Fabrication of r-GO/GO/α-Fe2O3/Fe2TiO5 Nanocomposite Using Natural Ilmenite and Graphite for Efficient Photocatalysis in Visible Light

Hematite (α-Fe2O3) and pseudobrookite (Fe2TiO5) suffer from poor charge transport and a high recombination effect under visible light irradiation. This study investigates the design and production of a 2D graphene-like r-GO/GO coupled α-Fe2O3/Fe2TiO5 heterojunction composite with better charge separation. It uses a simple sonochemical and hydrothermal approach followed by L-ascorbic acid chemical reduction pathway. The advantageous band offset of the α-Fe2O3/Fe2TiO5 (TF) nanocomposite between α-Fe2O3 and Fe2TiO5 forms a Type-II heterojunction at the Fe2O3/Fe2TiO5 interface, which efficiently promotes electron-hole separation. Importantly, very corrosive acid leachate resulting from the hydrochloric acid leaching of ilmenite sand, was successfully exploited to fabricate α-Fe2O3/Fe2TiO5 heterojunction. In this paper, a straightforward synthesis strategy was employed to create 2D graphene-like reduced graphene oxide (r-GO) from Ceylon graphite. The two-step process comprises oxidation of graphite to graphene oxide (GO) using the improved Hummer’s method, followed by controlled reduction of GO to r-GO using L-ascorbic acid. Before the reduction of GO to the r-GO, the surface of TF heterojunction was coupled with GO and was allowed for the controlled L-ascorbic acid reduction to yield r-GO/GO/α-Fe2O3/Fe2TiO5 nanocomposite. Under visible light illumination, the photocatalytic performance of the 30% GO/TF loaded composite material greatly improved (1240 Wcm−2). Field emission scanning electron microscopy (FE-SEM) and high-resolution transmission electron microscopy (HR-TEM) examined the morphological characteristics of fabricated composites. X-ray photoelectron spectroscopy (XPS), Raman, X-ray diffraction (XRD), X-ray fluorescence (XRF), and diffuse reflectance spectroscopy (DRS) served to analyze the structural features of the produced composites.


Dissolution of Ilmenite Sand and Precipitation
Washed and dried ilmenite sand was leached in 200 mL of concentrated HCl acid for 6 h at 110 • C and subjected to vigorous stirring under refluxing conditions. In a solid-liquid separation funnel, the leached slurry was allowed to cool and settle into layers. Orange colored supernatant was collected separately and is called the acid leachate. Oxygen gas was bubbled at 1 bar pressure overnight to oxidize ferrous ions to ferric ions. The homogenized mixture was filtered through a Whatman filter paper to separate the filtrate and solid residue. ICP-MS analysis examined the Fe and Ti concentrations in the leachate. The resulting solution was transferred to a two-neck round bottom flask, and the reaction mixture was bubbled with nitrogen gas for 1 h. In the nitrogen environment, 0.0237 mol FeSO 4 .7H 2 O was added to the reaction mixture. NH 4 OH was added dropwise with a continuing purge of nitrogen gas until the pH of the reaction mixture reached 10. The black slurry was then aged for another 12 h before being completely cleansed with ultra-pure water until the washings were chloride-free and neutral. The dried black color powder was calcined at 800 • C [32]. Powder that is not calcined is referred to as "amorphous TF", while powder that is calcined at 800 • C is known as TF.

Preparation of Graphene Oxide
The improved Hummer's method served to synthesize graphene oxide (GO) from natural graphite powder [46,47]. Graphite powder (3.0 g) and 12.0 g KMnO 4 were homogenized together through mechanical grinding. The acid combination was prepared by mixing conc. H 2 SO 4 (360 mL) and conc. H 3 PO 4 (40 mL) at a ratio of 9:1 and kept in an ice bath to lower the temperature to prevent the exothermic reaction that occurs when the acid mixture is treated with the graphite and KMnO 4 mixture. This mixture was treated with the acid mixture and the subsequent dark yellowish green solution was stirred for 12 h at 55 • C. The temperature of the mixture was allowed to cool down to room temperature before adding 3 mL of 30% hydrogen peroxide (H 2 O 2 ); after that the stirring was continued for 5 min. Ice cubes controlled the subsequent exothermic reaction, and the final solution had a yellowish orange color. The obtained solid was washed with deionized water until the pH reached neutral and negative for SO 4 2− ions. Finally, the collected material was dried at 60 • C for 12 h and is abbreviated as GO in this paper.

Synthesis of Photocatalysts
GO powder was ultrasonically dispersed in ultra-pure water maintaining the GO/TF weight ratio at 10%. Then, the respective amount of TF was added to the GO suspension and further ultrasonicated for 30 min. The produced suspension was subjected to hydrothermal treatment at 150 • C for 8 hr. Then, 50 mL of L-ascorbic acid (0.1 M) solution was added to the mixture and stirred at 60 • C for 1 h. Finally, the obtained precipitate was washed with water and 2-propanol followed by drying at 60 • C. This material is referred to as (0.1)r-GOTF in this paper. Similarly, (0.2)r-GOTF and (0.3)r-GOTF materials were fabricated by maintaining the percentages of GO with reference to TF as 20% and 30%, respectively.

Photocatalytic Measurements
The photodegradation of MB served as the model reaction to evaluate the photocatalytic performance of the synthesized nanocomposites. TF catalyst (50 mg) was dispersed in 50 mL of MB (20 mg/L) solution and shaken in the dark for 180 min until adsorptiondesorption equilibrium was achieved. Aliquots were withdrawn at desired time intervals and absorbance readings were recorded. After that, the solution was irradiated using a 50 W visible light generated by a LED source (the photon flux at the reactor was 1240 Wcm −2 ). Absorbance readings of the aliquots withdrawn at specific time intervals were recorded.

Materials Characterization
The Advanced Bruker X-ray diffraction (XRD) system investigated the crystalline structure of the produced samples. The X-rays were produced using a CuK-α anode and a 30-mA current at 40 kV voltage. The diffractograms were created using a 2 • /min scanning rate in the 5-80 • range, and the samples were analyzed using X'Pert High Score Plus (PANalytical) software. A Bruker Senterra Raman microscope spectrophotometer did the Raman analysis. A High-resolution transmission electron microscope (HR-TEM) and Zeiss field emission scanning electron microscope examined the morphology of the produced nanocomposites. Oxford Instruments energy dispersive X-ray (EDX) was used to acquire EDX spectra. X-ray fluorescence (XRF) determined the chemical composition of the samples using a HORIBA Scientific XGT-5200 X-ray analytical microscope with an Rh anode X-ray tube operating at a maximum voltage of 50 kV. Thermo Scientific TM ESCALAB Xi + X-ray Photoelectron Spectrometer (XPS) was utilized to examine the surface nature of the fabricated materials. The diffuse reflectance spectra (DRS) of the powder samples were analyzed using a Shimadzu 1800 UV/Visible spectrophotometer armed with a precision Czerny-Turner optical system. Measurements were made using a bandwidth of 1.0 nm and a wavelength range of 400-750 nm. Thermo Scientific X-Series 2 Inductively Coupled Plasma Mass Spectrometer (ICP-MS), Thermo Fisher Scientific, Waltham, MA USA helped to evaluate Fe 3+ and Ti 4+ concentrations of the acid leachate. Shimadzu UV-1990 double beam UV-Visible spectrophotometer was used to evaluate the absorbance of MB samples. The bacterial culture of E. coli used in the macro dilution assay was procured from Medical Research Institute, Sri Lanka. The initial inoculum was prepared by sub-culturing the pure cultures of E. coli in 250 mL of autoclaved nutrient broth media and then incubated at 37 • C for 24 h.
To obtain accurate results it is crucial to standardize the bacterial cell number used for susceptibility testing. The density of the cell suspension was measured spectrophotometrically and with a 0.5 McFarland turbidity standard which is equal to 1 − 2 × 10 8 CFU/mL as a visual yardstick. A 24 h aged bacterial culture was adjusted to obtain 5 × 10 5 CFU/mL and the adjusted bacterial suspension was used immediately (within 30 min) to prevent subsequent changes in the cell count.

