Relationship of Mineralogical Composition to Thermal Expansion, Spectral Reflectance, and Physico-Mechanical Aspects of Commercial Ornamental Granitic Rocks

The aim of the present study is to link the thermal expansion, spectral reflectance, and physico-mechanical aspects of different types of commercial granitic rocks with their mineralogical and chemical composition. The granitic rock types were characterized using several analyses, including petrography, chemical, mineralogical, and thermo-gravimetrical analysis using XRF, XRD, and TG/DTG/DSC techniques. The rock types were subjected to several performance tests, such as tests of their thermal expansion, spectral reflectance, and physico-mechanical properties. The results revealed that quartz, albite, and potash feldspar with minor amounts of mica (biotite/muscovite/annite) are the main mineralogical constitutes, in addition to some alteration minerals, such as kaolinite, saussorite, and prehnite. The studied granitic rocks were classified as monzogranite/syenogranite of high K-calc-alkaline and peraluminous characters and are related to late- to post-collisional settings. The thermogravimetrical analysis revealed that the overall mass loss over the whole temperature range up to 978 °C did not exceed 3% of the initial weight for all studied rocks. The results of thermal expansion revealed that the maximum change in linear thermal expansion for all rock types did not exceed 0.015% of their initial lengths at an unusual air temperature of 50 °C. The spectral analysis revealed that iron and hydroxyl ions are the main spectral absorption features that appeared in the VIS-NIR and SWIR regions, in addition to the appearance of the common and distinctive absorption peaks of the main mineral composition. Furthermore, the spectral reflectance demonstrated that the granitic rock types of low iron oxide content achieved a high reflectivity percent in the VIS-NIR and SWIR spectral regions compared with those of high iron content. As a general trend, the granitic rock types of high iron content and/or lower quartz content exhibited a high performance regarding their physical and mechanical properties, such as water absorption, apparent porosity, bulk density, compressive strength, and abrasion resistance. The results of water absorption, density, strength, and abrasion resistance of the studied granitic rocks are in the range of 0.14–0.31%, 2582–2644 kg/m3, 77.85–222.75 MPa, and 26.27–55.91 Ha, respectively, conforming to the requirements of ornamental stones according to the ASTM standard.


Introduction
Ornamental stones are natural stones of igneous, sedimentary, and metamorphic origins that can be cut into blocks and slabs and used for flooring, paving, cladding, funeral monuments, and statues due to the varieties of their colors in addition to their soundness and compactness. According to Gomes et al. [1], ornamental stones are subdivided into two Ludovico-Marques et al. [5] studied the mechanical evaluation of some historical building stones, particularly granite and sandstone, using physical properties. They found, using a proposed model, a distinct dependency of the mechanical properties of the rocks on their physical properties, particularly porosity.
The textural features, mineral composition, physical and mechanical properties, and the exposing environmental conditions are considered the important factors affecting the alteration and deterioration of the natural and artificial stone materials [17].
The research significance of the present paper is as follows.
The most pronounced characteristic of the granitic igneous rocks is the great variation of their mineralogical composition and, consequently, their chemical composition. Such variations in mineralogical composition could have a great effect on their physical properties, particularly density, as reported by Siegesmudet al. [10] and Gautamet al. [18]. Furthermore, the variation in the mineral composition of igneous rocks may affect their thermal and spectral reflectance behaviors [8][9][10][11][12][13][14][15][16].
Moreover, looking for the literature review, there are not enough studies about the physical and mechanical properties of granitic igneous rock and their relationship to the mineralogical composition and their suitability as ornamental stones.
Therefore, the present work is a comprehensive study that aims at linking the variations in thermal expansion behaviors, spectral reflectance features, and physico-mechanical properties of different types of commercial granitic rocks to their mineralogical and chemical composition.

Materials (Granitic Rock Types)
Eight types of granitic rocks of commercial names (Gandonna, pink granite, buff granite I (coarse grain), buff granite II (medium grain), red granite, Fantazia, Rosa granite, Qusseir brown) used as ornamental stones were selected in this study ( Figure 1). These commercial types were supplied from the marble and granite factories located in Shaq El-Theban Area, Cairo.

