Morphology and Photocatalytic Activity of Zinc Oxide Reinforced Polymer Composites: A Mini Review

: There is an approximately 3% of fresh water available globally for utilization, while the rest of the water is not available for usage, leaving billions of people with less water. Less water availability means that the majority of water consists of pollutants either in ground water or drinking water, which in turn may have a negative impact on the environment and people. Various methods such as plasma technology, ﬂocculation, neutralization, and disinfection have been utilized for wastewater treatment. The wastewater treatment methods have been found to be selective in terms of the removal of other pollutants, as a result, the majority of them are unable to remove pollutants such as antibiotics at a trace level. In order to ensure that there is a complete removal of pollutants from water, there is a need for the development of alternative wastewater treatment methods. The use of solar light by photocatalysis is an alternative method for the degradation of toxic pollutants. Different photocatalysts such as zinc oxide (ZnO), titanium dioxide (TiO 2 ), and silver (Ag) have been used in the process of photocatalysis. However, the above photocatalysts were found to have drawbacks such as agglomeration at higher contents and health problems during transportation. To solve the above problem, the nanoparticles were immobilized in various matrices such as polymers and ceramics, with polymers being preferred because of low cost, chemical inertness, and high durability. The current review discusses various methods for the preparation of ZnO and its synergy with other nanoparticles incorporated in various polymer matrices. Because it is known that the preparation method(s) affects the morphology, the morphology and the photocatalytic activity of various ZnO/polymer composites and hybrid systems of ZnO/other nanoparticles/polymer composites are discussed in depth.


Introduction
The current generation is having serious problems when it comes to the energy crisis and pollution [1][2][3][4][5]. More people have died due to pollution every year when compared to war or violence. According to the World Health Organization, there are approximately 250 million people who die every year due to diseases resulting from contaminated natural sources such as cholera, typhoid fever, polio, etc. [6].
Water pollution has been the major concern for researchers globally since it is associated with deadly diseases. Water pollution is caused by various sources such as the industrial and agricultural sectors [7]. The industrial sector is leading in terms of water pollution as various industries such as the leather, textile, food, printing, and pharmaceutical release wastewater into the environment [7]. Wastewater released by the industries consists mainly of dangerous pollutants in the form of organic and inorganic pollutants. There is a need for the utilization of environmentally friendly methods in order to reduce pollution as it is associated with dangerous diseases. There are different experimental methods that have been employed to reduce pollution, not all of it, however, they have contributed significantly in terms of the reduction in pollution. For example, methods such as membrane adsorption [8], chemical coagulation [9], adsorption techniques [10], sedimentation [11], flocculation [12], and photocatalysis [13] have been used for the removal of various pollutants. One of the most preferred methods in terms of reducing pollution is the utilization of the technique known as photo-catalysis. Except for photocatalysis, these techniques were found to have limitations with regard to the removal of pollutants, especially the dyes from an aqueous medium. Photocatalysis is the preferred method over other methods due to (i) the conversion of pollutants into less toxic products; (ii) advanced oxidation may result in non-selectivity of pollutants; and (iii) less possibility of forming hazardous materials as by-products [14][15][16][17][18]. Various nanoparticles have been used as photocatalysts, which include titanium dioxide (TiO 2 ) [14,15], stannic oxide (SnO 2 ) [16], ZnO [17], silver, and ferric oxide (Fe 2 O 3 ) [18]. Amongst the above-mentioned nanoparticles, the most commonly utilized nanoparticles for photocatalysis are ZnO, TiO 2 , and silver. Figure 1 illustrates the number of publications in the photocatalysis of the three nanoparticles. According to Figure 1, in 2018 and 2019, TiO 2 was found to be the leading nanoparticle with second place taken by silver (Ag) in terms of the photocatalytic activity research. However, there was a steady increase in the number of publications for ZnO in 2021 and 2022 when compared to both TiO 2 and Ag. The driving force behind this paradigm shift results from the abovementioned merits associated with ZnO. Figure 2 illustrates the top countries in terms of the research on the photocatalysis of ZnO. tion as it is associated with dangerous diseases. There are different experiment that have been employed to reduce pollution, not all of it, however, they have c significantly in terms of the reduction in pollution. For example, methods su brane adsorption [8], chemical coagulation [9], adsorption techniques [10], sed [11], flocculation [12], and photocatalysis [13] have been used for the remova pollutants. One of the most preferred methods in terms of reducing pollution zation of the technique known as photo-catalysis. Except for photocatalysis, niques were found to have limitations with regard to the removal of pollutants the dyes from an aqueous medium. Photocatalysis is the preferred method methods due to (i) the conversion of pollutants into less toxic products; (ii) ad idation may result in non-selectivity of pollutants; and (iii) less possibility of fo ardous materials as by-products [14][15][16][17][18]. Various nanoparticles have been use catalysts, which include titanium dioxide (TiO2) [14,15], stannic oxide (SnO2 [17], silver, and ferric oxide (Fe2O3) [18]. Amongst the above-mentioned nanop most commonly utilized nanoparticles for photocatalysis are ZnO, TiO2, and si 1 illustrates the number of publications in the photocatalysis of the three nan According to Figure 1, in 2018 and 2019, TiO2 was found to be the leading n with second place taken by silver (Ag) in terms of the photocatalytic activit However, there was a steady increase in the number of publications for ZnO i 2022 when compared to both TiO2 and Ag. The driving force behind this par results from the above-mentioned merits associated with ZnO. Figure 2 illustr countries in terms of the research on the photocatalysis of ZnO.  Various countries have taken the lead in terms of the photocatalytic activity of ZnO ( Figure 3). For example, India is the leading country in terms of the ZnO photocatalysis. The main reason why India is leading in terms of the photocatalysis of ZnO is because of the need to clean their wastewater to accommodate their high population needs. The pressure comes from their population, which is estimated to reach ~1.5 billion by 2050, with the projection that 50% of the total population is expected to be in urban areas [19]. An increase in urbanization will trigger more water usage, as a result, the need for the treatment of wastewater. There are other reasons as to why ZnO nanoparticles are favored over others. For example, ZnO has been chosen because of its wide band (viz. 3.37 eV) and large excitation binding energy (approximately 60 meV). Furthermore, the various morphologies associated with ZnO such as nanorods, nanotubes, and nanowires are also key for the utilization of ZnO in photocatalysis [20][21][22][23][24]. Aside from the photocatalytic efficacy of ZnO-based materials, their long-term effect on the environment/health and cost associated with their recovery and reusability have been of major concern. The incorporation of these materials into polymers overcomes these limitations. The immobilized ZnO onto polymeric materials offers the possibility for their recovery and reuse in wastewater treatment, hence reducing the costs. This review paper discusses the photocatalytic activity of zinc oxide incorporated in various polymer matrices. Furthermore, the synergistic effect of ZnO with other nanoparticles is also reported with regard to photocatalytic activity.  Various countries have taken the lead in terms of the photocatalytic activity of ZnO ( Figure 3). For example, India is the leading country in terms of the ZnO photocatalysis. The main reason why India is leading in terms of the photocatalysis of ZnO is because of the need to clean their wastewater to accommodate their high population needs. The pressure comes from their population, which is estimated to reach~1.5 billion by 2050, with the projection that 50% of the total population is expected to be in urban areas [19]. An increase in urbanization will trigger more water usage, as a result, the need for the treatment of wastewater. There are other reasons as to why ZnO nanoparticles are favored over others. For example, ZnO has been chosen because of its wide band (viz. 3.37 eV) and large excitation binding energy (approximately 60 meV). Furthermore, the various morphologies associated with ZnO such as nanorods, nanotubes, and nanowires are also key for the utilization of ZnO in photocatalysis [20][21][22][23][24]. Aside from the photocatalytic efficacy of ZnO-based materials, their long-term effect on the environment/health and cost associated with their recovery and reusability have been of major concern. The incorporation of these materials into polymers overcomes these limitations. The immobilized ZnO onto polymeric materials offers the possibility for their recovery and reuse in wastewater treatment, hence reducing the costs. This review paper discusses the photocatalytic activity of zinc oxide incorporated in various polymer matrices. Furthermore, the synergistic effect of ZnO with other nanoparticles is also reported with regard to photocatalytic activity.

