Removal of Thiol-SAM on a Gold Surface for Re-Use of an Interdigitated Chain-Shaped Electrode

The self-assembled monolayer (SAM) is the most common organic assembly utilized for the formation of the monolayers of alkane-thiolates on gold electrode, resulting in a wide range of applications for the modified SAM on gold in various research areas. This study examined the desorption of a SAM that was developed on the gold surface of an interdigitated chain-shaped electrode (the ICE, a unique electrode design, was fabricated by our group) with the goal of determining the most efficient strategy of SAM removal for the ICE to be re-used. A simple and proficient solution-based cleaning procedure was applied for the removal of a SAM on the gold surface of the ICE by using a sodium borohydride solution within short-term treatment, resulting in efficiency for the recovery of the originally electrochemical characteristic of ICE of 90.3%. The re-use of ICE after the removal process was confirmed by the successful re-deposition of a SAM onto the electrode surface, resulting in the high efficiency percentage of 90.1% for the reusability of ICE with the SAM modification. Electrochemical impedance spectroscopy (EIS) and cyclic voltammetry (CV) were used as tools to investigate the changes in the electrode interface at each stage of the SAM removal and the electrode recycling. X-ray photoelectron spectroscopy and Fourier-transform infrared spectroscopy were employed, being powerful spectrum techniques, for the characterization of the bonding structure and chemical state of the bare ICE and the modified ICE at each treatment step. Based on the comprehensive discussion of analytical chemistry from the obtained EIS and CV data in this study, we confirmed and proved the effectiveness of this promising method for the removal of a SAM from the ICE and the re-use of ICE in the field of material deposition, with the aims of saving money, improving experimental handling, and protecting the environment.