Methods
The aim of the present study was accomplished by characterizing the rock types from petrographical, mineralogical, chemical, and thermogravimetrical points of view using a PLM (polarizing light microscope), X-ray diffraction (XRD), X-ray fluorescence (XRF), thermogravimetry (TG) and its derivative (DTG), and differential scanning calorimetry (DSC) techniques, respectively. In addition, the thermal expansion, spectral reflectance, physical properties (water absorption, density, and porosity), and mechanical properties (compressive strength and abrasion resistance) were also measured. The results of the assessment of the physico-mechanical properties are compared with the international standard specifications related to ornamental stones.

Petrographical Investigation
The rock types were prepared by cutting the rock samples into thin slabs and polishing them carefully into thin sections (one section per rock type). The thin sections were then petrographically investigated under a polarizing light microscope (Olympus bx53 type (Tokyo, Japan)).

X-ray Diffraction Analysis
The selected types of granitic rocks were crushed and ground to a fine powder shape (<63 µm) using a ball mill machine. The ground rocks were quartered several times until the representative quantity was selected (one sample per rock type). The selected quantity was analyzed for mineralogical composition in the range of 4 to 75 (2θ) using XRD (Philips 1730 diffractometer with Ni filter, at a scan speed of 0.5 mine1, Cu Ka radiation, National Research Centre, Dokki, Egypt). The quantitative analysis of the rock-forming minerals was also performed using Reitveld refinement.

X-ray Fluorescence Analysis
The full chemical composition was assessed, including major oxides (%) and minor elements (ppm) in addition to the loss on ignition (L.O.I., %) of the ground rocks of less than 63 µm size (2 samples per rock type). The samples were measured using XRF at the National Research Centre Laboratories (Axios PANalytical 2005, Sequential WD-XRF Spectrotometer, Almelo, The Netherlands, using ASTM E-1621 standard guide for elemental analysis by wavelength-dispersive X-ray fluorescence spectrometer). The data were processed through the advanced data treatment software of the PAnalytical Super Q package with the multielemental synthetic standards prepared by the BGS/PAnalytical Corporation.

Thermo-Gravimetric Analysis
The thermal behavior of the selected rock types under gradual elevating, temperatures expressed by thermogravimetry (TG), derivative thermogravimetry (dTG), and differential scanning calorimetery (DSC) was measured. The powdered rock types (<63 µm size) of 16 mg mass were subjected to heating at 10 • C/min over the whole temperature range of 34 to 978 • C under inert nitrogen gas conditions using (LabSys EVO Setaram Instrumentation, Caluire-et-Cuire, France).

Linear Thermal Expansion
The measurement of the linear thermal expansion coefficient (αL) and thermal strain (∆L) for the selected granitic rock types was carried out using a dilatometer (model NET-ZSCH DIL 402 PC (Selb, Germany)). The rock types were prepared in a rod shape of 12.5 mm length (one sample per rock type) and heated at a rate of 5 • C/min in a temperature range of 30 to 1000 • C.

Spectral Reflectance
The spectral reflectance features of the rock types were measured using a double-beam spectrophotometer (GascoCorp., V. 570, Rev. 1, Easton, PA, USA) in the wavelength range of 350 to 2500 nm at intervals of 2 nm, with 1156 total points. The rock types were prepared in a polished square shape of 2 cm × 2 cm area and 0.5 cm thickness.

Physico-Mechanical Properties
The selected rock types were prepared as cubic shapes of 50 mm × 50 mm × 50 mm dimensions using a rock-cutting machine. The physical properties (water absorption, apparent porosity, and bulk density) were measured for the prepared rock types (six samples per test) according to standard test methods [19,20] at room temperature. The mechanical properties (compressive strength and abrasion resistance) were measured according to standard test methods [21,22].

