Impact of Sintering Temperature Variation on Porous Structure of Mo2TiAlC2 Ceramics

Mo, TiH2, Al and graphite elemental powders were used as starting materials for the activation reaction sintering process, which was employed to fabricate porous Mo2TiAlC2. The alteration of phase constitution, volume expansion, porosity, pore size and surface morphology of porous Mo2TiAlC2 with sintering temperatures ranging from 700 °C to 1500 °C were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and pore size tester. Both the pore formation mechanism and activation reaction process at each temperature stage were investigated. The experimental results illustrate that the sintered discs of porous Mo2TiAlC2 exhibit obvious volume expansion and pore structure change during the sintering process. Before 1300 °C, the volume expansion rate and porosity increase with the increment of temperature. However, with the sintering temperature above 1300 °C, the volume expansion rate and porosity decrease. At the final sintering temperature of 1500 °C, porous Mo2TiAlC2 with a volume expansion rate of 35.74%, overall porosity of 47.1%, and uniform pore structure was synthesized. The pore-forming mechanism of porous Mo2TiAlC2 is discussed, and the evolution of pressed pores, the removal of molding agents, the decomposition of TiH2, and the Kirkendall effect caused by different diffusion rates of elements in the diffusion reaction are all accountable for the formation of pores.


Introduction
MAX phases are compounds with the general formula M n+1 AX n (n = 1-6), where M represents a transition metal, A represents a main group element, and X is either C or N [1][2][3][4][5]. In the MAX phase, the M atom and the X atom are combined by a covalent bond and ionic bond, and the M atom and the A atom are combined by a metal bond. Because of their distinct structure makeup, MAX phase compounds grant the characteristics of both ceramics and metals, including high modulus, low specific gravity, good thermal conductivity, machinability, thermal shock resistance, damage tolerance, thermal stability, creep resistance and oxidation resistance [6][7][8][9].
As further research on MAX phase materials is conducted, more and more new MAX phases have been investigated. In 2014, Liu et al. [10] first discovered and successfully prepared Cr 2 TiAlC 2 . Then, Caspi et al. [11] successfully prepared V 2 CrAlC 2 . The discovery of these new phases broadens the field of the MAX phase. Cr 2 TiAlC 2 and V 2 CrAlC 2 can be summarized as a kind of quaternary MAX phase (M , M ) n+1 AX n , and the elements in the M position of this kind of quaternary MAX phase are composed of two transition elements, which may have better performance [12]. Since the new layered quaternary ceramic Mo 2 TiAlC 2 was reported, its highly ordered structure has attracted a lot of attention [13].
Gao et al. [14] successfully synthesized Mo 2 TiAlC 2 . The elastic, thermodynamic and optical properties of Mo 2 TiAlC 2 were studied by first-principles calculations, and the evidence of excellent stability of Mo 2 TiAlC 2 was successfully obtained. Anasori et al. [15] prepared Mo 2 TiAlC 2 by mixing and heating different elemental powder mixtures and found that it had stable structure and excellent electrical conductivity. Ma et al. [16] explored the structure, elastic and electronic properties, Debye temperature and theoretical Vickers hardness of Mo 2 TiAlC 2 by first principles, and they pointed out that it had significant elastic anisotropy. At the same time, the corresponding derivative MXene phase Mo 2 TiC 2 has also been widely studied. By preparing Mo 2 TiC 2 MXene-supported Ru clusters, Wu et al. [17] claimed that it had significant broadband sunlight absorption capacity, high sintering resistance, and good catalytic ability. In addition, Gao et al. [18] also pointed out that Mo 2 TiC 2 MXene exhibited effective N 2 affinity and high catalytic activity for electrocatalytic ammonia synthesis.
