Effect of Si Content on Microstructures and Electrochemical Properties of Al-xSi-3.5Fe Coating Alloy

Hot-dip aluminum alloy is widely used in the engineering fields. However, during the aluminum plating process, Fe inevitably enters and reaches a saturation state, which has a significant impact on the corrosion resistance and microstructure of the coating. Currently, adding Si during the hot-dip aluminum process can effectively improve the quality of the coating and inhibit the Fe-Al reaction. To understand the effect of Si content on the microstructure and electrochemical performance of Al-xSi-3.5Fe coating alloys, the microstructure and post-corrosion morphology of the alloys were analyzed using SEM (Scanning Electron Microscope) and XRD (X-ray Diffraction). Through electrochemical tests and complete immersion corrosion experiments, the corrosion resistance of the coating alloys in 3.5 wt.% NaCl was tested and analyzed. The results show that the Al-3.5Fe coating alloy mainly comprises α-Al, Al3Fe, and Al6Fe. With the increase in Si addition, the iron-rich phase changes from Al3Fe and Al6Fe to Al8Fe2Si. When the Si content reaches 4 wt.%, the iron-rich phase is Al9Fe2Si2, and the excess Si forms the eutectic Si phase with the aluminum matrix. Through SKPFM (Scanning Kelvin Probe Force Microscopy) testing, it was determined that the electrode potentials of the alloy phases Al3Fe, Al6Fe, Al8Fe2Si, Al9Fe2Si2, and eutectic Si phase were higher than that of α-Al, acting as cathode phases to the micro-galvanic cell with the aluminum matrix, and the corrosion form of alloys was mainly galvanic corrosion. With the addition of silicon, the electrode potential of the alloy increased first and then decreased, and the corrosion resistance results were synchronous with it. When the Si content is 10 wt.%, the alloy has the lowest electrode potential and the highest electrochemical activity.


Introduction
Corrosion is one of the primary forms of metal component failure, and corrosion problems exist in various fields of engineering construction.Metal corrosion not only causes enormous economic losses but also leads to catastrophic accidents.Developing anticorrosion technology is urgently needed to reduce corrosion losses and promote resource conservation.Therefore, seeking methods and technologies to prevent steel corrosion is significant.Among them, surface engineering technology for surface modification is one of the most active frontier fields in materials science, which is a crucial method to prolong the service life of steel and improve economic benefits [1][2][3].
Hot-dip galvanizing is the most important anticorrosion method for steel, which is widely used in automobile, ship, bridge, pressure vessel and other industries, but the shortage of zinc resources is becoming more and more severe.It is an inevitable trend and requirement to develop new materials for the hot plating of steel that can replace zinc, and aluminum is the most promising material to replace zinc [4].Hot-dip aluminizing is a simple and efficient surface-coating technology [5].The hot-dip aluminizing coating has a metallic luster surface and excellent high-temperature oxidation resistance, good corrosion resistance, wear resistance, and reflectivity to light and heat [6][7][8].During the continuous hot-dip aluminizing process, iron and aluminum atoms diffuse and react with each other, thus, forming a layer of the Fe-Al intermetallic compound layer.After cooling, a hot-dip aluminizing layer is formed on the surface of the steel matrix, which can effectively improve the corrosion resistance of steel [9].The intermetallic compound layer mainly comprises an inner layer of Fe 2 Al 5 and an outer layer of FeAl 3 .The corrosion resistance and adhesion of the hot-dip coating largely depend on the properties and morphology of the inner layer of Fe 2 Al 5 and the outer layer of FeAl 3 .However, there are still many problems in theory, performance, and preparation technology, which limit the wide application of continuous hot aluminum plating.The thickness of the Fe-Al intermetallic compound layer in the coating increases rapidly.It has greater brittleness and lower fracture strength, which deteriorates the bonding strength of the interface between the steel matrix and the aluminum-based coating and reduces the machinability of hot-dip aluminized steel [10][11][12][13].
As an additive element in hot-dip aluminizing, silicon can not only improve the fluidity of the aluminum liquid, reduce the temperature of the aluminum liquid, and reduce the oxide impurity content in the aluminum liquid but also significantly inhibit the increase in the thickness of the Fe/Al reaction layer.The main reason is that Si can inhibit the rapid growth of the η-Fe 2 Al 5 phase [14][15][16].Springer et al. [17] studied the reaction between low-carbon steel and pure aluminum and between low-carbon steel and a Al-5 wt.% Si alloy and concluded that the total thickness of the reaction layer mainly depends on the parabolic growth controlled by the diffusion of the η phase (Fe 2 Al 5 ), which exhibits orientation-dependent growth kinetics.When 6 wt.% Si is added, the thickness of the alloy layer can be effectively reduced.Some scholars believe that Si atoms can fill the atomic vacancies in Fe 2 Al 5 , preventing aluminum atoms from preferential fast diffusion along the c-axis direction [18][19][20].Our research group believes that silicon changes the diffusion channel of coating growth and then changes the coating phase composition, thereby reducing the growth rate of the alloy.
During the continuous hot-dip plating process, the steel plate and the sinking roller system are corroded by the aluminum liquid, and the Fe element inevitably dissolves into the aluminum liquid.Therefore, after a production period, the iron in the aluminum bath can reach the saturation point.The higher iron content in the Al-Si-Fe bath leads to the formation of several intermetallic phases, such as hexagonal τ 5 (α-Al 8 Fe 2 Si), monoclinic τ 6 (β-Al 9 Fe 2 Si 2 ), τ 11 (δ-Al 4 Fe 2 Si), as well as other binary Al-Fe compounds (Al 3 Fe, Al 5 Fe 2 , etc.) [21][22][23].Li et al. studied the effect of Fe on the mechanical properties of aluminum alloys and found that the appearance of an Al-Fe-Si phase decreased the plasticity and strength of the alloy, but the high-temperature mechanical properties increased [24].Piotr's research found that the separation and reduction in iron-rich phases may play a role in the removal of Fe from Al-Si alloys [25].Kakinuma et al.measured the open-circuit potentials of the bulk intermetallic compounds and Al-matrix of AA1050 without intermetallic particles.The cathodic reactivity on bulk Al-Fe was higher than that on bulk Al-Fe-Si under aspolished condition [26].The rich iron content in the aluminum matrix greatly influences the coating's corrosion resistance and electrochemical properties.
Although studies on Al-Fe-Si alloys have been reported, they have mainly focused on the influence of trace iron content on the alloy structure.There have been no reports on the effects of Si content variation on the microstructure and electrochemical properties of aluminum coating alloys in the iron-saturated state.This article conducted qualitative research on five types of iron-saturated aluminum alloys and conducted electrochemical analysis and microstructure characterization of the coating alloys to explore the impact of changes in Si content on the structure and electrochemical properties of Al-Fe-Si alloys.S. Pontevichi [27] found that the solubility of iron in the liquid aluminum is approximately 3.5 wt.% at 727 • C.This was combined with the melting temperature of this experiment, and it was determined that the Fe content in the coating alloy studied in this article is 3.5 wt.%.
After cooling, the alloys were cut into 10 mm × 10 mm × 5 mm alloy blocks using wire cutting (Sanguang Technology, Suzhou, China) and ground step by step on 400-mesh to 2000-mesh silicon carbide sandpaper (Sanguang Technology, Suzhou, China).After polishing with a diamond polishing agent (Maifeng Metering Technology, Taizhou, China), the samples were cleaned with absolute ethanol (Najing Reagent, Nanjing, China) and blown dry with cold air for later use.

