Feasibility Evaluation of Replacing River Sand with Copper Tailings

This study aims to realize the resource regeneration application of copper tailing (as fine aggregates for partial replacement of natural fine aggregates), which avoid environmental pollution due to many landfills of copper tailings. The compressive strength and durability (dry shrinkage and sulfate attack) tests were carried out to evaluate the effect of copper tailings replacement on the performance of mortar. The results show that the mortar with copper tailings has higher compressive strength than the one with natural sand. More than 14% improvement in compressive strength can be achieved by adding copper tailings with no more than 40% replacement level. The dry shrinkage of mortar was increased with the copper tailings due to the increase of micro pores in mortar by using copper tailings. Compared with the mortar with natural sand, the dry shrinkage can be reduced by adding copper tailings with no more than 20% replacement level. The sulfate attack resistance is improved by using copper tailings, when the replacement rate is more than 20%. In fact, the micro-aggregate filler effect of copper tailings effectively refines the pore structure and forms more stable, uniform and fine interface micro pores, which is of vital significance for mortar to resist external forces and sulfate ion erosion. However, copper tailings, as a porous material, have water release characteristics in cement mortar. This characteristic is not conducive to the filler effect, which decreases the filling rate in later hydration, leading to higher porosity of copper tailings mortar. More importantly, mortar can solidify heavy metals in copper tailings, which prevents loss of heavy metal such as Cu, Zn, Sr, Zr, As, Ga due to environmental problems.


Introduction
Waste tailings as filler of mortar proved to be a good choice. Ceren Ince [1] revealed that in replacing part of natural river sand with gold mine tailings from the Lefke-Xeros area, the performance (compressive strength, water penetration depth and carbonization depth) of the gold tailings test block is significantly improved due to the pozzolanic activity and filler effect. It is worth noting that the average particle size of gold tailings in Ceren Ince's paper is about 8 µm. SiO 2 + Al 2 O 3 + Fe 2 O 3 accounted for 79.36%, which is required by the ASTM C618-15 (Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete) [2]. Actually, the majority of waste tailings, such as copper tailings, iron tailings, nickel tailings, etc. do not have the inherent excellent physical and chemical properties of gold mine tailings from the Lefke-Xeros area, but are inert materials with relatively coarse particles, which are more suitable for use as an aggregate replacement [3][4][5][6][7][8]. Besides, the thing that cannot be ignored is that tailings (copper tailings and iron tailings) usually contain a small amount of soluble heavy metal ions, whether or not these soluble heavy metal ions can be solidified into the mortar test block [9].
The copper tailings used in this paper are waste byproducts from the Tongling Nonferrous Metals Company's beneficiation to refine useful metals. The copper tailings, micron  3 3.979 Therefore, this paper first comparatively analyzed the compactness of natural river sand and mixed fine aggregate based on the solid accumulation theory and particle grading parameters. Then, testing compressive strength, dry shrinkage and sulfate attack provide a reference for the practical application of copper tailings. The microscopic aspect mainly uses MIP test and binary image analysis to compare the internal pore structure of cop-per tailings mortar, especially the binary image analysis visually demonstrates the pore structure characteristics. Importantly, based on the leaching test, it is tested whether the solidification of heavy metals in the copper tailings mortar meets the requirements of ecological regulations. The replacement of natural sand by copper tailings has not only successfully solved the environmental problems caused by random stacking and loss of heavy metals such as Cu, Zn, Sr, Zr, As, Ga. It is also considered a feasible way to solve the shortage of natural sand resources in China.

Cement and Primary Copper Tailings
Ordinary Portland cement (P.O 42.5) is produced at the Bagongshan Cement Plant in Huainan City, Anhui Province, China. The copper tailings are from Tongling Nonferrous Metals Company, Tongling City, Anhui Province, China. Table 1 shows the chemical composition and physical properties of the primary copper tailings. Among them, the total content of CaO, SiO 2 and Fe 2 O 3 accounts for 82.85%, and the main mineral ingredients are silica, calcium longite, limestone, gypsum, calcium, iron, etc. (Figure 1). Additionally, the native copper tailings contain a small amount of heavy metal elements (Sr, Zr, Ga, Cu, Zn and As).

Cement and Primary Copper Tailings
Ordinary Portland cement (P.O 42.5) is produced at the Bagongshan Cement Plant in Huainan City, Anhui Province, China. The copper tailings are from Tongling Nonferrous Metals Company, Tongling City, Anhui Province, China. Table 1 shows the chemical composition and physical properties of the primary copper tailings. Among them, the total content of CaO, SiO2 and Fe2O3 accounts for 82.85%, and the main mineral ingredients are silica, calcium longite, limestone, gypsum, calcium, iron, etc. (Figure 1). Additionally, the native copper tailings contain a small amount of heavy metal elements (Sr, Zr, Ga, Cu, Zn and As).
The particle size distribution of copper tailings is detected with a laser particle size analyzer, as shown in Figure 2. The median particle size is 110 μm (Figure 2), which belongs to micron particles. The US FEI Inspect F50 field emission scanning electron microscope is used to observe the apparent morphology of copper tailings ( Figure 3). It is found that the copper tailings have sharp corner angles and a wide range of particle size distribution.   The particle size distribution of copper tailings is detected with a laser particle size analyzer, as shown in Figure 2. The median particle size is 110 µm (Figure 2), which belongs to micron particles. The US FEI Inspect F50 field emission scanning electron microscope is used to observe the apparent morphology of copper tailings ( Figure 3). It is found that the copper tailings have sharp corner angles and a wide range of particle size distribution.
In addition to the introduction of the physical properties and chemical composition of copper tailings, copper tailings as fine aggregates should also be tested in accordance with JGJ 52-2006 (Standard for technical requirements and test method of sand and crushed stone for ordinary concrete) [16], such as water content (standard method), sludge content (siphon method) and nuclear radiation (radiometer detection) of copper tailings. The results show that the water content of Tongling copper tailings is 26.12%, which is already a high-water content aggregate, and the sludge content of copper tailings is less than 5%, and there is no radiation.  In addition to the introduction of the physical properties and chemical composition of copper tailings, copper tailings as fine aggregates should also be tested in accordance with JGJ 52-2006 (Standard for technical requirements and test method of sand and crushed stone for ordinary concrete) [16], such as water content (standard method), sludge content (siphon method) and nuclear radiation (radiometer detection) of copper tailings. The results show that the water content of Tongling copper tailings is 26.12%, which is already a high-water content aggregate, and the sludge content of copper tailings is less than 5%, and there is no radiation.
The above content mainly tests the basic properties of copper tailings. To study the effect of copper tailings mixed with mortar on performance, the specific mix ratio design of copper tailings mortar (100 g) is designed as shown in Table 2. The numbers T-0% (control group), T-10%, T-20%, T-30% and T-40%, respectively, indicate that the replacement  In addition to the introduction of the physical properties and chemical composition of copper tailings, copper tailings as fine aggregates should also be tested in accordance with JGJ 52-2006 (Standard for technical requirements and test method of sand and crushed stone for ordinary concrete) [16], such as water content (standard method), sludge content (siphon method) and nuclear radiation (radiometer detection) of copper tailings. The results show that the water content of Tongling copper tailings is 26.12%, which is already a high-water content aggregate, and the sludge content of copper tailings is less than 5%, and there is no radiation.
The above content mainly tests the basic properties of copper tailings. To study the effect of copper tailings mixed with mortar on performance, the specific mix ratio design of copper tailings mortar (100 g) is designed as shown in Table 2. The numbers T-0% (control group), T-10%, T-20%, T-30% and T-40%, respectively, indicate that the replacement The above content mainly tests the basic properties of copper tailings. To study the effect of copper tailings mixed with mortar on performance, the specific mix ratio design of copper tailings mortar (100 g) is designed as shown in Table 2. The numbers T-0% (control  group), T-10%, T-20%, T-30% and T-40%, respectively, indicate that the replacement rate of copper tailings is 0%, 10%, 20%, 30% and 40%, and the water-cement ratio is set to 0.55.

