Wood Properties Characterisation of Thermo-Hydro Mechanical Treated Plantation and Native Tasmanian Timber Species

: Thermo-hydro mechanical (THM) treatments and thermo-treatments are used to improve the properties of wood species and enhance their uses without the application of chemicals. This work investigates and compares the e ﬀ ects of THM treatments on three timber species from Tasmania, Australia; plantation ﬁbre-grown shining gum ( Eucalyptus nitens H. Deane and Maiden), plantation saw-log radiata pine ( Pinus radiata D. Don) and native-grown saw-log timber of the common name Tasmanian oak (which can be any of E. regnans F. Muell, E. obliqua L’H é r and E. delegatensis L’H é r). Thin lamellae were compressed by means of THM treatment from 8 mm to a target ﬁnal thickness of 5 mm to investigate the suitability for using THM-treated lamellas in engineered wood products. The springback, mass loss, set-recovery after soaking, dimensional changes, mechanical properties, and Brinell hardness were used to evaluate the e ﬀ ects of the treatment on the properties of the species. The results show a marked increase in density for all three species, with the largest increase presented by E. nitens ( + 53%) and the smallest by Tasmanian oak ( + 41%). E. nitens displayed improvements both in sti ﬀ ness and strength, while sti ﬀ ness decreased in P. radiata samples and strength in Tasmanian oak samples. E. nitens also displayed the largest improvement in hardness ( + 94%) with respect to untreated samples. P. radiata presented the largest springback whilst having the least mass loss. E. nitens and Tasmanian oak showed similar dimensional changes, whilst P. radiata timber had the largest thickness swelling and set-recovery due to the high water absorption (99%). This study reported the e ﬀ ects of THM treatments in less-known and commercially important timber species, demonstrating that the wood properties of a ﬁbre-grown timber can be improved through the treatments, potentially increasing the utilisation of E. nitens for structural and higher quality timber applications. wood products such as laminated ﬂoors require high-dimensional stability and elevated structural properties, and our study found that E. nitens THM-treated samples had higher performance than pine after the soaking and drying cycle, as well as presenting increases in all the tested mechanical properties, showing that the treatment was most e ﬀ ective for this species. This study demonstrated the e ﬀ ectiveness of THM treatments in increasing the density of plantation-grown timbers ( E. nitens and P. radiata ) and native eucalypt timbers, as well as a ﬀ ecting their mechanical properties. Appreciable di ﬀ erences between the species were shown and the application of the treatment on ﬁbre-grown E. nitens wood showed promising results in wood properties. This ﬁnding might direct further investigations in the suitability of densiﬁcation of low-density ﬁbre-grown E. nitens for the production of engineered structural products. Future investigation might focus on examining di ﬀ erent degrees of densiﬁcation and initial di ﬀ erent preheating treatments, especially for the denser native timbers forming the Tasmanian oak samples. This initial study demonstrated the applicability of THM treatments on Australian timbers with satisfactory ﬁnal results, which might be transferred for potential industrial processes and engineered timber applications.


Introduction
Increasing demand for wood and wood-based products for construction is stimulating the use of fast-grown species to supplement and replace the more classical use of native forest species [1]. The area of planted forests has considerably increased in recent years, with plantations covering approximately 291 million ha in 2015 [2], allowing increased availability of fast-grown timbers to supply market demand. The species most commonly found in plantations are pines and eucalypts, covering 42% and 26% of the global planted areas, respectively [3]. In Tasmania, the most commonly planted species are shining gum (Eucalyptus nitens H. Deane and Maiden), native to Australia, and radiata pine (Pinus radiata D. Don), native to California, but extensively planted in temperate areas of Australia. Planted eucalypt species, which are grown for short rotations mainly to produce fibre for the pulp and paper sector, present lower density and different wood properties than their native counterparts-characteristics that might hinder their full deployment as structural products or engineered wood products (EWP) [4]. Concerns regarding important mechanical properties such as strength, hardness, dimensional stability, and durability of timbers have encouraged the adoption of wood modification treatments and processes [5][6][7][8]. Ecologically sustainable wood treatment options, avoiding the use of chemicals to preserve the timber, can benefit from the combined effects of temperature, moisture, and pressure to compress the timber and improve its properties and stability [9]. These thermo-hydro mechanical (THM) treatments evolved from the combination of heat treatments and densification of wood through compression [10]. Densification treatments have been a focus for decades as wood density is considered one of the most important properties for structural timber and EWP. High-density species are sought for construction purposes and treatments that contribute to its enhancement are favored.
