Influence of Solvent-Dependent Morphology on Molecular Doping and Charge Transport in Conductive Thiophene Polymer

The utility of a solvent is one of the key factors that impacts resultant film morphology. However, the effect of solvent-dependent morphology on the doping process and electrical conductivity has not been adequately elucidated. In this work, we compared the morphology of chloroform- and chlorobenzene-processed thiophene polymer films and investigated how the choice of solvent influences film morphology, doping level, charge transport properties, and thus electrical conductivity. It was found that the film drop-casted from chloroform exhibits better crystallinity than that drop-casted from chlorobenzene. The crystallinity has negligible impact on the doping level but significant impact on charge transport properties. As a result, the chloroform-processed film shows a higher electrical conductivity of up to 408 S cm−1 due to a high carrier mobility related to the continuously crystalline domains in film. This finding indicates that the choice of solvent for preparation of film, which strongly correlated with molecular orientation, is a new strategy to optimize the electrical conductivity of doped polymers.


Introduction
Molecular doping has been a promising way to control the electrical properties of polymer semiconductors [1,2]. The doped conjugated polymers are widely used as the active layers in the organic field-effect transistor, organic light-emitting diode, and organic thermoelectric devices [3][4][5][6][7]. Molecular doping will improve the electrical conductivity (σ) by increasing free carriers along polymer chains via charge transfer between polymer and dopant. To achieve a high σ, an extremely high doping concentration is usually required to obtain a high carrier concentration (n) [8,9]. However, the addition of large amounts of dopants results in a disruption of the polymer film morphology and induces a drop in carrier mobility (µ) [10], which leads to a low σ according to the relationship of σ = neµ. [8] Therefore, it is still challenging to effectively dope polymers without restraining the charge transport in polymer film. There have been great efforts recently to overcome film quality issues of heavily doped conjugated polymers. For example, several doping methods are developed in which the dopants are applied to a pre-casted polymer film, including vapor-phase deposition [11,12], immersion doping [13,14], sequential doping [15,16], etc. Other attention has been given to the modification of chemical structures of polymers to leave dopants in side chains without disturbing the packing of polymer backbones [17,18]. For instance, the introduction of π-conjugated subunits as a spacer can reduce the number of side chains and improve the accommodation of dopants into Materials 2022, 15, 3293 2 of 9 films [19]. Additionally, polythiophenes with oligo(ethylene oxide) side chains show high electrical conductivity of up to 100 S cm −1 and is attributed to the good miscibility between polar side chains and dopants [20,21]. It is accepted that the crystalline film of pristine polymers is beneficial for achieving good charge transport properties. The crystalline behavior of polymers is strongly related to the properties of the solvent for dissolving the given polymer [22,23]. However, how the solvent affects the solid-state orientation of pristine film, and therefore the molecular doping and charge transport in doped film, has not been sufficiently elucidated.
Herein, we investigate the influence of solvent for dissolving the polymer on the crystallinity of pristine polymer films, doping efficiency and charge transport by employing a thiophene polymer, PODTT-4T, drop-casted from chloroform (CF) and chlorobenzene (CB) solution, respectively. It is found that the pristine film prepared from CF solution (PODTT-4T CF ) shows a preferentially edge-on orientation and a highly ordered microstructure while the film prepared from CB solution (PODTT-4T CB ) exhibits a lower crystallinity with both edge-on and face-on orientations inside. PODTT-4T CF film shows a much higher σ of up to 408 S cm −1 compared to that of the PODTT-4T CB (280 S cm −1 ) although these two films have a similar doping level if doped by FeCl 3 . The higher σ of doped PODTT-4T CF can be ascribed to the higher carrier mobility due to larger crystalline domains upon doping compared to the PODTT-4T CB film. We propose that the choice of solvent to dissolve PODTT-4T determines the polymer crystalline behavior in the solid state, which prefers to dominate the transport property of free carriers rather than the doping efficiency.