Petrographical Investigation
An Olympus bx53 polarizing microscope was used for petrographic studies in order to identify the mineralogical constituents as well as textural relationships for each commercial rock type. The petrographical properties of the granitic rock types were presented in Figure 2 and summarized in Table 1. According to their modal analysis (quartz-plagioclase-K-feldspar percentage), the examined commercial rocks were classified based upon IUGS classification [23] and described as follows: The Gandonna rock type is a whitish-grey color and is characterized as a medium-to coarse-grained hand specimen ( Figure 1a). Petrographically, this rock type is described as a "monzogranite". It is composed of plagioclase, K-feldspar, quartz, and biotite as essential minerals. Allanite and zircon are the main accessory minerals. K-feldspar is represented by anhedral, medium-to coarse-grained (up to 6 mm in length and 4.3 mm in width), flamy (veins) orthoclase perthite and patchy perthite. Patchy perthite exhibits slight turbidity, whereas orthoclase perthite is pristine (Figure 2a). Quartz occurs as medium-to coarse-grained and exhibits a normal extinction. Plagioclase is represented by subhedral and tabular crystals. They include two types of plagioclase: the first is medium-grained, reaches up to 2.7 mm in width and 4.2 mm in length, is commonly Carlsbad-zoned and shows extensive saussuritization, while the second type is fine-grained, up to 1.2 mm in length and 0.4 mm in width, commonly reveals lamellar twinning and is less altered. Biotite occurs as flaky crystals mostly altered to chlorite and associated with plagioclase. Allanite occurs as reddish-brown crystals associated with biotite crystals. It is fractured and filled by iron oxides (Figure 2b). Short minute crystals of zircon occur as fine-grained and embedded in orthoclase perthite.  The pink granite rock type is characterized by a reddish color with a medium-grained in the hand specimen ( Figure 1b). Petrographically, this rock type is classified as "monzogranites". It is composed of plagioclase, K-feldspar, and quartz as the main constituents. Potash feldspars occur as medium-grained and turbid perthite and antiperthite. String and patch are the two types of perthite, while antiperthite is of patch type (up to 4.3 mm length × 4.1 mm width). A reaction rim of albite occurs between two crystals of perthite. Plagioclase occurs as medium-grained and is extensively saussuritized. In addition, lamellar twinning, pericline as well as zoned crystals occur (Figure 2c). Quartz mostly occurs as fine-to medium-grained and anhedral crystals. Normal as well as undulose extinction occur. Biotite occurs as fine-grained, flaky crystals that are partially altered to chlorite along their peripheries. Zircon and titanite are the main accessory minerals. Zircon is present as a euhedral that is commonly embedded in plagioclase crystals. Titanite is common as subhedral to euhedral (sphenoidal shape) (Figure 2d), is usually associated with biotite and quartz, and occurrs as aggregates.
The buff granite "I" rock type (coarse-grained) is described as coarse-grained with a buff color in the hand specimen ( Figure 1c). Petrographically, this rock type is classified as "Syenogranite". It mainly comprises potash feldspars, plagioclase, quartz, and muscovite minerals. K-feldspars are represented by coarse-grained perthite and microcline, which exhibit slightly turbid surfaces (due to the development of kaolinitization). Occasionally, these rocks engulf quartz, plagioclase, and muscovite crystals. Plagioclase (albite) occurs as medium-grained, euhedral to subhedral crystals. It exhibits lamellar twinning with slight saussuritization. They are sometimes twisted and fractured as a result of deformation processes ( Figure 2e). Quartz occurs as fine to medium-grained, anhedral crystals, rarely showing undulose extinction. Muscovite flacks occur as fine-to medium-grained crystals and are found either as primary or secondary shreds filling fractures of potash feldspar.
The buff granite "II" rock type (medium-grained) is described as medium-grained with a buff color in the hand specimen ( Figure 1d). Petrographically, this rock type is classified as "Syenogranite" and consists mainly of K-feldspar, plagioclase, quartz, and muscovite as essential minerals. K-feldspars are represented by anhedralflamy and patchy sections. They mostly engulf plagioclase and muscovite crystals ( Figure 2f). Plagioclase occurs assubhedral, tabular crystals measuring 3.5 mm in length and 1.8 mm in width. It shows lamellar and pericline twinning and is rarely zoned. It reveals slight to extensive saussuritization ( Figure 2g). Quartz occurs as fine-to medium-grained, anhedral crystals, and corrodes other constituents. Irregular flakes of muscovite are commonly associated with perthite.
The Fantazia rock typeis characterized by a white color with a medium-to coarsegrained in hand specimen ( Figure 1e). Petrographically, this rock type is classified as "monzogranite". It consists essentially of albitic plagioclase and quartz with a small amount of K-feldspar. Albite crystals are tabular, pristine, and medium-grained ( Figure 2h). They show both pericline and lamellar twinning that is slightly altered to saussurite. Occasionally, albite is twisted, fractured and cut by quartz. Quartz occurs as fine-to medium-grained, with normal extinction and mostly corroded plagioclase crystals. K-feldspars occur as patchy, pristine perthite. Biotite occurs as a fine-grained, flaky crystal and is hosted by plagioclase crystals.
The red granite rock type is described as a medium grain with a reddish color in the hand specimen (Figure 1f). Petrographically, this rock type is classified as "Syenogranite". It constitutes mainly of K-feldspar, quartz, plagioclase and biotite. Potash feldspar is represented by extensive turbid crystals, medium to coarse-grained (2.7 mm length × 3.1 mm width) perthite (Figure 2i,j), orthoclase perthite and antipertite crystals. They suffered from high kaolinization processes. Quartz occurs as medium-grained, anhedral (angular) to subrounded crystals with normal extinction and wavy extinction. It is commonly cracked and surrounded by perthite. Plagioclase is represented by subhedral, tabular, medium-grained (1.6 mm length × 1.2 mm width) crystals and exhibitspericline and lamellar twinning that has sometimes disappeared due to the kaolinization process. A small amount of biotite occurs as fine-grained and is completely altered to chlorite and muscovite along their cleavage and peripheries.
The Rosa granite rock typeis a pinkish-white color and is characterized by a medium-to coarse-grained in-hand specimen (Figure 1g). Petrographically, this rock type is classified as "monzogranite". It contains K-feldspar, quartz, plagioclase, and biotite as essential minerals. K-feldspar is represented by pristine, medium to coarse-grained orthoclase perthite. Quartz occurs as medium-grained with normal extinction. Plagioclase is represented by tabular crystals that show clear lamellar, pericline and zoned twinning. Fine-grained biotite occurs as flaky crystals, mostly altered to chlorite and mostly enclosed in orthoclase perthite.
The Qusseir brown rock type is a brownish color and is characterized by a mediumgrained in-hand specimen (Figure 1h). Petrographically, this rock type is classified as "monzogranite". It is equigranular, medium-grained and composed essentially of potash feldspars, plagioclase, quartz, and biotite. Potash feldspar is represented by turbid, fine-to medium-grained (av. 2.9 mm length × 2.7 mm width) perthite crystals. They are corroded by quartz, engulfing the skeletal quartz crystal, and are fractured and filled by quartz. Quartz occurs as interstitial grains filling the fractures between other constituents. It commonly reveals undulose extinction (Figure 2k). Granophyric textures are common due to intergrowth between quartz and potash feldspar (Figure 2l). Turbid plagioclase occurs as tabular, medium-grained crystals that are completely kaolinitized and occasionally fractured and filled by quartz. Biotite is represented by one crystal, which was fine-grained and surrounded by perthite crystals.

