Embedded Piezo-Sensor-Based Automatic Performance Monitoring of Chloride-Induced Corrosion inAlkali-Activated Concrete

The primary goal of the construction industries worldwide is to improve material durability and achieve sustainability. In recent years of sustainable cement industry innovation, alkali-activated cement has emerged as one of the most promising alternatives to ordinary Portland cement (OPC). In terms of durability, corrosion of steel is a significant problem and has become a major cause of deterioration of reinforced concrete structures worldwide. Thus, structural health monitoring techniques are essential to monitor the corrosion in real-time to avoid unexpected failure since civil engineering structures serve as a crucial pillar of the economy. This paper presents through an experimental campaign a novel method of automatically monitoring the performance of alkali-activated concrete (AAC) and ordinary Portland cement concrete (OPCC) under chloride-induced corrosion conditions using an embedded piezo sensor (EPS) based on the electro-mechanical impedance (EMI) technique. AAC was produced using alkali silicate-activated fly ash and ground granulated blast furnace slag. The accelerated corrosion tests were conducted on reinforced AAC and OPCC specimens in which the EPS was attached to reinforcing steel bars inside the specimens to monitor the changes in the EMI signature during the corrosion progression. To quantify the damage due to chloride-induced corrosion, statistical damage indices such as root mean square deviation were calculated. Further, the deterioration in structural parameters was identified by extracting the equivalent structural parameters (ESPs) such as stiffness, mass and damping from the raw EMI signatures. Based on qualitative and quantitative results, it can be seen that the changes in raw signature and damage in AAC were lower than OPCC. The deterioration in term of stiffness loss was found to be 39.35% in OPCC and 12.73% in AAC. Hence, it is demonstrated that the AAC exhibits a superior corrosion resistance to OPCC.