Synthesis and Characterization of Polymer
Polymer PODTT-4T was synthesized by Stille coupling reaction [24], copolymerizing 5,5 -dibromo-4,4 -bis(2-octyldodecyl)-2,2 -bithiophene and 2,6-bis(trimethylstannyl)thieno [2 ,3 :4,5]thieno [3,2-b]thieno [2,3-d]thiophene (4T) (Scheme 1). The large conjugated unit is used to allow good planarity, promoting the charge delocalization. The long and branched alkyl chains ensure the solubility of copolymers in common organic solvents, such as CF and CB. The synthesis details and basic properties of the polymer are given in the supporting information. PODTT-4T shows a high number-average molecular weight (M n ) of 22.2 kDa with a polydispersity index (PDI) of 2.08 ( Figure S1). It exhibits excellent thermal stability with a decomposition temperature (5% weight loss) of about 395°C measured by thermogravimetric analysis (TGA) ( Figure S2). Differential scanning calorimetry (DSC) analysis shows a melting transition peak at 296 • C and a crystallization peak at 271 • C during the heating and cooling cycle ( Figure S3), respectively, which suggests the existence of crystalline phases in the polymer [25]. PODTT-4T shows the highest occupied molecular orbit (HOMO) level around −5.26 eV by employing the cyclic voltammetry (CV) ( Figure S4), which is beneficial for p-doping by FeCl 3 [26]. The pristine films were prepared by dissolving the polymer into CF or CB with a concentration of 5 mg mL −1 . The polymer solution was drop-casted on the glass substrate and dried at ambient temperature. Then, the films were annealed at 160 • C for 30 min in the glovebox. The doped films were prepared by immersing the annealed films into FeCl 3 solution (in acetonitrile, 5 mg mL −1 ) for 10 min. of polymer backbones [17,18]. For instance, the introduction of π-conjugated subunits as a spacer can reduce the number of side chains and improve the accommodation of dopants into films [19]. Additionally, polythiophenes with oligo(ethylene oxide) side chains show high electrical conductivity of up to 100 S cm −1 and is attributed to the good miscibility between polar side chains and dopants [20,21]. It is accepted that the crystalline film of pristine polymers is beneficial for achieving good charge transport properties. The crystalline behavior of polymers is strongly related to the properties of the solvent for dissolving the given polymer [22,23]. However, how the solvent affects the solid-state orientation of pristine film, and therefore the molecular doping and charge transport in doped film, has not been sufficiently elucidated. Herein, we investigate the influence of solvent for dissolving the polymer on the crystallinity of pristine polymer films, doping efficiency and charge transport by employing a thiophene polymer, PODTT-4T, drop-casted from chloroform (CF) and chlorobenzene (CB) solution, respectively. It is found that the pristine film prepared from CF solution (PODTT-4TCF) shows a preferentially edge-on orientation and a highly ordered microstructure while the film prepared from CB solution (PODTT-4TCB) exhibits a lower crystallinity with both edge-on and face-on orientations inside. PODTT-4TCF film shows a much higher σ of up to 408 S cm −1 compared to that of the PODTT-4TCB (280 S cm −1 ) although these two films have a similar doping level if doped by FeCl3. The higher σ of doped PODTT-4TCF can be ascribed to the higher carrier mobility due to larger crystalline domains upon doping compared to the PODTT-4TCB film. We propose that the choice of solvent to dissolve PODTT-4T determines the polymer crystalline behavior in the solid state, which prefers to dominate the transport property of free carriers rather than the doping efficiency.

Synthesis and Characterization of Polymer
Polymer PODTT-4T was synthesized by Stille coupling reaction [24], copolymerizing 5,5'-dibromo-4,4'-bis(2-octyldodecyl)-2,2'-bithiophene and 2,6-bis(trimethylstannyl)thieno [2',3':4,5]thieno [3,2-b]thieno [2,3-d]thiophene (4T) (Scheme 1). The large conjugated unit is used to allow good planarity, promoting the charge delocalization. The long and branched alkyl chains ensure the solubility of copolymers in common organic solvents, such as CF and CB. The synthesis details and basic properties of the polymer are given in the supporting information. PODTT-4T shows a high number-average molecular weight (Mn) of 22.2 kDa with a polydispersity index (PDI) of 2.08 ( Figure S1). It exhibits excellent thermal stability with a decomposition temperature (5% weight loss) of about 395 ℃ measured by thermogravimetric analysis (TGA) ( Figure S2). Differential scanning calorimetry (DSC) analysis shows a melting transition peak at 296 °C and a crystallization peak at 271 °C during the heating and cooling cycle ( Figure S3), respectively, which suggests the existence of crystalline phases in the polymer [25]. PODTT-4T shows the highest occupied molecular orbit (HOMO) level around −5.26 eV by employing the cyclic voltammetry (CV) ( Figure S4), which is beneficial for p-doping by FeCl3 [26]. The pristine films were prepared by dissolving the polymer into CF or CB with a concentration of 5 mg mL −1 . The polymer solution was drop-casted on the glass substrate and dried at ambient temperature. Then, the films were annealed at 160 °C for 30 min in the glovebox. The doped films were prepared by immersing the annealed films into FeCl3 solution (in acetonitrile, 5 mg mL −1 ) for 10 min.