Molecular constituents from a solution adsorb onto a solid surface to form organic assemblies, which are known as self-assembled monolayers (SAMs) [13]. A SAM with a head group, a tail group, and a functional end group is representative of this. A wide range edge. The distribution of electric fields in the areas between the ICE fingers is relatively uniform, as determined through using a COMSOL simulation [31], leading to enhanced homogeneity in the electrode working area, resulting in improved capabilities for electrode surface modification. Furthermore, the Warburg diffusion impedance in EIS has been completely eliminated by using ICE [10,11].
EIS has experienced a significant increase in popularity in recent years, owing to its exceptional sensitivity. The EIS technique is used to estimate the electrical properties of materials and their interfaces with electrodes that have been surface-modified [11,33]. This method has been extensively used in electrochemistry [34,35], biomedical applications [36,37], materials science [38], and other fields. EIS is a type of impedance measurement using alternating current polarography, which includes electrochemical reactions, and results in signals corresponding to the charge-transfer resistance and the double-layer capacitance at the electrode interface [39].
Our past research has demonstrated that a SAM is the main components used to successfully modify the gold surface of the ICE, which has been used in the construction of a variety of electrochemical biosensors in the field of sensing technology [10][11][12]. Besides that, the formation of a SAM on the gold surface has been utilized as a platform for the development of analytical tools in electronics, such as introducing a SAM as a counterbalancing dipole to the work function of the electrode in order to modify organic thin film transistors [40], using a SAM as a molecular junction between two electrodes with gold to shrink the size of electronics by replacing traditional thin film transistors with ones based on SAMs [41], modifying graphene with SAMs in the construction of graphene-based field effect transistors (GFETs) to reduce power consumption and use in very high frequency electronic devices [42][43][44], and patterning of SAMs on metal surfaces in applications of organic solar cells for modifying cathodes to block holes [45]. However, each ICE with a modified SAM and the electronic devices based on the platform SAM-gold were discarded after only one usage in each application, since it is hard to remove the SAM from the gold surface, leading to electrode waste, manufacturing costs, and an environmental impact. The development of technologies to regenerate the underlying gold will enable the electrode surface to be re-used, resulting in cost savings, environmental protection, and improved experimental handling. In an ideal situation, the SAM should be entirely eliminated from the surface without affecting the gold substrate.
To remove the SAM molecules from gold substrates, there are a variety of approaches available. Ozone and UV radiation are approaches that can be used in the presence of air to decompose the thiol compounds of the SAM [46]. However, the limitation of these procedures would be that the fluctuation must be spread evenly over the surface to be wiped, and portions that are shaded from the light may not have been efficiently wiped down. Heat treatment is a practical method for removing thiol molecules from air [47], but it still needs high temperatures (of over 200 • C) to be used for a reasonable timeframe, which could harm the gold substrate. SAMs have recently been shown to dissolve when exposed to a laser beam [48]. Due to the fact that it could only eliminate a tiny amount of a SAM at a time, this approach has limitations for real implementations.
It is highly useful to operate with liquids, since they allow many samples to be cleaned uniformly, while also reaching complex surfaces. Electrochemical cleaning is the most commonly used solution-based cleaning procedure. Whenever a negative voltage is given to the gold substrate, the SAM's molecules begin to desorb, which is known as electrochemical desorption. It is common practice to immerse the SAM-coated gold substrate in an electrolyte solution with a pH that is basic or neutral [49]. Due to the fact that some alkane-thiolates are re-absorbed on the gold surface as a result of electrochemical cleaning, the potentials used and the time spent conducting the test are essential considerations [50].
In this study, we introduce a simple and efficient method for removing SAM from the gold surface of an ICE by using a sodium borohydride (NaBH 4 ) solution. The ICE with the SAM modification was immersed in an NaBH 4 solution for a short time to entirely remove the SAM on the ICE surface, and to recover the original electrochemical proper-ties of the ICE. Furthermore, an applicable re-use of ICE after the SAM removal process was performed by the re-deposition of the SAM on the electrode surface. EIS and cyclic voltammetry were used to characterize the electrochemical behavior, and the changes in the electrode interface in the SAM removal stage and in the ICE re-use stage. The two powerful spectroscopy techniques of X-ray photoelectron spectroscopy and Fourier-transform infrared spectroscopy were utilized to characterize the electronic structure and chemical bonding of the bare ICE and the electrode modification at each stage. Additionally, the efficiencies of the removal of the SAM on the ICE surface and the re-use of ICE in the material deposition were calculated in this paper. We also propose an easy and new process for cleaning the bare ICE with NaBH 4 solution, prior to beginning the electrode modifications, which is described in the following section.

Manufacture of the Interdigitated Chain Shaped-Electrode (ICE)
The ICE was manufactured on a glass slide substrate of (14 mm × 3.5 mm). The electron beam evaporator system (SEE-5, ULTECH, Daegu, South Korea) was used to deposit a 25 nm thick adhesive Ti layer (deposition rate of 1 A s −1 , emission current of 68-80 mA), and a 50 nm thick Au electrode layer (deposition rate of 1 A s −1 , emission current of 55-74 mA). Next, the lift-off process was used to generate the paired electrode finger, including the space of 5 µm and the width of 5 µm, for the working and reference electrodes, respectively. Figure 1a shows a photo of ICE including the working and reference electrodes, and microscopic images of the ICE containing Au fingers.

Deposition of the Self-Assembled Monolayer (SAM) on the ICE. Removing the SAM on the Surface of ICE. Re-Depositing the SAM on the ICE
Before developing the SAM on the ICE surface, the bare ICE was cleaned with 0.5 M NaBH4 solution in 1:1 H2O/Ethanol and dried under nitrogen flow to discard impurities on the ICE surface.
Subsequently, the bare ICE was dipped in 100 mM MHA solution for 2 h at room temperature (RT; 25 °C) to create the SAM on the Au surface of ICE (ICE/SAM) through the bonding between gold (Au) of ICE and sulfur (S) at the head group of the SAM, as shown in Figure 1.
To re-use the ICE, the ICE/SAM was immersed in 0.5 M NaBH4 solution for 10 min at RT to remove the SAM on the ICE surface (re-ICE) and return the ICE to its original state.
To approve the re-use of ICE, the SAM was again deposited on the re-ICE (re-ICE/SAM) by dipping the re-ICE in a 100 mM MHA solution for 2 h at room temperature (25 °C), and then it was washed with extra pure ethanol and DI H2O. This procedure is similar to the deposition of the SAM on bare ICE, as described above, which is a quality control process for the successful formation of the SAM on the gold surface of ICE, as shown in the Results and Discussion section.