The Mechanism of Photocatalytic Activity
It is known that organic pollutants, especially the colored (viz. dyes) ones, have a tendency of being fully dissolved in water. It is well-documented that during the process of dye coating, almost 20% of the dye is lost, and it is transferred directly into the environment [25]. The presence of organic pollutants in the environment has the following disadvantages in the environment and health at large: (i) they have a negative impact on the marine life; (ii) they cause significant ecological problems; and (iii) pose serious health complications [26]. To overcome the above problems caused by organic pollutants, the utilization of the photocatalysts provide a better solution, as explained in the Introduction section. Photocatalytic activity occurs when a semiconductor nanoparticle absorbs a photon that has an energy equal to or more than the band gap of the nanoparticle. The irradiation of the photocatalyst with a corresponding wavelength transfers the electrons from the valence band to the conduction band and therefore, equal electron-hole pairs are formed. The excited electrons advance in a single electron reduction, and together with the O2, forms superoxide radicals. A reaction between electron holes and water produces the hydroxyl radicals. The produced radicals (i.e., superoxide and hydroxyl radical) are highly reactive and leads to the degradation of the organic pollutants to less toxic products [27]. It is worth mentioning that the resulting superoxide radicals are essential for metal ion reduction, and thus serve as important radicals in wastewater treatment. Figure 3 provide a detailed photocatalytic mechanism.

The Mechanism of Photocatalytic Activity
It is known that organic pollutants, especially the colored (viz. dyes) ones, have a tendency of being fully dissolved in water. It is well-documented that during the process of dye coating, almost 20% of the dye is lost, and it is transferred directly into the environment [25]. The presence of organic pollutants in the environment has the following disadvantages in the environment and health at large: (i) they have a negative impact on the marine life; (ii) they cause significant ecological problems; and (iii) pose serious health complications [26]. To overcome the above problems caused by organic pollutants, the utilization of the photocatalysts provide a better solution, as explained in the Introduction section. Photocatalytic activity occurs when a semiconductor nanoparticle absorbs a photon that has an energy equal to or more than the band gap of the nanoparticle. The irradiation of the photocatalyst with a corresponding wavelength transfers the electrons from the valence band to the conduction band and therefore, equal electron-hole pairs are formed. The excited electrons advance in a single electron reduction, and together with the O 2 , forms superoxide radicals. A reaction between electron holes and water produces the hydroxyl radicals. The produced radicals (i.e., superoxide and hydroxyl radical) are highly reactive and leads to the degradation of the organic pollutants to less toxic products [27]. It is worth mentioning that the resulting superoxide radicals are essential for metal ion reduction, and thus serve as important radicals in wastewater treatment. Figure 3 provide a detailed photocatalytic mechanism.

The History and Origins of Photocatalysis with Regard to TiO 2 , ZnO, and Ag
According to the CAPLUS and MEDLINE database (Sci Finder), the concept of photocatalysis was first introduced between 1910 and 1920 [28]. However, Teichner [29] emphasized that the research, more especially, the reactions based on the photocatalytic concept, began 52 years ago. TiO 2 was utilized earlier than 1970 in various applications that are more related to its photocatalytic applications. For example, in 1929, Keidel et al. [30] reported on the degradation of the paints and fabrics that were coated with TiO 2 . In 1938, TiO 2 was utilized as a photosensitizer to photobleach the dyes, which occurred in the presence of oxygen and produced reactive oxygen species [31]. It was observed from the UV absorption that the produced reactive oxygen species eventually caused the bleaching of the dyes. In 1956, Kato and Mashio [32] reported on the auto-oxidation by TiO 2 , which was utilized as a photocatalyst. In this study, TiO 2 was added into solvents and the mixture was analyzed by UV irradiation. The results were such that there was an auto-oxidation of the solvents while there was the formation of hydrogen peroxide in the process. In 1972, Fujishima and Honda [33] reported on the electrochemical photolysis of water at the semiconductor electrode. The authors designed an electrochemical cell whereby the TiO 2 electrode was connected with the platinum black electrode via an external load. The irradiation of the TiO 2 electrode followed the current from the platinum electrode to the TiO 2 one via an external circuit. The authors concluded that the direction of the current showed that the oxidation reaction took place at the TiO 2 electrode and reduction occurred at the platinum black electrode. The authors concluded that the water may have been decomposed by visible light into both oxygen and hydrogen in the absence of any external voltage. Despite the studies above, a real breakthrough in the research of TiO 2 photocatalysis was conducted in the early 1960s under UV irradiation [14]. The first research paper that might be considered as the first one on the photocatalysis of TiO 2 under UV light was reported by Kato and co-workers in 1964 [34]. This study reported on the liquid phase oxidation of the tetralin by employing titanium oxide as the catalyst. Generally, the authors reported that the photocatalytic activity of the system was different, depending on various factors such as the type of titanium oxide used, surface area, and lattice defects. After the investigation of the above study by Kato et al., various authors began reporting on TiO 2 as a catalyst in photocatalytic reactions by using UV irradiation [35][36][37][38][39][40][41][42][43][44][45]. Despite TiO 2 being utilized in the past as a catalyst in photocatalysis, ZnO nanoparticles have shown a huge potential as an alternative catalyst to TiO 2 for photocatalysis. Generally, zinc oxide has been studied by scientists since the 1930s [42]. Naturally, zinc oxide is found as an oxidic material in mineral zincite in the hexagonal wurtzite structure and was discovered in 1810 before being synthesized in Europe in 1850. The mineral zincite is found in various countries such as USA (New Jersey), Italy (Tuscany), Namibia, Poland, Spain, and Australia [42]. The first applications of zinc oxide included in watercolors as well as a diluent in paints, while in the late 1890s, it was used for the fabrication of oil paints. Currently, the scientific community has emphasized ZnO as a semiconductor. The first piezoelectric properties of ZnO were discovered in 1960, which led to the first electronic applications of ZnO as a thin layer in a surface sound wave [42]. The first report on silver nanoparticles was conducted by M.C. Lea 133 years ago, which involved the synthesis of the citrate stabilized silver in the form of a colloid, with an average diameter in the range of 7-9 nm [43]. Furthermore, in 1902, there was a study that reported on the stabilization of silver by employing the proteins [44]. The study was conducted in 1902, however, this type of nano silver has been in existence since 1897 under the name "Collargol". Collargol was mostly used in medical applications, and it was found to have a diameter of 10 nm. After the discovery of silver nanoparticles, as briefly discussed above, more studies over the next decade have reported on silver nanoparticles. For example, in 1953, a patent was published by Moudry [45] about gelatin silver nanoparticles, which were reported to have a diameter of 2-20 nm. Nowadays, the most common utilization of these three nanoparticles (viz. TiO 2 , ZnO and Ag) is in photocatalysis.