Thermal Analysis by (TG/DTG/DSC)
Thermogravimetric analysis (TG) is an analytical technique used to measure the thermal stability of a material and its fraction of volatile components by monitoring its mass change upon heating at a constant rate [33]. According to Gautam et al. [34], high temperatures have a very important effect on the physical and mechanical properties of rocks in the field of rock mechanics for several engineering applications, including, for example, underground nuclear waste storage. These effects are closely related to their mineral composition and microstructure features.
The thermogravimetry (TG) and differential thermogravimetry (DTG) curves, as graphically plotted in Figure 6, showed a variation in the mass as a function of temperatures. A significant mass loss was observed at various temperatures less than 200 • C for all rock types that represented the evaporation of physically (absorbed) and chemically bonded water that was liberated at 300 • C [34][35][36][37]. In this study, the reduction in mass because of the release of physically free (absorbed) and chemically bound water up to 200 • C was found to be 1.949%, 1.210%, 1.093%, 0.164%, 0.471%, 0.257% for Gandonna (a), pink granite (b), buff granite II (d), fantazia (e), rosa granite (g), and qusseir granite (h) at temperatures of 137 • C, 150 • C, 137 • C, 85 • C, 132 • C, and 96 • C, respectively. The rock types buff granite I (c) and red granite (f) showed an inconsiderable mass loss at that range of temperatures, which was confirmed by their thermo-gravimetric derivative peaks at the same figure that indicated a very low rate of mass change by time (%/min.). A further mass loss was observed with excessive heating between 400 and 800 • C. Such loss in mass was attributed to the releasing of crystal water [36,37] or water-bearing mineral phases [34].
The variations in mass loss of the different rock types may be attributed to their mineralogical composition, especially the secondary (alteration) minerals. It was noticed that the loss in mass in the rock types (Figure 6a,b,d) was higher than other types due to the presence of high percentages of alteration minerals. However, the overall loss in mass over the whole temperature range of 34 to 978 • C did not exceed 3% of the initial weight for all studied rocks. As shown on the differential scanning calorimetery (DSC) or heat flow curve in Figure 6, a small endothermic peak marked by a circle was detected around 570 • C for all rock types representing the phase transition of α-β quartz at 573 • C [11].