The above research indicates that the Mo 2 TiAlC 2 MAX phase and its corresponding etching product Mo 2 TiC 2 MXene have excellent mechanical and electrical properties. However, the influence of pore structure on such properties in porous materials is also one of the factors that cannot be ignored. Maughan et al. [19] prepared layered porous Mo 2 TiC 2 MXene by an amine-assisted silicon pillar method, which has a very high specific surface area and enhances the cycling performance of lithium-ion storage. In the research of Yu et al. [20], porous Ni-Cu alloy, which was synthesized by step sintering, exhibited a good electrochemical activation energy of 26.7 kJ mol −1 . They believed that the microporous structure and the synergistic effect of Ni and Cu jointly contribute to this phenomenon. Wu et al. [21] studied the long-term HER activity of porous Ni 3 Al-Mo in a 6 M KOH solution, and they found that porous Ni 3 Al-Mo electrodes had high surface roughness, which was a key factor for enhancing the hydrogen evolution performance. Zhang et al. [22] prepared porous nickel-titanium alloy using the one-step spark plasma sintering (SPS) method. In their research, as the porosity and pore size increase, the elastic modulus and compressive strength of porous Ni-Ti alloy decrease. This porous material with interconnected pore characteristics, pure phase composition, and low elastic modulus is an ideal candidate for long-term load-bearing hard tissue implants. In our previous study [23], porous Ni-Sn alloy was prepared by activation reaction method and the HER performance was studied. With the increase in Ni content, the porosity showed a trend of first decreasing and then increasing, and the electrochemical active surface area (ECSA) of the electrode also showed the same changing trend. The experimental results revealed that Ni-45%Sn, which had the largest ECSA, displayed the best HER performance. Therefore, this is effective evidence that the pore structure parameter of porous materials is one of the important factors affecting the related electrochemical performance. Given this result, in this article, we do not pay too much attention on the influence of pore structure parameters on electrochemical performance and will focus on the changes in pore structure parameters and the phase transitions.
In the previous study, porous Mo 2 TiAlC 2 ceramics were prepared by activation reaction sintering method, and the effect of Al content on pore structures was also investigated [24]. Given the excellent performance of Mo 2 TiAlC 2 in oxidation resistance and other aspects, the introduction of porous structure allows for not only exploring the formation process of Mo 2 TiAlC 2 from the perspective of phase transition but also observing this process from the perspective of pore structure. What is more, the follow-up product of Mo-based MAX, Mo-based MXene, shows excellent performance in the field of catalysis [17,18,25], and the introduction of porous structure also increases the specific surface area, which can provide more active sites, thus further improve the catalytic activity. In this paper, the effects of different sintering temperatures on pore structure evolutions and phase transformation of the Mo 2 TiAlC 2 system are discussed. Furthermore, the pore-forming mechanism during the sintering process is described as well.