Test Methods
The compressive strength is the most basic parameter index for evaluating the mechanical properties of mortar. In order to obtain a more accurate compressive strength value, the preparation process of the test block needs to be standardized. The steps of test block preparation are as follows. First, put the copper tailings and natural sand in an oven at 105 ± 5 • C for 8 h, weigh them according to the design of the mix ratio, put them in a dry mixing pot, and mix them dry at slow speed for 30 s, and mix well. Then, add cement and dry mix for 1 min. Finally, pour all the mixing water into the mixing pot and wet mix for 2 ± 0.5 min. Subsequently, quickly place the freshly mixed mortar in a cube mold (5 cm × 5 cm × 5 cm), place it on a vibrating table for 15 ± 5 s, smooth the surface, and put it in the curing chamber for 24 h before demolding. After that curing for 6 days, 27 days and 89 days, take it out and measure its compressive strength. Dry shrinkage is used to evaluate the shrinkage deformation of mortar specimens, and it is one of the reference indicators of mortar durability. The drying shrinkage experiment in this study based on ASTM C596-2018 (Standard test method for drying shrinkage of mortar containing hydraulic cement) [17] prepare cuboid specimens with size of 25 mm × 25 mm × 280 mm for testing the shrinkage properties of copper tailings mortar. During the experiment, the curing temperature is 20 ± 3 • C and the curing humidity is 50 ± 5%.
Sulfate attack [18] requires that the cube mortar (50 mm × 50 mm × 50 mm) be cured in water bath for 28 days, and then completely immersed in 5% sodium sulfate solution (500 g sodium sulfate decahydrate and 3900 g water are mixed evenly). Take out the test block after soaking for 30 days and 120 days. The sodium sulfate solution needs to be replaced every two weeks. The same batch of mortar test blocks were taken out on the 58th and 148th days after being cured in water. The loss of compressive strength indicates the resistance of the mortar to sulfate erosion. Therefore, the compressive strength loss rate (%) is selected as the index [13], and the formula of compressive strength loss rate ∆C is as follows: Note: C s means that compressive strength after sulfate attack. C w represents compressive strength after water curing.

MIP and SEM
MIP experiment describes a test method for the characteristics of the pore structure inside the mortar. The mercury intrusion device is Autopore IV (9500), the pressure range is set from 0.1 to 61,000 psia, the contact angle is 130 • , and the quality of the sample to be tested is controlled between 1.6 g and 2.1 g to prevent the mass of the test block from being too large or too small to affect porosity test results [19]. The surface morphology analysis of the mortar used the electron microscope picture taken by the FEI Inspect F50 field emission scanning electron microscope under the electron beam acceleration voltage 20.00 kV.

Leaching Experiment
Copper tailings containing heavy metal elements are used as fine aggregates of mortar, and we should conduct leaching experiment on copper tailings mortar to detect whether it is toxic to the environment. The leaching test in this paper was carried out with reference to the British Standard BS EN12457-2002 [20]. First, a wet sample from the tailings mortar specimen was dried and crushed to a particle shape of less than 2 mm. Distilled water is used as the leaching agent for the leaching experiment to eliminate the interference of water ions on the experiment results. Here, the liquid to solid ratio is set to 10:1 (l/kg), and the water bath temperature is set to 20 ± 5 • C, and allowed to stand for 24 h. Next, filter the large particles with 0.45 µm filter paper, and remove the ultrafine slurry powder that may exist in the filtrate with a centrifuge. The stable pH value of the filtrate was recorded by pH meter at room temperature (20 ± 5 • C). The concentrations of five heavy metal elements (Sr, Zr, Ga, Cu, Zn and As) in the filtrate were determined by inductively coupled plasma emission spectrometer (ICP-OES) [21].  Figure 4 shows the dried natural sand and copper tailings. It can be seen that the particle size of copper tailings is smaller than that of river sand and the color is darker.
tar, and we should conduct leaching experiment on copper tailings mortar to detect whether it is toxic to the environment. The leaching test in this paper was carried out with reference to the British Standard BS EN12457-2002 [20]. First, a wet sample from the tailings mortar specimen was dried and crushed to a particle shape of less than 2 mm. Distilled water is used as the leaching agent for the leaching experiment to eliminate the interference of water ions on the experiment results. Here, the liquid to solid ratio is set to 10:1 (l/kg), and the water bath temperature is set to 20 ± 5 °C, and allowed to stand for 24 h. Next, filter the large particles with 0.45 μm filter paper, and remove the ultrafine slurry powder that may exist in the filtrate with a centrifuge. The stable pH value of the filtrate was recorded by pH meter at room temperature (20 ± 5 °C). The concentrations of five heavy metal elements (Sr, Zr, Ga, Cu, Zn and As) in the filtrate were determined by inductively coupled plasma emission spectrometer (ICP-OES) [21].