Linear Thermal Expansion
The relative change in sample length depending on the considered temperature interval is expressed as the linear thermal expansion [18]. The relationship between the coefficients of linear thermal expansion of different granitic rock types over a wide range of temperatures from 30 to 1000 • C was plotted in (Figure 7). In this figure, three relationships were plotted with the temperature change:(a) change in length or thermal strain (dL/Lo), (b) the linear thermal expansion coefficient (α T ), and (c) the rate of linear thermal expansion (dα). It is well known that the coefficient of linear thermal expansion (α T ) is calculated from the following equation [38]: where dL is the change in sample length (mm) over a temperature range (dT) ( • C), Lo is the initial sample length (mm), and dL/Lo is the derivative of thermal strain. Table 3 shows the measurements of thermal strain (relative length change, %) and the coefficient of linear thermal expansion for the studied rock types at different temperatures.  As shown in Figure 7, the first sharp increase in the linear thermal expansion coefficient of the studied igneous rocks was detected around 570 • C, which represented the quartz mineral (α-β transition phase) that appears at 573 • C [39]. This phase is supported by the appearance or jump in the peak of the thermal coefficient rate (dα) in the same figure; in addition, it is well confirmed in the curve of differential scanning calorimetry (DSC) (Figure 6). A second increase or jump in the coefficient of linear thermal expansion was observed in the range of 700 to 900 • C for some rock types ((a) Gandonna, (b) pink granite, (c) buff granite I, (d) buff granite II). Such an increase is also supported by a second appearance or jump in the peak of thermal coefficient rate (dα) in the same figure, which may be related to the high percentage of quartz in their composition (Table 3). It could be attributed to the phase transition of quartz to hexagonal tridymite at about 800 • C [39]; however, this transition was not indicated in the differential scanning calorimetry (DSC) curve. As given in Table 4, an increase in the values of the linear thermal expansion coefficient was clearly noticed with increasing temperature until 700 • C; after that, it begins to decrease with temperature increases up to 1000 • C. It was also observed that the relative change in length for all rock types of different colors did not exceed 0.015% of the initial sample length at an unusual air temperature of 50 • C.