The Doping Level of Films Prepared from Two Solvents
The doping behavior of PODTT-4T CF and PODTT-4T CB films is characterized by using UV-vis-NIR absorption spectra. It is observed that pristine PODTT-4T CF and PODTT-4T CB films show a similar absorption spectrum (Figure 1a). The maximum peak appears at 605 nm and no obvious absorption is observed over 700 nm. In addition, there is no obvious peak shift or absorption intensity change between these two films although the different solvents usually induce the wavelength shift of shoulder peaks due to the change of backbone interactions [27]. This indicates PODTT-4T chains dissolved in CF and CB probably adopt a similar π-π stacking distance in the solid state. Upon doping with FeCl 3 , the intensity of the neutral absorption peak of PODTT-4T CF and PODTT-4T CB films is significantly bleached. Meanwhile, the absorption band ascribed to the (bi)polarons appears above 800 nm in the near-infrared region. In order to compare the doping levels of the two films, two absorption bands-neutral absorption band I (380-710 nm) and (bi)polaron absorption band II (710-2000 nm)-are assigned. The ratio (R) of the integral area of these two absorption bands (band II /band I ) is calculated (Table S1). It is found that the doped PODTT-4T CF film and PODTT-4T CB film have a similar R value suggesting similar doping levels in the two films [21]. This indicates that CF and CB have a negligible effect on the polymer doping level under the same conditions. Raman spectroscopy ( Figure 1b) is further employed to characterize and analyze the vibrational mode of PODTT-4T CF and PODTT-4T CB upon doping. All intensities are normalized at the vibrational peak of mode A, which corresponds to the C=C symmetric stretching vibration on the 4T core. Mode B and mode C correspond to the C=C stretching vibration and the C=C/C-C stretching/shrinking on the thiophene ring, respectively [28]. These vibrational modes are sensitive to the structural order and π-electron delocalization [29]. The positions of mode B and mode C of the pristine PODTT-4T CF film and PODTT-4T CB film are almost the same while mode A of PODTT-4T CB is wider than that of PODTT-4T CF , indicating more disordered structures existing in the former film. Upon doping with FeCl 3 , both mode A and mode C shift to much lower wavenumbers, suggesting that the benzenoid structures along the conjugated backbone are transformed into quinoid structures. It should be noted that the shift of mode C of PODTT-4T CF is more significant (Table S2) and mode A is much wider compared to those of PODTT-4T CB film, which means the dopants have a significant influence on the molecular packing of polymer chains in PODTT-4T CF film. These results demonstrate that the doping level is not dependent on the molecular orientation in PODTT-4T film. Scheme 1. The synthetic route to the polymer PODTT-4T.

