Multifunctional Cu2SnS3 Nanoparticles with Enhanced Photocatalytic Dye Degradation and Antibacterial Activity

We present a simplistic, ultrafast, and facile hydrothermal deposition of ternary Cu2SnS3 nanoparticles (CTS NPs). The fabricated CTS NPs show superior antimicrobial and photocatalytic activities. In the presence of UV-Visible illumination, methylene blue (MB) dye was studied for photocatalytic dye degradation activity of CTS NPs. Excellent efficiency is shown by incorporating CTS NPs to degrade MB dye. There is a ~95% decrease in the absorbance peak of the dye solution within 120 min. Similarly, CTS NPs tested against three bacterial strains, i.e., B. subtilis, S. aureus, P. vulgaris, and one fungal strain C. albicans, defining the lowest inhibitory concentration and zone of inhibition, revealed greater antimicrobial activity. Hence, it is concluded that the CTS NPs are photocatalytically and antimicrobially active and have potential in biomedicine.


Introduction
The textile industry zone is considered the prevalent wastewater and overwhelming dye sector. Effluents unconstrained from such industries contain various pollutants that are hazardous to human health and the environment. Voluminous processing, such as printing and dying the cloths in textiles, also consumes large amounts of water and dyes. They discharge large quantities of wastewater, which contain significant amounts of dyes harmful to the ecosystem and human beings [1]. Dye is a chemical, colored substance used to form chemical bonding with the substrate. Dyes are the organic compounds almost universally employed in industries such as paints, food, plastics, paper, pulp, textile, pharmaceutical, and leather [2,3]. Dyes are categorized into diverse types according to their structure, function, or both. Acidic, basic, direct, disperse, reactive, cationic, anionic, etc., are the categories of dyes. Due to the colored nature of pigments and dyes, they absorb only specific wavelengths of visible light. Dyes are water-soluble, and pigments are water-insoluble. Lake pigments can be produced by rendering some dyes with salt. These p-type showing bulk band-gap in the range of 0.9 and 1.50 eV, and the coefficient of optical absorption of materials is 10 −4 cm −1 . Therefore, CTS is an appropriate material for use as a photocatalyst and antimicrobial agent. Many researchers have tried various chemical and physical approaches to synthesizing ternary CTS material. [36,37]. The present study shows that CTS nanoparticles are synthesized using a simple, economical, and eco-friendly hydrothermal route and are characterized structurally and optically. Degradation of MB dye was performed using synthesized nanoparticles in visible light illumination and antimicrobial activity in the case of three bacterial strains, i.e., S. aureus, P. vulgaris, B. subtilis, and one fungal strain, C. albicans, was also tested.

Synthesis of CTS Nanoparticles
All of the chemicals utilized in the synthesis of CTS NPs are of analytical grade. All chemicals were purchased from Sigma Aldrich, Saint Louis, MO, USA. Briefly, 0.8 mmol of tin (II) chloride-dehydrate (Sncl 2 ·2H 2 O), 1 mmol of copper (I) chloride (CuCl·2H 2 O), and 4 mmol of thiourea (CH 4 N 2 S) were individually dissolved in 30 mL of deionized water with constant stirring for 10 min. First, the CuCl 2 ·2H 2 O solution was mixed into the SnCl 2 ·2H 2 O solution and stirred for 15 min. Then, CH 4 N 2 S solution was slowly mixed with the above mixture with gentle stirring. A white precipitate was observed after adding CH 4 N 2 S. Then, the pH of the solution reached approximately 9.0 by using a liquor ammonia solution. To synthesize CTS NPs, the hydrothermal method was carried out in 100 mL Teflon-lined stainless-steel autoclave at a temperature of 190 • C for~24 h (heating rate 5 • C/min). To increase the crystallinity of CTS NPs, the collected powder was washed a few times with distilled water, and the obtained precipitate was dried at 80 • C in a vacuum oven for 2 h (Figure 1). also made them strong candidates for various applications. The conductivity of CTS is a p-type showing bulk band-gap in the range of 0.9 and 1.50 eV, and the coefficient of optical absorption of materials is 10 −4 cm −1 . Therefore, CTS is an appropriate material for use as a photocatalyst and antimicrobial agent. Many researchers have tried various chemical and physical approaches to synthesizing ternary CTS material. [36,37]. The present study shows that CTS nanoparticles are synthesized using a simple, economical, and ecofriendly hydrothermal route and are characterized structurally and optically. Degradation of MB dye was performed using synthesized nanoparticles in visible light illumination and antimicrobial activity in the case of three bacterial strains, i.e., S. aureus, P. vulgaris, B. subtilis, and one fungal strain, C. albicans, was also tested.

