A Review of Chemicals to Produce Activated Carbon from Agricultural Waste Biomass

The choice of activating agent for the thermochemical production of high-grade activated carbon (AC) from agricultural residues and wastes, such as feedstock, requires innovative methods. Overcoming energy losses, and using the best techniques to minimise secondary contamination and improve adsorptivity, are critical. Here, we review the importance and influence of activating agents on agricultural waste: how they react and compare conventional and microwave processes. In particular, adsorbent pore characteristics, surface chemistry interactions and production modes were compared with traditional methods. It was concluded that there are no best activating agents; rather, each agent reacts uniquely with a precursor, and the optimum choice depends on the target adsorbent. Natural chemicals can also be as effective as inorganic activating agents, and offer the advantages that they are usually safe, and readily available. The use of a microwave, as an innovative pyrolysis approach, can enhance the activation process within a duration of 1–4 h and temperature of 500–1200 °C, after which the yield and efficiency decline rapidly due to molecular breakdown. This study also examines the biomass milling process requirements; the influence of the dielectric properties, along with the effect of washing; and experimental setup challenges. The microwave setup system, biomass feed rate, product delivery, inert gas flow rate, reactor design and recovery lines are all important factors in the microwave activation process, and contribute to the overall efficiency of AC preparation. However, a major issue is a lack of large-scale industrial demonstration units for microwave technology.

The power density available for adsorption P is given in Equation (1), and is measured in W/m 3 .
Here, E represents the electric field vector; the vector H is the magnetic field; and б and µ are: electro conductivity and magnetic permeability, respectively. The dielectric factor and angular velocity are denoted with " and ω, respectively. Microwave processes can control the heating and materials being heated internally and uniformly, and rapidly with high efficiency to pyrolyse large particles [21].
This study reviews agricultural waste as an AC precursor regarding its activation conditions and chemical activating agents, with a substantial emphasis on the characteristic properties of AC [22] and adsorption application targets [23]. While there are reviews on this subject [24,25], none to date have considered the pre-processing challenges of parent materials, and only provide limited insight into kinetic and adsorption parameters and the important issue of scale-up.
This review attempts to evaluate multiple activating agent effects and make generic comparisons and assessments of multiple agricultural wastes, while outlining current process challenges. In

Modes of Activation
The preparation of AC typically involves two major steps: pyrolysis or carbonisation of the precursor, and activation. Carbonisation produces a stable structure, with an elementary and partially-developed pore structure [52], which must be enlarged properly by physical or chemical activation. The development stages are illustrated in Figure 2. In addition, physicochemical activation is also a potential form of activation [16]. Figure 2 illustrates the pore development of empty fruit bunch (EFB) AC, represented with A, B and C, following thermal treatment at 350, 500 and 600 °C, respectively [53]. The pore development is better defined with increased temperature, and modification and treatment methods for raw biomass are discussed by Pathak et al. [54]. Physical activation occurs over the dual stages of carbonisation of the precursor in a reactor with a steady flow of an inert gas, and then over a successive activation process of the char product with CO2. Steam, air or their mixtures or other fluid activating agents at 800-1100 °C are also used [55]. However, excessive temperatures of, say, 1200 °C and above, lead to low carbon yields, collapse of the pore structures and ash generation [56], while devolatilising processes encourage pore formation and further enlarge any micropores created [57]. Physical activation is environmentally safe, but the speed and the temperature requirements are problematic. Appropriate activation temperature and duration are important to ensure adequate porous development and the creation of functional groups.
The physicochemical activation process involves both physical and chemical methods [58], where the raw precursor or char is permeated with an activating agent; then, heated in a chamber with an oxidant flow [59]. This method is often employed when the activating agent used in activation is unable to be effectively removed through washing, and might otherwise lead to pore clogging [33]. This process is expensive due to the elevated temperature requirements, and the need for a two-step process, extended process time and a generally low-percentage AC yield [59]. There are various modifications and treatments, including acidic treatment, basic treatment, impregnation and microwave process treatment. Other routes include: ozone, plasma treatments and biological modification-which is a developing technology and will not be discussed here further [6]. Although conventional heating is still an effective method of AC production, there are basic challenges that affect the process, such as the high cost of the heating, extended heating duration and thermal energy flow from the outer layer to the core of a biomass material. Chemical treatment of agricultural waste and other biomass materials can also improve the overall efficiency of AC and provide opportunities for target applicability due to the potential to use several activating agents for the process [60]. Chemical activation processes are summarised in Table 2 with the key advantages and disadvantages presented.

