The Effect of Basalt Fiber on Mechanical, Microstructural, and High-Temperature Properties of Fly Ash-Based and Basalt Powder Waste-Filled Sustainable Geopolymer Mortar

: As the human population grows and technology advances, the demand for concrete and cement grows. However, it is critical to propose alternative ecologically suitable options to cement, the primary binder in concrete. Numerous researchers have recently concentrated their efforts on geopolymer mortars to accomplish this objective. The effects of basalt ﬁber (BF) on a geopolymer based on ﬂy ash (FA) and basalt powder waste (BP) ﬁlled were studied in this research. The compressive and ﬂexural strength, Charpy impact, and capillary water absorption tests were performed on produced samples after 28 days. Then, produced samples were exposed to the high-temperature test. Weight change, ﬂexural strength, compressive strength, UPV, and microstructural tests of the specimens were performed after and before the effect of the high temperature. In addition, the results tests conducted on the specimens were compared after and before the high-temperature test. The ﬁndings indicated that BF had beneﬁcial beneﬁts, mainly when 1.2 percent BF was used. When the ﬁndings of samples containing 1.2 percent BF exposed to various temperatures were analyzed, it was revealed that it could increase compressive strength by up to 18 percent and ﬂexural strength by up to 44 percent. In this study, the addition of BF to ﬂy ash-based geopolymer samples improved the high-temperature resistance and mechanical properties.


Introduction
In terms of environmental protection, it is critical to creating a sustainable product. The geopolymer mortars were used to reduce OPC use to as an alternative to Ordinary Portland cement (OPC). Cement manufacture accounts for 5-7 percent of global CO 2 emissions [1]. This scenario has severe environmental consequences. Finding alternate OPC replacements is essential. Industrial waste materials (slag, red mud, fly ash) were significant replacements. Alkaline activators were used to activate these waste materials in the geopolymer manufacture process. The carbon dioxide emissions are decreased due to recycling waste materials and using less OPC [2].
Additionally, geopolymer mortars have much superior durability and mechanical properties. In this instance, the compact and dense geopolymer microstructure is beneficial [3]. Industrial waste, produced as a byproduct of many technological operations, is a major environmental issue. One of these sectors is the quarry industry which generates a large quantity of industrial waste. The environmental cost for storing waste items rises year after year. The mining and processing of rock raw materials are rapidly expanding. Rock raw materials are treated to cutting and grinding operations in stone manufacturers. The fine-grained waste material generated during processing is transported to and deposited In this study, waste materials were used as binder and filler material in fly ash-based geopolymer mortars. Class F fly ash (FA) and slag (S) were used as binders. Basalt dust waste (BP) was also used as filling material. The physical and chemical properties of BP, S, and FA materials are given in Table 1. The particle diameters of BP range from 1 to 300 µm, with an average particle diameter of 120 µm. Sodium hydroxide (SH) and sodium silicate (SS) were used as activators to produce geopolymer mortar. Tables 2 and 3 illustrate the chemical characteristics of SS and SH, respectively. In addition, BF was used at 4, 8, and 12 percent by volume. BF properties used in blends are shown in Table 4. The images of FA, S, BP, and BF materials used in fly ash -based and BP-filled geopolymer mortars are given in Figure 1.

Mixing Procedure and Samples
In the first mixing stage of the fly ash-based geopolymer mortars produced in this study, 12 M sodium hydroxide solution was prepared and kept at 20 • C for 24 h to cool. 1000 g of deionized water was used for each 40 g of sodium hydroxide pellets to prepare 12 M sodium hydroxide solution. Then, sodium hydroxide solution (SH) was mixed with sodium silicate solution (SS) after cooling. Then, fly ash was placed in the mixer, and the prepared mixture of SS and SH (mixed activator solution) was added and mixed until homogeneous. Then, slag was added to the mixture and mixed homogeneously. BP waste, which is the filling material, was added to the mixture and mixed homogeneously. Finally, BF was added to the mixtures at different rates (0%, 4%, 8%, and 12%) and mixed homogeneously. In addition, the amounts of the materials used in the fly ash-based geopolymer mortar mixtures produced in this study are given in (kg/m 3 ), as Table 5 shows. BF was added at 0%, 4%, 8%, and 12% by volume. Previous trial experiments and earlier studies were used to prepare the mixture [8,25]. Freshly prepared mixtures were placed into 40 × 40 × 160 mm 3 prismatic molds and 50 × 50 × 50 mm 3 cubic molds. The molds were then vibrated while being placed on the vibration table. Then the samples were cured in an oven at 60 • C for 24 h. The cured samples were kept at 20 • C for 28 days.

