P-Doped Carbon Quantum Dots with Antibacterial Activity

It is a major challenge to effectively inhibit microbial pathogens in the treatment of infectious diseases. Research on the application of nanomaterials as antibacterial agents has evidenced their great potential for the remedy of infectious disease. Among these nanomaterials, carbon quantum dots (CQDs) have attracted much attention owing to their unique optical properties and high biosafety. In this work, P-doped CQDs were prepared by simple hydrothermal treatment of m-aminophenol and phosphoric acid with fluorescence emission at 501 nm when excited at 429 nm. The P-doped CQDs showed effective antibacterial activity against Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus). The minimal inhibitory concentrations (MICs) of P-doped CQD were 1.23 mg/mL for E. coli and 1.44 mg/mL for S. aureus. Furthermore, the morphologies of E. coli cells were damaged and S. aureus became irregular when treated with the P-doped CQDs. The results of zeta potential analysis demonstrated that the P-doped CQDs inhibit antibacterial activity and destroy the structure of bacteria by electronic interaction. In combination, the results of this study indicate that the as-prepared P-doped CQDs can be a promising candidate for the treatment of bacterial infections.


Introduction
Bacterial infections, especially those caused by drug-resistant bacteria, threaten public health and have always been a serious problem worldwide [1,2]. Due to the abuse of antibiotics, these infections have become more difficult to cure because of increasingly serious drug-resistance [3,4]. It is of urgent concern to develop alternative antimicrobial agents with excellent properties against bacterial infection. Recently, nanomaterials involving metal or metal oxide have aroused widespread interest due to their great potential in the treatment of bacterial infections from antibiotic-resistant bacteria [5][6][7][8]. However, it is essential to balance antibacterial efficiency and biosafety, which has become an obstacle in the clinical application of these semiconductor nanomaterials. Carbon-based nanomaterials, including fullerene, carbon nanotubes, graphene, graphene oxide, and carbon quantum dots [9][10][11], have been proved to have efficient antimicrobial activity and high biocompatibility. Therefore, these carbon-based nanomaterials offer more potential for the elimination of various bacterial infections with negligible cytotoxicity and excellent biocompatibility.
Carbon quantum dots (CQDs), a new type of zero-dimensional carbon-based nanomaterial, exhibit intriguing properties, such as photostability, great environmental sustainability, high water dispersibility, easy synthesis, low production cost, and low toxicity, as well as good biocompatibility [12][13][14][15]. These characteristics mean that CQDs are excellent candidates for use as optical nanoprobes for chemical analysis [16,17], and for fingerprint imaging [18], biosensors [19,20], fluorescent labeling, and bioimaging [21,22]. Recently, numerous studies on CQDs with antibacterial activity have been reported. Huang et al. reported that super-cationic CQDs possessed strong antibacterial activities against multidrugresistant bacteria and superior efficacy in treating eye-related bacterial infections [23]. Qu et al. reported that various surface-charged carbon dots induced programmed bacterial death and systematically analyzed the apoptosis mechanisms of E. coli cells [24]. Kang et al. developed a series of cationic carbon dots, which can selectively kill Gram-positive bacteria via electrostatic interaction, with a greater positive charge showing stronger the antibacterial ability [25]. Among them, the most positively charged CQDs have shown a considerable capacity for the inhibition of bacterial growth due to their strong antibacterial effect by interacting with the negatively charged components of bacterial cell walls. Therefore, it is critical to regulate the surface charge and to synthesize CQDs with a controllable positive charge.
Inspired by these superior properties and the potential applications, more researchers have focused on the preparation of positively charged CQDs. The heteroatoms, such as nitrogen (N) and boron (B), when used in the doping of CQDs, can effectively tune the electronic energy level and affect certain intrinsic chemical properties of CQDs, which has attracted growing interest from researchers [20,26,27]. The N atom has been widely used for chemical doping in CQDs because of its five valence electrons strongly bonding with carbon atoms [28,29]. Although the phosphorus (P) atom is larger than the carbon atom, it can work as an n-type donor to alter the electronic characteristics of CQDs [30,31]. Thus, in order to create more active electronic sites, the P atom is used as a heteroatom to synthesize the CQDs in our work, which could produce unanticipated and exceptional antibacterial effects.
