Treatment of Coal Fly Ash and Environmentally Friendly Use with Rubber in Cable Wires as Insulation Material

: Energy demand is increasing all over the world, and to fulﬁll this need, more energy is required to be produced. Coal power plants produce around 39% of energy, but during energy production, these coal power plants also generate waste in the form of coal ﬂy ash (CFA). The reuse of CFA is the only solution to control this waste; ﬂy ash can be used in di ﬀ erent products. Therefore, this study utilizes CFA with rubber as ﬁller materials in the rubber industry. There are di ﬀ erent techniques (such as nozzle design technology, air classiﬁer, and optimization of CFA to convert crushed ﬂy ash into valuable microparticles. Treated CFA is applied to produce medium voltage insulated cables and ﬁre resistance cables with di ﬀ erent kinds of rubber, such as styrene–butadiene and Ethylene–propylene. The study found that by applying CFA in insulated cables, the elongation at break increased by 50%, and volume resistance 2.2 × 10 16 Ω · cm, insulation resistance increased 70% by using CFA with magnesium in the recipe of insulated cables. The CFA increased the collection rate of cleaning by 30% using this technology, and product life expectancy increased by 5–20%. , insulation resistance 10,000 , and average thickness the 0.93 The other ﬁller used in the formation of insulated Results showed that the outer diameter of copper sheath DC resistance at 20 ◦ was , minimum insulation thickness conductor DC resistance of the at 20 ◦ C temperature was 0.112 , insulation resistance , and average thickness of the copper was


Introduction
Coal is of the world's primary source of electricity supply, demonstrating a drastic increase in its consumption. However, coal combustion has significant effects on human health and climate change [1,2]. Generally, 5-12% of the total coal persists un-blistered and is deposited as a dense layer of small particles, usually referred to as fly ash [3], a general name of all forms of byproducts, such as coal fly ash (CFA), formed during coal combustion [4]. Regardless of the current efforts to develop alternative energy sources, coal is expected to remain in the predictable prospect as the primary source of global power production, accounting for around 40% worldwide [5,6]. China is the largest coal consumer, accounting for approximately 40% of the overall world consumption in recent decades, followed by the European Union (EU), the United States (US), and India at 10%, 18%, and 8%, respectively [7,8].
Coal fly ash (CFA) manufactured as waste material derived from coal from power stations is considered a problematic solid waste worldwide [9]. Earlier literature estimated that CFA production globally is more than 500 million tons annually. Notably, in China, due to rapid economic development, the consumption of coal has been boosted by 50% [2]. A ubiquitous proportion of CFA produced annually is disposed of in those countries where its production is maximum, i.e., China, India, and the US [4]. It has been disposed of for many decades by diverting the ash into landfills known as ash lagoons. Ash lagoons have been known to breach and cause severe ecosystem and environmental current because of the low conductivity of the insulation [22].

66
Styrene-butadiene rubber demonstrates strong abrasion tolerance and flexibility in rubber 67 industries, that is why SBR is widely used in tire treading [23]. The synthesis of SBR was the first 68 rubber produced commercially with the help of the Ziegler-Natta catalyst and was generated in the 69 middle of the last century [18,24]. SBR is formed in a hydrocarbon solution, including initiators, and 70 develops a large molecular weight with small distribution by living polymerization.    Physiological and chemical attributes of CFA differ significantly depending on the basis and type of coal, combustion temperature, combustion process, fuel/air ratio, and feed coal particle size [12]. The key mechanism of CFA samples is enriched with aluminum oxides, silica, and iron with different amounts of carbon content as a loss on ignition (LOI), calcium oxide and magnesium oxide [13,14]. Higher content of magnesium and calcium oxide and lower contents of oxide of silica, iron, and aluminum are present in sub-bituminous and lignite CFA compared to bituminous CFA.
CFA can be significantly employed as a rubber filler [15], with a large fraction of precipitated silica [16], creating rubber compounds of maximum mechanical characteristics [17]. The mechanical attributes of styrene-butadiene rubber (SBR) can increase with fly ash [18]. It was found that when contrasted with carbon black filled SBR, CFA has a significant reinforcing impact in raising elongation, modulus, and strength of the rubber compound [19].
Over the last few years, silicon rubber and epoxy resin have demonstrated great potential in industry because they are used as an alternative material to ceramic and glass due to their properties, such as dielectric, volume resistivity, mechanical strength, thermal conductivity, and lightweight [20,21]. Due to their lightness, they are easier to use and control than other ceramic and glass materials. Furthermore, polymer insulator, especially silicone rubber, is a hydrophobic material. It has water repellent properties and also can be used as an outdoor insulator. Especially in rainy weather, the hydrophobic properties of silicon rubber have the benefit of preventing the leakage of current because of the low conductivity of the insulation [22].
Styrene-butadiene rubber demonstrates strong abrasion tolerance and flexibility in rubber industries, that is why SBR is widely used in tire treading [23]. The synthesis of SBR was the first rubber produced commercially with the help of the Ziegler-Natta catalyst and was generated in the middle of the last century [18,24]. SBR is formed in a hydrocarbon solution, including initiators, and develops a large molecular weight with small distribution by living polymerization.