Tests Conducted
In this study, mixtures of fly ash-based geopolymer contained BF were prepared. Compressive strength, flexural strength, Ultrasonic pulse velocity (UPV), Charpy impact, and capillary water absorption tests were performed to examine the impact of BF content on prepared samples. Then, 50 × 50 × 50 mm 3 cubic and 40 × 40 × 160 mm 3 prismatic samples were subjected to the high-temperature test. Weight change, compressive strength, flexural strength, and UPV tests of the samples exposed to the high-temperature test were performed. In addition, the results before and after the high-temperature test were compared. Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray (EDS) analyzes were performed to observe the BF content and changes in the matrices of the samples.

Compressive Strength, Flexural Strength, and Ultrasonic Pulse Velocity (UPV) Tests
Compressive strength, flexural strength, and UPV tests were performed to examine the impact of BF on produced samples after 28 days at 20 • C. The same tests were also carried out on samples exposed to high-temperature effects. For each mixture, the average compressive strength of three 50 × 50 × 50 mm 3 cube samples after 28 days was performed. Compressive strength was conducted with a rate of 0.602 MPa/s according to ASTM C39. In addition, compressive strengths were performed on the geopolymer samples exposed to 200 • C, 400 • C, 600 • C, and 800 • C temperatures, and the differences between the results were analyzed. The flexural test was performed after 28 days on three 40 × 40 × 160 mm 3 prism samples for each mixture. Flexural strength tests were conducted following ASTM C 348. As in the compressive strength test, the flexural strength test was also performed after the high-temperature test. The 4× and 40× magnified crack images of 12 BF specimens subjected to flexural strength test are shown in Figure 2. In addition, the UPV test of the geopolymer mortar samples was applied after 28 days according to ASTM C597-16. UPV test results of fly ash-based geopolymer samples contained BF exposed to 20 • C, and high temperatures were obtained. The damage degrees caused by high temperatures were calculated using the UPV results and the following formula: Dd was the damage degree of samples, V a was the UPV values of samples after the hightemperature test, and V b was the UPV values of samples before the high-temperature test.

Charpy Impact Test
The Charpy impact test was conducted following ASTM E23. 40 × 40 × 160 mm 3 prismatic fly ash-based geopolymer specimens were used for the Charpy impact test. In the first stage of the Charpy impact test, the sample was placed centered on the device, as shown in Figure 3a. Subsequently, the pendulum was raised, and the drag indicator was set to the zero position. Finally, the pendulum was released from the first height and swung through the specimen to the second height. Figure 3 illustrates the procedure of the Charpy impact test and the samples subjected to this test. Three fly ash-based geopolymer samples containing BF were subjected to the Charpy impact test, and the average results were recorded from the device in the Kgf-m unit.

Capillary Water Absorption
The capillary water absorption capacity of fly ash-based geopolymer samples was determined using ASTM C1585-20. 40 × 40 × 160 mm 3 fly ash-based geopolymer samples were dried in an oven at 105 • C for 24 h. Then, the samples surfaces were covered with paraffin except for the surface contacted with water and the opposite surface. Then, the dry weights (Wd) of the samples were obtained, and the dry samples were immersed in 5 mm depth water. After 15 min, 30 min, 1, 2, 3, 5, 24, 48, 72, and 96 h, the fly ash-based samples were withdrawn from the water, and their wet weight (Ww) was determined. Finally, the capillary water absorption curves and water absorption coefficient (Kc) using the following formula: where Q was the absorbed water mass (Ww-Wd) (kg), Wd was the dry weight (kg), Ww was the wet weight (kg), A was the immersed surface area (m 2 ), t was a time (s), and Kc was the water absorption coefficient ((kg/(m 2 . √ s)).