Synthesis of CTS Nanoparticles
All of the chemicals utilized in the synthesis of CTS NPs are of analytical grade. All chemicals were purchased from Sigma Aldrich, Saint Louis, MO, USA. Briefly, 0.8 mmol of tin (II) chloride-dehydrate (Sncl2·2H2O), 1 mmol of copper (I) chloride (CuCl·2H2O), and 4 mmol of thiourea (CH4N2S) were individually dissolved in 30 mL of deionized water with constant stirring for 10 min. First, the CuCl2.2H2O solution was mixed into the SnCl2·2H2O solution and stirred for 15 min. Then, CH4N2S solution was slowly mixed with the above mixture with gentle stirring. A white precipitate was observed after adding CH4N2S. Then, the pH of the solution reached approximately 9.0 by using a liquor ammonia solution. To synthesize CTS NPs, the hydrothermal method was carried out in 100 mL Teflon-lined stainless-steel autoclave at a temperature of 190 °C for ~24 h (heating rate 5 °C/min). To increase the crystallinity of CTS NPs, the collected powder was washed a few times with distilled water, and the obtained precipitate was dried at 80 °C in a vacuum oven for 2 h (Figure 1).

Characterization
A UV-visible spectroscopy analysis was used to measure the optical transparency of CTS NPs (V-530, Jasco, Tokyo, Japan). The band-gap was calculated by diffuse reflectance spectroscopy through Kubelka-Munk (K-M) function. SEM (JEOL JSM-6390, Tokyo, Japan) digital silhouettes were used to observe the surface morphology of the CTS NPs. The X-ray diffraction (XRD) spectrum with a Cu-radiation tube (Kα of λ= 1.54 Å) was used to investigate the crystal phase (BRUKER AXS D8 Advanced model, Billerica, MA, USA). The elemental composition was determined using an X-ray photoelectron spectroscopy

Characterization
A UV-visible spectroscopy analysis was used to measure the optical transparency of CTS NPs (V-530, Jasco, Tokyo, Japan). The band-gap was calculated by diffuse reflectance spectroscopy through Kubelka-Munk (K-M) function. SEM (JEOL JSM-6390, Tokyo, Japan) digital silhouettes were used to observe the surface morphology of the CTS NPs. The X-ray diffraction (XRD) spectrum with a Cu-radiation tube (K α of λ = 1.54 Å) was used to investigate the crystal phase (BRUKER AXS D8 Advanced model, Billerica, MA, USA). The elemental composition was determined using an X-ray photoelectron spectroscopy profile obtained with (VG Multilab 2000 instrument, Thermo VG Scientific, Oxford, UK). Furthermore, FTIR spectroscopy analysis was performed using a Jasco FT-IR/4100 spectrometer. The specific surface area and pore size distribution of CTS powder are studied

Photocatalytic Activity Measurement
To investigate the catalytic activity of the CTS NPs, photocatalytic degradation of MB dye was carried out under sunlight illumination. A 50 mL solution of MB dye (concentration: 1 × 10 −5 M) was used as an organic impurity. The beaker holding MB dye solution amidst the CTS photocatalyst was laid on the magnetic stirrer, and this entire assemblage was positioned under sunlight illumination. We used a visible light source, an LED light source (6 W), combining a 585-nm LED lamp and a 613-nm LED lamp for the photocatalysis analysis.