1.
Treatment of CFA with different pulverization technologies to make useable nanoparticles; 2.
Fly ash applied to medium voltage insulated cables (instead of filling the main material); 3.
Fly ash applied to inorganic fire-resistant cables (instead of filling the main material).

Treatment of Coal Fly Ash (CFA)
Fly ash is not waste but an available resource that is used in many countries after treatment to add value. The particle size of fly ash directly determines the product object, sales radius, and price generated by it. Therefore, it is necessary to treat CFA for further use to produce valuable products. The whole procedure of treatment and utilization of fly ash is shown in Figure 2. Various methods used to treat CFA are following.

77
Fly ash is not waste but an available resource that is used in many countries after treatment to 78 add value. The particle size of fly ash directly determines the product object, sales radius, and price 79 generated by it. Therefore, it is necessary to treat CFA for further use to produce valuable products.

80
The whole procedure of treatment and utilization of fly ash is shown in Figure 2. Various methods 81 used to treat CFA are following.

Nozzle Design Technology Based on Micro-Expansion Theory
Nozzle design technology pulverization takes place on two steps. In the first step, different sized nozzles are used to produce finer sized particles of CFA [1], with different pressures and velocities applied for different nozzles. One side of the nozzle produces pressure, and CFA particles move with different velocities and pass through the different sized nozzles. Another method, the nozzle back spray technology, is more efficient. In this method, water vapors spread by a nozzle through the passed-out particles of CFA. Induction back nozzle technology is the automatic method of collecting and separating finer particles of CFA by different densities. The graphical detail of this technology is shown in Figure 3.

Air Classifier
Air classifier used for the separation and extraction of bead particles of CFA. Fly ash was collected in a big chamber of the classifier. Air pressure was provided by an air pump to separate CFA particles. Furthermore, coal ash particles traveled through four different chambers, and different sized bead particles were collected and coated by these four chambers. The impacting ratio reached more than 98% by using this classifier machine without destroying the particle morphology [25,26]. This modifier machine was used for a small quantity of CFA, and can be applied to various modifiers. By using this technique, the efficiency rate increases, there is low wear and higher precision, and it can grade D97 = 3-75 µm fine powder. sized bead particles were collected and coated by these four chambers. The impacting ratio reached 99 more than 98% by using this classifier machine without destroying the particle morphology [25,26].

00
This modifier machine was used for a small quantity of CFA, and can be applied to various modifiers.

01
By using this technique, the efficiency rate increases, there is low wear and higher precision, and it 02 can grade D97=3-75 µm fine powder. of CFA produced on the basis of size [2]. Figure 4 explains the static pressure and size of CFA 07 produced, and velocity applied to reduce the size of particles. SEM results showed that more static 08 pressure decreased the size of CFA and increased the 300 µm size production of CFA [27]. Different

09
pressures showed different peaks of particle size. The highest peak showed the highest value of 10 pressure 180 kPa and particle size 300 µm produced on this highest peak of pressure. Similarly, the 11 velocity size particle graph shows that the highest peak of velocity was near 1200 (ms -1 ). On this peak 12 particle size, 380 µm, production increased more than 300 µm sized particles. X-ray diffraction results

