Ecofibers for the Reinforcement of Cement Mortars for Coating Promoting the Circular Economy

Nowadays, nobody can deny that climate change is a reality and that the life cycle of buildings contributes greatly to that reality. Therefore, proposals such as the circular economy must be integrated into the construction sector. This article shows part of the results of a research project whose objective is to introduce circular economy criteria in building materials, seeking new uses for construction and demolition waste from buildings. In particular, this article analyses the possibility of replacing fibres currently used to reinforce cement mortars with recycled fibres. After consulting the bibliography, we can conclude that some studies analyse the behaviour of cement mortars reinforced with different types of fibres, but none has been found that analyses the behaviour of these mortars for the application of continuous coatings. For this purpose, a two-stage experimental plan is designed to test cement mortar samples with different types of fibres, recycled fibres and commercial fibres, taking into consideration the characteristics that these mortars have to comply to be applied as continuous coatings. Moreover, a detailed study about the porosity of these mortars and its influence on how the mortars behave with regard to compression, water vapour permeability and impermeability has been conducted. From the results obtained, it can be concluded that the mortars containing recycled fibres have very similar resistance, absorption and permeability values to those containing commercial fibres, so that they might be suitable for application as external coatings.


Introduction
It is true that the climate has always been changing, but the problem is that currently the pace is faster than humans have ever seen. If this pace is maintained over time, if we do not stop it, climate change threatens to make parts of the planet uninhabitable for life as we know it.
It has been scientifically proven that the industry, and in particular the construction industry, is partially responsible for this problem since it is one of the sectors that consumes more resources and generates more emissions and waste [1]. Therefore, working to reduce the impact it generates is essential [2].
According to the UK Green Building Council (UKGBC), the construction sector uses more than 400 million tons of material each year. In particular, the products that are used during the construction process can damage the environment due to intensive extraction of raw materials, transporting to manufacturing plant and site, energy consumption in manufacture and in use, waste generation and so on [3].
The properties of mortars depend not only on their composition but also on certain external conditions such as the preparation of the substrate, the application of the product and the protection of the coating.
Cement-based coatings require compressive strength and water absorption that are achieved with relatively low cement dosages. In fact, it can be affirmed [27] that the proportion of cement added to the mortar is directly related to their impermeability and rigidity. Mortars with larger proportions of cement are more rigid, which means a greater probability of cracks appearing, which are their main setback. Mortars used in these study trials seek a balance between rigidity and impermeability without sacrificing good results in both aspects, which are fundamental in a good coating mortar.
Cracking can occur for different reasons, which have been studied in detail by several authors [28]. The primary causes range from microcracks caused by shrinkage during the setting or drying of the binder to the low plastic deformability of the mortar [29] and are usually combined with others of a secondary nature, such as sensitivity to thermal or mechanical actions [30].
A key consequence of the cracking of coating mortars is the increase in their permeability to water [31]. The appearance of cracks in the mortar causes major permeability problems both in the short and long term. One of the immediate problems is the appearance of dampness inside enclosures; one of the long-term problems is the logical increase (by attrition) in the size of the cracks and the consequent degradation of the mortar.
Different strategies are used to prevent this cracking. These include the use of additions to improve mortar plasticity [32], the incorporation of different types of fibres in their preparation [33], or the insertion of meshes or reinforcements between coating layers. These techniques can be used together to reduce the possibility of cracks but do not always eliminate them completely.
However, there is agreement in the academic community that the appearance of a crack implies a change in the permeability of the material. This leads to a reduction in its durability, since once the crack has occurred the properties of the material change drastically, and it cannot be assumed that the estimated durability for an uncracked surface can be maintained [28].

Purpose
This article shows part of the results of a research project that analyses the viability of replacing, in mortars for coatings, glass and polypropylene fibres (fibres commonly used today) by fibres from the recycling of mineral wool insulation panels [13] and analyses their cracking and water behaviour.

Experimental Plan
A two-phase experimental plan was designed to analyse the behaviour of these mortars with respect to the requirements of current regulations: resistance to compression and water absorption. The relationship between shrinkage cracks and mortar porosity with the different types of fibres used was also included in the experimental plan.

