Recovery of Metal Ions (Cd2+, Co2+, and Ni2+) from Nitrate and Sulfate on Laser-Induced Graphene Film Using Applied Voltage and Its Application

The urgent removal of Cd, Co, and Ni from nitrate and sulfate is essential to mitigate the potential risk of chemical pollution from large volumes of industrial wastewater. In this study, these metal ions were rapidly recovered through applying voltage on nitrate and sulfate, utilizing laser-induced graphene/polyimide (LIG/PI) film as the electrode. Following the application of external voltage, both the pH value and conductivity of the solution undergo changes. Compared to Co2+ and Ni2+, Cd2+ exhibits a lower standard electrode potential and stronger reducibility. Consequently, in both nitrate and sulfate solutions, the reaction sequence follows the order of Cd2+ > Co2+ > Ni2+, with the corresponding electrode adsorption quantities in the order of Cd2+ > Co2+ ~ Ni2+. Additionally, using the recovered Co(OH)2 as the raw material, a LiCoO2 composite was prepared. The assembled battery with this composite exhibited a specific capacity of 122.8 mAh g−1, meeting practical application requirements. This research has significance for fostering green development.


Introduction
Large amounts of residual metal ions remain in industrial wastewater.Once metal ions contaminate water or soil, they pollute the environment and affect people's health [1].Therefore, an efficient and environmentally friendly disposal method for treating polluted waterbodies is an urgent issue.
Researchers have employed various methods to recover valuable metal ions from waste batteries, including leaching, chemical reduction, metallurgy, and other techniques [2][3][4][5].Meshram et al. [6] reviewed the recovery of metals using various acids, which unfortunately led to secondary pollution caused by the chemical agents.In recent decades, electrosorption or capacitive deionization (CDI), which rapidly pushes the migration of ionics using electrical force, has been widely utilized for the recovery of metal ions in wastewater due to its low cost, ease of control, and absence of secondary pollution from the chemical agents [7][8][9].The adsorption electrode serves as the central component of the electric deionization device, playing a pivotal role in determining the device's adsorption capacity [8,10].Electrode materials featuring a carbon network structure have been extensively researched due to their high specific surface area, well-balanced pore size distribution, exceptional electrical conductivity, and favorable adsorption properties [9,[11][12][13].Li et al. [14] reported on the removal of Ni 2+ ions using an α-MnO 2 /carbon fiber paper composite, which exhibited pseudocapacitor properties, facilitating electron/charge transfer.Xue et al. developed a nitric acid-modified activated carbon electrode for the removal of Co 2+ , Mn 2+ , and Ni 2+ ions [15].Coconut-shell activated carbon, activated by CO 2 , served as the electrode, demonstrating a Ni removal capacity of 5.32 mg g −1 [16].This implies that modifying carbon materials with various functional groups can effectively be used to adsorb metal ions.
Laser-induced graphene (LIG), as an easily obtainable carbon material, has been utilized across various fields due to its high thermal stability, excellent conductivity, rich 3D porous network, and abundant functional groups [17].In our previous research, employing LIG as an electrode material exhibited outstanding capability in recovering rare earth ions [18].Li et al. reported that a Co 4 S 3 − modified LIG electrode exhibited a high adsorption capacity of 2702.79 mg g −1 for UO 2 2+ [19], indicating its potential as an absorbent electrode.
To our knowledge, the use of LIG films as electrodes for recovering Cd 2+ , Co 2+ , and Ni 2+ ions has not been reported previously.Therefore, the recovery of Cd 2+ , Co 2+ , and Ni 2+ ions in nitrate and sulfate forms was investigated in this work.The standard potential of Cd (E θ = −0.403V vs. SHE) is lower than that of Co (E θ = −0.277V vs. SHE) and Ni (E θ = −0.257V vs. SHE), indicating the easy recovery of cadmium ions under identical solution concentrations.Due to the superior oxidation capabilities of nitrate ions, the ions recovered from nitrate solutions are mainly hydroxides, whereas the products recovered from sulphate solutions are metals.Furthermore, the cobalt hydroxide recovered could serve as a raw material for the preparation of lithium-ion electrode materials.This has significance for fostering green development.

