Biodegradable Composites with Functional Properties Containing Biopolymers

: There is a major focus on natural biopolymers of bacterial, animal, or plant origin as ecological materials, replacing petrochemical products. Biologically derived polylactide (PLA), polyhydroxybutyrate (PHB), and polyhydroxyalkanoates (PHA) possess interesting properties, but they are currently too expensive for most applications. Therefore, researchers try to ﬁnd other biopolymers that are both durable and cheap enough to replace plastics in some applications. One possible candidate is gelatin, which can be transformed into a thin, translucent ﬁlm that is ﬂexible and has stable and high mechanical properties. Here, we present a method of synthesizing a composite material from gelatin. For preparation of such material, we used gelatin of animal origin (pig skin) with the addition of casein, food gelatin, glycerin, and enzymes as biocatalysts of chemical modiﬁcation and further extraction of gelatin from collagen. Compositions forming ﬁlms with homogeneous shapes and good mechanical properties were selected (Tensile strength reaches 3.11 MPa, while the highest value of elongation at break is 97.96%). After administering the samples to microbial scaring, the composites completely decomposed under the action of microorganisms within 30 days, which proves their biodegradation.


Introduction
Polymeric materials, from the earliest years, were widely used in medicine and other areas of industry. Over three thousand different types of medical devices are manufactured from polymers [1]. However, synthetic polymers are often the source of harmful pollutants due to their poor dispersion and excessive exposure to the natural environment [2]. Most modern synthetic polymers are made of petrochemical products and are not biodegradable [3][4][5]. For example, plastic bags have a negative impact on marine and ocean life [6,7]. Accumulation in the environment of toxic products resulting from the decomposition of such polymeric materials may inhibit plant growth and have a negative impact on ecosystems [8]. Unfortunately, the recycling of plastics has an adverse environmental balance in terms of the energy and resources needed to wash, grind and process the waste [9]. Incineration of plastic waste causes the emission of toxic compounds (e.g., dioxins) to the atmosphere and also entails certain limitations in the availability of effective and economically profitable facilities or devices for burning this type of materials [10]. As a consequence, it leads to the determination of the environmental toxicity of pollutants, known as their ecotoxicity [11][12][13][14][15][16]. Natural polymers due to their excellent biocompatibility and biocompatibility have been used in medicine for many years [17][18][19][20][21][22]. Biodegradable polymers have a great potential in many applications including tissue engineering, gene therapy, and regeneration. They can be used in temporary devices for implantology and implant coatings [23]. Due to their biocompatibility, biopolymeric hydrogels are also used in application materials (bandages, etc.), as well as for tissue and organ engineering and regeneration (hydrogels, alginates, etc.) [24]. A particularly important achievement in biopolymer technology was the use of biopolymers, both fiber-forming and natural polysaccharide polymers, to create materials for the controlled release of drugs. Natural polymers that are biodegradable inside the body (biohydrolysis) are used to create a temporary therapeutic matrix containing biologically active substances that can be released in a controlled manner [25]. These types of materials, after fulfilling their functions, biodegrade and are naturally removed from the body. Biopolymers have healing properties (biocidal, antioxidant, antiallergic, etc.), which is a great advantage over synthetic materials. Biopolymers are not only biodegradable but non-toxic. It is an important property in all applications, especially in medicine [26,27]. Unfortunately, biosourced polymers also have undesirable antigenic properties and are heterogeneous. Natural polymers can be classified based on the method of their synthesis. Examples of polymers derived from biomass include: agropolymers from agricultural raw materials (e.g., starch or cellulose); polymers obtained by the production of microorganisms (polyhydroxybutyrate); conventionally and chemically synthesized polymers from monomers obtained from agricultural raw materials (polylactic acid); and polymers derived from fossil fuels. Only the first three of these categories are considered sustainable [28]. Depending on the application, the required properties and the degradation rate are the basic criteria for selecting a polymer to be used as a biodegradable biomaterial. Plastics are highly resistant to temperature, environmental pH, mechanical deformation, etc. For the polymer material to meet the compostable or biodegradable criteria, and on the other hand to be adequately durable and thermally stable, it should be chemically or physically modified at some stage of its