Structural Characterization
X-ray photoelectron spectroscopy (XPS, Thermo Scientific MultiLab 2000, East Grinstead, UK) with X-ray sources of a twin anode (Al Kα, hν = 1486.6 eV) gun and a monochromatic gun was used to characterize the chemical state and the electronic structure of the bare electrode and the electrode modification.
Fourier-transform infrared spectroscopy (FT-IR, a wavenumber range of 400-4000 cm −1 , scanning speed of 2 mm s −1 , data interval of 0.964233 cm −1 , resolution of 4 cm −1 , Jasco-  Subsequently, the bare ICE was dipped in 100 mM MHA solution for 2 h at room temperature (RT; 25 • C) to create the SAM on the Au surface of ICE (ICE/SAM) through the bonding between gold (Au) of ICE and sulfur (S) at the head group of the SAM, as shown in Figure 1.
To re-use the ICE, the ICE/SAM was immersed in 0.5 M NaBH 4 solution for 10 min at RT to remove the SAM on the ICE surface (re-ICE) and return the ICE to its original state.
To approve the re-use of ICE, the SAM was again deposited on the re-ICE (re-ICE/SAM) by dipping the re-ICE in a 100 mM MHA solution for 2 h at room temperature (25 • C), and then it was washed with extra pure ethanol and DI H 2 O. This procedure is similar to the deposition of the SAM on bare ICE, as described above, which is a quality control process for the successful formation of the SAM on the gold surface of ICE, as shown in the Results and Discussion section.

Structural Characterization
X-ray photoelectron spectroscopy (XPS, Thermo Scientific MultiLab 2000, East Grinstead, UK) with X-ray sources of a twin anode (Al K α , hν = 1486.6 eV) gun and a monochromatic gun was used to characterize the chemical state and the electronic structure of the bare electrode and the electrode modification.
Fourier-transform infrared spectroscopy (FT-IR, a wavenumber range of 400-4000 cm −1 , scanning speed of 2 mm s −1 , data interval of 0.964233 cm −1 , resolution of 4 cm −1 , Jasco-4600, Jasco Inc., Easton, MD, USA) was used to characterize the functional and bonding groups on the electrode surface. The FT-IR result was obtained by measuring three consecutive runs for each sample.

Electrochemical Characterization
BioLogic's potentiostat/galvanostat instrument (SP-200, Seyssinet-Pariset, France) was used to investigate the electrochemical impedance spectroscopy (EIS) and the cyclic voltammetry (CV) measurements of the ICE and the ICE modification. EIS was performed in a two-electrode configuration with an input sinus amplitude of 50 mV and the applied frequency range of 1 MHz to 100 mHz, and CV was performed in a three-electrode configuration with an external Ag/AgCl electrode, in 1 mM K[Fe(CN) 6 ] 3−/4− containing 0.1 M KCl.

Results and Discussion
Cleaning ICE is an important step to remove numerous contaminants on the electrode surface and enhance the quality of the active Au surface of ICE for the chemical modification. Therefore, the bare ICE was cleaned with 0.5 M NaBH 4 solution to remove dust and impurities existing on the surface. Figure 2 shows the EIS and CV of the ICE before and after the cleaning process. EIS results express the changes in the interfacial electrode surface in the electrolyte of 1 mM K[Fe(CN) 6 ] 3−/4− containing 0.1 M KCl in a Nyquist plot of the image impedance (−Im(Z)) vs. the real impedance (Re(Z)), as shown in Figure 2a. The meanings of Nyquist plots were described using the Randle's equivalent circuit model (REC) (Figure 2a inset), which included three parameters: R s , corresponding to the solution resistance which can be found by reading the real axis (Re(Z)) value at the high frequency intercept; R ct , corresponding to the interfacial charge-transfer resistance which equals the semicircular diameter of the Nyquist plot; C dl , corresponding to the double-layer capacitance which is in parallel with the R ct .