Materials
Cem II/B-L 32.5 N cement and natural river sand sieved through a 4 mm mesh screen from a gravel pit or quarry were used.
The water used comes from the Canal de Isabel II of the Community of Madrid. Its technical characteristics are established in standard UNE EN 13279-2 [34].
Three types of mineral wool waste were also used ( Figure 1). These were collected manually from the Centre for the Integral Treatment of Construction and Demolition Waste on the N-1 motorway to Irún, Km 40, in the town of El Molar, Community of Madrid and managed by Gestión y Desarrollo del Medio Ambiente de Madrid (GEDESMA S.A.) They were stored outdoors and mixed with other waste materials. After selecting this waste, it was separated into piles of hand rock wool (RLR) and fibreglass (RFV). A sample of unselected mixed mineral wool waste, as it was found in the landfill, was also collected (RMIX). The three types of mineral fibre residues were subjected to grinding in a 550 W machine at a nominal voltage of 50 Hz, for 3 intervals of 3 min each, to obtain a format that was suitable to be included in the mortars with a length of 500-1000 µm.
Sustainability 2020, 11, x FOR PEER REVIEW 4 of 15 y Desarrollo del Medio Ambiente de Madrid (GEDESMA S.A.) They were stored outdoors and mixed with other waste materials. After selecting this waste, it was separated into piles of hand rock wool (RLR) and fibreglass (RFV). A sample of unselected mixed mineral wool waste, as it was found in the landfill, was also collected (RMIX). The three types of mineral fibre residues were subjected to grinding in a 550 W machine at a nominal voltage of 50 Hz, for 3 intervals of 3 min each, to obtain a format that was suitable to be included in the mortars with a length of 500-1000 µm. The commercial polypropylene fibres used were 6-metre long SikaCim ® Fibres-6 for concrete and mortars from Sika, S.A.U. and 12 mm long AR Tecnicret ® fibreglass ( Figure 2).

Composition of the mixtures
Six different cement mortar mixtures were prepared in the laboratory: a reference mortar without fibres (MREF), three mortars with mineral wool waste from insulation: mortar with rock wool waste (MRLR), mortar with fibreglass waste (MRFV) and mortar with a combination of mineral wool waste (MMIX), and two mortars with commercial fibres to compare their behaviour with the recycled samples: mortar with fibreglass (MFV), mortar with polypropylene fibre (MPP).
The dosage maintained in all mixtures is 1:3:0.6 (cement: sand: water), (Table 1); this dosage was established based on the bibliography consulted [19][20][21] and the results can be compared with other previous works [13].  The commercial polypropylene fibres used were 6-metre long SikaCim ® Fibres-6 for concrete and mortars from Sika, S.A.U. and 12 mm long AR Tecnicret ® fibreglass ( Figure 2). y Desarrollo del Medio Ambiente de Madrid (GEDESMA S.A.) They were stored outdoors and mixed with other waste materials. After selecting this waste, it was separated into piles of hand rock wool (RLR) and fibreglass (RFV). A sample of unselected mixed mineral wool waste, as it was found in the landfill, was also collected (RMIX). The three types of mineral fibre residues were subjected to grinding in a 550 W machine at a nominal voltage of 50 Hz, for 3 intervals of 3 min each, to obtain a format that was suitable to be included in the mortars with a length of 500-1000 µm. The commercial polypropylene fibres used were 6-metre long SikaCim ® Fibres-6 for concrete and mortars from Sika, S.A.U. and 12 mm long AR Tecnicret ® fibreglass ( Figure 2).

Composition of the mixtures
Six different cement mortar mixtures were prepared in the laboratory: a reference mortar without fibres (MREF), three mortars with mineral wool waste from insulation: mortar with rock wool waste (MRLR), mortar with fibreglass waste (MRFV) and mortar with a combination of mineral wool waste (MMIX), and two mortars with commercial fibres to compare their behaviour with the recycled samples: mortar with fibreglass (MFV), mortar with polypropylene fibre (MPP).
The dosage maintained in all mixtures is 1:3:0.6 (cement: sand: water), (Table 1); this dosage was established based on the bibliography consulted [19][20][21] and the results can be compared with other previous works [13].

Composition of the Mixtures
Six different cement mortar mixtures were prepared in the laboratory: a reference mortar without fibres (MREF), three mortars with mineral wool waste from insulation: mortar with rock wool waste (MRLR), mortar with fibreglass waste (MRFV) and mortar with a combination of mineral wool waste (MMIX), and two mortars with commercial fibres to compare their behaviour with the recycled samples: mortar with fibreglass (MFV), mortar with polypropylene fibre (MPP).
The dosage maintained in all mixtures is 1:3:0.6 (cement: sand: water), (Table 1); this dosage was established based on the bibliography consulted [19][20][21] and the results can be compared with other previous works [13].