Antimicrobial Activity Measurement
The sterile saline water was used to grow microbial cultures in inoculums. For the growth of bacteria, the nutrient agar plates were used as a medium. The development of C. albicans was spread on sterile sabouraud agar plates; likewise, the growth of S. aureus, B. subtilis, and P. vulgaris cultures was spread on clean nutrient agar plates. Using a micropipette, CTS NPs were dispersed in dimethyl sulfoxide (DMSO) and sterile distilled water. To observe antibacterial activity, plates were kept incubated at 37 • C for 24 h.

Structural Elucidation
The possible growth mechanism of CTS powder was proposed by using XRD, FTIR, and XPS techniques. During hydrothermal synthesis in airtight vessels, chemical reactions occur when the solution is heated at elevated temperatures. The growth mechanism involves coagulation, recrystallization, and nucleation depending on the temperature and reaction time [38]. To confirm that CTS NPs had indeed been formed and had the expected composition, structure, and phase, and XRD analysis was performed. The powder XRD pattern of CTS NPs is shown in Figure 2a [39,40]. The three peaks at 2θ = 28.56 • , 47.40 • , and 56.29 • are assigned to the (112), (220), and (312) lattice planes of a tetragonal structure (JCPDS: 01-089-4714). No impurity peaks and secondary phases occurred in the XRD analysis of binary sulfides such as Cu 2 S and SnS 2 materials. The Scherrer formula was applied to calculate the average particle size, which was 19 nm, cantered on the full width at half maximum of the (112) diffraction peak. FTIR spectroscopy was used to identify the covering ligands on the surface of CTS NPs, as shown in Figure 2b. The prepared CTS NPs were illuminated to the IR radiation in the form of a pallet. A pallet fabrication was conducted by mixing a small amount of the formed powder into potassium bromide (KBr), and all mixture was ground homogeneously for the construction of the sample into the KBr base. Consequently, the mixture was hard-pressed in a hydraulic press instrument applying a pressure up to~7 to 8 tons. The spectrum was obtained from 500 cm −1 to 4000 cm −1 with the resolution of 2 cm −1 . It is evident in Figure 2b that the vibrations reflected between 500 and 750 cm −1 correspond to Cu-S, Sn-S, Sn (IV)-O, and Sn (II)-O bonds present in the synthesized material [41]. The small peak in the spectra, which occurred at 2341.98 cm −1 , confirms the typical mode of Sn-S bond vibrations found in CTS NPs such as SnS and SnS 2 [42,43]. The asymmetric stretching of the carbonyl (C=O) causes the absorption band at 1116.70 cm −1 . The band at 1627.28 cm −1 is due to the O-H bending of water molecules [44]. The FTIR spectrum range 2000 to 2300 cm −1 shows a weak bond corresponding C≡S and nitrile bond C≡N [45]. Furthermore, N-H, O-H, C-H and thiourea bonds vibrated in the region 3350 to 3500 cm −1 [46]. The characteristic vibration symmetry of CTS NPs in the FTIR study is in accordance to the XRD results.  [46]. The characteristic vibration symmetry of CTS NPs in the FTIR study is in accordance to the XRD results.

X-ray Photoelectron Spectroscopy
X-ray photoelectron spectroscopy investigated the oxidation states and bonding changes in CTS NPs (see Figure 3a-d). The XPS spectra highlight the occurrence of Cu, Sn, S, O, and C elements. The occurrence of carbon and oxygen could be possible due to the environment (see Figure 3a). Figure 3b shows peaks located at 932.60 and 952.50 eV having binding energy splitting of 19.9 eV, highlighting the presence of Cu 1+ state. Figure  3c shows Sn 3d peaks, which occurred at 487.26 and 495.69 eV, with its peak separation of 8.43 eV confirming the Sn 4+ state. The presence of sulfide species confirmed by the sulfur 2p3/2 peak occurred at 163 eV, which agrees with the presence of sulfide species in the S 2− state (see Figure 3d). Thus, these results match reported data of CTS material in the literature [47][48][49][50].