Microstructure Analysis
A JSM-6510 scanning electron microscope (Oxford Instrument, Oxford, UK) and an Oxford energy dispersive spectrometer (EDS, Oxford Instrument, Oxford, UK) were used with an accelerating voltage of 20 kV to observe the surface morphology of the sample before and after corrosion and analyze the composition and distribution of the relevant elements on the alloy surface and cross-section.
The XRD measurements were performed on a Siemens D500 X-ray diffraction system (Siemens, Munich, Germany) with a scanning speed of 2 • /min and 2θ ranging from 10 • to 90 • to analyze the phase composition of the alloy.MDI Jade6 software (Jade6.0,2017, Materials Data, New City Square, PA, USA) was used to perform background subtraction analysis on the XRD spectrum and compared with the International Center for Diffraction Data (ICDD) PDF card.

Electrochemical Analysis
The PARSTAT-4000A electrochemical workstation (AMETEK, Philadelphia, PA, USA) was used to test the open circuit potential (OCP), electrochemical impedance spectroscopy (EIS), and potentiodynamic polarization curve (Tafel) of the sample with a surface area of 1 cm 2 .A three-electrode system was used, in which the sample was the working electrode, the reference electrode was a saturated calomel electrode (KCl), and the auxiliary electrode was a platinum electrode.The electrochemical test was carried out under a constant-temperature water bath at 25 • C.
When electrochemical testing was performed, the sample was first immersed in 3.5 wt.% NaCl solution (Sigma-Aldrich, Shanghai, China) for 3600 s to measure the open circuit potential in the steady state.Dynamic potential polarization and electrochemical impedance spectroscopy (EIS) tests were performed using an electrochemical potentiostat (AMETEK, Philadelphia, PA, USA).In the EIS test, a sinusoidal voltage with a frequency range of 10 5 -10 −2 Hz and an amplitude of 5 mV was used to measure the EIS at the OCP and use ZSimpWin software (1.0 of ZSimpWin, 2017, AMETEK, Philadelphia, PA, USA) to fit the EIS.The electrochemical dynamic potential polarization scanning interval was ±0.5 V (vs.OCP), and the scanning speed was 1 mV/s.CView2 software (2.0 of CView, 2007, AMETEK, Philadelphia, PA, USA) was used to fit and analyze the polarization curve.The scanning Kelvin probe force microscope (SKPFM) experiments were carried out on electrochemical samples using an atomic force microscope (Bruker Multimode, Salbuluken, Germany).

Full Immersion Corrosion Experiment
The size of the corrosion immersion sample was 10 × 10 mm 2 .The samples before and after soaking were dried and weighed using a precision balance (Huazhi, Putian, China).The sample was soaked in the 3.5 wt.% NaCl solution at 25 • C for 720 h.The samples were then washed with absolute ethanol and dried immediately.First, a scanning electron microscope (SEM) was used to observe the corrosion surface morphology of the sample.Then, the corroded samples were cut in the vertical direction, ground, and polished, and the cross-sections of the corroded samples were observed using SEM.
To elucidate the effect of alloy element Si content on corrosion products and alloy electrochemical properties in a 3.5 wt.% NaCl environment, the soaked alloy samples were dried in a drying oven for 24 h, and their corrosion products and relative contents were tested using XPS: X-ray Photoelectron Spectroscopy (Siemens, Munich, Germany).

Al-Fe-Si Ternary Phase Diagram
The vertical section phase diagram of the Al-xSi-3.5Fecoating alloy was calculated with cost50B database in Pandat software (2022 of Pandat, 2022, CompuTherm, Middleton, WI, USA), as shown in Figure 1.As the temperature gradually cooled from 720 • C, the initial phases forming in the Al-3.5Fealloy were Al 3 Fe, according to the phase diagram.The final solidified microstructure of the alloy consists of FCC (Face-centered cubic)-Al and Al 3 Fe phases.As the addition of Si in the alloy increased to 1 wt.%, the τ 5 (α-Al 8 Fe 2 Si) phase occurred during cooling.The Al 3 Fe phase disappeared in the Al-2Si-3.5Fealloy at room temperature, and the iron-rich phases were composed of τ 5 (α-Al 8 Fe 2 Si) and τ 6 (β-Al 9 Fe 2 Si 2 ) phases.As the Si content was above 2 wt.%, the τ 5 (α-Al 8 Fe 2 Si) phase disappeared, and the eutectic Si phase gradually precipitated at 577 • C. When the Si content was above 4 wt.%, the solidified Microstructure(microstrucyure) of Al-xSi-3.5Fecoating alloy was always composed of FCC-Al, Si, and τ 6 (β-Al 9 Fe 2 Si 2 ) phases.