There are several advantages of the use of THM treatments as wood treatment processes. For example, resistance to decay is improved by application of high temperatures [11], which has been largely employed for thermally treated wood [12,13]. The treated wood presents enhanced hygroscopicity due to the degradation of hemicellulose; a process that reduces the water absorption of wood [14] where effects are species-dependent according to the chemical composition of the timber [15]. However, mechanical properties tend to be reduced under heat treatments alone [16]. The addition of wood compression is an excellent combination to preserve and enhance important structural properties; the use of steaming and heating reduces the set-recovery of the modified timber, a phenomenon that occurs when timber is re-exposed to moisture and tends to recover the deformation created during the compression treatment. Hence, through reduction of the shape recovery of the treated wood, the effects of densification are stabilised [17][18][19]. The superior mechanical properties and increased durability are desirable for applications such as engineered wood floorings [20] and have generated interest for industrialisation of THM-treated material and improved processing options [21,22].
The modification of timber species originating from plantations has received considerable interest in Europe for species such as poplar [19,23,24], softwoods [25,26], and some eucalypt species [15,27,28]. Given the major representation of E. nitens and P. radiata in timber plantations, an understanding of the consequences of THM treatments on these species is warranted. To our knowledge, little to no research has examined the use of THM treatments to densify fibre-grown E. nitens, nor have the effects of the treatments been studied in comparison to other species such as P. radiata, or native-grown eucalypts. Given the positive effects of TMH treatments on other fast-grown species, there is much interest in understanding their suitability to modify eucalypt and pine plantation timbers. Such information would support the exploration of densification to enhance the properties of those fast-grown species, providing opportunities to increase their use in structural products.
The aim of this study was to investigate the effects of wood modification treatments (THM treatment and THM and preheating treatment) on timbers from the two plantation species (E. nitens and P. radiata), grown under different regimes, and on a mixture of native forest-grown eucalypt species commercially known as Tasmanian oak. We were interested in understanding the changes in density and mechanical properties due to the wood modification treatments on the fast-grown, short-rotation plantation hardwood, on the planted softwood, and on the slow-grown, long-rotation native hardwood, and in comparing the effects of the treatments across the wood types. The objectives of the study were to (i) quantify the change in basic density and mechanical properties (stiffness, strength, and Brinell hardness) within each species due to the treatments, (ii) compare that change across the species, and (iii) examine and compare across species the characteristics of the wood species after the treatments in terms of compression degree, immediate springback, mass loss, set-recovery after soaking, dimensional changes, mechanical properties, and Brinell hardness. Finally, (iv) we were interested in exploring the correlation between the mechanical properties and final density for each wood species. The characterisation of the treated timbers will inform the feasibility of using fast-grown plantation species as a substrate for high-quality engineered wooden floorings of other EWP.

Material
The wood material used in the study were kiln-dried and planed lamellae of three Australian commercially important species: plantation fibre-grown shining gum (Eucalyptus nitens H. Deane and Maiden) managed for fibre production, plantation-grown radiata pine (Pinus radiata D. Don) managed for saw-log production, and native-grown hardwood timber of the commercial brand Tasmanian oak (which comprises wood from any of three closely related native eucalypt species: E. regnans F. Muell, E. obliqua L'Hér, and E. delegatensis L'Hér). We chose samples harvested and milled according to conventional practices that represent timber commercially grown for production of structural products. Forty samples per species were used, of which ten per species were used as control samples. The samples were a mixture between quartersawn and transitional/backsawn cuts, with growth-ring orientation ranging from perpendicular to parallel to the wide face of the lamella. The samples were kept in a conditioning chamber at relative humidity (RH) 65% and 20 • C before transportation to the laboratory.