In this work, the P-doped CQDs derived from m-aminophenol and phosphoric acid were first prepared by one-step hydrothermal treatment. In vitro cytotoxicity analyses revealed the good biocompatibility of P-doped CQDs. Importantly, the as-prepared Pdoped CQDs showed excellent inhibitory effects on Escherichia coli (E. coli, Gram-negative bacteria) and Staphylococcus aureus (S. aureus, Gram-positive bacteria). Furthermore, the cell walls of the bacteria were broken after P-doped CQD treatment, and the zeta potential of P-doped CQDs was +23.1 mV. Thus, the antibacterial mechanism of P-doped CQDs may be attributed to the electrostatic interaction between the surface charge of P-doped CQDs and bacterial cell walls (Scheme 1).
as well as good biocompatibility [12][13][14][15]. These characteristics mean that CQDs are excellent candidates for use as optical nanoprobes for chemical analysis [16,17], and for fingerprint imaging [18], biosensors [19,20], fluorescent labeling, and bioimaging [21,22]. Recently, numerous studies on CQDs with antibacterial activity have been reported. Huang et al. reported that super-cationic CQDs possessed strong antibacterial activities against multidrug-resistant bacteria and superior efficacy in treating eye-related bacterial infections [23]. Qu et al. reported that various surface-charged carbon dots induced programmed bacterial death and systematically analyzed the apoptosis mechanisms of E. coli cells [24]. Kang et al. developed a series of cationic carbon dots, which can selectively kill Gram-positive bacteria via electrostatic interaction, with a greater positive charge showing stronger the antibacterial ability [25]. Among them, the most positively charged CQDs have shown a considerable capacity for the inhibition of bacterial growth due to their strong antibacterial effect by interacting with the negatively charged components of bacterial cell walls. Therefore, it is critical to regulate the surface charge and to synthesize CQDs with a controllable positive charge.
Inspired by these superior properties and the potential applications, more researchers have focused on the preparation of positively charged CQDs. The heteroatoms, such as nitrogen (N) and boron (B), when used in the doping of CQDs, can effectively tune the electronic energy level and affect certain intrinsic chemical properties of CQDs, which has attracted growing interest from researchers [20,26,27]. The N atom has been widely used for chemical doping in CQDs because of its five valence electrons strongly bonding with carbon atoms [28,29]. Although the phosphorus (P) atom is larger than the carbon atom, it can work as an n-type donor to alter the electronic characteristics of CQDs [30,31]. Thus, in order to create more active electronic sites, the P atom is used as a heteroatom to synthesize the CQDs in our work, which could produce unanticipated and exceptional antibacterial effects.
In this work, the P-doped CQDs derived from m-aminophenol and phosphoric acid were first prepared by one-step hydrothermal treatment. In vitro cytotoxicity analyses revealed the good biocompatibility of P-doped CQDs. Importantly, the as-prepared Pdoped CQDs showed excellent inhibitory effects on Escherichia coli (E. coli, Gram-negative bacteria) and Staphylococcus aureus (S. aureus, Gram-positive bacteria). Furthermore, the cell walls of the bacteria were broken after P-doped CQD treatment, and the zeta potential of P-doped CQDs was +23.1 mV. Thus, the antibacterial mechanism of P-doped CQDs may be attributed to the electrostatic interaction between the surface charge of P-doped CQDs and bacterial cell walls (Scheme 1). Scheme 1. Illustration of the synthesis of P-doped CQDs by one-step hydrothermal treatment for the effective killing of E. coli and S. aureus bacteria.

Materials
M-aminophenol (≥98%) was purchased from the Aladdin Reagent Co. Ltd. (Shanghai, China). A Britton-Robinson (BR) buffer and sodium chloride (NaCl) solution were prepared and adjusted to control the acidity and the ionic strength. Ultra-pure water (18.2 Scheme 1. Illustration of the synthesis of P-doped CQDs by one-step hydrothermal treatment for the effective killing of E. coli and S. aureus bacteria. purified by a Millipore water purification system (Milli-Q, Millipore, Billerica, MA, USA), was used for the preparation of all solutions.

