Feasibility Assessment of the Use of Recycled Aggregates for Asphalt Mixtures

The use of recycled aggregates, manufactured from several by-products, to replace virgin aggregates in the production of pavement asphalt mixtures needs to be encouraged. Nevertheless, there are some concerns and uncertainties about the actual environmental, economic and mechanical performance resulting from the incorporation of recycled aggregates in asphalt mixtures. Therefore, this paper has the goal of discussing important features to help decision makers to select recycled aggregates as raw materials for asphalt mixtures. Based on the literature review carried out and the own previous experience of the authors, the article’s main findings reveal that incorporating some of the most common recycled aggregates into asphalt mixtures is feasible, even in a life-cycle analysis perspective. Although some specific technical operations are sometimes necessary when using recycled aggregates in asphalt mixtures, some benefits in terms of environmental impacts, energy use and costs are likely to be achieved, as well as in what concerns the mechanical performance of the asphalt mixtures.


Introduction
The activities of constructing and maintain highways' pavements have a contribution to the footprint of transportation sector.In Portugal, as in many other countries, the most common pavements are flexible, with several layers formed by asphalt mixtures.These layers include different blends of aggregates (roughly 95% of weight), obtained by crushing rock extracted in quarries, and bitumen (about 5% of weight), produced in refineries as a by-product of distillation of crude oil, and, sometimes, also additives to change some specific features of the asphalt mixtures [1][2][3].Because this refining process is related to the energy sector, the footprint issues associated to bitumen have had generally more attention than the concerns related with the aggregates and, therefore, several solutions have been proposed to reduce the environmental impact of its use [1][2][3][4].
However, rocks are a natural non-renewable raw material and they are scarce in many territories.In addition, the capacity of landfills to dispose of by-products susceptible to being used as aggregates is running out in some countries [5].
Moreover, the production of natural aggregates demands considerable energy consumption, resulting in substantial emissions and environmental impacts [5,6].Therefore, one possible strategy to reduce the environmental impact of the exploration of natural aggregates is the use of by-products from Table 1.Portuguese specifications for the natural aggregates to be used in asphalt mixtures [20] for base, binder and surface layers.So far, it has been relatively competitive in the Portuguese market to get natural aggregates that respect these specifications.For example, in the central region of Portugal (around the capital, Lisbon, including its 3 bordering regions), there are an expressive number of quarries (50), which have Sustainability 2018, 10, 1737 3 of 23 availability of basalt, granite, greywacke, granodiorite and limestone aggregates (with enough good characteristics to be used in asphalt mixtures).Those quarries, with active licenses assigned by the Portuguese National Office for Energy and Geology, are distributed along that region as shown in Table 2 (updated on 9 March 2015) [29].
Table 2. Number of licensed quarries 1 for the region of Lisbon and surrounding regions, expressed by aggregates geological classification [29]. 1 For the production of natural aggregates for granular bases and asphalt mixtures.

Regions
In addition to these quarries, there are many others whose main activities are related to the extraction and processing of ornamental rocks, but sometimes also have crushing plants to process rock debris in order to obtain aggregates for the construction industry in general.
Taking into account the geological nature of the quarries mentioned in Table 2, it is noted that a large part (42 in 50) produce aggregates only for base and binder/regulating layers.The other quarries, only 16% (8 in 50), can provide aggregates for the production of asphalt mixtures to surface layers.These limitations are related with the properties that these aggregates can offer, whose values, on average, are summarized in Table 3. Analysing the number of licensed quarries and the main properties of three different geological natures, it is possible to verify the following reality: on the one hand, there are plenty of aggregates (limestone) for base/binder layers with good properties; on the other hand, there is a shortage of aggregates (basalt and granite) for surface layers, despite their properties being also good.

Artificial Aggregates
The incorporation of industrial by-products, so-called artificial aggregates, and their performance when used in pavements, has been described in several technical documents, namely treating their characterisation and applicability for several types of asphalt mixtures [7,[30][31][32].
Artificial aggregates come from the modification of materials, subjected to processes that may involve physical and/or chemical changes, being the most commonly used the electric arc furnace steel slag (EAFS).Other artificial aggregates may be used in asphalt mixtures, like fly ash or by-products from metal ore refining processes but only on a small scale in Portugal.
The overall quality of artificial aggregates, with the purpose of being used in asphalt mixtures, should be evaluated taking into account the key requirements related to: (a) cleanliness, size and grading; (b) strength (hardness); (c) durability; (d) particle shape; (e) texture and angularity; (f) water absorption; (g) affinity aggregate/bitumen.This kind of aggregates may substitute natural aggregates due to their scarcity in some regions and give a significant contribution to the circular economy by reducing raw material production and consumption.

Electric Arc Furnace Steel Slag (EAFS)
Aggregates obtained from the rejected slags in the production of steel, being previously processed for its reuse, can be incorporated into asphalt mixtures [7,10,33,34].
This by-product, in which oxides (calcium, magnesium and aluminium) represent more than 90% of its weight, is obtained from one of the following three sources [7]: Blast Furnace-liquid slag that solidifies by granulating under sudden cooling when thrown in a water tank, or by slow cooling (if exposed only to the air), or by a mix process that uses air and water (thus giving rise to a slag cluster); Electric Arc Furnace (such as those currently operating in Portugal-in Seixal and Maia, with a production together of more than 1.4 million tons of slag between 2007 and 2011-slag resulting from the melting of metallic scrap (caused by the electric arc produced between two graphite electrodes) that can be used after removing the metallic elements included in the initial slag; Mixed Slag-consisting essentially of oxides resulting from the injection of pure oxygen into the liquid pig iron from the first smelter coming from the blast furnace (they may be mixed with the blast furnace source for slag ).
On average, the production of a tonne of steel results in about 110 to 150 kg of black slag (potentially reusable in earthworks, other geotechnical works and pavements), as well as 20 to 30 kg of white slag, which contains very high levels of lime and, therefore, they are not reusable in this type of applications) [37].
About the properties, EAFS may have significant variations for its grade.For asphalt mixtures the most usual fraction is 0/16 or 0/20 mm.The density (due to its origin) and the water absorption (it can be more than 10%) of EAFS are high, showing an important appetence for binder consumption, much more than a natural aggregate used for the same purpose.These limitations usually exclude the coarser fraction of the slag (above 16 or 20 mm) which presents higher absorptions).
The use of EAFS in asphalt mixtures has been profoundly studied by different authors [10,30,33,34,[37][38][39][40][41][42], aiming to define the better framework to use this artificial aggregate, in general available in large quantities but with some variability for some key properties, as described.
When incorporated in asphalt mixtures to be used in surface layers, this artificial aggregate may lead to a reduction in the number of accidents due to a higher skid resistance on the pavement, thanks to its rough micro-texture [43].Figure 1 shows an example of EAFS grading curve and its respective characteristics.These characteristics came from the authors on-going consultancy work for the manager of EAFS in Portugal.