Microstructure and Morphology of Alloy before Corrosion
Combining the SEM morphologies (Figure 2), EDS results (Figure 3), and X-ray diffraction patterns (Figure 4) of the coating alloys with different Si contents, the phases in the alloys were determined.The original Al-Fe alloy without adding Si consisted of three phases: the gray α-Al matrix phase, the white fine primary Al 3 Fe phase, and the dispersed Al-Al 6 Fe eutectic phases, which were evenly distributed [28].As shown in Figure 2b,c, with the addition of the Si element, the Al-Fe phase disappeared in the Al-1Si-3.5Fealloy, and the iron-rich phase transformed into a Chinese character-shaped τ 5 (α-Al 8 Fe 2 Si) phase and a dispersed Al-τ 5 eutectic phase.The dispersed Al-τ 5 eutectic phase decreased, and the iron-rich τ 5 (α-Al 8 Fe 2 Si) phase increased in the Al-2Si-3.5Fealloy.As shown in Figure 2d,e, coarse dendritic τ 6 (β-Al 9 Fe 2 Si 2 ) and τ 5 coexist in the Al-4Si-3.5Fealloy.Excess Si reacted with the aluminum matrix to form a eutectic Si phase.τ 5 disappeared in the Al-10Si-3.5Fealloy, and the microstructure became coarse.The grayish-white τ 6 (β-Al 9 Fe 2 Si 2 ) and black eutectic Si phases were seen [29].

Microstructure and Morphology of Alloy before Corrosion
Combining the SEM morphologies (Figure 2), EDS results (Figure 3), and X-ray diffraction patterns (Figure 4) of the coating alloys with different Si contents, the phases in the alloys were determined.The original Al-Fe alloy without adding Si consisted of three phases: the gray α-Al matrix phase, the white fine primary Al3Fe phase, and the dispersed Al-Al6Fe eutectic phases, which were evenly distributed [28].As shown in Figure 2b,c, with the addition of the Si element, the Al-Fe phase disappeared in the Al-1Si-3.5Fealloy, and the iron-rich phase transformed into a Chinese character-shaped τ5(α-Al8Fe2Si) phase and a dispersed Al-τ5 eutectic phase.The dispersed Al-τ5 eutectic phase decreased, and the iron-rich τ5(α-Al8Fe2Si) phase increased in the Al-2Si-3.5Fealloy.As shown in Figure 2d,e, coarse dendritic τ6(β-Al9Fe2Si2) and τ5 coexist in the Al-4Si-3.5Fealloy.Excess Si reacted with the aluminum matrix to form a eutectic Si phase.τ5 disappeared in the Al-10Si-3.5Fealloy, and the microstructure became coarse.The grayish-white τ6(β-Al9Fe2Si2) and black eutectic Si phases were seen [29].

Surface Morphology of Alloy after Corrosion
Figure 5 shows the corrosion morphology of Al-xSi-3.5Fealloys immersed in a 3.5% NaCl solution for 30 min.After soaking, corrosion pits (black areas) appeared on the surface of the alloys, and insoluble corrosion products were present.From observing the position of the corrosion pits, it can be found that when the Si content is 0-1 wt.%, the corrosion pits of the alloys start around the Al3Fe and Al8Fe2Si phases, and galvanic corrosion occurs with the aluminum matrix, and the no corrosion phenomenon occurs around the dispersive phase; when the Si content is 2 wt.%, galvanic corrosion occurs between the aluminum matrix and Al8Fe2Si; when the Si content is 4 wt.%,galvanic corrosions oc-

Surface Morphology of Alloy after Corrosion
Figure 5 shows the corrosion morphology of Al-xSi-3.5Fealloys immersed in a 3.5% NaCl solution for 30 min.After soaking, corrosion pits (black areas) appeared on the surface of the alloys, and insoluble corrosion products were present.From observing the position of the corrosion pits, it can be found that when the Si content is 0-1 wt.%, the corrosion pits of the alloys start around the Al 3 Fe and Al 8 Fe 2 Si phases, and galvanic corrosion occurs with the aluminum matrix, and the no corrosion phenomenon occurs around the dispersive phase; when the Si content is 2 wt.%, galvanic corrosion occurs between the aluminum matrix and Al 8 Fe 2 Si; when the Si content is 4 wt.%,galvanic corrosions occurred between the aluminum matrix and Al 8 Fe 2 Si, Al 9 Fe 2 Si 2 , and eutectic Si, and the corrosion pits were mainly concentrated around the eutectic Si phase; when the Si content is 10 wt.%, there were noticeable corrosion pits around the eutectic Si phase, the Al 9 Fe 2 Si 2 phase was broken under the corrosion influence, and galvanic corrosion occurred between Al 9 Fe 2 Si 2 and eutectic Si [30].