Materials and Characteristics
Co(NO 3 ) 2 , Ni(NO 3 ) 2 , Cd(NO 3 ) 2 , CoSO 4 , NiSO 4 , and CdSO 4 were procured from Sinopharm Group Chemical Reagent Co., Ltd, Shanghai, China.A 100 µm polyimide (PI) film was supplied by Texiang Electrical Insulation Material Company, PRC, Tianjin.Ethanol was purchased from Chongqing Colon Chemical Co., Ltd., Chongqing, China.Deionized water specifically prepared for laboratory use was employed.The aforementioned chemicals are of analytical purity and were used without any further treatment.
The structure and morphology of the product were characterized using X-ray diffractometry (XRD, SmartLab, Shanghai, China) and field-emission scanning electron microscopy (FESEM, Hitachi S-4800, Tokyo, Japan).The bonds in the sample were analyzed using Fourier-transform infrared spectroscopy (FTIR, Thermo Scientific, Suzhou, China) and X-ray photoelectron spectroscopy (XPS, Thermo Fisher Scientific Escalab QXi, Waltham, America).The pH of the solution was determined using a PHS-3C pH acidity meter.The concentration of ions in solution during the application of external voltage was measured using atomic absorption spectrometry (AAS, TAS-990 SUPER, Weizhou, China).The electrochemical performance of the electrode was carried out using VMP3 multi-channel electrochemical impedance system.

Preparation of LIG/PI Film Electrodes via Laser Scribing
Firstly, commercial PI films were cleaned with ethanol and deionized water.Subsequently, a 100 µm thick PI film was affixed to a glass plate, and a CO 2 laser with a wavelength of 10.6 µm was utilized to carve the PI film, resulting in the production of an LIG/PI film electrode.The scanning speed and scanning power of the laser engraving machine were 100 mm/s and 6.6 W, respectively.Finally, an LIG/PI thin film electrode with a size of 2.5 × 1 cm 2 was obtained.Figure 1a shows the preparation process of the LIG/PI thin film electrode.
to the reference electrode, the ions were recovered.The formulas for calculating sorption capacity (Q) and removal rate (W) are provided in detail in the Supplem Materials.

Application of Recovered Co(OH)2
LiCoO2 was prepared using the sol-gel method.First, the recovered Co(OH)2 ric acid in a stoichiometric ratio of 1:2 were dissolved in 50 mL distilled water; th mixture was heated in an oil bath for 1 h at 80 °C with stirring.A certain amount o was added; meanwhile, an ammonia solution was used to adjust the pH of soluti mixture was dried at 120 °C to evaporate the water.Finally, it was annealed at 80 8 h to obtain LiCoO2.

Change in pH and Conductivity after Applying the External Potential
Figure 2 illustrates the changes in pH and conductivity following the applic an external potential to a 0.02 M solution of Cd(NO3)2, Co(NO3)2, and Ni(NO3)2 applying a potential of −1.2 V (vs.Ag/AgCl) to a 0.02 M solution of Cd(NO3)2, a white product was obtained (inset of Figure 2a).In the Co(NO3)2 solution, both product and a light blue product were obtained (inset of Figure 2b).And a green p was observed in the Ni(NO3)2 solution (inset of Figure 2c).Correspondingly, the creased from ~6.0 to ~2.5, and the conductivity increased from ~2.0 to ~2.9 in the tions.After the potential became −1.5 V, different color products were obtained, as in the inset of Figure S1.This illustrated a difference in the composition of pr Herein, a more obvious change in the pH and conductivity was detected.A higher voltage implies a strong electric driving force, which effectively influences the mo Co 2+ , Ni 2+ , and Cd 2+ ions.
When applying a potential of −1.2 V to the sulfate solutions (Figure 2d-f), th tion in the pH and conductivity was notably significant in the CdSO4 solution (ΔpH Δσ = 3.97 mS cm −1 ).However, it was relatively small in CoSO4 (ΔpH = 3.04, Δσ = cm −1 ) and NiSO4(ΔpH = 2.43, Δσ = 0.47 mS cm −1 ).Changing the potential to −1.5 V S1d-f) resulted in a dramatic change in pH (ΔpH = 4) and conductivity (Δσ = 8 m observed in the CdSO4 solution.It was smallest in the NiSO4 solution (ΔpH = 3, Δσ cm −1 ).These results illustrate that the reaction kinetics in sulfate and nitrate are d The reaction ability in this solution follows the order of Cd 2+ > Co 2+ > Ni 2+ unde conditions, disregarding the effect of anions.In this experiment, a traditional three-electrode system (Figure 1b) was employed to the simulated solutions containing 0.005-0.02M Co 2+ , Ni 2+ , and Cd 2+ .The LIG/PI film served as the working electrode, while a Pt electrode was utilized as the counter electrode.An Ag-AgCl electrode was employed as the reference electrode.Upon applying a voltage to the reference electrode, the ions were recovered.The formulas for calculating the adsorption capacity (Q) and removal rate (W) are provided in detail in the Supplementary Materials.

