Comparison of Argon and Oxygen Plasma Treatments for Ambient Room-Temperature Wafer-Scale Au–Au Bonding Using Ultrathin Au Films

Au–Au surface activated bonding is promising for room-temperature bonding. The use of Ar plasma vs. O2 plasma for pretreatment was investigated for room-temperature wafer-scale Au–Au bonding using ultrathin Au films (<50 nm) in ambient air. The main difference between Ar plasma and O2 plasma is their surface activation mechanism: physical etching and chemical reaction, respectively. Destructive razor blade testing revealed that the bonding strength of samples obtained using Ar plasma treatment was higher than the strength of bulk Si (surface energy of bulk Si: 2.5 J/m2), while that of samples obtained using O2 plasma treatment was low (surface energy: 0.1–0.2 J/m2). X-ray photoelectron spectroscopy analysis revealed that a gold oxide (Au2O3) layer readily formed with O2 plasma treatment, and this layer impeded Au–Au bonding. Thermal desorption spectroscopy analysis revealed that Au2O3 thermally desorbed around 110 °C. Annealing of O2 plasma-treated samples up to 150 °C before bonding increased the bonding strength from 0.1 to 2.5 J/m2 due to Au2O3 decomposition.


Introduction
Low-temperature wafer bonding is increasingly required due to the increasing use of heterogeneous integrations [1][2][3]. An effective approach to such bonding is to use intermediate layers [4,5]. Gold (Au) is a good candidate material for these bonding layers because of its high electrical and thermal conductivity, good deformability, and high oxidation resistance.
While Ar plasma is commonly used to activate Au surfaces by physically bombarding them with Ar ions or atoms, O 2 plasma is commonly used to clean surfaces because it can eliminate organic contaminants by chemical reaction [21,22]. It is also used for pretreatment before Au-Au bonding; O 2 plasma treatment has been reported to more effectively improve Au wire bond interfacial adhesion than Ar plasma treatment [23,24]. However, the Au-Au bonding may be weakened by the mixing of O 2 gas into the plasma processing gas [25,26]. The effect of plasma treatment, and especially the effect of O 2 plasma treatment on Au-Au bonding, thus needs further investigation.
This paper reports the investigation of Ar plasma vs. O 2 plasma as a pretreatment method for room-temperature wafer-scale Au-Au bonding using ultrathin Au films (<50 nm) in ambient air. The main difference between Ar plasma and O 2 plasma is their surface activation mechanism: physical etching and chemical reaction, respectively. The investigation included an analysis of Au surfaces treated with Ar or O 2 plasma.

