬁcantly enhances the electrocatalytic activity of NH 2 - f MWCNTs for cationic dyes such as methylene blue. Using the designed sensing platform, a linear calibration plot with a limit of detection of 0.21 nM was obtained for methylene blue under optimized conditions. The designed sensor was also employed to monitor the extent and kinetics of the degradation of methylene blue. Titania nanoparticles were used for photocatalytic degradation, and the kinetics of degradation was monitored by both UV-Visible spectroscopic and electrochemical methods. The results revealed more than 95% removal of methylene blue in a time span of just 30 min.


Introduction
Booming industrialization is fulfilling the demands of the growing population and sustaining a decent standard of living. However, the industrial revolution is also linked to environmental issues. The wastewater of textile, paint, and pigment industries is loaded with toxic dyes [1]. The presence of dyes changes the color, taste, smell, pH, and density of water. Their colors make the water too opaque for the penetration of light and reduce dissolved oxygen, which has a damaging impact on aquatic life. More than 7 × 10 5 metric tons of annual dye production is required to fulfill the demands of the industry. About 15% of these dyes are drained into water bodies, which contaminates the natural water [2]. The current global colorant market is 32 billion US dollars and is expected to increase by more saline (PBS) was prepared from 0.1 M Na 2 HPO 4 and 0.1 M NaH 2 PO 4 . HCl and NaOH solutions of 0.1 M each were used for the preparation of PBS solutions of different pH (3)(4)(5)(6)(7)(8)(9). The NH 2 -f MWCNTs (purity > 95%) were used for electrode modification.

Electrode Modification
Metrohm Autolab PGSTAT302N Switzerland was used for electrochemical studies. A three-electrode system was used, which comprised a bare GCE (0.07 cm 2 ) and modified GCE as working electrodes, platinum wire as a counter electrode, and Ag/AgCl (3 M KCl) as a reference electrode. Before the commencement of the electrochemical experiment, the GCE was used for cleaning until the appearance of a shiny surface was achieved [39]. For cleaning purposes, an 0.05 µm alumina-water slurry was used to rub the GCE over a rubbing pad in a figure-8 pattern to remove all the unwanted particles to obtain a clean surface. GCE was then sonicated and rinsed with deionized water to remove any loosely bonded particles. Cyclic voltammetry (CV) was performed in a potential window of 0-1.4 V to obtain reproducible CVs for ensuing cleanliness of the GCE surface [40]. To obtain the modified surface of GCE, a 5 µL droplet of the modifier solution was drop-casted on the activated surface of the bare GCEs.

Experimental Procedure
Stock solutions of the desired analyte were prepared by using distilled water as a solvent. First, 5 µL of MWCNTs and NH 2 -f MWCNTs with a concentration of 0.89 mg/mL was drop-casted on two separate pre-cleaned GCEs and were allowed to dry in a vacuum oven at 50 • C. Then, 10 µL of the targeted analyte (MB) with a concentration of 10 µM was drop-casted onto each of the prepared sensors and dried to ensure the dye molecules were properly absorbed onto the surface of the designed sensors. The ability of the designed sensors (MWCNTs/GCE, NH 2 -f MWCNTs/GCE) to detect MB was examined using square wave voltammetry in phosphate buffer saline as the supporting electrolyte. The voltammograms were recorded by applying a potential window from the negative to positive direction allowing the dye molecules to oxidize. The designed sensors significantly enhanced the signal of MB as compared to bare GCE. The NH 2 -f MWCNTs were found to be a very promising electrode modifier for the detection of cationic dye MB as compared to MWCNTs. The reason may be the nitrogen-containing group (NH 2 ) that lends a negative charge to the surface of MWCNTs to preconcentrate the positively charged MB molecules.