X-ray Photoelectron Spectroscopy
X-ray photoelectron spectroscopy investigated the oxidation states and bonding changes in CTS NPs (see Figure 3a-d). The XPS spectra highlight the occurrence of Cu, Sn, S, O, and C elements. The occurrence of carbon and oxygen could be possible due to the environment (see Figure 3a). Figure 3b shows peaks located at 932.60 and 952.50 eV having binding energy splitting of 19.9 eV, highlighting the presence of Cu 1+ state. Figure 3c shows Sn 3d peaks, which occurred at 487.26 and 495.69 eV, with its peak separation of 8.43 eV confirming the Sn 4+ state. The presence of sulfide species confirmed by the sulfur 2p 3/2 peak occurred at 163 eV, which agrees with the presence of sulfide species in the S 2− state (see Figure 3d). Thus, these results match reported data of CTS material in the literature [47][48][49][50].

Scanning Electron Microscopy (SEM)
The surface morphology of semiconducting material is significant in optoelectronic applications. Figure 4a-d demonstrates SEM images of CTS NPs at various magnifications. This result reveals that CTS powder is an agglomeration of different NPs. At the magnification of ×13,000, CTS NPs show that they are assembled and forming irregular agglomerates (see Figure 4a). At a magnification of ×30,000, the outer surface of the CTS material is constructed by the aggregation of NPs. Figure 4b illustrates the nanoplate-like

Scanning Electron Microscopy (SEM)
The surface morphology of semiconducting material is significant in optoelectronic applications. Figure 4a-d demonstrates SEM images of CTS NPs at various magnifications. This result reveals that CTS powder is an agglomeration of different NPs. At the magnification of ×13,000, CTS NPs show that they are assembled and forming irregular agglomerates (see Figure 4a). At a magnification of ×30,000, the outer surface of the CTS material is constructed by the aggregation of NPs. Figure 4b illustrates the nanoplate-like morphology indicated by the yellow circle. Figure 4a,b exhibits the fabrication of a mixture of tiny clusters of NPs with a horizontally aligned plate-like structure. These plates are separated from each other and create voids between them. Additionally, these clusters of NPs and leaves consist of a numerous mesopore surface. It is clear from the micrograph of Figure 4c that the particles are smaller, irregular, and have a 2D structure, revealing uniform oval-like spherical-shaped NPs, as indicated by the green circle at a magnification of ×80,000. The grain sizes are found to be in the 500 nm range. At a magnification of ×150 k, CTS shows agglomeration of oval-like spherical-shaped NPs with white spongy clusters (see Figure 4d). The agglomeration was mainly due to high surface energy with a smaller size [51]. In addition to these particles, crystallites and randomly oriented particles can be seen. Microscopy magnification has revealed that the agglomeration of more minor constituents forms almost all particles. The result detected in the existing work is analogous to the effects described previously for CTS nanostructures achieved through the solvothermal route [52]. In general, CTS NPs form with mesopores surface morphology which is suitable for dye degradation.

Brunauer-Emmett-Teller (BET) Analysis
The photocatalytic dye degradation performance of the active electrode material is mainly dependent on the surface conditions. The surface area plays an essential role in dye degradation for light absorption at different incident angles. The specific surface area of CTS NPs prepared at 180 °C hydrothermal temperature is measured by BET analysis. The higher specific surface area and appropriate pore volume of prepared NPs are essential for getting the best electrochemical dye degradation performance [5]. As the high specific surface area provides the more significant electroactive sites for electrochemical reactions, and appropriate pore volume offers the easiest way for an intercalation/deinter-

