Study on the Microstructure and Magnetic Properties of Nd-Fe-B/Fe-Co Composite Nanowires

To solve the problem of the low coercivity of Nd-Fe-B-based nanowires impeding their application in magnetic storage media, highly ordered Nd-Fe-B/Fe-Co composite nanowires were fabricated in an anodic alumina template by means of the alternating electrochemical deposition method. In this paper, the effect of soft and hard magnetic phase compositing on the magnetic properties of Nd-Fe-B-based nanowires was investigated, and the coercivity improvement mechanism was demonstrated. The results show that after annealing at 600 °C for 2 h, Nd-Fe-B/Fe-Co nanowires crystallize into a multiphase structure containing a hard Nd2(Fe, Co)14B phase and soft NdB4, NdB6, Fe7Nd, and Fe7Co3 phases. It is characterized that the Nd2(Fe, Co)14B phase preferentially nucleates, followed by NdB4 + NdB6 + Fe7Nd, while Fe7Co3 has been formed in as-deposited nanowires. The existence of a Nd2(Fe, Co)14B phase with high anisotropy fields, the remanence enhancement effect produced by exchange coupling between hard–soft magnetic phases, and the pinning effect between different phases make the composite nanowires approximately exhibit single hard magnetic phase characteristics with coercivity and remanence ratio as high as 4203.25 Oe and 0.89. The results indicate that synthesizing Nd-Fe-B/Fe-Co exchange-coupled composite nanowires via alternating electrodeposition is an effective way to optimize the magnetic performance of Nd-Fe-B-based nanowires.


Introduction
Magnetic nanowires with large aspect ratios and apparent shape anisotropy are one of the research focuses in the new magnetic functional materials field, which has good application prospects in high-density linear magnetic storage media.As the third-generation rare earth magnets, Nd-Fe-B has outstanding magnetic properties that other materials cannot surpass.However, the low coercivity of currently manufactured Nd-Fe-B nanowires hinders their application in magnetic storage [1][2][3].Therefore, how to prepare Nd-Fe-Bbased nanowires with high magnetism has certain theoretical significance for developing new-generation vertical magnetic storage media.There has been a great deal of research on how to improve the hard magnetism of Nd-Fe-B nanowires through doping alloy elements [4][5][6][7][8][9][10][11].In order to be better suitable for high-density linear perpendicular magnetic recording media, in addition to improving the coercivity of Nd-Fe-B nanowires, higher saturation magnetization should be expected to enhance their storage density.
The fabrication of nanocrystalline composites is an effective method to obtain both high coercivity and high saturation magnetization, which could obtain high magnetic energy products through the exchange coupling of hard-soft magnetic phases [12][13][14][15].Fe-Co alloy is an excellent soft magnetic material that has a high saturation magnetic moment and initial permeability [16][17][18].At the same time, the low coercivity and remanence ratio of soft magnetic materials limits their application in magnetic storage media [19].Mansouri et al. [20] fabricated FeCo and FeNi nanowires with a coercivity of 627 Oe and 279 Oe through electrochemical deposition.Han et al. [21] successfully prepared a series of Fe x Co 1−x (x = 0.0, 0.5, 1.0) nanowires with coercivity in the range of 450 Oe~570 Oe and a squareness of 0.23~0.41.Kaniukov et al. [22] researched the structural and magnetic performances of FeCo-alloy nanotubes deposited under different potentials and found that the nanotubes exhibited more excellent properties with a coercivity of 500 Oe and squareness of 0.2 due to the high crystallinity degree under the higher potential of 2 V.It is observed that most Fe-Co magnetic nanowires exhibit typical soft magnetic properties with low coercivity and a low magnetic energy product.
To simultaneously possess high coercivity and high saturation magnetization, there have been many studies about the combination of Fe-Co and rare earth permanent magnetic alloys.Chuanto et al. [23] fabricated SmCo 5 /FeCo core-shell composite materials, showing how the magnetic energy product of a composite material with 10 wt.% FeCo increased by 25% compared to a single hard magnetic phase SmCo 5 .Cui et al. [24] prepared Sm 2 Co 17 /Fe 7 Co 3 duplex-phase magnetic nanowires with excellent shape anisotropy via alternating electrodeposition.They found that the duplex-phase Sm 2 Co 17 /Fe 7 Co 3 magnetic nanowires have better remanence and coercivity in both annealed and deposited states than Fe 7 Co 3 and Sm 2 Co 17 nanowires.However, research on Nd-Fe-B-based nanocomposites mainly focuses on composites with soft magnetic α-Fe and Fe 3 B phases, currently [25][26][27].Therefore, Nd-Fe-B/Fe-Co composite nanowires are an exciting route to solve the low coercivity of Nd-Fe-B-based nanowires.
The present work demonstrates an alternating electrochemical deposition for fabricating aligned Nd-Fe-B/Fe-Co composite nanowires within AAO templates.It is expected that a Nd-Fe-B/Fe-Co hybrid magnet, which is more suitable for magnetic storage media, can be obtained through soft-hard magnetic exchange coupling.This article also discusses the effect of the Fe-Co alloy on the phase component, microstructure, and properties of the Nd-Fe-B/Fe-Co composite nanowires before and after annealing.Moreover, this article presents the evolution of microstructure phase transition and phase distribution.And finally, it investigates the effects of phase evolution, dislocation, and the coupling of the hard-soft phase exchange on the magnetic performance of Nd-Fe-B/Fe-Co nanowires.

Materials and Methods
The methodology flow chart of this work is illustrated in Figure 1.The detailed procedure is briefly described below.

Synthesizing Process of AAO Template
The highly ordered alumina (AAO) templates used in this experiment were prepared via secondary anodizing in 0.3 mol/L oxalic acid solution under 40 V DC.During the anodization process, the oxidation tanks were placed in an ice-water mixture, preventing the excessive temperature caused by the exothermic reaction from affecting the quality of the oxide film.Between the first (4 h) and second (6 h) anodization, we used chromic acid and phosphoric acid to remove the oxide layer with lower order generated during the first anodization process.Highly ordered AAO templates with a pore size of 70 nm and length of 30 µm were successfully prepared through removing the bottom and reaming (Figure 2).It can be seen that AAO templates contain self-assembled, highly uniform quasi-hexagonal ordered holes.As shown in Figure 2c,d, the pore channels are parallel to each other and perpendicular to the membrane surface.

Synthesizing Process of AAO Template
The highly ordered alumina (AAO) templates used in this experiment were prepared via secondary anodizing in 0.3 mol/L oxalic acid solution under 40 V DC.During the anodization process, the oxidation tanks were placed in an ice-water mixture, preventing the excessive temperature caused by the exothermic reaction from affecting the quality of the oxide film.Between the first (4 h) and second (6 h) anodization, we used chromic acid and phosphoric acid to remove the oxide layer with lower order generated during the first anodization process.Highly ordered AAO templates with a pore size of 70 nm and length of 30 µm were successfully prepared through removing the bottom and reaming (Figure 2).It can be seen that AAO templates contain self-assembled, highly uniform quasi-hexagonal ordered holes.As shown in Figure 2c,d, the pore channels are parallel to each other and perpendicular to the membrane surface.