Thermo-Hydro Mechanical (THM) Treatment and Preheating Treatment
The THM treatments and the tests were carried out at the InnoRenew CoE laboratories in Izola and Koper, Slovenia. Thirty 325 mm (L) × 45 mm (T) × 8 mm (R) samples per species were densified under THM treatment in an open-system process using a hydraulic, 30-ton capacity Langzauner "Perfect" LZT-UK-30-L model hot press (Langzauner Gesellschaft m.b.H., Lambrechten, Austria) equipped with a water-cooling system. The press plates were preheated to 170 • C, samples were inserted between the two plates and enclosed for a cycle of 30 min, during which a mechanical pressure of 300 kN was applied in the press. At reaching target thickness, the specimen was held at 170 • C for three min and the temperature was increased to 200 • C. When the temperature of 200 • C was reached, the plates were cooled under compression to 60 • C before opening the press. For the Tasmanian oak samples, a preheating treatment at 100 • C for 30 min was applied before the THM treatment to reduce the moisture content of samples to avoid bursting the samples during the THM treatment.

Physical Tests
The thickness of the samples was measured before treatment and again immediately after. Samples were compressed to the target thickness of 5 mm, and the compression ratio (CR), also known as target densification ratio, was calculated expressing the percentage of the target decrease in thickness compared to the initial thickness of the samples (Equation (1)): where T o is the original thickness (mm) and T t is the target compressed thickness (mm).
The actual densification was evaluated with the final achieved thickness T c , which calculates the actual densification ratio (DR) on the entire densified lamellae, expressing the percentage decrease in thickness compared to the initial thickness of the samples (Equation (2)): The difference between compression ratio and actual densification ratio is due to the springback of the samples at the opening of the press, which measures the immediate recovery of thickness in the samples due to the phenomenon of shape memory effect of wood (Equation (3)): The compression degree (CD) (Equation (4)) to which the samples were densified measures the deformation caused by the treatment and serves as a measure of the increase in the density of the samples: The mass loss (ML) was calculated (Equation (5)) to account for the variation in sample mass due to the treatment: where M o is the sample dry mass (g) of the conditioned samples (entire lamellae) before the treatment, and M c is the sample dry mass (g) measured after the treatment. The M o of Tasmanian oak samples was determined before the preheating treatment, as the samples were placed immediately into the press after the preheating, to avoid intake of moisture from the environment. Basic density and moisture content (MC) were measured following the oven-dry method according to AS 1080.1 and AS 1080.3 [29,30]. Measurements were made on a 25 × 45 mm strip (Section A, Figure 1) cut from the sample prior to the treatment and from a second 25 × 45 mm strip (Section B, Figure 1) cut from the sample after the treatment. From the same end, another 25 × 45 mm strip (Section D, Figure 1) was cut to perform the set-recovery and water absorption tests. The compression set-recovery (SR) determines the irreversible recovery in thickness of the THM-treated samples after soaking in water. Samples were first dried to 0% moisture content, then soaked for 24 h in water at 20 • C and then oven-dried at 103 • C for 24 h following the procedure described in Laine et al. (2013) [31]. Dimensions and weights of the samples were recorded after soaking and at oven-dried conditions. SR was calculated using Equation (6): where T r is the oven-dried thickness (mm) after soaking. Water absorption (WA) was calculated using Equation (7): where w 1 is the weight (g) after soaking for 24 h and w e is the oven-dried weight (g) before immersion in water. The change in dimensions was accounted through the measurement of thickness swelling (TS), according to Equation (8): where T s is the thickness (mm) of the saturated sample after soaking.

Mechanical Tests
Stiffness of the control and THM-treated samples was measured through Young's modulus in compression (MoE-modulus of elasticity) and strength through modulus of rupture (MoR), which were tested under a three-point bending arrangement. From the conditioned samples, a 150 × 15 mm strip was cut (Section C, Figure 1) and loaded in the Zwick (10 kN) universal testing machine (ZwickRoell, Germany) with the application of a load at a displacement rate of 7 mm/min. Tests were performed according to DIN 52-192 1979 [32] on a loading span of 85 mm. MoE and MoR were obtained through the recorded strain-stress curves provided by the precalibrated Zwick software. Two E. nitens and three Tasmanian oak samples were damaged during the treatment; hence the final sample size for the mechanical tests of stiffness and strength on these timbers was lower than initially planned. MoE and MoR were tested on control samples under a similar arrangement, on a loading span of 128 mm.