Tests
The experimental plan was conducted in two phases: Phase 1 In the first phase, 4 × 4 × 16 cm specimens are made of the reference mortar and the mortars reinforced with commercial fibres and fibres from the recycling of RCD ( Figure 3). The experimental plan was conducted in two phases: Phase 1 In the first phase, 4 × 4 × 16 cm specimens are made of the reference mortar and the mortars reinforced with commercial fibres and fibres from the recycling of RCD ( Figure 3). The physical, mechanical and behavioural tests against water were carried out on these specimens, as listed below: Bulk density of fresh mortar (UNE-EN 1015-6) [35]: it has been calculated as the mass of each of the mixtures divided by the volume occupied by the mortar introduced and compacted in a container. The mass considered has been that necessary to fill the 1-L container. The filling of the container has been carried out in two stages. In the first one, half of the container is filled and tapped 10 times for compaction; in the second stage, the container is filled to its limit and compacted again by striking it 10 times.
Compressive strength: (UNE-EN 1015-11) [25]: The Ibertest Autotest 200 cement strength testing machine was used in 4 × 4 × 16 cm 3 specimens. With constant speed, a load was gradually applied at a rate between 50 and 500 N/s until failure occurs and the value obtained was recorded.
Consistence (UNE-EN 1015-3) [36]: The flow table method was used, according to the procedure described in part 3 of the standard. The fresh mortar is poured in two layers on a frustoconical mould placed on the shaking table; each layer is compacted with ten tapping strokes. After 15 s, the mould is removed, and 15 vertical shakes are carried out with a constant frequency of approximately 1 s. using the calliper, the diameter of the mortar is measured in two perpendicular directions and the average value is calculated.
Water absorption by capillarity (UNE-EN 1015-18): [26] It was calculated by obtaining the amount of water absorbed by the 160 × 40 × 40 mm prismatic samples cured after 28 days and dried in an oven. The test specimens are impregnated with paraffin and then broken into two halves. On the break side they are submerged in water with a depth of between 5 and 10 mm.
Total absorption: The specimens are dried in a stove for 24 h, cooled in a desiccator to ambient laboratory temperature, and subsequently immersed in water, weight increases by water absorption after 24 and 48 h were recorded.
Water vapour permeability (UNE-EN 1015-19): [37]: The amount of water that has passed per unit area of the specimen in a unit of time when there is a pressure difference of one unit between its walls. The physical, mechanical and behavioural tests against water were carried out on these specimens, as listed below: Bulk density of fresh mortar (UNE-EN 1015-6) [35]: it has been calculated as the mass of each of the mixtures divided by the volume occupied by the mortar introduced and compacted in a container. The mass considered has been that necessary to fill the 1-L container. The filling of the container has been carried out in two stages. In the first one, half of the container is filled and tapped 10 times for compaction; in the second stage, the container is filled to its limit and compacted again by striking it 10 times.
Compressive strength: (UNE-EN 1015-11) [25]: The Ibertest Autotest 200 cement strength testing machine was used in 4 × 4 × 16 cm 3 specimens. With constant speed, a load was gradually applied at a rate between 50 and 500 N/s until failure occurs and the value obtained was recorded.
Consistence (UNE-EN 1015-3) [36]: The flow table method was used, according to the procedure described in part 3 of the standard. The fresh mortar is poured in two layers on a frustoconical mould placed on the shaking table; each layer is compacted with ten tapping strokes. After 15 s, the mould is removed, and 15 vertical shakes are carried out with a constant frequency of approximately 1 s. using the calliper, the diameter of the mortar is measured in two perpendicular directions and the average value is calculated.