Experimental Preparation
In the preparation procedure of this experiment, Mo (purity 99.6%), TiH 2 (purity 99.6%), Al (purity 99.5%) and graphite powder (purity 99.8%) with particle size of 38-74 µm were selected as experimental raw materials, which were mixed at a molar ratio of 2:1:1.3:2. In addition, 5% stearic acid was added into the mixture to facilitate the compression molding. The mixture was subsequently mixed in an omnidirectional planetary ball mill utilizing settings of 400 r/min and an effective mixing length of 6 h, with a 2:1 ratio of zirconia ball to the material. The mixed powders were cold pressed under a pressure of 160 MPa to form Φ25 mm × H2 mm green compacts. Finally, the green compacts were sintered in a vacuum furnace at 1.2 × 10 −3 Pa under the procedures shown in Figure 1. In order to study the effect of sintering temperature on the evolution of pore structure and phase transformation process of the Mo 2 TiAlC 2 system, the sintering temperature was gradually increased from 700 • C to 1500 • C, with a temperature increment of 200 • C, and holding each temperature for 2 h. The 120 • C and 360 • C temperatures were held for one hour each to remove the remaining water in the vacuum furnace and stearic acid in the pressed discs.

Experimental Preparation
In the preparation procedure of this experiment, Mo (purity 99.6%), TiH2 (pu 99.6%), Al (purity 99.5%) and graphite powder (purity 99.8%) with particle size of 38 µm were selected as experimental raw materials, which were mixed at a molar ratio 2:1:1.3:2. In addition, 5% stearic acid was added into the mixture to facilitate the compr sion molding. The mixture was subsequently mixed in an omnidirectional planetary b mill utilizing settings of 400 r/min and an effective mixing length of 6 h, with a 2:1 ratio zirconia ball to the material. The mixed powders were cold pressed under a pressure 160 MPa to form Φ25 mm × H2 mm green compacts. Finally, the green compacts w sintered in a vacuum furnace at 1.2 × 10 −3 Pa under the procedures shown in Figure 1 order to study the effect of sintering temperature on the evolution of pore structure a phase transformation process of the Mo2TiAlC2 system, the sintering temperature w gradually increased from 700 °C to 1500 °C, with a temperature increment of 200 °C, a holding each temperature for 2 h. The 120 °C and 360 °C temperatures were held for o hour each to remove the remaining water in the vacuum furnace and stearic acid in pressed discs. The size of the round press compacts was measured with vernier calipers before, a after sintering, then the volume expansion was calculated. X-ray diffractometer (XR Dmax 2500VB, Rigaku Corp, Tokyo, Japan) was used to analyze the phase transition a composition of porous Mo2TiAlC2 samples at different sintering temperatures with a s rate of 2°/min and a step size of 0.02°. Scanning electron microscopy (SEM, Zeiss SIGM Field Emission SEM, Germany) was introduced to characterize the pore structures of sintered samples. The bubble point method was utilized to determine pore size [26]. Op porosity and overall porosity were measured by the Archimedes method [27]. On the ba of the standard of DIN EN ISO 4022:2006 [28], the porometer was used to measure nit gen permeability at 23 °C. In addition, a pore size tester was introduced to meas Mo2TiAlC2 samples at different sintering temperatures to explore the development law pore structure. The size of the round press compacts was measured with vernier calipers before, and after sintering, then the volume expansion was calculated. X-ray diffractometer (XRD; Dmax 2500VB, Rigaku Corp, Tokyo, Japan) was used to analyze the phase transition and composition of porous Mo 2 TiAlC 2 samples at different sintering temperatures with a scan rate of 2 • /min and a step size of 0.02 • . Scanning electron microscopy (SEM, Zeiss SIGMA Field Emission SEM, Germany) was introduced to characterize the pore structures of the sintered samples. The bubble point method was utilized to determine pore size [26]. Open porosity and overall porosity were measured by the Archimedes method [27]. On the basis of the standard of DIN EN ISO 4022:2006 [28], the porometer was used to measure nitrogen permeability at 23 • C. In addition, a pore size tester was introduced to measure Mo 2 TiAlC 2 samples at different sintering temperatures to explore the development law of pore structure.

X-ray Diffraction Analysis (XRD)
In order to explore the effect of different sintering temperatures on the phase composition of porous Mo 2 TiAlC 2 ceramics, the sintered specimens ranging from 700 • C to 1500 • C are subjected to XRD analysis, and the tested results are shown in Figure 2. At 700 • C, there are just four single phases (Mo, Ti, Al and C), indicating that TiH 2 has fully decomposed and that the initial components have not interacted. At a sintering temperature of 900 • C, the AlMo 3 phase and TiC phase first appears, while the pure Ti and Al phases disappear. At this time, four phases (Mo, AlMo 3 , TiC and C) are present, with the AlMo 3 phase being the primary phase and the peak intensity of Mo diminishing. Mo 2 C phase and TiAl are clearly visible when the sintering temperature rises to 1100 • C constantly, while the Mo phase is depleted. There are now five phases (Mo 2 C, TiC, AlMo 3 , TiAl and C), with the Mo 2 C and TiC phases serving as the primary phases. When the temperature is further raised to 1300 • C, there are five phases, namely Mo 2 C, TiC, AlMo 3 , Mo 3 Al 2 C and Mo 2 TiAlC 2 . At this point, Mo 2 C, TiC and Mo 3 Al 2 C are the main phases, and the peak strength is enhanced. Concurrently, the C (graphite) phase vanishes, and a large number of Mo 3 Al 2 C and Ti 2 AlC peak phases emerge, along with a small amount of Mo 2 TiAlC 2 peak phase as minor components. When the temperature rises to 1500 • C, the pure phase Mo 2 TiAlC 2 , whose size of a coherent scattering region is estimated as D 104 = 63.9 nm, is finally obtained.