Brinell hardness (HB) was measured on 45 × 50 mm control and treated samples (Section E, Figure 1) adapting EN 1534:2000 [33] and following the methodology developed by Rautkari et al. (2011) [24]. The test was performed keeping the indentation depth constant, given the low thickness of the samples, and the applied force was recorded. The test was performed with the Zwick universal testing machine using a steel sphere 11.28 mm in diameter and HB (N/mm 2 ) was calculated using Equation (9): where F is the force (N) exerted into the samples, D is the radius (mm) of the indenter, and h is the depth (mm) of the indentation.

Statistical Analysis
Statistical analyses were performed with the RStudio software (RStudio Team 2016). The normality and homogeneity of variance in the data were verified with Shapiro-Wilk and Levene's tests, respectively. Datasets were inspected for outliers using the Tukey's fences method [34], as well as visual inspection of plots and outliers that could significantly bias the testing. Four samples of Tasmanian oak that presented exceptionally high basic density values prior to the treatment were removed from the dataset.
Two-way mixed measures analysis of variance (ANOVA) was used to compare the means of the basic density of the three species, using species and treatment as factor variables. Two-way analysis of variance (ANOVA) was used to compare the means of the mechanical properties (MoE, MoR, and HB) of the three species on control and treated samples. To identify differences between species, multiple pairwise comparisons were used as post hoc tests.
The differences across species in the properties after the treatment (CD, springback, ML, TS, WA, set-recovery) were evaluated with the Kruskal-Wallis test and the paired-samples Wilcoxon test, as the assumption of normality or homoscedasticity were not met for any of these variables.
Linear regression was used to model the relationships between structural properties (MoE and MoR) with the densities of THM-treated samples. All test results were compared with a significance threshold set at 0.01.

Densification of the Material
Initial densities were 0.52 g/cm 3 for E. nitens, 0.46 g/cm 3 for P. radiata, and 0.61 g/cm 3 for Tasmanian oak. The initial density before the treatment was significantly different between the three species (F(2,82) = 22.6, p < 0.01). While the THM treatment significantly increased the density in all three species (Table 1, Figure 2) (F(1,82) = 1143.1, p < 0.01), species response was different, showing a significant effect of treatment on the species (F(1,82) = 11.3, p < 0.01). E. nitens samples had the larger percentage increase in density (53%), compared to both the P. radiata and Tasmanian oak samples (respectively, 43% and 42%), and its final density of 0.80 g/cm 3 was not significantly different to that of the Tasmanian oak samples (p = 0.57), which reached 0.89 g/cm 3 on average. The density of P. radiata samples after the treatment was 0.66 g/cm 3 on average, significantly lower than both E. nitens and Tasmanian oak (p < 0.01). a, b, c letters denote significant differences within the group of species before the treatment; d and e denote significant differences within the group of species after the treatment. The asterisk indicates significant differences between the density prior to the treatment and the density after, per each species considered. All significant levels had p < 0.01. After the THM treatment, the basic density of E. nitens was close to that of the native Tasmanian oak samples and surpassed the density of the other plantation species, P. radiata. These results suggest selection of timber for densification might be better based on the species, rather than on the initial density, which is usually low for fast-grown species. It is worth noting that the variance in density after the treatment of Tasmanian oak samples was higher than both that of E. nitens and P. radiata, suggesting that the response of the slow-growing species to densification was less consistent than that for the two plantation species.
The target thickness was 5 mm for all the samples, hence the target densification ratios (CR) were 38.8% for E. nitens and 37.3% both for P. radiata and Tasmanian oak. The thickness was measured on the conditioned samples prior to the treatment and immediately after. The compressed thicknesses for the three species were on average 4.86, 5.29, and 5.37 mm for E. nitens, P. radiata, and Tasmanian oak, respectively, indicating final densification ratios of 40.5%, 33.8%, and 36.2%, as presented in Table 1.