Broth Dilution Assay
The antibacterial activities of TF, (0.3)r-GOTF, (0.2)r-GOTF, (0.1)r-GOTF and r-TF composites were evaluated using the macro broth dilution method. The susceptibility assay of the synthesized material was carried out against E. coli in sterilized nutrient broth media. The viable count of E. coli bacteria was determined by the standard plate count method to clearly and easily discriminate the viability of bacterial cells after the treatment with fabricated nanocomposites. Bacterial culture and without nanocomposite functioned as the control.
A 24 h-aged E. coli culture adjusted with the spectrophotometer and 0.5 McFarland turbidity standard to obtain 5 × 10 5 CFU/mL cell density was used for the broth dilution assay within 30 min to prevent any change in cell count. Suspensions of synthesized nanoparticles were prepared with deionized water by sonicating them at 50 • C for 40 min. Then, 1 mL of the prepared and adjusted bacterial culture was incorporated into 5 mL of sterilized nutrient broth media which contained 1 mL of 40 mg/mL nanocomposite suspensions. The positive control was prepared by inoculating 1 mL of adjusted bacterial suspension to 5 mL of sterilized nutrient broth media containing 1 mL of amoxicillin (40 mg/mL). Broth media inoculated with bacterial suspension yet free from nano-suspension was regarded as the growth control. The blank was prepared by adding the synthesized nanocomposites to sterilized nutrient broth media. The prepared solutions were placed in test tubes and incubated overnight for 24 h at 30 • C in a temperature-controlled shaker at 150 rpm. The inhibition of bacterial growth was determined through the spectrophotometric method. After 24 h, the optical density (O.D.) was measured at 600 nm using Shimadzu UV-VIS spectrophotometer.
Triplicates of each experiment were carried out. Each sample's OD values and their mean values were calculated along with the standard deviation. The following formula was used to determine the percentage of growth inhibition.

Results
The dissolution of ilmenite sand by hydrochloric acid produces iron and titanium chlorides as expressed in Equations (2)- (5). The ICP-MS quantified total Fe 3+ and Ti 4+ concentrations of oxygenated acid leachate, which were 5434 mg/L and 1078 mg/L, respectively. During bubbling of oxygen gas, all Fe 2+ in acid leachate was oxidized and produced Fe 3+ . Hence, the total Fe concentration recorded by the ICP-MS analysis represents only Fe 3+ . The molar ratio of Fe 2+ to Fe 3+ was adjusted to 1:2 by adding 0.0237 mol of FeSO 4 .7H 2 O to the acid leachate under nitrogen environment. The amorphous TiO 2 /Fe 3 O 4 composite after drying the precipitate obtained from the reaction of NH 4 OH and the acid leachate is shown in Equations (6)- (10). The XRD patterns of ilmenite sand and amorphous TiO 2 /Fe 3 O 4 composite are shown in the supplementary information, specifically Figure S1a,b.
The α-Fe 2 O 3 /Fe 2 TiO 5 heterojunction was formed after annealing of the TiO 2 /Fe 3 O 4 composite at 800 • C since the solid-state reaction at the surface of the material occurred at 700-800 • C. Fe 3 O 4 is converted to α-Fe 2 O 3 when the annealing temperature reaches 600 • C [48] while α-Fe 2 O 3 and TiO 2 are expected to transform to α-Fe 2 O 3 /Fe 2 TiO 5 once a further increase in the annealing temperature occurs [49]. The formation of Fe 2 TiO 5 is shown in Equation (11)  Surface morphological features of the fabricated nanocomposites were studied using scanning electron microscope and the collected images are shown in Figure 1. The SEM image of ilmenite sand (Figure 1a) reveals the macro nature of its particles with a heterogeneous particle size distribution. The crumpled and wrinkled lamellae structure arrangement is evident in the SEM image of GO developed from the oxidation of graphite (Figure 1b). The borders of individual sheets, including kinked and wrinkled portions, are distinct when these nanosheets are folded. This morphological feature of GO is very similar to the reported data [50]. Figure 1c shows the SEM image of TF nanoparticles. It is observed that the nanoparticles are fused at each end leading to aggregation, an outcome caused by Oswald ripening occurring during the calcination of the samples at elevated temperatures [51].
During Oswald ripening smaller nanoparticles dissolve and deposit as larger nanoparticles, thus achieving the most thermodynamically favorable configuration. The folded structure of GO disappears upon coupling with TF and reducing by L-ascorbic acid in the (0.3)r-GOTF nanocomposite, and the sample is dominated by nano-sized grains as shown in the SEM image ( Figure 1d). Further, the surface morphology of TF has been altered after the reduction by L-ascorbic acid where almost monodispersed spherical nanoparticles were obtained compared to the TF shown in Figure 1c. EDX analysis was undertaken to identify the elemental composition of the samples. Figure 1e,f show the EDX spectra of TF and L-ascorbic acid treated (0.3)r-GOTF. EDX elemental composition results are tabulated in Supplementary Information (Table S1a, The α-Fe2O3/Fe2TiO5 heterojunction was formed after annealing of the TiO2/Fe3O4 composite at 800 °C since the solid-state reaction at the surface of the material occurred at 700-800 °C. Fe3O4 is converted to α-Fe2O3 when the annealing temperature reaches 600 °C [48] while α-Fe2O3 and TiO2 are expected to transform to α-Fe2O3/Fe2TiO5 once a further increase in the annealing temperature occurs [49]. The formation of Fe2TiO5 is shown in Equation (11)  Surface morphological features of the fabricated nanocomposites were studied using scanning electron microscope and the collected images are shown in Figure 1. The SEM image of ilmenite sand (Figure 1a) reveals the macro nature of its particles with a heterogeneous particle size distribution. The crumpled and wrinkled lamellae structure arrangement is evident in the SEM image of GO developed from the oxidation of graphite ( Figure  1b). The borders of individual sheets, including kinked and wrinkled portions, are distinct when these nanosheets are folded. This morphological feature of GO is very similar to the reported data [50]. Figure 1c shows the SEM image of TF nanoparticles. It is observed that the nanoparticles are fused at each end leading to aggregation, an outcome caused by Oswald ripening occurring during the calcination of the samples at elevated temperatures [51].
During Oswald ripening smaller nanoparticles dissolve and deposit as larger nanoparticles, thus achieving the most thermodynamically favorable configuration. The folded structure of GO disappears upon coupling with TF and reducing by L-ascorbic acid in the (0.3)r-GOTF nanocomposite, and the sample is dominated by nano-sized grains as shown in the SEM image ( Figure 1d). Further, the surface morphology of TF has been altered after the reduction by L-ascorbic acid where almost monodispersed spherical nanoparticles were obtained compared to the TF shown in Figure 1c. EDX analysis was undertaken to identify the elemental composition of the samples.