Photocatalytic Activity of ZnO Reinforced Polymer Matrices
In this section, the preparation method, morphology, and photocatalytic activity of the ZnO/polymer composites are discussed. Furthermore, the morphology and photocatalytic activity of ZnO and its synergy with other nanoparticles incorporated in various polymer matrices is discussed. There is also a brief discussion on the properties of the two systems (viz. ZnO/polymer and ZnO/other nanoparticles/polymer composites) after the exposure to UV irradiation.

ZnO Reinforced Polymer Composites: Preparation, Morphology, and Photocatalytic Activity
A fair number of studies have investigated the photocatalytic activity of the polymer/ZnO composites [46][47][48][49][50][51]. Factors such as the type of ZnO nanoparticle, modification of the nanoparticle, type of pollutant (i.e., dyes, etc.), irradiation time, synergy of the nanoparticles, and type of the polymer utilized for the photocatalysis applications of the polymer nanocomposite were found to affect the photocatalytic activity. Qiu et al. [46] reported on the photocatalytic removal of three unwanted materials in the form of phenol, methyl orange, and rhodamine B by fabricating ZnO/poly-(fluorene-co-thiophene) (PFT). The nanocomposites were fabricated by the following steps: PFT was dissolved in the tetrahydrofuran (THF) for 1 h. Furthermore, 0.5 g of ZnO powder was dissolved in ethanol solution and the mixture was stirred for 120 min. The composite was formed by adding PTF solution into a ZnO suspension through stirring. To ensure a uniform dispersion, the PTF/ZnO composites were further stirred for 30 min. Generally, it is important in photocatalytic activity to have a better dispersion of the nanoparticle as this enhances the chances of getting positive results. The SEM images in the absence of PTF showed that the particle size of ZnO did not change in the presence of PTF ( Figure 4). The advantage of utilizing PTF in this system is that PTF is a good photosensitizer. The statement is supported by the fact that approximately 40% of the phenol was removed in the PFT/ZnO system when compared with 10% removal with neat ZnO alone. The photocatalytic removal of the dyes (i.e., rhodamine B and methyl orange) were also reported in the absence of light (experiment taking place in the dark). The two types of dyes were found to undergo different photocatalytic removal. For example, in the case of rhodamine B, for the PFT/ZnO system, there was a reduction in the absorption peak, which was accompanied by hypsochromic shifting, with the shifting associated with the dismantling of the dye chromogen. However, methylene blue showed a different behavior-there was still a reduction in the absorption peak, but there was no shifting in the hypsochromic form. In this section, the preparation method, morphology, and photocatalytic activity of the ZnO/polymer composites are discussed. Furthermore, the morphology and photocatalytic activity of ZnO and its synergy with other nanoparticles incorporated in various polymer matrices is discussed. There is also a brief discussion on the properties of the two systems (viz. ZnO/polymer and ZnO/other nanoparticles/polymer composites) after the exposure to UV irradiation.

ZnO Reinforced Polymer Composites: Preparation, Morphology, and Photocatalytic Activity
A fair number of studies have investigated the photocatalytic activity of the polymer/ZnO composites [46][47][48][49][50][51]. Factors such as the type of ZnO nanoparticle, modification of the nanoparticle, type of pollutant (i.e., dyes, etc.), irradiation time, synergy of the nanoparticles, and type of the polymer utilized for the photocatalysis applications of the polymer nanocomposite were found to affect the photocatalytic activity. Qiu et al. [46] reported on the photocatalytic removal of three unwanted materials in the form of phenol, methyl orange, and rhodamine B by fabricating ZnO/poly-(fluorene-co-thiophene) (PFT). The nanocomposites were fabricated by the following steps: PFT was dissolved in the tetrahydrofuran (THF) for 1 h. Furthermore, 0.5 g of ZnO powder was dissolved in ethanol solution and the mixture was stirred for 120 min. The composite was formed by adding PTF solution into a ZnO suspension through stirring. To ensure a uniform dispersion, the PTF/ZnO composites were further stirred for 30 min. Generally, it is important in photocatalytic activity to have a better dispersion of the nanoparticle as this enhances the chances of getting positive results. The SEM images in the absence of PTF showed that the particle size of ZnO did not change in the presence of PTF ( Figure 4). The advantage of utilizing PTF in this system is that PTF is a good photosensitizer. The statement is supported by the fact that approximately 40% of the phenol was removed in the PFT/ZnO system when compared with 10% removal with neat ZnO alone. The photocatalytic removal of the dyes (i.e., rhodamine B and methyl orange) were also reported in the absence of light (experiment taking place in the dark). The two types of dyes were found to undergo different photocatalytic removal. For example, in the case of rhodamine B, for the PFT/ZnO system, there was a reduction in the absorption peak, which was accompanied by hypsochromic shifting, with the shifting associated with the dismantling of the dye chromogen. However, methylene blue showed a different behavior-there was still a reduction in the absorption peak, but there was no shifting in the hypsochromic form.   Prasert et al. [48] reported on the various properties of the polypropylene/ZnO nanocomposites including the photocatalytic dye degradation. The composites were fabricated with a twin-screw extruder, with 0, 0.5, 1, and 2 wt% of ZnO. The ZnO nanoparticles was reported to have an average diameter of 72 ± 18 nm. There was a good dispersion of the ZnO nanoparticles into the PP matrix ( Figure 5). White spots circled in red represent the ZnO particles well dispersed within the host polymeric material with size less than 100 nm (Figure 5d).