Brunauer-Emmett-Teller (BET) Analysis
The photocatalytic dye degradation performance of the active electrode material is mainly dependent on the surface conditions. The surface area plays an essential role in dye degradation for light absorption at different incident angles. The specific surface area of CTS NPs prepared at 180 • C hydrothermal temperature is measured by BET analysis. The higher specific surface area and appropriate pore volume of prepared NPs are essential for getting the best electrochemical dye degradation performance [5]. As the high specific surface area provides the more significant electroactive sites for electrochemical reactions, and appropriate pore volume offers the easiest way for an intercalation/deintercalation process. Figure 5a provides the N2 adsorption-desorption isotherms measured for the CTS powder sample in the relative pressure (ρ/ρ0) range of 0.0-1.0. The curve shows the type IV isotherm attended by the H3 type hysteresis loop. This indicated the existence of mesopores in the sample, with the pore diameter ranging from 2 to 50 nm [53]. The analysis shows the presence of mesopores with specific surface areas of 87.31 m 2 g −1 of CTS material. Meanwhile, the pore size was calculated using the BJH method, and the result was 7.63 nm. The surface area and pore size are positively related to photocatalytic activity. Therefore, the photocatalytic activity of CTS NPs was higher [5]. Figure 5b shows the Barrett-Joyner-Halenda (BJH) pore size distribution plot of CTS NPs. The maximum pore size distribution occurs within 2 to 50 nm. The results from BET analysis support the SEM morphology as the nanoplates-like CTS possess maximum surface area.

Diffuse Reflectance Spectroscopy (DRS) Analysis
One of the essential characteristics of a promising photocatalyst is its optical properties. The band-gap is a significant factor of semiconductor materials, which decides the definite generation of carriers [54]. The UV-Visible diffuse reflectance absorption spectrum (DRS) of CTS NPs is illustrated in Figure 6a. The absorption spectrum of CTS NPs showed the characteristic band-gap absorption edge at 700 nm. This spectrum indicates that CTS NPs absorb the entire visible section of electromagnetic waves and that the tail is prolonged to a lengthier wavelength. This circumstance reflects the superior morphology of this sample, which allows for the scattering of incident light in the interior of molecules. This increases the photon path length and causes the reflection of incident light to shrink, a phenomenon known as the light-trapping effect [55]. The band-gap of CTS NPs was determined using the Kubelka-Munk (K-M) standard equation given below:

Diffuse Reflectance Spectroscopy (DRS) Analysis
One of the essential characteristics of a promising photocatalyst is its optical properties. The band-gap is a significant factor of semiconductor materials, which decides the definite generation of carriers [54]. The UV-Visible diffuse reflectance absorption spectrum (DRS) of CTS NPs is illustrated in Figure 6a. The absorption spectrum of CTS NPs showed the characteristic band-gap absorption edge at 700 nm. This spectrum indicates that CTS NPs absorb the entire visible section of electromagnetic waves and that the tail is prolonged to a lengthier wavelength. This circumstance reflects the superior morphology of this sample, which allows for the scattering of incident light in the interior of molecules. This increases the photon path length and causes the reflection of incident light to shrink, a phenomenon known as the light-trapping effect [55]. The band-gap of CTS NPs was determined using the Kubelka-Munk (K-M) standard equation given below: where F(r) is the Kubelka-Munk (K-M) function (i.e., k s ), s is the scattering factor (s = 2R), k is the molar absorption coefficient (i.e., k = (1 − R) 2 ), R is the reflectance data from DRS analysis, hν is the photon energy, and n are different values for allowed direct transition, n = 1 2 and allowed indirect transition n = 2. Equation (4)