Chemical Activation
A series of pre-activation steps is required to achieve an adequate and quick production process. Biomass materials must be free from soil and any other impurities by washing with deionized water, and then dried at a temperature between 65 and105°C [59]. The biomass selected often undergoes milling to reduce the particle size [61], enabling uniform and quick carbonisation by lowering the thermal gradient. The biomass physical properties influence the milling process. The chemical activation process can be achieved in several ways, as outlined below: The chemical activation method is accomplished by the infusion, mixing and permeation of a solution, usually a dehydrating chemical with the ability to induce and accelerate material decomposition by pyrolysis, while inhibiting the creation of semi-solid volatile substances before activation. Activating agents, such as bases; acids; and salts, such as K2CO3 and ZnCl2 are impregnated into the biomass by mixing and stirring [62]. Although this is a single-step technique, in some cases, the precursor may first be carbonised to produce char [63,64] The impregnated char is then heated in the presence of nitrogen [65]. The temperature requirement used in chemical activation range of 400-800 °C, which is lower than the average temperature for the physical activation process [64] and is applicable to lignocellulosic materials. Here, the raw precursor can be mixed and permeated with an activating agent directly before carbonisation [66]. Typically, the biomass material is added to the activating agent at an optimised ratio, and mixed, before undergoing thermal treatment. Each activating agent performs differently with different precursors, dependent on its structure and the activation conditions. It is also possible to use a two-step activation process by impregnating biochar with activating agent and then subjecting it to a second heat process, under the conditions outlined in Table 2 [63]. Table 2. An overview of the three modes for the chemical activation process. The one-step process system for AC production requires impregnation before heat treatment under a controlled environment, and this is known as direct activation. A wide thermal range between the hot exterior and the interior risks encourages significant combustion of the biomass. The microwave system can be used for this process and will shorten the process time compared to a twostep process [67].

Two-Step Activation Process
Two-step process systems for AC production involve carbonisation and then activation [68]. This process enhances the carbon content and forms a char with an initial porosity. It requires an extended time and consumes more energy. It can also be used for non-uniform particles so that a milling stage is not required in pre-processing. This process is common for microwave activation, but in the production of large quantities of AC, the transfer and reloading lead to loss of materials and increase production cost. Oginni et. al [69] reported that the two-step process does not result in more effective AC.

Microwave Activation Process
The high energy requirement and time involved in conventional heating can make the activation process expensive [70], making microwave heating attractive [71]. Some biomass types are good microwave absorbers, and hence, are interesting for possible use at the commercial scale [72].
Microwave-induced pyrolysis is more efficient, especially when a material with higher microwave absorbance is mixed with metal oxides [73]. Microwave pyrolysis reduces self-gasification during the activation process, unlike conventional pyrolysis, due to the high heating levels that are involved in conventional approaches [74].
Compared to conventional heating methods, the microwave method of activation has additional benefits, including uniform volumetric heating, regulation of the heating process, a high heating rate and ensuring that the biomass has indirect contact with the heat source. Thus, the microwave AC production technique has been suggested as a prospective method to replace the conventional thermal process [16]. In some cases, the activation process is planned according to the availability of resources and the heat source. Activation duration, though, depends on the type of precursor but can be affected strongly by the particle size and heat distribution mechanism. Carbon yield depends on the overall management of the sample, its temperature, its washing and handling techniques.

A Comparison of Activation by Microwave and the Conventional Process
Microwave-assisted activation produces AC with wider micropores and mesopores than the conventional products. The pore size, surface area and adsorption efficiency in both conventional and microwave activation processes are affected by activation temperature, dwell time, heating rate, type of activating agent, activation agent-feedstock ratio, particle size, inert gas flow rate, microwave power and weight of sample [75]. Figure 3 shows that heat flows from the external regions in conventional heating and from the interior for microwave heating [76]. This is the distinguishing factor between conventional and microwave heating. Direction of heat flow relative to the activation environment influences the molecular movement, volatile discharge and heat distribution. Conventional heating exhibits an extended temperature gradient, while thermal energy flows from the surface to the central portion of the biomass. However, it can be minimised by slow heating. An isothermal holding system may also be employed [77]. A thermal gradient results in the obstruction of the passage for volatiles through the pores, leading to the development of partial or undefined pores [49,77]. Microwave AC is characterised by wider micropores and mesopores than conventional activated AC, but it comes with process challenges [77,78]. Xin-hui et al. [64] studied activation approaches for AC production from Jatropha hulls with steam as the activation agent, and showed the carbon yields for microwave and conventional methods were 16.6% and 13.3%, respectively. With CO2 as an activating agent, the yield for conventional method was 18%, and it was 36.6% for the corresponding microwave method. Foo and Hameed [78] compared EFBAC produced through a conventional furnace and microwave and reported SBET and Vtotal values of 255.77 m 2 /g and 0.14 cm 3 /g, and 807.54 m 2 /g and 0.45 cm 3 /g, respectively. A general overview of the two approaches is shown in Table 3 [74,79].