Electrochemical Deposition of Nd-Fe-B/Fe-Co Composite Nanowires
Before electrodeposition, a thin layer of gold film was plated on the back of the template to improve the conductivity of the alumina template.The deposition was based on graphite as the anode and the AAO template as the cathode, conducted under 2 V DC.

Electrochemical Deposition of Nd-Fe-B/Fe-Co Composite Nanowires
Before electrodeposition, a thin layer of gold film was plated on the back of the template to improve the conductivity of the alumina template.The deposition was based on graphite as the anode and the AAO template as the cathode, conducted under 2 V DC.The alternating deposition was completed through depositing in Fe-Co electrolyte for 1 min followed by Nd-Fe-B electrolyte for 30 min, alternating deposition three times.Table 1 lists the composition of the Fe-Co and Nd-Fe-B solutions.The deposition process was carried out on a magnetic stirrer, and the deposited solution was constantly stirred to accelerate ion diffusion and ensure a uniform concentration of ions in the electrolyte.A portion of the nanowires within the AAO template was then annealed at 600 • C for 2 h in a vacuum heat treatment furnace at a heating rate of 5 • C/min in an atmosphere of 99.99% argon.

Characterization
The phase composition of the samples was analyzed using a Bruker D8 Discover X-ray diffractometer (XRD) (Bruker, Billerica, MA, USA) with Cu kα radiation (λ = 1.5406Å), a voltage of 40 kV, and a current of 20 mA.In the range of 2θ from 20 • to 90 • , the XRD patterns were scanned with a step length of 0.02 • and a scanning rate of 6 • /min.The chemical compositions and morphologies of nanowires with partially dissolved AAO templates were characterized using Quantum 450 FEG scanning electron microscopy (Beijing, China) (SEM) and energy dispersive spectroscopy (EDS).The microstructure of the nanowires was observed using the Tecnai G2 F30 S-TWIN transmission electron microscope (TEM) (Thermo Fisher Scientific, Waltham, MA, USA).The magnetic properties of nanowires in the AAO templates were measured using a Lake Shore 7407 type vibrating sample magnetometer (VSM) in a maximum 15 kOe magnetic field parallel to the long axis of the nanowires.

Phase Analysis
Figure 3a,b show the XRD patterns of Fe-Co, Nd-Fe-B, and Nd-Fe-B/Fe-Co composite nanowire arrays before and after annealing.It can be seen from Figure 3a that the asdeposited Nd-Fe-B/Fe-Co nanowires consist of a Fe 7 Co 3 phase.Compared with Fe-Co nanowires, there is a higher amount of amorphous diffuse scattering peaks in the XRD patterns of Nd-Fe-B and Nd-Fe-B/Fe-Co nanowires, which is due to the existence of a Nd atom with a large radius improving the amorphous forming ability of the nanowires.
Figure 3b shows the XRD patterns of nanowires annealed at 600 • C for 2 h in highpurity Ar.In comparison, the diffraction peak intensity for annealed nanowires increases and half-width decreases, indicating that the grains' size and crystallinity improved after annealing [28].The 600 • C-annealed Nd-Fe-B/Fe-Co nanowires present a complex phase composition containing the newly formed Nd 2 (Fe, Co) 14 B, NdB 4 , NdB 6 , and Fe 7 Nd phases as well as the Fe 7 Co 3 phase existing in as-deposited nanowires.The formation of the Nd 2 (Fe, Co) 14 B phase illustrates that in addition to forming the Fe 7 Co 3 phase with Fe atoms during the alternating electrodeposition process, some Co atoms also enter the Nd 2 Fe 14 B main phase through replacing some Fe atoms during heat treatment.As a result of the substitution of Co (0.126 nm) with a smaller atomic radius for Fe (0.127 nm), lattice contraction occurs in the 2:14:1-type phase according to the Bragg equation, λ = 2dsinθ, leading to the right shift of the 2:14:1-type phase diffraction peak as seen from the example of 204 peaks in the inset of Figure 3b, in which the right shift is approximately 0.4 wherein  and  are the crystallization rates for the phase in nanowires annealed at different temperatures of T1 (570 °C) and T2 (600 °C), respectively.Imaxi is the maximum diffraction peak intensity of each phase in annealed nanowires.The subscript i represents the phase formed during the annealing process, and R is the gas constant (8.314J/(mol•K)).3) to be 29,188.6J/mol, 90,461.4J/mol, 84,392.5 J/mol, 82,220.4J/mol, and −46,742.8J/mol, respectively.The ∆G (Fe7Co3) < 0 indicates that the Fe7Co3 phase can spontaneously nucleate and crystallize, consistent with the XRD results shown in Figure 3a, thus confirming that the Fe7Co3 phase exists in as-deposited nanowires.The generation of other phases in Nd-Fe-B/Fe-Co nanowires must be completed via absorbing the heat annealing process, corresponding to the positive ∆G values.During the multiphase phase transition process, the phase with a smaller energy barrier will preferentially nucleate and grow, then undergo phase transition.According to the thermodynamic calculation results, it can be inferred that the phase nucleation ordering Nd-Fe-B/Fe-Co nanowires during annealing is roughly as follows: a Nd2(Fe, Co)14B phase with the smallest phase transition energy barrier is preferentially formed, followed by Fe7Nd, NdB6, and NdB4 phases.It is noted that the ∆G of the Nd2(Fe, Co)14B phase formed after adding the Co atom is lower than that of the Nd2Fe14B phase, indicating that the addition of Co reduces the precipitation temperature of the 2:14:1-type phase, thus further promoting the precipitation of more 2:14:1-type hard magnetic phases in composite nanowires, which is consistent with the conclusion proposed by Kojima [30].
The XRD results show that the composite nanowires not only retain the soft magnetic Fe7Co3 phase formed in an as-deposited state but also stimulate the generation of greater amounts of the hard magnetic Nd2(Fe, Co)14B phase during the crystallization process.This improves the comprehensive magnetic properties of the nanowires.Assuming that the phase transition process only considers the energy required for phase crystallization without other heat, the phase Gibbs free energy ∆G (i.e., the latent heat of phase transition from amorphous to crystalline) can be considered to be approximately equal to the phase formation enthalpy ∆H.During multiphase structure transformation, it is easier for the phase with smaller ∆G to overcome the energy barrier, then nucleate and grow up, completing phase transition.Based on this, the thermodynamic formula of the Arrhenius Equation can be extended and obtained from the following formulas [29]: wherein k 1i and k 2i are the crystallization rates for the phase in nanowires annealed at different temperatures of T 1 (570 • C) and T 2 (600 • C), respectively.I maxi is the maximum diffraction peak intensity of each phase in annealed nanowires.The subscript i represents the phase formed during the annealing process, and R is the gas constant (8.314J/(mol•K)). Figure 4a,b show the XRD patterns of Nd-Fe-B/Fe-Co and Nd-Fe-B nanowires annealed at temperatures of T 1 (570 • C) and T 2 (600 • C), respectively.Table 2 lists the I max of each phase in nanowires.The ∆G of Nd 2 (Fe, Co) 14 B, NdB 4 , NdB 6 , Fe 7 Nd, and Fe 7 Co 3 phases in Nd-Fe-B/Fe-Co composite nanowires are calculated using Formulas (1)-( 3) to be 29,188.6J/mol, 90,461.4J/mol, 84,392.5 J/mol, 82,220.4J/mol, and −46,742.8J/mol, respectively.The ∆G (Fe 7 Co 3 ) < 0 indicates that the Fe 7 Co 3 phase can spontaneously nucleate and crystallize, consistent with the XRD results shown in Figure 3a, thus confirming that the Fe 7 Co 3 phase exists in as-deposited nanowires.The generation of other phases in Nd-Fe-B/Fe-Co nanowires must be completed via absorbing the heat annealing process, corresponding to the positive ∆G values.During the multiphase phase transition process, the phase with a smaller energy barrier will preferentially nucleate and grow, then undergo phase transition.According to the thermodynamic calculation results, it can be inferred that the phase nucleation ordering Nd-Fe-B/Fe-Co nanowires during annealing is roughly as follows: a Nd 2 (Fe, Co) 14 B phase with the smallest phase transition energy barrier is preferentially formed, followed by Fe 7 Nd, NdB 6, and NdB 4 phases.It is noted that the ∆G of the Nd 2 (Fe, Co) 14 B phase formed after adding the Co atom is lower than that of the Nd 2 Fe 14 B phase, indicating that the addition of Co reduces the precipitation temperature of the 2:14:1-type phase, thus further promoting the precipitation of more 2:14:1-type hard magnetic phases in composite nanowires, which is consistent with the conclusion proposed by Kojima [30].