Apparatus
All fluorescence spectra were acquired using a Shimatzu RF-5301PC fluorescence spectrophotometer (Kyoto, Japan). Transmission electron microscopy (TEM) and highresolution transmission electron microscopy (HRTEM) images were performed on a JEOL 2100F field emission transmission electron microscope (Tokyo, Japan). The thickness of CQDs was characterized using a Dimension Icon Scan Asyst atomic force microscope (AFM, Bruker Co., Karlsruhe, Germany). Elemental and functional group analyses were performed using an ESCALAB Xi + X-ray photoelectron spectrometer (XPS, Thermo Fisher Scientific Inc., Waltham, MA, USA) and a Nicolet iS5 Fourier Transform Infrared spectrometer (FTIR, Thermo Fisher Scientific Inc., Waltham, MA, USA). The Raman spectrum obtained on the Ag substrate (excited by a 532 nm laser) was recorded with a DXR 2xi Raman microscope (Thermo Fisher Scientific Inc., Waltham, MA, USA). The C9920-02G fluorescence spectrophotometer (Hamamatsu Photonics KK, Tokyo, Japan) was used to measure the fluorescence lifetime. Zeta potentials of CQDs were obtained with a Zetasizer Nano ZS90 System (Malvern, UK). The concentration of bacteria was determined by measuring the optical density at 600 nm (OD 600 ) via UV-vis spectroscopy. The morphology of bacteria was observed under a Hitachi S-3400N scanning electron microscope (SEM, Tokyo, Japan).

Preparation of the P-Doped CQDs
The P-doped CQDs were prepared by one-step hydrothermal treatment using maminophenol and phosphoric acid. Briefly, 0.10 g m-aminophenol and 1 ml phosphoric acid was first dispersed in 4.0 mL ultrapure water, and 5.0 mL of the mixture was added into a 25 mL teflon-lined autoclave and then kept at 200 • C for 48 h. Once cooled to room temperature naturally, the resultants were centrifuged at 6000 rpm for 5 min and then the supernatant was filtered with BIOSHARP membrane filters (0.22 µm) to remove insoluble impurities, and the transparent solution was subjected to dialysis (Mw = 500 Da) for 48 h to eliminate the residual unreacted material. Finally, the purified CQD solution was freeze-dried to obtain solid powder. The product was stored at 4 • C for future experiments.

Cellular Toxicity Test
In Dulbecco's Modified Eagle's Medium (DMEM) supplemented with 10% fetal bovine serum (FBS), 1 × 10 5 cells per mL BV2 microglia cells were plated on a 96-well cell culture plate (100 µL per well) and cultured at 37 • C with 5.0% CO 2 in a humidified incubator for 24 h. The medium was then replaced with 100 µL of DMEM medium supplemented with 2% FBS containing different doses of P-doped CQDs and was incubated for another 24 h. The control was cells without treatment with the P-doped CQDs. After removing the culture medium, a mixture of 10 µL MTT reagent and 90 µL DMEM medium was added to every well, which was washed with PBS buffer three times. The cells were further incubated for 1 h. After removing the culture medium with MTT, 150 µL of DMSO was added and shaken at room temperature for approximately 10 min. The OD was measured at 538 nm. The cell viability was estimated using Equation (1): where OD treated and OD control were the optical density of cells in the presence and absence of CQDs, respectively.

MIC Test
E. coli and S. aureus were cultured in Luria-Bertan (LB) liquid medium at 37 • C shaking at 180 rpm overnight. Bacteria were diluted to a concentration of 1.5 × 10 7 CFU/mL. A measure of 50 µL of diluted bacterial suspension and 50 µL of various concentrations of P-doped CQDs were transferred to a 96-well cell culture plate for a final volume of 100 µL/well. Bacterial suspension in an LB medium without the P-doped CQDs was used as the control, and only LB medium was used as the blank. The mixtures were incubated at 37 • C for 12 h. At the end of incubation, the concentration of bacteria was determined by measuring OD 600 .
2.6. SEM Images for Bacteria E. coli and S. aureus were incubated with the as-prepared P-doped CQDs for 4 h. Bacteria without the P-doped CQDs treatment were used as the control groups. The cells were centrifuged at 8000 rpm for 10 min at 4 • C and the precipitation was washed with phosphate-buffered solution (PBS, pH = 7.4). The cells were fixed with 5% glutaraldehyde for 2 h at 4 • C. The bacteria were soaked in a dehydration solution with different concentrations of alcohol (30%, 50%, 70%, 85%, 95%, 100%), which were dried by vacuum and sputter-coated with gold. The samples were observed under a Hitachi S-3400N scanning electron microscope.