Surface Morphology of Alloy after Corrosion
Figure 5 shows the corrosion morphology of Al-xSi-3.5Fealloys immersed in a 3.5% NaCl solution for 30 min.After soaking, corrosion pits (black areas) appeared on the surface of the alloys, and insoluble corrosion products were present.From observing the position of the corrosion pits, it can be found that when the Si content is 0-1 wt.%, the corrosion pits of the alloys start around the Al3Fe and Al8Fe2Si phases, and galvanic corrosion occurs with the aluminum matrix, and the no corrosion phenomenon occurs around the dispersive phase; when the Si content is 2 wt.%, galvanic corrosion occurs between the aluminum matrix and Al8Fe2Si; when the Si content is 4 wt.%,galvanic corrosions occurred between the aluminum matrix and Al8Fe2Si, Al9Fe2Si2, and eutectic Si, and the corrosion pits were mainly concentrated around the eutectic Si phase; when the Si content is 10 wt.%, there were noticeable corrosion pits around the eutectic Si phase, the Al9Fe2Si2 phase was broken under the corrosion influence, and galvanic corrosion occurred between Al9Fe2Si2 and eutectic Si [30].   Figure 6 shows the SEM image and corresponding element distribution of Al-10Si-3.5Fealloy after corrosion.Based on the enrichment of the Fe and Si elements, these phases were eutectic Si and Al9Fe2Si2, consistent with the results of the previous phase analysis.From the distribution of black corrosion areas, it can be determined that the corrosion pits are located in the middle of the eutectic Si phase and Al9Fe2Si2 phase.The eutectic Si and Al9Fe2Si2 formed a galvanic cell with the aluminum matrix, resulting in galvanic corrosion.The content of O and Cl elements in the corrosion area was very high, indicating the deposition of corrosion products such as hydroxide and chloride on the surface of the alloy.

Cross-Sectional Morphology of Alloy after Corrosion
In the cross-sectional morphology of the Al-xSi-3.5Fecoating alloy (Figure 7), corrosion pits were found around the iron-rich phase and eutectic silicon phase.Figure 7a displays noticeable corrosion pits and corrosion stripes on the cross-section of the Al-3.5Fe

Cross-Sectional Morphology of Alloy after Corrosion
In the cross-sectional morphology of the Al-xSi-3.5Fecoating alloy (Figure 7), corrosion pits were found around the iron-rich phase and eutectic silicon phase.Figure 7a displays noticeable corrosion pits and corrosion stripes on the cross-section of the Al-3.5Fealloy, indicating the poor corrosion resistance of the alloy.Figure 7b-d show that the corroded morphology of the alloys with silicon addition becomes more uniform, and the corrosion pits and corrosion stripes were mainly around Al 8 Fe 2 Si, Al 9 Fe 2 Si 2 , and the eutectic silicon phase.Figure 7e indicates that when the silicon content was too high, while the Al 9 Fe 2 Si 2 phase formed with the Fe element, the excess Si included the eutectic Si phase, which acted as the cathode phase and accelerated the corrosion rate of the alloy.

Corrosion Products
To further investigate the relationship between the corrosion products of Al-10Si-3.5Fealloy and the sacrificial anode performance, the compounds formed on the surface of the alloy samples soaked for 720 h were characterized by X-ray photoelectron spectroscopy (XPS), as shown in Figure 8.The chemical states of the Al and Fe alloy elements in XPS confirmed the presence of corrosion products, corresponding to the results in Figure 6.It was confirmed by the XPS database (NIST) that the Al 2p3/2 spectrum mainly consists of the Al 3+ valence state, and only the Al2O3•H2O peak existed.The O 1s spectrum was the OH − peak, corresponding to the corrosion products of hydroxide, with Al(OH)3 accounting for the highest proportion.The Fe 2p3/2 spectrum of alloy corrosion products had peaks at 710.5 eV and 715.4 eV, corresponding to Fe 2+ and Fe 3+ , respectively.The Cl − peak at approximately 198.6 eV corresponds to Cl 2p3/2, which reacted with Fe 2+ to form the corrosion product FeCl2.

Corrosion Products
To further investigate the relationship between the corrosion products of Al-10Si-3.5Fealloy and the sacrificial anode performance, the compounds formed on the surface of the alloy samples soaked for 720 h were characterized by X-ray photoelectron spectroscopy (XPS), as shown in Figure 8.The chemical states of the Al and Fe alloy elements in XPS confirmed the presence of corrosion products, corresponding to the results in Figure 6.It was confirmed by the XPS database (NIST) that the Al 2p3/2 spectrum mainly consists of the Al 3+ valence state, and only the Al 2 O 3 •H 2 O peak existed.The O 1s spectrum was the OH − peak, corresponding to the corrosion products of hydroxide, with Al(OH) 3 accounting for the highest proportion.The Fe 2p3/2 spectrum of alloy corrosion products had peaks at 710.5 eV and 715.4 eV, corresponding to Fe 2+ and Fe 3+ , respectively.The Cl − peak at approximately 198.6 eV corresponds to Cl 2p3/2, which reacted with Fe 2+ to form the corrosion product FeCl 2 .

Electrochemical Test and Analysis
To study the effect of Si content on the electrochemical behavior of the Al-xSi-3.5Fecoating alloy, electrochemical corrosion tests were carried out on alloys with different compositions at 25 °C.The electrochemical behaviors are shown in Figures 9-12

Open Circuit Potential
Figure 9 shows the open circuit potential (OCP) of Al-Si-Fe alloys with different Si contents.The samples were immersed in 3.5 wt.% NaCl aqueous solution and OCP was tested for 3600 s.It can be seen from Figure 9 that the OCP of Al-3.5Fe alloy without the Si element was relatively stable with minor fluctuations, and the potential was −0.82 V.The OCP of Al-1Si-3.5Fealloy became active and tended to be steady after the 2500 s.By comparing the steady-state OCP, it was found that with the increase in Si content, the potential of the Al-xSi-3.5Fealloy shifted positively and then negatively.As the Si content reached 4 wt.%, the electrode potential of the alloy rose to the highest value (−0.73 V).The electrode potential increased by nearly 100 mV.The electrode potential of the Al-10Si-3.5Fealloy dropped to the lowest value (−0.85 V); the maximum electrode potential difference of the alloy reached 120 mV, but the fluctuation range was small.