TEM Analysis
The inner structural and morphological features of TF and (0.3)r-GOTF composites were analyzed by TEM as shown in Figure 2. Bright field TEM image of TF (Figure 2a) shows spherical and irregular-shaped nanoparticles in the 60-100 nm range, and they are fused with each other forming aggregates being consistent with the SEM image of TF (Figure 1c). Fused nanoparticles are formed at high temperatures due to Oswald ripening. TiO2 and Fe3O4 nanoparticles formed at room temperature are converted to α-Fe2O3 and Fe2TiO5 at 800 °C and nanoparticle fusion forms a junction between α-Fe2O3 and Fe2TiO5, making possible the formation of α-Fe2O3/Fe2TiO5 heterojunctions. The HR-TEM images of TF composite are shown in Figure 2b,c, indicating atomic layer arrangement of varying phases.   Figure 2c with corresponding atomic layer distances of 0.34 and 0.49 nm, respectively [49]. Crystalline planes can result in distinct electrochemical and catalytic characteristics [52]. High-index crystal planes of α-Fe 2 O 3 nanocrystals are more susceptible to surface imperfections and have greater surface energy than low-index crystal planes [53]. As a result, the exposed crystal surfaces can drive photocatalytic activity. The selected area electron diffraction (SAED) patterns of TF are illustrated in Figure 2d. They appear to have scattered bright diffused rings, indicating the existence of a α-Fe 2 O 3 structure, while the dark less intense patches suggest the presence of Fe 2 TiO 5 in polycrystallinity [54,55].
The bright field TEM image of (0.3)r-GOTF nanocomposite shown in Figure Figure 2h shows the r-GO at the outer area of the composite. The lattice fringes with 0.33 nm of an interlayer distance which are uniformly distributed throughout the surface are assigned to the C(002) plane. Atomic planes with interplanar distance of 0.33 nm close to the metal nanoparticles suggest that the GO has been effectively reduced to r-GO even near the nanoparticles. Figure 2i depicts the selected area electron diffraction (SAED) patterns of (0.3)r-GOTF. The appearance of a set of diffraction patterns with sharp and clear diffraction patterns is denoted by the material's polycrystallinity [54]. They appear to have scattered bright diffused rings, indicating the existence of a α-Fe 2 O 3 structure, while the dark less intense patches suggest the presence of r-GO and Fe 2 TiO 5 in polycrystallinity [54][55][56]. Previous studies have reported that most graphene sheets exhibited a single set of hexagonal diffraction pattern with clear and sharp diffraction spots [57].