production. One of such solutions was proposed by X. Zhang et al. [29]. Gelatin was modified with a natural phenolic compound from the tannin group. The use of a tannin compound in the amount of 3% resulted in obtaining a stable structural network even during the thermal treatment process of the polymeric material at 100 • C. The increase in the degree of branching as a result of the grafting of the ingredients used resulted in an increase in the molecular mobility of the gelatin matrix, which consequently made it possible to obtain a protein material with plastic properties. In scientific research, [30,31] gelatin obtained from pig skin was also undergoing esterification with fatty acid. The chemical modification process was catalyzed by a fatty acid in an aqueous medium. In order to optimize the process, the type and concentration of the higher fatty acids used as well as the reaction time were appropriately selected. Based on the determination of the increase in acid concentration under the same conditions of time, the maximum amount of acid that is needed to esterify a given unit of gelatin mass was determined, and on this basis, it turned out that the process of blocking all gelatin hydroxyl groups with the fatty acid used was difficult, which in turn affects the cross-linking processes in gelatin matrices. Other compounds used in gelatin cross-linking are, for example, plant-derived phenolic compounds such as caffeic acid [32,33]. Optimization of the time and concentration of the applied acid to the gelatin system resulted in obtaining a different degree of cross-linking of the polymeric material. A lower degree of deformation at higher temperatures was achieved for gelatin cross-linked in this way as shown by rheological analysis.
In this article, we present the method of producing polymer films based on a gelatin matrix with the use of waste skin tissue of animal origin ("WĘDLINKA Sp. z o.o." Wieruszów, Poland). The films were enriched with casein, chitosan, agar, cellulose acetate, and glycerin plasticizer to obtain durable film-like coatings with a uniform shape and good mechanical parameters. In the designed chemical preparation, a specific type of catalyst was proposeda proteolytic enzyme (Novo Unhairing Enzyme NUE 12 MP Activity 8.37 KNPU (E)/g [33] 130,000 LVU g −1 [34,35] and acetic acid. The purpose of the biocatalyst introduced into the mixture with fragments of fractionated collagen tissues was to accelerate the catalytic partial disintegration reaction and obtain a homogeneous mixture. On the other hand, the introduction of the organic acid was aimed at loosening the fibrillar structure of collagen fibers without leading to complete conformational denaturation of the roll helix. In this way, we have obtained a composite with the desired performance parameters, thermally stable, with limited water absorption. This type of material could be used in tissue engineering. Potential application of this film is the base for growth factor sequestration, biomimetic composites, scaffolds for bone tissue or basis for bone substitute [36][37][38].  Table 1 shows the results of Shore (00) hardness tests' performer for each composition. The same results are summarized in Figure 1. From the graph, it can be seen that the HO composite has the highest hardness. The reason for this difference between the compositions is the network that formed in the material. As observed in previous research, HO was the most stable of the tested composites in terms of networks out of all the tested compositions [30]. The stability of its polymer network may be the result of synthesis at acidic pH with acetic acid, which does not break collagen bonds to the same extent as the sodium base. Therefore, the remaining compositions were mechanically weaker. The increase in hardness and density occurred as a result of the stronger or denser connection of the matrix with the additives and the strengthening due to the increased holding time and temperature [26]. The increase in the gelatin concentration resulted in biopolymer films with greater density and stability, as was reflected in the FTIR analysis.

Breaking Strength
A strength device (Zwick 1435, Zwick/Roell, Radeberg, Germany) was used to determine the static mechanical properties of the composites. The results are shown in Table 2 together with the standard deviations. The composite synthesized with the addition of acetic acid at a concentration of 0.5 M (H0) showed the highest mechanical strength (Figure 2). This. This value was four times higher than the that for the HA composite and six-times higher than the value for the HB composite. The mechanical properties depended on the structure of the polymer. The large increase in mechanical strength may be related to intramolecular interactions in the H0 sample-for example, the formation of hydrogen bonds due to the action of hydrogen derived from acid, as was observed by infrared analysis (Figure 3).  The HA composite showed the highest tensile strength. This may have been due to the much greater length of the macromolecule chains in the main chain ( Figure 4c).