Photocatalytic Activity
The absorbance spectra of a water-based dye solution of MB in the presence of 25 mg CTS NPs under visible light irradiation are shown in Figure 7a. The peak at 664 nm is taken as the reference peak of the MB dye solution. The degradation of MB dye does not occur in the absence of a photocatalyst. Under visible light irradiation, however, the dye solution exhibits exponential degeneration in the characteristic peak in the presence of photocatalyst (CTS NPs). As time surges, the decolorization of the dye within the solution occurs; as revealed in Figure 7a, the readings of the absorbance spectrum were obtained at 20 min of rest. Later, Figure 7a clearly shows that the peak of the MB dye solution nearly disappeared after 120 min, and the dye solution became colorless. According to Figure 7a, there is a 95% decline within 120 min of the dye solution's absorbance peak. The degradation rate of the reaction was calculated using the following equation: where A0 is the initial absorbance of MB dye in the absence of a catalyst and At is the absorbance of the dye solution at time t in the presence of a catalyst. Figure 7b denotes the degradation rate of MB dye solution in the presence and absence of CTS NPs catalyst. Under the illumination of visible light, a tiny quantity of CTS NPs shows noble adsorption and degradation, the same as in the report [56]. Figure 7b shows rate constant kapp was 0.0021 min −1 .

Photocatalytic Activity
The absorbance spectra of a water-based dye solution of MB in the presence of 25 mg CTS NPs under visible light irradiation are shown in Figure 7a. The peak at 664 nm is taken as the reference peak of the MB dye solution. The degradation of MB dye does not occur in the absence of a photocatalyst. Under visible light irradiation, however, the dye solution exhibits exponential degeneration in the characteristic peak in the presence of photocatalyst (CTS NPs). As time surges, the decolorization of the dye within the solution occurs; as revealed in Figure 7a, the readings of the absorbance spectrum were obtained at 20 min of rest. Later, Figure 7a clearly shows that the peak of the MB dye solution nearly disappeared after 120 min, and the dye solution became colorless. According to Figure 7a, there is a 95% decline within 120 min of the dye solution's absorbance peak. The degradation rate of the reaction was calculated using the following equation: The efficiency of degradation (%) = where A 0 is the initial absorbance of MB dye in the absence of a catalyst and A t is the absorbance of the dye solution at time t in the presence of a catalyst. Figure 7b denotes the degradation rate of MB dye solution in the presence and absence of CTS NPs catalyst. Under the illumination of visible light, a tiny quantity of CTS NPs shows noble adsorption and degradation, the same as in the report [56]. Figure 7b shows rate constant k app was 0.0021 min −1 .
Similarly, the value of 'k' was found to be 0.0848 min −1 g −1 using Equation (4).
where 'm' is the mass of the catalyst. CTS NPs' degradation effect concludes that they can be used in wastewater treatment in textile and other industries. Similarly, the value of 'k' was found to be 0.0848 min −1 g −1 using Equation (4). m k k app  (4) where 'm' is the mass of the catalyst. CTS NPs' degradation effect concludes that they can be used in wastewater treatment in textile and other industries. Figure 7c depicts a schematic representation of photocatalytic degradation of CTS NPs under visible-light illumination. As a result, CTS has p-type semi-conductivity, which means that holes are the primary carriers, advantageous for oxidizing organic compounds. Under visible light illumination, electrons (e − ) are excited from the valence band (VB) to the conduction band (CB) of CTS NPs, resulting in the production of holes (h + ) in the VB [57,58]. CTS NPs are stable in the environment; metal ion discharge does not contribute much to the photocatalytic degradation mechanism. In contrast, under visible-light irradiation, due to the defects side of CTS NPs or visible light electron-hole pair, the process of UV activating the production of reactive oxygen species (ROS) occurs. The generation of ROS is mainly because of electron-hole pairs and these ROSs, such as hydroxyl radicals    OH and superoxide radical anions   OH radicals are the primary active species in the photocatalytic degradation of organic pollutants. Holes and hydroxyl radicals can oxidize MB into degradation products [57]. The comparative elevation of degradation in CTS NPs shows high photon absorption in the visible region and the absence of any binary phases; however, the presence of binary phases in the NPs causes a non-radiative permutation of carriers, reducing their efficacy. Figure 7c proves that electron-hole pairs' production depends on the interaction of CTS NPs with light. Manufactured ROS interacts with organic matter (MB) and degrades them into reduced   [57,58]. CTS NPs are stable in the environment; metal ion discharge does not contribute much to the photocatalytic degradation mechanism. In contrast, under visible-light irradiation, due to the defects side of CTS NPs or visible light electron-hole pair, the process of UV activating the production of reactive oxygen species (ROS) occurs. The generation of ROS is mainly because of electron-hole pairs and these ROSs, such as hydroxyl radicals (OH • ) and superoxide radical anions O •− 2 . The OH • radicals are the primary active species in the photocatalytic degradation of organic pollutants. Holes and hydroxyl radicals can oxidize MB into degradation products [57]. The comparative elevation of degradation in CTS NPs shows high photon absorption in the visible region and the absence of any binary phases; however, the presence of binary phases in the NPs causes a non-radiative permutation of carriers, reducing their efficacy. Figure 7c proves that electron-hole pairs' production depends on the interaction of CTS NPs with light. Manufactured ROS interacts with organic matter (MB) and degrades them into reduced harmful yields [37]. The various photocatalyst studies for the photocatalytic degradation of the MB dye are summarized in Table 1. The probable reaction phases are as follows: Step 1 : hν + Catalyst(CTS) → electron e − + hole h + Step 2 : Step 3 : Step 4 : Step 5 : OH • + MB molecules → degraded product (9)