Morphology and Microstructure
Figure 5 shows the SEM image of Nd-Fe-B/Fe-Co composite nanowire arrays after partial dissociation from the AAO templates using 5 wt.% NaOH solution.As can be seen from Figure 5a, the Nd-Fe-B/Fe-Co composite nanowires are arranged orderly and uniformly throughout the template range, the deposition efficiency is very high, and the template filling rate is nearly 100%.Figure 5b shows the statistical analysis of the nanowires' diameter using Nano Measurer software, illustrating that the average diameter of the Nd-Fe-B/Fe-Co nanowire is 71 nm, which corresponds well to the pore diameter of the AAO template.The lateral-view SEM image shown in Figure 5c displays that the length of the nanowires array is approximately 27.01 µm, and the nanowires stand vertically and parallel to each other under the support of the residual AAO templates.The magnified image on the upper right shows the morphology of the nanowires separated from the template

Specimen
Phase The XRD results show that the composite nanowires not only retain the soft magnetic Fe 7 Co 3 phase formed in an as-deposited state but also stimulate the generation of greater amounts of the hard magnetic Nd 2 (Fe, Co) 14 B phase during the crystallization process.This improves the comprehensive magnetic properties of the nanowires.

Morphology and Microstructure
Figure 5 shows the SEM image of Nd-Fe-B/Fe-Co composite nanowire arrays after partial dissociation from the AAO templates using 5 wt.% NaOH solution.As can be seen from Figure 5a, the Nd-Fe-B/Fe-Co composite nanowires are arranged orderly and uniformly throughout the template range, the deposition efficiency is very high, and the template filling rate is nearly 100%.Figure 5b shows the statistical analysis of the nanowires' diameter using Nano Measurer software, illustrating that the average diameter of the Nd-Fe-B/Fe-Co nanowire is 71 nm, which corresponds well to the pore diameter of the AAO template.The lateral-view SEM image shown in Figure 5c displays that the length of the nanowires array is approximately 27.01 µm, and the nanowires stand vertically and parallel to each other under the support of the residual AAO templates.The magnified image on the upper right shows the morphology of the nanowires separated from the template holes, which present as elongated and uniformly cylindrical.SEM images present that Nd-Fe-B/Fe-Co nanowires with uniform size are arranged neatly, parallelly, and in a highly ordered fashion.The nanowire energy spectrum analysis results shown in Figure 5d illustrate that the as-deposited Nd-Fe-B/Fe-Co composite nanowires mainly contain Nd, Fe, Co, and B elements, revealing that the metal cations in the electrolyte used for synthesizing the main phases of the nanowire are successfully reduced to atoms and deposited in AAO template pores during the electrochemical deposition process.Figure 6 shows the SEM line scan result of nanowires to further confirm the compositional homogeneity along the nanowire.Figure 6a      Figure 7 shows the morphology and lattice structure of deposited Nd-Fe-B/Fe-Co composite nanowires.Figure 7a is the TEM image of the as-deposited nanowires.It can be seen that the dissociated nanowires are uniform elongated cylinders, some of which are agglomerated into bundles, while others are scattered.The illustration in Figure 7a Figure 7 shows the morphology and lattice structure of deposited Nd-Fe-B/Fe-Co composite nanowires.Figure 7a is the TEM image of the as-deposited nanowires.It can be seen that the dissociated nanowires are uniform elongated cylinders, some of which are agglomerated into bundles, while others are scattered.The illustration in Figure 7a shows that the nanowires possess a uniform diameter of about 70 nm, corresponding with the SEM results.The HRTEM image for zone b of Figure 7a   Figure 8 displays the TEM analysis of Nd-Fe-B/Fe-Co composite nanowires after annealing at 600 °C for 2 h. Figure 8a is the TEM image for a single nanowire, displaying that the nanowire presents a uniform cylinder-like structure with a smooth outer wall.The selected area electron diffraction (SAED) pattern shown in Figure 8b presents polycrystalline diffraction rings consisting of discrete electron diffraction points, which can be calibrated and analyzed.Based on XRD results, the annealed Nd-Fe-B/Fe Co nanowire is polycrystalline in structure, containing Nd2(Fe, Co)14B, NdB4, NdB6, Fe7Nd and Fe7Co3 phases.The phase analysis results of zone A, which corresponds to the core portion of nanowires, are shown in Figure 9.It can be seen that the core portion of nanowires is a mixed structure consisting of Nd2(Fe, Co)14B, Fe7Nd phases and a few amorphous phases.The diffraction spots of the FFT patterns for regions I and II shown in Figure 9b,c, respectively correspond to the (202 ), (303), (501) and (2 1 0), (105) (1 1 5) planes of Nd2(Fe, Co)14B phase with tetragonal structure.The interplanar spacing of the Fe7Nd phase with rhombohedral structure is about 0.2971 nm, 0.2835 nm, and 0.2742 nm, corresponding to the (113 ), (104), and (211) planes.The phase analysis results of zone A, which corresponds to the core portion of nanowires, are shown in Figure 9.It can be seen that the core portion of nanowires is a mixed structure consisting of Nd2(Fe, Co)14B, Fe7Nd phases and a few amorphous phases.The diffraction