Mechanical Properties
The mechanical properties of the samples are summarised in Table 2. MoE of the control samples were 13.41 GPa for E. nitens, 11.67 GPa for P. radiata samples, and 17.08 GPa for Tasmanian oak samples, significantly different among the wood of Tasmanian oak and the other two species (p < 0.01) but not significantly different among the wood of E. nitens and P. radiata samples (p = 0.018). After the treatments, MoE of the lamellae was significantly different among all three wood types (F(2,82) = 25.2, p < 0.01). The THM treatment significantly increased the MoE only of E. nitens samples (p < 0.01), which reached an average of 17 GPa after the treatment; conversely the MoE of P. radiata THM-treated samples was on average lower than that of control samples, indicating that this property was not improved due to the process. Tasmanian oak samples showed the largest improvement, from 17 GPa to almost 23 GPa on average, although the two values were not significantly different (p = 0.73).   MoR of control samples was also significantly different among the wood of Tasmanian oak and the other two species (p < 0.01) but not significantly different among the wood of E. nitens and P. radiata samples (p = 0.068). After the treatments, MoR was not significantly different among the three wood types (p = 1). E. nitens showed an increase in MoR, albeit not significant (p = 0.29), while for P. radiata there was a significant increase of this property (p < 0.05), reaching almost 140 MPa on average in THM-treated samples. MoR of THM-treated Tasmanian oak samples was lower than that of control samples, showing a reduction in strength after the treatment, results which might have been conducted by the preheating treatment on these wood samples. Similar results were obtained on P. elliotti and E. grandis by Pertuzzati et al. [15], with only slight increases in MoE for the pine and MoR for the eucalypt species. In other thermal modification studies, eucalypt species have shown either slight increases in their mechanical properties, as for E. nitens [35], or decreases, as for E. grandis and E. saligna [36] and E. globulus [37]. During wood treatment, the thermal degradation of the chemical components of wood cells can offset the improvement of mechanical properties [38,39], rendering the wood structure more fragile. During the mechanical test, failure of THM-treated samples occurred suddenly, indicating an increased brittleness of the wood, while control samples under loading deformed constantly before breakage occurred.
The modified Brinell hardness method was necessary to evaluate thin lamellae, as it has been noted before how the hardness values depend upon the force applied during the test and on the standard adopted [24]. The same method was used on control and THM-treated samples. The Brinell hardness was not significantly different among wood types either before or after the wood treatments. A significant increase in hardness was found for all three species (p < 0.01), with the largest increase displayed by E. nitens, reaching 23.22 N/mm 2 on average, an increase of almost 94% compared to control samples. The lowest increase was displayed on P. radiata THM-treated samples, reaching 18.39 N/mm 2 on average, while Tasmanian oak reached 21.18 N/mm 2 , albeit showing the largest hardness values on control samples. Similar values of Brinell hardness were found in Wentzel et al. [28] for E. nitens samples grown in Spain, although the method employed for the test was different than the one used in the present study. Hardness is known to improve through densification, as it is influenced especially by the density of the surface layer [40,41]. In this work, the hardness of all three species was positively correlated with their basic densities after the THM treatment, although being only significant for Tasmanian oak samples (p < 0.01, R 2 = 0.56, data not shown).
Bending properties of the three species studied and their densities after the THM treatment are shown in Figure 3a (MoE) and Figure 3b (MoR). The correlations between MoE, MoR, and post-THM density were positive and significant for all three species (Table 3). Regression models developed to predict final MoE and MoR considering initial densities are also shown. The increase in density also led to an increase in the MoE and MoR of the samples, and we hypothesise that the differences in the increase are due to the anatomical structure of the wood and the orientation of the wood samples.