Introduction
The built environment accounts for roughly 50% of annual global CO 2 emissions, of which embodied carbon (the carbon produced during the construction of structures) from building material and the construction industry is responsible for 20%, while building (residential and non-residential) operations are responsible for 27% [1][2][3]. To reduce these emissions, concrete technologists, scientists and engineers are engineering various types of innovative binders such as limestone-calcined clay cement (LC3) [4], alkali-activated materials (AAMs) [5][6][7][8] and calcium sulfoaluminate cement [9] for application in construction. Among them, AAMs have outstanding potential to achieve high mechanical strength at early curing ages, resistance to elevated temperature [10], high stability in aggressive environments along with low energy consumption and low carbon-dioxide emission [11].
These properties have made concretes based on alkali-activated binders a very interesting alternative for OPCC, and the substitution of OPCC by AAMs is viable for specific applications only. However, for civil engineering infrastructures, durability is the main concern as it affects the service life when an aggressive environmental agent reaches the reinforcement by de-passivating the protective layer, affecting the safety and serviceability of the reinforced concrete structures (RCSs). Furthermore, because of the degradation of corrosion pits, chloride-induced pitting corrosion is frequently regarded to be more severe than carbonation-induced uniform corrosion for reinforcing steel in ordinary Portland cement concrete (OPCC). Evaluation of the durability of AAMs when subjected to aggressive environments is of particular importance for their use in RCSs. So far, various researchers have evaluated and identified the mechanical fracture properties [12]; the effect of binder content [11]; the use of copper slag as fine aggregate [13]; the effect of the treatment method and curing time on the microstructure [14]; electrochemical performance in presence of chlorides [15]; chloride and transport properties (by measuring the electrical resistivity, non-steady state chloride diffusivity, rate of corrosion, onset of corrosion and pore solution chemistry) [16] and long-term corrosion resistance [17] on the performance of RCSs made with AMMs. For the durability-related issues, the techniques used for monitoring the corrosion condition of reinforcing steel bars in concrete are either direct or indirect, and sensor systems include half-cell potential sensors [18], concrete resistivity measurement sensors, macro-and microcell sensors, linear polarization resistance (LPR) sensors [19], galvanostatic pulse technique (GPT) sensors, electrochemical impedance spectroscopy (EIS) sensors [20], chloride monitoring sensors, pH-sensors, fiberoptic sensors (FOSs) and the electro-mechanical impedance (EMI) technique based on piezo sensors [21][22][23][24][25]. Among them, the EMI technique utilizing piezo sensors, which has a dual capacity of sensing and actuating, has shown promising results in almost all applications of civil engineering, including strength development monitoring during the curing process [26,27], deterioration monitoring in terms of equivalent structural parameters due to corrosion in RCSs and prestressed concrete structures [21,22], health monitoring in RCS impact loading [28] and damage due to tightening and loosening of bolts [29]. Pioneering studies were performed by Talakokula et al. [30][31][32] in extending the applications of the EMI technique to corrosion in RCSs by developing physical models based on the equivalent structural parameters for both chloride-and carbonation-induced corrosion in rebars, thereby circumventing the determination of actual structural parameters, which is either very difficult or impossible. Sriramadasu et al. [33] identified incipient pitting corrosion in RCSs using guided waves and piezoelectric wafer transducers. They found that the mechanism of the corrosion process can be established from the signal characteristics of the longitudinal and flexuralguided wave mode. Huo et al. [34] presented a corrosion detection method of steel bars based on a piezoceramic-transducer-enabled time reversal method and found that the signal recorded by the piezoceramic transducers changed linearly with the mass loss ratio of the reinforcement bar. Recently, Bansal et al. [35] identified the equivalent stiffness loss in concrete systems (OPC and LC3) with the chloride effect and combined effect (chlorination attack and compression loading) using piezo sensors. Their results showed that chloride penetration in both concrete systems with the combined loading effect is lower than ideal; however, LC3 is more corrosion resistant than OPC.
In the existing literature, studies on corrosion monitoring mainly focus on RCSs made with OPCC, with only a few covering the use of SCMs. The study by Talakokula et al. [30][31][32] identified the equivalent structural parameters (ESPs) to analyze the mechanical changes in the structure during the corrosion progression; however, this study is limited to RCSs made with OPC. In real-life practice, the RCSs are made up of different concretes involving AAC, therefore, it is necessary to understand the performance of AAC under chloride-induced corrosion conditions, and there is a need for a structural health monitoring technique to monitor the corrosion in real-time. Hence, the novelty of this study is that it focuses on automatic monitoring of the performance of AAC under chloride-induced corrosion conditions using an embedded piezo sensor (EPS) based on the electro-mechanical impedance (EMI) technique. The statistical indices such as RMSD of the conductance signature during the corrosion progression were analyzed, discussed and compared to OPCC reference systems. Furthermore, ESPs were extracted from the coupled EMI signature to collect more realistic information about mechanical changes occurring during the corrosion progression of AAC and OPCC.

Materials and Concrete Specimens
Reinforced steel bars, 16 mm in diameter, conforming to grade Fe 500 high yield strength deformed (HYSD) conforming to IS 1786 (2008) [36] were used, and their physical and chemical composition includes carbon 0.3%, sulfur 0.055%, phosphorous 0.055%, elongation 12%, carbon equivalent 0.42% and yield stress 500 N/mm 2 . Ordinary Portland cement, 43 grade, class F fly ash and ground granulated blast furnace slag (GGBFS) were used for preparing the OPCC and AAC. The images of powdered OPC, FA and GGBFS are shown in Figure 1. Sand obtained from Raipur City, India, with maximum size of 4.75 mm, zone II, specific gravity of 2.71 and water absorption of 2.04% was used as the fine aggregate (FA). Crushed stone of 10 and 20 mm obtained from Raipur, India, with specific gravity of 2.54 and water absorption of 0.6%, was used as the coarse aggregate (CA) conforming to IS 2386-3 (1963) [37]. Tap water was used as mixing water for OPCC. For preparing the AAC, an alkali activator with a 2.5 Na 2 SiO 3 /NaOH molarity ratio was prepared by mixing sodium silicate solution, sodium hydroxide solution and distilled water. The chemical composition of GGBFS is shown in Table 1. The specific gravity of Na 2 SiO 3 and NaOH is 1.6 and 1.47, respectively. The sodium silicate solution consists of SiO 2 = 29.4%, Na 2 O = 11.4% and water = 55.9%. The purity of sodium hydroxide flakes is 98% to 99%. The mix design of OPCC conforming to IS 10262 (2009) [38] and AAC [39] is shown in Table 2. The schematic diagram of the cylindrical concrete specimen with 100 mm diameter and 150 mm height with an embedded steel bar is shown in Figure 2. An embedded piezo sensor (PZT patch sandwich between the mortar and epoxy layers) was attached to the steel bar to monitor the deterioration during the corrosion process. The specification of PZT 5H is shown in Table 3. After casting, the concrete specimens were cured at the ambient temperature for 28 days.