Polarization Curve
It can be seen from Figure 10 that with the increase in Si content, the corrosion potential of the alloy first rose and then fell, and the corrosion current density first rose and then fell.When Si content was 4%, the corrosion potential of the alloy was the highest at −0.741 V, which is close to the previous research results [31,32], and the self-corrosion current density was the lowest.

Open Circuit Potential
Figure 9 shows the open circuit potential (OCP) of Al-Si-Fe alloys with different Si contents.The samples were immersed in 3.5 wt.% NaCl aqueous solution and OCP was tested for 3600 s.It can be seen from Figure 9 that the OCP of Al-3.5Fe alloy without the Si element was relatively stable with minor fluctuations, and the potential was −0.82 V.The OCP of Al-1Si-3.5Fealloy became active and tended to be steady after the 2500 s.By comparing the steady-state OCP, it was found that with the increase in Si content, the potential of the Al-xSi-3.5Fealloy shifted positively and then negatively.As the Si content reached 4 wt.%, the electrode potential of the alloy rose to the highest value (−0.73 V).The electrode potential increased by nearly 100 mV.The electrode potential of the Al-10Si- The key electrochemical parameters were obtained by tangentially fitting the cathode and anode regions of the polarization curve, as shown in Table 2.Among them, E corr is the self-corrosion potential of the corrosion system, I corr is the self-corrosion current density of the corrosion system, B a is the anodic Tafel constant, and B c is the cathodic Tafel constant.The experimental results show that the addition of the Si element has a specific reducing effect on the anodic polarization rate, reduces the oxidation reaction of aluminum, enhances the anodic dissolution activity, and improves the discharge efficiency.The B c values of aluminum alloy sacrificial anode samples with different Si contents are all greater than B a values, indicating that the cathodic hydrogen evolution reaction of the aluminum alloy sacrificial anode in seawater is a control step and, thus, plays an influential protective role.The average corrosion rate V corr (mm/y) is related to the corrosion current density I corr A/cm 2 .It can be estimated using the following relationship [33]: Among them, 3270 is a constant for establishing the unit of corrosion rate, I corr is the corrosion current density, ρ g•cm −3 is the material density, and M(g•equiv −1 is the equivalent weight.

Electrochemical Impedance
Figure 11a showed the EIS curves of the alloy.The Nyquist plots of the Al-xSi-3.5Fealloy only consist of one capacitance arc.The capacitive arc diameter of the Al-10Si-3.5Fealloy was the smallest, and that of the Al-4Si-3.5Fealloy was the largest.The capacitive arc's diameter gradually dropped and soared with the increased Si content.In this regard, the charge transfer resistance (Rp) of the Al-10Si-3.5Fewas approximately 11.27 kΩ•cm 2 which is the lowest corrosion resistance among the five samples.The Rp for Al-4Si-3.5Fewas approximately 308.10 kΩ•cm 2 , which was the highest corrosion resistance [34,35].Generally, the smaller the capacitive arc diameter, the greater the corrosion rate of the sample and the better the electrochemical activity of the alloy [36].The Bode curves shown in Figure 11b exhibited the same characteristics.In the relationship between impedance and frequency, the impedance of the Al-10Si-3.5Fealloy was the lowest at high frequencies, while that of Al-4Si-3.5Fealloy was the highest.The impedance followed a trend of first declining and then peaking with the increase in Si content.Figure 11c showed the relationship between phase angle and frequency, with the increase in Si content, the phase angle in the low-frequency region first rose and then fell.The peak of the phase angle gradually moves towards the high-frequency direction, indicating that the impedance value of the anodic film first rose and then fell.The dissolution activity of the anode first declined and then soared.The Al-4Si-3.5Fealloy has the highest phase angle in the high-frequency range, exhibiting better capacitive characteristics and a better ability to prevent corrosive ions from invading.The Al-10Si-3.5Fealloy has the lowest phase angle, indicating better activity.Figure 11a-c suggest that the trend of changes in various alloys is consistent, meaning that the corrosion mechanism of the alloys under different composition states is the same.
To quantitatively evaluate the electrochemical corrosion behavior of the Al-10Si-3.5Fealloy, the equivalent circuit in Figure 11d was used to fit the EIS.The equivalent circuit mainly consists of two parts.The first part is Rs, which represents the solution resistance; the second part is Rp and Q, which represent the double layer capacitance between the aluminum alloy substrate and the electrolyte solution, corresponding to the double layer capacitance and charge transfer resistance of the Faraday reaction.The charge transfer resistance Rp represents the difficulty of the substrate losing electrons.The EIS circuit fitting results are shown in Table 3.The larger the Rp, the higher the corrosion resistance of the alloy.Therefore, the Al-4Si-3.5Fealloy has the best corrosion resistance, while the Al-10Si-3.5Fealloy has the strongest activity.

Alloy Full Immersion Experiment
The whole immersion experiment can shorten the experimental period and quickly obtain corrosion products and surface morphology.The A1-3.5Fe-xSi alloy was immersed in a 3.5 wt.% NaCl solution for 720 h, and the surface corrosion was evident with varying degrees of corrosion products attached.Figure 12 is a graph based on the data in Table 4.According to the chart data, the weight of samples in each group increased after 720 h of the total immersion experiment due to different degrees of galvanic corrosion on the alloy during the immersion process, and the corrosion products attached to the alloy surface did not entirely fall off.Within the Si content range of 0-10 wt.%, the self-corrosion potential of the alloy first shifts positively and then negatively, and the alloy's dissolution activity and corrosion rate first decrease and then increase.The corrosion rate of the A1-10Si-3.5Fealloy is 0.1833 g/m 2 •h, and its self-corrosion potential is −0.8429V, indicating the best dissolution activity.The 720-h full immersion test has the fastest corrosion rate, with a corrosion current density of 0.24255 µA•m −2 .The alloy has the smallest current generated by self-corrosion and high current efficiency.The corrosion rate of the A1-4Si-3.5Fealloy is 0.0986 g/m 2 •h, and its self-corrosion potential is −0.7383V, indicating the best corrosion resistance and the slowest corrosion rate.
Generally, the larger the corrosion current, the faster the corrosion rate, the better the electrochemical activity, and the more corrosion products [37].The results of this full immersion corrosion experiment are consistent with the conclusions of the previous electrochemical impedance spectroscopy, polarization curve, and fitted self-corrosion parameters.