XPS Analysis
X-ray photoelectron spectroscopy (XPS) emerged as a more surface-sensitive approach to describe the surface chemical states of fabricated nanocomposites. The higher resolution spectra of the elements and survey spectra of the synthesized composites are shown in Figure 3. All binding energies were corrected for the sample charging effect considering the binding energy of sp 2 hybridized C=C as 284.6 eV. The higher resolution spectrum of Fe 2p of (0.3)r-GOTF is shown in Figure 3a while that of other composites are given in Supplementary Figure S2. The higher resolution spectrum of Fe 2p was mainly deconvoluted into two peaks as 2p 3/2 and 2p 1/2 and this generally indicated the spin orbital coupling. The peaks correspond to Fe 2p 3/2 of the nanocomposite materials that appeared in the 711.84-712.06 eV range and the peak corresponding to Fe 2p 1/2 appeared in the range of 725.28-726.03 eV, respectively [57]. The calculated binding energy differences are in the 13.64-13.73 eV range and satisfy the spin-orbit splitting of Fe 2p because Fe(III) is usually high-spin and exists in the form of Fe 3+ [58]. The chemical environments of Fe 3+ in α-Fe 2 O 3 and Fe 2 TiO 5 are different, although the oxidation number is the same. It can be observed that the resultant binding energies differ from those of the pure compounds, demonstrating the effective fabrication of Type II heterojunctions in the binary composites and altering the electronic environment of an individual element [59].
In the detailed analysis of Fe 2p 1/2 and Fe 2p 3/2 binding energies of fabricated nanocomposites, (0.3)r-GOTF exhibited by highest value in the above-reported range, values of 726.03 and 712.34 eV, respectively. The higher binding energy suggests an increment in the electron concentration of α-Fe 2 O 3 and Fe 2 TiO 5 , despite the fact that this may further revoke the reduction in electron and hole recombination in composites [60,61]. Figure 3b shows the higher resolution spectrum of Ti 2p XPS spectra of (0.3)r-GOTF nanocomposite material, while the other composites are shown in Supplementary Figure S2. As shown in Figure 3b, Ti 2p is deconvoluted to three peaks at 459.1, 464.8, 472.5 eV, corresponding to the 2p 3/2 , 2p 1/2 , and satellite peak of 2p 3/2 [32,39]. The spin-orbit splitting of the Ti 2p XPS spectrum of TF is = 5.7 eV, and its two binding energies of 459.1 and 464.8eV may be attributed to Ti 4+ characteristic peaks, demonstrating the existence of Fe 2 TiO 5 in the composite material [32,39]. The Ti 2p high resolution spectra of TF, (0.2)r-GOTF, (0.1)r-GOTF and r-TF materials do not indicate a considerable shift for calculated binding energy values. In the detailed analysis of Fe 2p1/2 and Fe 2p3/2 binding energies of fabricated nanocomposites, (0.3)r-GOTF exhibited by highest value in the above-reported range, values of 726.03 and 712.34 eV, respectively. The higher binding energy suggests an increment in the electron concentration of α-Fe2O3 and Fe2TiO5, despite the fact that this may further revoke the reduction in electron and hole recombination in composites [60,61]. Figure 3b shows the higher resolution spectrum of Ti 2p XPS spectra of (0.3)r-GOTF nanocomposite material, while the other composites are shown in Supplementary Figure S2. As shown in Figure 3b, Ti 2p is deconvoluted to three peaks at 459.1, 464.8, 472.5 eV, corresponding to the 2p3/2, 2p1/2, and satellite peak of 2p3/2 [32,39]. The spin-orbit splitting of the Ti 2p XPS spectrum of TF is = 5.7 eV, and its two binding energies of 459.1 and 464.8eV may be attributed to Ti 4+ characteristic peaks, demonstrating the existence of Fe2TiO5 in the composite material [32,39]. The Ti 2p high resolution spectra of TF, (0.2)r-GOTF, (0.1)r-GOTF and r-TF materials do not indicate a considerable shift for calculated binding energy values.
The high-resolution XPS C 1s spectra of the (0.3)r-GOTF is shown in Figure 3c and that of TF, (0.2)r-GOTF, (0.1)r-GOTF and r-TF are shown in Supplementary Figure S2. C 1s spectra of (0.3)r-GOTF and it depicts three peaks that appeared at 284.6 eV, 285.7, 287 and 289.2 eV representing, respectively, C=C, C-C and C=O [62]. Similarly, C 1s spectra of r-TF nanocomposite Supplementary Figure S2l exhibit identical behavior to the TF nanocomposite and C=C, C-C and C=O peaks appearing at 284.79, 285.79 and 288.91 eV, respectively. However, r-GO loaded samples reveal four significant peaks due to the presence of the C-O peak in GO samples. Moreover, sp 3 C bonding is an important attribute of GO in producing good hydrophilic and wear resistance properties. This is despite the fact that we primarily focus on the fabrication of nanocomposites with the presence of the sp 2 C bonding and sp 3 C bonding fractions at the edge of r-GO/GO ultrathin films.
For deeper analysis, C 1s high-resolution spectrum was deconvoluted in each sample using four Gaussian curves that correspond to sp2 carbon (sp 2 C) bonding (~284.8 eV), sp 3 carbon (sp 3 C) bonding (~285.6 eV), C-O bonding (~287.1 eV), and C=O bonding (~289.4 eV) [38]. Furthermore, the calculated chemical composition of carbon materials is summarized in Table 1. The surface chemical percentage of C 1s has been calculated using the deconvoluted Gaussian curves peaks area under the curve. According to the XPS data in The high-resolution XPS C 1s spectra of the (0.3)r-GOTF is shown in Figure 3c and that of TF, (0.2)r-GOTF, (0.1)r-GOTF and r-TF are shown in Supplementary Figure S2. C 1s spectra of (0.3)r-GOTF and it depicts three peaks that appeared at 284.6 eV, 285.7, 287 and 289.2 eV representing, respectively, C=C, C-C and C=O [62]. Similarly, C 1s spectra of r-TF nanocomposite Supplementary Figure S2l exhibit identical behavior to the TF nanocomposite and C=C, C-C and C=O peaks appearing at 284.79, 285.79 and 288.91 eV, respectively. However, r-GO loaded samples reveal four significant peaks due to the presence of the C-O peak in GO samples. Moreover, sp 3 C bonding is an important attribute of GO in producing good hydrophilic and wear resistance properties. This is despite the fact that we primarily focus on the fabrication of nanocomposites with the presence of the sp 2 C bonding and sp 3 C bonding fractions at the edge of r-GO/GO ultrathin films.
For deeper analysis, C 1s high-resolution spectrum was deconvoluted in each sample using four Gaussian curves that correspond to sp2 carbon (sp 2 C) bonding (~284.8 eV), sp 3 carbon (sp 3 C) bonding (~285.6 eV), C-O bonding (~287.1 eV), and C=O bonding (~289.4 eV) [38]. Furthermore, the calculated chemical composition of carbon materials is summarized in Table 1. The surface chemical percentage of C 1s has been calculated using the deconvoluted Gaussian curves peaks area under the curve. According to the XPS data in Table 1, (0.1)r-GOTF material shows the highest fraction of C=C (sp 2 C) which was 22.54%. Consequently, the XPS results corroborated the Raman analysis results. Figure 3d (p)-(t) shows the high resolution O 1s XPS spectra of (0.3)r-GOTF while the as-fabricated TF, (0.2)r-GOTF, (0.1)r-GOTF and r-TF nanocomposites are shown in Supplementary Figure S2. The spectra of TF, (0.3)r-GOTF, (0.1)r-GOTF and r-TF have been fitted to two deconvoluted peaks with binding energies of~530.8 and~531.86 eV with standard deviations of 0.11 and 0.16 eV, respectively [63]. The peak corresponding at~530.8 eV was ascribed to the O 2− of Fe 3+ and Ti 4+ for α-Fe 2 O 3 and Fe 2 TiO 5 , respectively [32,38,39]. As well, the peak appearing at 531.86 eV is ascribed to the OH. The O 1s high-resolution XPS spectra of (0.2)r-GOTF are represented in Supplementary Figure S2n), and it has been fitted into three deconvoluted peaks at binding energy values at 530.8, 532.36 and 534.04 eV, respectively [32]. In addition to the O 2− and OH peaks of Fe 3+ and Ti 4+ for α-Fe 2 O 3 and Fe 2 TiO 5 , the peak appearing at 534.04 eV corresponded to the oxygen bound to carbon. The survey spectra for TF, (0.3)r-GOTF, (0.2)r-GOTF, (0.1)r-GOTF and r-TF nanocomposites are shown in supplementary Figure S2. C 1s, O 1s, Ti 2p and Fe 2p are observed as the major constituents.