Materials and Methods
Silicon substrates with Au film and a Ti adhesion layer were used for analysis and bonding. A Ti adhesion layer followed by Au thin film was deposited on a Si substrate or a thermally oxidized Si substrate by direct current (DC) sputtering at a substrate temperature of 25 • C. The Ar or O 2 plasma used to activate the surfaces was generated by applying 200 W radio frequency (RF) power at 60 Pa. Both plasmas were generated using the same equipment; only the process gas was changed.
The effect of each plasma treatment on the surface properties was determined by evaluating the surface roughness, hydrophilicity, electrical characteristics, and chemical state of the Au surfaces before and after each treatment. Surface roughness was measured using an atomic force microscope (AFM, Hitachi High-Tech Science Co., Tokyo, Japan, L-trace) and Si wafers with Au thin film (thickness: 15 nm) and a Ti adhesion layer (thickness: 5 nm). The AFM measurement was performed with a scan area of 500 nm × 500 nm and a resolution of 256 × 256 pixels. Hydrophilicity was evaluated by measuring the contact angle of the Au surfaces as measured with a contact angle meter (Kyowa Interface Science Co, Ltd., Saitama, Japan, PCA-11). Pure water (1.5 µL) was dropped on the Au surfaces, and the contact angle was calculated using the half-angle method. The electrical characteristics were evaluated by four-point measurement of the sheet resistance using a resistivity processor (NPS Inc., Tokyo, Japan, Model Σ) and Si wafers with Au thin film (thickness: 15 nm) and a Ti adhesion layer (thickness: 5 nm). The effect of the plasma treatment time was measured by irradiating plasma onto the same wafer several times. The surface chemical states were determined using X-ray photoelectron spectroscopy (XPS) analysis and thermal desorption spectrometry (TDS) analysis. The XPS analysis was performed using an X-ray photoelectron spectroscope (JEOL Ltd., Tokyo, Japan, JPS9200-T). A non-monochromatic Mg Kα source (photon energy: 1253.6 eV) was used at an operating power of 10 kV × 10 mA. Smoothing, Shirley-type background subtraction, and charge correction using the Au 4f 7/2 binding energy were performed. The TDS analysis was performed using a thermal desorption spectrometer (ESCO Ltd., Tokyo, Japan, EMD-WA1000S). Thicker Au films (thickness: 300 nm) with Ti adhesion layers (thickness: 5 nm) deposited on thermally oxidized Si substrates were used to avoid the effect of diffusion from the adhesion layer or Si substrate during annealing. The temperature was increased at a rate of 30 • C/min and was corrected by measurement using a dummy Si substrate.
Four-inch Si wafers with Au thin film (thickness: 15 nm) and a Ti adhesion layer (thickness: 5 nm) were bonded after Ar or O 2 plasma treatment in ambient air by overlapping two wafers and pinching the wafers together with tweezers. Bond front propagation was observed using an infrared (IR) transmission setup. The effects of plasma treatment time and air exposure time after plasma treatment on self-propagation of the bonding area and on bonding strength were investigated. The effects of annealing before bonding on the self-propagation of the bonding area and on bonding strength were also investigated by annealing wafers that had been plasma-treated up to 150 • C for 10 min in vacuum and then bonding them together in ambient air at room temperature.
Bonding strength was measured using destructive razor blade testing, also known as the crack opening or double cantilever beam method [27,28]. This testing method is an effective way to evaluate the energy of the bonded surfaces (i.e., surface energy). It is performed by inserting a razor blade between the bonded wafer pairs and observing the crack length along the bonded interface. The surface energy γ (J/m 2 ) (i.e., half the bonding energy G) was calculated under plane strain conditions and the assumptions of beam theory using where E (Pa) is the Young's modulus of the wafer, T b (m) is the blade thickness, T w (m) is the wafer thickness, and L (m) is the crack length [27]. In this experiment, Si substrates with a thickness of 525 µm and a blade with a thickness of 100 µm were used. For calculation, we assumed that Si is isotropic, with Young's modulus of elasticity E = 169 GPa [29,30]. Although the measurement should be conducted using beam-shaped samples in order to accurately determine the surface energy [31], we used whole bonded wafer pairs because the fabrication of beam-shaped samples is particularly difficult for weakly bonded wafer pairs. The crack length along the bonded interface was observed with an IR camera in a standard clean room atmosphere. Since values obtained from Equation (1) are affected by the crack detection resolution, anisotropic mechanical properties, and humidity environment [28,30], the comparison of absolute energy values with published results requires careful consideration.

AFM Measurement
The measured RMS surface roughness for different plasma treatment times (30, 60, 120 s) are plotted in Figure 1. The roughness before plasma treatment was 0.38 nm. Both the Ar and O 2 plasma treatments of 60 s or less had little effect on surface roughness, while both treatments of 120 s increased it. This indicates that a short plasma treatment time is important for achieving low-temperature bonding. Bonding strength was measured using destructive razor blade testing, also known as the crack opening or double cantilever beam method [27,28]. This testing method is an effective way to evaluate the energy of the bonded surfaces (i.e., surface energy). It is performed by inserting a razor blade between the bonded wafer pairs and observing the crack length along the bonded interface. The surface energy γ (J/m 2 ) (i.e., half the bonding energy G) was calculated under plane strain conditions and the assumptions of beam theory using where E (Pa) is the Young's modulus of the wafer, Tb (m) is the blade thickness, Tw (m) is the wafer thickness, and L (m) is the crack length [27]. In this experiment, Si substrates with a thickness of 525 µm and a blade with a thickness of 100 µm were used. For calculation, we assumed that Si is isotropic, with Young's modulus of elasticity E = 169 GPa [29,30]. Although the measurement should be conducted using beam-shaped samples in order to accurately determine the surface energy [31], we used whole bonded wafer pairs because the fabrication of beam-shaped samples is particularly difficult for weakly bonded wafer pairs. The crack length along the bonded interface was observed with an IR camera in a standard clean room atmosphere. Since values obtained from Equation (1) are affected by the crack detection resolution, anisotropic mechanical properties, and humidity environment [28,30], the comparison of absolute energy values with published results requires careful consideration.