Prasert et al. [48] reported on the various properties of the polypropylene/ZnO composites including the photocatalytic dye degradation. The composites were fabr with a twin-screw extruder, with 0, 0.5, 1, and 2 wt% of ZnO. The ZnO nanoparticl reported to have an average diameter of 72 ± 18 nm. There was a good dispersion ZnO nanoparticles into the PP matrix ( Figure 5). White spots circled in red repres ZnO particles well dispersed within the host polymeric material with size less th nm (Figure 5d). The photocatalytic activity test was conducted through the degradation of met blue (MB) in UV irradiation [48]. PP containing 0.5% and 1% ZnO displayed MB de tion ranging in between 15 and 20% within 5 h, whereas the inclusion of 2% led degradation within 5 h. This is because of the limited number of ZnO exposed surface of PP, viz. at higher ZnO content, more of these fillers protrude on the sur the host polymer and hence higher MB degradation is achieved ( Figure 6). The ph bility and reusability of the composites for MB degradation were carried out three It was noticed that the nanocomposites maintained a MB degradation efficiency o for three cycles. It can be deduced that the use of melt-mixing has to be carefully c ered in order to control the number of ZnO particles being exposed to the dyed so Therefore, large quantities of ZnO are required to achieve a reasonable degradatio cacy because most of these fillers are embedded within the host polymeric materia The photocatalytic activity test was conducted through the degradation of methylene blue (MB) in UV irradiation [48]. PP containing 0.5% and 1% ZnO displayed MB degradation ranging in between 15 and 20% within 5 h, whereas the inclusion of 2% led to 59% degradation within 5 h. This is because of the limited number of ZnO exposed on the surface of PP, viz. at higher ZnO content, more of these fillers protrude on the surface of the host polymer and hence higher MB degradation is achieved ( Figure 6). The photostability and reusability of the composites for MB degradation were carried out three times. It was noticed that the nanocomposites maintained a MB degradation efficiency of~59% for three cycles. It can be deduced that the use of melt-mixing has to be carefully considered in order to control the number of ZnO particles being exposed to the dyed solution. Therefore, large quantities of ZnO are required to achieve a reasonable degradation efficacy because most of these fillers are embedded within the host polymeric material. Coating and growing particles on the surface of the polymers have been reported as an alternative method to ensure that there is a sufficient number of ZnO particles exposed on the surface of the polymer. For instance, Colmenares et al. reported [50] on the photocatalytic activity of ZnO nanorods incorporated into a polypropylene (PP) nonwoven fiber mat. The samples were prepared by three steps: (i) plasma treatment of PP polymer; (ii) discharge of ZnO into the PP fibers; and (iii) hydrothermal growth of the ZnO rods. Plasma treatment is very important since it enhances the coating of fibers with ZnO, and as a result, enhances the uniform dispersion of the nanoparticles. The uniform dispersion of the nanoparticle may result in high activity as well as stability during the photocatalytic activity of phenol. The fabricated samples were used for photocatalytic degradation of the aqueous phenol. The photocatalytic test was investigated for neat PP, PP/ZnO, and commercial ZnO. Figure 7 illustrates a typical photocatalytic reaction system employed in this study. The ZnO/PP system was found to be 3-fold higher than commercial ZnO in relation to the photocatalytic degradation of phenol. There are a few reasons associated with such an enhancement in the system consisting of ZnO/PP, first, this is due to the presence of 1D ZnO nanorods, which provides a vertical array structure with a lot of active sites and is able to collect light. Second, there is an ease of photo-electron flow to PP and resistance of the recombination of both the holes and the electrons. Coating and growing particles on the surface of the polymers have been reported as an alternative method to ensure that there is a sufficient number of ZnO particles exposed on the surface of the polymer. For instance, Colmenares et al. reported [50] on the photocatalytic activity of ZnO nanorods incorporated into a polypropylene (PP) nonwoven fiber mat. The samples were prepared by three steps: (i) plasma treatment of PP polymer; (ii) discharge of ZnO into the PP fibers; and (iii) hydrothermal growth of the ZnO rods. Plasma treatment is very important since it enhances the coating of fibers with ZnO, and as a result, enhances the uniform dispersion of the nanoparticles. The uniform dispersion of the nanoparticle may result in high activity as well as stability during the photocatalytic activity of phenol. The fabricated samples were used for photocatalytic degradation of the aqueous phenol. The photocatalytic test was investigated for neat PP, PP/ZnO, and commercial ZnO. Figure 7 illustrates a typical photocatalytic reaction system employed in this study. The ZnO/PP system was found to be 3-fold higher than commercial ZnO in relation to the photocatalytic degradation of phenol. There are a few reasons associated with such an enhancement in the system consisting of ZnO/PP, first, this is due to the presence of 1D ZnO nanorods, which provides a vertical array structure with a lot of active sites and is able to collect light. Second, there is an ease of photo-electron flow to PP and resistance of the recombination of both the holes and the electrons. A wide variety of conductive polymers including polyaniline (PANI), polythiophene, and polypyrrole have been employed to improve the photocatalytic efficiency of inorganic semi-conductors for various pollutants [49]. These polymers have extended πbonding that contribute to their conductivity. In general, the combination of the fillers and conductive polymers resulted in higher photocatalytic activity when compared to fillers alone [52][53][54]. Asgari et al. [49] reported on the preparation of PANI/ZnO via aniline in situ polymerization for the photodegradation of a metronidazole (MNZ) synthetic antibacterial agent. The pH of the solution was found to be one of the factors playing a key role in the removal of unwanted materials. The pH of the solution is key in terms of examining the influential radicals in the oxidation process [49]. The effect of pH of the ZnO/PANI photocatalytic degradation of the metronidazole (MNZ) at various radiation times was investigated under UV as well as visible light radiation [50]. The authors reported that at neutral pH (viz. pH = 7.0), both type of radiations (UV and visible light) showed 100% removal of the MNZ after 3 h radiation. However, at basic medium (pH = 10.0), the removal percentage of MNZ in both radiations were found to be 88% and 86%, respectively. A better adsorption of MNZ at pH 7.0 is attributed to a hydrogen bond and π-π interaction with the ZnO/PANI nanocomposite and MNZ. As explained earlier in this section, other factors that were reported to affect the photocatalytic activity include the type of the nanoparticle used and the type of polymer as a host material.