Antimicrobial Activity
The water rectification process contains organic pollutants and many other contaminants available in the wastewater. These toxin materials have a fragment of microbes, and it was reported earlier that the growth of pathogenic bacteria in the water is mainly because of organic metals [68]. Therefore, it is found that the photocatalyst has the property of inhabitation ability of microbial contaminants [69]. Commercial antibiotic (50 µg/mL) and antibacterial activity of CTS NPs (50 µg/mL) were scrutinized, and a significant zone of inhibition was detected. Figure 8a demonstrates a photograph representing the antibacterial activity of CTS NPs against three bacterial strains, S. aureus (NCIM-2654) gram-positive, P. vulgaris (NCIM 2813), and B. subtilis (NCIM-2635) gram-negative, using streptomycin as a positive control and dimethylsulfoxide (DMSO) and distilled water as a negative control. Similarly, one fungal strain, C. albicans (NCIM-3466), was treated with fluconazole as the standard drug after incubation for 12 h. The antimicrobial potential of CTS NPs was studied using the agar gel diffusion method. Suspensions of CTS NPs drops were applied on round filter paper in a disc. Preparation of the DMSO medium was achieved by using the liquid auger suspension. The bacterial strains, i.e., S. aureus, P. vulgaris, B. subtilis, and one fungal strain, i.e., C. albicans, were prepared separately for each sample and control. The dilution of the CTS NPs sample was conducted as 2.5 mg/mL, and 10 µL drops of the sample were mixed in bacterial and fungal suspensions. The incubation of three bacterial and one fungal control suspensions was at 37 • C for 12 h. It can be deduced from the present study that CTS NPs have an excellent antimicrobial activity toward the three bacterial strains. S. aureus, P. vulgaris, B. subtilis and one fungal strain C. albicans. From the zone of inhibition (ZOI) values, CTS NPs were more efficient in inhibiting the growth of the bacterial strain P. vulgaris, as the maximum ZOI was 14.00 ± 1.00 mm. The ZOIs of CTS NPs against S. aureus and B. subtilis bacterial strains were 11.67 ± 0.58 mm and 12.67 ± 1.15 mm, respectively, as illustrated in Table 2. Similarly, the ZOI against the fungal strain C. albicans was 10.33 ± 1.53 mm.