spots of the FFT patterns for regions I and II shown in Figure 9b,c, respectively correspond to the (202 ), ( 303), ( 501) and ( 2 10a.As can be seen from Figure 10b, zone C is composed of NdB4 and Nd2(Fe, Co)14B phases with a straightforward phase interface.The IFFT pattern of phase interface region IV shows many edge dislocations, indicating that the soft magnetic NdB4 exhibits a pinning effect relative to the Nd2(Fe, Co)14B main phase, increasing resistance to domain wall motion.According to thermodynamic calculation results in Table 2, the ∆G of Nd2(Fe, Co)14B, NdB4, NdB6, Fe7Nd, and Fe7Co3 in the nanowires are 29,188.6J/mol, 90,461.4J/mol, 84,392.5 J/mol, 82,220.4J/mol, and −46,742.8J/mol, respectively.That is, the Fe7Co3 phase prioritizes spontaneous nucleation and crystallization during electrodeposition.Subsequently, Nd2(Fe, Co)14B, Fe7Nd, NdB6, and NdB4 phases are successively formed according to the The phase analysis results of zone A, which corresponds to the core portion of nanowires, are shown in Figure 9.It can be seen that the core portion of nanowires is a mixed structure consisting of Nd 2 (Fe, Co) 14 B, Fe 7 Nd phases and a few amorphous phases.The diffraction spots of the FFT patterns for regions I and II shown in Figure 9b,c, respectively correspond to the (202), ( 303), ( 501) and ( 210), (105) (115) planes of Nd 2 (Fe, Co) 14 B phase with tetragonal structure.The interplanar spacing of the Fe 7 Nd phase with rhombohedral structure is about 0.2971 nm, 0.2835 nm, and 0.2742 nm, corresponding to the (113), (104), and (211) planes.
Figure 10a,b show the microstructure of zones B and C, which are in the outer walls of the nanowire.A two-phase structure consisting of Fe 7 Co 3 and Nd 2 (Fe, Co) 14 B is observed in Figure 10a.As can be seen from Figure 10b, zone C is composed of NdB 4 and Nd 2 (Fe, Co) 14 B phases with a straightforward phase interface.The IFFT pattern of phase interface region IV shows many edge dislocations, indicating that the soft magnetic NdB 4 exhibits a pinning effect relative to the Nd 2 (Fe, Co) 14 B main phase, increasing resistance to domain wall motion.
The FFT patterns for regions I-IV in Figure 11b-e show that zone D exhibits a multiphase structure composed of Nd 2 (Fe, Co) 14 B, NdB 4 , NdB 6 , and Fe 7 Nd phases with a clear phase interface.As shown in the IFFT patterns of regions V and VI, there are a large number of dislocations and dislocation rings at the phase boundary of Nd 2 (Fe, Co) 14 B-NdB 6 and Nd 2 (Fe, Co) 14 B-NdB 4 , resulting from the pinning effect of NdB 6 and NdB 4 to the (primary) main phase.The existence of the pinning effect will hinder the domain wall motion, making it difficult to twist the domain wall in the magnetization process, thereby facilitating and promoting coercivity.
Overall, the annealed Nd-Fe-B/Fe-Co nanowires comprise Nd 2 (Fe, Co) 14 B, Fe 7 Co 3 , NdB 4 , NdB 6, and Fe 7 Nd phases, showing a core-shell-like microstructure.Part of the Nd 2 (Fe, Co) 14 B phase and all of the Fe 7 Co 3 phase are distributed on the outer wall of the nanowire, and the soft-hard magnetic mixture of Nd 2 (Fe, Co) 14 B + NdB 4 + NdB 6 + Fe 7 Nd coexists in the core of nanowire.
According to thermodynamic calculation results in Table 2, the ∆G of Nd 2 (Fe, Co) 14 B, NdB 4 , NdB 6 , Fe 7 Nd, and Fe 7 Co 3 in the nanowires are 29,188.6J/mol, 90,461.4J/mol, 84,392.5 J/mol, 82,220.4J/mol, and −46,742.8J/mol, respectively.That is, the Fe 7 Co 3 phase prioritizes spontaneous nucleation and crystallization during electrodeposition.Subsequently, Nd 2 (Fe, Co) 14 B, Fe 7 Nd, NdB 6, and NdB 4 phases are successively formed according to the transition energy barrier for each phase during the heat treatment process.
The phase distribution in nanowires is determined to a great extent by the growth mechanism of the nanowires during electrodeposition (as shown in Figure 12).Prior to electrodeposition, the back of the AAO template is sputtered with a layer of gold film as the conductive electrode.In this process, some gold particles diffuse onto the wall of the template pore, giving it surface absorption energy, promoting the preferential growth of atoms into the tubular structure of the electrode surface and pore wall.Accompanying the formation of the nanotube structure, the surface absorption energy of the nanochannel gradually decreases, making the electric field force the major driving force of electrodeposition.At low current densities, metal atoms pile up from the electrode surface until the nanotubes are completely filled, forming nanowires.Because Fe 2+ (−0.447V) and Co 2+ (−0.28 V) exhibit higher electrode potentials than Nd 3+ (−2.40 V), Fe 2+ and Co 2+ preferentially enter AAO pores under an electric field force and are then reduced on the hole wall, resulting in the following reactions: outer wall, causing the internal components to deviate from 2:14:1.The formation of Fe7Co3 and Nd2(Fe, Co)14B phases reduces Fe and Co content in nanowire, providing conditions for the generation of a Nd-rich phase, leading to the crystallization of a Nd-rich phase in nanowire.Meanwhile, the existence of a Nd-rich phase makes the surrounding components close to 2:14:1 again, which results in a mixed structure composed of a hard magnetic Nd2(Fe, Co)14B phase and soft magnetic NdB4 + NdB6 + Fe7Nd phases inside the nanowires.