The Effects of Activating Agents on Renewable and Non-Renewable Precursors
Activating agents play major roles in the activation process, and the various compounds used react differently depending on the biomass type and the temperatures employed.
Several non-renewable precursors (petroleum tar pitch and coal) have been used for AC production. When coke is impregnated with KOH, the porosity decreases as the ratio varies from 4:1 to 2:1, and the results obtained are in the following ranges: SBET, 1800-1200 m 2 /g; Vmicro 0.71-0.48 cm 3 /g; and mean pore size, 1.12-0.76 nm [79]. AC from bituminous coal can be produced by chemical activation with KOH and Borax decahydrate, but the resulting AC produced has an irregular pore structure.
Similarly, paracetamol, phenol and salicylic acid can used for coal-based ACs [79], while nitric acid is used for the activation of pitch, resulting in an AC with a SBET of 1401 m 2 /g and an adsorption capacity of 3.51 mol/kg, and is employed for the adsorption of CO2 [80]. The microwave process for coal, produced an AC with a 1048 mg/g adsorption capacity for methyl blue (MB) and values of 1770 m 2 /g and 0.99 cm 3 /g, for SBET and Vtotal, respectively, under production conditions of a 1:3 impregnation ratio for 12 min at 700 W [81].
Gao et al. [82] showed tar residues permeated with H3PO4 were activated at 850 °C, resulting in the following: adsorption capacity, Vtotal and Vmicro values of 793 mg/g, 0.286 cm 3 /g and 0.255 cm 3 /g, respectively. In addition, the mixture of coal and carbon monolith for AC production had a SBET of 1044 m 2 /g [83].
The reactivity of chemical activating agents on biomass materials under high thermal conditions creates an intermolecular reaction that gives rise to efficient AC production. Surface textural analysis shows that the increase in the ratio of activating agents is proportional to the efficiency until the optimal range is reached, and this creates AC with higher pore volume on activation. There are clear morphological differences depending on the activating agent; thus, the K2CO3-impregnated sample forms columnar and hexagonal shapes. Köseoʇlu and Akmil-Başa, showed that ZnCl2-impregnated AC forms an asymmetrical and irregular surface morphology [81], and they found that K2CO3 produced AC with a higher SBET and a well-defined porosity; however, the implication of such studies is not clear, as results are strongly dependent on technical activation conditions and impregnation parameters.
Microwave treatment has the potential to eliminate some volatiles, starch molecules and saturated and acidic oxygen-linking functional groups; therefore, making the AC basic; thus, promoting reactivity [84]. The type of bonding on the carbon layer is influenced by type of feedstock, microwave power, impregnation ratio and radiation time. Other variables, such as inert gas flow rate, can influence AC characteristics. These have a substantial impact on the adsorption capacity and other applications of AC [85].
The adsorption capacity is attributable to the effectiveness and reactivity of ions and ionic exchange in the carbon structure. The increase in charge density is proportional to the adsorption capacity [83]. At certain ranges of microwave power, pores can be blocked by deposits formed from volatile substances [86]. Raw materials, precursor particle size, activation process and mode of heat treatment also influence the surface chemical and functional groups of ACs [87]. Foo and Hameed [88] identified the removal of loosely-bound atoms and switching with heteroatoms, which are naturally basic, within the molecular layers. For the microwave activation process, the power requirement is critical due to possible collapse of the pore structure beyond the optimum heat requirement [89].
Activating agents possess great capacity in the microwave activation process. Biomass materials, due to poor dielectric properties, heat quickly with higher thermal penetration when impregnated with chemical agents [90]. For example, AC prepared from orange peel when all processing parameters are constant, showed substantial changes. However, any activation effect is insignificant, and minimal adsorption occurs at microwave power below 200 W. A study by Foo and Hameed [91] showed that adsorption capacity increases directly proportionally to the increase in microwave power.
Deng et al. [92] explored the influence of microwave power on coconut shell-based AC. Therein, K2CO3 and KOH were used for impregnation and the resulting adsorption capacity was similar at same microwave power [93]. In some cases, impregnation ratio influences AC properties and is used in the optimum range of 0.5-2 wt.% [94]. A further challenge in AC production is incomplete activation, which results in poor adsorption caused by partial elimination of the acidic functional groups, and the dominance of saturated molecule and incomplete removal of volatiles [84]. Fouriertransform infrared spectroscopy (FTIR) evaluation shows the presence of individual bonds and clearly defines the difference between carbonisation and activation. It can also be used to determine the optimum range of activation at different parameters. The peaks are indicative of the reactive sites and functional groups responsible for adsorption [95].

Acidic Treatment of Agricultural Residues
The sensitivity of cellulose linkage to acidic hydrolysis is due to the presence of glycoside bonds and it varies relative to type of acid, the concentration and the reactive temperature within the amorphous region. It is homogenous with strong acids and heterogeneous with weak acids. The kinetics of the hydrolysis reaction are also governed by decrystallisation of microcrystalline cellulose. Hydrolysation, which results in the elimination of xylan, helps in the separation of complex structures. Most acids are able to transform crystalline cellulose to amorphous, while HCl can remove lignin to enable symmetric pore creation. The cell walls of plants, where cellulose and hemicellulose have polymeric bonds, are easily broken by acids, and that results in delignification.
Introducing nitric acid into AC production was successful in improving the physical properties of AC. HNO3 successfully removed some contaminants attached to the surface of AC, such as Fe, Si, K and Al. The surface of AC pores was clearly seen to have unbroken cavities when treated [96] and showed an improved hydrophilic character [6] Comparing HCl and HNO3 under the same conditions for palm kernel shell (PKS) activation produced: SBET values of 164.2 and 325.4 m 2 /g; Vtotal values 0.10 and 0.19 cm 3 /g; and pore diameters 9.50 and 8.00 nm, respectively. H3PO4 is corrosive to both metals and tissues, undergoing rapid polymerisation with epoxides and polymerisable compounds, but it can separate lignin and cellulose from lignocellulose [97]. H3PO4 breaks down cellulose and hemicellulose polymers in biomass to form monomeric sugars. It can also react directly with lignin under any conditions, and cellulose dissolves in it. H3PO4 has been used extensively in the activation of AC, whose adsorption isotherm indicates multilayer filling, with significant mesopore formation. H3PO4, used for AC production from olive stone, has a good SBET of about 1218 m 2 /g and a good pore volume of 0.6 cm 3 /g [98]. Örkün et al. [99] studied the impact of concentration variations of H3PO4 on some precursors and considered it effective for the development of pores and producing a significant improvement of the morphology, surface chemistry and size distribution. A significant contribution to microporosity and mesoporosity was observed for grape seed activation in the 1:1 to 3:1 ratio range, especially in the pore size arrangement.