Ö zbay et al. [52] reported on the photocatalytic activity of polyaniline/ZnO for the photodegradation of Sunfix red S3B reactive dye. The authors investigated the influence of the irradiation time, photocatalyst, and dye concentration. It was noticed that the increase in dye concentration and photocatalyst dosage increased the removal efficiency due to a large number of active sites that increased the number of available hydroxyl radicals. The optimal dosage was found to be 1.6 g/L. The irradiation period of 10 min was sufficient for the degradation of the dye, regardless of the dye concentration. In their work, Eskizeybek and coworkers reported that the PANI/ZnO nanocomposite exhibited high photodegradation efficiency for methylene blue (MB) and malachite green (MG) under sunlight and UV light irradiation [53]. The photocatalytic performance under sunlight radiation was higher when compared to UV-light radiation. The degradation efficiency for both dyes was found to increase with an increase in photocatalyst dosage until 0.4 mg/mL, A wide variety of conductive polymers including polyaniline (PANI), polythiophene, and polypyrrole have been employed to improve the photocatalytic efficiency of inorganic semi-conductors for various pollutants [49]. These polymers have extended π-bonding that contribute to their conductivity. In general, the combination of the fillers and conductive polymers resulted in higher photocatalytic activity when compared to fillers alone [52][53][54]. Asgari et al. [49] reported on the preparation of PANI/ZnO via aniline in situ polymerization for the photodegradation of a metronidazole (MNZ) synthetic antibacterial agent. The pH of the solution was found to be one of the factors playing a key role in the removal of unwanted materials. The pH of the solution is key in terms of examining the influential radicals in the oxidation process [49]. The effect of pH of the ZnO/PANI photocatalytic degradation of the metronidazole (MNZ) at various radiation times was investigated under UV as well as visible light radiation [50]. The authors reported that at neutral pH (viz. pH = 7.0), both type of radiations (UV and visible light) showed 100% removal of the MNZ after 3 h radiation. However, at basic medium (pH = 10.0), the removal percentage of MNZ in both radiations were found to be 88% and 86%, respectively. A better adsorption of MNZ at pH 7.0 is attributed to a hydrogen bond and π-π interaction with the ZnO/PANI nanocomposite and MNZ. As explained earlier in this section, other factors that were reported to affect the photocatalytic activity include the type of the nanoparticle used and the type of polymer as a host material.
Özbay et al. [52] reported on the photocatalytic activity of polyaniline/ZnO for the photodegradation of Sunfix red S3B reactive dye. The authors investigated the influence of the irradiation time, photocatalyst, and dye concentration. It was noticed that the increase in dye concentration and photocatalyst dosage increased the removal efficiency due to a large number of active sites that increased the number of available hydroxyl radicals. The optimal dosage was found to be 1.6 g/L. The irradiation period of 10 min was sufficient for the degradation of the dye, regardless of the dye concentration. In their work, Eskizeybek and coworkers reported that the PANI/ZnO nanocomposite exhibited high photodegradation efficiency for methylene blue (MB) and malachite green (MG) under sunlight and UV light irradiation [53]. The photocatalytic performance under sunlight radiation was higher when compared to UV-light radiation. The degradation efficiency for both dyes was found to increase with an increase in photocatalyst dosage until 0.4 mg/mL, after which the efficiency was stable. This was attributed to a large surface area, which allows for the exposure of active sites available for photocatalytic reactions. The availability of these active sites may increase with the increase in photocatalyst content, but the light penetration was reduced due to a smaller surface area resulting from aggregation as well as light scattering. The photocatalytic efficiency of 99% for both dyes under natural sunlight was attained after 5 h. The efficiency of the photocatalyst under UV-light irradiation was 95% for MB and~98% for MG after 10 h. The material maintained higher photocatalytic efficiency after five repeated cycles, indicating the reusability of the resultant composites.
