Mesoporous Highly-Deformable Composite Polymer for a Gapless Triboelectric Nanogenerator via a One-Step Metal Oxidation Process

The oxidation of metal microparticles (MPs) in a polymer film yields a mesoporous highly-deformable composite polymer for enhancing performance and creating a gapless structure of triboelectric nanogenerators (TENGs). This is a one-step scalable synthesis for developing large-scale, cost-effective, and light-weight mesoporous polymer composites. We demonstrate mesoporous aluminum oxide (Al2O3) polydimethylsiloxane (PDMS) composites with a nano-flake structure on the surface of Al2O3 MPs in pores. The porosity of mesoporous Al2O3-PDMS films reaches 71.35% as the concentration of Al MPs increases to 15%. As a result, the film capacitance is enhanced 1.8 times, and TENG output performance is 6.67-times greater at 33.3 kPa and 4 Hz. The pressure sensitivity of 6.71 V/kPa and 0.18 μA/kPa is determined under the pressure range of 5.5–33.3 kPa. Based on these structures, we apply mesoporous Al2O3-PDMS film to a gapless TENG structure and obtain a linear pressure sensitivity of 1.00 V/kPa and 0.02 μA/kPa, respectively. Finally, we demonstrate self-powered safety cushion sensors for monitoring human sitting position by using gapless TENGs, which are developed with a large-scale and highly-deformable mesoporous Al2O3-PDMS film with dimensions of 6 × 5 pixels (33 × 27 cm2).


Introduction
Mechanical energy is the most common energy in our surroundings, and it can be converted into electricity anytime and anywhere. Triboelectric nanogenerators (TENGs), which are power-generating devices introduced in 2012, have been proven as cost effective, simple, able to cover large areas, durable, and efficient for energy harvesting [1][2][3]. Due to their simple mechanism, which utilizes repeating cycles of contact and separation between two materials, TENGs have demonstrated promising capability in scavenging energy and as variable sensors of mechanical energy (vibration, rotating, etc.), ocean waves, fluids, and human activities. Further, TENGs can generate electric signals without relying on external power sources, thus enabling the development of self-powered Internet of Things (IoT) sensors [4,5].

Fabrication and Output Measurement of the TENGs
To design the vertical contact-separation mode TENG, the top electrode was prepared with a 3 × 3 cm 2 30-μm-thick conductive graphene tape (DASAN Solueta, SSC30) and mesoporous Al2O3-PDMS, with a thickness of 3 mm. The conductive graphene tape and mesoporous Al2O3-PDMS were attached to the acryl with double-sided tape.
To apply the vertical contact-separation mode, we used a pushing tester (JPT-110) ranging from 5 N-30 N of force. To measure TENG output performance, we used an oscilloscope (Tektronix MDO 3052, Beaverton, OR, USA) probe with 40 MΩ and a preamplifier (Stanford Research Systems, SR570, Sunnyvale, CA, USA) connected to the MDO 3052. TENG performance was measured at a working frequency of 4 Hz, and the gap distance was 4 mm between the two materials.

Analysis of the Al2O3-PDMS TENG
The surface morphology, cross-section, energy dispersive spectroscopic (EDS) mapping, and line scan characteristics of the PDMS layer and mesoporous Al2O3-PDMS were examined using high-resolution field emitting scanning electron microscopy (HR FE-SEM, Leo supra 55, Carl Zeiss, Stockholm, Sweden). The porosity was measured by changes of volume and mass. Compressive strength was tested using a Universal Testing System (Instron, MA, USA) following ASTM D 695.

Fabrication and Output Measurement of the TENGs
To design the vertical contact-separation mode TENG, the top electrode was prepared with a 3 × 3 cm 2 30-µm-thick conductive graphene tape (DASAN Solueta, SSC30) and mesoporous Al 2 O 3 -PDMS, with a thickness of 3 mm. The conductive graphene tape and mesoporous Al 2 O 3 -PDMS were attached to the acryl with double-sided tape.