Base Treatment of Agricultural Residues
Alkaline can cause the degradation of glucose and cause the branching of carbohydrates, such as 4-O-methylglucuronic acid. They are reactive to lignin and the solvation of ether linkages and hydroxyl groups. This is useful in AC production due to delignification. The dissolution of lignin causes the removal of xylan. The use of KOH results in the breakage of longer fibres and exfoliation [100]. Improved porosity as a result of activation with KOH can be attributed to potassium interaction and the stretching of carbon layers. KOH is more effective at creating micropores due to the evidence of an interaction between layers, while NaOH is extremely active for disordered carbon materials; however, both activating agents require temperature above 800 °C. Figure 4 shows how NaOH' interacts with biomass to breakdown the long chains. The use of KOH, in the temperature range of 230-650 °C, results in a high char yield. The oxidation of biomass with KOH creates oxygen-containing surface functional groups, which may not develop properly at temperatures below 600 °C [101]. KOH is highly-effective in biomass; sugar cane activated by KOH has an SBET of 2300 m 2 /g with high methyl blue adsorption [102]. During the KOH activation process, surface species, such as alkaloids, as well as molecular species like K2CO3 and K2O, are formed [101]. NaOH impregnation of corncob resulted in high SBET between 2318 and 2474 m 2 /g. When using the optimum ratio of 1:2 to 1:1, the mesopore volumes of the AC were increased from 21% to 58% [103]. AC perpared from date palm showed competitive characteristics of 1282.49 m 2 /g, 0.66 cm 3 /g and 20.73 nm-SBET, Vtotal and average pore diameter, respectively. The adsorption was determined to be lowest at pH 3 (104.88 mg/g), increasing to 106.4 mg/g at pH 7. AC properties vary indirectly with temperature, and a maximum of 612.1 mg/g at 30 °C for relative adsorption capacity was observed with the AC from guava seed, which showed an effectiveness for amoxicillin adsorption with a SBET of 2573 m 2 /g and an average pore diameter of 1.96 nm [1].

Salts Treatment of Agricultural Residues
The hydrolysis of hemicelluloses is strongly affected by temperature and pH; a near neutral pH lowers the activation process; however, ethers and carbon-carbon bonds are relatively stable. Some salts can catalyse the ether linkages in the lignin. At a high temperature, some salts undergo the Leidenfrost effect, causing steam explosion; thus, liberating soluble phenolics in the liquid form. The hydrophilicity of lignin is increased due the bond breakages at that stage. The increase in the reaction time or temperature results in the degradation of oligomers and monomers. That could also influence degradation to produce glycoaldehyde dimer, D-fructose, 1,3-dihydroxyacetone dimer, anhydroglucose, 5-HMF and furfural. Salt can also act as a catalyst to influence the gasification rate of cellulose at the low temperature of about 400 °C.
ZnCl2 is commonly used as an activating agent in AC production, especially with biomass to obtain a high-reactivity and high-surface-area AC [104]. ZnCl2 as an activating agent acts as a dehydrating agent when impregnated in biomass, resulting in hydrolysis reactions because of intermolecular exchange and molecular migration which would cause structural alteration due to weight loss and discharge of volatiles. Hydrocarbon and oxygenated organic compounds are not affected by ZnCl2, thereby providing the AC with a skeleton with developed pores. Şahin et al. [105] studied AC preparation from Elaeagnus angustifolia seeds using ZnCl2 at 500 °C, a 1:1.5 impregnation ratio for 48 h and activation for a 1 h duration, resulting in an SBET of 1836 m 2 /g. Potato peel biomass was studied for AC production with H3PO4, KOH and ZnCl2. The activation was done at 400 °C, resulting in: SBET 1642 and 1489 m 2 /g, and Vtotal 0.96 and 0.93 cm 3 /g, for KOH and ZnCl2, respectively [106]. K2CO3 has been proven effective for several agricultural waste precursors. For sisal, for example, the resultant AC had an SBET of 1038 m 2 /g, Vtotal of 0.49 cm 3 /g and was confirmed to be effective and appropriate for the purification of solutions contaminated by ibuprofen and paracetamol from the liquid phase. Studies on bamboo and pinewood showed a higher SBET when impregnated with K2CO3 with microwave activation than for any other method. Foo and Hameed [86] compared K2CO3 and KOH for pineapple peel for 6 minutes in a microwave; the results showed ACs with SBET values of 680 and 1006 m 2 /g, respectively. Furthermore, comparison using grapeseed as the precursor, activated at 800 °C with K2CO3 and KOH, yielded ACs with SBET values of 1238 m 2 /g and 1222 m 2 /g, respectively. The average pore diameter of both remained the same, at 1.7 nm [107].
FeCl2 and FeCl3 as activating agents can boost the intermolecular interactions between activating agent and biomass precursor. There are limited investigations on the use of FeCl2 and FeCl3 for biomass AC production [108]. At the temperature range of 400-1000 °C, FeCl3 as an activating agent proved itself effective on Tara gum with a resultant SBET of 1680 m 2 /g and a Vtotal of 1 cm 3 /g [109]. Under the same conditions for Arundo donax Linn activation, results were: SBET 760 and 927 m 2 /g; Vtotal 0.466 and 0.509 cm 3 /g; and average pore diameters (nm) 2.451 and 2.11, for FeCl2 and FeCl3, respectively [110]. Another comparative study with ZnCl2, FeCl3 and MgCl2 for waste coffee biomass resulted in SBET values of 123, 977 and 846 m 2 /g, respectively [111]. The comparative study of AC synthesis from coffee ground waste with ZnCl2 and FeCl3 resulted in SBET values of 977 and 846 m 2 /g, respectively. Further study with the same precursor using MgCl2 gave a value of 123 m 2 /g [111], and the same trend was observed for the date stone [112]. MgCl2 also proved to be effective in activation of Tara gum with SBET of 1680 m 2 /g [113]. Figure 5 and Table 4 clearly show the disparity of different activating agents compared alongside the production methods. However, this comparative table shows that most activating agents under optimum production conditions have different effects on different precursors. The fact that primary characteristics of AC depend on the pyrolytic conditions and activating agents, mean that the hydrogen and oxygen contents decrease with increases in carbonisation and activation temperature. The aromaticity of carbon and morphology increases as the hydrogen/carbon ratio decreases. The relationship between temperature and surface area is not linear due to other factors that contribute to the characteristics of AC. The impregnation time and activating agent are additional determinants of these characteristics because of their direct influence on the pore sizes, and thus, release of volatiles. However, an extended impregnation period can result in the gasification of pore walls. Therefore, the burn-off as a factor should be adequately considered. Figure  5 and Table 4 show that acids, bases and ZnCl2 are more effective for activation .