Other Artificial Aggregates
There are still some records on the use of other artificial aggregates in asphalt mixtures, but essentially at the level of research.These include the use of fly ash [48], waste wood and tyre chips [49], foundry sand [50] and ceramic aggregates [32].

Recycled Aggregates (with or without Binders)
Although more than 140 million tons per year of construction and demolition waste (CDW) have been produced in recent years in the US and over 970 million tons per year in Europe [51], only 30 to 40% are potentially reused in pavements [52].
With the aim of achieving the objectives for an effective circular economy, many countries are implementing some instruments, mechanisms and strategies to favour the reuse of materials (for example, the construction and demolition waste, CDW), in order to reduce the extraction of raw materials, resulting in less environmental pressure.
Many countries have already in place their own legislation on the CDW management, ensuring the implementation of policies to reduce, recycle and reuse waste and cover all operators, as well as the producers and holders of waste.In Portugal, for instance, this process is legally regulated since 2008 but, according to the administration's technical specifications, CDW listed in Chapter 17 of the European Waste List (Ordinance N. 209/2004) can be processed and applied only in unbound granular layers.Although in Portugal there is a clear orientation for the incorporation of CDW in the production of building materials (resolution issued by the Portuguese Council of Ministers N. 190-A/2017, December 11th), with a target of 70% for waste reuse and recycling, there is yet a lack of regularity regarding the use of recycled aggregates or their disposal in landfill in the Portuguese territory.
As concluded in the "Final Report Summary" of the "IRCOW (Innovative Strategies for High-Grade Material Recovery from CDW)" project [53], the main reasons that have led many European public authorities to pay more attention to this problem are the following: (a) CDW is an important source of waste in the EU and can be re-used or recycled; (b) there is a Directive since 2008 (Dir.2008/98/EC), which indicates a target of 70% by 2020 for the reuse of these materials; (c) recycling and reusing of CDW contributes to save natural resources, energy and may be cheaper than using natural aggregates.

Other Artificial Aggregates
There are still some records on the use of other artificial aggregates in asphalt mixtures, but essentially at the level of research.These include the use of fly ash [48], waste wood and tyre chips [49], foundry sand [50] and ceramic aggregates [32].

Recycled Aggregates (with or without Binders)
Although more than 140 million tons per year of construction and demolition waste (CDW) have been produced in recent years in the US and over 970 million tons per year in Europe [51], only 30 to 40% are potentially reused in pavements [52].
With the aim of achieving the objectives for an effective circular economy, many countries are implementing some instruments, mechanisms and strategies to favour the reuse of materials (for example, the construction and demolition waste, CDW), in order to reduce the extraction of raw materials, resulting in less environmental pressure.
Many countries have already in place their own legislation on the CDW management, ensuring the implementation of policies to reduce, recycle and reuse waste and cover all operators, as well as the producers and holders of waste.In Portugal, for instance, this process is legally regulated since 2008 but, according to the administration's technical specifications, CDW listed in Chapter 17 of the European Waste List (Ordinance N. 209/2004) can be processed and applied only in unbound granular layers.Although in Portugal there is a clear orientation for the incorporation of CDW in the production of building materials (resolution issued by the Portuguese Council of Ministers N. 190-A/2017, December 11th), with a target of 70% for waste reuse and recycling, there is yet a lack of regularity regarding the use of recycled aggregates or their disposal in landfill in the Portuguese territory.
As concluded in the "Final Report Summary" of the "IRCOW (Innovative Strategies for High-Grade Material Recovery from CDW)" project [53], the main reasons that have led many European public authorities to pay more attention to this problem are the following: (a) CDW is an important source of waste in the EU and can be re-used or recycled; (b) there is a Directive since 2008 (Dir.2008/98/EC), which indicates a target of 70% by 2020 for the reuse of these materials; (c) recycling and reusing of CDW contributes to save natural resources, energy and may be cheaper than using natural aggregates.
Another good effort to encourage the reuse of recycled aggregates was given by the "DIRECT-MAT (Techniques of demolition and recycling of road materials)" project, developed between 2009 and 2011 with the involvement of 20 partners from 15 European countries [54].
Nowadays, the main concepts involved in the comprehensive process of waste management should prioritize strategies that favour the implementation of the most recent 7 R's rule: Rethink, Redesign, Reuse, Repair, Remanufacture, Recycle and Recover [55].However, a risk assessment must be carried out when re-using waste materials in asphalt mixtures, targeting: (a) the type of waste; (b) mechanical risks; chemical/physical risks; (c) the lifecycle public health risks; (d) environmental risks [50].
The incorporation of recycled aggregates in asphalt mixtures or in other type of layers for pavements, or even in other type of works, has also been recently described in several articles and technical documents [2,7,[30][31][32]48,56].
A good way to contribute to the accomplishment of the aforementioned goals is to reuse reclaimed asphalt pavement (RAP) and recycled concrete aggregates (RCA) in asphalt mixtures.

Reclaimed Asphalt Pavement (RAP)
The use of RAP in asphalt mixtures offers a number of economic and environmental benefits already described for other reusing types, despite the fact that some gas emission types could have an increase [57], especially if pre-heating of RAP is used when fabricating HMA, in order to achieve a high rate of incorporation.This is irrelevant when the incorporation is made in the cold state (less rate of incorporation however) and if WMA is the asphalt mixture being produced.
The efforts to materialize the reuse of RAP come from 20 to 30 years ago.The tendency is trying to increase the incorporation rate of RAP in asphalt mixtures.The use of RAP in rates around 35% is frequent, as is reported in several studies [8,58,59], but there is a tendency to increase this percentage up to 100% [60][61][62].
In Europe, the numbers of the available RAP used in hot and warm recycling changed only slightly in recent years, despite the production of asphalt mixtures have had a reduction, as can be seen in Figure 2.This figure shows the masses (in Mt) of the oldest [63] and most recent [64] known figures about the total production of HMA and WMA in Portugal, in Spain, in the country with higher production (Germany) and in a country in the intermediate level (France).The amount of the available RAP and its use in asphalt mixtures for these countries and in Europe are also indicated.Another good effort to encourage the reuse of recycled aggregates was given by the "DIRECT-MAT (Techniques of demolition and recycling of road materials)" project, developed between 2009 and 2011 with the involvement of 20 partners from 15 European countries [54].
Nowadays, the main concepts involved in the comprehensive process of waste management should prioritize strategies that favour the implementation of the most recent 7 R's rule: Rethink, Redesign, Reuse, Repair, Remanufacture, Recycle and Recover [55].However, a risk assessment must be carried out when re-using waste materials in asphalt mixtures, targeting: (a) the type of waste; (b) mechanical risks; chemical/physical risks; (c) the lifecycle public health risks; (d) environmental risks [50].
The incorporation of recycled aggregates in asphalt mixtures or in other type of layers for pavements, or even in other type of works, has also been recently described in several articles and technical documents [2,7,[30][31][32]48,56].
A good way to contribute to the accomplishment of the aforementioned goals is to reuse reclaimed asphalt pavement (RAP) and recycled concrete aggregates (RCA) in asphalt mixtures.