Raman Analysis
Nanocomposites were analyzed by Raman spectroscopy to study the crystal structure (Figure 4a-e). Hematite (α-Fe 2 O 3 ) is a crystal form of iron oxide with a D 6 3d crystal space group and seven characteristic Raman vibration modes [64].  [38,54]. They appeared to have relatively low intensity, and this meant a small amount of Fe 2 TiO 5 was present in the composite.  The crystallographic defects define the D-band, whereas the sp 2 hybridized carbon atoms in the carbon network define the G-band [38]. The intensity ratio (ID/IG) is a quality measure of graphene derivatives based on the extent of flaws in their graphene-like structure [65]. In other words, the degree of functional and disordered sites in graphene-based The crystallographic defects define the D-band, whereas the sp 2 hybridized carbon atoms in the carbon network define the G-band [38]. The intensity ratio (I D /I G ) is a quality measure of graphene derivatives based on the extent of flaws in their graphene-like structure [65]. In other words, the degree of functional and disordered sites in graphenebased materials is represented by the I D /I G ratio. The variation of the I D /I G ratios of GO, (0.3)r-GOTF, (0.2)r-GOTF and (0.1)r-GOTF is shown in Figure 4b. The I D /I G ratio increases from 1.0 to 3.5 as reduction increases (GO < (0.3)r-GOTF < (0.2)r-GOTF < (0.1)r-GOTF). Suggested here is that the creation of small-sized sp 2 carbon domains or an increase in the fraction of edges is a result of reduction by the ascorbic acid.
Furthermore, as shown in Supplementary Figure S3, the D band of the nanocomposites has been blue-shifted away from the G band, further suggesting that reduction increased [63]. The rise in I D /I G values with the increasing range of reduction in the nanocomposites strongly emphasizes that defects created in the reduced samples were due to the removal of oxygen groups. A reduction of full width at half maximum (FWHM) ( Figure S3) in all the composites upon increasing the degree of reduction was observed as tabulated in Table 2; it was due to the reduction in the defective graphene-like domains. This finding confirms that the number of defect sites present in the (0.3)r-GOTF, (0.2)r-GOTF and (0.1)r-GOTF composites and the extent of reduction can vary by changing the amount of GO loaded. The presence of amorphous carbon and crystalline (graphene-like) materials is very important in photocatalytic applications. This is due to the simultaneous adsorption and photocatalytic performance. This phenomenon is further explained in Section 3.7. When pure Graphite was oxidized to GO, the I D /I G ratio of the resultant materials increased, indicating a higher level of structural disorder and more evident flaws in the graphene layers were the result of the oxidation process [66]. Following ascorbic acid reduction to produce a graphene-like composite, the I D /I G relationship in the resultant material increased as reduction increased, showing that the exfoliation process integrated more flaws into the structure. The crystallite size (La) and distance between defects (L D ) have been computed using Equations (12) and (13) (see below). In pure graphene, L D is infinite but in extremely disordered graphene it is zero [67].
As demonstrated in Figure 4c, the L a values of all GO-based composites improved as the reduction increased. This finding suggested that the average crystalline size of graphitic domains diminished when increasing the loading of GO. A similar pattern was seen with L D (Figure 4d). Both the variations of L a and L D support the observation made with the variation of the I D /I G ratio. Furthermore, Figure 4e [32,39] . However, the peaks corresponding to the Fe 2 TiO 5 are not present in the XRD pattern. Fe 3+ and Ti 4+ concentrations found by ICP-MS analysis are 5434 mg/L and 1078 mg/L, respectively. FeO and TiO 2 exist in weight percentages of 84.21% and 11.80%, respectively, in the TF material as revealed by the XRF analysis. Therefore, it is evident that the corresponding Ti present in the TF sample is comparatively low, producing a small amount of Fe 2 TiO 5 leading to absence of peaks corresponding to Fe 2 TiO 5 in the XRD pattern. The produced Fe 2 TiO 5 could have been dispersed in TF which would have contributed to no peaks in the XRD pattern. The XRD pattern of GO (Figure 2b) shows a sharp peak at 9.39° corresponding to the (001) atomic plane of graphene oxide [68]. The average crystalline size of the nanoparticles was calculated by the Debye-Scherrer Equation (14), and interlayer distance was calculated by Bragg's Equation (15) [69]. The interlayer distance of GO was calculated as 0.94 nm and the crystallite size was found to be 7.13 nm; it consists of approximately 7 graphene layers. The XRD patterns of (0.3)r-GOTF, (0.2)r-GOTF and (0.1)r-GOTF are shown in Figure 5e-g, respectively, and appear to be identical to the XRD pattern of α-Fe2O3. The diffraction peaks corresponding to GO were not present because the folded structure of GO disappears during the ascorbic acid reduction, while the restacking of the nanosheets was observed when α-Fe2O3 nanoparticles are incorporated into r-GO sheets. The diffractions for the (012), (104), (110), (113), (024), (116), (214) and (300) crystalline planes of α-Fe2O3 were clearly observed with only a slight variation in diffraction angles [32,39]. The interlayer distance and crystalline size have been calculated based on the (104) plane of α-Fe2O3 and the results are summarized in Table 3. Figure 5h shows the XRD pattern of the r-TF nanocomposite, synthesized by reducing TF by ascorbic acid. It highlights the presence of Fe2TiO5 and α-Fe2O3, and the crystallographic data are consistent The XRD pattern of GO (Figure 2b) shows a sharp peak at 9.39 • corresponding to the (001) atomic plane of graphene oxide [68]. The average crystalline size of the nanoparticles was calculated by the Debye-Scherrer Equation (14), and interlayer distance was calculated by Bragg's Equation (15) [69]. The interlayer distance of GO was calculated as 0.94 nm and the crystallite size was found to be 7.13 nm; it consists of approximately 7 graphene layers. The XRD patterns of (0.3)r-GOTF, (0.2)r-GOTF and (0.1)r-GOTF are shown in Figure 5e-g, respectively, and appear to be identical to the XRD pattern of α-Fe 2 O 3 . The diffraction peaks corresponding to GO were not present because the folded structure of GO disappears during the ascorbic acid reduction, while the restacking of the nanosheets was observed when α-Fe 2 O 3 nanoparticles are incorporated into r-GO sheets. The diffractions for the (012), (104), (110), (113), (024), (116), (214) and (300) crystalline planes of α-Fe 2 O 3 were clearly observed with only a slight variation in diffraction angles [32,39].
The interlayer distance and crystalline size have been calculated based on the (104) plane of α-Fe 2 O 3 and the results are summarized in Table 3. Figure 5h shows the XRD pattern of the r-TF nanocomposite, synthesized by reducing TF by ascorbic acid. It highlights the presence of  [64]. However, the XRD pattern of r-TF confirmed the surface-reducing effect of α-Fe 2 O 3 TF by L-ascorbic acid. This is because the peaks corresponding to Fe 2 TiO 5 appeared in the XRD pattern, suggesting that the material which covered Fe 2 TiO 5 was removed upon treatment with L-ascorbic acid. The relative percentages of Fe 2 TiO 5 and α-Fe 2 O 3 were calculated based on the integrated peak area, while the r-TF was found to be composed of 84.75% of Fe 2 TiO 5 (15.25%) and α-Fe 2 O 3 (84.75%). where,

XRF Analysis
XRF analysis quantified the elemental composition of fabricated nanocomposites (Table 4). This investigation shows that ilmenite sand consisted of a number of minor impurities apart from the dominating Ti (48.87%) and Fe (42.81%) species including Al, V, Si, P, K, Ca, Cr, Mn, Zn and Zr. Similarly, in the other nanocomposites Ti and Fe are present as the major constituents and less than 4% of trace impurities such as Al, Si, Cr, Mn and Zn were detected. Impurities including V, P, K, Ca and Zr which were present in ilmenite were not detected. These impurities were removed during leaching in conc. HCl and during washing of the obtained precipitate. The amount of Fe in the fabricated nanocomposites is larger than that of the natural ilmenite, which is due to the addition of FeSO 4 .7H 2 O externally during the production.

Optical Adsorption Properties (DRS Analysis)
Diffuse reflectance spectroscopy (DRS) is a technique used to study the interaction of light of "highly absorbing materials" such as metals, alloys and semiconductors [71]. The UV-Vis DRS optical absorption properties of the prepared nanocomposite materials are shown in Figure 6a-e. Tauc plots [F(R)hν] n vs. hν (photon energy) were plotted for direct transition using n = 2 as shown in Figure 6f-j to determine the band gaps of the fabricated nanocomposite materials. The Kubelka-Munk function, F(R), is given by Equation (17) and the band gap was determined using the Tauc plot.
where, transition using n = 2 as shown in Figure 6f-j to determine the band gaps of the fabricated nanocomposite materials. The Kubelka-Munk function, F(R), is given by Equation (17) and the band gap was determined using the Tauc plot.