X-ray Diffraction Analysis (XRD)
In order to explore the effect of different sintering temperatures on the phase composition of porous Mo2TiAlC2 ceramics, the sintered specimens ranging from 700 °C to 1500 °C are subjected to XRD analysis, and the tested results are shown in Figure 2. At 700 °C, there are just four single phases (Mo, Ti, Al and C), indicating that TiH2 has fully decomposed and that the initial components have not interacted. At a sintering temperature of 900 °C, the AlMo3 phase and TiC phase first appears, while the pure Ti and Al phases disappear. At this time, four phases (Mo, AlMo3, TiC and C) are present, with the AlMo3 phase being the primary phase and the peak intensity of Mo diminishing. Mo2C phase and TiAl are clearly visible when the sintering temperature rises to 1100 °C constantly, while the Mo phase is depleted. There are now five phases (Mo2C, TiC, AlMo3, TiAl and C), with the Mo2C and TiC phases serving as the primary phases. When the temperature is further raised to 1300 °C, there are five phases, namely Mo2C, TiC, AlMo3, Mo3Al2C and Mo2TiAlC2. At this point, Mo2C, TiC and Mo3Al2C are the main phases, and the peak strength is enhanced. Concurrently, the C (graphite) phase vanishes, and a large number of Mo3Al2C and Ti2AlC peak phases emerge, along with a small amount of Mo2TiAlC2 peak phase as minor components. When the temperature rises to 1500 °C, the pure phase Mo2TiAlC2, whose size of a coherent scattering region is estimated as D104 = 63.9 nm, is finally obtained. In order to conveniently observe the phase transformation of samples from 700 °C to 1500 °C, the phases present at each temperature stage are summarized in Table 1. The reaction processes at various sintering temperatures are analyzed according to the phase changes. At 700 °C, TiH2 is completely decomposed, and a titanium phase appears. At this time, the rest of the substances do not react significantly, and the main phases are the elemental powders. Sintering at 900 °C leads to the formation of AlMo3, which results from the reaction of melted aluminum with certain amounts of molybdenum, and a small amount of Ti reacts with graphite to generate TiC at the same time. At a sintering temperature of 1100 °C, graphite reacts with molybdenum to form Mo2C, while TiAl is formed by the reaction of molten aluminum with a certain amount of titanium. At 1300 °C, Ti2AlC is generated by the reaction of TiC and TiAl, while Mo2C and MoAl3 not only react with In order to conveniently observe the phase transformation of samples from 700 • C to 1500 • C, the phases present at each temperature stage are summarized in Table 1. The reaction processes at various sintering temperatures are analyzed according to the phase changes. At 700 • C, TiH 2 is completely decomposed, and a titanium phase appears. At this time, the rest of the substances do not react significantly, and the main phases are the elemental powders. Sintering at 900 • C leads to the formation of AlMo 3 , which results from the reaction of melted aluminum with certain amounts of molybdenum, and a small amount of Ti reacts with graphite to generate TiC at the same time. At a sintering temperature of 1100 • C, graphite reacts with molybdenum to form Mo 2 C, while TiAl is formed by the reaction of molten aluminum with a certain amount of titanium. At 1300 • C, Ti 2 AlC is generated by the reaction of TiC and TiAl, while Mo 2 C and MoAl 3 not only react with each other to yield Mo 3 Al 2 C but also react with graphite to form Mo 2 TiAlC 2 . When the temperature rises to 1500 • C, only the pure substance Mo 2 TiAlC 2 exists, signifying the complete reaction of all intermediate species to generate Mo 2 TiAlC 2 . The reaction of Mo 2 TiAlC 2 with increasing temperature is summarized below, and the reaction process is illustrated in Figure 3.