Reclaimed Asphalt Pavement (RAP)
The use of RAP in asphalt mixtures offers a number of economic and environmental benefits already described for other reusing types, despite the fact that some gas emission types could have an increase [57], especially if pre-heating of RAP is used when fabricating HMA, in order to achieve a high rate of incorporation.This is irrelevant when the incorporation is made in the cold state (less rate of incorporation however) and if WMA is the asphalt mixture being produced.
The efforts to materialize the reuse of RAP come from 20 to 30 years ago.The tendency is trying to increase the incorporation rate of RAP in asphalt mixtures.The use of RAP in rates around 35% is frequent, as is reported in several studies [8,58,59], but there is a tendency to increase this percentage up to 100% [60][61][62].
In Europe, the numbers of the available RAP used in hot and warm recycling changed only slightly in recent years, despite the production of asphalt mixtures have had a reduction, as can be seen in Figure 2.This figure shows the masses (in Mt) of the oldest [63] and most recent [64] known figures about the total production of HMA and WMA in Portugal, in Spain, in the country with higher production (Germany) and in a country in the intermediate level (France).The amount of the available RAP and its use in asphalt mixtures for these countries and in Europe are also indicated.Regarding the characterization of RAP samples, it must be taken into account that they can have significant variations, depending on the origin of the materials recovered.Therefore, it is essential to separate and identify the various lots according to their origin in order to obtain homogeneous materials, which may be more suitable for future reuse [37].Regarding the characterization of RAP samples, it must be taken into account that they can have significant variations, depending on the origin of the materials recovered.Therefore, it is essential to separate and identify the various lots according to their origin in order to obtain homogeneous materials, which may be more suitable for future reuse [37].
The properties of the asphalt mixture's new binder (pen n and/or T n R&B ), which include RAP, can be found by applying the European standard EN 13108-1 [65] according to Equation (1) or Equation (2) (adapted from EN 13108-1). or: where: p i -Percentage of: the "final mix", "old bitumen" or "new bitumen" (i = mix, o, n); mix, o, n-Indices, i, for: "mix of bitumens", "old bitumen" or "new bitumen", respectively; The characterization of RAP can be done according to the EAPA recommendations [66], determining: the percentage of residual binder (EN 12697-1 [67]), its penetration at 25 • C (EN 1426 [68]), ring and ball softening temperature (EN 1427 [69]) and viscosity (EN 12596 [70]), before and after the bitumen extraction, as well as the aggregate's gradation.The standard EN 13108-8 [71], may also be needed, in particular for the foreign matter content, determined in accordance with EN 12697-42 [72].Figure 3 shows an example of RAP grading curve and its properties after bitumen extraction coming from the authors' activities.The properties of the asphalt mixture's new binder ( and/or & ), which include RAP, can be found by applying the European standard EN 13108-1 [65] according to Equation (1) or Equation (2) (adapted from EN 13108-1). or: where: pi-Percentage of: the "final mix", "old bitumen" or "new bitumen" (i = mix, o, n); mix, o, n-Indices, i, for: "mix of bitumens", "old bitumen" or "new bitumen", respectively; -Bitumen penetration @ 25 °C (i = mix, o, n); The characterization of RAP can be done according to the EAPA recommendations [66], determining: the percentage of residual binder (EN 12697-1 [67]), its penetration at 25 °C (EN 1426 [68]), ring and ball softening temperature (EN 1427 [69]) and viscosity (EN 12596 [70]), before and after the bitumen extraction, as well as the aggregate's gradation.The standard EN 13108-8 [71], may also be needed, in particular for the foreign matter content, determined in accordance with EN 12697-42 [72].Figure 3 shows an example of RAP grading curve and its properties after bitumen extraction coming from the authors' activities.
The compliance with these standards can be facilitated by a correct sorting and by using suitable crushing and screening equipment.Figure 4 presents an example of an aggregates recycling installation, appropriate for RCA processing.
The compliance with these standards can be facilitated by a correct sorting and by using suitable crushing and screening equipment.Figure 4 presents an example of an aggregates recycling installation, appropriate for RCA processing.At a full processing facility, as the one identified in Figure 4, particular attention should be given to screening and pre-removal of debris (before and after primary crushing-jaw crusher).It is then essential to re-crush the coarser fraction (from that obtained in the primary crusher) by using a secondary impactor crusher.This procedure improves the shape index and the final quality of the resulting aggregates, which can thus be used in almost all domains of civil engineering.
The RCA used in asphalt mixtures generally has a range size for the grade of 0/20 mm. Figure 5 shows an example of RCA grading curve and its respective characteristics.This also came from the authors' activities.At a full processing facility, as the one identified in Figure 4, particular attention should be given to screening and pre-removal of debris (before and after primary crushing-jaw crusher).It is then essential to re-crush the coarser fraction (from that obtained in the primary crusher) by using a secondary impactor crusher.This procedure improves the shape index and the final quality of the resulting aggregates, which can thus be used in almost all domains of civil engineering.
The RCA used in asphalt mixtures generally has a range size for the grade of 0/20 mm. Figure 5 shows an example of RCA grading curve and its respective characteristics.This also came from the authors' activities.At a full processing facility, as the one identified in Figure 4, particular attention should be given to screening and pre-removal of debris (before and after primary crushing-jaw crusher).It is then essential to re-crush the coarser fraction (from that obtained in the primary crusher) by using a secondary impactor crusher.This procedure improves the shape index and the final quality of the resulting aggregates, which can thus be used in almost all domains of civil engineering.
The RCA used in asphalt mixtures generally has a range size for the grade of 0/20 mm. Figure 5 shows an example of RCA grading curve and its respective characteristics.This also came from the authors' activities.

Other Recycled Aggregates
As reported by EAPA [50], there are some other recycled aggregates likely to be used in asphalt mixtures, for example: (a) Recycled glass and plastic; (b) Recovered roofing membranes and shingles; (c) Spent catalyst fines.Poulikakos et al. [49] also mentioned several alternatives that can be reused, namely, different types of plastics and Silvestre et al. [32] pointed out another possibility in the design of open graded surface layers with recycled ceramic aggregates obtained from tile industry for medium-low volume roads.

Binders
At the moment, there are several binders available in the markets, which seek to respond to the most demanding requests, namely, those arising from adverse climates, aggressive traffic and difficult orography.The increased demands on bitumen performance have led to the improvement of its rheological properties by the addition of various types of modifying agents.The relevant information about bitumen and some products used to improve different properties of the final blends is beyond the scope of this paper but they can be found in several references [79][80][81][82][83].