Compression Degree, Springback, and Mass Loss
In this study, higher compression degrees (CD) were achieved with the two eucalypt species, as also illustrated in Gong and Lamason [42] and Pertuzzati et al. [15]. The largest compression degree was for E. nitens samples, which compressed to 68.2% of their thickness, followed by Tasmanian oak and P. radiata samples, with 58.3% and 52.1%, respectively (Table 4). There was significant variation in compression degree among species (χ2(2) = 42.31, p < 0.01), while CD was statistically significant between E. nitens and both P. radiata and Tasmanian oak (p < 0.01), but no significant difference was detected between CD of P. radiata and Tasmanian oak (p = 0.03). These results were influenced by the final thickness of the samples, which for E. nitens was less than the target thickness controlled by the mechanical stops; an outcome most likely influenced by the shrinkage of the samples under the high temperatures applied during the treatments. This additional shrinkage would have to be investigated further with a different target densification ratio. * Letters denote significant differences in the measurements within the group of species after the treatment. All significant levels had p < 0.01.
The differences between the target and the actual densification ratio are due to the immediate springback occurring at the opening of the press, due to the stresses built up during the THM treatment. The shrinkage of the E. nitens samples led to a negative value on the calculated springback (−4.52%), while different values were found on P. radiata (9.57%) and Tasmanian oak samples (2.49%). The results for P. radiata and Tasmanian oak samples are in agreement with those found in previous studies [43,44] where higher CRs lead to a greater springback. Earlywood and latewood compress differently, and different amounts of latewood present in the native slow-grown Tasmanian oak samples in comparison to the plantation-grown P. radiata samples might have impacted their rate of compression and the structural changes of the timber. This would lead to further considerations in the treatment of plantation timbers.
The springback was significantly different among the three species (χ2(2) = 36.87, p < 0.01), while being statistically significant only for E. nitens and P. radiata (p < 0.01), finding most likely due to the negative values of the springback in the E. nitens compared to the large springback in the P. radiata samples.
The P. radiata samples had the lowest compression degree and densification ratio but achieved the highest springback (Table 4). From the investigation of the densification ratio it appeared that the samples of this species had densified at different rates, an effect that might be due to the differences in initial densities of the samples. Furthermore, differences in springback of the samples are related to the amount of latewood present, as P. radiata is known to have significant differences in early and latewood density [45]. Detailed analysis was not made; however, it was noticed that samples with higher percentages of latewood undergo higher springback.
The mass loss on the entire lamellae was significantly different among the samples (χ2(2) = 25.81, p < 0.01). E. nitens samples had significantly lower mass loss than the other two species (p < 0.01), with an average of 2.42%, in comparison to P. radiata (3.6%) and Tasmanian oak (4.13%) ( Table 4). The larger mass loss on Tasmanian oak samples is in line with previous research, in which it was found that eucalypt species (Eucalyptus grandis and Eucalyptus globulus) had larger mass losses in comparison to pine species (Pinus elliottii and Pinus pinaster) [15,46]. Moreover, the higher mass loss of the Tasmanian oak samples might be related to the preheating treatment applied on the wood, which had affected the moisture content of the samples. This should be considered for the development of future treatment protocols for this species.
The variable level of mass loss in the samples might be explained by the differences in chemical composition of the wood, in which the substrates degrade in different ways; hemicellulose tends to be more subjected to degradation rather than lignin [47]. During densification, water vaporisation contributes to the mass loss, which is followed usually at higher temperatures by the degradation of extractives, hemicellulose, and at the latest stages, lignin [48]. Eucalypt wood has less cellulose and lignin, and more hemicellulose than pine wood, which is also more susceptible to thermal degradation due to the higher presence of xylans [49]. Moreover, there are differences in the amount of extractives that may have impacted the response of the species to the densification treatment. Growth rate and extractive concentrations are negatively correlated [50] and previous investigations have shown how younger eucalypt trees presented higher extractive contents than older ones [51]-findings that support the hypothesis of a different amount of extractives in the planted E. nitens with respect to the slower-grown native Tasmanian oak samples.