Photocatalytic Degradation
The visible light-driven photodegradation of fabricated nanocomposites was evaluated using MB. Experimental conditions were performed accordingly: catalyst loading (W = 50 mg), initial concentration of MB (C 0 = 20 mg/L), volume of MB solution (V = 50 mL), temperature (T = 25 • C) and pH = 7. The adsorption of MB to the nanocomposites was evaluated for 180 min dark conditions and the photocatalytic activity was determined for 180 min under exposure to visible light. Adsorption-desorption equilibrium was reached within the first 100 min. Adsorption capacities obtained for TF, (0.3)r-GOTF, (0.2)r-GOTF, (0.1)r-GOTF, r-TF are 5.7, 7.7, 6.8, 6.0 and 12.4 mg/g, respectively as tabulated in Table 5. The overall adsorption and photocatalytic degradation process is shown in Figure 7a. The kinetics parameters of the pseudo-first-order and pseudo-second-order dark adsorption model are tabulated in Table 5. The best fitting model was chosen based on the linear regression correlation coefficient (r 2 ) values. Equations (18) and (19) were used to express the linear form of the pseudo-first-order and pseudo-second-order adsorption kinetic models, respectively, and the respective plots are shown in Figure 7b,c [72,73]. It can be concluded that the adsorption of MB molecules to the composites follows the pseudo-second-order model as depicted by the higher correlation coefficient (r 2 ) value ( Table 5). The calculated q e values matched the experimental q e, exp values very well. This finding suggests that physical adsorption dominates the adsorption of MB dye molecules onto the composite surface: ln q e − q t = ln q e − k 1 t (18) t q t = 1 k 2 q e 2 + 1 q e t (19) where, t = time (min) q e = equilibrium absorption capacity mg g q t = adsorption capacity at time t mg g k 1 = first order rate constant (L/min) k 2 = sec ond order rate constant (g/mg * min) Furthermore, the r-TF photocatalyst shows the highest second-order rate constant value of 0.024 g mg −1 min −1 while that of other composite materials, i.e., (0.1)r-GOTF, (0.2)r-GOTF, (0.3)r-GOTF and TF report smaller rate constant values, these being 0.012, 0.015, 0.013 and 0.018 g mg −1 min −1 , respectively. The equilibrium adsorption capacity of photocatalysts follows the order of r-TF > (0.3)r-GOTF > (0.2)r-GOTF > (0.1)r-GOTF > TF. The enhanced adsorptive performance of r-TF could be attributed to the formation of a porous structure during the ascorbic acid treatment. This is despite the fact that increasing the loading of GO into photocatalysts meant that adsorptive performance improved. GO consists of oxygen functional groups, such as carboxyl groups and hydroxyl groups, bearing on the basal planes and edges of GO sheets. The (0.3)r-GOTF, (0.2)r-GOTF and (0.1)r-GOTF composites were subjected to the 1M ascorbic acid-based reducing process.
During the reducing process, functional groups present in GO were eliminated to some extent by yielding graphene-like material on the surface near the metal oxide nanoparticles. According to the Raman analysis (Figure 4o-q and Table 2), (0.3)r-GOTF exhibits the highest L a and L D values, suggesting a large amount of defects compared to the other two samples of (0.2)r-GOTF and (0.1)r-GOTF. From Figure 4i and Table 2, it can be seen that compared with (0.1)r-GOTF and (0.2)r-GOTF, the I D /I G ratio of (0.3)r-GOTF is further increased, indicating more defects are concentrated in the (0.3)r-GOTF sample. These results suggested the presence of more functional groups in (0.3)r-GOTF, compared to the (0.1)r-GOTF and (0.2)r-GOTF. Such a presence triggers strong electrostatic interaction between the negative surface and positively charged methyl nitride group [(CH 3 ) 2 N + ] of cationic MB dye molecule [72,74].
Photocatalytic degradation kinetics of organic molecules usually follow the Langmuir-Hinshelwood kinetics mechanism as shown in Equation (20) [75].
The apparent kinetic content, denoted by k app , can be incorporated into the equation and simplified when using the following Equations (21) and (22).  Photocatalytic degradation kinetics of organic molecules usually follow the Langmuir-Hinshelwood kinetics mechanism as shown in Equation (20) [75].
The apparent kinetic content, denoted by k , can be incorporated into the equation Simplified differentiation Equation (23) was integrated by applying the boundary conditions to create the photocatalytic degradation rate equation, as shown in Equation (24).
ln C t C 0 = −kt (25) where,  Figure 7d,e show the kinetic parameters of MB degradation as a function of irradiation time exposed to a 1240 Wm −2 LED light (580 nm) source. Figure 7d indicates the overall degradation process as a second-order polynomial arrangement with two independent slopes for the complete degradation. Table 6 depicts the equations used to calculate polynomial regression and polynomial regression coefficient values. The polynomial regression coefficient values fitted the experimental data of the photodegradation process. The proposed mathematical arrangement clearly demonstrated that the degradation process was followed by a second-order polynomial fit with two intermediate rates determining elementary reactions. The first 70 min of the degradation process displayed a linear variation, establishing a starting rate slope for the total process. Despite this, the remaining 110 min slowed down the deterioration process by producing a second slope for the total degradation. This was due to the production of intermediate pollutants. Figure 7e depicts the photodegradation of MB over the first 70 min, and the estimated linear regression coefficients and rate constants are tabulated in Table 6. Table 6. Linear and polynomial kinetic parameters for visible light photocatalysis. As shown in Figure 7e, the highest rate for the photodegradation of MB (0.033 min −1 ) was found with (0.3)r-GOTF because of the simultaneous adsorptive and photocatalytic mechanism, whereas r-TF degrades the slowest due to the creation of defective domains in the crystal lattices in α-Fe 2 O 3 . The impact of the defective domain formation effect during the ascorbic acid reduction of TF has been further explained in the Raman (Section 3.3) and XRD (Section 3.4) discussions. The calculated initial degradation rate constants of TF, (0.3)r-GOTF, (0.2)r-GOTF, (0.1)r-GOTF and r-TF were determined as 0.014, 0.033, 0.015, 0.013 and 0.012 min −1 , respectively (Figure 7e). The rate constant of (0.3)r-GOTF is double that of (0.2)r-GOTF. Figure 7f exhibits the elimination of MB through the adsorption and photocatalysis employing various photocatalysts. MB was effectively removed via adsorption by all the catalysts in which r-TF dominated the activity (55.27%) and the catalysts' performance varied as follows: r-TF > (0.3)r-GOTF > (0.2)r-GOTF > (0.1)r-GOTF > TF.
The residual dye concentration after reaching the adsorption-desorption equilibrium was subjected to photocatalysis and the photocatalytic elimination of MB was varied as TF, (0.3)r-GOTF, (0.2)r-GOTF, (0.1)r-GOTF, and r-TF. Here, the respective percentage removals were 66.68, 98.18, 74.24, 75.13, and 67.55%, in which the (0.3)r-GOTF performed the best. Furthermore, as revealed by the TEM analysis of (0.3)r-GOTF the crystalline r-GO and non-crystalline GO domains were located at the edges of nanocomposites and located away from the metal nanoparticles. Moreover, the variation of I D /I G ratio and L D evident in Figure 4b,d obtained from the Raman interpretation showed that the (0.3)r-GOTF nanocomposite has more functional groups than (0.1)r-GOTF after the ascorbic acid reduction.
The most important characteristic of adsorptive and photocatalytic performance is the extent of reduction. If the material has been greatly reduced, the absorptive performance may suffer due to decreased electrostatic attraction between the negatively charged photocatalyst surface and the positively charged MB molecule [76]. It is critical to precisely determine the appropriate degree of reduction by considering the total performance of the photocatalyst due to simultaneous adsorption and photodegradation. In summary, adequate defect concentration can significantly boost the r-GO/GO catalytic activity, whereas less defects will result in maximized charge carrier mobility. It may, however, limit the affinity towards the cationic MB dye molecule [77]. As a result, the recombination of excited electron-hole pair recombination centers may occur, limiting the samples' photocatalytic activity. This concept further explains the photocatalytic activity of TF being greater than that of (0.1)r-GOTF. The results reported above further confirmed the (0.3)r-GOTF system's better photocatalytic degradation, made possible by the appropriate degree of reduction. This has been further explained in Section 3.3.
Radical scavenging experiments were conducted to investigate the principal active radical species responsible for the degradation of MB in the presence of (0.3)r-GOTF. EDTA and IPA were added to the reaction mixture to test the impact of h + and • OH for the photodegradation of MB. Figure 8a depicts the variation of MB concentration with time showing the adsorption-desorption equilibrium followed by the photodegradation of MB upon exposure to visible light irradiation. Dark adsorption lasted for 180 min, and readings were collected for 100 min under visible light irradiation. Figure 8b depicts first-order kinetics whereas Figure 8c shows the estimated rate constants. No external reagents were added for the control experiment. Linear first-order rate constants in the control system and those with IPA and EDTA are 0.021, 0.009, and 0.003 min −1 , respectively. As shown in Figure 8d, the concentrations of MB following the degradation process in the presence of EDTA, and IPA were 10.26, and 4.97, respectively, and the degradation efficiencies were 53.81, and 77.58%, respectively. Conversely, it was 94.63% in the control experiment.
The IPA and EDTA system substantially inhibited the ultimate degradation efficiency of MB, suggesting that both • OH radicals and h + are responsible for the degradation of MB where the contribution of h + to the photodegradation of MB is greater than that of • OH radicals. Effect of persulfate (PS) ions on the photodegradation of MB was studied. The PS-added system demonstrated a rapid drop in MB concentration, reaching 0.35 mg/L in 75 min. The PS system was 2.61 times quicker than the control system, degrading 98.42% of MB. PS increased visible light-driven photocatalysis by producing • SO 4 − radicals, as shown in Equations (26) and (27). Further, such produced • SO 4 − radicals produce • OH with the reaction of OH − as shown in the reactions (28) and (29). Both • SO 4 − and • OH degrade MB increasing the rate of the reaction. Figure 8e shows the MB's change of color after the degradation process. The IPA and EDTA system substantially inhibited the ultimate degradation efficiency of MB, suggesting that both • OH radicals and h + are responsible for the degradation of MB where the contribution of h + to the photodegradation of MB is greater than that of • OH radicals. Effect of persulfate (PS) ions on the photodegradation of MB was studied.
The PS-added system demonstrated a rapid drop in MB concentration, reaching 0.35 mg/L in 75 min. The PS system was 2.61 times quicker than the control system, degrading Reusability of the best performing (0.3)r-GOTF catalyst (Figure 8e) was determined to figure out the suitability of the catalyst for industrial applications. It was evident that the drop of the conversion of MB was insignificant moving from cycle 1 to 5 and the slight drop is due to the loss of the material during washing and due to the coagulation of dye molecules in the porous system.