High-Temperature Test
In this study, a high-temperature test was performed to examine the high-temperature resistance of fly ash-based geopolymer samples and the effect on the BF contained in the samples. Fly ash-based geopolymer samples were dried in an oven at 105 • C for 24 h. Dried samples were exposed to temperatures of 200 • C, 400 • C, 600 • C, and 800 • C, respectively. The high-temperature degrees rose with the rate of 5 • C/min, and then the samples were exposed to temperatures for another 1 h.
The dry weight (Wd) of the samples dried at 105 • C for 24 h in the oven was performed. Then, the weights of the samples exposed to the effects of high temperatures were measured, and the percentages of change in weights were calculated. The images of the cracks were obtained using a microscope with 40× magnification to evaluate the effect of high temperature on the samples.

Compressive and Flexural Strength Results
Compressive strength, flexural strength, UPV, and Charpy impact tests were performed on geopolymer mortar samples after 28 days. These tests were conducted to study the effect of BF and determine the mechanical properties of the fly ash-based geopolymer mortars filled with BP. Subsequently, the results of these tests were determined.  Figure 5). Therefore, in this study, it was found that the increase of BF content in fly ash-based geopolymer mortars increased the compressive and flexural strength of the specimens. The increases in compressive strength were 6.43%, 9.65%, and 11.94% for 4 BF, 8 BF, and 12 BF, respectively.
Similarly, the flexural strength increased by 7.72%, 25.51%, and 34.15% for 4 BF, 8 BF, and 12 BF, respectively. Consequently, the increase in flexural strength due to basalt content was higher than the increase in compressive strength. Especially for the 12 BF series, the increase in flexural strength was 2.86 times larger than the increase in compressive strength. All specimens with BF exhibited higher strength than the 0 BF specimens. The use of BF increased the compressive and strength of the geopolymer matrix. The delicate and uniform distribution of crystal phases helped improve the BF materials' physical and mechanical properties. Applying a nucleating agent such as P 2 O 5 , TiO 2 , and ZrO 2 helped achieve the required degree of microstructure. At the same time, basaltic rock was not required for melting, creating a naturally occurring nucleating agent such as Fe 3 O 4 aided in the process. Thus, the nucleating agents outperformed the necessary fibers [17].
The addition of BF significantly reduced the number of fractures during the flexural test because they transferred the flexural load. In other words, they delayed the formation of cracks by distributing the resulting stress. As a result, BF had a massive effect on flexural strength [26].

Ultrasonic Pulse Velocity (UPV) Results
The UPV test was performed on fly ash-based geopolymer mortar samples after 28 days. The UPV test was carried out to study the effect of BF on the samples and to determine the compactness of the fly ash-based geopolymer mortars filled with BP waste. Figure 6 shows the UPV test results of the series. Similarly, Figure 6 illustrates the relationship between the UPV and BF content in the geopolymer series. The wave velocity and the number of voids in the matrix of geopolymer samples have a reciprocal relationship [27]. The penetration rate is determined by dividing the distance between the origin and the receiver by the elapsed time. When the matrix of samples contains more voids, the time required increases, and the penetration rate decreases.
Consequently, the void ratio has a significant effect on the mechanical properties of fly ash-based geopolymer specimens. The relationship between UPV and BF content was relatively high, with an R 2 of 0.99. Thus, in this study, it was found that the addition of BF to fly ash-based geopolymer mortars increased the UPV values of the geopolymer specimens. The UPV values increased by 3.34%, 6.05%, and 8.90% for series 4 BF, 8 BF, and 12 BF, respectively, compared to series 0 BF. Although the fiber exposure improved the UPV values by reducing the void ratio, the improvement was not significant. This situation was because the fibers had no direct effect on the homogeneity or compaction of the matrix. The observed behavior indicates that basalt fiber content influences the UPV of composites and is connected to the composite density and perceived porosity. Additionally, basalt fiber influences the geopolymer matrix and improved the UPV values of geopolymer mortar samples. Ozkan and Coban [28] investigated the hybrid effects of basalt and PVA fiber on the properties of cementitious composites, and the effect of BF on UPV results they found are consistent with the effect of BF performed in this study.