To apply the vertical contact-separation mode, we used a pushing tester (JPT-110) ranging from 5 N-30 N of force. To measure TENG output performance, we used an oscilloscope (Tektronix MDO 3052, Beaverton, OR, USA) probe with 40 MΩ and a preamplifier (Stanford Research Systems, SR570, Sunnyvale, CA, USA) connected to the MDO 3052. TENG performance was measured at a working frequency of 4 Hz, and the gap distance was 4 mm between the two materials.

Analysis of the Al 2 O 3 -PDMS TENG
The surface morphology, cross-section, energy dispersive spectroscopic (EDS) mapping, and line scan characteristics of the PDMS layer and mesoporous Al 2 O 3 -PDMS were examined using high-resolution field emitting scanning electron microscopy (HR FE-SEM, Leo supra 55, Carl Zeiss, Stockholm, Sweden). The porosity was measured by changes of volume and mass. Compressive strength was tested using a Universal Testing System (Instron, MA, USA) following ASTM D 695. Capacitance measurements of the mesoporous Al 2 O 3 -PDMS films were performed at room temperature, at an electrical frequency of 2000 Hz and a bias of 100 mV using an E4980a precision inductance, capacitance, and resistance meter (Agilent Technologies, Santa Clara, CA, USA). A custom-built sensor probe station with a programmable x-, y-, and z-axis stage (0.1-µm resolution) enabled the mesoporous Al 2 O 3 -PDMS films to be used to obtain the exact pressure, and a force gauge (Mark-10, Copiague, NY, USA) measured the load.

Fabrication of the Self-Powered Safety Cushion Sensors
We prepared 30 ea, to make a 6 × 5 pixels, of mesoporous Al 2 O 3 -PDMS films attached by conductive graphene tape with a size of 3 × 3 cm 2 for both the top and bottom side. We put them on the bottom polyethylene terephthalate (PET) film, and the total size was 33 × 27 cm 2 , 6 × 5 pixels, with 3 cm of distance between each cell, then we put the PET film on them. Each cell was connected by a wire to the DAQ 6011, multichannel. It could show the position pressure by color: green was assigned to 1.3-2.5 V, yellow from 2.5-3.8 V, orange from 3.8-5 V, and red over 5 V in real time.

Results and Discussion
The schematic diagrams for the synthesis process of the mesoporous Al 2 O 3 -PDMS-based TENGs are shown in Figure 1a. In previous studies, researchers generally made porous structure by using NaCl, ZnO, or polystyrene particles in the PDMS and removing them by immersion in water solution or by chemical treatments. In this study, we used a one-step method without removing anything. The advantages of a one-step method were two-fold. One was a chemical reaction increasing the number and size of pores, given as: Al can easily react with H 2 O because it is an active metal like K, Ca, Na etc., at room temperature or under the drying conditions (80 • C). H 2 gas, one product of the chemical reaction, increased the volume by increasing the size and the number of pores. Furthermore, Al 2 O 3 particles had a nano-flake surface following the reaction, increasing the surface area to increase the output performance, as shown in Figure 1c-ii. By most aspects (costs, characteristics like the output performance, particle size), we could choose Al as a suitable active metal and tribo-material. It also has higher density than PDMS and DI water. In a previous study, to increase the output performance, the authors had constructed a multi-layered structure, alternating positively-and negatively-charged layers. In this study, Al, positive material, sank to the bottom because of its relatively higher density than PDMS and DI water. As a result, the top layer was more negatively charged than the bottom layer [8]. The resultant mesoporous Al 2 O 3 -PDMS had a multi-layered structure, and this may have increased the output performance. A photograph of the mesoporous Al 2 O 3 -PDMS (30 × 30 × 7 mm 3 ) and the scanning electron microscope image are shown in Figure 1b  When the external force is removed, firstly, the inner surface and Al 2 O 3 separate, and e − inner move to the top electrode. Secondly, the top electrode and surface of mesoporous Al 2 O 3 -PDMS separate, and e − sur move to the top electrode to neutralize the negative charges in the bottom electrode; thus, charges occur not only at the surface of mesoporous Al 2 O 3 -PDMS, but also in the inner pore of mesoporous Al 2 O 3 -PDMS, and stacked charges increase. Stacked charges increase due to the advantage of the porous structure (double contact) and can increase the output performance of TENGs. The charge and the voltage were calculated by the following equation: Here, σ P is the total charge, σ sur is the surface charge, σ inner is the inner pore charge, V OC is the open-circuit voltage, and ε 0 is the permittivity in a vacuum.