Water absorption by capillarity (UNE-EN 1015-18): [26] It was calculated by obtaining the amount of water absorbed by the 160 × 40 × 40 mm prismatic samples cured after 28 days and dried in an oven. The test specimens are impregnated with paraffin and then broken into two halves. On the break side they are submerged in water with a depth of between 5 and 10 mm.
Total absorption: The specimens are dried in a stove for 24 h, cooled in a desiccator to ambient laboratory temperature, and subsequently immersed in water, weight increases by water absorption after 24 and 48 h were recorded.
Water vapour permeability (UNE-EN 1015-19): [37]: The amount of water that has passed per unit area of the specimen in a unit of time when there is a pressure difference of one unit between its walls.
For this purpose, circular specimens are made with fresh mortar. After curing, these specimens are placed on perimeter sealed containers. These vessels contain a saline solution of potassium nitrate that maintains the relative humidity at 93.2%. The difference in relative humidity between the two faces of the test piece causes the water to gradually evaporate.
Phase 2 In the second phase, a detailed study of the shrinkage cracking and porosity was conducted on the previous mortars, as described below: Contraction test (UNE 80112) [38]: (shrinkage): Changes in length of each sample were measured compared to the original length. The specimens used, measuring 25x25x285 mm3, had stainless steel cylinders at their ends, to be placed in a vertical position, on the length comparator, at the time of measurement. This measurement has been carried out at mould release, at 7 days and at 14 days.
Air content (UNE-EN 1015-7) [39]: Obtained by means of the pressure method in which pressurized air was applied to the chamber containing the mortar and, when it decreased, the air content present in the sample was indicated on the measuring device. This test was carried out by filling, in four layers, the container with fresh mortar. Each layer was compacted with 10 short strokes of the piston. Once the container-to which a manometer had been connected-was levelled, air was injected into the air chamber until it reached a stable pressure, which was determined in a first calibration test. The valves were closed and, once equilibrium was reached, the air content value was read from the manometer.
Porosimetry by injection of Hg: The AutoPore IV 9500 porosimeter was used to characterize the porosity of the material by applying several pressure levels to the sample submerged in mercury, with the pressure required to produce the penetration of the mercury being inversely proportional to the size of the pores. The specimens made for this test were cylindrical, with a diameter of 10 mm and a height of 10 mm. The test was carried out at room temperature, bringing the sample to a vacuum of 50 µmHg that was kept for five minutes. Subsequently, each sample was subjected to increasing pressures that force the mercury percolation into the pores up to 206MPa.
Scanning electron microscopy: The JEOL JSM-840 high-resolution environmental scanning microscope was used to study of the crystalline texture and morphology of the 6 different mortar mixtures. This microscope allows the observation of samples of sizes up to 50-100-150 mm in the motorized stage. The samples tested, small fragments of approximately 10x10 mm2, were taken from rests of the specimens that were subjected to flexion and compression tests. Once placed under the microscope, "the beam passes through the condenser and objective lenses, and is swept across the sample by the scanning coils, while a detector records the number of low-energy secondary electrons emitted for each point on the surface ", so that an SEM image is formed [40].