Magnetic Properties Analysis
Figure 13a,b show the hysteresis loops of Fe-Co, Nd-Fe-B, and Nd-Fe-B/Fe-Co composite nanowire arrays before and after annealing at 600 °C for 2 h, respectively.Samples without removing the AAO template were measured in an external magnetic field parallel to the long axis of the nanowires.Figure 13c,d display the dependences of coercivity (Hc) and saturated magnetization (Ms) on nanowire compositions.The magnetic parameters of coercivity (Hc), remanence (Mr), saturated magnetization (Ms), and remanence ratio (Mr/Ms) are listed in Table 3.After Fe and Co generate the initial nucleus, the Fe-Co phase is formed on the pore wall; then, Nd 3+ is induced to conduct co-deposition via the following reaction: Under the combined effect of electric field and surface-absorbed energy, the Fe-Co phase mainly distributes in the outermost layer.Accompanied by heat treatment, a Nd 2 (Fe, Co) 14 B phase with a more minor transition energy barrier first crystallizes at the outer wall, causing the internal components to deviate from 2:14:1.The formation of Fe 7 Co 3 and Nd 2 (Fe, Co) 14 B phases reduces Fe and Co content in nanowire, providing conditions for the generation of a Nd-rich phase, leading to the crystallization of a Nd-rich phase in nanowire.Meanwhile, the existence of a Nd-rich phase makes the surrounding components close to 2:14:1 again, which results in a mixed structure composed of a hard magnetic Nd 2 (Fe, Co) 14 B phase and soft magnetic NdB 4 + NdB 6 + Fe 7 Nd phases inside the nanowires.

Magnetic Properties Analysis
Figure 13a,b show the hysteresis loops of Fe-Co, Nd-Fe-B, and Nd-Fe-B/Fe-Co composite nanowire arrays before and after annealing at 600 • C for 2 h, respectively.Samples without removing the AAO template were measured in an external magnetic field parallel to the long axis of the nanowires.Figure 13c,d display the dependences of coercivity (Hc) and saturated magnetization (Ms) on nanowire compositions.The magnetic parameters of coercivity (Hc), remanence (Mr), saturated magnetization (Ms), and remanence ratio (Mr/Ms) are listed in Table 3.    13a displays the hysteresis loops of as-deposited nanowires with different compositions, and the inserted image at the lower right corner is the magnified image of the selected region I.The as-deposited nanowires exhibit prominent soft magnetic properties, with a coercivity of 413.52 Oe for Fe-Co, 366.70 Oe for Nd-Fe-B, and 399.75 Oe for Nd-Fe-B/Fe-Co nanowire arrays.It can be clearly seen from Figure 13c that the Hc for Fe-Co nanowire arrays is slightly higher than that of the other two component nanowires.The Fe-Co nanowires consist of a pure Fe7Co3 phase, while the phase composition of asdeposited Nd-Fe-B and Nd-Fe-B/Fe-Co nanowires is incompletely crystallized Fe or Fe7Co3 with a few amorphous and microcrystalline phases, resulting in low crystallinity and slightly lower coercivity.
Figure 13b shows that the magnetic properties of Nd-Fe-B/Fe-Co composite nanowires are significantly improved after annealing, with Hc and Mr significantly increasing and Ms slightly decreasing, showing excellent comprehensive magnetic properties of Hc  Figure 13b shows that the magnetic properties of Nd-Fe-B/Fe-Co composite nanowires are significantly improved after annealing, with Hc and Mr significantly increasing and Ms slightly decreasing, showing excellent comprehensive magnetic properties of Hc = 4203.25Oe, Mr = 68.51emu/g, Ms = 76.45 emu/g, and Mr/Ms = 0.89.It should be noted that compared with Fe-Co and Nd-Fe-B nanowires, the coercivity of composite nanowires is increased without sacrificing the saturation magnetization, as shown in Figure 13d.The excellent magnetic performances of Nd-Fe-B/Fe-Co nanowires are mainly attributed to the following aspects: (1) The as-deposited Nd-Fe-B/Fe-Co nanowires are soft magnetic Fe 7 Co 3 and amorphous phases with low Hc.After annealing, the amorphous phase crystallizes into a polycrystalline structure containing Nd 2 (Fe, Co) 14 B, NdB 4 , NdB 6, and Fe 7 Nd, while the soft magnetic Fe 7 Co 3 phase still exists in the nanowires.The generation of the hard magnetic phase Nd 2 (Fe, Co) 14 B with a high anisotropy field hinders the nucleation of the magnetization reversal domain nucleus and the rotation of the magnetic domain, thereby enhancing the coercivity.At the same time, according to the XRD results and Formula (8) [31,32]: The content of the hard magnetic Nd2(Fe, Co)14B phase in Nd-Fe-B/Fe-Co composite nanowires prepared via alternating electrodeposition can be calculated as a volume fraction of 0.81, which is significantly higher than that of the hard magnetic phase Nd2Fe14B (volume fraction of 0.73) in Nd-Fe-B nanowires.This is due to the presence of Co ions in the alternating deposition process, which promotes more Nd ions in the electrolyte to be pulled into the AAO template and induces co-deposition, increasing the deposition quantity of Nd atoms and providing favorable conditions for the subsequent generation of a greater amount of hard magnetic phases.In the subsequent heat treatment process, some Co atoms enter the 2:14:1-type main phase to replace the Fe atoms, reducing the crystallization formation energy of the 2:14:1-type hard magnetic phase and contributing to precipitating more hard magnetic phases in nanowires.The coercivity is further enhanced by the increased content of the hard magnetic 2:14:1-type phase.(2) After annealing, the soft and hard magnetic phases intersect with each other in composite nanowires, existing with a large number of edge dislocations at phase interfaces.This causes the domain wall motion in nanowires to be hindered, enhancing the pinning effect between the soft and hard magnetic phases and increasing the pinning resistance, thus increasing the coercivity.(3) The exchange coupling between the hard magnetic Nd 2 (Fe, Co) 14 B phase and soft magnetic phase of Fe 7 Co 3 will prevent the magnetic moments from orienting along the respective easy magnetization directions and promote the improvement of Mr. According to the exchange spring model proposed by Kneller and Hawig, the exchangecorrelation length of the soft magnetic phase can be written as [33]: wherein A s is the exchange energy for the soft magnetic phase, and K h is the magnetic crystal anisotropy constant of the hard magnetic phase [34].In order to achieve sufficiently strong exchange coupling, the grain size for the soft magnetic phase must be less than 2b cm .According to Formula (8), where A(Fe 7 Co 3 ) = 1.67 × 10 −11 J/m [35], K(Nd 2 Fe 14 B) = 4.3 × 10 6 J/m 3 , it can be calculated that the soft magnetic phase size in the Nd-Fe-B/Fe-Co composite magnet is less than 13.8 nm, which in line with the results observed in the TEM image.Therefore, there is a strong exchange coupling effect in soft-hard magnetic phases in annealed nanowires, facilitating to increase Ms. Based on the Stoner Wohlfarth theory, the phenomenon of remanence enhancement will occur in the magnet under the coupling of soft and hard magnetic exchange when Mr/Ms is much higher than 0.5.As the data listed in Table 3, the Mr/Ms of annealed Nd-Fe-B/Fe-Co composite nanowires is as high as 0.89, therefore exhibiting the magnetic characteristics of high remanence and a high magnetic energy product of 28 MGOe under strong exchange coupling.
It can be seen from the magnetic properties analysis that the characteristics of Nd-Fe-B/Fe-Co magnetic nanowires are mainly controlled via the magnetic exchange coupling mechanism with the assistance of the nucleation field and pinning field.The presence of the Fe 7 Co 3 phase and the strong exchange coupling of soft and hard magnetic phases increase Hc and produce a remanent magnetic enhancement effect, showing a demagnetization curve similar to that of the hard magnetic phase, and the magnetic energy product is significantly increased.The magnetic performance of Nd-Fe-B magnetic nanowires has been significantly improved in comparison with those obtained in previous research.That is to say, compositing with a soft magnetic Fe-Co alloy is an effectual route to enhance the comprehensive magnetic properties of Nd-Fe-B-based nanowires, rendering it more suitable for application in magnetic storage media.