Surface Chemistry Mechanisms and Morphology
AC porosity, pore volume, size, surface area and other structural characteristics are relative to adsorption capacity. FTIR analysis identifies the functional groups and chemical on the edges and planes of ACs, which are very important in AC characterisation and in prediction of adsorption performance. The surface chemistry and functional groups of AC are reliant on the precursor, activating agent, activation process and conditions. Franca et al., [83] identified oxygen, nitrogen and hydrogen, as important atoms on the surface of AC, because of their ability to bond with other elements [1].
In surface chemistry analysis, metal ions are bound by electrostatic forces into the permeable networks at acidic pH, as most effective adsorptions occur below pH 7. This is because of the strong role of the oxygenated acidic surfaces. Some adsorption at higher pH is assisted by chelating and complex formation [24]. Carboxyl groups also contribute to heavy metal adsorption by biomass adsorbents while phenolic groups are associated with the formation of complexes with heavy metal pollutants [145], and these could be direct determinants of the effectiveness of AC. While FTIR analysis provides important information, monoatomic speciesdo not possess infrared spectra and this makes complex mixtures difficult to analyse [146].
A comparison of the FTIR spectra of bamboo feedstock, traditional and conventionally activated AC and microwave-assisted activated AC [116] shows the effect of the H3PO4-induced microwave activation of bamboo's spectral pattern and shows that thermal activation with a furnace and microwave have distinctive differences. Pathak and Mandavgane examined the FTIR frequencies and the resultant effects of activation with citric acid on banana peels, showing that there are major differences dependent on the method of activation and the activating agent [147].
Huang et al. [84] demonstrated that H3PO4 breaks bonds and dissociates aliphatic and aromatic molecules, especially in biomasses, encouraging the removal of many volatile substrates, and initiating partial aromatisation and carbonisation for a defined AC. A study investigating pineapple peel impregnated with KOH activation showed FTIR spectra of the AC as major peaks within these ranges: 3230, 2360, 2040, 1420, 1050 and 830 cm -1 , indicating the location of N-H and C≡C, which are highly unstable; C=C-moderately unstable; and C-N, C-O and N-O functionalities, respectively, which indicates AC's capacity to permit attachment [86]. KOH and K2CO3-induced AC were both enhanced in relation to its char and developed better when activated by microwave irradiation [94]. The same activation process when used on a cotton stalk as a precursor showed identical absorbance bands. However, there was substantial variance in the spectra of ZnCl2-activated AC. Sharp bands of 1630 and 1600 cm −1 are distinctive and are absent in KOH and K2CO3 ACs [126]. The surface chemistry of NaOH-induced AC from pomelo skin was observed to have an FTIR spectrum within 3413 and 3247 cm −1 correlated to the amine groups, and the band at 2980 cm −1 indicated the presence of an alkane group [88]. For PKS, AC was produced through microwave and conventional methods with ZnCl2; the O-H stretching vibration receded, validating the effectiveness of the two processes. The significant effect and reduction of hydrogen bonding spectral bands show that the ZnCl2 typically dehydrates the sample from the point of impregnation.