The Doping Level of Films Prepared from Two Solvents
The doping behavior of PODTT-4TCF and PODTT-4TCB films is characterized by using UV-vis-NIR absorption spectra. It is observed that pristine PODTT-4TCF and PODTT-4TCB films show a similar absorption spectrum (Figure 1a). The maximum peak appears at 605 nm and no obvious absorption is observed over 700 nm. In addition, there is no obvious peak shift or absorption intensity change between these two films although the different solvents usually induce the wavelength shift of shoulder peaks due to the change of backbone interactions [27]. This indicates PODTT-4T chains dissolved in CF and CB probably adopt a similar π-π stacking distance in the solid state. Upon doping with FeCl3, the intensity of the neutral absorption peak of PODTT-4TCF and PODTT-4TCB films is significantly bleached. Meanwhile, the absorption band ascribed to the (bi)polarons appears above 800 nm in the near-infrared region. In order to compare the doping levels of the two films, two absorption bands-neutral absorption band Ⅰ (380-710 nm) and (bi)polaron absorption band Ⅱ (710-2000 nm)-are assigned. The ratio (R) of the integral area of these two absorption bands (band Ⅱ /band Ⅰ ) is calculated (Table S1). It is found that the doped PODTT-4TCF film and PODTT-4TCB film have a similar R value suggesting similar doping levels in the two films [21]. This indicates that CF and CB have a negligible effect on the polymer doping level under the same conditions. Raman spectroscopy (Figure 1b) is further employed to characterize and analyze the vibrational mode of PODTT-4TCF and PODTT-4TCB upon doping. All intensities are normalized at the vibrational peak of mode A, which corresponds to the C=C symmetric stretching vibration on the 4T core. Mode B and mode C correspond to the C=C stretching vibration and the C=C/C-C stretching/shrinking on the thiophene ring, respectively [28]. These vibrational modes are sensitive to the structural order and π-electron delocalization [29]. The positions of mode B and mode C of the pristine PODTT-4TCF film and PODTT-4TCB film are almost the same while mode A of PODTT-4TCB is wider than that of PODTT-4TCF, indicating more disordered structures existing in the former film. Upon doping with FeCl3, both mode A and mode C shift to much lower wavenumbers, suggesting that the benzenoid structures along the conjugated backbone are transformed into quinoid structures. It should be noted that the shift of mode C of PODTT-4TCF is more significant (Table S2) and mode A is much wider compared to those of PODTT-4TCB film, which means the dopants have a significant influence on the molecular packing of polymer chains in PODTT-4TCF film. These results demonstrate that the doping level is not dependent on the molecular orientation in PODTT-4T film.

The Electrical Conductivity of Doped Films
To investigate how the solvents impact the electrical properties, the electrical conductivity of PODTT-4T CF and PODTT-4T CB films doped by FeCl 3 was tested by four-probe measurement. As shown in Figure 2, the electrical conductivities of the two films dramatically increase with increasing the immersing time in the range of 10 min. As a result, the σ tend to be saturated. The σ of doped PODTT-4T CF film is higher than that of doped PODTT-4T CB film if doping time is greater than 10 min. The highest σ of PODTT-4T CF is up to 408 S cm −1 , which is 1.5 times higher than that of PODTT-4T CB (280 S cm −1 ). In addition, the Seebeck coefficient (S, the potential difference arises from per unit temperature difference) of the doped PODTT-4T CF film is slightly higher than that of the PODTT-4T CB film ( Figure S5a). As a result, the power factor (S 2 σ) of the doped PODTT-4T CF film is two times higher than that of the PODTT-4T CB film at a doping time of 10 min, indicating the potential thermoelectric application of this polymer. Considering a similar doping level observed in two-doped films, the higher TE performance could probably be attributed to the higher mobility in PODTT-4T CF film. To further support our hypothesis, Hall effect measurements were employed to investigate the effect of solvents on carrier concentrations and mobilities in doped polymers at doping times of 10 min ( Figure S6). The results show that the mobility of the doped PODTT-4T CF film and PODTT-4T CB film is 0.96 cm 2 V −1 s −1 and 0.76 cm 2 V −1 s −1 , respectively. Meanwhile, the carrier concentration of the doped PODTT-4T CF film and PODTT-4T CB film is 2.74 × 10 21 cm −3 and 2.62 × 10 21 cm −3 , respectively (Table S3). These data indicate that both films show higher mobilities than that of a typical thiophene polymer, such as FeCl 3 -doped P3HT [13], due to a large and delocalized backbone of PODTT-4T. In addition, the PODTT-4T CF film exhibits a 1.3-fold higher carrier mobility with slightly more free carriers compared to PODTT-4T CB film, affirming the importance of solvent selection for electrical conductivity optimization.