Spectroscopic Analysis
The spectra show a large proportion of -OH/NH (3270 cm −1 ), -CH (2850-2920 cm −1 ), [39], and COO-(1680 cm −1 ) groups ( Figure 3). Aromatic bonds derived from casein are also visible (920 cm −1 ), as are primary and secondary proteins (1240-1530 cm −1 ) [39]. The shift of the amide bands towards their lower intensity may mean a reduction in the energy of the amine bonds and also indicates the enhancement of the interactions between gelatin and other components [40].
The main difference in the spectra of the obtained composites is the appearance or disappearance of peaks in the 800-950 cm −1 range. In the case of composite H0, a peak appears at the wave number of 875 cm −1 . A similar peak was observed in the spectra of the HA composite, but not for the HB samples. This peak corresponds to the long [40] chain -C 3 H 6 .
The H0 composite has a peak corresponding to HCO bonds (943 cm −1 ) [39]. The HB samples are distinguished by the appearance of a large amount of CH 2 -CH 2 -(849 cm −1 ). This bond may have arisen as a result of the main chain branches breaking during the operation of the base.
Possible schemes of the reaction mechanisms are presented in Section 2.1.4.

Microscopic Research (SEM and TEM) and Reaction Mechanisms
Pictures taken with a scanning electron microscope (SEM) showed the structures of the composites (Figure 4b,d,f). Figure 4b shows minor imperfections in the structure of the HO composite, which may be the result of undissolved casein agglomerates. The structure of the HA composite ( Figure 4d) shows large imperfections, in the form of air bubbles and undissolved substrates. The structure of the HB composite ( Figure 4f) shows small imperfections, which are more numerous than those seen in the picture of the HO composite ( Figure 4b).All three composites were translucent. However, most likely due to their non-cross-linked substrates, due to the pH of the solutions during their synthesis, HA and HB were less transparent than the HO composite. Figure 4a,c, and e show the predicted structures and mechanisms of the interactions between the individual components of each composite. The H0 composite shown in Figure 4b (SEM) together with the proposed fragment of the structure shown in Figure 4a, was the best in terms of mechanical properties. FTIR spectroscopy showed that there were long C 8 H 17 O 9 bonds in the backbone lattice. Therefore, the H0 composite had a better produced polymer network in terms of mechanical parameters. Moreover, with the help of glycerin, carboxylic bonds formed in gelatin between the casein and gelatin, and an ether bond formed in the casein. The HA composite shown in Figure 4d with the structure in Figure 4c was weaker in terms of mechanical properties, but more flexible. This composite also interacted with glycerin. However, it did not have an additional chain like the H0 composite, most likely due to the unstable lattice, which would explain its behavior. The HB composite shown in Figure 4f with the structure in Figure 4e was the weakest of the composites. This was probably due to the reorganization of the chains derived from gelatin during chemical modifications, as well as changes in the structure of the hydrocarbon chains of the -CH 2 groups. Because of the lack of branches that would allow the polymer to flow, the composite stiffened and its properties deteriorated [41][42][43].
Analysis with Transmission Electron Microscope was carried out to determine the chemical composition of the obtained materials. Figure 5 shows graphs of different elements content in a samples H0, HA, and HB (Figure 5a-c). All three matrices are similar in chemical composition where majority of atoms consist of carbon (65-73%) and oxygen (19-32%). It is only logical that these atoms have definite majority than others hence the presence of aromatic groups from casein or aliphatic chains in gelatin. The presence of other atoms: chlorine (0.2-4%), sodium (0.2-1%), potassium (0.05-0.11%), nitrogen (0-6%), phosphorus (0.02-0.06%), sulfur (0.06-0.11%), and calcium (0-0.11%) depends on the kind of skin used in the synthesis, level of preparation of said skin, source, the diet of the animal it came from, etc. [44][45][46].

