Catalytic Evaluation of Nanoﬂower Structured Manganese Oxide Electrocatalyst for Oxygen Reduction in Alkaline Media

: An electrochemical nanoﬂowers manganese oxide (MnO 2 ) catalyst has gained much interest due to its high stability and high speciﬁc surface area. However, there are a lack of insightful studies of electrocatalyst performance in nanoﬂower MnO 2 . This study assesses the electrocatalytic performances of nanoﬂower structure MnO 2 for both oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) in a zinc–air battery as a bifunctional electrocatalyst. The prepared catalyst was characterized in term of morphology, crystallinity, and total surface area. Cyclic voltammetry and linear sweep voltammetry were used to evaluate the electrochemical behaviors of the as-prepared nanoﬂower-like MnO 2 . The discharge performance test for zinc–air battery with a MnO 2 catalyst was also conducted. The results show that the MnO 2 prepared at dwell times of 2, 4 and 6 h were nanoﬂowers, nanoﬂower mixed with nanowires, and nanowires with corresponding speciﬁc surface areas of 52.4, 34.9 and 32.4 g / cm 2 , respectively. The nanoﬂower-like MnO 2 catalyst exhibits a better electrocatalytic performance towards both ORR and OER compared to the nanowires. The number of electrons transferred for the MnO 2 with nanoﬂower, nanoﬂower mixed with nanowires, and nanowire structures is 3.68, 3.31 and 3.00, respectively. The as-prepared MnO 2 nanoﬂower-like structure exhibits the best discharge performance of 31% higher than the nanowires and reaches up to 30% of the theoretical discharge capacity of the zinc–air battery. The results indicate that the nanoﬂower structure exhibits a higher surface area compared to nanowires. experimentally must be between two and four to show that the electrocatalyst promotes some of the ORR pathways to occur in the four-electron pathway. The results show that MnO 2 nanoﬂower has the best electrocatalyst performance towards the ORR, as the number of transferred electrons is close to four, suggesting the likelihood of promoting the ORR reaction toward the four-electron pathway. Meanwhile, the electrocatalytic performance for carbon Vulcan XC 72 mixed with major nanoﬂower and minor nanowires and carbon Vulcan XC 72 mixed with major nanowires and minor nanoﬂower are also within the acceptable range of two to four.


Introduction
Renewable energy sources have broadly attracted attention to supply global energy demand due to the excess utilization of petroleum-based fuels [1,2]. Nevertheless, the efficient utilization of renewable energy sources requires safe and cost-effective electricity storage systems. Zinc-air batteries are considered as the most promising alternative energy storage due to several advantages such as high theoretical specific energy density with a flat constant discharge voltage, the low reactivity of zinc, environmental safety and quick refueling with fresh zinc powder and granules. Moreover, the use of Figure 1 shows the SEM images for the synthesized MnO 2 catalysts with different dwell times. It shows that the rod-like MnO 2 structure was formed at a longer dwell time. This phenomenon can be explained by the Ostwald Ripening process during formation of the catalyst [23]. The nanoflower structure was produced in a dwell time of 2 h, nanoflower mixed with nanowires was produced in a dwell time of 4 h, and nanowires were produced in a dwell time of 6 h. The obtained nanoflower structure of the MnO 2 particles exhibits irregular shape with sizes ranging from 1 to 3 µm and all clumping together. Meanwhile, the nanowire morphology developed from one into a few microns' length, about 50 nm in diameter. Figure 2 displays N 2 adsorption/desorption isotherms of all the catalysts, showing (from the slopes of the linear region of the curves) that the nanoflower MnO 2 has a higher specific surface area (52.4 cm 2 /g) followed by nanoflower mixed with nanowires (34.9 cm 2 /g) and nanowires (32.4 cm 2 /g).
The results indicate that the nanoflower structure exhibits a higher surface area compared to nanowires. Therefore, more abundant nanoflower structures are present on the surface of the catalyst. This general Catalysts 2020, 10, 822 3 of 14 statement suggests that the higher surface is mainly responsible for higher catalytic performance for all types of catalysts, regardless of the type of metals and support [34]. The surface area varies from material to material and depends on preparation methods. In this study, a higher surface area was observed in nanoflower MnO 2 , which is a significant factor for high catalytic performance.  showing (from the slopes of the linear region of the curves) that the nanoflower MnO2 has a higher specific surface area (52.4 cm 2 /g) followed by nanoflower mixed with nanowires (34.9 cm 2 /g) and nanowires (32.4 cm 2 /g). The results indicate that the nanoflower structure exhibits a higher surface area compared to nanowires. Therefore, more abundant nanoflower structures are present on the surface of the catalyst. This general statement suggests that the higher surface is mainly responsible for higher catalytic performance for all types of catalysts, regardless of the type of metals and support [34]. The surface area varies from material to material and depends on preparation methods. In this study, a higher surface area was observed in nanoflower MnO2, which is a significant factor for high catalytic performance.