To confirm the additional advantages of Al 2 O 3 on TENG output performance, we compared the output performance of other materials. We compared the output performance (voltage, current) of metal oxides such as Al, Al 2 O 3 , TiO 2 , SiO 2 , and HfO by sputtering them on an Al sheet (S-Al, S-Al 2 O 3 , S-TiO 2 , S-SiO 2 , S-HfO) and other materials (alkali-treated micro-nano-flaked aluminum hydroxide (Al(OH) 3 ), polished Al (P-Al), Al sheet dipped in DI water and dried (Al 2 O 3 )), as shown in Table 1. The results showed that sputtered Al 2 O 3 had the best output performance (40.96 V, 2.86 µA). In previous studies, materials with greater dielectric constants had better output performance [16]. Although TiO 2 (ε r = 80) and HfO (ε r = 25) have larger dielectric constants than Al 2 O 3 (ε r = 9), they had lower output performance than Al 2 O 3 . Based on this result, we believe that Al 2 O 3 was suitable for fabricating the porous structure and increasing the output performance.   Figure 2 shows the characteristics of mesoporous Al 2 O 3 -PDMS. First, we confirmed that Al powder changed to Al 2 O 3 according to the chemical reaction in Equation (1). By energy dispersive spectrometry, we confirmed that the elements Si, Al, C, and O were present. Figure 2a,b shows the SEM and EDS images. Through the SEM image, we confirmed the location of ball-like Al 2 O 3 . By comparison of the SEM images and the distribution of Al (7.48%) and O (28.28%) via EDS images, we see that Al powder, mixed with PDMS and DI water, reacted to form Al 2 O 3 powder after drying (for 1 h at 80 • C). In previous studies by J. Chun et al., a mesoporous structure made by DI water and demonstrating pores impregnated with Au nanoparticles had 59% of the maximum porosity at a 50% DI water concentration. However, in this study, at the same condition, we got 45.4% of the maximum porosity. When Al MPs were embedded, the porosity increased to approximately 71.35% as the amount of Al increased to 15%, as shown in Figure 2c. The meaning of high porosity is that the mesoporous film is much lighter, more flexible, and deformable. At the same volume, we can get mass ratios of 1:0.37:0.35:0.27 of 0 wt%:5 wt%:10 wt%:15 wt% of Al MP concentration. Figure 2d shows the deformability of mesoporous Al 2 O 3 -PDMS (5, 10, 15 wt%) films with a diameter size of 50 mm and a height of 13 mm by ASTM D-695. We limited the jig amplitude to 8 mm and measured the maximum compressed stress at the same conditions. When we compared them, the compressive stress of a mesoporous Al 2 O 3 -PDMS (5 wt%) film was 148.5 MPa with 58.3% of the porosity. However, in the case of mesoporous Al 2 O 3 -PDMS (15 wt%) films, because they had 71.35% of porosity, the maximum compressed stress was the minimum value, 11.7 MPa. That means low compressed stress can be easily deformed, and it is easy to fully contact between the top electrode and a mesoporous Al 2 O 3 -PDMS, like the inset of Figure 2d. We believe that the high porosity and light weight are major factors; if their values increase, they can be higher deformability and can increase the relative capacitance change and output performance of TENGs.