Results Obtained in Phase 1
The results obtained from the physical, mechanical and water behaviour tests are shown. Figure 4, shows the average of the results obtained in three test specimens of each mixture of the bulk density test on the fresh mortar and the consistency of the mixtures. It can be seen that adding fibres, whether they be from waste or commercial sources, decreases their density with regard to the reference mixture (MREF) but very slightly due to the small amount of fibres added. The mortar containing commercial fibres MPP has the lowest density (1201 kg/m 3 ) very similar to that containing MRFV fibre waste (1204 kg/m 3 ), representing only a decrease of 2.50% in comparison with the reference density (1232 kg/m 3 ). MFV and MRLR mixtures have the highest density value (1216 kg/m 3 ), although this is 1.30% lower than the reference mortar. It should be noted that all of them could be considered as lightweight mortars as they have a density of less than 1300 kg/m 3 according to UNE EN 1015-6 [35].

Apparent Density of Fresh Mortar and Consistency
Regarding It should be pointed out that MRFV and MFV mortars behave differently, while the former has a lower density value and a drier consistency (within the plasticity range), the latter has a higher density value with a higher, more fluid consistency.

Compressive strength test
Compressive strength of the test pieces after the test is shown in Figure 5. These results are the average of those obtained in 3 test specimens of each mixture considered.
Compressive strength for mortars MRLR-MRFV decreased by 0.04%-10.53% in relation to the reference and, on the contrary, mortars MMIX-MPP-MFV increased by 9.34%-1.06%-7.56%. Similar to what occurs in the compressive strength test in the previous section, the mortar containing the fibre waste with better compression resistance was MMIX (25.75 N/mm 2 ), and the worst was MRFV (21.07 N/mm 2 ). In the case of mortars with commercial fibres, MFV (25.33 N/mm 2 ) showed an improved performance of 3.39% compared to MPP (23.80 N/mm 2 ), as stated by other researchers [41,42].
In all cases, the minimum values established in standard UNE-EN 1015-11:2000/A1:2007 [25] were exceeded for the case of mortars R1 and/or R3, whose compressive strength should be 3.5-7.5 N/mm 2 and/or ≥ 6 N/mm 2 . It should be pointed out that MRFV and MFV mortars behave differently, while the former has a lower density value and a drier consistency (within the plasticity range), the latter has a higher density value with a higher, more fluid consistency.

Compressive Strength Test
Compressive strength of the test pieces after the test is shown in Figure 5. These results are the average of those obtained in 3 test specimens of each mixture considered.
Compressive strength for mortars MRLR-MRFV decreased by 0.04%-10.53% in relation to the reference and, on the contrary, mortars MMIX-MPP-MFV increased by 9.34%-1.06%-7.56%. Similar to what occurs in the compressive strength test in the previous section, the mortar containing the fibre waste with better compression resistance was MMIX (25.75 N/mm 2 ), and the worst was MRFV (21.07 N/mm 2 ). In the case of mortars with commercial fibres, MFV (25.33 N/mm 2 ) showed an improved performance of 3.39% compared to MPP (23.80 N/mm 2 ), as stated by other researchers [41,42].

Absorption of water by capillarity
The average of the results of the tests carried out on 3 test pieces of each mixture for the absorption of water by capillarity test is shown in Figure 6. These mortars must absorb as little as possible due to their application. This particularly affects mortars exposed to rainwater and those located at the base of the foundations. The greater the water absorption, the greater the possibilities of the appearance of moisture by filtration. In any case, the standard UNE-EN 1015-18 [26]: requires for mortars R1 c ≤ 0.4 kg/m 2 min 0.5 and mortars R3 c ≤ 0.2 kg/m 2 min 0.5 . While mortars containing fibre waste had a higher absorption coefficient in relation to the reference mortar, MRFV 16.7%, MRLR and MMIX 8.3%, this was considerably lower for mortars containing commercial fibres, MPP by 20.8% and MFV by 25%. The mortar with the greatest water absorption capacity by capillarity was MRFV (0.28 kg/m 2 •min 0.5 and the lowest capacity MFV (0.18 kg/m 2 •min 0.5 ). Therefore, all mortars in this study would comply with the specifications of standard mortars (R1) with medium resistance to filtration, and only mortars containing commercial fibres would comply with the provisions of mortars (R3), that is, with very high resistance to filtration. The

Absorption of Water by Capillarity
The average of the results of the tests carried out on 3 test pieces of each mixture for the absorption of water by capillarity test is shown in Figure 6. These mortars must absorb as little as possible due to their application. This particularly affects mortars exposed to rainwater and those located at the base of the foundations. The greater the water absorption, the greater the possibilities of the appearance of moisture by filtration. In any case, the standard UNE-EN 1015-18 [26]: requires for mortars R1 c ≤ 0.4 kg/m 2 min 0.5 and mortars R3 c ≤ 0.2 kg/m 2 min 0.5 .