Electrochemical Properties of the As-Prepared Catalysts
ORR is a complex and multi-electron reaction. The ORR can proceed via two different reaction pathways, namely, a direct four-electron pathway, as shown in Equation (1), or a two-electron pathway, as exhibited in Equations (2) and (3)

Electrochemical Properties of the As-Prepared Catalysts
ORR is a complex and multi-electron reaction. The ORR can proceed via two different reaction pathways, namely, a direct four-electron pathway, as shown in Equation (1), or a two-electron pathway, as exhibited in Equations (2) and (3) [35]. Figure 3 shows all the samples have a small but observable peak around −0.4 to −0.5 V vs. Ag/AgCl. This position of the reduction peak is close to the reduction potential of four-electron ORR.
The findings indicate that all the samples tend to go for the four-electron ORR that does not produce hydrogen peroxide (HO 2 − ). A further reduction of HO 2 − to OH − was also not observed at around −1.0 V. Moreover, the carbon Vulcan XC 72 has, overall, a higher reduction peak compared to all the MnO 2 catalysts, which can be ascribed due to the low electrical conductivity of the MnO 2 .
Catalysts 2020, 10, x FOR PEER REVIEW 4 of 14 V. Moreover, the carbon Vulcan XC 72 has, overall, a higher reduction peak compared to all the MnO2 catalysts, which can be ascribed due to the low electrical conductivity of the MnO2.

Oxygen Reduction Reaction Performance
To further investigate the number of electron transferred and ORR performance of the catalyst, a linear sweep voltammetry (LSV) was conducted to obtain the polarization curves at different rotational speed in 0.1-M oxygen-saturated KOH for all the samples. Figure 4 demonstrates the polarization curves of all samples at 1600 rpm. It clearly shows that the onset potential and terminal current density of the prepared catalysts are both strongly influenced by the nanostructure. The carbon Vulcan XC 72/nanoflower-like MnO2 has the highest terminal current density (−6.65 mA/cm 2 ) at a potential of −1.0 V and a higher onset potential (−0.13 V) at 1 mA/cm 2 . The carbon Vulcan XC 72/nanoflower-like MnO2 catalyst has the highest performance followed by carbon Vulcan XC 72 mixed with major nanoflower and minor nanowires, carbon Vulcan XC 72 mixed with major nanowires and minor nanoflower, pure carbon Vulcan XC 72 and carbon Vulcan XC 72/commercial MnO2. This trend indicates that the nanoflower-like is better than the nanowire-like structure due to its higher specific surface area that provides more abundant active sites for the ORR.