DSC and TGA Analysis
The results of differential scanning calorimetry (DSC) show that the sample of HA synthesized with the addition of NaOH had the highest value for glass transition, while the lowest value was for the sample synthesized with acetic acid H (Table 3; Figure 6). The difference may be due to the lower dissolution of casein, which is a natural flame retardant. This conclusion is supported by the results for the specific enthalpy of fusion, which was the lowest for the HA synthesized with the addition of NaOH, indicating a worse distribution of the additive in the sample. The specific enthalpy of melting was the highest for sample H0, which proves that the components were well mixed. These results are supported by the SEM photos in Figure 4. Different Tg values determined by different authors for biopolymers such as gelatin, starch, etc. [47,48] result not only from different processing conditions of the samples before the analysis, i.e., different water content [49], but also from different content of amino acids: hydroxyproline, proline, etc. resulting from the different histological origins of the protein source.    Table 4 summarizes the results of analysis of the contact angles of the H0, HA, and HB composites, proving their hydrophilicity. The reason for their hydrophilicity is the water contained in their network and the -OH groups, which are visible in the FTIR analysis. The angles of the non-polar liquid are in the result group < 90 • , which means that the composite atoms on the surface also attract atoms from non-polar liquids, although less so than in the case of a polar liquid. Table 4. Contact angles of the tested films for water, diiodomethane, and ethylene glycol. Surface free energy (SFE) describes the surface tension of a solid, which arises as a result of molecular interactions between the body and air. The HB composite was characterized by the highest SFE (Table 5; Figure 7). This higher value is probably indicative of it having good wettability with any liquid.

Measurement of Equilibrium Swelling
Equilibrium swelling (Q w ) and the degree of cross-linking (α c ) were determined to investigate the water barrier for the absorption of the composites (Table 6). The highest degree of cross-linking was noted for the H0 composite. A durable network was produced during the synthesis of H0, due to the acidic pH and also by the use of an organic acid. The degradation of the collagen was also not as drastic as in the case of the base. From the FTIR spectra, it appears that the acidic pH enables the extension and/or modification of the main chain, which is later noticeable in the mechanical results. However, due to their similar processes of synthesis, there is only a small difference between the degree of cross-linking in the HA and HB composites.

Determining the Susceptibility of the Composites to Biodegradation
To determine the biodegradability of the composites, spatula-shaped samples were placed in containers and covered with a layer of universal primer (pH 6.0-7.0). Measurements were made in accordance with the PN-EN ISO 846 standard. The containers were placed in a climatic chamber with a temperature of 30 • C and a humidity of WWP 80%. The measurement period was 30 days. After 30 days, the samples had completely decomposed. We concluded that the composites were characterized as well biodegradable. 90% of the material degraded, under conditions determined by the standard, throughout 7 days which is true for those type of materials in comparison with literature. [50] Thermo-oxidative aging was carried out in accordance with the PN-821C-04216 standard. Paddle-shaped samples were placed in a circulating air dryer for seven days at 70 • C.
Atmospheric aging samples were left exposed to air and sunlight in the laboratory at 22-25 • C with varying humidity for 180 days. They were then subjected to further tests, to compare the changes occurring in the material under room conditions. Due to the low mechanical strength and brittleness of the HA and HB compositions after thermo-oxidative aging, we decided to focus our further investigations on the best H0 material.

FTIR after Aging
Fourier transform (FTIR) infrared spectroscopy was performed on the H0 samples after thermo-oxidative and atmospheric aging, as shown in Figure 8. In the H0_Atm samples after atmospheric aging, compared to other samples a peak appeared corresponding to the wavenumber of 1030 cm −1 , which includes C-OH bonds. The peak at 1165 cm −1 disappeared [32,33,47], which indicates a lower effect of -CH 2 -CH 2bonds. These results may indicate that the double bonds in the chain (e.g., in the gelatin chain) were broken during atmospheric aging and that the OH groups were combined in these places, as a result of the action of water in the air.
In the samples after thermo-oxidative aging, the peak disappearance was observed at the wave number of 1328 cm −1 , corresponding to the OH deformation vibration bands. This was probably due to the fact that crystalline and bound water evaporates as a result of the temperature during aging.
After degradation, the structure of the composite did not show any major changes, proving its stability.