XPS and FT-IR Results of ICE, ICE/SAM, and Re-ICE
To identify the change in the Au surface of ICE after the SAM modification and the SAM removal (as described in Section 2.3), the Au 4f spectra of the ICE, ICE/SAM, and re-ICE samples (Figure 3) were identified by using XPS, since XPS is a powerful technique to analyze the chemical state and electronic structure of an electrode surface [56]. As seen in Figure 3a, the Au 4f spectra of the bare ICE had the two typical peaks of bulk metallic gold Au(0), of the Au 4f7/2 Au(0) at 84 eV and the Au 4f5/2 Au(0) at 88 eV of binding energy, respectively [57]. After the deposition of the SAM, a shift in the Au 4f peaks was observed for the ICE/SAM sample ( Figure 3a); this phenomenon is attributed to the formation of Au-S bonding between the Au surface of ICE and the terminal S group of the SAM. As seen in Figure 3b, the deconvolution of the Au 4f spectra of the ICE/SAM indicates two peaks of metallic gold of Au 4f7/2 Au(0) (84 eV) and Au 4f5/2 Au(0) (88 eV), along with the peaks that occurred for Au 4f7/2 Au-S (85 eV) and Au 4f5/2 Au-S (89 eV) [57], demonstrating the successful deposition of the SAM on the Au surface of the bare ICE. Subsequently, the Using the REC for fitting the measured Nyquist plots in Figure 2a, the obtained R ct value of ICE decreased significantly to 86 kΩ after the cleaning step, as compared to the high R ct value (390 kΩ) of ICE before the cleaning step. This decrease in R ct was due to the easy transport of the K[Fe(CN) 6 ] 3−/4− redox probes toward the electrode surface; this result indicated that the movement obstruction of redox probes was prevented by elimination of the impurities that existed on the electrode surface, demonstrating the successful removal of contaminants on the electrode surface, and that the original electrochemical behavior of the ICE had been brought back. CV of the ICE after cleaning (Figure 2b) showed the increase in current intensity, re-confirming the enhancement in the electrochemical properties of ICE.
Recent studies of gold electrode cleaning procedures, such as electrochemical cleaning (via applying cyclic voltammetry between −1.0 and 1.3 V, scan rate of 0.1 V s −1 in a solution of 0.05 M H 2 SO 4 ) [51][52][53][54] and heat treatment (via increasing temperature) [55], also displayed an increase in current intensity in the CV of gold electrode after the cleaning step, agreeing with the tendency of the obtained CV in this report, and proving the improvement in the quality of bare ICE after using the NaBH 4 for cleaning.