Application of Recovered Co(OH) 2
LiCoO 2 was prepared using the sol-gel method.First, the recovered Co(OH) 2 and citric acid in a stoichiometric ratio of 1:2 were dissolved in 50 mL distilled water; then, the mixture was heated in an oil bath for 1 h at 80 • C with stirring.A certain amount of LiOH was added; meanwhile, an ammonia solution was used to adjust the pH of solution.The mixture was dried at 120 • C to evaporate the water.Finally, it was annealed at 800 • C for 8 h to obtain LiCoO 2 .

Change in pH and Conductivity after Applying the External Potential
Figure 2 illustrates the changes in pH and conductivity following the application of an external potential to a 0.02 M solution of Cd(NO 3 ) 2 , Co(NO 3 ) 2 , and Ni(NO 3 ) 2 .When applying a potential of −1.2 V (vs.Ag/AgCl) to a 0.02 M solution of Cd(NO 3 ) 2 , a silverwhite product was obtained (inset of Figure 2a).In the Co(NO 3 ) 2 solution, both a gray product and a light blue product were obtained (inset of Figure 2b).And a green product was observed in the Ni(NO 3 ) 2 solution (inset of Figure 2c).Correspondingly, the pH decreased from ~6.0 to ~2.5, and the conductivity increased from ~2.0 to ~2.9 in these solutions.After the potential became −1.5 V, different color products were obtained, as shown in the inset of Figure S1.This illustrated a difference in the composition of products.Herein, a more obvious change in the pH and conductivity was detected.A higher applied voltage implies a strong electric driving force, which effectively influences the mobility of Co 2+ , Ni 2+ , and Cd 2+ ions.