Optimization of Coal Fly Ash by Static Pressure and Velocity
The optimization of CFA showed the difference between static pressure of fly ash size and different velocity. Scanning electron microscopy (SEM) X-ray diffraction showed four different kinds of CFA produced on the basis of size [2]. Figure 4 explains the static pressure and size of CFA produced, and velocity applied to reduce the size of particles. SEM results showed that more static pressure decreased the size of CFA and increased the 300 µm size production of CFA [27]. Different pressures showed different peaks of particle size. The highest peak showed the highest value of pressure 180 kPa and particle size 300 µm produced on this highest peak of pressure. Similarly, the velocity size particle graph shows that the highest peak of velocity was near 1200 (ms −1 ). On this peak particle size, 380 µm, production increased more than 300 µm sized particles. X-ray diffraction results showed that particle size result varies with different pressures and velocities; the production of nanoparticles increased at high pressure instead of velocity and effectively reduced energy consumption and reduced turbulence in the material chamber.

Properties of Fly Ash
Different coal-fired power generation processes produce different fly ash, which is divided into low-temperature fly ash and high-temperature fly ash. The high-temperature pulverized CFA temperature was 1400 • C-1600 • C of power generation, and low-temperature CFA was produced by 800 • C-900 • C of power generation. The physical properties, chemical composition, and mineral composition of different fly ash were different. It depended on different ways of use, different ultra-fine processes [3]. A low-temperature fluidized bed can form irregular sheet-like and laminated structures, and then be crushed and classified to form a finer micron-sized and more granular structure so that it can be used in various industrial materials. Table 1 shows the physical and chemical composition of low-temperature and high-temperature CFA. Figure 5 shows an anomalous flakes' magnification graph by SEM of low-temperature CFA and high-temperature CFA. Figure 6 shows packed nana beads by SEM magnification (3500×) of high-temperature produced CFA. The fly ash of the microbead structure was light in weight, and the porous adsorption property had the properties of insulation, high-temperature resistance, wear resistance, heat preservation, heat insulation, and aging resistance, and had excellent characteristic materials and is widely used.

Application of Coal Fly Ash in the Manufacturing of Medium Voltage Insulated Cables
Coal fly ash can be used as filler material instead of other materials, such as coal and quartz, in the manufacturing of medium voltage insulated cables. The recipe used for this production was ethylene-propylene rubber (Dow 3722P,) + vulcanizing agent DCP3.5 + cross-linking agent TAIC2.2 + fly ash (D97-10 microns) + stearic acid + zinc oxide + paraffin. This formula was designed for a medium-voltage rating (6000 V). Medium-voltage insulated cables have two parts one is a copper conductor which transforms the electrical current, and the other part is insulation parts of the cable. This part protects the conductor and increases the lifetime of the conductor and cables. This study was conducted to produce the insulation part of the cables using the above-mentioned recipe. The insulation part was further divided into the covering part, which was also produced by the above-mentioned formula. Different kinds of filler materials, such as coal gangue, clay, quartz powder, and fly ash, was used to produce insulation material of medium voltage cables. The vulcanization process was done at different temperatures for different types of filler materials in 16 minutes. D97-10 modified micro nanocrystals of CFA were used for the insulation material of the cable. After the completion of the vulcanization process and cooling at room temperature to harden, different tests were applied to compare the CFA made product with other expensive material products. Sustainability 2020, 12, x FOR PEER REVIEW 6 of 20 chemical composition of low-temperature and high-temperature CFA. Figure 5 shows an anomalous 130 flakes' magnification graph by SEM of low-temperature CFA and high-temperature CFA. Figure 6 131 shows packed nana beads by SEM magnification (3500×) of high-temperature produced CFA. The fly 132 ash of the microbead structure was light in weight, and the porous adsorption property had the 133 properties of insulation, high-temperature resistance, wear resistance, heat preservation, heat

147
This part protects the conductor and increases the lifetime of the conductor and cables. This study 148 was conducted to produce the insulation part of the cables using the above-mentioned recipe. The

149
insulation part was further divided into the covering part, which was also produced by the above- where S is the thickness of the medium voltage cable, the π value used is 3.14, R is the radius of tested 163 cable, which is measured by a Vernier caliper.

Thickness of Medium Voltage Cables
A digital Vernier caliper was used to measure the thickness of the insulation part of the medium voltage cable; the cross-sectional area of the insulated material was measured in mm. Different filler material manufactured cables were measured one by one and compared with the fly ash made insulation part. The cross-sectional area equation measures the thickness of medium voltage by measuring the diameter of the insulated part of the cable by following Equation (1).
where S is the thickness of the medium voltage cable, the π value used is 3.14, R is the radius of tested cable, which is measured by a Vernier caliper.