Microstructure of Coating Alloy
In this study, we employed scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques to characterize the microstructure of Al-xSi-3.5Fealloys used for hotdip coating.Combined with the results of Figures 2-4, we observed that the changes and outcomes of various phases in the coating alloy showed some discrepancies with the calculated phase diagram in Figure 1.For hypoeutectic Al-Fe alloys under non-steadystate solidification conditions, the appearance of stable phase Al 3 Fe and metastable phase Al 6 Fe is attributed to the varying cooling rates.The study revealed that in the binary system, the non-equilibrium phase transition of AlFe intermetallic compounds occurred at temperatures below 400 • C, forming Al 6 Fe compounds.In contrast, the Al 3 Fe compounds emerged at temperatures above 400 • C [38].When the cooling rate T L is lower than 1.5 K/s, there is a coexistence region for the Al 3 Fe and Al 6 Fe phases in the eutectic mixture [28].During the solidification process of the alloy, temperature gradients between the alloy surface and the interior result in increased cooling rates, promoting the formation of metastable phases and eutectic structures.
Furthermore, this study also investigated the relationship between the formation of compounds in Al-Si-Fe alloys and both the cooling rate and the content of Fe and Si elements.It was found that a higher Fe/Si concentration ratio and a faster cooling rate both favored the increase in τ5 (Al 8 Fe 2 Si) phase.Additionally, the addition of Si reduced the critical cooling rate.When the alloy solidified, exceeding the critical cooling rate led to the final solidification structure being composed solely of the τ5 phase.During the solidification process, if there is a significant difference between the external temperature and the temperature of the molten alloy, and if the cooling rate is too fast, high-temperature phases solidify first, while low-temperature phases do not form.This study provides important theoretical insights into understanding the solidification process of aluminumbased composite materials and optimizing their manufacturing processes [29,39].

Corrosion Phenomenon of Coating Alloy
Aluminum alloys exposed to the atmospheric environment form a protective oxide film on their surface.However, the existence of iron-rich phases in the intermetallic compounds can affect the thickness uniformity of the oxide film, resulting in surface defects [40].At the same time, corrosive chloride ions in the environment can penetrate through these defects and interact with the oxide film, reducing the corrosion resistance of the alloy [41].The alloy phases Al 6 Fe, Al 3 Fe, Al 8 Fe 2 Si, and Al 9 Fe 2 Si 2 and the eutectic Si phase are the main intermetallic compounds in Al-xSi-Fe alloys, and their electrochemical activity is lower than that of the aluminum matrix, resulting in potential differences and local galvanic corrosion phenomena around the matrix.
To further investigate the influence of the second phase on the electrochemical performance of the alloy, SKPFM was used to measure the potential difference between the second phase particles and the aluminum matrix [42].As shown in Figure 13, Al 6 Fe, Al 3 Fe, Al 8 Fe 2 Si, Al 9 Fe 2 Si 2 , and eutectic Si have higher electrode potentials than the aluminum matrix.The potential differences between Al 3 Fe and Al 6 Fe relative to the matrix were +372 mV and +215 mV, respectively (Figure 13b); the potential difference between Al 8 Fe 2 Si and the matrix was +251 mV (Figure 13d); and the potential differences between Al 9 Fe 2 Si 2 and Si relative to the matrix were +162 mV and +281 mV, respectively (Figure 13f).The electrode potentials of the iron-rich phase and eutectic Si were more positive relative to the matrix α-Al, resulting in potential differences and micro-galvanic cell formation, causing galvanic corrosion around the second phase and generating corrosion points.mV and +215 mV, respectively (Figure 13b); the potential difference between Al8Fe2Si and the matrix was +251 mV (Figure 13d); and the potential differences between Al9Fe2Si2 and Si relative to the matrix were +162 mV and +281 mV, respectively (Figure 13f).The electrode potentials of the iron-rich phase and eutectic Si were more positive relative to the matrix α-Al, resulting in potential differences and micro-galvanic cell formation, causing galvanic corrosion around the second phase and generating corrosion points.For aluminum alloys, the initial development of corrosion is often related to the metal interphase compounds present in the alloy.Combined with the corrosion morphology of the alloy shown in Figure 9, when the alloy does not contain Si elements, the corrosion is mainly due to the significant potential difference between the Al3Fe phase and the aluminum matrix, resulting in galvanic corrosion.The surrounding dispersoid Al6Fe phase has a high Al content and a relatively small potential difference compared to the aluminum matrix, and no corrosion occurs; when the Si content is 1-2 wt.%, the Al8Fe2Si phase undergoes galvanic corrosion with the aluminum matrix.The Fe and Si contents in Al-Al8Fe2Si phases are relatively low, and there is no significant corrosion due to the slight potential difference compared to the aluminum matrix; when the Si content is 4 wt.%,galvanic corrosion occurs between the eutectic Si phase and the aluminum matrix due to the larger potential difference, while the potential difference of the iron-rich phase is relatively small; when the Si content is 10 wt.%, the eutectic Si phase increases significantly, For aluminum alloys, the initial development of corrosion is often related to the metal interphase compounds present in the alloy.Combined with the corrosion morphology of the alloy shown in Figure 9, when the alloy does not contain Si elements, the corrosion is mainly due to the significant potential difference between the Al 3 Fe phase and the aluminum matrix, resulting in galvanic corrosion.The surrounding dispersoid Al 6 Fe phase has a high Al content and a relatively small potential difference compared to the aluminum matrix, and no corrosion occurs; when the Si content is 1-2 wt.%, the Al 8 Fe 2 Si phase undergoes galvanic corrosion with the aluminum matrix.The Fe and Si contents in Al-Al 8 Fe 2 Si phases are relatively low, and there is no significant corrosion due to the slight potential difference compared to the aluminum matrix; when the Si content is 4 wt.%,galvanic corrosion occurs between the eutectic Si phase and the aluminum matrix due to the larger potential difference, while the potential difference of the iron-rich phase is relatively small; when the Si content is 10 wt.%, the eutectic Si phase increases significantly, and its electrode potential is higher.There is a potential difference between the aluminum matrix and Al 9 Fe 2 Si 2 , causing galvanic corrosion of the aluminum matrix and the Al 9 Fe 2 Si 2 phase.
The corrosion pits preferentially initiate at the locations of the iron-rich second phase particles and eutectic Si phase [43].The locally cathodic iron-rich and eutectic Si phases enhance the cathodic reaction, leading to galvanic corrosion near the second phase.As a result, the α-Al matrix preferentially dissolves near the second-phase particles.Figure 14 describes the corrosion mechanism of the Al-10Si-3.5Fecoating alloy.The alloy is exposed to an environment rich in corrosive ions (Cl − ), penetrating the aluminum matrix through the defect points around the iron-rich and eutectic Si phases, dissolving the oxide film on the surface, and causing corrosion.The iron-rich phase AlFeSi, AlFe particles, and eutectic Si phase act as cathodic phases, forming a potential difference with the adjacent aluminum matrix and generating many micro-galvanic cells, resulting in galvanic corrosion.result, the α-Al matrix preferentially dissolves near the second-phase particles.Figure 14 describes the corrosion mechanism of the Al-10Si-3.5Fecoating alloy.The alloy is exposed to an environment rich in corrosive ions (Cl − ), penetrating the aluminum matrix through the defect points around the iron-rich and eutectic Si phases, dissolving the oxide film on the surface, and causing corrosion.The iron-rich phase AlFeSi, AlFe particles, and eutectic Si phase act as cathodic phases, forming a potential difference with the adjacent aluminum matrix and generating many micro-galvanic cells, resulting in galvanic corrosion.