Electrochemical Characterization
Electrochemical Impedance Spectroscopy (EIS) was used to assess the charge transfer features of bare and modified GCEs. The frequency was varied from 1 to 14 kHz with an amplitude of 10 mV in a solution of 5 mM K 3 [Fe(CN) 6 ] and 0.1 M KCl. Nyquist plots constructed from the EIS data obtained at bare and modified GCEs showed a semicircle in the high-frequency region and a linear portion in the low-frequency region. The resistance due to the charge transfer at the electrode/electrolyte interface is shown by the semicircular part, while the straight-line segment of the plot in the lower-frequency region corresponds to diffusion mass transfer as represented by Warburg impedance [41][42][43]. The lower diameter of the semicircle in the Nyquist plot for NH 2 -f MWCNTs/GCE as compared to MWCNTs/GCE and the bare GCE demonstrates faster charge transfer as evident from Figure 1A [44]. The R ct values obtained for MWCNTs/GCE (3070.5 Ω) and NH 2 -f MWCNTs/GCE (2.6 Ω) are lower than the bare glassy carbon electrode (5493.7 Ω). This may be attributed to an increase in surface area of the modified GCE with enhanced conductivity characteristics for rapid charge transport of the redox probe. Randle's equivalent circuit (inset Figure 1A) was used to fit EIS data for the evaluation of parameters as listed in Table S1 where R s denotes the solution resistance, R ct is the charge transfer resistance, and CPE is the constant phase element. The solution resistance (R s ) is offered to the migration of charges through the electrolyte solution, the constant phase element corresponds to the electrical double layer capacitance, R ct corresponds to the occurrence of charge transfer of the redox probe at the surface of the electrode, and the Warburg (W) impedance models represent the diffusional mass transport from the electrode surface to the bulk, and vice versa. This may be attributed to an increase in surface area of the modified GCE with enhanced conductivity characteristics for rapid charge transport of the redox probe. Randle's equivalent circuit (inset Figure 1A) was used to fit EIS data for the evaluation of parameters as listed in Table S1 where Rs denotes the solution resistance, Rct is the charge transfer resistance, and CPE is the constant phase element. The solution resistance (Rs) is offered to the migration of charges through the electrolyte solution, the constant phase element corresponds to the electrical double layer capacitance, Rct corresponds to the occurrence of charge transfer of the redox probe at the surface of the electrode, and the Warburg (W) impedance models represent the diffusional mass transport from the electrode surface to the bulk, and vice versa. CV was performed to probe the current response of the analyte to the bare and modified GCEs. A 5 mM K3[Fe(CN)6] was used as a redox probe with a 0.1 M potassium chloride solution as a supporting electrolyte. In Figure 1B, the modified GCE shows an enhanced peak current of the redox probe as compared to bare GCE. The Randle-Sevcik equation (Ip = 2.6 × 10 5 n 3/2 D 1/2 ν 1/2 AC) was used to measure the active surface area of the modified and bare GCE. The calculated active surface areas, redox peak currents, and ΔEp of the modified and bare GCEs are listed in Table S2, which indicates that the designed sensor (NH2-fMWCNTs/GCE) provides more sites for [Fe(CN)6] −3/−4 than the signals obtained at MWCNTs/GCE and bare GCE, as witnessed by the enhanced peak current signal of K3[Fe(CN)6].