Spectral Reflectance
As the rocks are composed of minerals and are compositionally more complex and variable than minerals, their diagnostic spectral curves are therefore difficult to define. However, the description of the spectral characters of rocks is possible based on the spectral characters of the constituent minerals and textural properties such as grain size; i.e., it depends on their chemical composition, mineralogy, grain size, and color [12].
In the present study, the spectral characterization of the different granitic rock types was determined in the solar reflectance region over the wavelength range of 0.35-2.500 µm or 350-2500 nm. This region is subdivided into the visible-near infrared region (VIS-NIR) in the range of 0.4-1.0 µm or 400-1000 nm and the short-wave infrared region (SWIR) in the range of 1.0-3.0 µm or 1000-3000 nm (Figure 8). The results of bidirectional spectral reflectance of the eight igneous rock types (gandonna, pink granite, buff granite I, buff granite II, fantazia, red granite, rosa granite, gusseir brown) are graphically plotted against the wavelength in Figure 9a-h, respectively. It is observed from Figure 9 that the reflectance scale (Y-axis) for all rock types is not uniform due to the variable response of these rocks to spectral reflectance, which indicates the variation in the mineral content and type.
The rock types revealed a notable increase in the spectral reflectance with variable proportions from shorter to longer wavelengths in the visible-near infrared region (VIS-NIR) around 800 nm, except for rock type Fantazia (e), which exhibited an early increase in the spectral reflectance at lower wavelengths around 450 nm which decreased gradually with increasing wavelength. A higher spectral reflectance in the visible-near infrared region (VIS-NIR) was recorded for the rock type (e) fantazia, with increasesof about 67% observed. This was followed by rock types (d) buff granite II, (c) buff granite I, (b) pink granite, (g) rosa granite, (a) gandonna, (f) red granite, and (h) qusseir brown, with reflectance values of 57%, 50%, 46%, 40%, 35%, 28%, and 21%, respectively. This order is well-matched with the gradient in the colours of rock type, beginning with a light colour as in fantazia type (e) and ending with a dark colour as in qusseir brown type (h). This variation may be attributed to the variation in the iron content, as given in Table 2. The reflectivity values of the studied granitic rocks were deemed similar to those recorded by Bailin and Xingli [12] (40-70%) for several acidic rock samples.
It was mentioned that the different granitic rock types have similar mineral compositions as detected from X-ray diffraction analysis (XRD), with their compositions including quartz, plagioclase (albite), alkali feldspar (orthoclase), and mica (annite, biotite), while some alteration minerals such as kaolinite, zeolite, and prehnite were detected in some rock types. The double beam spectrophotometer analysis revealed the appearance of major common absorption peaks of different depths for all rock types at approximately similar wavelengths (400 nm, 900 nm, 1400 nm, 1900 nm, 2200 nm) that are distinctive to their mineral composition, as shown in Figure 9. The spectral curves of the studied rock types were found near to the standard characteristics features of the rock-forming minerals according to the library of the U.S Geological Survey (USGS, file report) [40]. It was observed from Figure 9 that the main spectral absorption features that dominated in the VIS-NIR (400-1000 nm) region are related to iron ions (Fe 2+ , Fe 3+ ) [14]. Iron occurs as a variety of oxides and hydroxides, with ferric ions displaying a positive absorption border between 400-600 nm and two other bands near 520 nm and 900 nm. Moreover, ferrous ions display an absorption band near 1100 nm [12].
In the present study, two major broad absorption bands were detected for iron in the VIS-NIR region. One absorption band was around 400 nm, while the other band is around 900 nm.
Regarding the SWIR region of the wavelength range 1000-2500 nm, it is marked by the spectral absorption features of hydroxyl ions (O-H), water molecules (H 2 O), and carbonates (CO 3 ) [12].
In the rock types Gandonna (a) and Pink granite (b), the absorption bands at the approximate wavelengths of 1400 nm and 1900 nm may be attributed to H 2 O molecules due to the presence of zeolite in their mineral composition according to XRD analysis. The hydroxyl ion (O-H) is a widespread constituent in rock-forming minerals such as clays, mica, and chlorites. In the present study, the spectral absorption features of (O-H) were observed at several bands around 1400 nm, 1900 nm, 2200 nm, which was typically for Al-OH, 2350 nm, which was typically for Mg-OH, and 2400 nm. Similarly, Zhou and Wang [15] recorded the presence of hydroxyl absorption bands for their studied granitic rocks at the same wavelengths, which indicatedthe existence of multiple hydrated mineral species. The presence of the last three bands is very common in clay and hydrous silicates. This is the case of rock types (a) gandonna and (h) qusseir brown due to the presence of kaolinite and annite minerals. Figure 10 illustrates the relationship between the spectral reflectance of the rock types and their contents of iron oxide (Fe 2 O 3 , %). It was observed that the percentage of reflectance decreases with increasing iron content. These results were similar to those obtained by Borisova [41].