Analysis of the Adsorption Product
The product compositions obtained on electrode surfaces after application of −1.2 V voltage in nitrate and sulfate solutions was determined using X-ray diffraction (XRD) analysis, as depicted in Figure 3.It can be observed that the sharp and strong peaks at 2θ = 18.7, 29.5, 35.1, and 59.7 • belonged to Cd(OH) 2 (JCPDS 31-0228) and the peaks at 2θ = 19.1,32.5, 37.9, and 51.4 • were identified as well-crystallized Co(OH) 2 (JCPDS 30-0443) in nitrates [20,21].However, the peaks around 2θ = 33.5, 38.5, and 59.7 • were broad and poor, indicating the formation of amorphous Ni(OH) 2 /NiOOH (JCPDS 38-0715).The SEM further revealed that irregular blocks of Cd(OH) 2 formed due to the rapid reaction (Figure 4a).A sheet-like structure of Co(OH) 2 (Figure 4b) and an irregular rod-like shape of Ni(OH) 2 /NiOOH (Figure 4c) were generated, with the particles aggregating to form blocks.However, the adsorption products in the sulfate solutions consisted of metallic Cd (JCPDS 85-1328), Co (JCPDS 05-0727), and Ni (JCPDS 87-0712).Among them, metallic Cd and Co exhibited dendritic morphology, as depicted in Figure 4d,e.The morphology of Ni appeared as irregular spherical shapes (Figure 4f).4a).A sheet-like structure of Co(OH)2 (Figure 4b) and an irregular rod-like shape of Ni(OH)2/NiOOH (Figure 4c) were generated, with the particles aggregating to form blocks.However, the adsorption products in the sulfate solutions consisted of metallic Cd (JCPDS 85-1328), Co (JCPDS 05-0727), and Ni (JCPDS 87-0712).Among them, metallic Cd and Co exhibited dendritic morphology, as depicted in Figure 4d,e.The morphology of Ni appeared as irregular spherical shapes (Figure 4f).When the voltage was −1.5 V, hydroxides could be obtained in these nitrates (Figure S2).However, the morphology of the Cd(OH)2, Ni(OH)2/NiOOH and Co(OH)2 obviously changed (Figure S3).Although no change in the adsorbed products was detected from the XRD profiles in sulfate solution, the dendritic crystal became more obvious (Figure S4).
The chemical state of the product on the surface of the LIG film was analyzed using XPS, as shown in Figure 5.All XPS data were calibrated and fitted using PeakFit software 4.12.In the fitted spectra of products in Cd(NO3)2 solution (Figure 4a), two characteristic peaks were observed at 405.3 eV (Cd 3d5/2) and 412.11 eV (Cd 3d3/2), indicative of Cd 2+ in Cd(OH)2 [22].The position of the fitted peak in the Cd 3d spectrum of CdSO4 was identical to that of Cd(NO3)2, as zero-valent cadmium exhibits no characteristic peak.The results of XRD show that the adsorbed product of CdSO4 is Cd.This illustrates that besides the metallic Cd, trace of hydroxide existed.In the Co(NO3)2 solution, the peaks observed at 781.44 and 797.29 eV corresponded to Co 2p3/2 and Co 2p1/2 in Co(OH)2, respectively [23].The satellite peaks at 787.18 and 803.54 eV, respectively, corresponded to the high spin state of Co 2+ [24].The fitting of the Co 2p spectra from CoSO4 (Figure 5e) exhibited significant differences compared to that from Co(NO3)2.Herein, characteristic peaks emerge at 778.When the voltage was −1.5 V, hydroxides could be obtained in these nitrates (Figure S2).However, the morphology of the Cd(OH) 2 , Ni(OH) 2 /NiOOH and Co(OH) 2 obviously changed (Figure S3).Although no change in the adsorbed products was detected from the XRD profiles in sulfate solution, the dendritic crystal became more obvious (Figure S4).
The chemical state of the product on the surface of the LIG film was analyzed using XPS, as shown in Figure 5.All XPS data were calibrated and fitted using PeakFit software 4.12.In the fitted spectra of products in Cd(NO 3 ) 2 solution (Figure 4a), two characteristic peaks were observed at 405.3 eV (Cd 3d 5/2 ) and 412.11 eV (Cd 3d 3/2 ), indicative of Cd 2+ in Cd(OH) 2 [22].The position of the fitted peak in the Cd 3d spectrum of CdSO 4 was identical to that of Cd(NO 3 ) 2 , as zero-valent cadmium exhibits no characteristic peak.The results of XRD show that the adsorbed product of CdSO 4 is Cd.This illustrates that besides the metallic Cd, trace of hydroxide existed.In the Co(NO 3 ) 2 solution, the peaks observed at 781.44 and 797.29 eV corresponded to Co 2p 3/2 and Co 2p 1/2 in Co(OH) 2 , respectively [23].The satellite peaks at 787.18 and 803.54 eV, respectively, corresponded to the high spin state of Co 2+ [24].The fitting of the Co 2p spectra from CoSO 4 (Figure 5e) exhibited significant differences compared to that from Co(NO 3 ) 2 .Herein, characteristic peaks emerge at 778.1, 781.1, and 783.1 eV, respectively, corresponding to metallic Co [25].The Ni 2p spectrum in Ni(NO 3 ) 2 was fitted with six characteristic peaks located at 854.8, 855.7, 857.7, 860.1, 861.5 and 866.5 eV, respectively.This indicates that the product is Ni(OH) 2 or NiOOH, aligning with the reports in the literature [26].The characteristic peaks of the Ni 2p spectra from NiSO 4 (Figure 5f) were observed at 852.9, 856.4 and 859.2 eV, respectively, corresponding to metallic Ni.