AFM Measurement
The measured RMS surface roughness for different plasma treatment times (30, 60, 120 s) are plotted in Figure 1. The roughness before plasma treatment was 0.38 nm. Both the Ar and O2 plasma treatments of 60 s or less had little effect on surface roughness, while both treatments of 120 s increased it. This indicates that a short plasma treatment time is important for achieving lowtemperature bonding.

Contact Angle Measurement
The measured contact angles for different plasma treatment times (30, 60, 120 s) are shown in Figure 2. The Au films had been exposed to air for over 1 month, and the measurement was performed immediately after plasma treatment. Typical images of the measured contact angle are shown in Figure 3. Figures 3b and 3c were taken 30 s after plasma treatment. Before treatment, the contact angle was about 80-100°, and the Au surfaces were hydrophobic. Both treatments reduced the contact angle, which means that the Au surfaces became hydrophilic with plasma treatment. The

Contact Angle Measurement
The measured contact angles for different plasma treatment times (30, 60, 120 s) are shown in Figure 2. The Au films had been exposed to air for over 1 month, and the measurement was performed immediately after plasma treatment. Typical images of the measured contact angle are shown in Figure 3. Figure 3b,c was taken 30 s after plasma treatment. Before treatment, the contact angle was about 80-100 • , and the Au surfaces were hydrophobic. Both treatments reduced the contact angle, which means that the Au surfaces became hydrophilic with plasma treatment. The contact angle for Au surfaces with O 2 plasma treatment was less than 5 • , which is smaller than that with Ar plasma treatment. The treatment times were the same.
contact angle for Au surfaces with O2 plasma treatment was less than 5°, which is smaller than that with Ar plasma treatment. The treatment times were the same.
The changes in the contact angle with the air exposure time after Au film deposition and after plasma treatment are plotted in Figure 4. Previous studies reported that Au film is hydrophilic immediately after deposition and that the Au surface quickly becomes hydrophobic after exposure in air [32,33]. The measured change in the contact angle after deposition agrees well with the results of previous studies. The contact angles of Au surfaces that received Ar plasma treatment increased rapidly after exposure in air, similar to the results for the Au film immediately after deposition. In contrast, the rate of increase was much lower for Au surfaces that received O2 plasma treatment.   plasma treatment are plotted in Figure 4. Previous studies reported that Au film is hydrophilic immediately after deposition and that the Au surface quickly becomes hydrophobic after exposure in air [32,33]. The measured change in the contact angle after deposition agrees well with the results of previous studies. The contact angles of Au surfaces that received Ar plasma treatment increased rapidly after exposure in air, similar to the results for the Au film immediately after deposition. In contrast, the rate of increase was much lower for Au surfaces that received O2 plasma treatment.    The changes in the contact angle with the air exposure time after Au film deposition and after plasma treatment are plotted in Figure 4. Previous studies reported that Au film is hydrophilic immediately after deposition and that the Au surface quickly becomes hydrophobic after exposure in air [32,33]. The measured change in the contact angle after deposition agrees well with the results of previous studies. The contact angles of Au surfaces that received Ar plasma treatment increased rapidly after exposure in air, similar to the results for the Au film immediately after deposition. In contrast, the rate of increase was much lower for Au surfaces that received O 2 plasma treatment. contact angle for Au surfaces with O2 plasma treatment was less than 5°, which is smaller than that with Ar plasma treatment. The treatment times were the same.
The changes in the contact angle with the air exposure time after Au film deposition and after plasma treatment are plotted in Figure 4. Previous studies reported that Au film is hydrophilic immediately after deposition and that the Au surface quickly becomes hydrophobic after exposure in air [32,33]. The measured change in the contact angle after deposition agrees well with the results of previous studies. The contact angles of Au surfaces that received Ar plasma treatment increased rapidly after exposure in air, similar to the results for the Au film immediately after deposition. In contrast, the rate of increase was much lower for Au surfaces that received O2 plasma treatment.

Sheet Resistance Measurement
The relationship between the measured sheet resistance and the plasma treatment time is plotted in Figure 5. Before plasma treatment, the sheet resistance was about 4.7 Ω. While Ar plasma treatment did not change the resistance, 30 s O 2 plasma treatment increased it to about 5.4 Ω. Additional O 2 plasma treatment time did not increase it.
Micromachines 2019, 10, x 5 of 11 The relationship between the measured sheet resistance and the plasma treatment time is plotted in Figure 5. Before plasma treatment, the sheet resistance was about 4.7 Ω. While Ar plasma treatment did not change the resistance, 30 s O2 plasma treatment increased it to about 5.4 Ω. Additional O2 plasma treatment time did not increase it.