A thin coating layer of PANI on ZnO was obtained by mixing ZnO with dedoped PANI followed by filtration and drying at 60 • C [54]. It was reported that the maximum photocatalytic efficacy for ampicillin was achieved under sunlight irradiation when the irradiation period was 2 h, at a pH value of 5, and the initial ampicillin concentration of 4.5 mg/L. It can be deduced that aa combination of ZnO with conductive polymers facilitates the photocatalytic efficiency of pollutants because of the strong interaction between these polymers and ZnO, which contribute to more electrons to the conduction band of ZnO. On the other hand, experimental conditions such as pH, concentration of the pollutant, and photocatalyst dosage are important to achieve the desired photocatalytic results. The studies on the effect of ZnO content on the photocatalytic behavior of conductive polymers are scarce, hence, more studies are required to give an overview of the resulting degradation performance. It can be estimated that the higher content of ZnO within the host conductive polymer can positively increase the overall degradation performance because more of the particles will be exposed. Nonetheless, Saravanan et al. [55] studied the influence of PANI concentration on the photocatalytic behavior of the nanocomposites. The authors kept the ZnO content at 1.0 g while varying the ratio of PANI (i.e., 1, 1.5, 2 M) in the polymerization solution. The BET surface area increased with an increase in the PANI ratio, but the TEM images deduced that at high PANI content, there was significant agglomeration of the nanoparticles. The latter was ascribed to strong intermolecular interaction between ZnO and PANI. The band gap was, however, reported to decrease with an increase in the PANI content. The maximum photocatalytic performance was attained for 1.5 M PANI with a MO degradation of~98% and MB degradation of~99% within 2 h. In addition, the composite exhibited good stability and reusability for the photodegradation of dye after three cycles, suggesting its applicability in wastewater remediation. The efficiency of 1.5 M PANI-based composites was attributed to high crystallinity and strong intermolecular interaction between ZnO and PANI without noticeable agglomeration. When comparing the photocatalytic efficiency of a non-conductive polymer in the form of PMMA with the conductive polymers' systems, it was realized that the conductive polymer showed higher photocatalytic efficiencies. For example, Mauro et al. [56] reported on the photocatalysis of the ZnO/PMMA by low-temperature atomic layer deposition. The nanocomposites were fabricated by three various methods: (i) atomic layer deposition (ALD) of ZnO on PMMA and Si plates; (ii) atomic layer deposition of ZnO PMMA and solution; and (iii) sonication and solution casting. The photocatalytic activity of the nanocomposites was tested against two organic pollutants in water (i.e., methylene blue (MB) dye and sodium lauryl sulfate (SDS), an anionic surfactant). The morphology of the ZnO/PMMA fabricated by the ALD revealed that ZnO covered the PMMA, while the ALD + solution casting revealed the presence of voids, and the solution casting method showed holes in the PMMA matrix in which the ZnO embedded itself into those holes. The samples were subjected to UV light irradiation for the photocatalytic activity of MB. All the samples showed a reasonable efficacy in terms of the degradation of the MB dye. To be specific, the degradation of MB was reported to be approximately 62%, 55%, and 67% for ZnO "ALD", ZnO "ALD + solution casting", and ZnO solution casting, respectively. The difference in degradation % of MB was associated with the varied nanostructures of the samples. The SDS degradation was conducted for 4 h under UV light. The degradation of SDS was reported to be 64% (ZnO "ALD"), 66% (ZnO "ALD + solution casting"), and 73% (solution casting). When comparing the degradation of the two pollutants, the SDS pollutants were more degraded when compared with the MB. The behavior is associated with the positive charge of the ZnO, which enhances the interaction with the anionic surfactant, whereas the interaction is hindered with MB, which is positively charged.

Synergistic Effect of the ZnO with Other Nanoparticles Reinforced Polymer Composites
There have been a few studies [57][58][59][60] that have investigated the morphology and photocatalytic activity of ZnO with other nanoparticles incorporated into the polymer matrices. The synergy of the nanoparticles is expected to show better efficiency when compared with ZnO alone. Furthermore, the synergy of ZnO with other nanoparticles is important since ZnO undergoes easy self-oxidation when exposed to UV irradiation, in the process reducing the photocatalytic activity. In order to solve such a problem, ZnO is paired with another filler in order to avoid self-oxidation and improve the photostability of the overall composites. Naji et al. [57] reported on the photocatalytic degradation of methylene blue by the ZnO-Ag/polystyrene and ZnO/polystyrene systems. The ZnO-Ag synergy was fabricated by the photo deposition, and the ZnO-Ag/PS composite film was prepared by solution mixing using chloroform as a solvent. The photocatalytic activity of the ZnO-Ag/PS as well as ZnO/PS composites were analyzed by the degradation of methylene under a UV lamp. The synergy of ZnO-Ag within the polystyrene was found to be effective in terms of enhancing the photodegradation of methylene blue when compared with the ZnO-PS. According to the UV-Vis spectra (Figure 8), the MB was realized to have a maximum absorption at 665 nm, with the absorption at this peak being monitored to investigate the extent of MB degradation. Both ZnO-Ag/PS and ZnO-Ag/PS composites reduced the MB absorption gradually with time until the color changed due to the photocatalytic reaction. According to Figure 8d, the photodegradation efficiency of the samples is as follows: (i) 97% for ZnO-Ag/PS; (ii) 70% efficiency for ZnO/PS; and (iii) PS alone was found to be 19%. The main reason the ZnO-Ag/PS was found to be more effective in photocatalytic degradation was due to the presence of more active sites in the presence of Ag in the ZnO-Ag/PS composite.
The very same samples (i.e., (a) ZnO/PS composite, and (b) ZnO-Ag/PS film) were investigated for photodegradation after being reused three times. The aim of re-using the catalysts after they underwent three lots of photodegradation was to prove that the catalysts are cost-effective. This is beneficial in ensuring that there is a reduction in terms of the consumption of the catalyst. The efficiency of photodegradation was found to be 89% for ZnO-Ag/PS, while the ZnO/PS film reached an efficiency of 76%. In some cases, semiconductor quantum dots were incorporated into the synergistic system in order to enhance the photocatalytic properties. Iqbal and co-workers [58] reported on the photodegradation of the mesoporous TiO 2 in synergy with the ZnO quantum dots incorporated in the linear low polyethylene (LLDPE). The composites were fabricated by the solution casting for photodegradation of the tetracycline (TC) antibiotics through the fluorescent light irradiation. The composite was prepared by incorporating 8% of the TiO 2 /ZnO-quantum (TZ) into the LLDPE matrix. The morphology of the ZT incorporated into the LLDPE was undertaken by transmission electron microscopy (TEM). The neat nanoparticles of ZnO QDs and ZT were found to be irregular and spherical, accompanied by agglomeration (Figure 9). The average particle sizes for ZT and ZnO QDs were reported to be 12.5 ± 2.05 nm and 4.12 ± 0.23 nm, respectively. The very same samples (i.e., (a) ZnO/PS composite, and (b) ZnO-Ag/PS film) were investigated for photodegradation after being reused three times. The aim of re-using the catalysts after they underwent three lots of photodegradation was to prove that the catalysts are cost-effective. This is beneficial in ensuring that there is a reduction in terms of the consumption of the catalyst. The efficiency of photodegradation was found to be 89% for ZnO-Ag/PS, while the ZnO/PS film reached an efficiency of 76%. In some cases, semiconductor quantum dots were incorporated into the synergistic system in order to enhance the photocatalytic properties. Iqbal and co-workers [58] reported on the photodegradation of the mesoporous TiO2 in synergy with the ZnO quantum dots incorporated in the linear low polyethylene (LLDPE). The composites were fabricated by the solution casting for photodegradation of the tetracycline (TC) antibiotics through the fluorescent light irradiation. The composite was prepared by incorporating 8% of the TiO2/ZnO-quantum (TZ) into the LLDPE matrix. The morphology of the ZT incorporated into the LLDPE was undertaken by transmission electron microscopy (TEM). The neat nanoparticles of ZnO QDs and ZT were found to be irregular and spherical, accompanied by agglomeration (Figure 9). The average particle sizes for ZT and ZnO QDs were reported to be 12.5 ± 2.05 nm and 4.12 ± 0.23 nm, respectively. According to the FESEM, ZT was found to have pores and the average pore diameter was reported to be 1.17 μm (Figure 10). The reason for pores was attributed to the utilization of starch during the synthesis of the nanoparticles. The cross-sectional image of the 8%ZT@LLDPE (Figure 10d) was reported to be free of microcracks and voids. According to the FESEM, ZT was found to have pores and the average pore diameter was reported to be 1.17 µm (Figure 10). The reason for pores was attributed to the utilization of starch during the synthesis of the nanoparticles. The cross-sectional image of the 8%ZT@LLDPE (Figure 10d) was reported to be free of microcracks and voids. Green arrows indicate white spots representing ZnO QDs. Reprinted from [58].