Electrochemical Properties
Figure 6 illustrates the cyclic voltammetry (CV) curves of the LIG/PI thin film electrode under different scan rates in various nitrate and sulfate solutions.At scan rates of 5 to 20 mV s −1 in the Cd(NO3)2 solution, a quasi-rectangular shape was observed, illustrating stable capacitance behavior without a redox reaction.However, an oxidation peak appeared in CdSO4, indicating the possible decomposition of water.No obvious reduction peak from Cd 2+ to Cd was detected due to the rapid scan.An obvious difference in Co(NO3)2 and CoSO4 was detected; however, a slight difference was observed in Ni(NO3)2 and NiSO4.Because the applied potential was higher (−1.2 V), both H + and H2O participated in the reaction, reducing the pH of the solutions and increasing the conductivity.

Electrochemical Properties
Figure 6 illustrates the cyclic voltammetry (CV) curves of the LIG/PI thin film electrode under different scan rates in various nitrate and sulfate solutions.At scan rates of 5 to 20 mV s −1 in the Cd(NO 3 ) 2 solution, a quasi-rectangular shape was observed, illustrating stable capacitance behavior without a redox reaction.However, an oxidation peak appeared in CdSO 4 , indicating the possible decomposition of water.No obvious reduction peak from Cd 2+ to Cd was detected due to the rapid scan.An obvious difference in Co(NO 3 ) 2 and CoSO 4 was detected; however, a slight difference was observed in Ni(NO 3 ) 2 and NiSO 4 .Because the applied potential was higher (−1.2 V), both H + and H 2 O participated in the reaction, reducing the pH of the solutions and increasing the conductivity.
After applying a potential of −1.2 V, the current density remained stable in the nitrate solution (Figure 7a).At the moment the voltage was applied, the current density surged in the nitrate solutions.Afterward, the current density decreased and stabilized.The stable current density values were approximately 1.5 mA cm −2 in the Co(NO 3 ) 2 solution, 2 mA cm −2 in the Ni(NO 3 ) 2 solution, and 4 mA cm −2 in the Cd(NO 3 ) 2 solution, respectively.Combining the changes in pH and conductivity, water decomposition occurred, and the generated H + ions compensated for the adsorption of the Cd 2+ , Co 2+ , and Ni 2+ ions, thereby ensuring that the mobility of the ions in the nitrate salt solutions remained unchanged.The current density was relatively stable in the NiSO 4 (approximately 1.3 mA cm −2 ) and CoSO 4 solution (approximately 2.3 mA cm −2 ).However, the current density in CdSO 4 rapidly and linearly increased over time.This further illustrates that the stable reduction reaction in NiSO 4 and CoSO 4 was supported by the generated H + ions.In addition, the reduction of Cd 2+ ions was dramatically affected by the polarization.After applying a potential of −1.2 V, the current density remained stable in the nitrate solution (Figure 7a).At the moment the voltage was applied, the current density surged in the nitrate solutions.Afterward, the current density decreased and stabilized.The stable current density values were approximately 1.5 mA cm −2 in the Co(NO3)2 solution, 2 mA cm −2 in the Ni(NO3)2 solution, and 4 mA cm −2 in the Cd(NO3)2 solution, respectively.Combining the changes in pH and conductivity, water decomposition occurred, and the generated H + ions compensated for the adsorption of the Cd 2+ , Co 2+ , and Ni 2+ ions, thereby ensuring that the mobility of the ions in the nitrate salt solutions remained unchanged.The current density was relatively stable in the NiSO4 (approximately 1.3 mA cm −2 ) and CoSO4 solution (approximately 2.3 mA cm −2 ).However, the current density in CdSO4 rapidly and linearly increased over time.This further illustrates that the stable reduction reaction in NiSO4 and CoSO4 was supported by the generated H + ions.In addition, the reduction of Cd 2+ ions was dramatically affected by the polarization.
When the voltage was −1.5 V, the current density exhibited changes as depicted in Figure S5.Except for CdSO4 and CoSO4, the current density changes in other solutions were consistent with the changes observed at −1.2 V, wherein the current density initially increased sharply before decreasing and ultimately stabilizing.The change was more pronounced in the CdSO4 solution, with a current density of 20 mA cm −2 at −1.2 V and 45 mA cm −2 at −1.5 V at 1200 s, respectively.In the CoSO4 solution, the current density did not remain stable but instead increased with time.