Properties of Mixed Fine Aggregate
3.1.1. Testing the Basic Properties of the Mixed Sand Figure 4 shows the dried natural sand and copper tailings. It can be seen that the particle size of copper tailings is smaller than that of river sand and the color is darker. Refer to JGJ 52-2006 (Standard for technical requirements and test method of sand and crushed stone for ordinary concrete) to test the loose bulk density, close bulk density, and fineness of the mixed fine aggregate (river sand and copper tailings). The results are shown in the Table 3. It can be seen that the bulk density and dense packing density of the mixed fine aggregate increase with the increase of the copper tailing content. The fineness decreases with the increase of the copper tailing content. River sand belongs to medium sand, the mixed fine aggregate mixed with 10% to 30% copper tailings in river sand belongs to fine sand, and the mixed fine aggregate mixed with 40% copper tailings in river sand belongs to superfine sand. Therefore, the incorporation of copper tailings greatly reduces the fineness of fine aggregates. Refer to JGJ 52-2006 (Standard for technical requirements and test method of sand and crushed stone for ordinary concrete) to test the loose bulk density, close bulk density, and fineness of the mixed fine aggregate (river sand and copper tailings). The results are shown in the Table 3. It can be seen that the bulk density and dense packing density of the mixed fine aggregate increase with the increase of the copper tailing content. The fineness decreases with the increase of the copper tailing content. River sand belongs to medium sand, the mixed fine aggregate mixed with 10% to 30% copper tailings in river sand belongs to fine sand, and the mixed fine aggregate mixed with 40% copper tailings in river sand belongs to superfine sand. Therefore, the incorporation of copper tailings greatly reduces the fineness of fine aggregates.

Packing Theory of Solid Particles (Fuller Theory)
It is meaningful for Chao-Lung Hwang to study the packing density of solid particles based on Fuller's curve [22]. Fuller theory is used to optimize the filling ratio. It is to determine the distribution of various particle sizes in the gradation from the perspective of the combination of aggregates in which proportions can achieve the maximum density [22]. The closer the material (fine aggregate) gradation curve is to the parabola (Fuller curve), the higher the degree of compaction. Here is the Fuller general formula of A.N.Talbol: Here, y is theoretical cumulative pass rate (%), x is the particle size, D is the maximum particle size of solid aggregate and n is gradation index. A.N.Talbol proposes that materials have better density (n = 0.3~0.5). The larger the n, the denser the material system, that is, the tightest packing and the smallest porosity are reached when n = 0.5. However, modern concrete requires a certain degree of fluidity and excessive density will reduce the slump of concrete, so 0.45 is the best value for n. Hence, MATLAB software fit five sets of sample data based on Equation (2), and the gradation index n and the RMSE and R-square of the fitted curve are obtained, as shown in Table 4. Table 4. The gradation index n of sample T-0%, T-10%, T-20%, T-30% and T-40% and evaluation of fitting accuracy.

Serial Number
Gradation Index Evaluation of Fitting Accuracy The result reveals that the gradation index of the T-0% is less than 0.3, while the gradation index values of T-10%, T-20%, T-30% and T-40% are all greater than 0.3. With the increase of tailings content, the gradation index shows an overall increasing trend, which shows that the density of the mixed fine aggregate mixed with copper tailings is indeed greater than that of river sand. Besides, the smaller the RMSE and the larger the R-square of the fitted curve, the higher the fitting accuracy, namely, the more suitable the fitting using Equation (2). In Table 4, the continuous incorporation of copper tailings makes the fitting precision of the sand gradation curve higher and higher, and the sample T-40% has the highest fitting degree.
Next, MATLAB software is used to draw the particle gradation diagram and Fuller curve (n = 0.45) of T-0%, T-10%, T-20%, T-30% and T-40% mixed fine aggregates, as shown in Figure 5. It was found that the incorporation of copper tailings mainly increased the number of particles in a small interval around 0.15 mm. With the increase of the amount of copper tailings, the gradation curve of the mixed fine aggregate becomes closer to the ideal Fuller curve (n = 0.45) with the increase of the copper tailings.

Characteristics Analysis of Mixed Sand Gradation
The characteristic analysis parameters of the mixed sand are the non-uniform efficient Cu and the curvature coefficient Cc (derived from the index used by soil me ics to analyze the gradation of soil particles), such as Equations (3) and (4).
The Cu is used to describe the degree of unevenness of the soil particles. The the Cu, the more uneven and the better the particle gradation. The Cc describes the d Passing (%) Figure 5. Sample T-0%, T-10%, T-20%, T-30% and T-40% particle gradation map and ideal Fuller curve (n = 0.45).

Characteristics Analysis of Mixed Sand Gradation
The characteristic analysis parameters of the mixed sand are the non-uniformity coefficient C u and the curvature coefficient C c (derived from the index used by soil mechanics to analyze the gradation of soil particles), such as Equations (3) and (4).
The C u is used to describe the degree of unevenness of the soil particles. The larger the C u , the more uneven and the better the particle gradation. The C c describes the degree of continuity of the soil particle size. The decrease of C c indicates absence of larger or smaller particles. In engineering, it is considered that C u ≥ 5 and C c = 1 and 3, which is a well-graded soil.
In the paper, the C u and C c of soil particle grading are used to evaluate the aggregate particle grading of T-0%, T-10%, T-20%, T-30% and T-40%. The results are shown in Table 5. Noting that the non-uniformity coefficient C u increases with the increase of the amount of copper tailings. The C u of T-30% and T-40% are greater than 5, and the C u of T-20% is close to 5. The C u of sample T-0% and T-10% are 2.457 and 3.436 (<5), respectively. This suggests that the incorporation of copper tailings makes the aggregate particles become uneven and the gradation is better. Moreover, the curvature coefficient C c of T-0%, T-10%, T-20%, T-30% and T-40% fluctuates. Except that the C c of the T-40% is 0.44, the C c of T-0%, T-10%, T-20% and T-30% are all in the interval of 0.8~0.95. Therefore, we propose that only the non-uniformity coefficient C u is considered, the samples T-20%, T-30% and T-40% gradation is better, and only the curvature coefficient C c is considered, the samples T-0%, T-10%, T-20% and T-30% are better. Combining these two indicators, the gradation of samples T-20% and T-30% are better than the other three.  Figure 6 shows the compressive strength values and corresponding error bars of T-0%, T-10%, T-20%, T-30% and T-40% in four curing ages (3 days, 7 days, 28 days and 90 days).