Absorption of water by capillarity
The average of the results of the tests carried out on 3 test pieces of each mixture for the absorption of water by capillarity test is shown in Figure 6. These mortars must absorb as little as possible due to their application. This particularly affects mortars exposed to rainwater and those located at the base of the foundations. The greater the water absorption, the greater the possibilities of the appearance of moisture by filtration. In any case, the standard UNE-EN 1015-18 [26]: requires for mortars R1 c ≤ 0.4 kg/m 2 min 0.5 and mortars R3 c ≤ 0.2 kg/m 2 min 0.5 . While mortars containing fibre waste had a higher absorption coefficient in relation to the reference mortar, MRFV 16.7%, MRLR and MMIX 8.3%, this was considerably lower for mortars containing commercial fibres, MPP by 20.8% and MFV by 25%. The mortar with the greatest water absorption capacity by capillarity was MRFV (0.28 kg/m 2 •min 0.5 and the lowest capacity MFV (0.18 kg/m 2 •min 0.5 ). Therefore, all mortars in this study would comply with the specifications of standard mortars (R1) with medium resistance to filtration, and only mortars containing commercial fibres would comply with the provisions of mortars (R3), that is, with very high resistance to filtration. The  While mortars containing fibre waste had a higher absorption coefficient in relation to the reference mortar, MRFV 16.7%, MRLR and MMIX 8.3%, this was considerably lower for mortars containing commercial fibres, MPP by 20.8% and MFV by 25%. The mortar with the greatest water absorption capacity by capillarity was MRFV (0.28 kg/m 2 ·min 0.5 and the lowest capacity MFV (0.18 kg/m 2 ·min 0.5 ). Therefore, all mortars in this study would comply with the specifications of standard mortars (R1) with medium resistance to filtration, and only mortars containing commercial fibres would comply with the provisions of mortars (R3), that is, with very high resistance to filtration. The reference mortar would not meet the values established for mortars (R3) either, as occurs in other studies [43]. Figure 7 shows total water absorption values of the mixtures under study. These results are the average of the data obtained in the 3 test specimens of each mixture. It can be seen that, after 24 h, the samples are practically saturated since the increase is between 0% and 0.02%. Sustainability 2020, 11, x FOR PEER REVIEW 9 of 15 reference mortar would not meet the values established for mortars (R3) either, as occurs in other studies [43]. Figure 7 shows total water absorption values of the mixtures under study. These results are the average of the data obtained in the 3 test specimens of each mixture. It can be seen that, after 24 h, the samples are practically saturated since the increase is between 0% and 0.02%. In this test, all the mixtures exceeded the 4.5% increase in weight obtained by MREF, except for MMIX, which decreased its total absorption by approximately 8.90% with respect to said reference. It should be noted that, at 24 h, the mortar containing fibre waste with the greatest total absorption is MRLR (4.75%), compared to that containing commercial fibre, MPP (4.93%). MMIX (4.1%) and MFV (4.59%), with fibre waste and commercial fibres, respectively, have a lower total absorption capacity.

Permeability to water vapour
This section contains an analysis of the degree of resistance to the passage of water vapour through ready-made mortars. The previous section showed that mortars for outdoor use should be as impermeable as possible, and it should be noted that they must maintain their water vapour permeability to allow for transpiration of walls and prevent the appearance of condensation on the inside. Table 2 shows the results of the weights obtained during the 6-week duration of the water vapour permeability test in one test specimen of each mixture; Figure 8 shows the water vapour permeability values, which are very similar to those of the reference mortar.  In this test, all the mixtures exceeded the 4.5% increase in weight obtained by MREF, except for MMIX, which decreased its total absorption by approximately 8.90% with respect to said reference. It should be noted that, at 24 h, the mortar containing fibre waste with the greatest total absorption is MRLR (4.75%), compared to that containing commercial fibre, MPP (4.93%). MMIX (4.1%) and MFV (4.59%), with fibre waste and commercial fibres, respectively, have a lower total absorption capacity.