Adsorption and Kinetics Mechanism
Pyrolysis takes place under inert conditions; this causes the release of volatile substances that form tar at elevated temperatures, depending on the type and quantity of material. Current kinetic models are inadequate for biomass pyrolysis, specifically in terms of the prediction of pyrolysis rate. Molecular modelling can potentially identify the pathways for cellulose and lignin to production of biofuels and AC. Models presume that kinetic constraints, such as the frequency factor and activation energy, are interdependent and contingent on both conversion mechanism and the extent of heating. Kinetic models presume a series of decompositions, for n th order reactions. By contrast, the distributed activation energy model (DAEM) describes the pyrolysis reaction itself, and postulates that many decomposition, n th order reactions occur simultaneously, with distributed activation energies [148]. There are also double exponential terms which can be used to describe the distributed activation energy model for isothermal pyrolysis. In order to find the accurate approximation, an asymptotic methodology is implemented [148]. The amount of tar depends on the temperature and duration of carbonisation. Feed rate also affects tar deposition, due to prevention of the escape of volatiles. Furthermore, the type of activating agent is also critical in determining the rate of tar transformation into gas.
Adsorption can be classified as physisorption or chemisorption. Physisorption uses van der Waals forces, whose effects rapidly decrease with increasing temperature [149], while chemisorption results in the formation of chemical bonds between the adsorbate and adsorbent [150]. Several factors and variables influence adsorption processes of pollutants with AC. Consequently, AC adsorbs through van der Waals, hydrogen bonding and electrostatic charge [151]. The functional groups of the adsorbent are primarily relative to the production process. Skouteris et al., [152] showed that, in some types of adsorption processes, such as in liquid-phase, the adsorption efficiency and potency of AC are strongly dependent on the physical structure of the AC, the pore assemblage and the functional groups with respect to the parent materials, and also showed that molecular weight and polarity of adsorbent are influential. Other secondary properties of the solutions that are potentially important include the adsorption thermodynamics, pH, molecular diffusion, concentration of adsorbate and ionic energy [153].
Adsorption capacity is generally determined by the percentage of the pollutant removed, calculated as in Equations (2) where, qt (mg/g) symbolises the adsorption capacity, C0 represents, initial pollutant concentration at start time and Ct (mg/cm 3 ) represents pollutant concentration at time (t). V (cm 3 ) denotes the volume of the adsorption medium and m (g), the adsorbent weight. The adsorption performances of ACs derived from agricultural wastes are shown in Table 5. Unfortunately, the literature usually provides insufficient information on the adsorption parameters. However, AC activated by H3PO4 is very effective in the removal of contaminants and adsorption, taking place at 25-30 °C. Adsorption occurs mostly in the pH range of 4-7. Salt activators have a wide range of pH for adsorption, which also depends on concentration of the solution. Adsorption isotherms are series of measurements relative to adsorbed and non-adsorbed amounts in a single process. The gas and solute adsorptions are functions of pressure and are dependent on chemical structure. Isotherm models are necessary for AC when a batch system for wastewater treatment is designed. This evaluates the suitability of the adsorption system, also showing the system to be endothermic or exothermic [69]. The thermodynamic assumptions provide a guide to the adsorption mechanism, adsorbent affinity and the fundamental approaches. The models are illustrated in Table 6 and consider several assumptions and parameters for plotting adsorption isotherms. Table 6. Adsorption isotherm models descriptions and challenges.

Washing and Milling
Some biomass wastes, such as oil palm residue (OPR), have a high percentage of tramp material, including soil, while oil palm processing waste (OPW) does not, and instead has a high oil content. Hence, the need for washing can vary significantly. A high water requirement raises the production cost and hot water may be required to remove the oil attached to the biomass precursor. If the oil is not properly removed, it produces copious amounts of smoke during carbonisation, and if the temperature is not high enough (say below 400 °C), it forms tars within the biomass material, preventing the escape of volatiles, thereby resulting in improper development of pore structure, which requires a high inert gas flow rate to effectively displace volatile materials.
OPW is produced mostly in the form of large particles and lumps; therefore, size reduction is crucial for utilisation in AC production. This is done by milling figure 6 [172], a high-energy operation [173]. Particle size is one of the crucial determinants in the thermochemical route; physical condition of biomass notwithstanding, the method influences activation rate and other production parameters [174]. There is also difficulty in milling mesocarp fibre (MF) and EFB, rather than palm kernel shell (PKS), due to low brittleness. Conventional hammer mills typically have a 250 mm diameter rotor at a rated power of about 20 kW [175], but there may be a need to use swinging hammers operating at high velocity [176]. Biomass waste can be crushed when dry, sieved and graded into different uniform sizes of less than 2 mm using a milling machine [126], to achieve uniform distribution of heat. The mechanical properties of different parts of OPW vary and it is important to minimise dust production. To minimise loss of biomass, a dust collector is installed, which aids in throughput flow and overcomes air flow resistance [177]. Pre-treatments, such as drying and sieving, occasionally play a role in determining energy consumption. Establishing uniformity of particle sizes is largely contingent on their moisture content and other physical properties. Brittleness, hardness and elasticity also affect the energy requirements in milling. Phillip et al. [178], studied the mechanical and physical influence of PKS, and showed that the aggregate crushing value is 5.3% and that of the flakiness index is 63.2%, indicating that PKS milling behaviour is acceptable. The efficiency of a hammer milling operation is determined by the nature of the biomass, and thus, milling tendencies vary widely. Several physical and mechanical properties are important, e.g., material breakage, as the fracture reaction is contingent on impact frequency, energy, moisture content and biomass properties [172]. Vogel and Peukert [179] expressed the phenomenon of breakage as in Equation (4): X represents the initial particle size, and k and Wm,ki are the impact frequency and specific kinetic energy of the impact, respectively. Wm,min is the threshold energy. The material properties in terms of its resistance and minimum specific energy are relevant to determine fracture and breakage factor which define the milling rate [180]. The energy requirement increases with reducing particle size [181]. However, it should be noted that the physical properties influence feeder design, biomass flow rate and reactor performance [182]. For each batch of AC production, the biomass should be of uniform particle size. Higher density also translates to lower tensile strain. The energy requirement for the milling process contributes to about 15%-30% of the overall energy requirement for AC production [181].