The TiO2/LLDPE composite removed 42.7% of the tetracycline (TC) while the zinc oxide quantum was found to be effective when compared with TiO2, with the ZnO QD revealing a 53.4% removal of tetracycline (TC). This might be due to the generation of more reactive sites for ZnO QDs than the TiO2. The 8%ZT/LLDPE composite resulted in the highest efficiency removal of 85.4%. This was associated with the designation of the heterojunction between the nanofillers (viz. ZnO QDs and TiO2), which results in separation of the photogenerated e -/h + pairs. The mineralization efficiency and reusability of the composites after photodegradation were reported. There was an enhancement in the mineralization efficiency with an increase in time. The 8%-TZ@LLDPE system was found to have a higher mineralization efficiency (Figure 11a) than both the neat LLDPE and P25@LLDPE. For neat LLDPE, low mineralization efficiency was expected since there was no catalyst. The high efficiency in the presence of both semiconductive nanofillers was attributed to the formation of an effective heterojunction between the nanofillers, which most probably allows for the separation of the e − /h + , which in turn improves the recombination rate for photocatalytic activity. Similarly, the reusability is very important in photocatalysis since it provides more information on the photostability. Since the 8%-TZ@LLDPE system was found to be effective in terms of the photocatalytic degradation of the tetracycline (TC), it was chosen for the analysis of reusability wherein the sample was subjected to eight cycles of photodegradation. According to Figure 11b, the sample The TiO 2 /LLDPE composite removed 42.7% of the tetracycline (TC) while the zinc oxide quantum was found to be effective when compared with TiO 2 , with the ZnO QD revealing a 53.4% removal of tetracycline (TC). This might be due to the generation of more reactive sites for ZnO QDs than the TiO 2 . The 8%ZT/LLDPE composite resulted in the highest efficiency removal of 85.4%. This was associated with the designation of the heterojunction between the nanofillers (viz. ZnO QDs and TiO 2 ), which results in separation of the photogenerated e − /h + pairs. The mineralization efficiency and reusability of the composites after photodegradation were reported. There was an enhancement in the mineralization efficiency with an increase in time. The 8%-TZ@LLDPE system was found to have a higher mineralization efficiency (Figure 11a) than both the neat LLDPE and P25@LLDPE. For neat LLDPE, low mineralization efficiency was expected since there was no catalyst. The high efficiency in the presence of both semiconductive nanofillers was attributed to the formation of an effective heterojunction between the nanofillers, which most probably allows for the separation of the e − /h + , which in turn improves the recombination rate for photocatalytic activity. Similarly, the reusability is very important in photocatalysis since it provides more information on the photostability. Since the 8%-TZ@LLDPE system was found to be effective in terms of the photocatalytic degradation of the tetracycline (TC), it was chosen for the analysis of reusability wherein the sample was subjected to eight cycles of photodegradation. According to Figure 11b, the sample exhibited a comparable degradation efficiency after eight cycles, which supports the idea that this system may be stable enough for potential use in photocatalyst film applications.
Catalysts 2022, 12, x FOR PEER REVIEW 15 of 20 exhibited a comparable degradation efficiency after eight cycles, which supports the idea that this system may be stable enough for potential use in photocatalyst film applications. Figure 11. (a) Photocatalytic mineralization of TC for neat LLDPE and its hybrid system, and (b) recycled experiments utilizing 8%-ZT@LLDPE. Reprinted from [58].
ZnO and CuO were grafted into the polyester membrane to improve the photocatalytic reduction of Cr(VI). The reason Cr(IV) was investigated is because it is a toxic heavy metal, as a result, there is a need for its removal in wastewater. Scheme 1 illustrates the various steps for fabrication of the ZnO/CuO nanocomposite into the polyester [59]. The SEM images of the ZnO/CuO/polyester nanocomposite revealed that the polyester fabric was covered with flake-nanostructures. The reason for such a dense covering of the nanoparticles into the polyester fabric was associated with the alkaline treatment of the fabric, which produced roughness on the surface. It is generally known that in most cases, a rough surface is able to produce reaction sites for the ease of penetration by other materials, in this case, the nanoparticles. As a reference point, the concentration of Cr(VI) was measured by UV-Vis spectroscopy and recorded to be 200 ppm. The inserted test tubes in Figure 12 shows the wastewater before treatment (yellow test tube) and after treatment (clear test tube). The yellow color in the other container indicated the presence of Cr(VI), while the clear color indicated that the solar photocatalytic reduction reduced the concentration Cr(VI) in wastewater. According to Figure 12, it became evident that the continuous exposure of pure wastewater to irradiation reduced the concentration of Cr(VI) in water. For example, at 0 h, the concentration was approximately 200 ppm, while after 6 h, the concentration was found to be 24 ppm. ZnO and CuO were grafted into the polyester membrane to improve the photocatalytic reduction of Cr(VI). The reason Cr(IV) was investigated is because it is a toxic heavy metal, as a result, there is a need for its removal in wastewater. Scheme 1 illustrates the various steps for fabrication of the ZnO/CuO nanocomposite into the polyester [59]. The SEM images of the ZnO/CuO/polyester nanocomposite revealed that the polyester fabric was covered with flake-nanostructures. The reason for such a dense covering of the nanoparticles into the polyester fabric was associated with the alkaline treatment of the fabric, which produced roughness on the surface. It is generally known that in most cases, a rough surface is able to produce reaction sites for the ease of penetration by other materials, in this case, the nanoparticles. As a reference point, the concentration of Cr(VI) was measured by UV-Vis spectroscopy and recorded to be 200 ppm. The inserted test tubes in Figure 12 shows the wastewater before treatment (yellow test tube) and after treatment (clear test tube). The yellow color in the other container indicated the presence of Cr(VI), while the clear color indicated that the solar photocatalytic reduction reduced the concentration Cr(VI) in wastewater. According to Figure 12, it became evident that the continuous exposure of pure wastewater to irradiation reduced the concentration of Cr(VI) in water. For example, at 0 h, the concentration was approximately 200 ppm, while after 6 h, the concentration was found to be 24 ppm.