Conclusions
In conclusion, highly ordered Nd-Fe-B/Fe-Co hybrid magnetic nanowires with cylinderlike structures were fabricated in porous AAO templates by means of alternating electrochemical deposition in Nd-Fe-B and Fe-Co aqueous solution.The as-deposited Nd-Fe-B/Fe-Co hybrid nanowires are composed of Nd-atom-doped incompletely crystallized Fe 7 Co 3 and amorphous phases, which have typical soft magnetic properties.The annealing treatment recombines the atoms to form a polycrystalline structure containing hard magnetic Nd 2 (Fe, Co) 14 B and soft magnetic NdB 4 , NdB 6 , Fe 7 Nd, and Fe 7 Co 3 phases.The nucleation sequence of each phase in nanowires is as follows: the Fe 7 Co 3 phase prioritizes spontaneous nucleation and crystallization in as-deposited nanowires.Subsequently, the Nd 2 (Fe, Co) 14 B phase preferentially nucleates, followed by Fe 7 Nd + NdB 6 + NdB 4, in order, during the heat treatment process.The structural characterization revealed that part of the Nd 2 (Fe, Co) 14 B and all of the Fe 7 Co 3 phase distribute in the outer wall of a nanowire; the soft-hard magnetic mixture of Nd 2 (Fe, Co) 14 B + NdB 4 + NdB 6 + Fe 7 Nd coexists in the core of nanowire.The coercivity improvement after annealing is mainly due to the formation of a hard magnetic Nd 2 (Fe, Co) 14 B phase with a high anisotropy field, hindering the nucleation of the magnetization reversal domain nucleus and the rotation of the domain wall, thereby heightening the nucleation field of the annealed nanowires.
Compared with Nd-Fe-B nanowires, the comprehensive magnetic properties of Nd-Fe-B/Fe-Co composite nanowires are significantly improved with a coercivity of 4203.25 Oe and a saturation magnetization of 76.45 emu/g.The excellent magnetic performances can be attributed to the generation of a greater amount of the hard magnetic Nd 2 (Fe, Co) 14 B phase in composite nanowires, the pinning effect between different phases, and the remanence enhancement effect generated by the strong exchange coupling of hard and soft magnetic phase after being combined with Fe-Co alloy, cooperatively resulting in a remanence ratio as high as 0.89 and a high magnetic energy product of 28 MGOe.
Therefore, synthesizing Nd-Fe-B/Fe-Co composite nanowires through alternating electrochemical deposition is an effectual method to improve coercivity without sacrificing remanence.And the RE-Fe-B-based nanowires have a broad application prospect in the field of magnetic memory materials.

Figure 1 .
Figure 1.The flow chart describing the procedure for preparing nanowires based on electrochemical deposition in an AAO template.

Figure 1 . 18 Figure 2 .
Figure 1.The flow chart describing the procedure for preparing nanowires based on electrochemical deposition in an AAO template.Materials 2023, 16, x FOR PEER REVIEW 4 of 18

Figure 2 .
Figure 2. SEM images of AAO template prepared via two-step oxidation method: (a) top-view SEM image, the inset showing pore size distribution in AAO template; (b) top-view SEM image in high magnification; (c) cross-sectional SEM image; (d) cross-sectional SEM image in high magnification.

Figure 3 .
Figure 3. XRD patterns of nanowires with different compositions: (a) as-deposited; (b) annealed at 600 °C for 2 h.The inserted image is the magnification view of the diffraction peak for the (204) plane at the angle of 34.5°-36.5°.

Figure
Figure 4a,b show the XRD patterns of Nd-Fe-B/Fe-Co and Nd-Fe-B nanowires annealed at temperatures of T1 (570 °C) and T2 (600 °C), respectively.Table 2 lists the Imax of each phase in nanowires.The ∆G of Nd2(Fe, Co)14B, NdB4, NdB6, Fe7Nd, and Fe7Co3 phases in Nd-Fe-B/Fe-Co composite nanowires are calculated using Formulas (1)-(3) to be 29,188.6J/mol, 90,461.4J/mol, 84,392.5 J/mol, 82,220.4J/mol, and −46,742.8J/mol, respectively.The ∆G (Fe7Co3) < 0 indicates that the Fe7Co3 phase can spontaneously nucleate and crystallize, consistent with the XRD results shown in Figure3a, thus confirming that the Fe7Co3 phase exists in as-deposited nanowires.The generation of other phases in Nd-Fe-B/Fe-Co nanowires must be completed via absorbing the heat annealing process, corresponding to the positive ∆G values.During the multiphase phase transition process, the phase with a smaller energy barrier will preferentially nucleate and grow, then undergo phase transition.According to the thermodynamic calculation results, it can be inferred that the phase nucleation ordering Nd-Fe-B/Fe-Co nanowires during annealing is roughly as follows: a Nd2(Fe, Co)14B phase with the smallest phase transition energy barrier is preferentially formed, followed by Fe7Nd, NdB6, and NdB4 phases.It is noted that the ∆G of the Nd2(Fe, Co)14B phase formed after adding the Co atom is lower than that of the Nd2Fe14B phase, indicating that the addition of Co reduces the precipitation temperature of the 2:14:1-type phase, thus further promoting the precipitation of more 2:14:1-type hard magnetic phases in composite nanowires, which is consistent with the conclusion proposed by Kojima[30].The XRD results show that the composite nanowires not only retain the soft magnetic Fe7Co3 phase formed in an as-deposited state but also stimulate the generation of greater amounts of the hard magnetic Nd2(Fe, Co)14B phase during the crystallization process.This improves the comprehensive magnetic properties of the nanowires.