Specificities in the Use of non-Traditional Aggregates
In general, the technical community has some concerns regarding performance of non-traditional aggregates as constituents of asphalt mixtures.Moreover, particularly in territories where there is abundance of natural aggregates and, consequently, the cost of natural aggregates is moderate, there are also concerns about the possible increasing of the production costs of non-traditional aggregates in comparison with the costs of natural aggregates.
Although the aggregates should be selected according to the desired characteristics of asphalt concrete, it must be emphasized that the acceptance thresholds generally indicated in the aggregates' specifications issued by the administrations of transport infrastructures may constitute an obstruction to the use of non-traditional aggregates.This may happen because the fulfilment of prescription-based requirements is likely to result in (an undesirable) rejection of most non-traditional aggregates.
A prescriptive approach considers that a specific aggregate material will behave satisfactorily as constituent of a specific bituminous mixture if, for instance, it fulfils some physical, geometric or chemical requirements previously evaluated in the aggregate alone.If a performance-based approach was followed to select the aggregates, the accept/reject criteria would be verified based on the mechanical and/or functional performance achieved by the asphalt mixture.There is, therefore, a great margin of progression of the principles behind the way requirements of non-traditional aggregates are established.
In Portugal, LNEC, the Portuguese National Laboratory of Civil Engineering, has published a guide for the production of recycled HMA [84] providing some guidelines on the use of the recycled aggregates.The recommendations consider some aspects on the limit of presence of strange materials, particle size distribution, limit of water content, maximum rate of incorporation of recovered material (from 10 to 50%), among others.Despite these rules have been published, different studies and applications may support the use of RAP in asphalt mixtures in a different way, aiming to increase the achieved level of material recycling.This will be discussed in the next sections aiming the incorporation of own and elsewhere experiences.

Mechanical Performance of Asphalt Mixtures with Non-Traditional Aggregates
Being concerned with the durability of pavements and road network quality, the administrations look for solutions of asphalt mixtures with potential to meet those requirements.They aspire to providing the road the adequate functional features, such as ride quality, skid resistance and low noise emissions, as well as satisfactory mechanical performance, this being achieved through appropriate stiffness of the asphalt mixtures, good resistance to cracking, rutting and water damage.
Although more attention is usually paid to bitumen, seen as the key factor of the expected mechanical behaviour of the asphalt mixtures, the truth is, apart from the bitumen, the observed performance depends on the aggregate and the interaction between the aggregate and the binder.Consequently, this section focuses on the performance tendencies achieved when non-traditional aggregates are used in bituminous mixtures as partial substitutes of natural aggregates.Most of the available outcomes are from laboratory studies, which consisted of submitting specimens produced in laboratory or collect from experimental pavement sections to performance tests.Even though, the knowledge accumulated up to now reveals a promising evolution of using different sources of recycled aggregates to incorporate into asphalt mixtures (HMA or WMA).

Asphalt Mixtures with RAP
Based on the American long-term pavement performance program (LTPP) database, which considers roughly 15 years of data records, the authors participated in a study to evaluate the influence of using RAP in asphalt mixtures on the evolution of pavement conditions, when the mixes are applied in pavements rehabilitation [85].Because there was some lack of information in the database, it did not allow derivation of definitive conclusions.Nevertheless, a statistical analysis carried out allowed verifying a favourable contribution to pavement performance in terms of ride quality and rutting resistance.In what concerns cracking, considering the climatic conditions and the levels of traffic observed, the contribution of RAP in the asphalt mixtures applied to reinforce pavements was unfavourable.
Apart from that study, some others have evaluated the use of RAP to produce asphalt mixtures [58,[60][61][62]86,87].The available information allows drawing general tendencies about the expected performance and, thus, emphasises the relevance of recycling RAP in new asphalt mixtures.
The authors can declare, based on their own previous experience, that up to 40% of RAP (by total weight) can be incorporated in the production process in a conventional batch plant just by premixing RAP and new aggregates 20 s before adding the new binder [86,87].Adding RAP in a plant allow a better control of the process, increasing the level of confidence on expected properties of the final blend and allowing a mechanical performance comparable to that of similar mixtures produced without RAP [2,8,59].
The most common mechanical properties of hot-mix asphalt with RAP, e.g., stiffness, resistance to fatigue cracking and rutting, tend to be better or at least equal to the characteristics of a traditional mixture [8,59,88].
Consequently, if feasible standards are developed, the industry and the highways' administrations could considerably increase the use of RAP to produce asphalt mixtures [59].
In the case of WMA with up to 35% of RAP, the use of additives to lower the handling temperature is an additional source of variability of mechanical performance results.Nevertheless, the studies carried out [2,89] also reveal that mechanical performance of WMA with RAP is suitable, enlarging the possibilities of using RAP in asphalt mixtures.
Based on literature and own experience of the authors, Table 4 summarises the general asphalt mixtures' performance when incorporating RAP as a constituent.More detailed information on the specific aspects of mechanical behaviour can be found elsewhere [7,8,88,90].
Table 4. Effect on mechanical performance of using RAP as partial substitute of the components (adapted from [7,8,88,90]).Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Mor fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA usually high porosity and water absorption [77,91] as stated before.This has been reported main reason to increase bitumen content in asphalt concrete (AC) to compensate the b absorption [77,91].Because RCA fractions have a considerable percentage of angular and textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,7 In what concerns water sensitivity of the asphalt concrete, the substitution of part o aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to h induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt co [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease w higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorpo together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA ten contribute to reduce the observed performance [96].That tendency was not observed in s studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (W [7], produced with temperature reduction allowable by the use of additives in the form of p such as organic waxes or surfactants.The effect on the mechanical performance of WM incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned ou for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved good results.On the contrary, the use of RCA and the specific surfactant applied led to weak r in what concerns resistance to permanent deformation.Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreove fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA hav usually high porosity and water absorption [77,91] as stated before.This has been reported as th main reason to increase bitumen content in asphalt concrete (AC) to compensate the bind absorption [77,91].Because RCA fractions have a considerable percentage of angular and roug textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91 In what concerns water sensitivity of the asphalt concrete, the substitution of part of th aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occu mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concre [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporate together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends contribute to reduce the observed performance [96].That tendency was not observed in sever studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA [7], produced with temperature reduction allowable by the use of additives in the form of pellet such as organic waxes or surfactants.The effect on the mechanical performance of WMA b incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcom for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved ver good results.On the contrary, the use of RCA and the specific surfactant applied led to weak resul in what concerns resistance to permanent deformation.Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Mor fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA usually high porosity and water absorption [77,91] as stated before.This has been reported main reason to increase bitumen content in asphalt concrete (AC) to compensate the b absorption [77,91].Because RCA fractions have a considerable percentage of angular and textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,7 In what concerns water sensitivity of the asphalt concrete, the substitution of part o aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to h induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt co [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease w higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorpo together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA ten contribute to reduce the observed performance [96].That tendency was not observed in s studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (W [7], produced with temperature reduction allowable by the use of additives in the form of p such as organic waxes or surfactants.The effect on the mechanical performance of WM incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned ou for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved good results.On the contrary, the use of RCA and the specific surfactant applied led to weak r in what concerns resistance to permanent deformation.usually decreases.may increas unchanged. 1Comparing with conventional HMA without RAP blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser nat fine particles of RCA have much more voids than coarse aggr usually high porosity and water absorption [77,91] as stated b main reason to increase bitumen content in asphalt concre absorption [77,91].Because RCA fractions have a considerab textured particles, Marshall stability tend to increase, and Mars In what concerns water sensitivity of the asphalt concr aggregates by RCA generally has a negative contribution [9,74,7 mainly if RCA is used as the fine fraction [9,94], particularly i induce some ageing [95].
In what concerns resistance to fatigue cracking of hot m contribute to reduce the observed performance [96].That ten studies referred to by Pasandín & Pérez [9], in which RCA imp The authors have also studied the effect of using RCA in [7], produced with temperature reduction allowable by the us such as organic waxes or surfactants.The effect on the me incorporating RCA as aggregates (Table 5) was slightly differe for hot-mix asphalt.Particularly, the combination of RCA and w good results.On the contrary, the use of RCA and the specific s in what concerns resistance to permanent deformation.Comparing with a similar WMA t RAP. 3 Depends on the applied additives.
ixtures with RCA mortar present in RCA around the coarser natural aggregates is porous.Moreover, RCA have much more voids than coarse aggregates.As a consequence, RCA have osity and water absorption [77,91] as stated before.This has been reported as the increase bitumen content in asphalt concrete (AC) to compensate the binder 1].Because RCA fractions have a considerable percentage of angular and rough s, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].ncerns water sensitivity of the asphalt concrete, the substitution of part of the A generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur used as the fine fraction [9,94], particularly if the blends are submitted to heat to ing [95].y contribute to improve the resistance to permanent deformation of asphalt concrete ut the literature [9] also mentions that permanent deformation can decrease when a e of RCA requires more bitumen and when fine fractions of RCA are incorporated arser particles.cerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to uce the observed performance [96].That tendency was not observed in several to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) ith temperature reduction allowable by the use of additives in the form of pellets, waxes or surfactants.The effect on the mechanical performance of WMA by A as aggregates (Table 5) was slightly different from the aforementioned outcome alt.Particularly, the combination of RCA and wax in the same blends achieved very the contrary, the use of RCA and the specific surfactant applied led to weak results resistance to permanent deformation.ct on mechanical performance of using RCA as partial substitute of the aggregates [7,90])  Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives. .