Mechanism of the Photocatalytic Activity
Based on the aforementioned results of different characterization analyses and lightdriven degradation studies, Figure 6 proposes a probable synergistic mechanism of (0.3)r-GOTF. The proposed structure of (0.3)r-GOTF nanocomposite composed of Fe 2 TiO 5 /α-Fe 2 O 3 /r-GO/GO and the photocatalytic mechanism of nanocomposite is defined as follows. The band gaps for Fe 2 TiO 5 and α-Fe 2 O 3 found by diffuse reflectance spectroscopy are 2.25 and 2.20 eV, respectively. The conduction band and valance band potentials were determined using Equations (30) and (31), respectively.
where, X-Absolute electronegativity of the semiconductor, which is defined as the geometric mean of the absolute electronegativity of the constituent atoms E C -Energy of free electrons on the hydrogen scale  Table 7 lists the parameters used to calculate the VB and CB energy positions, and Figure 9a depicts the derived Type II band alignment in the Fe 2 TiO 5 and α-Fe 2 O 3 binary composite system.  Figure 9. (a) Type II band alignment for Fe2TiO5 and α-Fe2O3 binary composite and (b) elucidated visible light-driven photodegradation mechanism of (0.3)r-GOTF.
When exposed to visible light, both α-Fe2O3 and Fe2TiO5 simultaneously generate electron-hole pairs because they are visible light sensitive semiconductors. In this scenario, r-GO can act as an electron reservoir, rapidly capturing and transporting photogenerated electrons from the CB of α-Fe2O3. Meanwhile, electrons at the CB of α-Fe2O3 migrate to the CB of Fe2TiO5 via the semiconductor heterojunction. This is due to the favorable potential difference in addition to the self-photogenerated electrons that would When exposed to visible light, both α-Fe 2 O 3 and Fe 2 TiO 5 simultaneously generate electron-hole pairs because they are visible light sensitive semiconductors. In this scenario, r-GO can act as an electron reservoir, rapidly capturing and transporting photo-generated electrons from the CB of α-Fe 2 O 3 . Meanwhile, electrons at the CB of α-Fe 2 O 3 migrate to the CB of Fe 2 TiO 5 via the semiconductor heterojunction. This is due to the favorable potential difference in addition to the self-photogenerated electrons that would locate at the CB of Fe 2 TiO 5 . The electrons in the CB of Fe 2 TiO 5 would also move into the conductive network of r-GO sheets, as a result of the coupling interfacial contact between r-GO and semiconductor heterojunction. Meanwhile the photo-generated holes in the VB of Fe 2 TiO 5 move to the VB of α-Fe 2 O 3 . Therefore, Type II band alignment in (0.3)r-GOTF prevents photo-generated electron-hole pair recombination. The
Neutralization of OH − groups by photo holes to produce OH • radicals: 4. Neutralization of O •− 2 by protons:

5.
Transient hydrogen peroxide formation and dismutation of oxygen:

6.
Decomposition of H 2 O 2 and the second reduction of oxygen:

7.
Oxidation of the MB by OH • radicals:

8.
Direct oxidation by reaction with holes:

Antibacterial Activity against Escherichia coli
The antibacterial activity of TF, (0.3)r-GOTF, (0.2)r-GOTF, (0.1)r-GOTF and r-TF was evaluated for its effectiveness against Gram-negative bacteria E. coli (Figure 10). The maximum antibacterial activity against Escherichia coli resulted in the presence of TF leading to the removal of 82.5%. Antibacterial activity of GO-coupled nanocomposites followed the order of (0.3)r-GOTF > (0.2)r-GOTF > (0.1)r-GOTF while that of r-TF was lower than TF and (0.3)r-GOTF as shown in Figure 10a,b. The nanocomposites' inhibition of bacteria growth is accompanied by four primary mechanisms (Figure 10c), namely: (1) the disruption of cell wall by nanocomposites; (2) migration of nanocomposites into the cells and interfering with the ribosomes, DNA replication, and interrupting ATP production; (3) perforation of the cellular membrane; and (4) disruption of cellular membrane by reactive oxygen species [38]. Upon excitation by light, the photon energy generates electronhole pairs on the surface of nanocomposites, which produce • OH radicals which can inhibit the growth of bacteria [78,79]. It can be deduced that the TF nanomaterial which exhibited less photocatalytic activity compared to (0.3)r-GOTF, has predominantly deterred the growth of bacteria via mechanisms (1), (2) and (3) with a minimum contribution from mechanism (4). This is due to the relatively small amount of reactive oxygen species generated as revealed in the photodegradation study. However, the antibacterial activity of GO-coupled nanocomposites is lower than that of TF as the amount of nano-metal oxides present within the considered weight is low, signifying that mechanisms (1), (2) and (3) dominate mechanism (4) in preventing the growth of bacteria. The antibacterial activity of r-TF was poorer than that of TF, suggesting the antibacterial activity caused by α-Fe2O3 is comparatively superior to Fe2TiO5 since more of the Fe2TiO5 is exposed to bacterial cells than Fe2O3 upon reduction by ascorbic acid. Based on this, it could be concluded that inhibiting the growth of E. coli via mechanisms (1), (2) and (3) is more effective than mechanism (4). Furthermore, the size, surface charge and hydrophobicity influence the antibacterial activity of the fabricated nanocomposites.