Oxygen Reduction Reaction Performance
To further investigate the number of electron transferred and ORR performance of the catalyst, a linear sweep voltammetry (LSV) was conducted to obtain the polarization curves at different rotational speed in 0.1-M oxygen-saturated KOH for all the samples. Figure 4 demonstrates the polarization curves of all samples at 1600 rpm. It clearly shows that the onset potential and terminal current density of the prepared catalysts are both strongly influenced by the nanostructure. The carbon Vulcan XC 72/nanoflower-like MnO 2 has the highest terminal current density (−6.65 mA/cm 2 ) at a potential of −1.0 V and a higher onset potential (−0.13 V) at 1 mA/cm 2 . The carbon Vulcan XC 72/nanoflower-like MnO 2 catalyst has the highest performance followed by carbon Vulcan XC 72 mixed with major nanoflower and minor nanowires, carbon Vulcan XC 72 mixed with major nanowires and minor nanoflower, pure carbon Vulcan XC 72 and carbon Vulcan XC 72/commercial MnO 2 . This trend indicates that the nanoflower-like is better than the nanowire-like structure due to its higher specific surface area that provides more abundant active sites for the ORR.
Vulcan XC 72/nanoflower-like MnO2 catalyst has the highest performance followed by carbon Vulcan XC 72 mixed with major nanoflower and minor nanowires, carbon Vulcan XC 72 mixed with major nanowires and minor nanoflower, pure carbon Vulcan XC 72 and carbon Vulcan XC 72/commercial MnO2. This trend indicates that the nanoflower-like is better than the nanowire-like structure due to its higher specific surface area that provides more abundant active sites for the ORR.  The number of electrons transferred per oxygen molecule for oxygen reduction was further evaluated by using the Koutecky-Levich (K-L) equation to study the ORR mechanism of the synthesized catalysts. The K-L equation is shown accordingly in Equations (4) and (5): Figure 5 shows the K-L plot for carbon Vulcan XC 72/nanoflower-like MnO 2 , carbon Vulcan XC 72/nanoflower-nanowire-like MnO 2 , and carbon Vulcan XC 72/nanowire-like MnO 2 catalysts. It shows that as the potential increase, the gradient of the K-L plot which also refers as the number of electrons transferred decreases. The linear and parallel behavior of these plots indicate the first-order kinetics with respect to molecular oxygen for the ORR [29].
The number of electrons transferred for ORR reaction obtained from the K-L plot for the Vulcan XC 72/nanoflower-like MnO 2 , carbon Vulcan XC 72/nanoflower-nanowire-like MnO 2 and Vulcan XC 72/nanowire-like MnO 2 catalysts are 3.68, 3.6 and 2.98 at −1.0 V, −0.8 V and −0.6 V, respectively. This result indicates that the synthesized nanoflower-like MnO 2 exhibits excellent electrocatalytic performance and stability at higher potentials. Meanwhile, the carbon Vulcan XC 72, mixed with major nanoflower and minor nanowires, and the carbon Vulcan XC 72, mixed with major nanowires and minor nanoflower, exhibit a similar trend as the carbon Vulcan XC 72/nanoflower-like MnO 2 but differ in the number of electrons transferred.
When comparing the K-L Plot of all samples at a fixed potential of −1.0 V and by obtaining the number of electrons transferred from the gradient of the K-L plot, the number of electrons transferred for carbon VXC 72 mixed with nanoflower MnO 2 , carbon Vulcan XC 72 mixed with nanoflower mixed with nanowires, and carbon VXC 72 mixed with nanowires is 3.68, 3.31 and 3.00, respectively.
In order to suppress the evolution of hydrogen peroxide, the desired ORR pathway is the four-electron pathway in which the number of electrons transferred experimentally must be between two and four to show that the electrocatalyst promotes some of the ORR pathways to occur in the four-electron pathway. The results show that MnO 2 nanoflower has the best electrocatalyst performance towards the ORR, as the number of transferred electrons is close to four, suggesting the likelihood of promoting the ORR reaction toward the four-electron pathway. Meanwhile, the electrocatalytic performance for carbon Vulcan XC 72 mixed with major nanoflower and minor nanowires and carbon Vulcan XC 72 mixed with major nanowires and minor nanoflower are also within the acceptable range of two to four.