Figure 2e,f shows that mesoporous Al 2 O 3 -PDMS is much more deformable than non-porous PDMS and mesoporous PDMS (0 wt%). To compare the deformability of non-porous PDMS and mesoporous Al 2 O 3 -PDMS (0, 5, 10, 15 wt%), we measured the relative capacitance with 7 × 7 × 3 mm 2 films at 0, 16.7, and 33.3 kPa, given respectively as C 0 , C 16.7kPa , and C 33.3kPa . When non-porous PDMS, 0, 5, 10, 15 wt% mesoporous Al 2 O 3 -PDMS, is pressed at 33.3 kPa (C 33.3kPa ), the max relative capacitance was 1.08, 1.69, 1.97, 2.07, and 3.03, respectively, at 33.3 kPa. When comparing 0 wt% and 15 wt% of mesoporous Al 2 O 3 -PDMS, the capacitance of the film increased 1.79-times more. Generally, capacitance is expressed by the following Equation (3): Here, C is the capacitance, ε 0 is the permittivity in a vacuum, ε r is the relative permittivity, A is the area of the film, and d is the thickness of the film. Based on this equation, if ε r and A are constants, the capacitance inversely depends on the thickness of the film. Thus, as the film is deformable, the film thickness can be easily compressed, and the capacitance increases. Figure 2e,f shows that mesoporous Al2O3-PDMS is much more deformable than non-porous PDMS and mesoporous PDMS (0 wt%). To compare the deformability of non-porous PDMS and mesoporous Al2O3-PDMS (0, 5, 10, 15 wt%), we measured the relative capacitance with 7 × 7 × 3 mm 2 films at 0, 16.7, and 33.3 kPa, given respectively as C0, C16.7kPa, and C33.3kPa. When non-porous PDMS, 0, 5, 10, 15 wt% mesoporous Al2O3-PDMS, is pressed at 33.3 kPa (C33.3kPa), the max relative capacitance was 1.08, 1.69, 1.97, 2.07, and 3.03, respectively, at 33.3 kPa. When comparing 0 wt% and 15 wt% of mesoporous Al2O3-PDMS, the capacitance of the film increased 1.79-times more. Generally, capacitance is expressed by the following Equation (3): Here, C is the capacitance, is the permittivity in a vacuum, is the relative permittivity, A is the area of the film, and d is the thickness of the film. Based on this equation, if and A are constants, the capacitance inversely depends on the thickness of the film. Thus, as the film is deformable, the film thickness can be easily compressed, and the capacitance increases.  Figure 3 shows the output voltage and output current of non-porous PDMS and P-Al2O3-PDMS (5, 10, 15 wt%). First, we confirmed the advantage of the porous structure. In Figure 3a, we compare non-porous PDMS and mesoporous P-Al2O3-PDMS (15 wt%) at 30 N of force, a 4-Hz frequency, a 4-mm gap distance, and a 3 × 3 cm 2 active area. The output voltage of non-porous PDMS and mesoporous Al2O3-PDMS (15 wt%) was 39 V and 259.58 V, respectively. The mesoporous structure film had 6.66-times greater output voltage than the non-porous PDMS film. To understand the influence of porous structure in mesoporous Al2O3-PDMS, we compared one cycle of the output voltage generated by non-porous PDMS and mesoporous Al2O3-PDMS. In non-porous PDMS, the contact and releasing peaks took 34 and 32 ms to generate electric energy, as shown in Figure 3a-i. However, in mesoporous Al2O3-PDMS, contact and releasing peaks took 70 and 77 ms, 2.22-times longer, as shown in Figure 3a-ii. The reason is structural. In a previous study, soft membranes and   Figure 3a-ii. The reason is structural. In a previous study, soft membranes and porous structures have been shown to increase the output performance by maximizing effective contact area and the potential difference produced between the Al 2 O 3 MPs and PDMS inside pores by contact due to different triboelectric tendencies.
contact area and the potential difference produced between the Al2O3 MPs and PDMS inside pores by contact due to different triboelectric tendencies.