Compressive Strength
It could be seen that the error bar of the test group (90 days) is larger than that of the test group (28 days) error bar. This shows that the copper tailings mortar will increase the strength difference of the same group of test blocks in the later curing. Since the error bar does not exceed 15%, it can be regarded as an effective strength data value.
The compressive strength of control group T-0% and copper tailing mortar (T-10%, T-20%, T-30% and T-40%) increases with the increase of curing age. In the same curing age, the compressive strength of copper tailings mortar is basically higher than that of the control group, and with the increase of the replacement rate of tailings, the strength value has a trend of increasing at first and then decreasing. Figure 6 shows that there is an optimal replacement rate (30%) of river sand replaced by tailing powder. Compared with T-0%, T-30% increased by 17.99%, 16.75%, 14.82% and 14.65% (3 days, 7 days, 28 days and 90 days). During the early curing age (3 days~28 days), T-30% has the highest compressive strength value. The strength of T-20% and T-40% increased obviously during the curing period from 28 days to 90 days, almost catching up with T-30%. All the above data indicate that copper tailings replace part of river sand as fine aggregate of mortar to promote strength in both early strength (3 days~28 days) and later strength (90 days), which is consistent with the results of previous research papers [23,24].
The strength of copper tailing mortar is higher than the control group T-0%, which due to the higher packing density of mixed fine aggregate in copper tailing mortar. Micron Sustainability 2021, 13, 7575 9 of 21 scale copper tailings have a more micro-filling effect than millimeter-level river sand. In addition, the copper tailings particles have distinct edges and corners, and the river sand has a smoother surface after long-term erosion by river water, so the mechanical engagement force between the copper tailings and the cement paste matrix is greater.    It could be seen that the error bar of the test group (90 days) is larger than that of the test group (28 days) error bar. This shows that the copper tailings mortar will increase the strength difference of the same group of test blocks in the later curing. Since the error bar does not exceed 15%, it can be regarded as an effective strength data value.

Compressive Strength
The compressive strength of control group T-0% and copper tailing mortar (T-10%, T-20%, T-30% and T-40%) increases with the increase of curing age. In the same curing age, the compressive strength of copper tailings mortar is basically higher than that of the control group, and with the increase of the replacement rate of tailings, the strength value has a trend of increasing at first and then decreasing. Figure 6 shows that there is an optimal replacement rate (30%) of river sand replaced by tailing powder. Compared with T-0%, T-30% increased by 17.99%, 16.75%, 14.82% and 14.65% (3 days, 7 days, 28 days and 90 days). During the early curing age (3 days~28 days), T-30% has the highest compressive strength value. The strength of T-20% and T-40% increased obviously during the curing period from 28 days to 90 days, almost catching up with T-30%. All the above data indicate that copper tailings replace part of river sand as fine aggregate of mortar to promote strength in both early strength (3 days~28 days) and later strength (90 days), which is consistent with the results of previous research papers [23,24].
The strength of copper tailing mortar is higher than the control group T-0%, which due to the higher packing density of mixed fine aggregate in copper tailing mortar. Micron scale copper tailings have a more micro-filling effect than millimeter-level river sand. In addition, the copper tailings particles have distinct edges and corners, and the river sand has a smoother surface after long-term erosion by river water, so the mechanical engagement force between the copper tailings and the cement paste matrix is greater.

Drying Shrinkage
Drying shrinkage is an important indicator of the durability of cement-based materials. It characterizes the mortar from standard curing conditions (humidity above 95%) to dry

Drying Shrinkage
Drying shrinkage is an important indicator of the durability of cement-based materials. It characterizes the mortar from standard curing conditions (humidity above 95%) to dry curing conditions (low humidity 50 ± 5%), capillary storage of free water evaporation, resulting in the generation of capillary stress, mass decline, volume shrinkage deformation. Figure 7 shows the shrinkage rate of copper tailings mortar (25 mm × 25 mm × 280 mm) with a water-cement ratio of 0.55 in 90 days. It is obvious that with the increase of copper tailings (10-40%), the shrinkage rate of mortar specimen increases. When the replacement rate of copper tailings is 10-20%, the shrinkage rate is less than T-0%. When the replacement rate of copper tailings is 30-40%, the drying shrinkage rate after stabilization is greater than T-0%. This shows that the addition of 10-20% copper tailings has an inhibitory effect on the shrinkage of the mortar, and overmuch copper tailings (30-40%) will accelerate the shrinkage of the mortar specimens.
Generally, curing of mortar specimens in a low-humidity environment (50 ± 5%) will cause the macro pore water to evaporate in the mortar; nevertheless, the macro pore has little effect on the shrinkage volume. Then there is the evaporation of capillary water (capillary pores are the main influencing factor of volume shrinkage) until all the pore water larger than the critical pore evaporates (the lower the humidity, the smaller the critical pore size); at this time, the volume shrinkage of the mortar is stable [25]. In Figure 7, the dry shrinkage of T-0% on the 21st day of curing was significantly more serious than that of T-10%, T-20% and T-30%. Considering that all mortar specimens in this experiment have the same humidity, the critical pore size is the same. This indicates that after curing for 21 days, T-0% may generate more pores than T-10%, T-20% and T-30%. As the dry curing continues, the capillary pores of T-30% increase and the pores are more refined, so that the drying shrinkage stable period of T-30% is 28% higher than the drying shrinkage rate of T-0%. T-40% has much more capillary pores than T-0% during the whole curing period, so the shrinkage rate of T-40% is much greater than the number of other groups, including T-0%. for 21 days, T-0% may generate more pores than T-10%, T-20% and T-30%. As the dry curing continues, the capillary pores of T-30% increase and the pores are more refined, so that the drying shrinkage stable period of T-30% is 28% higher than the drying shrinkage rate of T-0%. T-40% has much more capillary pores than T-0% during the whole curing period, so the shrinkage rate of T-40% is much greater than the number of other groups, including T-0%.