Entry
Antibacterial Activity Antifungal Activity S. aureus (NCIM-2654) B. subtilis (NCIM-2635) P. vulgaris (NCIM 2813) C.  These results were compared to the commercial antibiotic streptomycin, which is only applicable to bacterial strains. The ZOIs were 16.33 ± 0.58 mm, 20.67 ± 0.58 mm, and 20.33 ± 0.58 mm for S. aureus, P. vulgaris, and B. subtilis, respectively (from Figure 8a) [70]. Similarly, the ZOI of one fungal strain, C. albicans, using fluconazole as the standard drug, was 14.67 ± 1.00 mm, which is more efficient. The above data represent the mean ± standard error of three replicates illustrated in Table 2. Figure 8b illustrates the statistical analysis of CTS NPs antibiotics against bacterial and fungal strains. Additionally, DMSO + CTS NPs show good ZOIs compared to bare DMSO, H2O + CTS NPs, and bare H2O, as shown in Figure 8a. CTS possesses p-type characteristics; meanwhile, it resides in holes as the majority carriers. Thus, it degraded an enormous percentage of P. vulgaris as it collated with S. aureus and B. subtilis. Bacterial degradation is commonly connected with oxidative stress caused by ROS generated by functional materials. The cell membrane is the most crucial fragment of bacteria which safeguards it from the severity of the environment. The damage of this membrane in bacteria can lead to physiochemical changes resulting in inactivation. This stress leads to polyunsaturated acids and crust lipids destruction leading to free radicals that break the bonds. Later, as a second toxic reactive messenger, aldehydes destroy internal protein molecules and cause leakage of the membrane, which inactivates bacteria [71].  These results were compared to the commercial antibiotic streptomycin, which is only applicable to bacterial strains. The ZOIs were 16.33 ± 0.58 mm, 20.67 ± 0.58 mm, and 20.33 ± 0.58 mm for S. aureus, P. vulgaris, and B. subtilis, respectively (from Figure 8a) [70]. Similarly, the ZOI of one fungal strain, C. albicans, using fluconazole as the standard drug, was 14.67 ± 1.00 mm, which is more efficient. The above data represent the mean ± standard error of three replicates illustrated in Table 2. Figure 8b illustrates the statistical analysis of CTS NPs antibiotics against bacterial and fungal strains. Additionally, DMSO + CTS NPs show good ZOIs compared to bare DMSO, H 2 O + CTS NPs, and bare H 2 O, as shown in Figure 8a. CTS possesses p-type characteristics; meanwhile, it resides in holes as the majority carriers. Thus, it degraded an enormous percentage of P. vulgaris as it collated with S. aureus and B. subtilis. Bacterial degradation is commonly connected with oxidative stress caused by ROS generated by functional materials. The cell membrane is the most crucial fragment of bacteria which safeguards it from the severity of the environment. The damage of this membrane in bacteria can lead to physiochemical changes resulting in inactivation. This stress leads to polyunsaturated acids and crust lipids destruction leading to free radicals that break the bonds. Later, as a second toxic reactive messenger, aldehydes destroy internal protein molecules and cause leakage of the membrane, which inactivates bacteria [71].

Conclusions
In conclusion, Cu 2 SnS 3 (CTS) NPs were synthesized using a simple and environmentally friendly hydrothermal technique. The XRD study shows that CTS NPs exhibit a tetragonal structure with a kesterite phase. FTIR and XPS studies confirmed the formation of CTS compounds with pure phases. The morphological study revealed the formation of oval-like spherical-shaped NPs with white spongy clusters, consisting of several small crystallites that exist due to aggregation of the NPs. Additionally, the CTS sample's band-gap value was 1.20 eV, leading to superior photocatalytic activities.
Moreover, CTS NPs exhibit high efficiency for MB dye degradation, thus making them a potential candidate for dye treatment in wastewater. There is a~95% decrease in the absorbance peak of the dye solution within 120 min. The antimicrobial results demonstrated that CTS NPs display excellent antimicrobial and antifungal activity against three bacterial strains, i.e., S. aureus, P. vulgaris, B. subtilis, and one fungal strain C. albicans. Hence, it is proven that the CTS NPs are photocatalytically and antimicrobially active when exposed to visible light. As a result, the current study reports a new approach to acquiring NPs with a potential for dye degradation, UV protection, and antifungal and antibacterial areas.