Accelerated Corrosion Test
After 28 days of curing, the bottom end of the specimens was sealed with epoxy coating to avoid the transport of aggressive chloride ions. Later, OPCC and AAC specimens with an embedded reinforcing bar were dipped in brine solution (3.5% by weight NaCl solution) for 115 days for accelerated corrosion as shown in Figure 3. The height of the specimens dipped in the brine solution was 70% of the original height. To accelerate the

Accelerated Corrosion Test
After 28 days of curing, the bottom end of the specimens was sealed with epoxy coating to avoid the transport of aggressive chloride ions. Later, OPCC and AAC specimens with an embedded reinforcing bar were dipped in brine solution (3.5% by weight NaCl solution) for 115 days for accelerated corrosion as shown in Figure 3. The height of the specimens dipped in the brine solution was 70% of the original height. To accelerate the corrosion process, an electrical loop was developed in which the steel bar acted as the anode and a copper rod as a cathode. A constant 12 V of voltage was applied throughout the specimens to accelerate the process. corrosion process, an electrical loop was developed in which the steel bar acted as the anode and a copper rod as a cathode. A constant 12 V of voltage was applied throughout the specimens to accelerate the process.

EMI Technique
The EMI technique was employed for monitoring the corrosion process. In this technique, a high-strength epoxy adhesive is used to attach a PZT patch to the host structure. An inductance-capacitance-resistance (LCR) meter is then used to electrically excite the PZT patch between the 30 to 300 kHz frequency range to acquire the admittance signatures in the form of conductance vs. frequency and susceptance vs. frequency. The LCR meter measures the electrical signals obtained from the PZT sensor in terms of electromechanical admittance, representing the electrical and structural mechanical impedance of the piezo sensor and the specimen, respectively. The electro-mechanical admittance deviation measured various time intervals from the sensor indicates a change or shift in the specimen/host structure's mechanical properties. Any change in mechanical impedance of the structure is detected by the patch (attached to the host structure) since the electrical impedance of the patch and mechanical impedance of the structure are related and can be represented by the following equation [40].
where G is the conductance; B is the susceptance with its imaginary unit (j); w is the width, l is the length, and h is the thickness of the PZT patch; ω is the angular frequency; , and , are the effective mechanical impedance of the structure and PZT patch respectively; is Poisson's ratio,); is the complex electric permittivity of the PZT patch (at constant stress); is the complex Young's modulus of the PZT patch (at constant electric field); is the piezoelectric strain coefficient and is the complex tangent ratio.