Oxygen Evolution Reaction
As the MnO 2 has potential as a bifunctional catalyst towards OER, the OER performance of the nanostructure MnO 2 was further investigated. An LSV from 0.2 V to 1.0 V was conducted to obtain the polarization curves for the OER on rotating disk electrode as shown in Figure 6. The results confirm that the nanoflower-like MnO 2 has the lowest onset potential. The onset potential and the overpotential of the samples are summarized in Table 1. Table 1 shows that the nanoflower-like MnO 2 has the lowest onset potential. As overpotential is defined as the difference between the theoretical half-reaction reduction potential of OER and the onset potential (which is 0.3244 V), the trend of the overpotential is the same as the onset potential. At lower overpotential, the energy lost during the reaction in the electrode is also lower. As shown in Table 1, the pure carbon VXC 72 has the highest overpotential (energy lost) during OER, while the nanoflower MnO 2 has the least energy lost. The difference in overpotential between MnO 2 and pure carbon VXC 72 can be explained by the electrocatalyst behaviors of the MnO 2 , where the hydroxide ions can be adsorbed on the surface of MnO 2 due to the valence state of MnO 2 . Such a phenomenon can be observed in Figure 6, which shows that the sharp increment in the current density (indicating the OER for MnO 2 samples and pure carbon VXC 72) has significant differences. The electrocatalyst behaviors of MnO 2 increases the rate of reaction and alters the pathway for the OER. Therefore, a higher gradient of the faradaic region from 0.7 to 1.0 V can be observed for the MnO 2 samples. Overall, the results suggest that the nanoflower structure has a better nanostructure with a higher stability and better electrocatalyst performance at a high potential. confirm that the nanoflower-like MnO2 has the lowest onset potential. The onset potential and the overpotential of the samples are summarized in Table 1.   Table 1 shows that the nanoflower-like MnO2 has the lowest onset potential. As overpotential is defined as the difference between the theoretical half-reaction reduction potential of OER and the onset potential (which is 0.3244 V), the trend of the overpotential is the same as the onset potential. At lower overpotential, the energy lost during the reaction in the electrode is also lower. As shown in Table 1, the pure carbon VXC 72 has the highest overpotential (energy lost) during OER, while the nanoflower MnO2 has the least energy lost. The difference in overpotential between MnO2 and pure carbon VXC 72 can be explained by the electrocatalyst behaviors of the MnO2, where the hydroxide ions can be adsorbed on the surface of MnO2 due to the valence state of MnO2. Such a phenomenon can be observed in Figure 6, which shows that the sharp increment in the current density (indicating the OER for MnO2 samples and pure carbon VXC 72) has significant differences. The electrocatalyst behaviors of MnO2 increases the rate of reaction and alters the pathway for the OER. Therefore, a higher gradient of the faradaic region from 0.7 to 1.0 V can be observed for the MnO2 samples. Overall, the results suggest that the nanoflower structure has a better nanostructure with a higher stability and better electrocatalyst performance at a high potential.

Zinc-Air Battery Discharge Performance
During discharge, at the anode, the zinc electrode reacts with hydroxide ion (OH ) and oxidize to form zincate ion Zn OH , shown in Equation (6). Consequently, the precipitation of zinc oxide (ZnO) takes place when the dissolved zincate ion saturates and reaches its solubility, as shown in Equation (7).

Zinc-Air Battery Discharge Performance
During discharge, at the anode, the zinc electrode reacts with hydroxide ion (OH − ) and oxidize to form zincate ion Zn(OH) 2− 4 , shown in Equation (6). Consequently, the precipitation of zinc oxide (ZnO) takes place when the dissolved zincate ion saturates and reaches its solubility, as shown in Equation (7).
At the cathode, the oxygen reduction reaction (ORR) occurs via four-electron (Equation (1)) or two-electron (Equations (2) and (3)) pathways. ORR consumes oxygen (O 2 ) and water (H 2 O) and simultaneously produces a hydroxide ion. The hydroxide ion and water then transfers across the cell. Normally, the ORR kinetics are sluggish, and an ORR electrocatalyst is required to enhance ORR activity and battery performance. In alkaline solution, platinum (Pt) is an excellent ORR electrocatalyst, having excellent stability and showing a four-electron pathway. Nonetheless, its high cost hinders its practical applications. MnO 2 is a good alternative because it is significantly cheaper and more abundant than platinum.
The performances of the synthesized nanostructure MnO 2 as a catalyst in the cathode are presented in Figure 7. The galvanostatic discharge profiles indicate that the nanostructure MnO 2 follows the expected electrochemical behavior from the electrochemical characterization. In all cases, the batteries exhibited flat discharge profiles, having a voltage plateau at around 1.25 V. The Vulcan XC 72/nanoflower-like MnO 2 has the highest specific discharge capacity of up to 240 mAh/g zinc corresponding to a 31% higher performance than the nanowire-like MnO 2 in terms of discharge capacity. However, the theoretical specific discharge capacity of a zinc-air battery is 819 mAh/g, suggesting that the nanoflower-like MnO 2 only achieves 30% of the theoretical value, while the nanowire-like MnO 2 only achieves up to 20%. Such a phenomenon might be contributed to by the passivation that occurred on the zinc anode that usually exists in a zinc-air coin cell battery. the batteries exhibited flat discharge profiles, having a voltage plateau at around 1.25 V. The Vulcan XC 72/nanoflower-like MnO2 has the highest specific discharge capacity of up to 240 mAh/g zinc corresponding to a 31% higher performance than the nanowire-like MnO2 in terms of discharge capacity. However, the theoretical specific discharge capacity of a zinc-air battery is 819 mAh/g, suggesting that the nanoflower-like MnO2 only achieves 30% of the theoretical value, while the nanowire-like MnO2 only achieves up to 20%. Such a phenomenon might be contributed to by the passivation that occurred on the zinc anode that usually exists in a zinc-air coin cell battery.