Tensile Strength and Elongation at Break
The tensile strength of the medium voltage cable was the force to pull the cable at the point of breakdown of the cable. The elongation of the cable was the stretched point before the breakdown of the cable. The tensile strength of the medium voltage cable was measured without a conductor; the insulated part of the cable was tested. A testometric was applied to test the elongation at break and tensile strength. The tested cables to be marked into two points with 20 mm length. The force applied to breakdown the cables was measure in MPa, and the stretched points were also measured in %. Test results shown on the screen connected with the tensile testometric machine.

Volume Resistivity (VR)
The volume resistance (VR) test confirmed a material of low enough resistance test to function appropriately in a medium insulated cable. A cable sample was placed in the test machine, and all electrodes were covered. Then the testing machine was closed. Readings of the tested cables appeared in volts and amps by ammeter and voltmeter. Further results were calculated by the following equation: where VR is the volume resistivity of cable, v is the volts of electric current passed through the cables, A is the amps of the cable, and TF is the thickness factor of the medium voltage cable.

Application of Coal Fly Ash in the Manufacturing of Fire-Resistant Cables
Fire resistance cables are used to protect fire to spread, high-temperature resistance, corrosion resistance, water resistance, and protection from short circuits. Fire resistance cables contain a fire retardant insulation part and a conductor part to conduct the electric current [28]. Coal fly ash was used to manufacture the fire-retardant insulation part of fire resistance cables instead of other filler materials, such as calcined high-pressure clay, medium pressure clay, low-pressure clay, Maoming washed calcined clay, and quartz powder.
The vulcanization process takes place to produce the insulation part of the cables by different materials. The insulation part contains cross-linked polyethylene (XLPE), cross-linked ethylene-vinyl acetate (XLEVA), ethylene-propylene rubber (EPR), polyethylene (PE), and polyvinyl chloride (PVC) [29]. The mixture of these materials was mixed with different filler materials, such as magnesium, kaolin, talcum powder, magnesium oxide, and treated CFA. These materials were used for bonding of the insulation part of the cable and to make a solid fire-resistance cover sheath of the cable to protect it from fire. Different filler materials were used to produce fire resistance cables and compared with different tests with the CFA filler material in the production of the cables. Fire resistance cables are mostly used in hospitals, airports, and other important buildings.
Different tests were applied to check the quality of fire resistance tests and a comparison of different filler materials used in the vulcanization process of 64 m produced cable was made. First of all, the exterior of the cable was checked to confirm the defect in the laboratory manufactured fire resistance cable, and then, an immersion test with water at room temperature for one hour was applied to check the corrosion damage. All the filler material-produced cables were tested and compared with CFA filler production cables. The copper sheath outer diameter was checked with the help of a digital Vernier caliper, and results were noted; same as for the medium voltage test. Another test applied was the DC resistance of the copper sheath used in fire resistance cables. A DC resistance digital micro-ohm meter was used to check the DC resistance in the lab. Values of the test were calculated by the following formula of DC resistance: where R is the DC resistance of the fire resistance cable, ρ20 is the electrical resistivity of the conductor material at 20°C temperature, S is the cross-sectional area of the conductor. The R value was calculated by this formula using the SI Ω unit. Insulation material thickness of the produced cables was also measured one by one by a digital Vernier caliper. Another test applied to the fire resistance cable was conductor continuity, to check the continuity of the conductor multimeter. Two conductors of the multimeter were connected with the testing wires one by one with different conductor wire to check the continuity of wire conductors. Another important test for electrical safety testing is the insulation resistance test. The insulation resistance test was done by a tera ohm meter tester (megger meter). The value shown on the screen of the meter by testing insulation resistance tests was the measured value of resistance that had to be higher than the international standard value. Another test applied to test cable was the withstand voltage test. Actually, this test is a high voltage test of the cable conductor. A high voltage was passed through the cable to check the insulator quality to see if the current passed through without damaging the insulation part of the cable. This test evaluates the quality of the insulation material present on the conductors. Two point five kilovolt was applied to the all manufactured wires using different filler materials for 1 minute to check the voltage test. The average thickness of the copper sheath was also measured and compared with the international standard. Table 2 shows the physical tests' results of the insulated cable and compares fly ash with different expensive filler materials. The vulcanization time for this formula with different materials was the same-16 minutes, using coal gangue 850-degree calcined high-pressure clay (CGCHPC). In the above-mentioned formula, the thickness of the insulated cable was 1.45 mm, tensile strength was 8.46 MPa, elongation of break was 247.65%, and VR was 2.9 × 10 16 Ω cm. Another filler material was coal-based calcined high-pressure clay (CBCHPC), which was used in the above-mentioned recipe of medium voltage insulated cable. Data showed that the thickness was 1.3 mm, tensile strength 9.51 MPa, elongation at break 241.3%, and VR was 2 × 10 16 Ω cm. The third filler material was 700-degree medium pressure clay (MPC). Results showed that the thickness of the insulated cable value was 1.4 mm, tensile strength was 8.73 MPa, elongation at break was 276.18%, and VR was 3 × 10 16 Ω cm.