Charpy Impact Test Results
The Charpy impact test was performed on prismatic fly ash-based geopolymer samples. The Charpy impact test was performed on samples of the series, and the average results were reported in Kgf-m units. This test uses a falling pendulum's potential energy to fracture samples at high strain rates and characterize the composites. Mechanical property testing procedures are based on the principles of stress wave propagation, kinetic energy, or potential energy [29]. The absorption of impact energy and comparable characteristics are highly dependent on the fiber properties [30]. In this study, the correlation between Charpy impact test values and BF content was strong, and the R2 was 0.90.  Figure 7.

Water Absorption
After 28 days, the capillary water absorption test was performed on the samples, and the results are shown in Figure 8. In this study, the amount of water absorbed over time was determined as a function of the area in contact with the water, and the capillary water absorption curves shown in Figure 8 were obtained using formula two given in Section 2.3.3. Series 0 BF absorbed the least amount of water, and series 12 BF absorbed the most water compared to the other series. Increasing the BF percentage increased the amount of water absorbed, as shown by the slopes of the capillary water uptake. The percentage increase in water absorption was 9.38%, 11.88%, and 18.13% for 4 BF, 8 BF, and 12 BF, respectively, compared to sample 0 BF. These results are supported by the slopes of the capillary water uptake tests. Figure 9 also shows the capillary water absorption coefficient (Kc) values of fly ash-based geopolymer mortar samples containing BF in different proportions. The water absorption coefficient (Kc) values were determined using the least-squares method. The percentage increases in the water absorption coefficients of samples 4 BF, 8 BF, and 12 BF were 9.04%, 10.55%, and 17.99%, respectively. As a result of capillary water absorption of fly ash geopolymer samples containing BF in different ratios, increasing the content of BF increased the amount of water absorbed by the samples. This increase is because the addition of BF improves pore connectivity at large volume fractions. Similar results were obtained in [21,31].

Weight Measurement Results
The behaviors of the produced geopolymer specimens after a high-temperature test were analyzed and compared with samples cured at 20 • C for 28 days. Fly ash-based samples were exposed to 200 • C, 400 • C, 600 • C, and 800 • C temperatures to perform the high-temperature test. Figures 10-15 showed the weight loss, compressive strength, flexural strength, UPV, and damage degree values of fly ash geopolymer samples after and before the high-temperature test. After 400 • C, the increase in weight loss ratio was observed, as seen in Figure 10. The 12 BF samples had the smallest weight loss, and the 0 BF had the highest weight loss. After 800 • C, the weight loss percentages of 0 BF, 4 BF, 8 BF,12 BF were 8.73%, 8.49%, 8.38%, and 8.17% respectively. The inclusion of BF slowed down the weight reduction. This occurred as a result of BF's ability to limit the hightemperature cracks in the samples. Thus, reducing the formation of cracks reduced the samples' weight loss exposed to the high-temperature effect. Sahin et al. [32] investigated the effect of basalt fiber on metakaolin-based geopolymer mortars, and they found that the inclusion of BF reduced weight reduction. Generally, the interface bonds between paste and aggregate weaken at high temperatures, leading to weight loss [33,34]. For example, the weight loss percentages of 12 BF samples exposed to 200 • C, 400 • C, 600 • C, and 800 • C were 1.26%, 4.26%, 7.18%, and 8.17 respectively. Figure 10. The weight loss percentages of fly ash-based geopolymer samples exposed to high temperatures.