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, ine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have sually high porosity and water absorption [77,91] as stated before.This has been reported as the ain reason to increase bitumen content in asphalt concrete (AC) to compensate the binder bsorption [77,91].Because RCA fractions have a considerable percentage of angular and rough extured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the ggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur ainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to nduce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete 9,74,77,91-95] but the literature [9] also mentions that permanent deformation can decrease when a igher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated ogether with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to ontribute to reduce the observed performance [96].That tendency was not observed in several tudies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) 7], produced with temperature reduction allowable by the use of additives in the form of pellets, uch as organic waxes or surfactants.The effect on the mechanical performance of WMA by ncorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome or hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very ood results.On the contrary, the use of RCA and the specific surfactant applied led to weak results n what concerns resistance to permanent deformation.Comparing with conventional HMA. 2 Comparing with similar WMA blends without RCA. .

Asphalt Mixtures with EAFS
usually unchanged.Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur  Comparing with a similar WMA blend without RAP.3 Depends on the applied additives. .

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have lly high porosity and water absorption [77,91] as stated before.This has been reported as the reason to increase bitumen content in asphalt concrete (AC) to compensate the binder rption [77,91].Because RCA fractions have a considerable percentage of angular and rough red particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].In what concerns water sensitivity of the asphalt concrete, the substitution of part of the egates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur  Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur  Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Comparing with conventional HMA without RAP blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser nat fine particles of RCA have much more voids than coarse aggr usually high porosity and water absorption [77,91] as stated b main reason to increase bitumen content in asphalt concre absorption [77,91].Because RCA fractions have a considerab textured particles, Marshall stability tend to increase, and Mars In what concerns water sensitivity of the asphalt concr aggregates by RCA generally has a negative contribution [9,74,7 mainly if RCA is used as the fine fraction [9,94], particularly i induce some ageing [95].
RCA usually contribute to improve the resistance to perma WMA with RCA  Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreove fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA hav usually high porosity and water absorption [77,91] as stated before.This has been reported as th main reason to increase bitumen content in asphalt concrete (AC) to compensate the bind absorption [77,91].Because RCA fractions have a considerable percentage of angular and roug textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91 In what concerns water sensitivity of the asphalt concrete, the substitution of part of th aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occu mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat induce some ageing [95].Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].ct on mechanical performance of using RAP as partial substitute of the components [7,8,88,90]). .

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, ine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have sually high porosity and water absorption [77,91] as stated before.This has been reported as the ain reason to increase bitumen content in asphalt concrete (AC) to compensate the binder bsorption [77,91].Because RCA fractions have a considerable percentage of angular and rough usually unchanged.Comparing with conventional HMA. 2 Comparing with similar WMA blends without RCA.