Figure 3 .
Figure 3. XRD patterns of nanowires with different compositions: (a) as-deposited; (b) annealed at 600 • C for 2 h.The inserted image is the magnification view of the diffraction peak for the (204) plane at the angle of 34.5 • -36.5 • .Compared with Nd-Fe-B nanowires, there are more diffraction peaks of the 2:14:1 type phase in the XRD pattern of Nd-Fe-B/Fe-Co nanowires, which is related to the deposition efficiency of Nd atoms and their structural evolution.(1) Rare earth metals are difficult to reduce due to their low potential, which can be realized through the co-deposition of an RE-TM alloy.The transition metal Fe and Co ions in Fe-Co solutions with similar structural properties and positive electrode potential are easily reduced and deposited into the AAO template.The generation of a large number of Fe and Co atoms promotes dragging more Nd ions into AAO template pores during the alternating electrodeposition process, inducing more Nd atoms to realize co-deposition, thereby improving the deposition efficiency and quantity of Nd atoms.Assuming that the phase transition process only considers the energy required for phase crystallization without other heat, the phase Gibbs free energy ∆G (i.e., the latent heat of phase transition from amorphous to crystalline) can be considered to be approximately equal to the phase formation enthalpy ∆H.During multiphase structure transformation, it is easier for the phase with smaller ∆G to overcome the energy barrier, then nucleate and grow up, completing phase transition.Based on this, the thermodynamic formula of the Arrhenius Equation can be extended and obtained from the following formulas[29]: Materials 2023, 16, x FOR PEER REVIEW 7 of 18

Figure 4 .
Figure 4. XRD patterns of nanowires with different compositions after annealing at 600 • C and 570 • C: (a) Nd-Fe-B/Fe-Co nanowires; (b) Nd-Fe-B nanowires.Table 2.The maximum peak intensities of each phase in Nd-Fe-B/Fe-Co and Nd-Fe-B nanowires after annealing at 600 • C and 570 • C, and the corresponding Gibbs free energy.
demonstrates a low-magnification SEM image of Nd-Fe-B/Fe-Co nanowires, and the distribution of the main component elements Fe, Nd, and Co along the nanowires is shown in Figure 6b.The content ratios of Nd, Fe, and Co elements at different positions of 3 µm, 10 µm, and 18 µm are 1:11.23:3.60,1:9.73:3.01,and 1:10.02:3.28,respectively, illustrating that the relative content of Nd, Fe, and Co is basically consistent along the nanowires.The intensity of every element fluctuates in a tiny range, indicating that the composition distribution of the main elements in nanowires is uniform along the nanowires.Materials 2023, 16, x FOR PEER REVIEW 8 of 18 1:10.02:3.28,respectively, illustrating that the relative content of Nd, Fe, and Co is basically consistent along the nanowires.The intensity of every element fluctuates in a tiny range, indicating that the composition distribution of the main elements in nanowires is uniform along the nanowires.

Figure 5 .
Figure 5. SEM images of Nd-Fe-B/Fe-Co nanowires prepared by means of the alternate electrodeposition method: (a) top-view SEM image-the illustration in the upper right corner is the high magnification SEM image; (b) the diameter statistical distribution diagram of nanowires; (c) cross-sectional SEM image; (d) EDS spectrum of nanowires.

Figure 5 .
Figure 5. SEM images of Nd-Fe-B/Fe-Co nanowires prepared by means of the alternate electrodeposition method: (a) top-view SEM image-the illustration in the upper right corner is the high magnification SEM image; (b) the diameter statistical distribution diagram of nanowires; (c) crosssectional SEM image; (d) EDS spectrum of nanowires.

Figure 5 .
Figure 5. SEM images of Nd-Fe-B/Fe-Co nanowires prepared by means of the alternate electrodeposition method: (a) top-view SEM image-the illustration in the upper right corner is the high magnification SEM image; (b) the diameter statistical distribution diagram of nanowires; (c) cross-sectional SEM image; (d) EDS spectrum of nanowires.

Figure 6 .
Figure 6.(a) SEM image of as-deposited Nd-Fe-B/Fe-Co nanowires; (b) the SEM-EDS line scan along the long axis of nanowire (red line in the SEM image).

Figure 6 .
Figure 6.(a) SEM image of as-deposited Nd-Fe-B/Fe-Co nanowires; (b) the SEM-EDS line scan along the long axis of nanowire (red line in the SEM image).
Figure7shows the morphology and lattice structure of deposited Nd-Fe-B/Fe-Co composite nanowires.Figure7ais the TEM image of the as-deposited nanowires.It can be seen that the dissociated nanowires are uniform elongated cylinders, some of which are agglomerated into bundles, while others are scattered.The illustration in Figure7ashows that the nanowires possess a uniform diameter of about 70 nm, corresponding with the SEM results.The HRTEM image for zone b of Figure7ais shown in Figure 7b, and the inserted images in red and blue borders show the Inverse Fast Fourier Transform (IFFT) patterns of regions I and II, respectively.From the IFFT patterns, it can be measured that the d values of regions I and II are 0.2121 nm and 0.2209 nm, both corresponding to the (110) plane of the Fe 7 Co 3 phase.The measured values are slightly larger than the interplanar spacing of the bcc Fe 7 Co 3 phase listed in standard X-ray crystallography (d(110)Fe 7 Co 3 = 0.2025 nm).The larger d values indicate that the RE atom of Nd with a larger radius has existed as a solid solution atom in the Fe 7 Co 3 phase; therefore, the phase structure of as-deposited Nd-Fe-B/Fe-Co nanowires is the incomplete crystalline Fe 7 Co 3 phase with Nd atom doping.Materials 2023, 16, x FOR PEER REVIEW 9 of 18

Figure 7 .
Figure 7. TEM observation and analysis of as-deposited Nd-Fe-B/Fe-Co nanowires: (a) TEM image of nanowire bundle, and the inserted image is the magnified view of the selected portion with a red border; (b) HRTEM image of zone b in (a) and the corresponding IFFT patterns of regions I and II.

Figure 7 .
Figure 7. TEM observation and analysis of as-deposited Nd-Fe-B/Fe-Co nanowires: (a) TEM image of nanowire bundle, and the inserted image is the magnified view of the selected portion with a red border; (b) HRTEM image of zone b in (a) and the corresponding IFFT patterns of regions I and II.

Figure 8 18 Figure 8 .
Figure 8 displays the TEM analysis of Nd-Fe-B/Fe-Co composite nanowires after annealing at 600 • C for 2 h. Figure 8a is the TEM image for a single nanowire, displaying

Figure 9 .
Figure 9. HRTEM analysis of annealed Nd-Fe-B/Fe-Co nanowires: (a) HRTEM of zone A in Figure

Figure 8 . 18 Figure 8 .
Figure 8. TEM observation and analysis of Nd-Fe-B/Fe-Co nanowires after annealing at 600 • C for 2 h: (a) the morphology of a single composite nanowire; (b) SAED pattern of the annealed nanowire.

Figure 9 .
Figure 9. HRTEM analysis of annealed Nd-Fe-B/Fe-Co nanowires: (a) HRTEM of zone A in Figure 8a; (b-e) the corresponding FFT patterns of regions I-IV.Figure 9. HRTEM analysis of annealed Nd-Fe-B/Fe-Co nanowires: (a) HRTEM of zone A in Figure 8a; (b-e) the corresponding FFT patterns of regions I-IV.