Dimensional Changes
The absorption of water during the soaking treatment caused a dimensional change in the samples. The dimensional change and shape recovery after soaking and drying were significantly different among the three species studied (χ2(2) = 50.27, p < 0.01) (Figure 4). While the two eucalypt species had similar amounts of swelling in thickness (almost 30% for E. nitens and 24% for Tasmanian oak samples), pine samples exhibited significantly larger thickness swelling (p < 0.01), reaching more than 50%. The final thickness after soaking and drying of pine samples was 22% higher than that of the eucalypts.
The major swelling of pine samples was due to their high rate of water absorption (99.2%), which was significantly different (p < 0.01) compared to the other two timbers (Table 5), relating to previous findings on the same species where similar rates of water absorption were found [25]. Samples of E. nitens and Tasmanian oak had moderate water absorption rates of 53.4% and 45.2%, respectively. In our study, the water absorption rate of P. radiata samples was extremely high for samples that achieved a densification ratio over 35%, suggesting that more compression (hence large densification) would induce a greater swelling ratio and water absorption volume for this species.
Set-recovery values were different among species (χ2(2) = 55, p < 0.01), while being significant only for the pine (p < 0.01; Table 5). No samples achieved a full recovery, indicating that some of the structural changes induced by the THM treatment were permanent. The treatment combination of pressure, high temperature, and increased moisture is known to ameliorate the build-up of internal stresses that are the principal cause of the springback and set-recovery of the samples. This was confirmed in our study, also highlighting the differences in the recovery among eucalypt and pine species.

Conclusions
In this study, samples of fibre-grown E. nitens, saw-log managed P. radiata, and native eucalypt species from Tasmania were treated under short-period thermo-hydro mechanical treatment and densified to a final thickness of 5 mm. The treatments successfully increased the basic density in all three species, with the major increment present on E. nitens samples (53%). The initial density of E. nitens prior to the THM treatment was significantly lower than that for Tasmanian oak. After the treatment there was no significant difference between the two species. Furthermore, the final density of the two eucalypt species was significantly higher than that of pine samples. This highlights the potential use of THM-treated fibre-grown E. nitens as a substitute for native eucalypt species (e.g., Tasmanian oak) in applications requiring high density materials, such as laminated floors. This is further enhanced by the higher availability and faster growth rate of E. nitens compared to native eucalypt species [1]. The relatively lower density of the THM-treated pine samples makes this alternative less suitable to applications requiring high density materials when compared to the other two eucalypt species.
The mechanical properties of stiffness and strength had different responses to the treatments, with an increase in stiffness only for the eucalypt timbers (E. nitens and Tasmanian oak samples) and a slight decrease for the P. radiata samples. There was no significant difference in the strength of THM-treated E. nitens and treated Tasmanian oak, which highlights the possibility of treating and deploying E. nitens timber for structural applications requiring stiff material. Additional testing will be required to further explore these opportunities. Strength was reduced after treatment only on Tasmanian oak samples. This will require further investigation as the current study highlights a possible impact due to the necessary preheating of this timber to avoid the bursting of the wood. The adapted Brinell hardness test revealed an improvement in hardness for all three wood types, with higher values for the eucalypt species compared to pine, and E. nitens obtaining the highest increment in hardness (+94%). For flooring applications, hardness is of large importance, and the high values obtained for the E. nitens samples support their suitability in such applications. Engineered wood products such as laminated floors require high-dimensional stability and elevated structural properties, and our study found that E. nitens THM-treated samples had higher performance than pine after the soaking and drying cycle, as well as presenting increases in all the tested mechanical properties, showing that the treatment was most effective for this species.
This study demonstrated the effectiveness of THM treatments in increasing the density of plantation-grown timbers (E. nitens and P. radiata) and native eucalypt timbers, as well as affecting their mechanical properties. Appreciable differences between the species were shown and the application of the treatment on fibre-grown E. nitens wood showed promising results in wood properties. This finding might direct further investigations in the suitability of densification of low-density fibre-grown E. nitens for the production of engineered structural products. Future investigation might focus on examining different degrees of densification and initial different preheating treatments, especially for the denser native timbers forming the Tasmanian oak samples. This initial study demonstrated the applicability of THM treatments on Australian timbers with satisfactory final results, which might be transferred for potential industrial processes and engineered timber applications.