Resistance to Sulfate Attack
Sulfate attack is a more dangerous form of deterioration, which is widely present in building structures, and it is another important indicator of durability [26]. Sulfate attack is a complex physical and chemical process. The free SO4 -in the saturated sulfate solution reacts with the calcium hydroxide in the mortar and the aluminum phase substances in the cement to form expansive substances (expandable gypsum and ettringite), these expansive substances start to fill the internal voids of the mortar and increase the strength

Resistance to Sulfate Attack
Sulfate attack is a more dangerous form of deterioration, which is widely present in building structures, and it is another important indicator of durability [26]. Sulfate attack is a complex physical and chemical process. The free SO 4 − in the saturated sulfate solution reacts with the calcium hydroxide in the mortar and the aluminum phase substances in the cement to form expansive substances (expandable gypsum and ettringite), these expansive substances start to fill the internal voids of the mortar and increase the strength of the mortar. This stage is called the compaction stage. With the continuous progress of the chemical reaction, there is no extra space to load expanded gypsum and ettringite. These expandable substances will produce expansion stress on the pore wall. Once the ultimate tensile stress borne by the pore wall is exceeded, the pore structure will be destroyed. The edges and corners of the test block are broken and microcracks are generated, which is called the micro-crack propagation stage. The generation of microcracks provides a transport channel for more sulfate ions to enter the interior of the mortar. These sulfate ions not only consume calcium ions (mainly from calcium hydroxide in the pore solution), but also consume cohesive C-S-H gel, AFm and hydration products containing aluminum phase such as calcium sulfoaluminate hydration. These chemical activities severely damaged the stability of the internal pore structure of the mortar, increased the area of the transition zone between the aggregate and the matrix, and caused a sharp drop in the strength of the mortar. This stage is called the rapid deterioration stage. Figure 8 shows the appearance of deterioration after five groups of cube mortar specimens (T-0%, T-10%, T-20%, T-30% and T-40%) fully immersed in 5% sodium sulfate solution for 30 days and 120 days. Table 6 gives the strength loss rate after T-0%, T-10%, T-20%, T-30% and T-40% sulfate attack.
It can be seen that after 30 days of full immersion, there are no obvious visible cracks on the surface of all the specimens. With the increase of the replacement rate of copper tailings, there is no obvious rule of the strength loss rate. Except for the decrease in compressive strength of T-20% and T-40%, the compressive strength of other specimen groups increased after sulfate attack (Table 6). This suggests that T-0%, T-10% and T-30% are in the compacting stage, while T-20% and T-40% are in the early stage of microcrack propagation. It shows that the external sulfate ion has reacted with the calcium-rich hydration product Ca(OH) 2 or C-S-H gel on the surface of the specimen to form swelling corrosion products (mainly ettringite and gypsum). There may already be micro-cracks inside to provide a convenient channel for more sulfates to enter [26]. T-10% has obvious large missing corners and micro-cracks, and the strength loss rate is −12.15%, indicating that T-10% is in the late stage of rapid deterioration. The surface of T-20% has part missing corners and the strength loss rate is −7.64%, indicating that T-20% is in the micro-crack propagation stage. Corners of T-30% have slight peeling and the strength loss rate is −2.66%, implying that T-20% is in the early stage of micro-crack propagation. T-40% seems to have no obvious erosion damage and the strength loss rate is 4.16% (minimal loss of strength). The strength value of T-40% immersion for 120 days is still in the rising stage, so it is considered to still be in the compacting stage. It can be seen that there is a correspondence between the apparent deterioration and the strength loss of the copper tailings mortar in Figure 8 and Table 6. Generally, the more severe the surface deterioration, the greater the loss of strength. It is concluded that with the increase of copper tailings, the resistance to sulfate attack is enhanced. The main reason is that the filler effect of micron scale copper tailings optimizes the internal pore structure of the mortar and effectively prevents the input of sulfate ions. of the mortar. This stage is called the compaction stage. With the continuous progress of the chemical reaction, there is no extra space to load expanded gypsum and ettringite. These expandable substances will produce expansion stress on the pore wall. Once the ultimate tensile stress borne by the pore wall is exceeded, the pore structure will be destroyed. The edges and corners of the test block are broken and microcracks are generated, which is called the micro-crack propagation stage. The generation of microcracks provides a transport channel for more sulfate ions to enter the interior of the mortar. These sulfate ions not only consume calcium ions (mainly from calcium hydroxide in the pore solution), but also consume cohesive C-S-H gel, AFm and hydration products containing aluminum phase such as calcium sulfoaluminate hydration. These chemical activities severely damaged the stability of the internal pore structure of the mortar, increased the area of the transition zone between the aggregate and the matrix, and caused a sharp drop in the strength of the mortar. This stage is called the rapid deterioration stage. Figure 8 shows the appearance of deterioration after five groups of cube mortar specimens (T-0%, T-10%, T-20%, T-30% and T-40%) fully immersed in 5% sodium sulfate solution for 30 days and 120 days. Table 6 gives the strength loss rate after T-0%, T-10%, T-20%, T-30% and T-40% sulfate attack.    MIP experiment is the most commonly used and reliable method to characterize the internal pore structure of mortar. The pores of the internal structure of the mortar are usually divided into four levels: gel pores (pore size less than 10 nm), transition pores (10~100 nm), capillary pores (100~1000 nm) and macro pores (greater than 1000 nm). The gel pores are mainly the cavities left after the hydration product C-S-H gel is filled, with the smallest pore volume and basically no effect on the strength. Transition pores mainly refer to the unfilled spaces of large-sized hydration products such as calcium hydroxide, ettringite, and agglomerated C-S-H gel. Spaces that are not filled by hydration products and aggregates may be large pores or the transition zone between the slurry and the aggregate interface. Those with a size less than 1000 nm are considered to be capillary pores, and the rest are macro pores. These two types of pores have a direct impact on the strength. In the early stage of cement hydration (curing time <28 days), large pores may be the main factor affecting the strength. Since the mortar has a water-cement ratio of 0.55, there will be larger pores at the initial stage of hydration, and the large pores will be continuously filled in the later stage of cement hydration; the pore structure distribution will move to small pores, and the pore structure will be continuously optimized. Table 7 gives the pore characteristic parameters of T-0% and T-30% at the curing ages of 7 days, 28 days and 90 days (including total porosity, average pore size, most probable pore size and fractal dimension). The most probable pore size means the pore size corresponding to the largest pore volume. The fractal dimension represents the roughness and complexity of the pore structure. Currently, the larger the fractal dimension, the more complex the internal structure and the rougher the pore surface. Figure 9a-c shows the pore accumulation curve and pore size distribution diagram of T-0% and T-30% at the ages of 7 days, 28 days and 90 days. Table 7. Pore characteristic parameters of T-0% and T-30% after 7 days, 28 days and 90 days.