The Electrical Conductivity of Doped Films
To investigate how the solvents impact the electrical properties, the electrical conductivity of PODTT-4TCF and PODTT-4TCB films doped by FeCl3 was tested by four-probe measurement. As shown in Figure 2, the electrical conductivities of the two films dramatically increase with increasing the immersing time in the range of 10 min. As a result, the σ tend to be saturated. The σ of doped PODTT-4TCF film is higher than that of doped PODTT-4TCB film if doping time is greater than 10 min. The highest σ of PODTT-4TCF is up to 408 S cm −1 , which is 1.5 times higher than that of PODTT-4TCB (280 S cm −1 ). In addition, the Seebeck coefficient (S, the potential difference arises from per unit temperature difference) of the doped PODTT-4TCF film is slightly higher than that of the PODTT-4TCB film ( Figure S5a). As a result, the power factor (S 2 σ) of the doped PODTT-4TCF film is two times higher than that of the PODTT-4TCB film at a doping time of 10 min, indicating the potential thermoelectric application of this polymer. Considering a similar doping level observed in two-doped films, the higher TE performance could probably be attributed to the higher mobility in PODTT-4TCF film. To further support our hypothesis, Hall effect measurements were employed to investigate the effect of solvents on carrier concentrations and mobilities in doped polymers at doping times of 10 min ( Figure S6). The results show that the mobility of the doped PODTT-4TCF film and PODTT-4TCB film is 0.96 cm 2 V −1 s −1 and 0.76 cm 2 V −1 s −1 , respectively. Meanwhile, the carrier concentration of the doped PODTT-4TCF film and PODTT-4TCB film is 2.74 × 10 21 cm −3 and 2.62 × 10 21 cm −3 , respectively (Table S3). These data indicate that both films show higher mobilities than that of a typical thiophene polymer, such as FeCl3-doped P3HT [13], due to a large and delocalized backbone of PODTT-4T. In addition, the PODTT-4TCF film exhibits a 1.3-fold higher carrier mobility with slightly more free carriers compared to PODTT-4TCB film, affirming the importance of solvent selection for electrical conductivity optimization.

Microstructural Characterization
To further understand the relationship between solvent-dependent morphology and charge transport properties, grazing-incidence wide-angle X-ray scattering (GIWAXS) was performed (Figures 3 and S7). Pristine PODTT-4TCF film shows intense (h00) multiorder diffraction peaks in the out-of-plane direction (along the qz direction) and a (010) diffraction peak at qxy = 1.6-1.8 Å −1 generated by π-π stacking in the in-plane direction. That indicates a dominantly edge-on orientation existing in PODTT-4TCF film [30,31]. In contrast, pristine PODTT-4TCB film shows weak and broad Debye rings of (h00) peaks with a (010) diffraction peak appearing both in the out-of-plane and in-plane directions, meaning that both edge-on and face-on orientation exists in the PODTT-4TCB film. Since CF and

Microstructural Characterization
To further understand the relationship between solvent-dependent morphology and charge transport properties, grazing-incidence wide-angle X-ray scattering (GIWAXS) was performed (Figures 3 and S7). Pristine PODTT-4T CF film shows intense (h00) multi-order diffraction peaks in the out-of-plane direction (along the q z direction) and a (010) diffraction peak at q xy = 1.6-1.8 Å −1 generated by π-π stacking in the in-plane direction. That indicates a dominantly edge-on orientation existing in PODTT-4T CF film [30,31]. In contrast, pristine PODTT-4T CB film shows weak and broad Debye rings of (h00) peaks with a (010) diffraction peak appearing both in the out-of-plane and in-plane directions, meaning that both edge-on and face-on orientation exists in the PODTT-4T CB film. Since CF and CB have different boiling points, the difference of molecular orientations from two solvents can be attributed to the evaporation rate of solvent during the film preparation. In addition, the face-on orientation is thermodynamically stable packing for the polymer. The lamellar distance and π-π stacking distance of the PODTT-4T CF film are 20.26 Å and 3.67 Å, while the distances are 20.93 Å and 3.67 Å for PODTT-4T CB film, respectively. (Table S4). These results demonstrate that the utility of solvent mainly affects the packing orientation in pristine films and has a negligible effect on the lamellar distance and π-π stacking distance. Upon doping by FeCl 3 , the lamellar stacking distance of PODTT-4T CF film is increased to 22.43 Å (∆d 100 = 2.17 Å), while the π-π stacking distance