By analyzing the output voltage and fitting the curve of voltage response to dynamic pressure in the range of 5.5-33 kPa, we determined that the voltage pressure sensitivity of the non-porous PDMS and mesoporous Al2O3-PDMS (5, 10, 15 wt%) reached approximately 0.95, 3.87, 5.57, and 6.71 V/kPa, as shown in Figure 3b. In previous studies, the linearity of pressure sensitivity was divided into several regimes, such as low-pressure and medium-pressure. In this study, however, we found linear pressure sensitivity (sensitivity = 6.37 V/kPa, R 2 = 0.991 in the 5.5-33 kPa pressure region) across the entire pressure regime. This linearity of the sensitivity of mesoporous Al2O3-PDMS is affected by the deformability of the film with the porosity (78%) effect; thus, as porosity increases, the linearity of pressure sensitivity (R 2 value) is high because of the relative capacitance change with thickness change. Like the voltage sensitivity, the current pressure sensitivity reached approximately 0.04, 0.06, 0.10, and 0.18 μA/kPa in Figure 3c, and the linearity was maintained.  Figure 4 shows the schematic and output voltage and current of gapless TENGs, fabricated by attaching an electrode to both sides of mesoporous Al2O3-PDMS film. In gapless TENGs, the output performance was much less than contact-separation mode TENGs because the charge density on the surface had a greater influence than in the pores. Thus, by Relation (1), the total charge density (σp) was reduced, and the output voltage and current were also reduced. However, the advantages of gapless devices are simple, allowing for large-scale fabrication, low cost, and good special qualities. In other words, gapless TENGs had very poor output performance, but they neither require complicated fabrication, nor limit the large-scale fabrication of practical systems.
Unlike contact separation mode, charge generation of the mesoporous Al2O3-PDMS TENG under pressure is caused by the triboelectric effect and electrostatic induction. First, when mesoporous Al2O3-PDMS film is pressurized, friction occurs between PDMS and nano-flake Al2O3 MPs in the pores, resulting in negative and positive charges on both surfaces. Furthermore, Al2O3 with a nano-flake structure increases charge density due to increasing the surface and friction due to electrostatic induction. With these factors, electrons move from the top electrode to the bottom By analyzing the output voltage and fitting the curve of voltage response to dynamic pressure in the range of 5.5-33 kPa, we determined that the voltage pressure sensitivity of the non-porous PDMS and mesoporous Al 2 O 3 -PDMS (5, 10, 15 wt%) reached approximately 0.95, 3.87, 5.57, and 6.71 V/kPa, as shown in Figure 3b. In previous studies, the linearity of pressure sensitivity was divided into several regimes, such as low-pressure and medium-pressure. In this study, however, we found linear pressure sensitivity (sensitivity = 6.37 V/kPa, R 2 = 0.991 in the 5.5-33 kPa pressure region) across the entire pressure regime. This linearity of the sensitivity of mesoporous Al 2 O 3 -PDMS is affected by the deformability of the film with the porosity (78%) effect; thus, as porosity increases, the linearity of pressure sensitivity (R 2 value) is high because of the relative capacitance change with thickness change. Like the voltage sensitivity, the current pressure sensitivity reached approximately 0.04, 0.06, 0.10, and 0.18 µA/kPa in Figure 3c, and the linearity was maintained. Figure 4 shows the schematic and output voltage and current of gapless TENGs, fabricated by attaching an electrode to both sides of mesoporous Al 2 O 3 -PDMS film. In gapless TENGs, the output performance was much less than contact-separation mode TENGs because the charge density on the surface had a greater influence than in the pores. Thus, by Relation (1), the total charge density (σ P ) was reduced, and the output voltage and current were also reduced. However, the advantages of gapless devices are simple, allowing for large-scale fabrication, low cost, and good special qualities. In other words, gapless TENGs had very poor output performance, but they neither require complicated fabrication, nor limit the large-scale fabrication of practical systems.