A ternary system composed of ZnO/ reduced graphene oxide (rGO)/PANI was prepared to evaluate the synergy among the components on the photocatalytic performance of nanocomposites toward methyl orange (MO) under UV-light irradiation [61]. The ternary composite composed of ZnO/rGO/PANI was prepared via the in situ chemical oxidative polymerization of aniline. It was found that rGO was decorated with ZnO particles and both were wrapped with PANI sheets. The increase in PANI in the system decreased the photocatalytic efficiency of the composites. The maximum MO photodegradation efficiency of~99% under UV-light was attained within an hour. Such an improvements resulted from PANI providing dye adsorption sites, allowing light penetration, and increasing the separation efficacy of the photogenerated electron-hole pairs. However, the excessive PANI content formed a thick layer aggregating on the surface of ZnO, thus blocking the light and migration of excited electrons from the PANI layer to the encapsulated ZnO particles. The composites maintained high photodegradation efficiency even after three cycles, indicating its reusability and stability. A ternary system composed of ZnO/ reduced graphene oxide (rGO)/PANI was prepared to evaluate the synergy among the components on the photocatalytic performance Since the recovery of the photocatalyst is one essential factor from the ecological and economic viewpoints, the decoration of ZnO with magnetic particles for their recovery using an external magnet was demonstrated by Zhang et al. [62]. The authors prepared PANI-Fe 3 O 4 @ZnO core-shell microsphere photocatalysts using Pickering emulsion one-step synthesis. Spherical microspheres with diameters of~1.5 µm displayed high magnetization to afford their separation using an external magnet. With a BET surface area of~11.2 m 2 /g, the as-prepared microspheres showed high photocatalytic activity. The highest MB photocatalytic degradation efficiency of~91% was achieved within 40 min under visible light irradiation. A recent study by Neda et al. [63] demonstrated that the Fe 3 O 4 /ZnO/PANI core-shell structure can be prepared by encapsulating Fe 3 O 4 with ZnO followed by the in situ polymerization of PANI as a host matrix. In this case, Fe 3 O 4 nanoparticles were synthesized separately and then dropped into a zinc acetate dehydrate solution to afford the synthesis of ZnO as a shell. Subsequently, PANI synthesis using aniline was carried out in the presence of the as-prepared core-shell nanoparticles. Spherical particles with diameters ranging in between 35 and 50 nm with a magnetization of~20 emu/g were obtained. It was noticed that Congo red (CR) decomposition reached 81% within 15 min under visible light at the photocatalyst dosage of 2.0 g/L and initial dye concentration of 60 g/L. The maximum photodegradation pH value was~3 with 86% CR decomposition after 15 min. The decomposition of (CR) increased with an increase in temperature and the composites showed 7.3% reduction after five repeated cycles, whereas Fe 3 O 4 /ZnO had 14.8%. The Ag/ZnO/PMMA nanocomposite was fabricated for the degradation of organic pollutants such as methylene blue, sodium lauryl sulfate, and paracetamol [64]. The addition of Ag into the ZnO/PMMA nanocomposites facilitated a 30% enhancement in the photocatalytic capacity of MB when compared with PMMA/ZnO. According to the authors, this behavior was associated with a delayed recombination time of the charge carriers by the metal. The Ag/ZnO/PMMA nanocomposites was also reported to have 65% improvement in the photocatalytic degradation of paracetamol when compared with the ZnO/PMMA nanocomposite. There was more than 90% in the degradation of SDS in the presence of the Ag/ZnO/PMMA nanocomposite. The presence of Ag enhanced the photocatalytic activity of the ZnO/PMMA nanocomposites due to the ability of the Ag to act as an electron sink, decreasing the possibility of the electron-hole recombination and promoting an effective charge separation.

Conclusions and Future Recommendations
The limitations in the availability of fresh water and continuous water pollution have prompted researchers to invest more time in various methods for the treatment of water. The source of polluted water is attributed to the pollutants (i.e., oils, organic solvents, dyes, etc.) produced by industries due to their evolution. The photocatalytic activity was found to be very efficient in terms of the removal of pollutants. ZnO has been identified as one of the most effective photocatalysts in the process of photocatalytic degradation due to its wide bandgap (viz. 3.37 eV), low cost, and thermal stability. Factors such as the dispersion of ZnO within the polymer matrix, type of ZnO (i.e., nanorods, spheres, and nanowires), synergy with other nanoparticles, pH, and preparation method were reported to have an effect on the photocatalytic activity of the ZnO/polymer composites. The use of preparation methods that can result in more photocatalytic fillers being exposed is of essence to reduce the time required while maintaining a high degradation efficiency. On the other hand, experimental conditions such as pH, concentration of the pollutant, and photocatalyst dosage are important to achieve the desired photocatalytic results. In general, the use of conventional non-conductive polymers as host materials can negatively affect the photocatalytic behavior of ZnO particles. With most of these systems resulting in a degradation efficacy of less than 70%, this is a major concern from an economic viewpoint. In addition, this type of composite takes longer to achieve the desired degradation efficiency. The use of conductive polymers could even further improve the photocatalytic efficiency of the resultant composites [49]. These polymers are known to act as a sensitizer to promote the spectrum response of inorganic semiconductors within the visible light region. Up to now, conductive polymers can be regarded as the best polymer systems when incorporated with a photocatalyst, since higher photocatalytic activity has been reported in such systems and photocatalytic efficiency has been reported to be as high as 99%. The synergy of ZnO with other photocatalysts such as Ag and TiO 2 were found to be effective in terms of photocatalytic degradation, with an efficiency as high as 89% in some cases due to the presence of more reactive sites in the synergy of nanoparticles. For future purposes, it would be very interesting if more work is conducted on the polymer blends as host matrices for ZnO in the process of photocatalytic degradation, as this may widen the applications of ZnO. It would be interesting to report on the molecular weight and resultant properties of the polymer blends/ZnO nanocomposites after being exposed to UV irradiation. Another suggestion for future purposes would be the utilization of ZnO with more than two photocatalysts, since it has been observed that the utilization of ZnO with another nanoparticle enhances the photocatalytic degradation more.