Compressive and Flexural Strength Results
The Compressive strength and flexural strength tests were performed on geopolymer mortar samples which exposed to 200 • C, 400 • C, 600 • C, and 800 • C. Then the results of the samples conducted after and before the high-temperature test were compared. The strength tests were conducted to study the effect of high temperature on the fly ash-based geopolymer mortars' mechanical properties contained BF. Figures 11 and 12 show the results of the compressive and flexural strength of the fly ash-based geopolymer samples. The 12 BF mix had the highest compressive and flexural strength results, and the 0 BF mix had the lowest compressive and flexural strength results. Thus, the BF improved the mechanical properties of the geopolymer samples. The increases of the results of 4 BF, 8 BF, 12 BF samples exposed to 800 • C were 9.01%, 12.79%, and 15.79% for compressive strength and 11.61%, 32.87%, and 44.69% for flexural strength, respectively compared to 0 BF samples. In addition, the increases of the results of 12 BF samples exposed to 200 • C, 400 • C, 600 • C, and 800 • C were 14.31%, 17.18%, 18.65%, and 15.79% for compressive strength and 36.94%, 39.95%, 37.80%, and 44.69% for flexural strength, respectively compared to 0 BF samples.
At 200 • C, the flexural and compressive strengths of the samples did not change significantly (Figures 11 and 12), but beyond 400 • C, the reduction rate of compressive and flexural increased more. Endothermic processes caused these reductions. Dehydration and water vapor of free water occurred concurrently with the processes in the matrix structure of the geopolymer [8,35,36]. In addition, the flexural strength decreases due to the high-temperatures effect were lower than the compressive strength decreases. Where the decreases of the strength of the 12 BF samples exposed to 200 • C, 400 • C, 600 • C, and 800 • C were 7.53% 28.17%, 41.36%, and 54.57% for compressive strength and 2.27%, 14.02%, 33.71%, and 44.32%for flexural strength, respectively compared to the samples not exposed to high-temperature test.
The vapor action emphasized the decrease of compressive and flexural strength as the temperature rose. The geopolymer matrix structure's water transformed into vapor whenever the specimens were exposed to high temperatures. Additionally, increasing temperatures make the Al SiO gel composition crystallized in the geopolymer matrix, causing more microcracks [37]. When the temperature surpassed 100 • C, the internal pressure rose steadily. This scenario produced microcracks in the geopolymer specimens due to crystallization stress. Thermal fractures and thermochemical breakdown in crystal lattices were apparent as the temperature rose. While the sample's strength values decreased, it became more brittle, and fragile cracking appeared. In addition, when the temperature surpassed 100 • C, there was a substantial thermal incompatibility between the paste and the aggregate in geopolymer. Increased temperature also caused microcracks in the aggregate-paste interface transition region, resulting in thermal incompatibilities [38].