Asphalt Mixtures with EAFS
When EAFS is incorporated in asphalt mixtures as part of the natural aggregates the general mechanical performance of the produced hot asphalt mixtures tends to improve.This generally happens in what concerns Marshall stability, indirect tensile strength, stiffness modulus, resistance to fatigue cracking and resistance to rutting.Since the roughness of steel slag is high, an improved adhesion between the binder film and the aggregate is usually achieved [97].A better interlock between aggregate particles is also reported to contribute to a better behaviour of asphalt mixture [97].The specific features of EAFS allow an improved resistance to heavy loads and shear stress [10].Although the best results have been achieved with incorporation of up to 30% of EAFS, a number of successful cases with higher levels of EAFS have been reported [10].
Resistance to water seems to be an area in which the results are not consistent.Some authors [98] have obtained higher resistance to water in asphalt mixtures with coarse and fine EAFS aggregates.A thicker bitumen film involves the aggregates of EAFS because a higher binder content is generally used, and the improved aggregate-binder adhesion are the explanation for the enhanced performance achieved.Other authors [42] have observed higher water sensitivity in WMA with coarse slag aggregates in comparison with identical mixtures with limestone aggregates.A worse affinity of the EAFS with the binder than that of limestone aggregate was reported in that study to explain the reduction of resistance to water.
Taking into consideration the results available in the literature and the own experience of the authors, Table 6 reviews the typical performance of asphalt mixtures in which part of natural aggregates were substituted by EAFS.Specific discussion on the mechanical behaviour can be found elsewhere [7,10,90].Table 6.Effect on mechanical performance of using EAFS as partial substitute of the aggregates (adapted from [7,10,90]).Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Usually increases.usually decreases.may increase.may decrease.usuall unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Mor fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA usually high porosity and water absorption [77,91] as stated before.This has been reported main reason to increase bitumen content in asphalt concrete (AC) to compensate the b absorption [77,91].Because RCA fractions have a considerable percentage of angular and textured particles, stability tend to increase, and Marshall flow tend to decrease [74,7 In what concerns water sensitivity of the asphalt concrete, the substitution of part o aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to h induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt co [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease w higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorpo together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA ten contribute to reduce the observed performance [96].That tendency was not observed in s studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (W [7], produced with temperature reduction allowable by the use of additives in the form of p such as organic waxes or surfactants.The effect on the mechanical performance of WM incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned ou for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved good results.On the contrary, the use of RCA and the specific surfactant applied led to weak r in what concerns resistance to permanent deformation.Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Comparing with a similar WMA blend without RAP.3 Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results in what concerns resistance to permanent deformation.Usually increases.usually decreases.may increase.may decrease.usually unchanged. 1Comparing with conventional HMA without RAP. 2 Comparing with a similar WMA blend without RAP. 3Depends on the applied additives.

Asphalt Mixtures with RCA
The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, fine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have usually high porosity and water absorption [77,91] as stated before.This has been reported as the main reason to increase bitumen content in asphalt concrete (AC) to compensate the binder absorption [77,91].Because RCA fractions have a considerable percentage of angular and rough textured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the aggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur mainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to induce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete [9,74,77,[91][92][93][94][95] but the literature [9] also mentions that permanent deformation can decrease when a higher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated together with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to contribute to reduce the observed performance [96].That tendency was not observed in several studies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) [7], produced with temperature reduction allowable by the use of additives in the form of pellets, such as organic waxes or surfactants.The effect on the mechanical performance of WMA by incorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome for hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very good results.On the contrary, the use of RCA and the specific surfactant applied led to weak results  The cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, ine particles of RCA have much more voids than coarse aggregates.As a consequence, RCA have sually high porosity and water absorption [77,91] as stated before.This has been reported as the ain reason to increase bitumen content in asphalt concrete (AC) to compensate the binder bsorption [77,91].Because RCA fractions have a considerable percentage of angular and rough extured particles, Marshall stability tend to increase, and Marshall flow tend to decrease [74,77,91].
In what concerns water sensitivity of the asphalt concrete, the substitution of part of the ggregates by RCA generally has a negative contribution [9,74,77,[91][92][93].The opposite tends to occur ainly if RCA is used as the fine fraction [9,94], particularly if the blends are submitted to heat to nduce some ageing [95].
RCA usually contribute to improve the resistance to permanent deformation of asphalt concrete 9,74,77,91-95] but the literature [9] also mentions that permanent deformation can decrease when a igher percentage of RCA requires more bitumen and when fine fractions of RCA are incorporated ogether with coarser particles.
In what concerns resistance to fatigue cracking of hot mix asphalt the use of RCA tends to ontribute to reduce the observed performance [96].That tendency was not observed in several tudies referred to by Pasandín & Pérez [9], in which RCA improved resistance to fatigue.
The authors have also studied the effect of using RCA in warm-mix asphalt mixtures (WMA) 7], produced with temperature reduction allowable by the use of additives in the form of pellets, uch as organic waxes or surfactants.The effect on the mechanical performance of WMA by ncorporating RCA as aggregates (Table 5) was slightly different from the aforementioned outcome or hot-mix asphalt.Particularly, the combination of RCA and wax in the same blends achieved very ood results.On the contrary, the use of RCA and the specific surfactant applied led to weak results usually unchanged. 1Comparing with conventional HMA. 2 Comparing with similar WMA blends without EAFS.

Asphalt Mixtures with Other Types of Non-Conventional Aggregates
As abovementioned, other non-conventional aggregates have been used to produce asphalt mixtures but the level of use is secondary as compared to the other aforementioned by-products.
The addition of recycled brick powders as filler, for instance, has been reported in the literature [99].In comparison with similar blends with limestone filler, the asphalt mixtures with recycled brick filler demonstrated in laboratory tests enhanced resistance to rutting and fatigue, as well as lower water sensitivity [99].The substitution of up to 30% by weight of the asphalt mixture with recycled ceramic wastes from tiles industry in HMA was reported to be reasonable for binder course performance requirements for medium-low volume roads [32].
Several authors, mentioned by [49] have studied the use of polyethylene terephthalate (PET), a thermoplastic polymer resin of polyester, typically used in plastic bottles, to substitute aggregates in HMA.PET has been tested in the form of granules sizes (from 1.2 mm to 2.4 mm) to replace up to 25% by weight of the asphalt mixture [100].Generally speaking, the preliminary uses of PET as aggregates allowed an increase of stiffness and fatigue resistance [101] of the asphalt mixtures, as well as an improved resistance to permanent deformation [102,103].
Other types of plastic wastes, such as PEX-cross-linked polyethylene-were used as partial substitutes of aggregates and binder modifier [104].Although resistance to permanent deformation was better in the asphalt mixtures with PEX, resistance to water and resistance to fatigue were not improved with the introduction of 5% by volume of the asphalt mixture, despite the stiffness has increased.
Glass was also evaluated as aggregate substitute in asphalt mixtures [105,106].In some cases, it was used in the form of powder or fibres.Because the particles of glass are usually flat and elongated they are likely to difficult compaction of the mixtures.Also, some stripping problems have been reported for asphalt mixtures with glass wastes but the simultaneous adding of hydrated lime as anti-stripping agent can overcome the problem [107].According to Huang et al. [107], although satisfactory performance was observed for asphalt pavements containing from 10 to 15% of crushed glass in surface course mixtures, higher content of glass and particles larger than 4.75 mm are considered more suitable for binder and base layers.