Discussion
MnO2 can exist in various crystal structures, such as α-, β-, γ-, δ-and λ-MnO2, depending on the way in which the MnO6 octahedral unit shares their edges and corners. In δ-MnO2, all MnO6 octahedra are edge sharing, however, they are corner sharing in α-MnO2. δ-MnO2 has a layered structure and shows a nanoflower-like architecture, whilst α-MnO2 has a tunnel structure and exhibited architecture of nanowires [36]. The SEM images of the MnO2 catalysts, shown in Figure 1, indicate that the rod-like MnO2 structure was formed at longer dwell time, indicating that the catalyst formation follows the Ostwald Ripening process [23]. In this process, smaller particles gain thermodynamic stability by depositing on a larger particle to minimize the surface area to volume ratio. Hence, as the reaction time increased larger nanostructures were formed, leading to a smaller surface area. The N2 adsorption/desorption data suggest that nanostructure electro-catalysts improve

Discussion
MnO 2 can exist in various crystal structures, such as α-, β-, γ-, δand λ-MnO 2 , depending on the way in which the MnO 6 octahedral unit shares their edges and corners. In δ-MnO 2 , all MnO 6 octahedra are edge sharing, however, they are corner sharing in α-MnO 2 . δ-MnO 2 has a layered structure and shows a nanoflower-like architecture, whilst α-MnO 2 has a tunnel structure and exhibited architecture of nanowires [36]. The SEM images of the MnO 2 catalysts, shown in Figure 1, indicate that the rod-like MnO 2 structure was formed at longer dwell time, indicating that the catalyst formation follows the Ostwald Ripening process [23]. In this process, smaller particles gain thermodynamic stability by depositing on a larger particle to minimize the surface area to volume ratio. Hence, as the reaction time increased larger nanostructures were formed, leading to a smaller surface area. The N 2 adsorption/desorption data suggest that nanostructure electro-catalysts improve electronic and catalytic properties due to the higher surface area, i.e., (52.4 cm 2 /g) compared to other counterparts such as nanoflower mixed with nanowires (34.9 cm 2 /g) and nanowires (32.4 cm 2 /g), offering more active reaction sites as proven from the highest anodic and cathodic current peaks of the Vulcan XC 72/nanoflower-like MnO 2 , which correlates well with the high performances in ORR and OER owing to its highest specific surface area. This claim is confirmed by the data of the linear sweep voltammetry curves in Figure 4.
The results on the number of electrons transferred for the ORR reaction obtained from the K-L plot for different MnO 2 structures confirm that the synthesized nanoflower-like MnO 2 exhibits excellent electrocatalytic performance and stability at higher potentials, as also proven by the K-L plot. It shows that the MnO 2 nanoflower has the highest number of electrons transferred towards the four-electron pathway on the ORR. The results can be explained by the specific surface area of the synthesized MnO 2 . A higher specific surface area leads to more active sites for reaction, ascribing the superiority of the nanoflower-like MnO 2 over the other structures, as also shown by the Onset potential and overpotential in Table 1. Table 2 compares the performance of the MnO 2 catalysts developed in this study with other MnO 2 catalysts reported in the literature. The results obtained in the study are somewhat in line with earlier report. Despite showing a similar structure (nanoflower) and lower surface area, the number of electrons transferred for ORR is slightly higher than the reference [29]. It shows that the nanoflower-like MnO 2 poses surface area close to the nanorod-and nanoflake-like catalysts developed via the electrosynthesis method [20]. Despite showing a lower surface area, it shows higher electrons transferred for ORR from K-L plot. It is also worth noting that there is consistency in the data of the literature on the positive impact of the nanoflower structure in enhancing surface area, but this does not always positively correlate with the number of electrons transferred for the ORR.