decreases to 3.50 Å (∆d 010 = −0.17 Å). For the PODTT-4T CB film, the lamellar packing distance is increased to 23.26 Å (∆d 100 = 2.33 Å) while the π-π stacking distance also decreases from 3.67 to 3.50 Å (∆d 010 = −0.17 Å). These results indicate that the dopants prefer to intercalate into the lamellar alkyl side-chain region without disturbing the intense π-π stacking attributed to the electronic coupling between the conjugated backbone. Moreover, the molecular orientations of pristine films are still maintained upon doping. The size of the crystalline grain of pristine and doped films is compared by extracting the data of the full-width at half-maximum (FWHM) of (100) peaks according to the Scherrer equation [32,33]. It is observed that the FWHM of pristine PODTT-4T CF film (0.072 Å −1 ) is slightly smaller than that of pristine PODTT-4T CB film (0.078 Å −1 ), indicating larger crystalline domains in the pristine PODTT-4T CF film. Upon doping, the crystalline domains of doped films are significantly increased. In addition, the crystalline size of doped PODTT-4T CF film is still much larger than that of doped PODTT-4T CB film. CB have different boiling points, the difference of molecular orientations from two solvents can be attributed to the evaporation rate of solvent during the film preparation. In addition, the face-on orientation is thermodynamically stable packing for the polymer. The lamellar distance and π-π stacking distance of the PODTT-4TCF film are 20.26 Å and 3.67 Å, while the distances are 20.93 Å and 3.67 Å for PODTT-4TCB film, respectively. ( Table S4). These results demonstrate that the utility of solvent mainly affects the packing orientation in pristine films and has a negligible effect on the lamellar distance and π-π stacking distance. Upon doping by FeCl3, the lamellar stacking distance of PODTT-4TCF film is increased to 22.43 Å (Δd100 = 2.17 Å), while the π-π stacking distance decreases to 3.50 Å (Δd010 = −0.17 Å). For the PODTT-4TCB film, the lamellar packing distance is increased to 23.26 Å (Δd100 = 2.33 Å) while the π-π stacking distance also decreases from 3.67 to 3.50 Å (Δd010 = −0.17 Å). These results indicate that the dopants prefer to intercalate into the lamellar alkyl side-chain region without disturbing the intense π-π stacking attributed to the electronic coupling between the conjugated backbone. Moreover, the molecular orientations of pristine films are still maintained upon doping. The size of the crystalline grain of pristine and doped films is compared by extracting the data of the full-width at half-maximum (FWHM) of (100) peaks according to the Scherrer equation [32,33]. It is observed that the FWHM of pristine PODTT-4TCF film (0.072 Å −1 ) is slightly smaller than that of pristine PODTT-4TCB film (0.078 Å −1 ), indicating larger crystalline domains in the pristine PODTT-4TCF film. Upon doping, the crystalline domains of doped films are significantly increased. In addition, the crystalline size of doped PODTT-4TCF film is still much larger than that of doped PODTT-4TCB film. The microscopic morphology of the pristine and doped films is further characterized by atomic force microscopy (AFM) (Figure 4). Both the pristine PODTT-4TCF and pristine PODTT-4TCB films are smooth with an average roughness of 1.2 nm and 5.0 nm, respectively. Pristine PODTT-4TCF shows a fibrous zone while PODTT-4TCB film looks amorphous, which is consistent with the GIWAXS results. The surface roughness of doped films is slightly increased, which is in agreement with the enlarged crystalline domains observed in GIWAXS. For the doped PODTT-4TCF film, the self-aggregation of dopants is not obviously observed at the surface compared to that of PODTT-4T CB film, suggesting better miscibility of FeCl3 with the former film. The GIWAXS information and AFM results support the fact that the ordered molecular packing and higher crystallinity in PODTT-4TCF film are responsible for its higher mobility compared to that of PODTT-4TCB film. The use of chloroform solvent can promote polymer chains to form more ordered packing and larger crystalline domains. The microscopic morphology of the pristine and doped films is further characterized by atomic force microscopy (AFM) (Figure 4). Both the pristine PODTT-4T CF and pristine PODTT-4T CB films are smooth with an average roughness of 1.2 nm and 5.0 nm, respectively. Pristine PODTT-4T CF shows a fibrous zone while PODTT-4T CB film looks amorphous, which is consistent with the GIWAXS results. The surface roughness of doped films is slightly increased, which is in agreement with the enlarged crystalline domains observed in GIWAXS. For the doped PODTT-4T CF film, the self-aggregation of dopants is not obviously observed at the surface compared to that of PODTT-4T CB film, suggesting better miscibility of FeCl 3 with the former film. The GIWAXS information and AFM results support the fact that the ordered molecular packing and higher crystallinity in PODTT-4T CF film are responsible for its higher mobility compared to that of PODTT-4T CB film. The use of chloroform solvent can promote polymer chains to form more ordered packing and larger crystalline domains.  