Fly Ash Applied to Medium Voltage Insulated Cable (Instead of Filling Main Material)
Another filler material used in the above-mentioned formula was 980-degree low-pressure clay (LPC). By using this filler material, the thickness of the insulated cable was 1.4 mm, tensile strength was 8.57 MPa, elongation at break was 250.22%, and VR value was 1.7 × 10 16 Ω·cm. Maoming washed calcined clay (MWCC) was also used as a filler material in the above formula for the production of medium voltage insulated cable. Using this filler material, results showed that the thickness was 1.3 mm, tensile strength was 5.11 MPa, elongation at break was 240.52%, and volume resistivity was 2.7 × 10 16 Ω·cm. Another main material that was used as an alternative material in the above formula for the making of insulated cable was treated CFA. By using D97-10 micron CFA in this product, the test result data showed that the thickness of the insulated cable was 1.3 mm, tensile strength was 8.12 MPa, elongation at break was 334.82%, and VR was 2.2 × 10 16 Ω·cm. The final and last filler material was quartz fine powder 3500 eyes (QFP), which was used in the above-mentioned recipe. According to this recipe, results showed that the thickness of the insulated cable was 1.4 mm, tensile strength was 4.9 MPa, elongation at break was 378.41%, and VR was 2.7 × 10 16 Ω·cm. Table 3 shows the different test results of inorganic fire-resistant cables. The immersion test was applied to check the corrosion for all four kinds of cables passed through this test, including fly ash and magnesium oxide filler-used cables. Exterior and voltage tests were also the same for four different filler products of cables, but the inspection results were different, which were tested by the national standard. In detail, the results found that magnesium and kaolin magnesia filler qualified for this test, but talcum powder and magnesium oxide filler failed. And fly ash and magnesium oxide results were found to be the best rather than the other three fillers.