Effects of Temperature on Volume Evolution
The diameter and height of the compact before and after sintering were repeatedly measured by a vernier caliper, and the volume and size changes of the discs were calculated. As shown in Figure 4, with the increase in sintering temperature from 700 • C to 1500 • C, the volume and axial and radial expansion rate of the compact first increase and then decrease. The volume expansion rate keeps growing as the temperature increases from 700 • C to 1300 • C, quickly rising from 18.90% to 38.72%. This phenomenon arises as a result of the fact that when the temperature rises, chemical interactions between substances intensify, intermediate products undergo a constant transformation and an enormous number of pores are subsequently created. When the temperature rises to 1500 • C, the volume expansion rate decreases to 35.74%. This is because the Mo 2 TiAlC 2 phase is finally formed at this stage and densifies at high temperatures.

Effects of Temperature on Volume Evolution
The diameter and height of the compact before and after sintering were repeatedly measured by a vernier caliper, and the volume and size changes of the discs were calculated. As shown in Figure 4, with the increase in sintering temperature from 700 °C to 1500 °C, the volume and axial and radial expansion rate of the compact first increase and then decrease. The volume expansion rate keeps growing as the temperature increases from 700 °C to 1300 °C, quickly rising from 18.90% to 38.72%. This phenomenon arises as a result of the fact that when the temperature rises, chemical interactions between substances intensify, intermediate products undergo a constant transformation and an enormous number of pores are subsequently created. When the temperature rises to 1500 °C, the volume expansion rate decreases to 35.74%. This is because the Mo2TiAlC2 phase is finally formed at this stage and densifies at high temperatures.

Pore Structure Parameters
Pore structure parameters, including porosity, pore size and permeability, are significant for porous materials; therefore, further exploration helps to study the pore structure and phase changes of porous materials. Figure 5 depicts the trend in pore structural parameters, as it can be seen that the overall porosity is highly similar to open porosity. With the sintering temperature increases from 700 °C to 1300 °C, the porosity increases rapidly from 26.4% to 56.3%. What is worth noting is that the porosity shows a decreasing trend from 1300 °C to 1500 °C, from 56.3% to 47.1%.
Comparing the trend of volume expansion rate in Figure 4, the change of porosity and expansion rate tends to be consistent. In the research of Jiang. et al. [29], the relationship between the volume expansion and the open porosity can be expressed as: where and are the theoretical densities of the compact before and after the sintering, is the initial overall porosity in green compacts, is the open porosity after the sintering, is the volume expansion ratio and is the closed porosity in the sintered compact. Through the data fitting calculation displayed in Figure 6, it is evident that the trend of change between the two curves is almost proportional.