Influence of Aging on the Mechanical Properties of Samples
After thermo-oxidative and atmospheric aging, the composites were tested for their mechanical properties. Hardness was tested using the Shore method. The breaking strength (Ts) and the elongation at break (E b ) were tested on a Zwick Roell device. The results are presented in Table 7.
Changes were noted in the mechanical properties of the samples before and after aging. The unaged H0 specimen had the highest values for hardness and tensile strength, but the lowest elongation at break compared to aged H0_TO and H0_Atm. The reason for such changes under the influence of aging is the fact that the bonds in the material structure change, as evidenced by the FTIR spectrum. The disappearance of double bonds and the appearance of -OH groups causes the composite to plasticize and increase its flexibility, but deteriorates its mechanical properties.

TGA and DSC Analysis after Degradation Processes
To analyze the degradation of the H0 samples subjected to thermo-oxidative and atmospheric degradation, we conducted TGA analyses ( Figure 9a) and DSC analysis (Figure 9b,c and Table 8).    Figure 9a shows the results of TGA analysis of the H0 samples before and after aging. As can be seen from the thermogram, the initial weight loss occurs at 136 • C. This is when the volatile substances present in the composites are formed. The second weight loss occurs at 608 • C. At this point, the composite releases medium-volatility compounds. Figure 9b,c shows the DSC H0 curves before and after aging. Atmospheric aging of the material shows an endothermic peak shifted to higher temperatures as a function of time. This was probably related to the enthalpy relaxation of the amorphous area.
As can be seen from the DSC results, the H0 composite shows different glass transition temperatures depending on the aging method. The sample after atmospheric aging showed the highest glass transition temperature. This may be related to the formation of -OH groups (Figure 9), which resulted in morphological changes such as secondary crystallization in the amorphous area of the material.

Determination of Color Changes after Aging Processes
The color changes in the composites before and after thermo-oxidative and atmospheric aging were tested in accordance with the PN-EN ISO 105-J01 standard, using a CIE Lab spectrophotometer. The results are given in Table 9 and presented for comparison in Figure 10. Composite H0 showed the strongest color change, which was visible with the naked eye. The color changes of the remaining composites were hardly noticeable or invisible to the human eye. The probable reason for the large color change of the H0 composite may be its stronger and more stable polymer network, which is degraded by the action of temperature and humidity, affecting the color of the composite.

Research Facilities
Frozen pig skin was obtained from "WĘDLINKA Sp. z o.o." (Wieruszów, Poland). The skin was cleaned under water, then the fat from the inner skin was scraped off. A skin 0.3-0.5 cm thick was obtained, then the skin was cut into 1 cm × 1 cm strips.