Characterizations of the P-Doped CQDs
The TEM image (Figure 1a) shows that the size of P-doped CQDs was distributed in the range from 2.75 nm to 4.25 nm with an average diameter of 3.4 nm. The HRTEM image (inset of Figure 1a) shows 0.21 nm of in-plane lattice spacings ([100] facet), revealing a typical graphite-like structure formed during the synthesis of P-doped CQDs [25,32]. The AFM image (Figure 1b) shows that the topographic height of the P-doped CQDs varied mostly from 2.7 nm to 3.8 nm, which was similar to the TEM characterization, indicating that the P-doped CQDs had a nearly spherical morphology.

MIC Test
E. coli and S. aureus were cultured in Luria-Bertan (LB) liquid medium at 37 °C shak ing at 180 rpm overnight. Bacteria were diluted to a concentration of 1.5 × 10 7 CFU/mL. measure of 50 μL of diluted bacterial suspension and 50 μL of various concentrations o P-doped CQDs were transferred to a 96-well cell culture plate for a final volume of 10 μL/well. Bacterial suspension in an LB medium without the P-doped CQDs was used a the control, and only LB medium was used as the blank. The mixtures were incubated a 37 °C for 12h. At the end of incubation, the concentration of bacteria was determined b measuring OD600.

SEM Images for Bacteria
E. coli and S. aureus were incubated with the as-prepared P-doped CQDs for 4 h. Ba teria without the P-doped CQDs treatment were used as the control groups. The cells wer centrifuged at 8000 rpm for 10 min at 4 °C and the precipitation was washed with pho phate-buffered solution (PBS, pH = 7.4). The cells were fixed with 5% glutaraldehyde fo 2 h at 4 °C. The bacteria were soaked in a dehydration solution with different concentra tions of alcohol (30%, 50%, 70%, 85%, 95%, 100%), which were dried by vacuum and spu ter-coated with gold. The samples were observed under a Hitachi S-3400N scanning ele tron microscope.