Physico-Mechanical Properties
Figure 11a-d shows the results of water absorption, apparent porosity, bulk density, compressive strength, and abrasion resistance of the studied granitic rock types. It was observed that the increase in the apparent porosity led to an increase in water absorption (Figure 11a) and, consequently, a reduction in dry and SSD bulk density (Figure 11b). The results revealed that the density of the studied granitic rock types ranged from 2582 kg/m 3 to 2645 kg/m 3 . Siegesmund et al. [10] found that the values of apparent density and porosity of several granitic rocks are in the range of 2.54-2.67 g/cm 3 and 0.3-3.37%, which seemed similar to the results obtained in the present study. It was observed that the rock types with high iron contents have a high bulk density, except for the rock type (e) fantazia, which was of a very low iron content (0.486%) but exhibited a higher bulk density (2619 kg/m 3 ) compared to the rock type (f) red granite, which was of a higher iron content (1.126%). This is due to the lower apparent porosity of fantazia (0.54%) compared to red granite (0.66%). According to the results of the compressive strength test, as plotted in Figure 11c, it was observed that the rock types of higher bulk density have higher compressive strength values except for the rock type (f) red granite, which demonstrated high compressive strength despite its relatively lower density. This may be attributed to its lower quartz content.
In the same line, the results of abrasion resistance, as plotted in Figure 11d, showed an increase in the groove width representing a reduction in the abrasion resistance. On the contrary, a decrease in the hardness of the granitic rock types occurs with decreasing bulk density.
Comparing the results of physical properties with the limits of international standard specification ASTM C615/C615M [42] relating to "Granite Dimension Stone", it was found that the water absorption values of the granitic rock types range from 0.14% to 0.31%, which complies with the requirements of the water absorption limit (0.4% max.). The results of bulk density of the granitic rock types range from 2582 kg/m 3 to 2645 kg/m 3 , which complies with the requirements of the density limit (2560 kg/m 3 min.).
Regarding the results of the mechanical properties and their relationship with the standard specification (ASTM C615/C615M) [42], it was observed that the values of compressive strength of the granitic rock types are in the range of 77.85 MPa to 222.75 MPa, which indicates that not all rock types achieved the requirement of compressive strength limit (131 MPa min.). However, the rock types that did not satisfy the recommended limit can be used in building cladding, which does not require high strengths; they can also be used in light-duty purposes.
The values of abrasion resistance of all rock types range from 25.12 Ha to 55.91 Ha, which satisfies the requirement of the specification limit (25 Ha min).
The X-ray diffraction analysis and petrographical investigation demonstrated that the main mineralogical constitutes are quartz, albite, and potash feldspar, with minor amounts of mica (biotite/muscovite/annite). Some alteration minerals such as kaolinite, saussorite, and prehnite, in addition to some accessory minerals such as zircon and titanite, were detected.
According to thermogravimetrical analysis, the overall mass loss over the whole temperature range up to 978 • C did not exceed 3% of the initial weight for all studied rocks. Moreover, significant mass loss was observed at various temperatures less than 200 • C for all rock types, which represented the evaporation of physically (absorbed) and chemically bonded water that was liberated at 300 • C.
The results of thermal expansion revealed that the maximum change in linear thermal expansion for all rock types did not exceed 0.015% of their initial lengths at an unusual air temperature of 50 • C.
The spectral analysis revealed that iron and hydroxyl ions are the main spectral absorption features appearing in the VIS-NIR and SWIR regions, in addition to the appearance of the common and distinctive absorption peaks of the main mineral composition. Furthermore, the spectral reflectance demonstrated that the granitic rock types with low iron oxide contents achieved a high reflectivity percent in the VIS-NIR and SWIRspectral regions compared to rock types with high iron contents.
The results of water absorption, density, strength, and abrasion resistance of the studied granitic rocks are in the range of 0.14-0.31%, 2582-2644 kg/m 3 , 77.85-222.75 MPa, and 26.27-55.91 Ha, respectively, conforming to the requirements of ornamental stones according to the ASTM standard.  Data Availability Statement: The study did not report any data.