Permeability to Water Vapour
This section contains an analysis of the degree of resistance to the passage of water vapour through ready-made mortars. The previous section showed that mortars for outdoor use should be as impermeable as possible, and it should be noted that they must maintain their water vapour permeability to allow for transpiration of walls and prevent the appearance of condensation on the inside. Table 2 shows the results of the weights obtained during the 6-week duration of the water vapour permeability test in one test specimen of each mixture; Figure 8 shows the water vapour permeability values, which are very similar to those of the reference mortar.  Mortars with fibre waste, MRLR-MRFV-MMIX, have the lowest values of water vapour permeability, i.e., 2.87%-0.38%-1.15% less than the reference mortar. In the case of commercial fibres, MPP also showed a reduction of 5.37% in relation to the reference mortar but MFV increased its value by 3.83% (Figure 8). The mortar with the lowest water vapour permeability was MPP with a value of 5.0321*10 −14 . This is due to the fact that, contrary to water absorption values, higher values of water vapour permeability are obtained in mortars with a greater amount of aggregate [44], since CO2 diffuses better in the aggregate than in the matrix, favouring permeability. Figure 9 shows the values obtained in the contraction test in 24 h, 7 days and 14 days. They represent the average of 4 test specimens of each mixture. After the first day, there were significant differences between the reference mortar and some of the prepared samples. Mortars with fibre waste, MRLR-MRFV-MMIX, have the lowest values of water vapour permeability, i.e., 2.87%-0.38%-1.15% less than the reference mortar. In the case of commercial fibres, MPP also showed a reduction of 5.37% in relation to the reference mortar but MFV increased its value by 3.83% (Figure 8). The mortar with the lowest water vapour permeability was MPP with a value of 5.0321*10 −14 . This is due to the fact that, contrary to water absorption values, higher values of water vapour permeability are obtained in mortars with a greater amount of aggregate [44], since CO2 diffuses better in the aggregate than in the matrix, favouring permeability. Figure 9 shows the values obtained in the contraction test in 24 h, 7 days and 14 days. They represent the average of 4 test specimens of each mixture. After the first day, there were significant differences between the reference mortar and some of the prepared samples. Mortars with fibre waste, MRLR-MRFV-MMIX, have the lowest values of water vapour permeability, i.e., 2.87%-0.38%-1.15% less than the reference mortar. In the case of commercial fibres, MPP also showed a reduction of 5.37% in relation to the reference mortar but MFV increased its value by 3.83% (Figure 8). The mortar with the lowest water vapour permeability was MPP with a value of 5.0321*10 −14 . This is due to the fact that, contrary to water absorption values, higher values of water vapour permeability are obtained in mortars with a greater amount of aggregate [44], since CO2 diffuses better in the aggregate than in the matrix, favouring permeability. Figure 9 shows the values obtained in the contraction test in 24 h, 7 days and 14 days. They represent the average of 4 test specimens of each mixture. After the first day, there were significant differences between the reference mortar and some of the prepared samples. After 24 h, mortars containing fibre waste, MRLR-MRFV-MMIX, reached 90.91%-27.27%-54.55% respectively, in relation to the reference mortar. The commercial fibre mortar MPP had the same shrinkage as MREF, but MFV had 18.18% less shrinkage.

Air Content and Porosimetry
The amount of air content from fresh mortars directly influences the porosity of the material, a greater amount of air causes greater porosity, which improves workability but reduces mechanical resistance.
The results of both tests are shown in Figure 10. This test was carried out on one test specimen of each mixture. When the fibre waste or commercial fibres were incorporated into the mortars, the air content decreased in relation to the reference sample [46].

Air content and porosimetry
The amount of air content from fresh mortars directly influences the porosity of the material, a greater amount of air causes greater porosity, which improves workability but reduces mechanical resistance.
The results of both tests are shown in Figure 10. This test was carried out on one test specimen of each mixture. When the fibre waste or commercial fibres were incorporated into the mortars, the air content decreased in relation to the reference sample [46]. Mortar containing fibre waste, MRLR, showed a greater amount of air content (5.2%) and still represented 16.13% less than MREF; MRFV showed the least amount of air content (4.5%), 27.42% less than MREF. Regarding commercial fibres, MFV showed the highest air content (5.8%), 6.45% less than the reference sample.
The results of the air content tests in the fresh mortar did not coincide exactly with those obtained in the porosimetry test on dry mortars. The mortar containing fibre waste that showed the highest percentage of pores is MRFV (17.2%), 11.47% more than MREF; the lowest percentage was shown by MRLR (14.73%), with 4.54% less pores than the reference sample. Amongst mortars containing commercial fibres, MPP showed the least amount of pores (16.92%), 9.66% more than MREF, and MFV showed the lowest amount (16.09%), 4.28% more than the reference sample.

Scanning electron microscopy
Photomicrographs of selected compounds are shown in Figures 11-13. It can be seen in the images that there is a good dispersion of the fibres in the mortars, although it is also obvious that the distribution may not be homogeneous, preventing control of surface properties.
Mortar containing fibre waste, MRLR, showed a greater amount of air content (5.2%) and still represented 16.13% less than MREF; MRFV showed the least amount of air content (4.5%), 27.42% less than MREF. Regarding commercial fibres, MFV showed the highest air content (5.8%), 6.45% less than the reference sample.
The results of the air content tests in the fresh mortar did not coincide exactly with those obtained in the porosimetry test on dry mortars. The mortar containing fibre waste that showed the highest percentage of pores is MRFV (17.2%), 11.47% more than MREF; the lowest percentage was shown by MRLR (14.73%), with 4.54% less pores than the reference sample. Amongst mortars containing commercial fibres, MPP showed the least amount of pores (16.92%), 9.66% more than MREF, and MFV showed the lowest amount (16.09%), 4.28% more than the reference sample.