Al2O3-PDMS (15 wt%) gapless system. As mentioned before, gapless systems had output performance inferior to that of contact-separation systems due to no surface charging, and only inner pore charging. At 33.3 kPa, 4 Hz, and 30 × 30 × 3 mm 3 , we obtained a maximum voltage of 34.00 V and a current of 1.77 μA. Similar to the contact-separation mode, we measured a pressure sensitivity of 1.00 V/kPa and 0.02 μA/kPa.
The output voltage and power of the mesoporous Al2O3-PDMS (15 wt%) were also measured with external loads varying from 1 MΩ-100 MΩ, as shown in Figure 4f,g. It is clearly seen that the output voltage increased with increasing resistance. Consequently, the instantaneous power of the external resistance was 541.11 μW (60.12 μW/cm 2 ) at a resistance of 10 MΩ. We also demonstrated the self-powered safety cushion sensor for monitoring the sitting position of the human. Conductive tape arrays (6 × 5), total 30 cells, with each cell size of 3 cm × 3 cm on PET films (33 cm × 27 cm), were fabricated on mesoporous Al2O3-PDMS (15 wt%) films, as shown in Figure 5a. To demonstrate the sitting position as represented by color, green was assigned from 1.3-2.5 V, yellow from 2.5-3.8 V, orange from 3.8-5 V, and red over 5 V in real time. We connected the self-powered safety cushion sensor to the multichannel and monitor, as shown in Figure 5b. To confirm the resolution, we sat at the front, in the middle, and towards the back of the safety cushion sensor, as shown in Figure 5c-e. When sitting at the front, only parts of the hips made contact with the safety cushion sensor and only the front of the safety cushion sensor had output voltage. The closer the hips were to the back of the chair, the greater the proportion of safety cushion sensor output Unlike contact separation mode, charge generation of the mesoporous Al 2 O 3 -PDMS TENG under pressure is caused by the triboelectric effect and electrostatic induction. First, when mesoporous Al 2 O 3 -PDMS film is pressurized, friction occurs between PDMS and nano-flake Al 2 O 3 MPs in the pores, resulting in negative and positive charges on both surfaces. Furthermore, Al 2 O 3 with a nano-flake structure increases charge density due to increasing the surface and friction due to electrostatic induction. With these factors, electrons move from the top electrode to the bottom electrode to keep electrical neutrality. When the pressure is released, the surfaces in contact are separated, and electrons flow from the bottom electrode to the top electrode. Figure 4b-e shows the output voltage, current, and pressure sensitivity of a mesoporous Al 2 O 3 -PDMS (15 wt%) gapless system. As mentioned before, gapless systems had output performance inferior to that of contact-separation systems due to no surface charging, and only inner pore charging. At 33.3 kPa, 4 Hz, and 30 × 30 × 3 mm 3 , we obtained a maximum voltage of 34.00 V and a current of 1.77 µA. Similar to the contact-separation mode, we measured a pressure sensitivity of 1.00 V/kPa and 0.02 µA/kPa.
The output voltage and power of the mesoporous Al 2 O 3 -PDMS (15 wt%) were also measured with external loads varying from 1 MΩ-100 MΩ, as shown in Figure 4f,g. It is clearly seen that the output voltage increased with increasing resistance. Consequently, the instantaneous power of the external resistance was 541.11 µW (60.12 µW/cm 2 ) at a resistance of 10 MΩ.