Voltammetric Analysis of the Targeted Analyte
Square wave voltammetry is a sensitive and rapid electroanalytical technique for analyzing the analyte signals with a high resolution. The voltammetric response of the MB dye at the bare and modified working electrodes was obtained in a 0.1 M PBS solution of pH 6 in a potential window of −0.6 V to 0.5 V at a scan rate of 125 mV/s. MB oxidized at −0.24 V with a maximum current response of 8.3 μA at bare GCE. The current response of MB jumped to 12.6 μA and 19.5 μA at MWCNTs/GCE and NH2-fMWCNTs/GCE, respectively, as shown in Figure 2. Thus, GCE modified with NH2-fMWCNTs is the best platform for MB detection. The amino group is introduced for enhancing the electrocatalytic activity of MWCNTs. However, due to the amino group, the modified electrode (NH2-fMWCNTs/GCE), when tested in a blank solution, gives an CV was performed to probe the current response of the analyte to the bare and modified GCEs. A 5 mM K 3 [Fe(CN) 6 ] was used as a redox probe with a 0.1 M potassium chloride solution as a supporting electrolyte. In Figure 1B, the modified GCE shows an enhanced peak current of the redox probe as compared to bare GCE. The Randle-Sevcik equation (I p = 2.6 × 10 5 n 3/2 D 1/2 ν 1/2 AC) was used to measure the active surface area of the modified and bare GCE. The calculated active surface areas, redox peak currents, and ∆E p of the modified and bare GCEs are listed in Table S2, which indicates that the designed sensor (NH 2 -f MWCNTs/GCE) provides more sites for [Fe(CN) 6 ] −3/−4 than the signals obtained at MWCNTs/GCE and bare GCE, as witnessed by the enhanced peak current signal of K 3 [Fe(CN) 6 ].

Voltammetric Analysis of the Targeted Analyte
Square wave voltammetry is a sensitive and rapid electroanalytical technique for analyzing the analyte signals with a high resolution. The voltammetric response of the MB dye at the bare and modified working electrodes was obtained in a 0.1 M PBS solution of pH 6 in a potential window of −0.6 V to 0.5 V at a scan rate of 125 mV/s. MB oxidized at −0.24 V with a maximum current response of 8.3 µA at bare GCE. The current response of MB jumped to 12.6 µA and 19.5 µA at MWCNTs/GCE and NH 2 -f MWCNTs/GCE, respectively, as shown in Figure 2. Thus, GCE modified with NH 2 -f MWCNTs is the best platform for MB detection. The amino group is introduced for enhancing the electrocatalytic activity of MWCNTs. However, due to the amino group, the modified electrode (NH 2f MWCNTs/GCE), when tested in a blank solution, gives an oxidation peak at 0.03 V. Every material has its own electrochemical oxidation potential [45]. It is interesting to note that the signal does not overlap with the response of MB. Hence, NH 2 -f MWCNTs/GCE allows the sensitive detection of MB.

of 13
Catalysts 2022, 12, x FOR PEER REVIEW 5 of 13 oxidation peak at 0.03 V. Every material has its own electrochemical oxidation potential [45]. It is interesting to note that the signal does not overlap with the response of MB. Hence, NH2-fMWCNTs/GCE allows the sensitive detection of MB.

Effect of Scan Rate
CV was performed to check the effect of the scan rate on the peak current of MB ( Figure 3A). To ascertain whether the electrochemical reactions are surface assisted or diffusion controlled, the relation between the signal intensity and scan rate was investigated. A linear plot between the peak current and scan rate shows a surface-controlled reaction, while linearity between the peak current and the square root of the scan rate shows a diffusion-controlled reaction. The oxidative peak current of MB was plotted against the scan rate and square root of the scan rate as shown in Figure S1A,B, respectively. A literature survey reveals that the process should be diffusion controlled if the plot of the log of the peak current vs. the log of the scan rate has a slope of 0.5 and adsorption controlled if the slope is equal to 1 [46]. The plot between the log of the oxidation peak current and the log of scan rates shown in Figure 3B, with a slope of 0.72, suggests the involvement of both surface and diffusional processes. However, the adsorption process seems dominant as the correlation coefficient of the plot between the peak current and scan rates ( Figure S1A) is higher as compared to the R 2 of the plot between the peak current and the square root of scan rates ( Figure S1B).