Scanning Electron Microscopy
Photomicrographs of selected compounds are shown in Figures 11-13. It can be seen in the images that there is a good dispersion of the fibres in the mortars, although it is also obvious that the distribution may not be homogeneous, preventing control of surface properties.   It should be noted that ready-made mortars do not have a high percentage of fibres and that these quantities are not enough to produce significant changes in the microscopic structure of the composite material [20].
Therefore, these results indicate that the presence of fibres does not affect the setting process of the mortar, where the mortar mass sets around the fibres without any additional or significant porosity occurring in the pore size range covered by these experimental techniques. In other words, the fibres are "surrounded" by the set mass, indicating good adhesion between the mortar and the fibres, which is also proven by good mechanical behaviour.

Conclusions
As a general conclusion, it can be confirmed that it is possible to replace in coatings the fibres usually used by fibres from recycling.   It should be noted that ready-made mortars do not have a high percentage of fibres and that these quantities are not enough to produce significant changes in the microscopic structure of the composite material [20].
Therefore, these results indicate that the presence of fibres does not affect the setting process of the mortar, where the mortar mass sets around the fibres without any additional or significant porosity occurring in the pore size range covered by these experimental techniques. In other words, the fibres are "surrounded" by the set mass, indicating good adhesion between the mortar and the fibres, which is also proven by good mechanical behaviour.

Conclusions
As a general conclusion, it can be confirmed that it is possible to replace in coatings the fibres usually used by fibres from recycling.   It should be noted that ready-made mortars do not have a high percentage of fibres and that these quantities are not enough to produce significant changes in the microscopic structure of the composite material [20].
Therefore, these results indicate that the presence of fibres does not affect the setting process of the mortar, where the mortar mass sets around the fibres without any additional or significant porosity occurring in the pore size range covered by these experimental techniques. In other words, the fibres are "surrounded" by the set mass, indicating good adhesion between the mortar and the fibres, which is also proven by good mechanical behaviour.

Conclusions
As a general conclusion, it can be confirmed that it is possible to replace in coatings the fibres usually used by fibres from recycling. It should be noted that ready-made mortars do not have a high percentage of fibres and that these quantities are not enough to produce significant changes in the microscopic structure of the composite material [20].
Therefore, these results indicate that the presence of fibres does not affect the setting process of the mortar, where the mortar mass sets around the fibres without any additional or significant porosity occurring in the pore size range covered by these experimental techniques. In other words, the fibres are "surrounded" by the set mass, indicating good adhesion between the mortar and the fibres, which is also proven by good mechanical behaviour.

Conclusions
As a general conclusion, it can be confirmed that it is possible to replace in coatings the fibres usually used by fibres from recycling.
As specific conclusions: All the mortars studied show that fibres from recycling do not affect the setting of the mortar, nor do they produce significant changes in the microscopic structure of the compound, as their behaviour is very similar to that of the mortars reinforced with commercial fibres.
In addition, and because the amount of fibres added is not very large, the density of the mortars reinforced with fibres from recycling is similar to the density without fibres or reinforced with commercial fibres. These can be considered lightweight mortars, since their density is lower than 1300 Kg/m 3 according to UNE EN 1015-6 [35].
Regarding consistency, it should be noted that mortars reinforced with recycled fibres have consistencies similar to those reinforced with commercial fibres, such as plastic mortars, and are within the range established in the standard mentioned in the previous paragraph.
These mortars are found to be viable for exterior coatings as, similar to all of those with recycled fibres, they exceed the minimum values of compressive strength established in standard UNE-EN 1015-11:2000/A1:2007 [25] for mortars R1 and/or R3, 3.5-7.5 N/mm2 and/or ≥ 6 N/mm2 and with water absorption values that are typical of mortars designated as R1, medium resistance to filtration. They can be suitable for application as exterior coatings even on walls exposed to rain and moisture. At this point, it should be noted that mortar reinforced with commercial fibres complies with the provisions of the standard for mortars (R3), i.e., mortars with very high resistance to filtration would be obtained.
Finally, it has been found that the type of fibre does not affect the water vapour permeability of mortars, since the permeability values obtained in all reinforced types are very similar to those of the reference mortar. However, shrinkage of mortars is lower in those reinforced with commercial fibres, which is probably due to the greater length of these, so it would be interesting to work with longer recycled fibres to confirm that their length plays a decisive role in the reduction of shrinkage.