XPS and FT-IR Results of ICE, ICE/SAM, and Re-ICE
To identify the change in the Au surface of ICE after the SAM modification and the SAM removal (as described in Section 2.3), the Au 4f spectra of the ICE, ICE/SAM, and re-ICE samples ( Figure 3) were identified by using XPS, since XPS is a powerful technique to analyze the chemical state and electronic structure of an electrode surface [56]. As seen in Figure 3a, the Au 4f spectra of the bare ICE had the two typical peaks of bulk metallic gold Au(0), of the Au 4f 7/2 Au(0) at 84 eV and the Au 4f 5/2 Au(0) at 88 eV of binding energy, respectively [57]. After the deposition of the SAM, a shift in the Au 4f peaks was observed for the ICE/SAM sample ( Figure 3a); this phenomenon is attributed to the formation of Au-S bonding between the Au surface of ICE and the terminal S group of the SAM. As seen in Figure 3b, the deconvolution of the Au 4f spectra of the ICE/SAM indicates two peaks of metallic gold of Au 4f 7/2 Au(0) (84 eV) and Au 4f 5/2 Au(0) (88 eV), along with the peaks that occurred for Au 4f 7/2 Au-S (85 eV) and Au 4f 5/2 Au-S (89 eV) [57], demonstrating the successful deposition of the SAM on the Au surface of the bare ICE. Subsequently, the Au 4f spectra of the ICE after the removal of the SAM from the electrode surface-the re-ICE sample (Figure 3a)-showed the disappearance of the Au-S peaks, and the return of the two peaks of Au(0) at 84 and 88 eV, as compared to the Au 4f spectra of the ICE and ICE/SAM, indicating that using the NaBH 4 treatment brought back the ICE's original characteristics.  FT-IR was used to identify the bonding groups of the electrode and the modified electrode. Figure 4 shows the FT-IR spectra of the ICE, ICE/SAM, and re-ICE. The spectra of ICE/SAM show the formation of the covalent bonding of Au-S and the stretch mode of C-S groups of the SAM in the band range (500 to 850) cm −1 , and the O-H deformation mode and methyl antisymmetric bending mode of the SAM in the band (950 to 1400) cm −1 , respectively, demonstrating the deposition of the SAM on the Au surface of the bare ICE [58,59]. The re-ICE showed the FT-IR spectra that match the spectra of the bare ICE in all regions of wavenumbers after the SAM removal by NaBH4. This result indicated the successfully reorganization of the ICE after the SAM deposition and removal process, respectively. FT-IR was used to identify the bonding groups of the electrode and the modified electrode. Figure 4 shows the FT-IR spectra of the ICE, ICE/SAM, and re-ICE. The spectra of ICE/SAM show the formation of the covalent bonding of Au-S and the stretch mode of C-S groups of the SAM in the band range (500 to 850) cm −1 , and the O-H deformation mode and methyl antisymmetric bending mode of the SAM in the band (950 to 1400) cm −1 , respectively, demonstrating the deposition of the SAM on the Au surface of the bare ICE [58,59]. The re-ICE showed the FT-IR spectra that match the spectra of the bare ICE in all regions of wavenumbers after the SAM removal by NaBH 4 . This result indicated the successfully reorganization of the ICE after the SAM deposition and removal process, respectively.
FT-IR was used to identify the bonding groups of the electrode and the modified electrode. Figure 4 shows the FT-IR spectra of the ICE, ICE/SAM, and re-ICE. The spectra of ICE/SAM show the formation of the covalent bonding of Au-S and the stretch mode of C-S groups of the SAM in the band range (500 to 850) cm −1 , and the O-H deformation mode and methyl antisymmetric bending mode of the SAM in the band (950 to 1400) cm −1 , respectively, demonstrating the deposition of the SAM on the Au surface of the bare ICE [58,59]. The re-ICE showed the FT-IR spectra that match the spectra of the bare ICE in all regions of wavenumbers after the SAM removal by NaBH4. This result indicated the successfully reorganization of the ICE after the SAM deposition and removal process, respectively.