Effect of Scan Rate
CV was performed to check the effect of the scan rate on the peak current of MB ( Figure 3A). To ascertain whether the electrochemical reactions are surface assisted or diffusion controlled, the relation between the signal intensity and scan rate was investigated. A linear plot between the peak current and scan rate shows a surface-controlled reaction, while linearity between the peak current and the square root of the scan rate shows a diffusion-controlled reaction. The oxidative peak current of MB was plotted against the scan rate and square root of the scan rate as shown in Figure S1A,B, respectively. A literature survey reveals that the process should be diffusion controlled if the plot of the log of the peak current vs. the log of the scan rate has a slope of 0.5 and adsorption controlled if the slope is equal to 1 [46]. The plot between the log of the oxidation peak current and the log of scan rates shown in Figure 3B, with a slope of 0.72, suggests the involvement of both surface and diffusional processes. However, the adsorption process seems dominant as the correlation coefficient of the plot between the peak current and scan rates ( Figure S1A) is higher as compared to the R 2 of the plot between the peak current and the square root of scan rates ( Figure S1B).   Several parameters were optimized to obtain the maximum current response of MB using NH 2 -f MWCNTs modified GCE. The selection of the supporting electrolyte is important for obtaining a robust, intense signal of the targeted analyte. To investigate the maximum current response of the targeted analyte (MB), different supporting electrolytes, such as the Britton Robinson buffer (BRB), KCl, NaCl, HCl, H 2 SO 4 , NaOH, Acetate buffer, and phosphate buffer saline (pH = 6.0), of a 0.1 M concentration were examined. The most suitable supporting electrolyte was found to be PBS in which the analyte oxidized with the maximum current response and well-defined peak shape as compared to other electrolytes, as shown in Figure S2. The corresponding bar graph shown in Figure 4 demonstrates PBS as the most suitable supporting electrolyte for the detection of MB.