Adsorption Capacity
The adsorption amount of metal ions was measured using an atomic absorption spectrometer to evaluate the adsorption capability of the LIG/PI membrane electrode towards metal ions.We calculated Q and W using Formulas (1) and (2) (Supplementary Materials).The standard curves for different metal ions are depicted in Figure S6, while Figure 8 illustrates the temporal changes in the adsorption capacity.It was evident that with the increasing concentration, the adsorption capacity also increased.The adsorption capacity in Cd(NO3)2 increased from 913.5 mg g −1 at 0.005 M to 3479.8 mg g −1 at 0.02 M. Approximately 39% of Cd 2+ ions were adsorbed on the electrode surface in 0.02M Cd(NO3)2 over 300 min.The adsorption capacity of 1381.5 mg g −1 in 0.02 M Co(NO3)2 solution was slightly lower than that of 1448.7 mg g −1 in Ni(NO3)2 solution.The adsorption capacity in the 0.005 M CdSO4 solution reached 2634.27 mg g −1 , indicating the easy migration of Cd 2+ and its reduction in the sulfate solution.Moreover, the adsorption capacity of 0.02 M CoSO4 and NiSO4 was also higher than that in the nitric acid solution.However, the recovery capability at a low concentration of CoSO4 and NiSO4 was similar.In sulfuric acid solution, the When the voltage was −1.5 V, the current density exhibited changes as depicted in Figure S5.Except for CdSO 4 and CoSO 4 , the current density changes in other solutions were consistent with the changes observed at −1.2 V, wherein the current density initially increased sharply before decreasing and ultimately stabilizing.The change was more pronounced in the CdSO 4 solution, with a current density of 20 mA cm −2 at −1.2 V and 45 mA cm −2 at −1.5 V at 1200 s, respectively.In the CoSO 4 solution, the current density did not remain stable but instead increased with time.

Adsorption Capacity
The adsorption amount of metal ions was measured using an atomic absorption spectrometer to evaluate the adsorption capability of the LIG/PI membrane electrode towards metal ions.We calculated Q and W using Formulas (1) and (2) (Supplementary Materials).The standard curves for different metal ions are depicted in Figure S6, while Figure 8 illustrates the temporal changes in the adsorption capacity.It was evident that with the increasing concentration, the adsorption capacity also increased.The adsorption capacity in Cd(NO 3 ) 2 increased from 913.5 mg g −1 at 0.005 M to 3479.8 mg g −1 at 0.02 M. Approximately 39% of Cd 2+ ions were adsorbed on the electrode surface in 0.02M Cd(NO 3 ) 2 over 300 min.The adsorption capacity of 1381.5 mg g −1 in 0.02 M Co(NO 3 ) 2 solution was slightly lower than that of 1448.7 mg g −1 in Ni(NO 3 ) 2 solution.The adsorption capacity in the 0.005 M CdSO 4 solution reached 2634.27 mg g −1 , indicating the easy migration of Cd 2+ and its reduction in the sulfate solution.Moreover, the adsorption capacity of 0.02 M CoSO 4 and NiSO 4 was also higher than that in the nitric acid solution.However, the recovery capability at a low concentration of CoSO 4 and NiSO 4 was similar.In sulfuric acid solution, the adsorption capacity followed the order of Cd 2+ > Co 2+ > Ni 2+ .The recycling stability of the LIG electrode was one of the important factors for application.After the product was collected, which involved soaking in 5% nitric acid for 1 h, the electrode was washed with deionized water and then dried at 30 °C.The conductivities in this solution were stable in five adsorptions-desorption cycles, indicating that the LIG film possesses regenerative properties, as shown in Figure 9.As the voltage was −1.5 V, the adsorption capacity also changed, as depicted in Figure S7.Approximately 40% Ni 2+ in Ni(NO 3 ) 2 was covered in 100 min; then, the adsorption showed no obvious change due to the occupation of the active sites.It showed a faster adsorption with a longer adsorption time in Cd(NO 3 ) 2 than in Co(NO 3 ) 2 .The recovery of Cd 2+ , Ni 2+ , and Co 2+ was lower than approximately 20% when the concentration was 0.002 M. The recovery efficiency in the 0.002 M CoSO 4 solution remained approximately 10%, while it increased in the NiSO 4 and CdSO 4 solution.
The recycling stability of the LIG electrode was one of the important factors for application.After the product was collected, which involved soaking in 5% nitric acid for 1 h, the electrode was washed with deionized water and then dried at 30 • C. The conductivities in this solution were stable in five adsorptions-desorption cycles, indicating that the LIG film possesses regenerative properties, as shown in Figure 9.