Figure 9 .
Figure 9. HRTEM analysis of annealed Nd-Fe-B/Fe-Co nanowires: (a) HRTEM of zone A in Figure 8a; (b-e) the corresponding FFT patterns of regions I-IV.Figure 9. HRTEM analysis of annealed Nd-Fe-B/Fe-Co nanowires: (a) HRTEM of zone A in Figure 8a; (b-e) the corresponding FFT patterns of regions I-IV.

Figure
Figure10a,b show the microstructure of zones B and C, which are located in the outer walls of the nanowire.A two-phase structure consisting of Fe7Co3 and Nd2(Fe, Co)14B is observed in Figure10a.As can be seen from Figure10b, zone C is composed of NdB4 and Nd2(Fe, Co)14B phases with a straightforward phase interface.The IFFT pattern of phase interface region IV shows many edge dislocations, indicating that the soft magnetic NdB4 exhibits a pinning effect relative to the Nd2(Fe, Co)14B main phase, increasing resistance to domain wall motion.

Figure 10 .
Figure 10.HRTEM analysis of annealed Nd-Fe-B/Fe-Co nanowires: (a,b) HRTEM images of zones B-C in Figure 8a; (c) FFT pattern of the selected region I in (a); (d,e) the magnified view of regions II-III in (a); (f-h) FFT patterns of regions I-III in (b); (i) the corresponding IFFT pattern of region IV in (b).The FFT patterns for regions I-IV in Figure11b-e show that zone D exhibits a multiphase structure composed of Nd2(Fe, Co)14B, NdB4, NdB6, and Fe7Nd phases with a clear phase interface.As shown in the IFFT patterns of regions V and VI, there are a large number of dislocations and dislocation rings at the phase boundary of Nd2(Fe, Co)14B-NdB6 and Nd2(Fe, Co)14B-NdB4, resulting from the pinning effect of NdB6 and NdB4 to the (primary) main phase.The existence of the pinning effect will hinder the domain wall motion, making it difficult to twist the domain wall in the magnetization process, thereby facilitating and promoting coercivity.Overall, the annealed Nd-Fe-B/Fe-Co nanowires comprise Nd2(Fe, Co)14B, Fe7Co3, NdB4, NdB6, and Fe7Nd phases, showing a core-shell-like microstructure.Part of the Nd2(Fe, Co)14B phase and all of the Fe7Co3 phase are distributed on the outer wall of the nanowire, and the soft-hard magnetic mixture of Nd2(Fe, Co)14B + NdB4 + NdB6 + Fe7Nd coexists in the core of nanowire.

Figure 10 .
Figure 10.HRTEM analysis of annealed Nd-Fe-B/Fe-Co nanowires: (a,b) HRTEM images of zones B-C in Figure 8a; (c) FFT pattern of the selected region I in (a); (d,e) the magnified view of regions II-III in (a); (f-h) FFT patterns of regions I-III in (b); (i) the corresponding IFFT pattern of region IV in (b).

Materials 2023 , 18 Figure 11 .
Figure 11.HRTEM analysis of annealed Nd-Fe-B/Fe-Co nanowires: (a) HRTEM image for zone D in Figure 8a; (b-e) FFT patterns of the selected regions I-IV in (a); (f,g) the corresponding IFFT patterns of regions V-VI in (a).

Figure 11 .
Figure 11.HRTEM analysis of annealed Nd-Fe-B/Fe-Co nanowires: (a) HRTEM image for zone D in Figure 8a; (b-e) FFT patterns of the selected regions I-IV in (a); (f,g) the corresponding IFFT patterns of regions V-VI in (a).

Figure 12 .
Figure 12.Schematic illustrations for the electrodeposition growth mechanism of Nd-Fe-B/Fe-Co composite nanowires in AAO pores and the phase distribution in nanowires.

Figure 12 .
Figure 12.Schematic illustrations for the electrodeposition growth mechanism of Nd-Fe-B/Fe-Co composite nanowires in AAO pores and the phase distribution in nanowires.

Figure 13 .
Figure 13.Magnetic hysteresis loops of nanowires with different compositions measured at room temperature under external magnetic field applied direction parallel to the long axis of nanowires: (a) as-deposited; (b) annealed at 600 °C for 2 h; (c) the variation trends of Hc and Ms for as-deposited nanowires with different compositions; (d) the variation trends of Hc and Ms for 660 °C-annealed nanowires with different compositions.

Figure 13 .
Figure 13.Magnetic hysteresis loops of nanowires with different compositions measured at room temperature under external magnetic field applied direction parallel to the long axis of nanowires: (a) as-deposited; (b) annealed at 600 • C for 2 h; (c) the variation trends of Hc and Ms for as-deposited nanowires with different compositions; (d) the variation trends of Hc and Ms for 660 • C-annealed nanowires with different compositions.

Figure
Figure 13a displays the hysteresis loops of as-deposited nanowires with different compositions, and the inserted image at the lower right corner is the magnified image of the selected region I.The as-deposited nanowires exhibit prominent soft magnetic properties, with a coercivity of 413.52 Oe for Fe-Co, 366.70 Oe for Nd-Fe-B, and 399.75 Oe for Nd-Fe-B/Fe-Co nanowire arrays.It can be clearly seen from Figure 13c that the Hc for Fe-Co nanowire arrays is slightly higher than that of the other two component nanowires.The Fe-Co nanowires consist of a pure Fe 7 Co 3 phase, while the phase composition of as-deposited Nd-Fe-B and Nd-Fe-B/Fe-Co nanowires is incompletely crystallized Fe or Fe 7 Co 3 with a few amorphous and microcrystalline phases, resulting in low crystallinity and slightly lower coercivity.Figure13bshows that the magnetic properties of Nd-Fe-B/Fe-Co composite nanowires are significantly improved after annealing, with Hc and Mr significantly increasing and Ms slightly decreasing, showing excellent comprehensive magnetic properties of Hc = 4203.25Oe, Mr = 68.51emu/g, Ms = 76.45 emu/g, and Mr/Ms = 0.89.It should be noted that compared with Fe-Co and Nd-Fe-B nanowires, the coercivity of composite nanowires is increased without sacrificing the saturation magnetization, as shown in Figure13d.The excellent magnetic performances of Nd-Fe-B/Fe-Co nanowires are mainly attributed to the following aspects:

Table 1 .
The electrolyte composition of Nd-Fe-B/Fe-Co composite nanowires prepared via alternate deposition.

Table 2 .
The maximum peak intensities of each phase in Nd-Fe-B/Fe-Co and Nd-Fe-B nanowires after annealing at 600 °C and 570 °C, and the corresponding Gibbs free energy.

Table 3 .
The magnetic parameters of nanowires with different compositions.

Table 3 .
The magnetic parameters of nanowires with different compositions.