Optimization of Experimental Parameters. Influence of Supporting Electrolyte, pH, Deposition Potential, and Deposition Time
Several parameters were optimized to obtain the maximum current response of MB using NH2-fMWCNTs modified GCE. The selection of the supporting electrolyte is important for obtaining a robust, intense signal of the targeted analyte. To investigate the maximum current response of the targeted analyte (MB), different supporting electrolytes, such as the Britton Robinson buffer (BRB), KCl, NaCl, HCl, H2SO4, NaOH, Acetate buffer, and phosphate buffer saline (pH = 6.0), of a 0.1 M concentration were examined. The most suitable supporting electrolyte was found to be PBS in which the analyte oxidized with the maximum current response and well-defined peak shape as compared to other electrolytes, as shown in Figure S2. The corresponding bar graph shown in Figure 4 demonstrates PBS as the most suitable supporting electrolyte for the detection of MB. The effect of pH on the response of MB was investigated using PBS solutions of pH 3-9. The most intense signal was obtained in a medium of pH 6.0 as shown in Figure 5A. In an acidic electrolyte, the oxidation peak of methylene blue was decreased due to the high concentration of H + ions. The reason could be the gain of protons from the solution by the electron-rich modifier (NH2-fMWCNTs) instead of MB. With the increase in pH of The effect of pH on the response of MB was investigated using PBS solutions of pH 3-9. The most intense signal was obtained in a medium of pH 6.0 as shown in Figure 5A. In an acidic electrolyte, the oxidation peak of methylene blue was decreased due to the high concentration of H + ions. The reason could be the gain of protons from the solution by the electron-rich modifier (NH 2 -f MWCNTs) instead of MB. With the increase in pH of the medium, the availability of H + competing with cationic MB should decrease in the solution and, as a result, modifier molecules are expected to interact with more MB molecules and thus preconcentrate them at the electrode surface. Hence, at the oxidation potential of MB, an intense anodic peak appears in the solution of pH 6. At a pH higher than 6, the availability of more OH − ions in the solution may hinder cationic MB molecules from accessing the electrode surface, and as a consequence, lower peak current MB is evidenced. Therefore, in a basic medium, the oxidation current of MB decreased significantly. The pH-dependent shift of the peak potential suggests the involvement of protons during electron transfer reactions. The ratio of the number of electrons and protons participating in the proton-coupled oxidation process was calculated from the plot of the peak potential as a function of pH using the equation ∆E p /∆pH = 2.303 mRT/nF, where m/n is the ratio of protons and electrons. The Nernstian slope of 58 mV/pH as shown in Figure 5B was obtained by the linear fitting of the peak potential vs. the pH plot, which reveals an equal number of protons and electrons involved in the oxidation process of MB. The proposed oxidation mechanism of MB involving two electrons and two protons can be seen in Scheme 1. tons participating in the proton-coupled oxidation process was calculated from the plot of the peak potential as a function of pH using the equation ΔEp/ΔpH = 2.303 mRT/nF, where m/n is the ratio of protons and electrons. The Nernstian slope of 58 mV/pH as shown in Figure 5B was obtained by the linear fitting of the peak potential vs. the pH plot, which reveals an equal number of protons and electrons involved in the oxidation process of MB. The proposed oxidation mechanism of MB involving two electrons and two protons can be seen in Scheme 1. SWV was used to investigate the effect of the deposition potential and time on the peak current of 10 μM MB. The signal intensity was found to increase by increasing the negative potential up to −0.3 V. With the increase in negative potential, cationic dye molecules are expected to bind strongly to the anionic modifier NH2-fMWCNTs as evident from Figure S3. The effect of deposition time on the response of MB was also investigated. At an accumulation time of 60 s, the maximum current response, as shown in Figure S4, can be related to the effective orientation of preconcentrated molecules at the modified GCE. Therefore, in the subsequent experiments, a 60 s accumulation time was chosen for the analytical detection of the targeted analyte. protons during electron transfer reactions. The ratio of the number of electrons and protons participating in the proton-coupled oxidation process was calculated from the plot of the peak potential as a function of pH using the equation ΔEp/ΔpH = 2.303 mRT/nF, where m/n is the ratio of protons and electrons. The Nernstian slope of 58 mV/pH as shown in Figure 5B was obtained by the linear fitting of the peak potential vs. the pH plot, which reveals an equal number of protons and electrons involved in the oxidation process of MB. The proposed oxidation mechanism of MB involving two electrons and two protons can be seen in Scheme 1. SWV was used to investigate the effect of the deposition potential and time on the peak current of 10 μM MB. The signal intensity was found to increase by increasing the negative potential up to −0.3 V. With the increase in negative potential, cationic dye molecules are expected to bind strongly to the anionic modifier NH2-fMWCNTs as evident from Figure S3. The effect of deposition time on the response of MB was also investigated. At an accumulation time of 60 s, the maximum current response, as shown in Figure S4, can be related to the effective orientation of preconcentrated molecules at the modified GCE. Therefore, in the subsequent experiments, a 60 s accumulation time was chosen for the analytical detection of the targeted analyte. SWV was used to investigate the effect of the deposition potential and time on the peak current of 10 µM MB. The signal intensity was found to increase by increasing the negative potential up to −0.3 V. With the increase in negative potential, cationic dye molecules are expected to bind strongly to the anionic modifier NH 2 -f MWCNTs as evident from Figure S3. The effect of deposition time on the response of MB was also investigated. At an accumulation time of 60 s, the maximum current response, as shown in Figure S4, can be related to the effective orientation of preconcentrated molecules at the modified GCE. Therefore, in the subsequent experiments, a 60 s accumulation time was chosen for the analytical detection of the targeted analyte.

Analytical Characterization
The designed sensor was applied for the determination of MB up to its lowest limit of detection by using square wave voltammetry. The concentration-based voltammograms of MB are shown in Figure 6A. A linear calibration curve plotted between the peak current and concentration (0.01 µM to 0.5 µM) can be seen in Figure 6B. The limit of detection (LOD = 3 σ/m) and limit of quantification (LOQ = 10 σ/m) of the targeted analyte were evaluated from the calibration plot by applying IUPAC guidelines [47]. The standard deviation represented by σ was calculated by the current values (n = 11) of the blank solution at the peak position of the analyte [48]. The calculated limit of detection and limit of quantification of MB are 0.21 nM and 0.70 nM, respectively. Table 1 shows the comparison of MB sensors and reveals figures of merit of our designed sensing platform. grams of MB are shown in Figure 6A. A linear calibration curve plotted between the peak current and concentration (0.01 μM to 0.5 μM) can be seen in Figure 6B. The limit of detection (LOD = 3 σ/m) and limit of quantification (LOQ = 10 σ/m) of the targeted analyte were evaluated from the calibration plot by applying IUPAC guidelines [47]. The standard deviation represented by σ was calculated by the current values (n = 11) of the blank solution at the peak position of the analyte [48]. The calculated limit of detection and limit of quantification of MB are 0.21 nM and 0.70 nM, respectively. Table 1 shows the comparison of MB sensors and reveals figures of merit of our designed sensing platform.