Fly Ash Applied to Inorganic Fire-Resistant Cables (Instead of Filling Main Materials)
The results showed that by using magnesium as the filler material, the different tests data were an outer diameter of copper sheath of 18.32 mm, copper sheath DC resistance at 20 • C of 0.479 Ω, minimum insulation thickness of 0.93 m, conductor DC resistance of the wire at 20 • C temperature of 0.116 Ω, insulation resistance of 12,100 MΩ, and an average thickness of the copper sheath of 0.93 mm. As well when using kaolin and magnesium as the filler material in the formation of insulated cables, the test result showed that the outer diameter of the copper sheath was 18.35 mm, copper sheath DC resistance at 20 • C was 0.498 Ω, minimum insulation thickness was 0.93 m, conductor DC resistance of the wire at 20 • C temperature was 0.116 Ω, insulation resistance was 10,000 MΩ, and average thickness of the copper sheath was 0.93 mm. The other filler materials used in the formation of insulated cable were talcum powder and magnesium oxide. Results showed that the outer diameter of the copper sheath was 17.98 mm, copper sheath DC resistance at 20 • C was 0.392 Ω, minimum insulation thickness was 0.91 m, conductor DC resistance of the wire at 20 • C temperature was 0.112 Ω, insulation resistance was 9800 MΩ, and average thickness of the copper sheath was 0.95 mm.  The other main material which was used in the formation of insulated cable instead of talcum powder with magnesium oxide was CFA. Results showed that by using CFA, the outer diameter of copper sheath was 18.37 mm, copper sheath DC resistance at 20 • C was 0.386 Ω, minimum insulation thickness was 0.93 m, conductor DC resistance of the wire at 20 • C temperature was 0.117 Ω, insulation resistance was 13,900 MΩ, and average thickness of the copper sheath was 0.93 mm. Figure 7 shows different test results of medium insulated cables. The results for the thickness (Figure 7A.) of insulated cables by using different materials and compared with CFA, showed that the highest thickness recorded was 1.45 mm using coal gangue 850-degree calcined high-pressure clay (CGCHPC). Results of the three materials, including fly ash (1.3 mm), were the same as 1.4 mm, but CFA is a waste material and cheaper than other materials used. CFA-produced insulation material of cable thickness comparable with other filler material thicknesses. Figure 7B shows the tensile strength results of the insulated cables using different materials in the recipe. The highest tensile strength was 9.51 MPa shown by using coal-based calcined high-pressure clay (CBCHPC), and the lowest value was 4.9 MPa by using quartz fine powder (QFP). Using fly ash D97-10 micron, the result of the tensile strength test value was 8.12 MPa, which is acceptable and better than other filler materials, such as Maoming washed calcined clay (MWCC) and quartz fine powder 3500 eyes (QFP). Thus, results found that the fly ash filler insulation part of the medium voltage cable breakdown was at the 8.12 MPa point. At 30 phr, fly ash composition showed that tensile strength and elongation at break had a good result in the rubber matrix. The rubber matrix bond increased not just due to temperature but also with increased fly ash quantity [30].   Figure 7C shows the results of elongation at break of insulated cable. This is an important test of any cable. If a cable cannot tolerate stretching and is damaged quickly, that cable is not safe and electric current can leak out. The results showed that the highest value for this test was recorded at 334.82% by using CFA. This value is greater than the other five filler materials used in the formation of medium voltage cables. Elongation at break increased by 50% by using CFA. However, the highest value was 378.41% using quartz fine powder (QFP). For clay material, tensile strength and elongation at break were higher, as increasing the loading filler material creates more surface area of clay as compared to other filler materials [30]. Figure 7D shows the volume resistivity test result of insulated cables by using different fillers in the recipe. The highest peak value was recorded as 3 × 10 16 (Ω·cm) using 700-degree medium pressure clay (MPC), and the lowest peak value recorded was 1.7 × 10 16 (Ω·cm) using 980-degree low-pressure clay (LPC). However, the value for fly ash was recorded at 2.2 × 10 16 (Ω·cm), which was greater than the two main filler expensive filler materials, 980-degree low-pressure clay (LPC) and coal-based calcined high-pressure clay (refining type) (CBCHPC). Thus, the result described that fly ash can be used in the insulated cables' recipe instead of other expensive filler material.

Fly ash applied to inorganic fire-resistant cables (instead of filling main materials).
257 Table 3 shows the different test results of inorganic fire-resistant cables. The immersion test was 258 applied to check the corrosion for all four kinds of cables passed through this test, including fly ash 259 and magnesium oxide filler-used cables. Exterior and voltage tests were also the same for four 260 different filler products of cables, but the inspection results were different, which were tested by the 261 national standard. In detail, the results found that magnesium and kaolin magnesia filler qualified 262 for this test, but talcum powder and magnesium oxide filler failed. And fly ash and magnesium oxide 263 results were found to be the best rather than the other three fillers.   Figure 8A shows the results of the outer diameter of the copper sheath. According to the national standard, 18.4 ± 0.05 mm is the benchmark. The measured result for the test fly ash was very close, 18.37 mm and perfect as the national standard. Magnesium and kaolin magnesia results were also better, but a lower value was recorded for the talcum powder and magnesium oxide test, which was 17.98 mm. It was found that talcum powder and magnesium oxide were more expensive than fly ash, and the results of the outer diameter as filler in fire resistance cable were not good and less than the standard value. Figure 8B shows the result of the 20 • C copper sheath DC resistance test. The national standard (≤0.479 Ω) was used. According to the national standard, fly ash and magnesium oxide filler results were better than other fillers at 0.386 Ω. DC resistance depends on conductor materials. It means that fly ash with magnesium oxide can be used instead of talcum powder and other materials. If the insulation part of the fire resistance cable quality is not good and has a lower thickness, then direct current resistance will also be affected. The study found that the thickness of the insulation part produced by CFA was better than other materials, and ultimately, DC resistance was also better than other expensive filler materials. Fly ash was also used as an alternative to carbon black in styrene-butadiene rubber (SBR) composites. Nano particle-sized fly ash (148 nm) had a major reinforcing effect instead of carbon black (CB), encouraged silica, or untreated fly debris (60-100 µm) as uncovered by a higher modulus, rigidity, and hardness [24].    Figure 8C shows the result of the minimum insulation thickness. According to the national standard, the requirement of this test is 0.94 m. Three different filler materials' results were the same and close to the standard and included fly ash and magnesium oxide filler, which was 0.93 m. However, the talcum powder result was lower (0.91 m). So, if the talcum powder is used as a filler material in fire resistance cables, due to its thickness, it will also affect the DC resistance. Therefore, fly ash filler applied in fire resistance cables is better than talcum powder filler. Figure 8D shows the result of the 20 • C conductor DC resistance test. The national standard of this test is ≤0.124 Ω.