Microwave Power and Radiation Duration
The energy requirement is dependent on the type of reactor and the effect of power is relative to the duration of the process. The reaction temperature is maintained after the heating stage, as power remains constant. Evaluating the influence of microwave power on yield, time is a primary factor. Hoseinzadeh Hesas et al. [95] assessed the influence time of the microwave radiation relative to the surface consistency of AC, in order to optimise power output to achieve the appropriate heating rate and process temperature. High radiation power of above 1000 W for an extended time may result in total carbonisation with the adverse effect of reducing surface area and porosity [183]. For activation, the power range of 100-200 W is inadequate to create complete release of volatile substances, thereby resulting in improper development of pores with negligible influence on the adsorption capacity. At about 300-1000 W, the adsorption efficiency increases and pore development is better defined. However, with a higher thermal radiation there is greater loss in weight beyond the optimum range and collapse of the pore structures; thus, there needs to be a balance between activation duration and microwave power.
Microwave radiation duration is another important factor and strongly affects the resulting characteristics of the activated material. Thus, using the microwave heating method for a period of 5 min, the SBET initially increases to a maximum value of 2996 m 2 /g at 20 min, and then hardly changed with the increase in the activation duration for the char of Mesocarbon microbeads [184].
Adsorption can be improved by an increase in radiation time. For example, with pineapple as a precursor, a 4 min radiation time difference increased adsorption from 206 to 283 mg/g, which then decreased after 6 min as carbon yield decreased. Further increase in process time beyond the optimum always leads to the formation of hotspots and collapse of pore structures [86]. A typical duration is 5-20 min for char, but if raw biomass is impregnated with activation agent, an appropriate time will be about 15 min. Moisture content could also create imbalance in the prediction table for process duration.

Activation Interaction and Temperature
The inter-molecular interaction within the biomass precursor under an electromagnetic field involves the release of an enormous amount of energy relative to the quantity of material being processed. The process outcome is dependent on the dielectric factors of the precursor [185]. Reaction during activation is highly influenced by the type of activating agent. Each biomass material reacts differently to different activating agents and the products differ. Palm kernel shell (PKS) and other oil palm wastes (OPW) were used in biochar production by microwave process, at different radiation levels. The biochar yields were 38, 35 and 33 wt.%, for 500, 600, 700 W respectively [186,187]. Typically, more volatiles are released as microwave power is increased. In conventional systems, the major carbon losses occur during milling, sieving and washing. The losses during carbonisation can be minimised by the right choice of carbonisation temperature range. Mushtaq et al. [188] have explored the effects of sample variability, particle size, moisture content, type of activating agent and inert gas flow rate on the pyrolysis and activating process and concluded that each type of biomass must be individually characterised.
The external surface temperature can be measured with infrared pyrometer; however, not during the actual processing itself. Another challenge of microwave radiation is the generation of hot spots because of the non-vegetative impurities in the precursor [79,94]. The thermal energy and temperature value of the sample core can be up to 500 °C higher than the external temperature [95]. Nonetheless, microwave power of 450 W is considered to be the lowest possible power required to cause significant changes in the in the biomass's structure for production of an efficient AC; below that, AC cannot be effectively produced [84]. In order to reduce AC process time, a novel method of impregnating OPW char with CuO receptors resulted in the rapid increase of sample thermal energy, although its use resulted in the generation of widely varying pore structures [189].
Unfortunately, due to limited choices of measuring technique, sample temperature measurement was often ignored in previous works on microwave-assisted reactions [189]. There are three options for the measurement of temperature in microwaves operation: shielded thermocouples; IR-sensors, which measure infrared radiation as passive sensors; and a fibre optics sensor, which measures temperature up to 400 °C using an external transducer based on the wavelength modulation principle. Shielded thermocouple measurement is a cost-effective option [184]. However, it is inappropriate in the presence of non-polar solvents. In AC production occurring above 300 °C, thermocouples are not recommended [189]. The temperature of the sample during MW treatment can also be measured by using an infrared pyrometer [184]. In general, there is difficulty in ensuring good temperature regulation, though the use of a water jacket is possible [190]. However, such an approach will not work for any large-scale process, given the thermal inertia inherent in such a system. A built-in-sensor on the reactor and further research on the appropriate reactor material could help to overcome such challenges.

Tar Deposition
The constituents and characteristics of tars depend on the type of fuel and thermal process. The formation of tar is common; however, at a high temperature, primary tars vapours can be cracked. This situation can be influenced by reactor.
The primary tars contain substances such as dimethoxy phenol, trimethoxybenzene and hydroxy methoxy benzoic acid, and these can be transformed into xylene phenol and toluene. There are tertiary tars also contain materials such as benzene, naphthalene, acenaphthylene, phenalene and pyrene. The presence of tar compounds such as 1-methylnaphthalene, which has a boiling point of 244.8 °C, are problematic, as they can emit acrid smoke during decomposition.
The presence of tar in a thermal process creates complex problems, especially in the utilisation downstream. During AC production, AC can re-adsorb it. Tar can be removed by decomposition or adsorption by activated carbon. In the process of AC production, tar causes reduction in the performance of AC [191]. Phenol and cresol available in biomass can be degraded by microbial agents such as yeast [192] in tar removal.
A study by Abu El-Rub et al., [193] showed that tar can be removed by thermal cracking and a catalytic processes. It is necessary to address the influence of tars due to their carcinogenic character, ability to form coke and plugging which could disrupt the system. However, some catalysts can also affect the characteristics of AC. Finally, the use of alkali-metal-base for the removal of tar can also result in particle agglomeration at a high temperature.