Data Acquisition
By using this technique, the EMI data in the form of conductance and susceptance were acquired at the baseline or healthy state and during the corrosion period up to 115 days using an LCR meter as shown in Figure 4. The baseline signatures for OPCC and AAC are shown in Figure 5. To acquire the signatures, the specimens were taken out of the accelerated corrosion setup and dried at room temperature for half an hour. The measurement was taken at standard room temperature to avoid the temperature effect on the

EMI Technique
The EMI technique was employed for monitoring the corrosion process. In this technique, a high-strength epoxy adhesive is used to attach a PZT patch to the host structure. An inductance-capacitance-resistance (LCR) meter is then used to electrically excite the PZT patch between the 30 to 300 kHz frequency range to acquire the admittance signatures in the form of conductance vs. frequency and susceptance vs. frequency. The LCR meter measures the electrical signals obtained from the PZT sensor in terms of electromechanical admittance, representing the electrical and structural mechanical impedance of the piezo sensor and the specimen, respectively. The electro-mechanical admittance deviation measured various time intervals from the sensor indicates a change or shift in the specimen/host structure's mechanical properties. Any change in mechanical impedance of the structure is detected by the patch (attached to the host structure) since the electrical impedance of the patch and mechanical impedance of the structure are related and can be represented by the following equation [40].
where G is the conductance; B is the susceptance with its imaginary unit (j); w is the width, l is the length, and h is the thickness of the PZT patch; ω is the angular frequency; Z s,e f f and Z a,e f f are the effective mechanical impedance of the structure and PZT patch respectively; ν is Poisson's ratio,); ε T 33 is the complex electric permittivity of the PZT patch (at constant stress); Y E is the complex Young's modulus of the PZT patch (at constant electric field); d 31 is the piezoelectric strain coefficient and T is the complex tangent ratio.

Data Acquisition
By using this technique, the EMI data in the form of conductance and susceptance were acquired at the baseline or healthy state and during the corrosion period up to 115 days using an LCR meter as shown in Figure 4. The baseline signatures for OPCC and AAC are shown in Figure 5. To acquire the signatures, the specimens were taken out of the accelerated corrosion setup and dried at room temperature for half an hour. The measurement was taken at standard room temperature to avoid the temperature effect on the EMI signature. To ensure the repeatability of the signature, each specimen was measured thrice. The entire experimental campaign layout shown in Figure 6. EMI signature. To ensure the repeatability of the signature, each specimen was measured thrice. The entire experimental campaign layout shown in Figure 6.  EMI signature. To ensure the repeatability of the signature, each specimen was measured thrice. The entire experimental campaign layout shown in Figure 6.  frequency. Figure 6. The experimental campaign layout.

Statistical Indices
The statistical parameter root mean square deviation (RMSD), which has been established in numerous structural health monitoring (SHM) fields [41,42], was calculated for the quantification of EMI signature. The RMSD is expressed by: including conductance or resistance of the PZT patch during the hydration process (G i ) and the baseline value (G i 0 ), with i representing the frequency index.

Extraction of Equivalent Structural Parameters
To gain a better understanding of chloride-induced corrosion deterioration, an equivalent stiffness parameter (ESP) was identified from the raw signatures (conductance and susceptance) by developing a physical model based on spring, mass and the damper element and correlating it with the corrosion initiation phase and visual inspection. Using Equation (1) as mentioned in Section 2.3, the effective mechanical impedance (Zs, eff = x + yj) of the host structure can be divided into its real and imaginary components, which may provide critical information on the behavior of the deteriorating host structure. This well-

Statistical Indices
The statistical parameter root mean square deviation (RMSD), which has been established in numerous structural health monitoring (SHM) fields [41,42], was calculated for the quantification of EMI signature. The RMSD is expressed by: including conductance or resistance of the PZT patch during the hydration process (G i ) and the baseline value (G 0 i ), with i representing the frequency index.

Extraction of Equivalent Structural Parameters
To gain a better understanding of chloride-induced corrosion deterioration, an equivalent stiffness parameter (ESP) was identified from the raw signatures (conductance and susceptance) by developing a physical model based on spring, mass and the damper element and correlating it with the corrosion initiation phase and visual inspection. Using Equation (1) as mentioned in Section 2.3, the effective mechanical impedance (Z s , eff = x + yj) of the host structure can be divided into its real and imaginary components, which may provide critical information on the behavior of the deteriorating host structure. This well-established concept has been successfully implemented by several researchers [23,31,35,[43][44][45] and has been proven to be successful in damage detection, where 'x' represents the real part and 'y' represents the imaginary parts of structural mechanical impedance. In order to identify an equivalent system based on the impedance plots provided by Hixon (1998) [46], 'x' and 'y' for all specimens were computed and plotted versus frequency to monitor variation in the structure's physical properties.