T-0% T-30% T-0% T-30% T-0% T-30%
Curing First, Figure 9a shows the pore size distribution (including the cumulative pore size curve and the pore size distribution curve) for T-0% and T-30% ages at seven days. T-30% and T-0% have little difference for pore size range of the gel. The pore volume of T-30% is slightly larger than T-0% for transition pore size range. The pore volume of T-30% is obviously smaller than T-0% for capillary pore and macropore interval. This shows that T-30% increases the transition pores and reduces the number of capillary pores and macropores. The copper tailings in the early hydration stage have obvious micro-aggregate filler effects. The pore parameters of T-0% and T-30%, such as total porosity, average pore size, most probable pore size and fractal dimension are 20.51%, 20.77%, 22.81 nm, 21.53 nm, 77.16 nm, 40.25 nm, 2.968 and 3.008.
The total porosity of T-0% and T-30% are similar. The average pore size and most probable pore size of T-30% are smaller than T-0% and the fractal dimension is larger. This declares that the replacement of river sand with 30% copper tailings did not significantly reduce the total porosity of the mortar. However, a large amount of copper tailings effectively filled the micron-sized pores and increased the roughness of the pore structure. Figure 9b shows the pore size distribution (including pore cumulative curve and pore distribution curve) of T-0% (28 days) and T-30% (28 days). The cumulative pore size curves of T-0% and T-30% almost coincide with the pore size distribution curves. At this moment, 30% copper tailings seem to have the same effect as 30% river sand. The pore parameters of T-0% and T-30%, such as total porosity, average pore size, most probable pore size and fractal dimension are 18 Table 7. Pore characteristic parameters of T-0% and T-30% after 7 days, 28 days and 90 days. First, Figure 9a shows the pore size distribution (including the cumulative pore curve and the pore size distribution curve) for T-0% and T-30% ages at seven days. T and T-0% have little difference for pore size range of the gel. The pore volume of T-3 slightly larger than T-0% for transition pore size range. The pore volume of T-30% i viously smaller than T-0% for capillary pore and macropore interval. This shows th 30% increases the transition pores and reduces the number of capillary pores macropores. The copper tailings in the early hydration stage have obvious micro-a gate filler effects. The pore parameters of T-0% and T-30%, such as total porosity, ave pore size, most probable pore size and fractal dimension are 20.51%, 20.77%, 22.81 21.53 nm, 77.16 nm, 40.25 nm, 2.968 and 3.008.

T-0% T-30% T-0% T-30% T-0% T-
The total porosity of T-0% and T-30% are similar. The average pore size and probable pore size of T-30% are smaller than T-0% and the fractal dimension is larger declares that the replacement of river sand with 30% copper tailings did not signific reduce the total porosity of the mortar. However, a large amount of copper tailings e tively filled the micron-sized pores and increased the roughness of the pore structur Figure 9b shows the pore size distribution (including pore cumulative curve and distribution curve) of T-0% (28 days) and T-30% (28 days). The cumulative pore curves of T-0% and T-30% almost coincide with the pore size distribution curves. A moment, 30% copper tailings seem to have the same effect as 30% river sand. The parameters of T-0% and T-30%, such as total porosity, average pore size, most prob Compared with T-0%, T-30% has larger total porosity, smaller average pore size and most probable pore size, and larger fractal dimension. This shows that the replacement of river sand with 30% copper tailings will increase the total pores at the age of 28 days, but still has the effect of refining the pore size, and the complexity of the internal pore space becomes more obvious. Figure 9c gives pore size distribution (including pore cumulative curve and pore distribution curve) of T-0% (90 days) and T-30% (90 days). The pore accumulation curves of T-0% and T-30% in the intervals of capillary pores and macro pores basically coincide, but in the gel pores and transition pores interval, the pore volume of T-30% is obviously larger than that of T-0%. The pore parameters of T-0% and T-30%, such as total porosity, average pore size and most probable pore size are 14.46%, 16 It can be seen that the total porosity of T-30% is higher than T-0% when the hydration age reaches 90 days, the average pore size and the most probable pore size are both larger, and the fractal dimension is smaller. The pore structure of T-30% is looser. It is worth noting that the fractal dimension of T-0% increases with the increase of the curing age, indicating that the increase of hydration products causes the internal structure to be denser and rougher. However, the fractal dimension of T-30% decreases with the increase of curing age. At the initial hydration stage (seven days), the hydration product C-S-H gel is too small to encapsulate the sharp copper tailings, leading to the increase of internal pore structure roughness. Therefore, the fractal dimension of T-30% (seven days) is greater than T-0%. With the continuous hydration, the products are constantly generated to fill and smooth the edges and corners of copper tailings, so the fractal dimension decreases and is lower than T-0%. Accordingly, the sharp edges and corners of copper tailings can effectively increase the pore structure roughness in addition to mechanical bite force.