Validity of the Designed Sensor
Reproducibility and repeatability are the key factors for assessing the validity of a sensor. For the reproducibility test, we prepared four modified GCEs under the same conditions and applied these for recording SW voltammograms of MB under optimized conditions. On all four electrodes, the oxidation peak current of MB was almost the same, with an RSD value of 1.27%, as shown in Figure 7A. The repeatability of the designed sensor was also examined under optimized conditions. For this purpose, one electrode was prepared with NH2-fMWCNTs as a sensing platform and the same electrode was repeated several times for sensing experiments of MB. The peak current remained almost the same in all six experiments as shown in Figure 7B. Thus, the designed sensor showed inter-day repeatability and stability up to 20 h with an RSD value of 2.3%.

Validity of the Designed Sensor
Reproducibility and repeatability are the key factors for assessing the validity of a sensor. For the reproducibility test, we prepared four modified GCEs under the same conditions and applied these for recording SW voltammograms of MB under optimized conditions. On all four electrodes, the oxidation peak current of MB was almost the same, with an RSD value of 1.27%, as shown in Figure 7A. The repeatability of the designed sensor was also examined under optimized conditions. For this purpose, one electrode was prepared with NH 2 -f MWCNTs as a sensing platform and the same electrode was repeated several times for sensing experiments of MB. The peak current remained almost the same in all six experiments as shown in Figure 7B. Thus, the designed sensor showed inter-day repeatability and stability up to 20 h with an RSD value of 2.3%.

Degradation Study of MB on the Designed Electrochemical Sensor
The photocatalytic degradation of MB by TiO2 nanoparticles was investigated in an electrochemical cell. A stock solution of 0.1 mM MB (pH = 13.0) was prepared. Fifty milliliters of the stock solution were added to a beaker, to which 10 mg of TiO2 nanoparticles

Degradation Study of MB on the Designed Electrochemical Sensor
The photocatalytic degradation of MB by TiO 2 nanoparticles was investigated in an electrochemical cell. A stock solution of 0.1 mM MB (pH = 13.0) was prepared. Fifty milliliters of the stock solution were added to a beaker, to which 10 mg of TiO 2 nanoparticles were added. This was then stirred for 10 min in the dark. Ten microliters of the as-prepared solution were drop-casted onto the modified GCE (NH 2 -f MWCNTs/GCE) and subsequently dried. The influence of pH on the photodegradation of MB was studied. The breakdown of dye was found to occur faster in basic conditions. [52] Therefore, photodegradation experiments were conducted in an alkaline medium using 0.3 M NaOH solution as the supporting electrolyte. The voltammogram of the MB was recorded under optimized conditions by employing a modified electrode under direct sunlight. At intervals of every 3 min, the same procedure was followed as described above. The corresponding voltammograms for the photodegradation of MB are shown in Figure 8A. The concentration of the dye in the solution decreased over time due to degradation, and as a result, a decrease in the peak current was observed. Initially, the peak current decreased more rapidly, indicating faster loss of electrophores (moiety of the MB molecule undergoing oxidation) present in the dye structure. The overall degradation percentage of MB was calculated using Equation (1).