Electrochemical Characterization of the ICE, ICE/SAM, and Re-ICE, and the Application of Re-ICE for the Deposition of the SAM on the Electrode Surface
The EIS tests of ICE, ICE/SAM, re-ICE, and re-ICE/SAM were performed in 1 mM K[Fe(CN)6] 3−/4− containing 0.1 M KCl, and results are expressed through Nyquist plots, as shown in Figure 5a-c. Using REC to fit the EIS data, the values of the three parameters of Rct, Cdl, and Rs were obtained, and are displayed in Table 1. The fitted Rct value of the ICE was 86 kΩ. Significant enhancement in Rct was observed after the addition of the SAM to  Figure 5a-c. Using REC to fit the EIS data, the values of the three parameters of R ct , C dl , and R s were obtained, and are displayed in Table 1. The fitted R ct value of the ICE was 86 kΩ. Significant enhancement in R ct was observed after the addition of the SAM to the ICE surface ( Figure 5a and Table 1), and the obtained R ct value of ICE/SAM was 1900 kΩ. This increment in the R ct was attributed to the non-conductivity of the long hydrocarbon chains and the carboxylic acids group of the SAM, which led to impeding the movement of the K[Fe(CN) 6 ] 3−/4− redox couple to the ICE surface. As seen in Figure 5d, after SAM modification on the ICE, the CV result showed a rapid decrease in current intensity, indicating the reduced conductivity of the electrode due to the formation of the SAM on the electrode surface, agreeing with the EIS results. Figure 5a,b shows the EIS results of the re-ICE after the removal of the SAM from the ICE surface with the treatment of NaBH 4 solution. The Nyquist plot of the re-ICE demonstrates the expressive decrease in the R ct with a value of 87 kΩ. This decrease in R ct was due to the easy transportation of the K[Fe(CN) 6 ] 3−/4− redox couple toward the electrode surface; the hindrance of the transfer of the redox probe to the surface of electrode was removed, which was caused by the elimination of the SAM on the ICE surface. It is observed that the R ct value of the re-ICE (87 kΩ) approximately equals the R ct of the bare ICE (86 kΩ), demonstrating that removal of the SAM from the ICE was successfully completed by the treatment with NaBH 4 solution. The re-confirmation of the elimination of the SAM from the ICE's surface was also performed by CV measurement. The CV result of the re-ICE after removing SAM in Figure 5d indicates a significant increase in the current intensity, and equals the current intensity of the CV result of the bare ICE, re-confirming the removal of the SAM from the ICE, and the restoration of the original electrochemical behaviors of ICE.  Table 1. EIS parameters of the electrode and the modified electrode, extrapolated by fitting the measured spectra in Figure 5 to the REC.

Efficiency Percentage
To evaluate the possible factors for the recovery of ICE's characteristic after the removal of the SAM and the re-use of ICE with the SAM modification, the efficiency percentage was determined by calculation, as described in the following evaluation: The efficiency percentage of the ICE recovery after SAM removal can be calculated as follows: where RICE is the Rct of the bare ICE, and Rre-ICE is the Rct of the re-ICE after the removal of the SAM.  Table 1. EIS parameters of the electrode and the modified electrode, extrapolated by fitting the measured spectra in Figure 5 to the REC.

Electrode R ct (kΩ) C dl (F) R s (kΩ)
ICE 86 ± 1.0 (11.8 × 10 −7 ) ± 10 −5 0.36 ± 10 −4 After the successful removal of the SAM from the ICE, the re-ICE was used to immobilize the SAM for the purpose of demonstrating the ICE's reusability, as described in Section 2.3. Figure 5a,c shows that after the addition of the SAM to the re-ICE, the R ct in the Nyquist plot of the re-ICE/SAM showed a remarkable increment (1870 kΩ in Table 1), as compared to the R ct of the re-ICE (87 kΩ) and the ICE (86 kΩ). This increment in R ct confirmed the formation of the SAM insulator on the surface of re-ICE, leading to delaying the transfer of the K[Fe(CN) 6 ] 3−/4− redox couple to the electrode surface. The re-ICE/SAM showed the approximate R ct value, as compared to the R ct of the ICE/SAM, as seen in Figure 5c and Table 1, indicating the reusability of the ICE in the field of material deposition. The CV result of the re-ICE/SAM in Figure 5d displays the rapid decline of current intensity compared to the CV of the re-ICE and shows a similar tendency to the CV result of the ICE/SAM, which was related to the non-conductivity of the SAM EIS results. All EIS and CV results indicate or confirm the successful restoration of the original properties, and the reusability of ICE in material deposition.