XPS Analysis
The Au surface conditions were evaluated by using XPS analysis to investigate Au surfaces after Ar or O2 plasma treatment. The treatment time was set to 60 s. The relative peak intensities in the Au 4f region are plotted in Figure 6a,b, and the relative peak intensities in the O 1s region are plotted in Figure 6c. The results plotted in (a) show that the Au surfaces that received Ar plasma treatment were pure Au, while those plotted in (b) show that an Au2O3 peak appeared for the Au surfaces that received O2 plasma treatment. The results plotted in (c) show that the O2 plasma treatment increased the oxygen contamination intensity.

XPS Analysis
The Au surface conditions were evaluated by using XPS analysis to investigate Au surfaces after Ar or O 2 plasma treatment. The treatment time was set to 60 s. The relative peak intensities in the Au 4f region are plotted in Figure 6a,b, and the relative peak intensities in the O 1s region are plotted in Figure 6c. The results plotted in (a) show that the Au surfaces that received Ar plasma treatment were pure Au, while those plotted in (b) show that an Au 2 O 3 peak appeared for the Au surfaces that received O 2 plasma treatment. The results plotted in (c) show that the O 2 plasma treatment increased the oxygen contamination intensity. The relationship between the measured sheet resistance and the plasma treatment time is plotted in Figure 5. Before plasma treatment, the sheet resistance was about 4.7 Ω. While Ar plasma treatment did not change the resistance, 30 s O2 plasma treatment increased it to about 5.4 Ω. Additional O2 plasma treatment time did not increase it.

XPS Analysis
The Au surface conditions were evaluated by using XPS analysis to investigate Au surfaces after Ar or O2 plasma treatment. The treatment time was set to 60 s. The relative peak intensities in the Au 4f region are plotted in Figure 6a,b, and the relative peak intensities in the O 1s region are plotted in Figure 6c. The results plotted in (a) show that the Au surfaces that received Ar plasma treatment were pure Au, while those plotted in (b) show that an Au2O3 peak appeared for the Au surfaces that received O2 plasma treatment. The results plotted in (c) show that the O2 plasma treatment increased the oxygen contamination intensity.  Intensity (a.u.) Figure 6. X-ray photoelectron spectroscopy (XPS) spectra of Au surfaces that received different plasma treatments: (a) relative peak intensity in the Au 4f region of surface that received Ar plasma treatment; (b) relative peak intensity in the Au 4f region of surface that received O 2 plasma treatment; (c) relative peak intensities in the O 1s region of surface that received Ar and O 2 plasma treatments.

TDS Analysis
The results of the TDS analysis are plotted in Figure 7. There was little desorption from the Au surface with the Ar plasma treatment. In contrast, with the O 2 plasma treatment, mass-to-charge ratio (m/z) peaks of 16 and 18 were detected at annealing temperatures around 70 • C, and m/z peaks of 16 and 32 were detected at annealing temperatures around 110 • C. Since m/z 16, 18, and 32 correspond to O, H 2 O, and O 2 , it appears that H 2 O was desorbed around 70 • C from the Au surfaces that received O 2 plasma treatment, while O 2 was desorbed around 110 • C.
Micromachines 2019, 10, x 6 of 11 treatment; (b) relative peak intensity in the Au 4f region of surface that received O2 plasma treatment; (c) relative peak intensities in the O 1s region of surface that received Ar and O2 plasma treatments.

TDS Analysis
The results of the TDS analysis are plotted in Figure 7. There was little desorption from the Au surface with the Ar plasma treatment. In contrast, with the O2 plasma treatment, mass-to-charge ratio (m/z) peaks of 16 and 18 were detected at annealing temperatures around 70 °C, and m/z peaks of 16 and 32 were detected at annealing temperatures around 110 °C. Since m/z 16, 18, and 32 correspond to O, H2O, and O2, it appears that H2O was desorbed around 70 °C from the Au surfaces that received O2 plasma treatment, while O2 was desorbed around 110 °C.