Results and Discussion
This section covers the results and discussion on the qualitative analysis of piezo signature changes during the corrosion progression. Further, the quantitative analysis in the form of RMSD is discussed. The deterioration analysis based on equivalent structural parameters (ESPs) is also discussed by extracting the equivalent stiffness, mass and damping parameters.

Analysis Based on EMI Signature
The changes in conductance signature during accelerated chloride-induced corrosion at different time intervals for a typical OPCC specimen in a frequency range of 30 to 300 kHz is shown in Figure 7. It can be observed that the trend of conductance signatures shifts in the right-upwards direction from the baseline signature during the corrosion exposure period. Figure 8 shows the resonance peak frequency and conductance value shift during accelerated chloride-induced corrosion of OPCC. It can be observed that the amplitudes of the resonance peak increase significantly (0.0014 to 0.0022 S) up to 14 days, whereas as the corrosion progresses, this amplitude value increases up to 0.0037 S during the period of 115 days. In terms of the resonance frequency, which shows a good correlation with the corrosion progression, the resonance frequency presents a significant increase (130 to 260 kHz) up to 14 days; afterwards, it decreases and reaches 200 kHz during the period of 115 days. Upon visual observation of the specimens, it can be seen that the OPCC shows mild rust particles on the surface along with a minor crack at 14 days of corrosion exposure. As the corrosion progressed, the width of the crack was increased, and the mild exposure stage converted into the severe stage which is clearly visible in Figure 9. In the case of AAC, the variation in the amplitude and frequency at the resonance peak is different in comparison to the OPCC specimen as shown in Figures 10 and 11. The resonance frequency (180 to 240 kHz) and its amplitude in terms of conductance value (0.0014 to 0.0023 S) presents a significant increase up to 60 days; afterwards, it follows a minimal increment in resonance frequency (240 to 242 kHz) shift and amplitude (0.0023 to 0.0025 S) during the period of 115 days. From the visual observation of the specimens, only mild rust formation on the surface of the specimen was seen after 60 days of exposure and moderate corrosion at 115 days ( Figure 12). Hence, based on visual observation of the specimens and the analysis of the raw signatures for both OPCC and AAC specimens, it can be concluded that the EPS records the changes effectively, and the resonance frequency shift indicates a good correlation with the mild, moderate and severe corrosion formation in the specimens.

Analysis Based on Statistical Indices
In quantitative analysis, a significant increment is also found in RMSD value, which is about 27% in AAC with respect to the baseline value during the 14 days of corrosion exposure; after that, it reaches 33% in the period of 115 days, which indicates a gradual increment as shown in Figure 13. Upon comparing the RMSD indices of OPCC and AAC as shown in Figure 14, it was found that the RMSD value of OPCC is about 61% in the period of 115 days of corrosion exposure, while AAC is about 33%. These values show that the variation in terms of RMSD values is significant in OPCC when compared to AAC. From the raw signatures and visual observations, it was also confirmed that the changes are significant and exhibit more severe rust formation in OPPC in comparison to AAC. Hence, from all these observations, it is concluded that damage due to chloride-induced corrosion is higher in OPCC than AAC, and the sensor embedded inside the RC specimens is able to capture the damage well as the corrosion progresses.