To further elucidate the carrier transport mechanism in the doped PODTT-4TCF and PODTT-4TCB films, the temperature-dependent σ was measured. It has been found that the σ increases with increased temperature (Figure 5), indicating thermal activated transport properties in doped films [34,35]. The transport activation energy (Ea) of the doped PODTT-4TCF film and PODTT-4TCB film can be calculated according to the equation of σ=σ0exp(−Ea/kBT), where σ0 is the pre-exponential conductivity and kB is Boltzmann constant [35]. It has been found that the Ea of the doped PODTT-4TCF film is 5.2 meV, which is lower than that of doped PODTT-4TCB films (Ea = 8.0 meV). The low Ea suggests a low transport barrier exists, and thus more polaronic states can contribute to electrical conductivity due to the continuous carrier transport channels in the doped PODTT-4TCF film [36]. Therefore, the film prepared from CF solution allows highly ordered and crystalline domains, resulting in strong coupling between doped polymer chains and thus a high carrier mobility.

Conclusions
In this work, the effect of solvent on morphology, doping process and electrical conductivity of thiophene polymers has been investigated. It has been found that the molecular orientation in films is strongly related to the solvent used for dissolving the polymer, which is dominated by the evaporation rate of solvent during film formation. The films prepared from chloroform (PODTT-4TCF) mainly have an edge-on orientation, while the films prepared from chlorobenzene (PODTT-4TCB) show both edge-on and face-on orientations. PODTT-4TCF film exhibits better crystallinity than that of the chlorobenzene-processed film. The crystallinity has significant influence on charge transport properties To further elucidate the carrier transport mechanism in the doped PODTT-4T CF and PODTT-4T CB films, the temperature-dependent σ was measured. It has been found that the σ increases with increased temperature (Figure 5), indicating thermal activated transport properties in doped films [34,35]. The transport activation energy (E a ) of the doped PODTT-4T CF film and PODTT-4T CB film can be calculated according to the equation of σ=σ 0 exp(−E a /k B T), where σ 0 is the pre-exponential conductivity and k B is Boltzmann constant [35]. It has been found that the E a of the doped PODTT-4T CF film is 5.2 meV, which is lower than that of doped PODTT-4T CB films (E a = 8.0 meV). The low E a suggests a low transport barrier exists, and thus more polaronic states can contribute to electrical conductivity due to the continuous carrier transport channels in the doped PODTT-4T CF film [36]. Therefore, the film prepared from CF solution allows highly ordered and crystalline domains, resulting in strong coupling between doped polymer chains and thus a high carrier mobility.

Conclusions
In this work, the effect of solvent on morphology, doping process and electrical conductivity of thiophene polymers has been investigated. It has been found that the molecular orientation in films is strongly related to the solvent used for dissolving the polymer, which is dominated by the evaporation rate of solvent during film formation. The films prepared from chloroform (PODTT-4T CF ) mainly have an edge-on orientation, while the films prepared from chlorobenzene (PODTT-4T CB ) show both edge-on and face-on orientations. PODTT-4T CF film exhibits better crystallinity than that of the chlorobenzeneprocessed film. The crystallinity has significant influence on charge transport properties rather than the doping level. As a result, FeCl 3 -doped PODTT-4T CF film shows a higher electrical conductivity of up to 408 S cm −1 and is attributed to a high carrier mobility correlated to the continuous and largely crystalline domains in film compared to that of chlorobenzene-processed film. Our findings show that the selection of solvents for the preparation of film is a promising strategy to optimize the electrical conductivity of doped polymers.