264
The minimum value of this test was recorded at 0.112 Ω, which was found for talcum powder and magnesium oxide. The maximum value (0.117 Ω) was recorded for the fly ash and magnesium oxide filler. The results of all four fillers were promising and can be used in making fire resistance cables. In addition, fly ash is cheaper than other materials, and applications of fly ash are also remarkable. The surface resistivity level is directly proportional to fly ash quantity. When the fly ash quantity in silicon rubber was increased, the test material results were also increased in the following measurement results, namely FA20 (Fly ash 20%) was 6.7 G Ohm/sq, FA30 (Fly ash 30%) was 8.4 G Ohm/sq., FA40 (Fly ash 40%) was 9.1 G Ohm/sq., and FA50 (Fly ash 50%) was 11.4 G Ohm/sq. Figure 8E shows the test results of insulation resistance, which is an important measure and prevents electric shocks, and has a ≥10,000 MΩ standard. The highest value recorded was 13,900 MΩ, which was for fly ash and magnesium oxide as filler materials. The minimum value recorded was 9800 MΩ using talcum powder and magnesium oxide. Insulation resistance protects the fire resistance cables from fire. If this insulation part of cable resistance is not according to the standard, it cannot be used in important buildings, such as hospitals, airports. So that test result showed that fly ash is a promising filler material to use in fire resistance cables.
Consequently, fly ash results were better than talcum powder. Moreover, fly ash is a cheaper and waste material, so it can be used as filler material. Figure 8F shows the results of the average thickness of the copper sheath and has a 0.90 mm required national standard value. According to three filler materials, test results were the same, 0.93 mm, including fly ash and magnesium oxide filler material, but the talcum powder and magnesium oxide value (0.95 mm) was greater than the others, which exceeded the standard value.

Conclusions
Overall results concluded that by applying CFA in insulated cables, elongation at break was increased by 50%, volume resistance 2.2 × 10 16 (Ω·cm), and there was a better flame retardant effect using CFA in the insulated cable. This is due to fly ash bonding with other elements as silica has anionic properties that have strong bond strength and hold the element. Insulation resistance increased by 70% by using CFA with magnesium in the recipe of insulated cables. Fly ash results were better in insulated cables because it controls the temperature and humidity, which are very important factors for insulation resistance. Different test results for fly ash used in the formation of electrical cables showed that, by using this material as filler, crack problems, permeability, reduced heat of hydration and temperature and humidity can be controlled. Fly ash test results were better in fire resistance cables as insulation resistance was highest (13,900 MΩ) by using treated CFA. For making microparticles of CFA by using nozzle-based technology, the collection rate of cleaning ash was increased by 30%, and the anti-clogging function, product life expectancy increased by 5-20%.
Author Contributions: First author Z.H. did the research, collected the data, and wrote the paper with all methodology and results finalized, and the paper was checked and analyzed by G.L.; M.M. applied software, such as Origin, etc., to the data. All authors have read and agreed to the published version of the manuscript.
Funding: There was no funding provided for this research; this research was done with the help of the Ph.D. supervisor.