Equipment Selection and Mode
The laboratory scale microwave typically only produces small quantities of material and 10-20 g of AC is typical. Pyrex glass reactors and Teflon reactors generally perform well in the laboratory but may not be suitable for scaling up. Ceramic/solid sintering materials also seem suitable for microwave processing but require further study. Evaluating AC production by means of laboratoryscale microwave systems is inexpensive, but cannot provide appropriate understanding of the molecular interactions and transformational kinetics in AC production at scale [187], and there is an urgent need for results from appropriately sized equipment.
There are advantages related to using a concentrated stream of energy when utilising unimode microwave radiation. However, most practical systems will use multimode radiation in a thermochemical process [189]. Multimode is relatively cheap and can be designed to deal with large sample sizes. However, unimode is better in terms of controllability [194]. The energy release of unimode radiation depends on reactor material, size, waveguide channel, the properties precursor and other contents of the sample. Generally, these devices have magnetrons directed through a waveguide and an electromagnetic field [189]. Operation is also influenced by the mixing of biomass and activating agents, the cooling method, control heating rate, the seal and microwave leakage rate. To overcome these technical challenges and reduce overall process time, a continuous process should be used, since it eliminates wastage during transfer and mechanical washing, and ensures uniform production, as most operations are automated.

Dielectric Properties
The dielectric properties of any material are primary factors in the transformation of electromagnetic energy into heat for AC production. Most biomass has poor microwave absorbing properties [195]. Abubakar et al. [196] explored the influence of dielectric properties of OPW and several studies have explored the dielectric properties of agricultural waste and other biomass materials.
The relative dielectric constant, dielectric loss factor (εr) and tangent loss for OPW and corresponding biochar, at varying frequencies (0.2-10 GHz) and at ambient conditions (room temperature of about 25 °C) are given in Table 7, for a range of materials. The dielectric constant for most materials decreases with increasing frequency [195], while the loss factor varies in the opposite direction. Most biomass materials are only weak absorbers. The average loss tangent of biomass feedstock is less than 0.1. The addition of activating agents improves the microwave absorbability [197]. In some biomass materials, absorbability increases rapidly at elevated temperatures and this can result in process challenges due to thermal runaway [198]. The poor understanding of the relative influence of electromagnetic energy on combined and mixed biomass on the microwave heating remains a challenge in obtaining homogeneous products [20]. High moisture content in a material can affect its dielectric properties and result in a high microwave treatment efficiency [197]. Table 7. Relationship between penetration depth of biomass and various microwave frequencies [196,199,200]  During carbonisation and activation, the delivery of products helps to release volatiles. When the volatile products are not desired, the issue of how to exhaust them arises in the design setup. In most laboratory tests and analyses of microwave-induced activation, modified domestic systems are used for the work, so are not relevant for industrial applications. There are also a few issues with the use of stirrers in microwave systems. Small particles are capable of elutriating with any vapour generated, especially at higher stirring speeds, affecting the carbon yield; therefore, a stirrer should not be installed close to the volatiles delivery line and size should be designed to reduce arcing which is seen as flashes or sparks [201].

Scale of Microwave for Use in Preparing AC
The technique of the microwave method to produce AC depends first and foremost on the scale of potential units. In 2010, Leonelli and Mason published an article claiming that microwave and ultrasonic processing have good prospects for industry, but the focus was primarily on the food industry [202]. Progress in the food area seems to have continued, with microwaves being used in particular for lower-temperature applications, such as drying, although interestingly, even for this type of application, there are issues with the formation of hot spots [203]. Generally, what has been offered is still relatively small, with levels of 6 L/h being suggested as adequite [204]. However, there does seem to be some recent progress and a current paper suggested that microwave units were available able to process flow rates of up to 750 kg/h for drying [205]. There is also at least one company offering a microwave reactor with a capacity of 7 m 3 , which seems to be sufficient for this type of application [206]. Interestingly, a recent patent for AC preparation from nuts, gave the technology a technological readiness level of 5 [207]. Thus, it is clear that, at least to date, there are no full-scale demonstrations of microwave technology producing AC at an industrial scale, and it is there that future research is essential if this technology is to be meaningfully used to make commercial quantities of AC in the near future [208].

Summary
The chemical activation approach for AC production is widely applied because of its ability to produce AC with a wide range of activating agents under a myriad of processing conditions. The choice of activating agent is contingent on the adsorption target and precursor. Each activating agent has a unique impact on the characteristics and applications of the resultant AC. However, due to the challenges of AC production from biomass, there is a need to develop techniques to achieve industrial-scale production of AC. Microwave systems accelerate the activation process. Bases, acids and ZnCl2 are generally considered to be particularly effective. Unfortunately, natural chemicals are rarely used for activation despite their potential to reduce secondary contamination which arises when materials like ZnCl2 and inorganic acids are used, due to the difficulty of effectively removing them by washing. It is clear that microwave treatment is potentially better than conventional approaches, especially in terms of energy saving and process duration; however, to date there are no commercial application of such technology. Despite the existence of larger and larger microwave systems, there remains an urgent need to demonstrate this technology at a commercial or nearcommercial scale.
Author Contributions: K.S.U., concept development and preparation of the original manuscript; K.P., design and formulation of the research question and supervision; R.S., arrangement of the manuscript and supervision; EA, modified and edited the manuscript; S.M., data collection for comparative study. All authors have read and adopted the manuscript.

Conflicts of Interest:
The authors declare no conflict of interest.