Conclusions
Employing ilmenite and graphite powders as natural materials, we developed a facile ultrasonic and hydrothermal technique for fabricating the r-GO/GO/α-Fe2O3/Fe2TiO5 nanocomposite. Three distinct r-GO/GO/α-Fe2O3/Fe2TiO5 composites were created by varying the degree of reduction in GO domains, with ascorbic acid serving as the reduction agent. In this work, 30% loading of GO to α-Fe2O3/Fe2TiO5 photocatalyst ((0.3)r-GOTF) demonstrated better photodegradation efficiency of MB under visible light irradiation than pure α-Fe2O3/Fe2TiO5. The initial visible light-driven photodegradation rates of (0.3)r-GOTF and α-Fe2O3/Fe2TiO5 (TF) were 0.033 min −1 and 0.014 min −1 , respectively. These enhancements can be attributed to the better charge transportation, separation and simultaneous adsorption and photodegradation, properties exhibited by (0.3)r-GOTF. Electrons photogenerated by α-Fe2O3 and Fe2TiO5 move over the conductive r-GO matrix, producing O2 •− and HO2 • radicals, while holes produce OH • by interacting with the adsorbed water. Under visible light, these radicals successfully photodegraded MB molecules. The sacrificial agent investigation and DRS analysis both confirmed charge carrier The antibacterial activity of the GO derivatives is affected by distinctive physicochemical features, i.e., orientation, size, shape, structural defects, and surface functional groups wielding a substantial impact on the biological response [80,81]. Moreover, the efficacy of the GO-coupled nanocomposites in discouraging bacterial cell growth is primarily influenced by their surface charge, size, and hydrophobicity [78]. The fabricated (0.3)r-GOTF nanocomposite was found to be between 30 nm to 80 nm, offering a high surface-to-volume ratio for the interaction with bacterial cells. A previous study proposed that relatively large GO sheets can cover bacterial cells more readily and once fully covered and biologically detached from their environment, cells cannot proliferate, resulting in cell viability loss observed in the subsequent colony counting test [78]. The r-GO formed following the reduction with ascorbic acid is hydrophobic in nature and the nanosheets tend to aggregate via π−π stacking.
Consequently, bacterial cell adsorption occurs rapidly and strongly on hydrophobic surfaces, while adhesion on hydrophilic substrates follows a reversible adhesion model [78,80]. The negative charge imparted by coupling TF with GO, followed by reduction from ascorbic acid, plays a key role in lowering the overall antibacterial activity of the GO-coupled nanocomposites. Weak electrostatic interaction between the negatively charged E. coli cell wall and negatively charged GO-coupled nanocomposite surface owing to the charge repulsion, accounts for the muted antibacterial activity when compared to that of TF. The GO-coupled nanocomposites mainly adhered to mechanism (4) as the amounts of radicals generated are comparatively higher than that of TF; this agrees with the overall adsorption and photocatalysis degradation activity against methylene blue. Among GO-coupled nanocomposites, (0.3)r-GOTF with the highest photocatalytic activity demonstrated the best antibacterial activity thus confirming the aforementioned statement.
However, the antibacterial activity of GO-coupled nanocomposites is lower than that of TF as the amount of nano-metal oxides present within the considered weight is low, signifying that mechanisms (1), (2) and (3) dominate mechanism (4) in preventing the growth of bacteria. The antibacterial activity of r-TF was poorer than that of TF, suggesting the antibacterial activity caused by α-Fe 2 O 3 is comparatively superior to Fe 2 TiO 5 since more of the Fe 2 TiO 5 is exposed to bacterial cells than Fe 2 O 3 upon reduction by ascorbic acid. Based on this, it could be concluded that inhibiting the growth of E. coli via mechanisms (1), (2) and (3) is more effective than mechanism (4). Furthermore, the size, surface charge and hydrophobicity influence the antibacterial activity of the fabricated nanocomposites.

Conclusions
Employing ilmenite and graphite powders as natural materials, we developed a facile ultrasonic and hydrothermal technique for fabricating the r-GO/GO/α-Fe 2 O 3 /Fe 2 TiO 5 nanocomposite. Three distinct r-GO/GO/α-Fe 2 O 3 /Fe 2 TiO 5 composites were created by varying the degree of reduction in GO domains, with ascorbic acid serving as the reduction agent. In this work, 30% loading of GO to α-Fe 2 O 3 /Fe 2 TiO 5 photocatalyst ((0.3)r-GOTF) demonstrated better photodegradation efficiency of MB under visible light irradiation than pure α-Fe 2 O 3 /Fe 2 TiO 5 . The initial visible light-driven photodegradation rates of (0.3)r-GOTF and α-Fe 2 O 3 /Fe 2 TiO 5 (TF) were 0.033 min −1 and 0.014 min −1 , respectively. These enhancements can be attributed to the better charge transportation, separation and simultaneous adsorption and photodegradation, properties exhibited by (0.3)r-GOTF. Electrons photogenerated by α-Fe 2 O 3 and Fe 2 TiO 5 move over the conductive r-GO matrix, producing O 2 •− and HO 2 • radicals, while holes produce OH • by interacting with the adsorbed water. Under visible light, these radicals successfully photodegraded MB molecules. The sacrificial agent investigation and DRS analysis both confirmed charge carrier recombination and light absorption augmentation. XRD, Raman, XPS and TEM analyses reveal the crystal structures and morphological features of fabricated nanocomposites.
The TF and (0.3)r-GOTF composites were effective in inhibiting E. coli growth when exposed to visible light. The photosterilization and inhibition of TF (82.5%) was greater than (03)r-GOTF (56.5%). The r-GO produced after ascorbic acid reduction is hydrophobic in nature, and the nanosheets prefer to cluster via stacking. As a result, bacterial cell adsorption on hydrophobic surfaces happens quickly and robustly. The negative charge supplied by coupling TF with GO, followed by reduction from ascorbic acid, is critical in reducing the overall antibacterial activity of the GO-linked nanocomposites. Because of charge repulsion, the weak electrostatic connection between the negatively charged E. coli cell wall and the negatively charged GO-linked nanocomposite surface explains the diminished antibacterial activity when compared to that of TF. The present study describes a low-cost, simple approach for assembling r-GO into nanostructured semiconductors for use in removing MB dye from wastewater and photosterilization of E. coli for environmental remediation strategies.

Data Availability Statement:
The generated data during the study are available from the corresponding author upon request.