Direct Costs
Direct costs associated to the use of recycled aggregates are just a small part of all the costs related to the incorporation of non-conventional aggregates in asphalt mixtures.In fact, if the evaluation of costs takes all the funds expended in the life-cycle of asphalt mixtures into account, the costs incurred with manufacturing, operation and end-of-life may be considerably higher [108].The perspective of life-cycle cost (LCC) is more useful to the highways administrations as they are managing the infrastructure throughout its life span.Apart from the administration costs, LCC analysis has been increasingly considering the stakeholders standpoint by including the user costs and the environmental costs [109].
However, in the viewpoint of contractors, direct costs are a crucial variable because they are one of the most important topics of analysis to support the decision of using recycled aggregates to produce asphalt mixtures.Despite this, the attractiveness of recycled aggregates to the contractors will depend on two main factors: the costs of the raw material itself as well as the production costs of the asphalt mixtures with recycled aggregates; and the durability and in-service performance of the resulting asphalt layer throughout the contract's warranty period.
In view of the above, direct costs of typical asphalt mixtures, with and without recycled aggregates, were determined to assess the expected influence of incorporating of EAFS, RAP or RCA as non-conventional aggregates.The analysis was carried out for the Portuguese reality, including average purchase costs of raw materials, equipment costs, labour costs and the common margins considered in public works.Table 7 summarises de computation of average direct costs of asphalt mixtures produced with the constituents shown in the table.Some assumptions were included in these simulations in what concerns transport, for instance.It was assumed that the aggregate transport costs (from the quarries or processing facilities to the asphalt plants) were those corresponding to an average transport distance of 20 km.
The results allow to conclude that for both HMA and WMA the blends produced with roughly 35% of recycled aggregates by weight of the aggregates' blend have lower direct costs than similar blends manufactured with conventional virgin aggregates.In the case of HMA the costs may reduce from 1.6 to 16.3% (RAP), while for WMA the costs may decrease from 1.5 to 15.6%.The highest decreases in direct costs were obtained for RAP because the recovered binder from RAP also contributes to reduce the use of new bitumen.
Another important question related with direct costs is the durability of the in-service asphalt layers.Based on the information reported by EAPA [110], the authors considered a life span of 15 years for the HMA and WMA.This durability of the asphalt mixtures was used to calculate the direct costs per year of in-service life.Since there is some uncertainty on the in-service life of asphalt layers, particularly in the case of blends with recycled aggregates, an additional analysis was carried out in which a variation a ±20% of in-service life of blends with recycled aggregates was considered.Figure 6 presents the obtained direct costs for the three scenarios of analysis, and Figure 7 shows the corresponding variation of annual costs in comparison to those of blends without recycled aggregates.All the costs correspond to the present value, not having included any type of discount factor.
As the results show, the reduction of the annual direct costs considerably depends on the in-service material's life span.If the mechanical performance of the asphalt mixtures produced with recycled aggregates is somehow lower than that of conventional asphalt mixtures, the benefits in direct costs can be eliminated.Nevertheless, as aforementioned, the general expectations on the mechanical performance and, hence, the life span of asphalt mixtures with recycled aggregates are similar of those of comparable conventional asphalt mixtures.Therefore, the use of recycled aggregates in real pavements must be increased to allow systematic observation of in-service durability of asphalt mixtures with that type of aggregates.It must be also emphasized that other costs, such as those related with energy consumption and emissions, have also a crucial significance in terms of analysis of life-cycle analysis and are of major relevance to support the decisions of using recycled aggregates as constituents of asphalt mixtures.Table 7.Estimated costs per tonne of asphalt mixture.

Issues Related with Energy Consumption and Emissions
This section intends to emphasize the issues related to energy spent and emissions specifically connected to the use of non-conventional aggregates as compared to virgin aggregates.
Some authors [6] state that, from a standpoint of greenhouse gas emissions throughout the entire life cycle of pavements, the benefits of using recycled non-conventional aggregates can be reduced if the recycled raw materials must be transported from long distances, or if performance achieved by the materials is worse than that of conventional materials.In the study carried out by [5] the transport of aggregates was found to have the highest impact and energy consumption in an analysis from cradle to site.
In general, energy use and emissions in a life-cycle assessment (LCA) is based on a cradle to grave analysis [6,111].This LCA may be organised in five parts, such as proposed by Thives and Ghisi [112]: 1-raw materials and production; 2-construction; 3-use; 4-maintenance; 5-end-of-life.The incorporation of recycled aggregates in asphalt mixtures is likely to result in certain benefits in phases 1 and 2, since for recycled aggregates the extraction and crushing operations are partially eliminated, the transport distance is potentially shortened, and the use of a non-renewable resource is reduced.Also, some impacts of landfilling are avoided in phase 5 for recycled aggregates [5,113].If non-conventional recycled aggregates improve mechanical performance of the asphalt mixtures, some environmental benefits can also be expected in phase 4, as less maintenance operations will be necessary.Nevertheless, the opposite will occur if the evolution of pathologies is earlier in asphalt layers with recycled aggregates and, thus, the frequency of maintenance actions is higher [5,114].
Detailed results of energy consumption, GHG's emissions and environmental damage assessment can be found elsewhere [5,114].This section focuses on the general tendencies, allowing it to illustrate the environmental advantages of using recycled aggregates as constituents of asphalt mixtures.
The production of asphalt mixtures whose constituents need to be dried and heated is responsible for the most part of energy consumption and emissions, which result from the fuel spent in the burners installed in the plants' dryers [112].The emissions released during the heating phase of the aggregate consist mainly of water steam from the aggregate moisture, products of combustion (CO 2 , NO x , SO x ), CO and low volumes of organic compounds [112,115].
The energy involved in the production process of asphalt mixtures and, consequently, the greenhouse gas emissions (GHG), greatly depend on the moisture content of the aggregates at the moment they are introduced into the production flow.Thives and Ghisi [112] stated that a 2% reduction of aggregate moisture can represent a decrease of 8.7 kWh and 2.02 kg CO 2 per ton of asphalt mixture.Another study conducted in WMA [52] concluded that every 1% rise of the aggregate water content implies spending more 10% of fuel.This can be achieved just by protecting the aggregates' stockpiles from rainwater.Additionally, according to a preliminary study described in the literature [112,116], the use of a specific process involving solar aggregate stockpiles (stock conditions with an external thermal insulation shell) will allow preheating the aggregate and, hence, reducing its moisture content without energy consumption.
Since RAP includes aged bitumen, when HMA with RAP (typically up to 40%) is produced in a conventional batch plant, the process requires a higher spent of energy to heat the components in order to achieve suitable workability conditions [8].The literature [112] indicates more 25% of energy usage in plant and in compaction for HMA with 20% of RAP incorporation.The use of 40% of RAP in WMA has revealed a reduction of about 10% in energy consumption in comparison to conventional HMA without RAP [112].
In some territories the needed natural aggregates are not available and, therefore, it is necessary to transport large amounts of manufactured aggregates from distant quarries to the construction sites.In fact, average emission values of 0.185 kg CO 2 eq./ton.kmare mentioned in the literature for a heavy lorry [117] and, therefore, this transport circumstances easily increase the emissions associated with the production phase of asphalt mixtures.This kind of scenario is likely to increase attractiveness of using recycled aggregates available at shorter distances of the construction place, and if environmental policies consider some measures to penalise disposal in landfills or the use of non-renewable raw materials instead of recycled constituents.
According to the literature, the production and transport of recycled aggregates instead of virgin crushed rock, lead to considerable reduction of environmental impacts and energy consumption.Based on LCA results, [5], for instance, obtained roughly 49 to 51% reduction of in environmental impacts (human health, ecosystem quality, climate change and resources) if aggregates from CDW are produced instead of virgin aggregates.They also concluded that 185 MJ of non-renewable energy can be saved and a reduction on 14 kg CO 2 eq can be achieved.
Moreover, as calculated by Ferreira et al. [118] an environmental benefit of around 10% associated with the use of recycled aggregates can be achieved if slag is used instead of virgin aggregates.