Preparation of the Composites
Components of the composites and the technical parameters of their preparation (i.e., temperature, time, and ratios) were selected to obtain the desired chemical modifications. The best compositions are presented in Table 10. The solutions were prepared by mixing the raw materials in appropriate proportions by weight. The previously washed, peeled off, and cut skin (about 10 g) was immersed in the enzyme solution (NUE 12 MG 33 g was dissolved in 7.5 mL of water). In the case of the HA and HB samples, 0.5 M sodium hydroxide solution at pH 6-8 was also introduced into this solution. For the H0 composite, only the enzyme solution was introduced. The solutions with the skin were left at room temperature for 24 h. The difference between samples HA and HB is that HB enzyme and sodium hydroxide solution (pH 7) with skin (solution A) was prepared alongside with enzyme and sodium hydroxide solution (pH 6) with food gelatin, casein, and glycerin (solution B) and both solutions were left for 24 h.
The enzyme solution was then transferred to a reaction flask equipped with a reflux condenser, a thermometer, and magnetic stirrers. After the preparation of the synthesis setup, designated additives were added accordingly: • H0: 0.5M acetic acid, glycerin, casein, and food gelatin • HA: 0.5M sodium hydroxide (pH 7), glycerin, casein, and food gelatin • HB: Solution A was transferred to the reaction flask and to it solution B was added and mixed The synthesis was carried out at the temperature of 75 • C for 4 h, while stirring with a magnetic stirrer (Figure 11). An exemplary reaction set is shown in Figure 11. The products were thermostabilized (thermal chamber with air circulation Binder GmbH, Germany) for 24 h at 80 • C. The samples were formed on a hydraulic press into shapes corresponding to the measuring device (Skamet 54436, SKAMET, Skarżysko-Kamienna, Poland) at a temperature of 105 • C and a pressure of 120 bar (Figure 12). The samples obtained are 5 × 5 cm in size and have a thickness of 1.50-1.60 mm Sample H0 (Figure 12a) formed a hard, brittle, translucent material. Sample HA (Figure 12b) formed a hard, translucent, but more flexible material compared to the H0 sample. The HB sample (Figure 12c) formed a hard and brittle material similar to the H0 sample.
The prepared biocomposites were subjected to mechanical analysis both before and after the thermo-oxidative aging processes. Measurements were made in accordance with PN ISO 37: 1998 (D1235 ASTM). The paddle-shaped specimens were stretched to determine the tensile strength (T Sb , MPa) and the relative elongation at break (Eb, %). The hardness of the samples was measured (ISO 7619-1 standard) with a Shore 00 digital hardness tester on the 00 scale.
FTIR spectroscopy was used to identify vibrations characteristic for functional groups on the basis of changes that occurred in the tested biopolymers compared to the reference sample. Measurements were carried out in the radiation wavelength range of 4000-500 cm −1 with a resolution of 0.25 cm −1 .
To determine the surface energy value for synthesized samples using the Owens, Wendt, Rabel, and Kaelble method. Measurements of the contact angle for composites were made with two liquids: polar (distilled water) and non-polar (diiodomethane). The deposition mechanism of the surface layer indicates the morphology of the layer itself and its electrical properties. The surface free energy was calculated using Equation (1), based on the surface energies of a polar and non-polar substance [51,52]: Using the equation, the relationship (2) was derived, the polar component γ p S was determined, which corresponds to the sum of the forces of: hydrogen, acid-base and inductive interactions, and the dispersion component γ p S is determined by the London forces: Calculation of structural parameters of three-dimensional networks based on the results of equilibrium swelling measurements is based on the theoretical work of Florry and Rener [53]. When the polymeric three-dimensional network swells, the solvent penetrates into the macromolecule and the free energy changes as a result of mixing the polymer and solvent molecules. Dissolving the polymer chain is difficult through the chemical bonds that bind macromolecules together. The Thermogravimetric analysis (TG) and differential scanning calorimetry (DSC) are methods of thermal analysis. TGA analysis-the change in sample weight as a function of temperature is recorded. This method of analysis is based on the observation of the mass of the test substance sample with changes in temperature. The results of the analysis are TG curves describing the dependence of the sample mass (or change in sample mass) on temperature or time [54].
The difference in the amount of heat required to raise the temperature of the sample and standard, measured as a function of temperature, was determined by Differential Scanning Calorimetry (DSC) [55]. DSC is used to measure heat power, allows for estimation of glass transition temperature (Tg) and determination of capacitance changes heat capacity (∆Cp). The change in heat capacity at glass transition ∆Cp can be defined as the amount of heat necessary to change the body temperature by the temperature unit per 1 g of the sample, expressed in [J/g·K].
Thermo-oxidative aging was carried out in accordance with the PN-821C-04216 standard. Samples cut into the shape of a paddle were dried in a Binder dryer with circulating air for seven days at 70 • C. Biodegradation of the samples was carried out in accordance with the PN-EN ISO 846 standard. Paddle-shaped samples were cut from the composites, placed in containers with soil, then put into a Memmert climate chamber (Memmert GmbH, Schwabach, Germany) for 14 days at 30 • C with air humidity of 80%. All three compositions of HO, HA, and HB were dissolved in soil after the study. Therefore, they were not subjected to further tests. Using the PN-EN ISO 105-J01 standard, the samples were tested for color changes on a UV-VIS CIE Lab color space spectrophotometer.