Electrochemical Analysis of Coating Alloys
The electrochemical behavior of the Al-xSi-3.5Fealloys in 3.5 wt.% NaCl solution was tested, and the results showed that as the Si content increased, the electrode potential of the alloy first rose and then fell, the corrosion rate decreased initially and then increased, and the corrosion resistance first rose and then fell.When the Si content is 4 wt.%, the alloy has the strongest corrosion resistance; when the Si content is 10 wt.%, the alloy has the optimal activity.The research results show that the lower the corrosion potential, the higher the corrosion current density, the faster the corrosion rate, and the better the corresponding alloy activity.
Due to the higher electrode potential of the iron-rich phases (Al6Fe, Al8Fe2Si, and Al9Fe2Si2) and the eutectic Si phase compared to the aluminum matrix, galvanic corrosion occurs.Combined with the microstructure analysis of the corroded coating alloys, without adding Si elements, the iron-rich phase Al3Fe in the alloy mainly accumulates at the grain boundaries.Its electrode potential is higher, forming a significant potential difference with the aluminum alloy surface and activating the alloy to develop local sacrificial anode reactions-the electrode potential drops compared to pure Al.When the Si content is 1 wt.%, the iron-rich phase in the alloy transforms into the ternary alloy compound Al8Fe2Si and the eutectic phase Al-Al8Fe2Si, reducing the potential difference with the matrix and the decreasing galvanic corrosion, improving corrosion resistance and increasing the electrode potential.When the Si content is 2 wt.%, the iron-rich phase in the alloy does not change much.Still, the increase in Si content raises the electrode potential of the aluminum matrix, further reducing the potential difference between the iron-rich phase and the ma-

Electrochemical Analysis of Coating Alloys
The electrochemical behavior of the Al-xSi-3.5Fealloys in 3.5 wt.% NaCl solution was tested, and the results showed that as the Si content increased, the electrode potential of the alloy first rose and then fell, the corrosion rate decreased initially and then increased, and the corrosion resistance first rose and then fell.When the Si content is 4 wt.%, the alloy has the strongest corrosion resistance; when the Si content is 10 wt.%, the alloy has the optimal activity.The research results show that the lower the corrosion potential, the higher the corrosion current density, the faster the corrosion rate, and the better the corresponding alloy activity.
Due to the higher electrode potential of the iron-rich phases (Al 6 Fe, Al 8 Fe 2 Si, and Al 9 Fe 2 Si 2 ) and the eutectic Si phase compared to the aluminum matrix, galvanic corrosion occurs.Combined with the microstructure analysis of the corroded coating alloys, without adding Si elements, the iron-rich phase Al 3 Fe in the alloy mainly accumulates at the grain boundaries.Its electrode potential is higher, forming a significant potential difference with the aluminum alloy surface and activating the alloy to develop local sacrificial anode reactions-the electrode potential drops compared to pure Al.When the Si content is 1 wt.%, the iron-rich phase in the alloy transforms into the ternary alloy compound Al 8 Fe 2 Si and the eutectic phase Al-Al 8 Fe 2 Si, reducing the potential difference with the matrix and the decreasing galvanic corrosion, improving corrosion resistance and increasing the electrode potential.When the Si content is 2 wt.%, the iron-rich phase in the alloy does not change much.Still, the increase in Si content raises the electrode potential of the aluminum matrix, further reducing the potential difference between the iron-rich phase and the matrix.At the same time, the aggregation of iron-rich phases in the microstructure minimizes the tendency of aluminum alloys towards galvanic corrosion, which promotes electrode potential and improves corrosion resistance.When the Si content is 4 wt.%, the number of Al 8 Fe 2 Si phases significantly decreases, while Al 9 Fe 2 Si 2 phases are generated along with a small amount of eutectic Si phase.The overall potential difference shrinks, galvanic corrosion slows down, and the electrode potential drops.When the Si content is 10 wt.%, a large number of Al 9 Fe 2 Si 2 and eutectic Si phases are generated in the alloy, both of which act as cathode phases in the aluminum matrix, forming more corrosion micro-galvanic cells with greater potential differences, accelerating galvanic corrosion of the coating alloy and causing the electrode potential to drop.
The change trend in the corrosion rate measured after the full immersion experiment is consistent with the change trend in the corrosion rate calculated based on the corrosion current, indicating that the change in corrosion resistance of the alloy is the same as the electrochemical results.However, the corrosion rate measured after the full immersion experiment is lower than the corrosion rate calculated based on the corrosion current, because the immersion experiment is the result of long-term testing, and the corrosion products peeling off and the uneven surface structure of the alloy during the immersion process lead to different corrosion rates.