Characterizations of the P-Doped CQDs
The TEM image (Figure 1a) shows that the size of P-doped CQDs was distributed i the range from 2.75 nm to 4.25 nm with an average diameter of 3.4 nm. The HRTEM imag (inset of Figure 1a) shows 0.21 nm of in-plane lattice spacings ([100] facet), revealing typical graphite-like structure formed during the synthesis of P-doped CQDs [25,32]. Th AFM image (Figure 1b) shows that the topographic height of the P-doped CQDs varie mostly from 2.7 nm to 3.8 nm, which was similar to the TEM characterization, indicatin that the P-doped CQDs had a nearly spherical morphology.  The P-doped CQDs had unique absorption and emission abilities. As shown in Figure 1c, the P-doped CQDs had a strong absorption band at 257 nm and a broad absorption band characterized at 384 nm owing to the π→π * transition of C=C and the n→π * transition of the surface groups, respectively. The maximum emission peak was located at 501 nm with a maximum excitation at 429 nm. The fluorescence emission of P-doped CQDs was independent with the excitation wavelength ranging from 300 nm to 460 nm ( Figure S1a). In addition, the absolute quantum yield (QY) of P-doped CQDs was approximately 14.4%. The average fluorescence lifetime of P-doped CQDs was calculated as 3.9 ns ( Figure S1b).
In order to understand the functional group composition and structures of P-doped CQDs, Raman spectra, FTIR spectra, and XPS were measured. The Raman spectrum (Figure 1d) illustrated two narrow peaks, a G-line peak at around 1595 cm −1 and a D-line peak at around 1387 cm −1 , which was attributed, respectively, to sp 2 hybridized carbon and sp 3 hybridized carbon in the P-doped CQDs. The FTIR spectra (Figure 2a [16,26,33]. The FTIR spectrum revealed that the P-doped CQDs had abundant carboxyl, hydroxy, and amino functional groups, and that P had indeed been doped into the P-doped CQDs in the synthesis process. The XPS full spectrum of P-doped CQDs (Figure 2b) presented five dominant peaks of C 1s at 283.7 eV, O 1s at 533.5 eV, N 1s at 401.3 eV, and P 2s and P 2p at 191.5 eV and 133.5 eV, respectively, further indicating the successful incorporation of the P element into the Pdoped CQDs [26,30]. The elemental analysis showed the composition of C 20.15%, O 60.64%, N 3.48%, and P 15.72%, in the as-prepared P-doped CQDs. The high-resolution C 1s spectra of P-doped CQDs (Figure 2c) was divided into three peaks at 284.3, 285.7, and 288.6 eV, corresponding to C=C/C-C, C-O/C-N/C-P, and C=O, respectively [20,34]. Highresolution N 1s spectra of P-doped CQDs (Figure 2d) showed two peaks at 400.1 and 402.1 eV, which were assigned to pyrrolic N (C-N) and N-H bands, respectively [32]. The bands in the O 1s spectra (Figure 2e) presented two peaks at 531.3 and 532.8 eV, attributed to C=O and C-O/P=O, respectively [35]. The high-resolution P 2p spectra (Figure 2f) revealed the existence of P=O (134.2 eV) and P=C (135.3 eV) [36]. As shown by the results of FTIR and XPS, the as-prepared P-doped CQDs had abundant functional groups, including -COOH, -OH, and a small number of N, P-containing groups. ure 1c, the P-doped CQDs had a strong absorption band at 257 nm and a broad absorption band characterized at 384 nm owing to the π→π * transition of C = C and the n→π * transition of the surface groups, respectively. The maximum emission peak was located at 501 nm with a maximum excitation at 429 nm. The fluorescence emission of P-doped CQDs was independent with the excitation wavelength ranging from 300 nm to 460 nm ( Figure  S1a). In addition, the absolute quantum yield (QY) of P-doped CQDs was approximately 14.4%. The average fluorescence lifetime of P-doped CQDs was calculated as 3.9 ns (Figure S1b).
In order to understand the functional group composition and structures of P-doped CQDs, Raman spectra, FTIR spectra, and XPS were measured. The Raman spectrum (Figure 1d) illustrated two narrow peaks, a G-line peak at around 1595 cm −1 and a D-line peak at around 1387 cm −1 , which was attributed, respectively, to sp 2 hybridized carbon and sp 3 hybridized carbon in the P-doped CQDs. The FTIR spectra (Figure 2a [16,26,33]. The FTIR spectrum revealed that the P-doped CQDs had abundant carboxyl, hydroxy, and amino functional groups, and that P had indeed been doped into the P-doped CQDs in the synthesis process. The XPS full spectrum of P-doped CQDs (Figure 2b) presented five dominant peaks of C 1s at 283.7 eV, O 1s at 533.5 eV, N 1s at 401.3 eV, and P 2s and P 2p at 191.5 eV and 133.5 eV, respectively, further indicating the successful incorporation of the P element into the P-doped CQDs [26,30]. The elemental analysis showed the composition of C 20.15%, O 60.64%, N 3.48%, and P 15.72%, in the as-prepared P-doped CQDs. The high-resolution C 1s spectra of P-doped CQDs (Figure 2c) was divided into three peaks at 284.3, 285.7, and 288.6 eV, corresponding to C = C/C-C, C-O/C-N/C-P, and C = O, respectively [20,34]. High-resolution N 1s spectra of P-doped CQDs (Figure 2d) showed two peaks at 400.1 and 402.1 eV, which were assigned to pyrrolic N (C-N) and N-H bands, respectively [32]. The bands in the O 1s spectra (Figure 2e) presented two peaks at 531.3 and 532.8 eV, attributed to C = O and C-O/P = O, respectively [35]. The high-resolution P 2p spectra (Figure 2f) revealed the existence of P = O (134.2 eV) and P = C (135.3 eV) [36]. As shown by the results of FTIR and XPS, the asprepared P-doped CQDs had abundant functional groups, including -COOH, -OH, and a small number of N, P-containing groups.