Analysis Based on Statistical Indices
In quantitative analysis, a significant increment is also found in RMSD value, which is about 27% in AAC with respect to the baseline value during the 14 days of corrosion exposure; after that, it reaches 33% in the period of 115 days, which indicates a gradual increment as shown in Figure 13. Upon comparing the RMSD indices of OPCC and AAC as shown in Figure 14, it was found that the RMSD value of OPCC is about 61% in the period of 115 days of corrosion exposure, while AAC is about 33%. These values show that the variation in terms of RMSD values is significant in OPCC when compared to AAC. From the raw signatures and visual observations, it was also confirmed that the changes are significant and exhibit more severe rust formation in OPPC in comparison to AAC. Hence, from all these observations, it is concluded that damage due to chlorideinduced corrosion is higher in OPCC than AAC, and the sensor embedded inside the RC specimens is able to capture the damage well as the corrosion progresses.

Analysis Based on Equivalent Structural Parameters
In this study, an equivalent system consisting of the spring element (k), mass (m) and damper element (c) in a series combination was chosen because it exhibits similar trends to the experimental system under close observation of 'x' and 'y' in a healthy state with a

Analysis Based on Statistical Indices
In quantitative analysis, a significant increment is also found in RMSD value, which is about 27% in AAC with respect to the baseline value during the 14 days of corrosion exposure; after that, it reaches 33% in the period of 115 days, which indicates a gradual increment as shown in Figure 13. Upon comparing the RMSD indices of OPCC and AAC as shown in Figure 14, it was found that the RMSD value of OPCC is about 61% in the period of 115 days of corrosion exposure, while AAC is about 33%. These values show that the variation in terms of RMSD values is significant in OPCC when compared to AAC. From the raw signatures and visual observations, it was also confirmed that the changes are significant and exhibit more severe rust formation in OPPC in comparison to AAC. Hence, from all these observations, it is concluded that damage due to chlorideinduced corrosion is higher in OPCC than AAC, and the sensor embedded inside the RC specimens is able to capture the damage well as the corrosion progresses.

Analysis Based on Equivalent Structural Parameters
In this study, an equivalent system consisting of the spring element (k), mass (m) and damper element (c) in a series combination was chosen because it exhibits similar trends to the experimental system under close observation of 'x' and 'y' in a healthy state with a Figure 14. Comparison of changes in RMSD for OPCC and AAC.