Conclusions
Al-xSi-3.5Fealloys were analyzed using SEM, X-ray diffraction, and electrochemical experiments in this research.The effects of different Si contents on the microstructure and electrochemical properties of Al-xSi-3.5Fealloys were studied.The conclusions are as follows: 1.
α-Al and iron-rich phases exist in Al-xSi-3.5Fecoatings with different Si contents.As the Si content increases, the iron-rich phase transforms from Al 3 Fe, Al 6 Fe to Al 8 Fe 2 Si, and finally to Al 9 Fe 2 Si 2 .When the Si content exceeds 4 wt.%, the excess Si forms an eutectic silicon phase with the aluminum matrix.

2.
The electrode potential of the alloy first rises and then falls with the increasing Si content, and the corrosion resistance follows the same trend.The sacrificial anode performance is the best when the Si content is 10 wt.%.

3.
The corrosion mode of the Al-xSi-3.5Fealloys is galvanic corrosion.When the Si content is below 4 wt.%, the iron-rich phase acts as the cathode phase and forms micro-galvanic cells with the aluminum matrix.When the Si content is above 4 wt.%, the eutectic silicon phase acts as the cathode phase, forming micro-galvanic cells with the aluminum matrix and iron-rich phase.4.
These findings are of great significance for optimizing the performance of the Al-xSi-3.5Fealloy for hot-dip aluminum in industrial applications.The follow-up research can investigate the electrochemical performance of the alloy under different concentrations of Cl ions.Institutional Review Board Statement: Not applicable.

Figure 6
Figure6shows the SEM image and corresponding element distribution of Al-10Si-3.5Fealloy after corrosion.Based on the enrichment of the Fe and Si elements, these phases were eutectic Si and Al 9 Fe 2 Si 2 , consistent with the results of the previous phase analysis.From the distribution of black corrosion areas, it can be determined that the corrosion pits are located in the middle of the eutectic Si phase and Al 9 Fe 2 Si 2 phase.The eutectic Si and Al 9 Fe 2 Si 2 formed a galvanic cell with the aluminum matrix, resulting in galvanic corrosion.The content of O and Cl elements in the corrosion area was very high, indicating the deposition of corrosion products such as hydroxide and chloride on the surface of the alloy.
To study the effect of Si content on the electrochemical behavior of the Al-xSi-3.5Fecoating alloy, electrochemical corrosion tests were carried out on alloys with different compositions at 25 • C. The electrochemical behaviors are shown in Figures9-12 .

6 .
It was confirmed by the XPS database (NIST) that the Al 2p3/2 spectrum mainly consists of the Al 3+ valence state, and only the Al2O3•H2O peak existed.The O 1s spectrum was the OH − peak, corresponding to the corrosion products of hydroxide, with Al(OH)3 accounting for the highest proportion.The Fe 2p3/2 spectrum of alloy corrosion products had peaks at 710.5 eV and 715.4 eV, corresponding to Fe 2+ and Fe 3+ , respectively.The Cl − peak at approximately 198.6 eV corresponds to Cl 2p3/2, which reacted with Fe 2+ to form the corrosion product FeCl2.

Figure 8 .
Figure 8. High-resolution X-ray photoelectron spectroscopy of corrosion products of Al-10Si-3.5Fealloy.The black line represents the raw data, the red line represents the fitted data and the blue line represents the background.

Figure 8 .
Figure 8. High-resolution X-ray photoelectron spectroscopy of corrosion products of Al-10Si-3.5Fealloy.The black line represents the raw data, the red line represents the fitted data and the blue line represents the background. .

Figure 14 .
Figure 14.Schematic diagram of the local corrosion of the Al-10Si-3.5Fesample.

Figure 14 .
Figure 14.Schematic diagram of the local corrosion of the Al-10Si-3.5Fesample.

Author Contributions:
Conceptualization, Y.W. and Y.S.; Methodology, Y.W.; Validation, Y.W.; Formal analysis, Y.L. (Yuhang Liu), Y.S and Q.W.; Data curation, Y.W. and Q.W. and D.S.; Writing-original draft, Y.W., Y.L. (Yuhang Liu) and Q.W.; Writing-review & editing, D.S. and X.S.; Supervision, Y.L. (Ya Liu); Project administration, X.S.; Funding acquisition, X.S.All authors have read and agreed to the published version of the manuscript.Funding: The authors gratefully acknowledge the financial support from the National Science Foundation of China [No.52171003] and a project funded by the Priority Academic Program Development of Jiangsu higher education institutions are greatly acknowledged.