Effect of Plasma Treatment Time
To determine the effect of the plasma treatment time, Au-Au bonding with or without plasma treatment was performed. The treatment times were 30 s or 60 s because a longer treatment time increased the surface roughness. Bonding was performed immediately after plasma treatment. Without plasma treatment, bonding front propagation did not occur, and bonding did not succeed. With plasma treatment, bonding front propagation occurred, and bonding succeeded. IR images of typical bond front propagation between two Si wafers for a plasma treatment time of 60 s are shown in in Figure 8. The contrast and brightness of the images were adjusted, and the edges of the bonding area were marked to make it more visible. With Ar plasma treatment, the bonding area quickly expanded across the entire 4-inch wafer after pushing the center. With O2 plasma treatment, the bonding area expanded much more slowly.

Effect of Plasma Treatment Time
To determine the effect of the plasma treatment time, Au-Au bonding with or without plasma treatment was performed. The treatment times were 30 s or 60 s because a longer treatment time increased the surface roughness. Bonding was performed immediately after plasma treatment. Without plasma treatment, bonding front propagation did not occur, and bonding did not succeed. With plasma treatment, bonding front propagation occurred, and bonding succeeded. IR images of typical bond front propagation between two Si wafers for a plasma treatment time of 60 s are shown in in Figure 8. The contrast and brightness of the images were adjusted, and the edges of the bonding area were marked to make it more visible. With Ar plasma treatment, the bonding area quickly expanded across the entire 4-inch wafer after pushing the center. With O 2 plasma treatment, the bonding area expanded much more slowly.
bonding was achieved. With O2 plasma treatment, although much of the area was bonded, the bonding strength (surface energy) was only about 0.1-0.2 J/m 2 , lower than the surface energy of Au (1.6 J/m 2 ) [34]. Debonding thus occurred between the Au-Au bonding interfaces.
Transmission electron microscope (TEM) images of a bonded sample that received Ar plasma treatment are shown in Figure 9. Bonding was achieved at the atomic level, and part of the grain boundary grew beyond the bonding interface.   The results of the destructive razor blade testing are summarized in Table 1. With Ar plasma treatment (30 s and 60 s), the bonding was sufficient to break the substrate, meaning that strong bonding was achieved. With O 2 plasma treatment, although much of the area was bonded, the bonding strength (surface energy) was only about 0.1-0.2 J/m 2 , lower than the surface energy of Au (1.6 J/m 2 ) [34]. Debonding thus occurred between the Au-Au bonding interfaces. Transmission electron microscope (TEM) images of a bonded sample that received Ar plasma treatment are shown in Figure 9. Bonding was achieved at the atomic level, and part of the grain boundary grew beyond the bonding interface.

Effect of Air Exposure
To investigate the effect of air exposure after plasma treatment, bonding was performed after air exposure. The bonding of Au films immediately after deposition was also compared. Because Au films immediately after deposition have clean and activated surfaces, bonding can be performed at room temperature. This bonding technique is usually called atomic diffusion bonding [4,13,14]. The effect of air exposure time on the occurrence of self-propagation of the bonding area and on the bonding strength of atomic diffusion bonding for Au films immediately after deposition is summarized in Table 2. Self-propagation occurred even after 1 h of air exposure. Though the bonding strength decreased as the exposure time increased, sufficient bonding strength (greater than the surface energy of bulk Si (2.5 J/m 2 ) [35]) was obtained even after 1 h of air exposure.
The effect of air exposure time for surface activated bonding is summarized in Table 3. In the cases where self-propagation did not occur, bonding was achieved by pushing the whole wafer with tweezers. With Ar plasma treatment, self-propagation did not occur after 30 min of air exposure. Moreover, the bonding strength greatly decreased as the air exposure time increased. With O2 plasma treatment, while self-propagation occurred even after 1 hour of air exposure, the bonding strength was lower under all conditions.

Effect of Air Exposure
To investigate the effect of air exposure after plasma treatment, bonding was performed after air exposure. The bonding of Au films immediately after deposition was also compared. Because Au films immediately after deposition have clean and activated surfaces, bonding can be performed at room temperature. This bonding technique is usually called atomic diffusion bonding [4,13,14]. The effect of air exposure time on the occurrence of self-propagation of the bonding area and on the bonding strength of atomic diffusion bonding for Au films immediately after deposition is summarized in Table 2. Self-propagation occurred even after 1 h of air exposure. Though the bonding strength decreased as the exposure time increased, sufficient bonding strength (greater than the surface energy of bulk Si (2.5 J/m 2 ) [35]) was obtained even after 1 h of air exposure. The effect of air exposure time for surface activated bonding is summarized in Table 3. In the cases where self-propagation did not occur, bonding was achieved by pushing the whole wafer with tweezers. With Ar plasma treatment, self-propagation did not occur after 30 min of air exposure. Moreover, the bonding strength greatly decreased as the air exposure time increased. With O 2 plasma treatment, while self-propagation occurred even after 1 hour of air exposure, the bonding strength was lower under all conditions. Table 3. Effect of air exposure time on the occurrence of self-propagation of the bonding area and on the bonding strength of surface activated bonding. Here, annealing up to 150 • C after plasma treatment was investigated: Ar or O 2 plasma was irradiated onto Au surfaces for 60 s, and then the wafers were annealed at 150 • C for 10 min in vacuum. After annealing, the wafers were bonded in ambient air at room temperature. The entire annealing process took about one hour.