Stability of the As-Prepared P-Doped CQDs
In order to determine the stability of P-doped CQDs, a series of experiments were designed. The P-doped CQDs showed excellent photostability under continuous Xe lamp illumination (429 nm) for 60 min ( Figure S2a). The fluorescence intensity of P-doped CQDs was pH-independent in the BR pH range 2.09-11.92 ( Figure S2b). The fluorescence retained 78% of the initial intensity after incubation with 2.0 M NaCl ( Figure S2c), illustrating that the P-doped CQDs were stable in a medium of high ionic strength and not aggregated in this medium. The fluorescence intensity of P-doped CQDs slightly decreased when the concentrations of H 2 O 2 were as high as 500 mM (Figure S2d), indicating that the P-doped CQDs had good antioxidation. These results indicate that the as-prepared P-doped CQDs have great potential in the application of fluorescent nanoprobes for complex matrixes.

Cellular Toxicity and Confocal Microscopy Imaging of the P-Doped CQDs
The cytotoxicity of P-doped CQDs was evaluated by the MTT method using BV2 microglioma cells. The cell viability changed slightly after 24 h incubation with a relatively high concentration of P-doped CQDs (500 µg/mL) (Figure 3a), suggesting that the CQDs had good biocompatibility. To explore the potential application of P-doped CQDs in bioimaging, cellular imaging was investigated through a confocal fluorescence microscope. The confocal image showed that the P-doped CQDs were dispersed in the cytoplasmic and nuclear area (Figure 3b), indicating that the P-doped CQDs can be applied for cytoplasmic and nuclear staining and labelling.

Stability of the As-Prepared P-Doped CQDs
In order to determine the stability of P-doped CQDs, a series of experiments designed. The P-doped CQDs showed excellent photostability under continuous Xe l illumination (429 nm) for 60 min ( Figure S2a). The fluorescence intensity of P-doped C was pH-independent in the BR pH range 2.09-11.92 ( Figure S2b). The fluorescenc tained 78% of the initial intensity after incubation with 2.0 M NaCl ( Figure S2c), illus ing that the P-doped CQDs were stable in a medium of high ionic strength and not ag gated in this medium. The fluorescence intensity of P-doped CQDs slightly decre when the concentrations of H2O2 were as high as 500 mM (Figure S2d), indicating tha P-doped CQDs had good antioxidation. These results indicate that the as-prepare doped CQDs have great potential in the application of fluorescent nanoprobes for plex matrixes.

Cellular Toxicity and Confocal Microscopy Imaging of the P-Doped CQDs
The cytotoxicity of P-doped CQDs was evaluated by the MTT method using BV croglioma cells. The cell viability changed slightly after 24 h incubation with a relat high concentration of P-doped CQDs (500 μg/mL) (Figure 3a), suggesting that the C had good biocompatibility. To explore the potential application of P-doped CQDs i oimaging, cellular imaging was investigated through a confocal fluorescence microsc The confocal image showed that the P-doped CQDs were dispersed in the cytopla and nuclear area (Figure 3b), indicating that the P-doped CQDs can be applied for plasmic and nuclear staining and labelling.

Antibacterial Activity of the P-Doped CQDs
The antibacterial activity of P-doped CQDs was explored with E. coli and S. au as the model pathogens of Gram-negative and Gram-positive bacteria, respectively. E amounts of 1.5 × 10 7 CFU/mL bacterial suspension were treated with different conce tions (0, 0.41, 0.82, 1.23, 1.44, 1.64, 1.84, 2.05 mg/mL) of P-doped CQDs. The bacteria bility was evaluated by recording OD600 values of the bacterial mixture. The re showed that the viability of E. coli and S. aureus decreased with the increasing conce tion of P-doped CQDs (Figure S3a,b; Table S1,2). When the concentration of P-d CQDs was up to 1.23 and 1.44 mg/mL, respectively, the OD600 values were almost sistent with that of the blank group, indicating that the P-doped CQDs had signif antibacterial abilities with MIC values of P-doped CQDs of 1.23 mg/mL on E. coli and mg/mL on S. aureus. Furthermore, the P-doped CQDs could effectively inhibit Gramative and Gram-positive bacteria on a time-dependent basis at different doses (Fi 4a,b).