Binary Image Analysis Based on SEM
In fact, although the MIP experiment is a common test method for studying mortar pores, its results are not intuitive enough to express the pore structure. It is impossible to calculate closed pores and there will still be measurement errors for non-cylindrical pores and ink bottle-shaped pores [27]. Here, this article attempts to use Image-pro software to make binary images of SEM pictures with the gray value threshold value [28], visually and clearly observe the pore characteristics of the micro-section of the mortar, and quantitatively count the number of pores, the maximum area and the area ratio, and combing with the MIP results to analyze the effects of T-0% and T-30% pore structure on the mortar strength, shrinkage and sulfate attack resistance. This analysis is based on the fact that substances with different densities in the electron microscope images correspond to different gray values. For example, the pores with the smallest density appear black, while the unhydrated cement particles with higher density appear bright white [29]. Figure 10a,b show the surface morphologies of T-0% (7 days) and T-30% (7 days), respectively. In Figure 10a, needle-like ettringite and granular C-S-H can be observed crossstacked, and there are obvious holes (original SEM image). In Figure 10b, the granular C-S-H is filled with some net-like C-S-H, and the surface looks denser (original SEM image). Then, comparing the binary images after Image-pro software processing, it is found that the pore distribution of T-30% (seven days) is more uniform and the interface micro-cracks are narrower.  Figure 11a,b show the surface morphologies of samples T-0% (28 days) and (28 days), respectively. The micro section of T-0% (28 days) has no obvious interface but there are obvious large pores. T-30% (28 days) has aggregate interface area an pores. After Image-pro software is processed, the binary image can more clearly ca the micro-interfaces and pores. Similar to the conclusion in the previous paragraph pared with T-0% (28 days), T-30% (28 days) has more pores (white dots) and a larg terface area, but the pores in other areas are more refined.   ) and T-30% (28 days), respectively. The micro section of T-0% (28 days) has no obvious interface area, but there are obvious large pores. T-30% (28 days) has aggregate interface area and tiny pores. After Image-pro software is processed, the binary image can more clearly capture the micro-interfaces and pores. Similar to the conclusion in the previous paragraph, compared with T-0% (28 days), T-30% (28 days) has more pores (white dots) and a larger interface area, but the pores in other areas are more refined.  Figure 11a,b show the surface morphologies of samples T-0% (28 days) and T (28 days), respectively. The micro section of T-0% (28 days) has no obvious interface but there are obvious large pores. T-30% (28 days) has aggregate interface area and pores. After Image-pro software is processed, the binary image can more clearly ca the micro-interfaces and pores. Similar to the conclusion in the previous paragraph, pared with T-0% (28 days), T-30% (28 days) has more pores (white dots) and a larg terface area, but the pores in other areas are more refined.  The T-0% (90 days) micro-section aggregate part is wrapped by dense hydration products; there are still obvious small pores, and the o pore structure is relatively dense. The micro section of T-30% (90 days) looks rela loose, and the interface transition zone and small pores still exist. The binary image that the number of T-30% (90 days) pores (white dots) is obviously more than tha 0% (90 days). After 90 days of curing, with the continuous generation of hydration ucts, the large pores of T-0% (28 days) in the medium are filled with hydration pr into small pores or directly filled densely. And T-30% still has more micro pores.  The T-0% (90 days) micro-section aggregate part is tightly wrapped by dense hydration products; there are still obvious small pores, and the overall pore structure is relatively dense. The micro section of T-30% (90 days) looks relatively loose, and the interface transition zone and small pores still exist. The binary image shows that the number of T-30% (90 days) pores (white dots) is obviously more than that of T-0% (90 days). After 90 days of curing, with the continuous generation of hydration products, the large pores of T-0% (28 days) in the medium are filled with hydration products into small pores or directly filled densely. And T-30% still has more micro pores.
wrapped by dense hydration products; there are still obvious small pores, and the o pore structure is relatively dense. The micro section of T-30% (90 days) looks rela loose, and the interface transition zone and small pores still exist. The binary image s that the number of T-30% (90 days) pores (white dots) is obviously more than tha 0% (90 days). After 90 days of curing, with the continuous generation of hydration ucts, the large pores of T-0% (28 days) in the medium are filled with hydration pro into small pores or directly filled densely. And T-30% still has more micro pores.  Table 8 shows the pore parameters of the mortar micro-section in the binary i the pores of T-0% (seven days) and T-30% (seven days), such as pore number, av area and area ratio are 5010, 4810, 7.19 μm 2 , 5.53 μm 2 , 4.05% and 2.95%, respectively. pared with T-0% (seven days), the micro section of T-30% (seven days) has fewer nu of pores, and the average area and area ratio are smaller. MIP experiment reveals th total porosity and fractal dimension of T-30% are slightly larger than T-0%, and the age pore size and the most probable pore size are smaller. Although the conclusio slightly different, the binary image analysis is more intuitive (pictures and statisti sults), indicating that the 30% copper tailings instead of river sand can effectively the pores in the early stage of hydration (seven days). The reasons for the optimizat the pore structure: (1) Copper tailings are used as fine aggregates, and the gradation is closer to the Fuller ideal curve, the mixed aggregate gradation is better and the pactness becomes larger (provided in Section 3.1). (2) The micron scale of copper ta becomes an excellent filler, effectively filling the micro pores of the mortar (micro a gate effect).   Table 8 shows the pore parameters of the mortar micro-section in the binary image, the pores of T-0% (seven days) and T-30% (seven days), such as pore number, average area and area ratio are 5010, 4810, 7.19 µm 2 , 5.53 µm 2 , 4.05% and 2.95%, respectively. Compared with T-0% (seven days), the micro section of T-30% (seven days) has fewer number of pores, and the average area and area ratio are smaller. MIP experiment reveals that the total porosity and fractal dimension of T-30% are slightly larger than T-0%, and the average pore size and the most probable pore size are smaller. Although the conclusions are slightly different, the binary image analysis is more intuitive (pictures and statistical results), indicating that the 30% copper tailings instead of river sand can effectively refine the pores in the early stage of hydration (seven days). The reasons for the optimization of the pore structure: (1) Copper tailings are used as fine aggregates, and the gradation curve is closer to the Fuller ideal curve, the mixed aggregate gradation is better and the compactness becomes larger (provided in Section 3.1). (2) The micron scale of copper tailings becomes an excellent filler, effectively filling the micro pores of the mortar (micro aggregate effect).      The pore number, average area and area ratio of T-0% (28 days) and T-30% (28 days) are 4363, 7349, 7.90 µm 2 , 5.65 µm 2 , and 3.86%, 4.67%, respectively. Compared with T-0% (28 days), T-30% (28 days) has more pores and a larger pore area ratio, but the average area is smaller. The MIP experiment suggests that the total porosity of T-30% (28 days) is higher than that of T-0% (28 days), the average pore size is slightly smaller, the fractal dimension is larger and the pore size distribution is similar (Figure 9b) [4]. The MIP experiment concluded that the pore structure of T-30% is relatively loose. However, the binary image analysis provides the image basis that T-30% has more micro pores and more uniform pore distribution. In addition to the reasons for (1) and (2) in the previous section, this pore feature is also due to the release of water from the copper tailings, which makes a water film around the copper tailings aggregate. This behavior dilutes the water-cement ratio of the interface slurry, resulting in a weakening of the interface between the copper tailings and the cement paste matrix. Compared with micron scale copper tailings, the millimeter size of river sand magnifies the interface damage effect, and it is easier to form large-scale cracks around the river sand (Figure 11a). Although the interface adhesion of copper tailings is poor, the stable and uniform small pore structure (Figure 11b and Table 8) is not prone to damage caused by stress concentration when subjected to external pressure, so T-30% strength is higher. However, the total porosity of T-30% (28 days) is large, and the increase of capillary pores makes the mortar specimen shrink more obviously (Figure 7). Therefore, this more interfacial small pore structure (diluted water-cement ratio) has a lower concentration of Ca(OH) 2 solution. The hydration product C-S-H is looser, which provides more space for the conversion of sulfate ions into interface ettringite and reduces the damage to the original pore structure. In addition, the lower calcium ion pore solution at the interface between the tailings powder and the cement paste also hinders the recrystallization process of the interface ettringite and weakens the expansion and failure of the recrystallization pressure of the interface pores ( Figure 8 and Table 6).
The pore number, average area and area ratio of T-0% (90 days) and T-30% (90 days) white areas (representing pores) are 2438, 3602, 4.737 µm 2 , 5.64 µm 2 , 1.28% and 2.25%, respectively. Compared with T-0% (28 days), T-30% (28 days) has more pore numbers and larger average area and area ratio than T-0% (90 days). It shows that adding 30% copper tailings reduces the filling rate of hydration products in the later stage. The water-release stage reduces the alkalinity of the pore solution and forms loose C-S-H around the copper tailings. Moreover, locally high water-cement ratio makes more interface micro pores difficult to be filled (Figure 12b), and the later hydration filling rate decreases. The growth of the compressive strength becomes slower, although it is higher than the control group (T-0%). The shrinkage deformation of T-0% is basically stable at 14 days, while T-30% is stable at 28 days and slightly higher than T-0%. The decrease of the filling rate makes the pore space larger, carries more sulfate-eroded swelling substances, and alleviates the physical expansion effect of 5% sulfate full erosion, which is similar to the explanation in the previous paragraph.