Types of Plasmas
Self-propagation did not occur in either the Ar or O 2 plasma-treated samples. The wafers were thus bonded by pushing the entire wafers with tweezers. Although the bonding strength of samples that received Ar plasma treatment exceeded the surface energy of bulk Si (2.5 J/m 2 ), the annealing reduced the bonding strength, as evidenced by the breaking of the wafers during blade testing for wafers that had not been annealed. The bonding strength of samples that received O 2 plasma treatment increased substantially (from 0.1 J/m 2 without annealing to 2.5 J/m 2 with annealing). To investigate whether Au 2 O 3 was desorbed, XPS analysis of annealed Au surfaces after O 2 plasma treatment was also performed. The results did not reveal an Au 2 O 3 peak, meaning that Au 2 O 3 formed by O 2 plasma treatment impedes Au-Au bonding. To investigate the change in surface roughness due to annealing, AFM analysis was also performed. The results did not reveal any changes in surface roughness.

Discussion
While Ar plasma treatment improved room-temperature wafer-scale Au-Au bonding strength, O 2 plasma treatment did not. The O 2 plasma treatment reduced the contact angle to less than 5 • and increased the sheet resistance. XPS analysis showed that the O 2 plasma treatment formed Au 2 O 3 on the Au surface. This indicates that the changes in contact angle and sheet resistance were both apparently caused by oxidation of the Au surfaces and that the Au 2 O 3 formed by the O 2 plasma treatment impeded Au-Au bonding.
Because TDS analysis showed that Au 2 O 3 desorbed at around 110 • C, bonding after annealing up to 150 • C was performed. While the bonding strength of samples that received Ar plasma treatment was reduced by the annealing, that of samples that received O 2 plasma treatment was improved from 0.1 to 2.5 J/m 2 . This also demonstrates that the Au 2 O 3 formed by O 2 plasma treatment impeded Au-Au bonding. The decrease in bonding strength with Ar plasma treatment may have been due to the annealing processing time (~1 h).
The effects of air exposure after Au film deposition or plasma treatment on the contact angle and bonding strength were also investigated. The changes in surface hydrophilicity due to contact angle measurement of water on Au surfaces that received Ar plasma treatment were similar to those on Au surfaces immediately after deposition. The bonding strength of samples that were exposed in air following Ar plasma treatment decreased more rapidly than that of samples bonded immediately after deposition. Further research on the effects of air exposure and the relationship between surface conditions and bonding strength is necessary.
Previous studies found that O 2 plasma treatment improved Au-Au bonding strength [23,24], possibly because Au 2 O 3 desorbed due to the high bonding temperature (150 • C) or ultrasonic vibrations.

Conclusions
Pretreatment using Ar or O 2 plasma was investigated for ambient room-temperature wafer-scale Au-Au bonding using ultrathin Au films. Surface activation by Ar plasma is mainly due to physical etching by Ar ions, while surface activation by O 2 plasma is mainly due to chemical reaction. The O 2 plasma treatment increased the sheet resistance of the Au surfaces but did not increase the bonding strength. XPS analysis revealed that Au 2 O 3 formed on the Au surfaces that received O 2 plasma treatment, and TDS analysis revealed that annealing at over 110 • C is necessary for desorption of Au 2 O 3 . Annealing up to 150 • C before bonding increased the bonding strength of samples that received O 2 plasma treatment, demonstrating that Au 2 O 3 impedes strong Au-Au bonding.
On the other hand, Ar plasma treatment increased the Au-Au bonding strength enough for the Si substrate to be broken in destructive razor blade testing. Although an Au surface that receives Ar plasma treatment is more activated than one that receives O 2 plasma treatment, bonding should be performed immediately after plasma treatment.