Synthesis of Nanoflower-Like MnO 2 Catalyst
The nanoflower-like MnO 2 was synthesized using hydrothermal synthesis. Separately, 0.1 g of MnSO 4 ·H 2 O and 0.25 g of KMnO 4 were dissolved in 25 mL of deionized water and the solutions were mixed and transferred into a 100-mL, Teflon-lined, stainless-steel autoclave and heated at 140 • C in an oil bath or oven for 2 h. The autoclave was cooled down to room temperature and then the excess solution was filtered. Lastly, the obtained MnO 2 powder was washed with ethanol and water and dried in an oven at 60 • C for overnight. The synthesis was repeated with different reaction times for 4 and 6 h to obtain the different nanostructures of MnO 2 .

Characterization
The obtained samples were characterized by Scanning electron microscopy (SEM, JEOL-JSM-6480) to investigate the nanostructure of the MnO 2 . Brunauer-Emmett-Teller (BET) specific surface areas of the samples were determined from nitrogen adsorption isotherms that were performed on a BEL Japan BELSORP-mini II.

Electrochemical Measurement
All electrochemical measurements were carried out in a three-electrode configuration by a potentiostat/galvanostat with an impedance measurement unit (AMETEK, PAR VersaSTAT 3A). The standard three-electrode cell consists of platinum foil as the counter electrode, a Ag/AgCl electrode as a reference electrode, and a modified glassy carbon electrode (GCE) as the working electrode. The electrocatalytic activity of the as-prepared catalysts towards ORR was measured by cyclic voltammogram (CV) in a mixture of 0.1-M KOH at a scan rate of 50 mV s −1 from −1.8 to 1 V under an ambient atmosphere. For the ORR, Linear Sweep Voltammetry (LSV) was applied with a scan rate of 1 mV/s from 0.2 to −1 V, with the cathodic traces set at a rotational speed of 0, 400, 800, 1200, 1600 and 2000 RPM. For OER, the LSV was applied with a scan rate of 1 mV/s from 0.2 to 1 V, with the anodic traces set at rotational speeds of 0, 400, 800, 1200, 1600 and 2000 RPM.

Preparation of Working Electrode
In a typical procedure, 0.5 g of the nanoflower-like MnO 2 catalysts were ultrasonically mixed in 1 mL 5% polyvinylidene fluoride (PVDF) solutions to form homogenous catalyst ink under room condition. Then, 0.05 mL of the catalyst ink was dripping onto the surface of the glassy carbon electrode (GCE) attached to the rotary machine using a micropipette and then dried at room temperature.

Electrode and Battery Fabrication
Zinc-air coin cell batteries were fabricated and used to evaluate the discharge capacity of batteries with different catalysts. The fabricated coin cell consisted of three main parts: cathode, anode, and separator. The cathode was synthesized by coating carbon ink solution on a nickel foam. One side of the nickel foam (exhibited hydrophilic properties for reaction occur in the electrolyte) was coated with carbon homogeneous ink solution which consisted of 30 wt.% MnO 2 , 70 wt.% carbon Vulcan XC 72, and 2.5 wt.% of (MnO 2 /carbon) dissolved in toluene. Another side of the nickel (exhibited hydrophobic properties as an air diffusion layer) was coated with carbon homogeneous ink solution consisted of 40 wt.% of carbon Vulcan XC 72, 40 wt.% Polytetrafluoroethylene (PTFE), 20% glucose and ethanol were used as the solvent. The anode was prepared by zinc electroplating in 500 cm 3 of 1-M ZnSO 4 ·7H 2 O solution on the surface of the nickel foam. Nickel foams with dimensions of 10 × 1 × 0.1 cm were placed vertically, in parallel at the opposite side of the zinc plate in the electrolyte. The electrodes were connected to a digital DC power supply (ATTEN APS 3005s) operated at galvanostatic mode at voltage of 1.6 V for 2 h for each side of the nickel foam. The separator was a solid polymer electrolyte (SPE) prepared homogeneously by mixing 0.6 g of Carbopol 940 and 15 g of PVAC in 40 mL of deionized water and 15 mL of 7-M KOH solution using a homogenizer. The prepared Carbopol solution was then transferred into a petri dish and dried at open air for 2 to 3 days. The obtained SPE should be around 0.1 to 0.2 mm. After the cathode, anode and separator were ready, a coin cell battery was set up according to the schematic diagram shown in Figure 8. The assembled coin-cell stack was then pressed under 100 kg/cm 2 using hydraulic presser. In a typical procedure, 0.5 g of the nanoflower-like MnO2 catalysts were ultrasonically mixed in 1 mL 5% polyvinylidene fluoride (PVDF) solutions to form homogenous catalyst ink under room condition. Then, 0.05 mL of the catalyst ink was dripping onto the surface of the glassy carbon electrode (GCE) attached to the rotary machine using a micropipette and then dried at room temperature.