Leaching Test
To detect the environmental hazard of copper tailings mortar, this paper conducted a leaching test on the T-30% (curing for 28 days and 90 days) and recorded the pH of the leaching solution and the leaching concentration of heavy metals. The leaching test in this paper was carried out with reference to the British Standard BS EN12457-2002 [20]. The leaching agent was distilled water, the s/L ratio was 1:10 (l/kg), and the stirring mode was standing for 24 h. Table 9 shows the pH of the T-0% and T-30% leaches. T-30% (curing age 28 days and 90 days) has almost no effect on the pH of the leach. What is important is that ICP-OES is used to detect heavy metal elements in the T-30% (28 days and 90 days curing) leaching solution. The results are shown in Table 10. Group 1 uses XRF to detect six heavy metal elements Sr (19.452), Zr (8.567), Ga (3.270), Cu (56.100), Zn (44.400) and As (4.998) mg/g in copper tailings. It can be seen that the content of Sr, Cu and Zn is higher. If copper tailings as fine aggregate mixed into mortar, T-30% (28 days) in group 2 can only solidify four heavy metal elements (Ga, Cu, Zn and As), and the Sr and Zr elements in the leaching solution are still out of standard state. The six heavy metals in the T-30% (90 days) leachate of group 3 basically meet the environmental quality standard limit. This indicates that copper tailings mortar T-30% has an obvious curing effect on heavy metals in the late curing, and Sr and Zr elements are not cured in the early curing. Therefore, the environmental hazards caused by the loss of heavy metals from copper tailings mortar should not be ignored in actual projects, and the maintenance work of moisture-proof and leaching prevention of copper tailings should be strengthened [30].

Conclusions
This paper attempted to replace natural sand with copper tailings, studied the properties of mixed fine aggregates and the performance and microstructure of copper tailings mortar, and obtained the following conclusions.

•
The characteristics of mixed fine aggregates were discussed, and it was found that the incorporation of copper tailings mainly increased the number of particles in a small interval near 0.15 mm, making the gradation curve closer to the ideal Fuller curve (n = 0.45), optimized river sand with poor gradation, and its compactness is increased.

•
The compressive strength of copper tailings mortar is basically higher than that of the control group T-0% in the 7-90 days curing age, especially T-30%. The shrinkage rate and the sulfate attack resistance increases with the increase of copper tailings.

•
The conclusion of binary image analysis is similar to the results of MIP experiment. However, the binary image can more clearly and intuitively express that T-30% have more, smaller, denser, more complex pores. The micro-aggregate effect (account for micron scale) is more obvious in the early stage of hydration, and the decrease of the hydration filling rate (reason for water release) in the later curing. • This paper verifies the environmental friendliness of copper tailings mortar through leaching tests. However, environmental pollution caused by the loss of heavy metals in the early stage (28 days) of copper tailings mortar maintenance should be avoided.