Pore Structure Parameters
Pore structure parameters, including porosity, pore size and permeability, are significant for porous materials; therefore, further exploration helps to study the pore structure and phase changes of porous materials. Figure 5 depicts the trend in pore structural parameters, as it can be seen that the overall porosity is highly similar to open porosity. With the sintering temperature increases from 700 • C to 1300 • C, the porosity increases rapidly from 26.4% to 56.3%. What is worth noting is that the porosity shows a decreasing trend from 1300 • C to 1500 • C, from 56.3% to 47.1%.
Comparing the trend of volume expansion rate in Figure 4, the change of porosity and expansion rate tends to be consistent. In the research of Jiang. et al. [29], the relationship between the volume expansion and the open porosity can be expressed as: where ρ 0 and ρ are the theoretical densities of the compact before and after the sintering, θ 0 is the initial overall porosity in green compacts, θ p is the open porosity after the sintering, α is the volume expansion ratio and θ c is the closed porosity in the sintered compact.
Through the data fitting calculation displayed in Figure 6, it is evident that the trend of change between the two curves is almost proportional.    Figure 7a illustrates the relationship between pore size and sintering temperature 700 °C, the compact displays a large pore size parameter, which is attributed to the composition of TiH2. When the temperature reaches 900 °C, the interaction of the slow diffusing Mo with the melting Al to produce AlMo3 causes the pore size to shrink s stantially. After that, a considerable number of pores form at their starting locations a consequence of the reaction of several intermediate products (Mo2C, TiC, AlMo3, Mo3A Ti2AlC and Mo2TiAlC2), and the pore size increases rapidly between 900 and 1300 °C a  Figure 7a illustrates the relationship between pore size and sintering temperature. At 700 • C, the compact displays a large pore size parameter, which is attributed to the decomposition of TiH 2 . When the temperature reaches 900 • C, the interaction of the slowly diffusing Mo with the melting Al to produce AlMo 3 causes the pore size to shrink substantially. After that, a considerable number of pores form at their starting locations as a consequence of the reaction of several intermediate products (Mo 2 C, TiC, AlMo 3 , Mo 3 Al 2 C, Ti 2 AlC and Mo 2 TiAlC 2 ), and the pore size increases rapidly between 900 and 1300 • C as a result. However, at 1500 • C, the compact exhibits slight densification, leading to shrinkage of internal pores and, finally, a decrease in pore size.  Figure 8 illustrates the surface morphology of the sintered compacts at different temperatures. It can be seen that at 700 °C, the sample is composed of irregular particles squeezed into each other, and there are a lot of pores between particles. A small amount of layered structure formed on the surface of the sample at 900 °C as a result of the reaction of Mo with melted Al to generate AlMo3. When the temperature reaches 1100 °C, the reactions intensify, and particles further connect with one another, resulting in a gradually smooth surface and a more pronounced layer structure. The particles are completely bound at 1300 °C, creating a laminated surface that is neatly polished. The porous Mo2TiAlC2 ceramic eventually displays a lamellar surface with a substantial number of pores, which show a rather uniform distribution and even pore size at the final sintering temperature of 1500 °C. It can be clearly found that the permeability of the sample is linearly correlated with the pressure in Figure 7b. At the same time, the permeability also increases gradually with the increase in temperature and slightly decreases at the final sintering temperature of 1500 • C. Figure 8 illustrates the surface morphology of the sintered compacts at different temperatures. It can be seen that at 700 • C, the sample is composed of irregular particles squeezed into each other, and there are a lot of pores between particles. A small amount of layered structure formed on the surface of the sample at 900 • C as a result of the reaction of Mo with melted Al to generate AlMo 3 . When the temperature reaches 1100 • C, the reactions intensify, and particles further connect with one another, resulting in a gradually smooth surface and a more pronounced layer structure. The particles are completely bound at 1300 • C, creating a laminated surface that is neatly polished. The porous Mo 2 TiAlC 2 ceramic eventually displays a lamellar surface with a substantial number of pores, which show a rather uniform distribution and even pore size at the final sintering temperature of 1500 • C.