Reaction Mechanism
In nitrate, NO 3-ions migrate towards the counter electrode after the application of voltage, where they may acquire electrons and undergo reduction to form NO 2-ions (Equation (1)).Meanwhile, reaction Equation (2) occurs, generating H + ions and reducing the pH of these solutions.Correspondingly, metallic ions swiftly migrate towards and combine with hydroxyl and carboxyl groups on the surface of the LIG film.Moreover, the generated OH -ions further combine with metal ions to facilitate the formation of hydroxide precipitates (Equation (3)).However, water is decomposed in sulfates, and the acidic condition accelerates the reduction to form the corresponding metals (Equation ( 4)).

Application of the Product
Taking recycled cobalt as an example, the investigation focused on the reutilization of the recovered product.The obtained Co(OH)2 served as the raw material for preparing LiCoO2.The CV curves (Figure 10) displayed a distinct redox peak at 4.1/3.7 V, corresponding to the insertion/extraction of Li.The specific capacity reached 122.8 mAh g −1 at a current density of 0.5 C, highly consistent with the reported data from commercially prepared materials [27].The initial discharge capacity exhibited no significant change at a current density of 1 C.However, it rapidly decreased with increasing cycles, a phenomenon attributed to the particle size of the LiCoO2.In summary, the products recovered through this method also hold potential application value in other fields.

Reaction Mechanism
In nitrate, NO 3− ions migrate towards the counter electrode after the application of voltage, where they may acquire electrons and undergo reduction to form NO 2− ions (Equation (1)).Meanwhile, reaction Equation (2) occurs, generating H + ions and reducing the pH of these solutions.Correspondingly, metallic ions swiftly migrate towards and combine with hydroxyl and carboxyl groups on the surface of the LIG film.Moreover, the generated OH − ions further combine with metal ions to facilitate the formation of hydroxide precipitates (Equation (3)).However, water is decomposed in sulfates, and the acidic condition accelerates the reduction to form the corresponding metals (Equation ( 4)).

Application of the Product
Taking recycled cobalt as an example, the investigation focused on the reutilization of the recovered product.The obtained Co(OH) 2 served as the raw material for preparing LiCoO 2 .The CV curves (Figure 10) displayed a distinct redox peak at 4.1/3.7 V, corresponding to the insertion/extraction of Li.The specific capacity reached 122.8 mAh g −1 at a current density of 0.5 C, highly consistent with the reported data from commercially prepared materials [27].The initial discharge capacity exhibited no significant change at a current density of 1 C.However, it rapidly decreased with increasing cycles, a phenomenon attributed to the particle size of the LiCoO 2 .In summary, the products recovered through this method also hold potential application value in other fields.

Figure 1 .
Figure 1.(a) Schematic diagram of the fabrication of LIG/PI film electrodes.(b) Schematic of the three-electrode system.

Figure 1 .
Figure 1.(a) Schematic diagram of the fabrication of LIG/PI film electrodes.(b) Schematic diagram of the three-electrode system.

Figure 3 .
Figure 3. XRD pattern of electrode surface products in (a) nitric acid and (b) sulfate solutions with a voltage of −1.2 V.