% degradation =
Maximum peak current − Minimum peak current Maximum peak current × 100 (1) The graphs of the percent degradation and extent of degradation vs. time can be seen in Figure S5. The % degradation was calculated to be 95.9%. The kinetics of MB degradation was also investigated. The rate constant (k) with a value of 0.11 min −1 was calculated from the plot between ln[(I p ) t /(I p ) o ] and time using the equation of first-order kinetics ( Figure 8B).

Spectrophotometric Study of the Degradation of MB
Time-based UV-visible spectra of the irradiated MB solution containing titania nanoparticles were recorded. Figure 9A shows a decrease in the absorption spectra of MB over time. The diminution in the absorption spectra corresponds to the degradation of MB by TiO2 nanoparticles under sunlight. The study was conducted in basic conditions to determine the influence of irradiation time on the photocatalytic degradation of MB. The increase in radiation time of sunlight caused an increase in the photodegradation of dye molecules. Over a time span of 30 min, the maximum degradation (98.1%) was observed. The order of the reaction was ensured from the linearity of the plot between ln (Ct/C0) and the irradiation time ( Figure 9B) using a first-order equation (ln(Ct/Co) = −kt), where Co

Spectrophotometric Study of the Degradation of MB
Time-based UV-visible spectra of the irradiated MB solution containing titania nanoparticles were recorded. Figure 9A shows a decrease in the absorption spectra of MB over time. The diminution in the absorption spectra corresponds to the degradation of MB by TiO 2 nanoparticles under sunlight. The study was conducted in basic conditions to determine the influence of irradiation time on the photocatalytic degradation of MB. The increase in radiation time of sunlight caused an increase in the photodegradation of dye molecules. Over a time span of 30 min, the maximum degradation (98.1%) was observed. The order of the reaction was ensured from the linearity of the plot between ln (C t /C 0 ) and the irradiation time ( Figure 9B) using a first-order equation (ln(C t /C o ) = −kt), where C o represents the absorbance at time 0 and C t is the absorbance at time t. The rate constant with a value of 0.12 min −1 was calculated from the slope of the first-order kinetic plot. Figure S6 shows graphs of the percent and extent of the degradation of MB.

Spectrophotometric Study of the Degradation of MB
Time-based UV-visible spectra of the irradiated MB solution containing titania nanoparticles were recorded. Figure 9A shows a decrease in the absorption spectra of MB over time. The diminution in the absorption spectra corresponds to the degradation of MB by TiO2 nanoparticles under sunlight. The study was conducted in basic conditions to determine the influence of irradiation time on the photocatalytic degradation of MB. The increase in radiation time of sunlight caused an increase in the photodegradation of dye molecules. Over a time span of 30 min, the maximum degradation (98.1%) was observed. The order of the reaction was ensured from the linearity of the plot between ln (Ct/C0) and the irradiation time ( Figure 9B) using a first-order equation (ln(Ct/Co) = −kt), where Co represents the absorbance at time 0 and Ct is the absorbance at time t. The rate constant with a value of 0.12 min −1 was calculated from the slope of the first-order kinetic plot. Figure S6 shows graphs of the percent and extent of the degradation of MB.

Conclusions
A fast, sensitive, and stable sensor based on NH 2 -f MWCNTs/GCE was developed for the determination of the concentration of MB. Under optimized conditions, detection and quantification limits were found to be 0.21 nM and 0.70 nM, respectively. MB was found to oxidize in a pH-dependent manner involving the loss of two electrons and two protons. The sensor demonstrated the qualities of simplicity, reproducibility, and repeatability. The sensor also showed promise for monitoring the photocatalytic degradation of MB. The results of both electrochemical and UV-Vis spectrophotometric techniques suggested that the breakdown of MB follows first-order kinetics. The percent degradation evaluated by employing voltammetric and spectrophotometric methods was found to be 95.9% and 98.1%, respectively. In the future, the applicability horizon of such sensors may be extended by coupling them with industries for early sensing and degradation of dye pollutants prior to the release of industrial effluents into freshwater bodies.