Antibacterial Activity of the P-Doped CQDs
The antibacterial activity of P-doped CQDs was explored with E. coli and S. aureus, as the model pathogens of Gram-negative and Gram-positive bacteria, respectively. Equal amounts of 1.5 × 10 7 CFU/mL bacterial suspension were treated with different concentrations (0, 0.41, 0.82, 1.23, 1.44, 1.64, 1.84, 2.05 mg/mL) of P-doped CQDs. The bacterial viability was evaluated by recording OD 600 values of the bacterial mixture. The results showed that the viability of E. coli and S. aureus decreased with the increasing concentration of P-doped CQDs (Figure S3a,b; Tables S1 and S2). When the concentration of P-doped CQDs was up to 1.23 and 1.44 mg/mL, respectively, the OD 600 values were almost consistent with that of the blank group, indicating that the P-doped CQDs had significant antibacterial abilities with MIC values of P-doped CQDs of 1.23 mg/mL on E. coli and 1.44 mg/mL on S. aureus. Furthermore, the P-doped CQDs could effectively inhibit Gram-negative and Gram-positive bacteria on a time-dependent basis at different doses (Figure 4a,b).

Antibacterial Mechanism of P-Doped CQDs
To further explore the mechanism, the morphologies of bacteria, before and aft doped CQDs treatment, were observed by SEM. E. coli and S. aureus were incubated the P-doped CQDs (1.23 mg/mL and 1.44 mg/mL) for 4 h. It was obvious that the inte of E. coli without the P-doped CQDs treatment was kept well, while the cell walls of E with the P-doped CQDs treatment were wrinkled and broken (Figure 6a,b). Similarly cell walls of S. aureus incubated without the P-doped CQDs were intact and smooth, w the cell surfaces of S. aureus incubated with the P-doped CQDs became damaged, some cytoplasm exudated from the cells (Figure 6c,d). Furthermore, zeta potential a sis (Figure 7) showed that the P-doped CQDs were positively charged (+23.1 mV), a coli (−11.6 mV) and S. aureus (−16.0 mV) were negatively charged. The zeta potential slightly more positive (−7.7 mV for E. coli and −8.8 mV for S. aureus) after the bacteria treated with the P-doped CQDs, indicating that the positively charged P-doped C were likely to be bonded with the bacteria by electrostatic interaction, ultimately resu in the cell walls being disturbed and the death of the bacteria.

Antibacterial Mechanism of P-Doped CQDs
To further explore the mechanism, the morphologies of bacteria, before and aft doped CQDs treatment, were observed by SEM. E. coli and S. aureus were incubated the P-doped CQDs (1.23 mg/mL and 1.44 mg/mL) for 4 h. It was obvious that the inte of E. coli without the P-doped CQDs treatment was kept well, while the cell walls of E with the P-doped CQDs treatment were wrinkled and broken (Figure 6a,b). Similarly cell walls of S. aureus incubated without the P-doped CQDs were intact and smooth, w the cell surfaces of S. aureus incubated with the P-doped CQDs became damaged, some cytoplasm exudated from the cells (Figure 6c,d). Furthermore, zeta potential an sis (Figure 7) showed that the P-doped CQDs were positively charged (+23.1 mV), an coli (−11.6 mV) and S. aureus (−16.0 mV) were negatively charged. The zeta potential slightly more positive (−7.7 mV for E. coli and −8.8 mV for S. aureus) after the bacteria treated with the P-doped CQDs, indicating that the positively charged P-doped C were likely to be bonded with the bacteria by electrostatic interaction, ultimately resu in the cell walls being disturbed and the death of the bacteria.