Conclusions
This work has presented the results of research on biopolymer composites based on animal-derived gelatin with the addition of casein, food gelatin, glycerin, cellulose acetate, chitosan, and agarose. The additives were selected for their cross-linking properties. Glycerin was added to assist with the production of a film. Food gelatin was also added to improve the mechanical properties of the material. Composite H0 was obtained by extracting gelatin from pig skin by an enzymatic reaction in acetic acid solution. It was the hardest of the tested composites. H0 also showed the best mechanical strength. These results indicate that H0 was a homogeneous material, in terms of additive dispersion. Infrared analysis showed a large proportion of the -OH (2800-3500 cm −1 ), NH 2 (3500-3300 cm −1 ), and CH 2 (3095-3050 cm −1 ) groups, as well as many of the aromatic bonds (3075-3030 cm −1 ), were derived from casein. Primary and secondary proteins (1550-1650 cm −1 ), as well as tertiary proteins (approximately 1100 cm −1 ), were also visible, as they were in the other composites (HA and HB). However, the share of the -OH group in the H0 composite was smaller than that in the HA and HB composites.
SEM pictures showed that the H0 sample had some imperfections, due to the casein being not fully dissolved in the solution. On the basis of infrared analysis, we concluded that H0 had the least branched and cross-linked structure of long polymer chains, and therefore it may be characterized as the least stable spatial network.
TGA and DSC analysis showed that all three compositions had a similar glass transition temperature. However, the H0 composite had twice the heat capacity. A contact angle test revealed that all three compositions were wettable by both polar and non-polar liquids. This means that they were also hydrophilic, which may limit their use in the packaging industry.
The HB composite had the highest free surface energy, and H0 the lowest. Equilibrium swelling showed that the H0 composite had the highest degree of cross-linking. Its strong network was created during the process of synthesis, thanks to the acidic environment. It was also influenced by the use of a weak organic acid, which did not completely degrade the helical collagen fibers, but led to loosening of the structure of polypeptide chains. This ensured their appropriate strength. In contrast, the H0 composite had the highest degree of cross-linking, due to the alkaline environment in which it was synthesized.
Due to their poor mechanical properties after aging, HA and HB were excluded from further testing. The reason for their advanced degree of degradation may be the use of a strong base, which broke the peptide bonds in the collagen and gelatin helices, hindering the formation of a stable polymer network.
The results of infrared spectroscopy showed slight changes in the absorption bands of the H0 composite, which means that it had a stable polymer network. There were, however, changes in the -OH bonds. Atmospheric aging indicated an increase in the presence of hydroxyl groups, associated with the absorption of water from the air. On the other hand, after thermo-oxidative aging the -OH groups disappeared, which means that most of the crystalline and structurally bound water evaporated under the influence of temperature.
In terms of mechanical properties, the aged H0 composite specimens had a higher percentage of elongation at break. The disappearance of -CH 2 groups caused the composite to plasticize and increased its flexibility, at the expense of reducing its mechanical properties.
Thermogravimetric analysis (TGA) showed the presence of volatile and semi-volatile substances in the H0 composite, which were released during degradation at high temperatures. The results of DSC measurements showed a change in the glass transition temperature under the influence of atmospheric aging. Secondary crystallization in the amorphous space of the material may have occurred, due to the absorption of moisture from the air, leading to a decrease in the homogeneity of the material.
Color changes were measured for all three compositions. Compared to HA and HB, the H0 composite was characterized by a large change in color after both atmospheric and thermo-oxidative aging. This was due to the degradation of the more stable polymer network in the composite compared to the other samples, in which the main polymer chains were shorter.
These composites do not stray from the materials used in tissue engineering research. We suspect its potentiality in nanostructural growth as well as base for new biomimetic cement as bone replacement as well as biodegradable implantations for better biocompatibility [38,44,45].