Electrode and Battery Fabrication
Zinc-air coin cell batteries were fabricated and used to evaluate the discharge capacity of batteries with different catalysts. The fabricated coin cell consisted of three main parts: cathode, anode, and separator. The cathode was synthesized by coating carbon ink solution on a nickel foam. One side of the nickel foam (exhibited hydrophilic properties for reaction occur in the electrolyte) was coated with carbon homogeneous ink solution which consisted of 30 wt.% MnO2, 70 wt.% carbon Vulcan XC 72, and 2.5 wt.% of (MnO2/carbon) dissolved in toluene. Another side of the nickel (exhibited hydrophobic properties as an air diffusion layer) was coated with carbon homogeneous ink solution consisted of 40 wt.% of carbon Vulcan XC 72, 40 wt.% Polytetrafluoroethylene (PTFE), 20% glucose and ethanol were used as the solvent. The anode was prepared by zinc electroplating in 500 cm 3 of 1-M ZnSO4·7H2O solution on the surface of the nickel foam. Nickel foams with dimensions of 10 × 1 × 0.1 cm were placed vertically, in parallel at the opposite side of the zinc plate in the electrolyte. The electrodes were connected to a digital DC power supply (ATTEN APS 3005s) operated at galvanostatic mode at voltage of 1.6 V for 2 h for each side of the nickel foam. The separator was a solid polymer electrolyte (SPE) prepared homogeneously by mixing 0.6 g of Carbopol 940 and 15 g of PVAC in 40 mL of deionized water and 15 mL of 7-M KOH solution using a homogenizer. The prepared Carbopol solution was then transferred into a petri dish and dried at open air for 2 to 3 days. The obtained SPE should be around 0.1 to 0.2 mm. After the cathode, anode and separator were ready, a coin cell battery was set up according to the schematic diagram shown in Figure 9. The assembled coin-cell stack was then pressed under 100 kg/cm 2 using hydraulic presser.

Battery Performance Test
The prepared coin cell was connected to a coin cell battery tester, Netware (TOB-CT-4008-5V10mA-164), and discharged at a discharge current of 5 mA until the potential of coin cell depleted below the cut-off voltage of 0.01 V. The specific discharge capacity was obtained by divide the mass of zinc electroplated on the nickel foam which required to measure and record every time before setting up the coin cell.

Battery Performance Test
The prepared coin cell was connected to a coin cell battery tester, Netware (TOB-CT-4008-5V10mA-164), and discharged at a discharge current of 5 mA until the potential of coin cell depleted below the cut-off voltage of 0.01 V. The specific discharge capacity was obtained by divide the mass of zinc electroplated on the nickel foam which required to measure and record every time before setting up the coin cell.

Conclusions
The nanoflower-like MnO 2 catalyst structure was successfully prepared by the hydrothermal method. The formation of such structure was confirmed from the SEM shows image in which the dwell times of 2, 4 and 6 h resulting in nanoflowers, nanoflower mixed with nanowires and nanowires structures, respectively. BET results confirm that the nanoflower poses the highest specific surface area of 52.4 cm 2 /g followed by nanoflower mixed with nanowires of 34.9 cm 2 /g and nanowires of 32.4 cm 2 /g. The ORR and OER LSV polarization curve prove the hypothesis of the high performance of nanoflower MnO 2 due to its large specific surface area. In terms of ORR, the number of electrons transferred for carbon VXC 72 mixed with nanoflower MnO 2 , carbon VXC 72 mixed with nanoflower mixed with nanowires and carbon VXC 72 mixed with nanowires are 3.68, 3.31 and 3.00, respectively. The synthesized MnO 2 has an excellent coin cell battery performance on improving the discharge capacity of a zinc-air battery. Among all the samples, nanoflower MnO 2 exhibits the best discharge performance, reaching up to 30% of the theoretical discharge capacity of the zinc-air battery.