Pore Forming Mechanism
From the initial surface morphology, the pressed compact is composed of irregular mixed raw powders, with a large number of retained pores between the powder particles. Combined with the XRD phase constitution analysis, it is obvious that TiH 2 decomposes completely at 700 • C. At the same time, during the preparation stage, in order to make the mixed powders to be pressed smoothly in the mold, the molding agent stearic acid is added to the mixed powders, which is removed at high temperature, resulting in a significant number of pores as well. As the temperature rises to 900 • C, Mo reacts with melted Al to form AlMo 3 . During the formation of AlMo 3 intermetallics, due to the diffusion rate of Al being significantly higher than that of Mo [30], the diffusion of Al is dominant, and a large number of pores are produced by the Kirkendall effect [31]. Therefore, when the temperature is lower than 900 • C, the formation of pores is mainly caused by the decomposition of TiH 2 and the partial diffusion of Al in the Kirkendall effect. Based on Figures 4 and 5, when the temperature rises from 700 • C to 900 • C, the volume expansion rate of the sample increases from 18.9% to 23.6%, with an increase of 29%, while the overall porosity increases from 26.4% to 31.2%, with an increase of 18.2%. At temperatures between 900 • C and 1100 • C, in addition to the TiAl and Mo-Al compounds formed by the Kirkendall effect [32], the formation of carbides TiC and Mo 2 C also promotes the formation of pores. At this stage, the growth rate of the corresponding volume expansion rate is 29.2%, and the overall porosity is 31.1%, both of which are greater than the growth rate from 700 • C to 900 • C. As the temperature continues to rise, between 1100 • C and 1300 • C, with the formation of carbides, MAX also begins to appear at this stage. At this point, the changes in volume expansion rate and overall porosity are 26.9% and 27.9%, respectively, with the variation in porosity still greater than the variation from 700 to 900 • C. Finally, when the temperature rises to 1500 • C, the previously generated intermediate products further participate in the reaction, resulting in the formation of pure phase Mo 2 TiAlC 2 . At the same time, the sample becomes denser, leading to a reduction in pores. Therefore, we can draw a conclusion that in order to control the pore structure of porous Mo 2 TiAlC 2 , controlling the sintering process between 900 and 1300 • C is crucial.

Pore Forming Mechanism
From the initial surface morphology, the pressed compact is composed of irregular mixed raw powders, with a large number of retained pores between the powder particles. Combined with the XRD phase constitution analysis, it is obvious that TiH2 decomposes completely at 700 °C. At the same time, during the preparation stage, in order to make the mixed powders to be pressed smoothly in the mold, the molding agent stearic acid is added to the mixed powders, which is removed at high temperature, resulting in a significant number of pores as well. As the temperature rises to 900 °C, Mo reacts with melted Al to form AlMo3. During the formation of AlMo3 intermetallics, due to the diffusion rate of Al being significantly higher than that of Mo [30], the diffusion of Al is dominant, and a large number of pores are produced by the Kirkendall effect [31]. Therefore, when the temperature is lower than 900 °C, the formation of pores is mainly caused by the decomposition of TiH2 and the partial diffusion of Al in the Kirkendall effect. Based on Figures  4 and 5, when the temperature rises from 700 °C to 900 °C, the volume expansion rate of the sample increases from 18.9% to 23.6%, with an increase of 29%, while the overall porosity increases from 26.4% to 31.2%, with an increase of 18.2%. At temperatures between 900 °C and 1100 °C, in addition to the TiAl and Mo-Al compounds formed by the Kirken-

Conclusions
(1) Porous Mo 2 TiAlC 2 ceramic is prepared by activation reaction sintering of Mo, Ti, Al and graphite powders at a ratio of 2:1:1.1:2. In addition, the final sintering temperature is 1500 • C, resulting in an expansion rate of 35.74% and a porosity of 47.1%.
(2) The pore-forming mechanism of porous Mo 2 TiAlC 2 ceramic involves the evolution of the pressed pores, the removal of the molding agent, the decomposition of TiH 2 and the Kirkendall effect caused by the different diffusion rates of Mo, Ti, Al and C powders and a serious reaction of intermediates during the diffusion process. Firstly, TiH 2 decomposes at 700 • C. As the temperature progressively rises, the molten Al will combine with Ti and Mo to create TiAl compounds and MoAl compounds, accompanied by the appearance of a small number of carbides. When the temperature continues to rise, the carbides react to the intermetallic complexes TiAl and MoAl to produce the respective intermediate products, Ti-Al-C and Mo-Al-C, which then combine to form the pure Mo 2 TiAlC 2 at the final sintering temperature of 1500 • C.