Summary and Conclusions
Natural rocks are non-renewable raw materials used in large scale in asphalt mixtures.Moreover, the extraction of these natural materials and the following processing activities to manufacture and transport the aggregates resultant from natural rocks involve considerable energy consumption and GHG emissions.Also, because some territories have shortage of natural rocks, the necessary aggregates to be used in asphalt mixtures need to be transported from long distances, increasing the emissions associated to the use of natural aggregates.
In addition to the circumstances related to the natural aggregates, the industrial activity produces several by-products potentially suitable to substitute part of the aggregates as constituents of asphalt mixtures.These by-products are typically not reused and, therefore, most of the time they are disposed in landfills, without any added-value to the society and creating environmental impacts.Also, the available volume in landfills is running out in several countries.
The issues related to the manufacture of natural aggregates as well as the implementation of environmental policies to reduce the carbon footprint of the transport sector, have encouraged the attention the stakeholders pay to the possible use of recycled aggregates in asphalt mixtures.
Apart from the natural aggregates, which usually have different properties depending on the type of rocks used in their production, a few types of non-conventional aggregates, such as EAFS, RCA and RAP have been used more frequently in asphalt mixtures.The first recycled material is a by-product of the steel industry, while RCA and RAP are originated in the construction industry, being the RAP a by-product of the highways construction industry itself.There are several other by-products tested as substitutes of aggregates, such as glass, different types of plastic, ceramic from CDW, among others, but with a lower level of use.
Although mechanical performance of asphalt mixtures whose part of the aggregates are recycled may exhibit different tendencies, in general the performance is quite good and even better than the observed for comparable asphalt mixtures with natural aggregates.Nevertheless, it must be emphasized that the use of recycled aggregates is not always favourable for all the required mechanical properties of the asphalt mixtures.Also, the variability of the recycled aggregates' properties is higher and, therefore, this increases the level of uncertainty.Therefore, the incorporation of different types of recycled aggregates in asphalt mixtures requires carrying out previous mix-design studies to evaluate the expected mechanical behaviour of the final material.
In what concerns direct costs of the asphalt mixtures manufactured with recycled aggregates, taking the Portuguese reality as reference, the findings revealed some reduction of costs per year if the life span of the asphalt mixture is equal or greater than the life span of the comparable conventional asphalt mixtures.For instance, the reduction in direct cost can achieve 30.4% when 35% of RAP is incorporated and the life span achieved is 20% higher.This cost advantage is eliminated if the life span of the asphalt mixture with RAP is 20% lower.In this case, the direct cost per year increases, achieving 4.4% more than that of a comparable asphalt mixture with natural aggregates.
Most of the emissions and the consumption of energy are related to extraction and crushing of natural aggregates as well as the operations of drying and heating the aggregates to produce asphalt mixtures.Consequently, if these phases are somehow reduced or changed, the energy consumption and the related emissions can be considerably improved.The findings show that decreasing the level of incorporation of natural aggregates, substituting them by recycled aggregates, part of the extraction, crushing and transport impacts will be avoided.Moreover, the protection of the aggregates from rainwater and moisture in stockpiles is also a great contribution to reduce the energy (and emissions) necessary to dry and heat the aggregates before mixing them with the bitumen to produce asphalt mixtures.
In a whole, in the technical, economic and environmental standpoint it can be affirmed that the use of recycled aggregates as constituent of asphalt mixtures is feasible if the necessary evaluations are carried out.Despite the use phase of the transport infrastructure has a considerably higher environmental impact associated to the use of fossil fuels, the use of recycled aggregates is more a contribution to the goal of reducing the environmental footprint of the transportation sector.

Figure 2 .
Figure 2. Total production of HMA and WMA, availability and use of RAP in some European countries, as per the oldest [63] and most recent [64] known figures.

Figure 2 .
Figure 2. Total production of HMA and WMA, availability and use of RAP in some European countries, as per the oldest [63] and most recent [64] known figures.

Figure 3 .
Figure 3. Example of a grading curve of RAP (left) and its characteristics after bitumen extraction (right).

Figure 3 .
Figure 3. Example of a grading curve of RAP (left) and its characteristics after bitumen extraction (right).

Figure 4 .
Figure 4. Example of a top aggregates recycling installation, primarily suitable for RCA processing.

Figure 5 .
Figure 5. Example of a grading curve of RCA (left) and its characteristics (right).

Figure 4 .
Figure 4. Example of a top aggregates recycling installation, primarily suitable for RCA processing.

Figure 4 .
Figure 4. Example of a top aggregates recycling installation, primarily suitable for RCA processing.

Figure 5 .
Figure 5. Example of a grading curve of RCA (left) and its characteristics (right).

Figure 5 .
Figure 5. Example of a grading curve of RCA (left) and its characteristics (right).

Figure 6 .
Figure 6.Costs per tonne of asphalt mixture and costs per year of life.

Figure 7 .
Figure 7. Variation of annual direct costs in comparison with similar asphalt mixtures without recycled aggregates.

Table 3 .
Average properties of limestone, basalt and granodiorite aggregates in Portugal (Lisbon and surrounding regions).
1 South of Lisbon.2North of Lisbon.3East of Lisbon.

Table 5 .
[7,90] on mechanical performance of using RCA as partial substitute of the aggregates (adapted from[7,90]) 1Comparing with conventional HMA.2Comparing with similar WMA blends without RCA.

Table 5 .
[7,90] on mechanical performance of using RCA as partial substitute of the aggregates (adapted from[7,90]) 1Comparing with conventional HMA.2Comparing with similar WMA blends without RCA.

Table 5 .
[7,90] on mechanical performance of using RCA as partial substitute of the aggregates (adapted from[7,90]) 1Comparing with conventional HMA.2Comparing with similar WMA blends without RCA.
[74,77,91]xtures with RCA he cement mortar present in RCA around the coarser natural aggregates is porous.Moreover, articles of RCA have much more voids than coarse aggregates.As a consequence, RCA have ly high porosity and water absorption[77,91]as stated before.This has been reported as the reason to increase bitumen content in asphalt concrete (AC) to compensate the binder ption[77,91].Because RCA fractions have a considerable percentage of angular and rough ed particles, Marshall stability tend to increase, and Marshall flow tend to decrease[74,77,91].