Ultrasonic Pulse Velocity (UPV) Results
The UPV test of fly ash geopolymer samples was conducted, and using the UPV results, the damage degrees of samples were calculated ( Figure 13). The 12 BF samples had the highest UPV, and the 0 BF had the smallest UPV. Where the UPV results of 0 BF, 4 BF, 8 BF,12 BF samples exposed to 800 • C were 2512.05, 2627.69, 2700.42, and 2785.63 m/s respectively. Thus, the addition of BF in the fly ash geopolymer samples increased the UPV. The UPV readings dropped as the temperature rose for all samples. Due to evaporation in the interior structure, the pore size grew, and the continuity reduced, resulting in this situation [39]. When the UPV findings were compared to the mechanical results, it was observed that the values were almost consistent. At high temperatures, the interface bonds between the aggregates and pastes of the samples weaken, resulting in a reduction in UPV [33]. Where the UPV results of 12 BF samples exposed to 200 • C, 400 • C, 600 • C, and 800 • C were 3312.63, 3190.17, 3020.59, 2905.46, and 2785.63 m/s, respectively.
In addition, the damage degrees of the fly ash-based geopolymer samples exposed to high temperatures were performed. The damage degrees of the fly ash-based geopolymer samples containing BF are shown in Figure 14. The width and number of the cracks of fly ash-based geopolymer samples increased as the high temperatures increased. The UPV values were used to evaluate the degree of damage. In previous studies, Singh and Gupta [40] were used the UPV values to perform the damage degree in their study. A proportional relationship was obtained between the damage degrees and the increase of high temperatures in all series. In addition, as Figure 14 shows, the increase in basalt content decreased the damage degrees of fly ash-based geopolymer mortar samples containing BF with different ratios. The performed damage degrees were ranged between 3.69% for 12 BF samples exposed to 200 • C and 17.42% for 0 BF samples exposed to 800 • C. In other words, the UPV values of the samples exposed to the high-temperature effect were smaller than the initial UPV values of the samples. Thus, high-temperature increases increased the damage degrees of geopolymer samples. The damage degrees of the 12 BF samples at temperatures of 200 • C, 400 • C, 600 • C, and 800 • C were 3.70%, 8.82%, 12.29%, and 15.91%, respectively. This result is compatible with the weight measurement and mechanical strength tests performed in the study. The damage degrees of 0 BF, 4 BF, 8 BF and 12 BF samples exposed to 800 • C were 17.42%, 16.41%, 16.29%, and 15.91%. In addition, the damage degrees of 0 BF, 4 BF, 8 BF, and 12 BF samples exposed to 200 • C were 4.54%, 4.38%, 4.04%, and 3.70%. Thus, the increase in the BF ratio decreased the damage degrees. This situation was because BF inhibited high-temperature cracks in the samples and limited the damage.  The damage degree of fly ash-based geopolymer samples exposed to high temperature.

Visual Assessment of High-Temperature Test
Fly ash-based geopolymer mortar samples exposed to various temperatures are shown in Figure 15. In general, it was found that the color of the samples and BF exposed to 200 • C and 400 • C did not change compared to the samples not exposed to the high temperature (20 • C). The color of samples exposed to 600 • C and 800 • C changed from gray to brown and white spots were formed in the cross-section. In addition, the BF of the samples exposed to 600 • C and 800 • C changed in color. Unequal volume changes between geopolymer components caused by temperature exposure were referred to as thermal incompatibility of components. This situation also resulted in microcracks in the interfacial transition zone between the geopolymer paste and the aggregate. Microcracks were also increased because of the loss of homogeneity [38]. A 40× magnification microscope was used to examine better the complexity of the outer surfaces of the BF-containing geopolymer samples exposed to high temperatures. The preliminary visual evaluation determined that series 12 BF was the most compact series, as the BF content was higher than the other series. For this reason, 12 BF samples were selected to be examined under the microscope. The microscope images of the 12 BF samples subjected to the high-temperature tests are shown in Figure 16.  Figure 16a,b show that the geopolymer mortar samples exposed to 200 • C and 400 • C did not show any cracks on the surface and the samples maintained their compactness. Figure 16c shows that superficial microcracks formed on the outer surfaces of the geopolymer mortar specimens exposed to 600 • C. Figure 16d shows that the outer surfaces of the specimens exposed to the transition from 600 • C to 800 • C loosened due to superficial cracks, and the cracks were filled with dust formed due to the deteriorated outer surfaces and the aggregates emerged from under the outer surface. As a result, it was observed that the compactness of the geopolymer samples exposed to 600-800 • C deteriorated significantly due to dehydration [8,41].