Antibacterial Mechanism of P-Doped CQDs
To further explore the mechanism, the morphologies of bacteria, before and after P-doped CQDs treatment, were observed by SEM. E. coli and S. aureus were incubated with the P-doped CQDs (1.23 mg/mL and 1.44 mg/mL) for 4 h. It was obvious that the integrity of E. coli without the P-doped CQDs treatment was kept well, while the cell walls of E. coli with the P-doped CQDs treatment were wrinkled and broken (Figure 6a,b). Similarly, the cell walls of S. aureus incubated without the P-doped CQDs were intact and smooth, while the cell surfaces of S. aureus incubated with the P-doped CQDs became damaged, with some cytoplasm exudated from the cells (Figure 6c,d). Furthermore, zeta potential analysis (Figure 7) showed that the P-doped CQDs were positively charged (+23.1 mV), and E. coli (−11.6 mV) and S. aureus (−16.0 mV) were negatively charged. The zeta potential was slightly more positive (−7.7 mV for E. coli and −8.8 mV for S. aureus) after the bacteria were treated with the P-doped CQDs, indicating that the positively charged P-doped CQDs were likely to be bonded with the bacteria by electrostatic interaction, ultimately resulting in the cell walls being disturbed and the death of the bacteria.

Conclusions
In summary, we have prepared P-doped CQDs with m-aminophenol as a carbo source and phosphoric acid as a phosphorus source by a facile hydrothermal method Based on surface functional group analyses of the as-prepared P-doped CQDs by FTI and XPS, the P-doped CQDs were successfully doped with phosphorus. The as-prepare P-doped CQDs have high photostability and environmental stability. Furthermore, the P doped CQDs exhibit a strong inhibitory effect on Gram-negative bacteria (E. coli) an Gram-positive bacteria (S. aureus) with MIC at 1.23 mg/mL and 1.44 mg/mL, respectively The Zeta potential measurements indicate that a strong electrostatic interaction betwee the negatively charged bacteria and the positively charged P-doped CQDs causes th wrinkled and damaged bacteria. This work is of great significance for the development o antibacterial nanomaterials as promising alternative antibacterial agents.  Table S1: OD values of E. coli treated with different concentrations of P doped CQDs. Table S2: OD values of S. aureus treated with different concentrations of P-dope

Conclusions
In summary, we have prepared P-doped CQDs with m-aminophenol as a carbon source and phosphoric acid as a phosphorus source by a facile hydrothermal method Based on surface functional group analyses of the as-prepared P-doped CQDs by FTIR and XPS, the P-doped CQDs were successfully doped with phosphorus. The as-prepared P-doped CQDs have high photostability and environmental stability. Furthermore, the Pdoped CQDs exhibit a strong inhibitory effect on Gram-negative bacteria (E. coli) and Gram-positive bacteria (S. aureus) with MIC at 1.23 mg/mL and 1.44 mg/mL, respectively The Zeta potential measurements indicate that a strong electrostatic interaction between the negatively charged bacteria and the positively charged P-doped CQDs causes the wrinkled and damaged bacteria. This work is of great significance for the development of antibacterial nanomaterials as promising alternative antibacterial agents.
Supplementary Materials: The following are available online at www.mdpi.com/arti cle/10.3390/mi12091116/s1: Figure S1. (a) Fluorescent emission spectra of P-doped CQDs under dif ferent excitation wavelengths from 300 to 460 nm, (b) fluorescence lifetime of P-doped CQDs; Figure  S2. Fluorescent spectra of P-doped CQDs at (a) different incubation times, (b) pH solutions, (c) dif ferent concentration of NaCl, (d) H2O2; Figure S3: The antibacterial ability of P-doped CQDs on (a E. coli and (b) S. aureus. Table S1: OD values of E. coli treated with different concentrations of P doped CQDs. Table S2: OD values of S. aureus treated with different concentrations of P-doped

Conclusions
In summary, we have prepared P-doped CQDs with m-aminophenol as a carbon source and phosphoric acid as a phosphorus source by a facile hydrothermal method. Based on surface functional group analyses of the as-prepared P-doped CQDs by FTIR and XPS, the P-doped CQDs were successfully doped with phosphorus. The as-prepared P-doped CQDs have high photostability and environmental stability. Furthermore, the P-doped CQDs exhibit a strong inhibitory effect on Gram-negative bacteria (E. coli) and Gram-positive bacteria (S. aureus) with MIC at 1.23 mg/mL and 1.44 mg/mL, respectively. The Zeta potential measurements indicate that a strong electrostatic interaction between the negatively charged bacteria and the positively charged P-doped CQDs causes the wrinkled and damaged bacteria. This work is of great significance for the development of antibacterial nanomaterials as promising alternative antibacterial agents.