We also demonstrated the self-powered safety cushion sensor for monitoring the sitting position of the human. Conductive tape arrays (6 × 5), total 30 cells, with each cell size of 3 cm × 3 cm on PET films (33 cm × 27 cm), were fabricated on mesoporous Al 2 O 3 -PDMS (15 wt%) films, as shown in Figure 5a. To demonstrate the sitting position as represented by color, green was assigned from 1.3-2.5 V, yellow from 2.5-3.8 V, orange from 3.8-5 V, and red over 5 V in real time. We connected the self-powered safety cushion sensor to the multichannel and monitor, as shown in Figure 5b. To confirm the resolution, we sat at the front, in the middle, and towards the back of the safety cushion sensor, as shown in Figure 5c-e. When sitting at the front, only parts of the hips made contact with the safety cushion sensor and only the front of the safety cushion sensor had output voltage. The closer the hips were to the back of the chair, the greater the proportion of safety cushion sensor output voltage, as shown in Figure 5f-h. We are convinced that the self-powered safety cushion sensor could be applied to wheel chairs to control braking if patients sit too far forward. voltage, as shown in Figure 5f-h. We are convinced that the self-powered safety cushion sensor could be applied to wheel chairs to control braking if patients sit too far forward.

Conclusions
In summary, we have demonstrated a mesoporous highly-deformable composite polymer with metal oxide by a scalable one-step synthesis unlike the two-step fabrications of previous studies. The oxidation of Al MPs in a polymer film formed a nano-flake morphology on the surface and enhanced the output performance by increasing contact area. As a result, it increased the output performance 6.67-times more than the non-porous PDMS, and the porosity of mesoporous Al2O3-PDMS (15 wt%) film reached 71.35%. Thus, mesoporous Al2O3-PDMS (15 wt%) film was found to be more deformable and light weight than the non-porous PDMS film and mesoporous films without metal MPs. As a result, we obtained a relative capacitance change of 3.03, about 1.8-times higher compared with mesoporous films without metal MPs at 33.3 kPa. The output performance of mesoporous Al2O3-PDMS (15 wt%) films showed an instantaneous voltage of 259.68 V under contact-separation mode, an over six-fold enhancement compared with non-porous PDMS. Further, it had a linear pressure sensitivity of 6.71 V/kPa due to the high porosity. We are convinced that the enhancement was affected by the increased charge density created by contact not only between the top electrode and surface of mesoporous Al2O3-PDMS, but also between PDMS and the nano-flake structure on

Conclusions
In summary, we have demonstrated a mesoporous highly-deformable composite polymer with metal oxide by a scalable one-step synthesis unlike the two-step fabrications of previous studies. The oxidation of Al MPs in a polymer film formed a nano-flake morphology on the surface and enhanced the output performance by increasing contact area. As a result, it increased the output performance 6.67-times more than the non-porous PDMS, and the porosity of mesoporous Al 2 O 3 -PDMS (15 wt%) film reached 71.35%. Thus, mesoporous Al 2 O 3 -PDMS (15 wt%) film was found to be more deformable and light weight than the non-porous PDMS film and mesoporous films without metal MPs. As a result, we obtained a relative capacitance change of 3.03, about 1.8-times higher compared with mesoporous films without metal MPs at 33.3 kPa. The output performance of mesoporous Al 2 O 3 -PDMS (15 wt%) films showed an instantaneous voltage of 259.68 V under contact-separation mode, an over six-fold enhancement compared with non-porous PDMS. Further, it had a linear pressure sensitivity of 6.71 V/kPa due to the high porosity. We are convinced that the enhancement was affected by the increased charge density created by contact not only between the top electrode and surface of mesoporous Al 2 O 3 -PDMS, but also between PDMS and the nano-flake structure on metal MPs' inside pores and high deformation, which changed thickness and increased the electric field. We demonstrated a self-powered safety cushion sensor to detect a human sitting position that can be applied to wheel chair safety. This approach provides a promising large-scale power supply for realizing self-powered safety systems such as matrices, blankets, and road sensors.