SEM and EDS Analysis
SEM images of 0 BF and 12 BF samples not exposed to high-temperature tests are shown in Figure 17. As Figure 17a,b shows, 0 BF samples without basalt contained microcracks. The basalt-containing 12 BF samples shown in Figure 17c,d prevented the formation of cracks with the effect of basalt, and it was seen that the 12 BF samples were more compact. The BF acted as a bridging agent, slowing the formation of fractures [42]. In addition, SEM images of both 0 BF and 12 BF samples contain N-A-S-H gel and unreacted FA particles. This finding is consistent with previous fly ash-based geopolymers discovered in the literature [43].
Moreover, SEM images of 12 BF samples exposed to 200 • C, 400 • C, 600 • C, and 800 • C are shown in Figure 18. In Figure 18a,c, it was seen that the structure of the BF of 12 BF samples exposed to 200 • C and 400 • C was the same and did not change. In addition, the 12 BF samples exposed to 200 • C were more compact and had fewer microcracks than the samples exposed to different high temperatures. In this study, the authors were noticed that the matrix of 12 BF samples started to form microcracks after 400 • C and became less compact than the samples exposed to 200 • C. As shown in Figure 18e, voids were formed in the sample exposed to 600 • C due to dehydration and evaporation. Figure 18g shows that the sample exposed to 800 • C had more voids than the sample exposed to 600 • C. Additionally, the voids formed caused volume reduction and structural deterioration of the sample. After exposure to high temperatures, the samples' evaporation rate and water losses increase, leading to structural deterioration and increased formation defects [44].
Moreover, EDS traces of the 0 BF and 12 BF samples not exposed to high-temperature test and 12 BF samples exposed to high-temperature test are shown in Figure 19. Figure 19a,b show that Si/Al ratios of 0 BF and 12 BF fly ash-based geopolymer samples exposed to high-temperature tests are 2.18 and 2.16, respectively. Thus, no significant change was observed in the Si/Al ratio of 12 BF compared to 0 BF. The Si/Al ratio of 12 BF samples exposed to 200 • C, given in Figure 19c, increased to 2.72. Additionally, it was observed that the increase in Si/Al ratio of 12 BF samples exposed to 400 • C given in Figure 19d decreased to 2.41. Figure 19e,f show that the Si/Al ratios of 12 BF samples exposed to 600 • C and 800 • C, respectively, decreased to 2.12 and 2.02. These results are consistent with the study conducted by Abdulkareem et al. [45]. They found that the Si/Al ratio decreased when the fly ash paste samples were exposed to 800 • C.   Figure 19. EDS traces of (a) 20 • C exposed 0 BF sample; (b) 20 • C exposed 12 BF sample; (c) 200 • C exposed 12 BF sample; (d) 400 • C exposed 12 BF sample; (e) 600 • C exposed 12 BF sample and (f) 800 • C exposed 12 BF sample.

Conclusions
This research examined the impact of BF on a geopolymer based on FA and filled with waste BP. The following summarizes the findings of the tests conducted:

•
The study revealed that adding BF to fly ash-based geopolymer mortars improved compressive strength after 28 days. Compressive strength increased by 6.43%, 9.65%, and 11.94% for 4 BF, 8  respectively. At elevated temperatures, the interface bonds between the paste and aggregate deteriorate, resulting in weight loss. Consequently, the increase of high temperatures increased the weight loss percentages of geopolymer samples.

•
The BF improved the compressive and flexural strengths of the samples after and before the high-temperature test. The increases of the compressive and flexural strengths of 4BF, 8BF, 12BF samples exposed to 800 • C were 9.01%, 12.79%, and 15.79% for compressive strength and 11.61%, 32.87%, and 44.69% for flexural strength, respectively compared to 0 BF samples. Thus, the high-temperature effect reduced flexural strength more than compressive strength. • BF inhibited high-temperature cracks and limited the damages. Thus, the increase in basalt content decreased the damage degrees of fly ash-based geopolymer mortar samples. After the high-temperature test, the damage degrees of samples ranged from 3.69 to 17.42% for 12 BF samples. Additionally, the damage degrees of the samples exposed to high-temperature effects increased proportionally with the increase in high temperatures.

•
The color of the samples and BF exposed to 200 • C and 400 • C did not change significantly compared to the samples exposed to 20 • C. Additionally, the samples exposed to 600 • C and 800 • C turned from gray to brown. Dehydration also affected the compactness of the geopolymer samples exposed to 600-800 • C.

•
After 400 • C, 12 BF samples developed microcracks and became less compact than the 12 BF samples exposed to 200 • C. In addition, the Si/Al ratio of 12 BF samples exposed to 800 • C decreased compared to 12 BF samples exposed to 20 • C. After exposure to 600 • C and 800 • C, the samples' evaporation rate and water loss rise, resulting in structural deterioration.