Analysis Based on Equivalent Structural Parameters
In this study, an equivalent system consisting of the spring element (k), mass (m) and damper element (c) in a series combination was chosen because it exhibits similar trends to the experimental system under close observation of 'x' and 'y' in a healthy state with a frequency range of 220 to 280 kHz for both OPCC and AAC. The result of the comparison between experimental and equivalent plots of OPCC is shown in Figure 15. The expression of 'x' and 'y' are shown in Table 4.
The automatically identified deterioration of the equivalent stiffness parameter (ESP) during accelerated chloride-induced corrosion exposure for AAC at different intervals is shown in Figure 16a. It can be observed in Figure 16 that the equivalent stiffness (k) decreases with the increase in corrosion exposure period. At the age of 7 days, the decrease in k values from baseline ranged from 4100 to 3883.34 Ns/m, while at 60 days it was 4100 3665.70 Ns/m, and at 115 days it was 4100-3578.05 Ns/m (stiffness loss = 12.73%) in AAC. This finding indicates that the equivalent stiffness was reduced significantly up to 60 days, whereas further reductions in stiffness values were minimal as the corrosion progressed up to 115 days. This is due to the fact that the initial changes up to 60 days were captured well by the EPS. Similar observations were also noticed by Talakokula et al. [32] while assessing the corrosion in reinforced concrete structures using the EPS as shown in Figure 16b. The visual observation of the specimens also confirms that the mild rust formation on the surface of the specimen at 60 days and moderate corrosion at 115 days, as shown in Figure 12. The comparison of deterioration in terms of equivalent stiffness parameter during accelerated chloride-induced corrosion exposure for OPCC and AAC is shown in Figure 17. It can be observed in Figure 17 that the equivalent stiffness (k) decreases with corrosion progression up to 32 days, while afterwards it becomes constant. At the age of 7 days, the decrease in k values from baseline ranges from 5172. 37  frequency range of 220 to 280 kHz for both OPCC and AAC. The result of the comparison between experimental and equivalent plots of OPCC is shown in Figure 15. The expression of 'x' and 'y' are shown in Table 4. Table 4. Identified series combination of spring, mass and damper element. The automatically identified deterioration of the equivalent stiffness parameter (ESP) during accelerated chloride-induced corrosion exposure for AAC at different intervals is shown in Figure 16a. It can be observed in Figure 16 that the equivalent stiffness (k) decreases with the increase in corrosion exposure period. At the age of 7 days, the decrease in k values from baseline ranged from 4100 to 3883.34 Ns/m, while at 60 days it was 4100 3665.70 Ns/m, and at 115 days it was 4100-3578.05 Ns/m (stiffness loss = 12.73%) in AAC.  frequency range of 220 to 280 kHz for both OPCC and AAC. The result of the comparison between experimental and equivalent plots of OPCC is shown in Figure 15. The expression of 'x' and 'y' are shown in Table 4.
Sustainability 2022, 14, x FOR PEER REVIEW 12 of 16 frequency range of 220 to 280 kHz for both OPCC and AAC. The result of the comparison between experimental and equivalent plots of OPCC is shown in Figure 15. The expression of 'x' and 'y' are shown in Table 4. frequency range of 220 to 280 kHz for both OPCC and AAC. The result of the comparison between experimental and equivalent plots of OPCC is shown in Figure 15. The expression of 'x' and 'y' are shown in Table 4. Table 4. Identified series combination of spring, mass and damper element.  Figure 17. It can be observed in Figure 17 that the equivalent stiffness (k) decreases with corrosion progression up to 32 days, while afterwards it becomes constant. At the age of 7 days, the decrease in k values from baseline ranges from 5172.37 to 5121.45 Ns/m, while at 28 days it ranges from 5172.37 to 4390.90 Ns/m and at 115 days between 5172.37 and 3136.90 Ns/m (stiffness loss = 39.35%). This finding indicates that the deterioration in terms of stiffness loss at 115 days of AAC is lower than OPCC, and therefore AAC is more corrosion resistant than conventional concrete made with OPC.

Conclusions
In this study, the performance of AAC under accelerated chloride-induced corrosion conditions was automatically monitored using the EPS via EMI technique. Based on raw EMI signatures of the EPS, it was found that changes in conductance signature during chloride-induced corrosion at different time intervals for OPCC and AAC are well captured by the EPS. These findings provide a proof-of-concept validation for the use of the embedded sensor for corrosion exposure monitoring in both OPCC and ACC concretes. In general, it is already well established in the literature through conventional durability tests that AAC has better durability in comparison to OPCC, which can lead to adaptability of AAC for sustainable construction. Based on the results obtained from the EPS, it was again reaffirmed using piezo sensors non-destructively. Further, based on equivalent structural analysis, it was found that the deterioration in terms of stiffness loss in AAC is lower than OPCC, which indicates that AAC is more corrosion resistant as compared to

Conclusions
In this study, the performance of AAC under accelerated chloride-induced corrosion conditions was automatically monitored using the EPS via EMI technique. Based on raw EMI signatures of the EPS, it was found that changes in conductance signature during chloride-induced corrosion at different time intervals for OPCC and AAC are well captured by the EPS. These findings provide a proof-of-concept validation for the use of the embedded sensor for corrosion exposure monitoring in both OPCC and ACC concretes. In general, it is already well established in the literature through conventional durability tests that AAC has better durability in comparison to OPCC, which can lead to adaptability of AAC for sustainable construction. Based on the results obtained from the EPS, it was again reaffirmed using piezo sensors non-destructively. Further, based on equivalent structural analysis, it was found that the deterioration in terms of stiffness loss in AAC is lower than OPCC, which indicates that AAC is more corrosion resistant as compared to OPCC. Hence, it can be concluded that the ESP is a good indicator for identifying corrosion deterioration and could be used in real-life scenarios without any destructive testing.