Efficiency Percentage
To evaluate the possible factors for the recovery of ICE's characteristic after the removal of the SAM and the re-use of ICE with the SAM modification, the efficiency percentage was determined by calculation, as described in the following evaluation: The efficiency percentage of the ICE recovery after SAM removal can be calculated as follows: where R ICE is the R ct of the bare ICE, and R re-ICE is the R ct of the re-ICE after the removal of the SAM. The efficiency percentage of the reusability of ICE with the SAM modification on the surface can be calculated as follows: where R ICE/SAM is the R ct of the ICE/SAM with the addition of the SAM to the ICE, and R re-ICE/SAM is the R ct of the re-ICE/SAM with the re-modification of re-ICE with a SAM. Therefore, as shown in Figure 6, the efficiency percentage of the recovery of the ICE was found to be 90.3%, and the efficiency percentage of the recovery of the SAM modification was determined to be 90.1%, demonstrating the high efficiency results of the restoration of the ICE and the reusability of ICE for the SAM modification. These results confirmed the effectiveness of the method for the removal of thiol SAM on the gold surface of ICE, which was explored in this study, allowing us an estimation of the efficacy of this means for the property rebuilding of the ICE for the material deposition applications. The efficiency percentage of the reusability of ICE with the SAM modification on the surface can be calculated as follows: Efficiency (%) = (RICE/SAM/Rre-ICE/SAM) × 100 (2) where RICE/SAM is the Rct of the ICE/SAM with the addition of the SAM to the ICE, and Rre-ICE/SAM is the Rct of the re-ICE/SAM with the re-modification of re-ICE with a SAM. Therefore, as shown in Figure 6, the efficiency percentage of the recovery of the ICE was found to be 90.3%, and the efficiency percentage of the recovery of the SAM modification was determined to be 90.1%, demonstrating the high efficiency results of the restoration of the ICE and the reusability of ICE for the SAM modification. These results confirmed the effectiveness of the method for the removal of thiol SAM on the gold surface of ICE, which was explored in this study, allowing us an estimation of the efficacy of this means for the property rebuilding of the ICE for the material deposition applications.

Conclusions
The aim of this work was to study the most effective method for removing the modified SAM on an ICE's gold surface in order to determine the plausibility of a reuse procedure for the electrode.
Therefore, in this study, a convenient, simple, and efficiency strategy to remove SAM on the gold surface of ICE was explored by treatment for 10 min with a solution of NaBH4 with the purpose of reusing ICE to save money, protect the environment, and expeditiously manage experiments.
The full removal of the SAM and the good reusability of ICE with re-addition of the SAM were evaluated and confirmed by analyzing the electrochemical measurements, such as EIS and CV, and by using microscopy techniques such as XPS and FT-IR.
The high-efficiency percentages for the recovery of the electrochemical characteristics of ICE, and for the re-deposition of the SAM on the ICE surface, were also determined, and found to be 90.3% and 90.1%, respectively, indicating a well-founded approach for the regeneration of ICE's gold surface in applications of material deposition, providing advantages in terms of cost savings, experimental control, and environmental protection.
A new and concise route for cleaning the bare electrode surface by applying a NaBH4

Conclusions
The aim of this work was to study the most effective method for removing the modified SAM on an ICE's gold surface in order to determine the plausibility of a reuse procedure for the electrode.
Therefore, in this study, a convenient, simple, and efficiency strategy to remove SAM on the gold surface of ICE was explored by treatment for 10 min with a solution of NaBH 4 with the purpose of reusing ICE to save money, protect the environment, and expeditiously manage experiments.
The full removal of the SAM and the good reusability of ICE with re-addition of the SAM were evaluated and confirmed by analyzing the electrochemical measurements, such as EIS and CV, and by using microscopy techniques such as XPS and FT-IR.
The high-efficiency percentages for the recovery of the electrochemical characteristics of ICE, and for the re-deposition of the SAM on the ICE surface, were also determined, and found to be 90.3% and 90.1%, respectively, indicating a well-founded approach for the regeneration of ICE's gold surface in applications of material deposition, providing advantages in terms of cost savings, experimental control, and environmental protection.
A new and concise route for cleaning the bare electrode surface by applying a NaBH 4 solution was also presented in this paper.