Coupling Removal of P-Chloronitrobenzene and Its Reduction Products by Nano Iron Doped with Ni and FeOOH (nFe/Ni-FeOOH)

The removal of chlorinated pollutants from water by nanoparticles is a hot topic in the field of environmental engineering. In this work, a novel technique that includes the coupling effect of n-Fe/Ni and its transformation products (FeOOH) on the removal of p-chloronitrobenzene (p-CNB) and its reduction products, p-chloroaniline (p-CAN) and aniline (AN), were investigated. X-ray diffraction (XRD) and transmission electron microscopy (TEM) were employed to characterize the nano-iron before and after the reaction. The results show that Fe0 is mainly oxidized into lath-like lepidocrocite (γ-FeOOH) and needle-like goethite (α-FeOOH) after 8 h of reaction. The coupling removal process and the mechanism are as follows: Fe0 provides electrons to reduce p-CNB to p-CAN and then dechlorinates p-CAN to AN under the catalysis of Ni. Meanwhile, Fe0 is oxidized to FeOOH by the dissolved oxygen and H2O. AN is then adsorbed by FeOOH. Finally, p-CNB, p-CAN, and AN were completely removed from the water. In the pH range between 3 and 7, p-CAN can be completely dechlorinated by n-Fe/Ni within 20 min, while AN can be nearly 100% adsorbed by FeOOH within 36 h. When the temperature ranges from 15 °C to 35 °C, the dechlorination rate of p-CAN and the removal rate of AN are less affected by temperature. This study provides guidance on the thorough remediation of water bodies polluted by chlorinated organics.


Introduction
P-chloronitrobenzene (p-CNB) has been classified as a persistent toxic substance in which the main pathway of release into the environment encompasses its utilization in the manufacture of dyes, corrosion inhibitors, medicines and pesticides [1,2]. The extent of its toxicity, carcinogenicity, mutagenicity and teratogenicity on humans and biodiversity has already been established [3][4][5][6][7]. Thus, it is very necessary to devise feasible and effective methods to remove p-CNB from the environment in order to prevent the fatal consequences of the chemical on human health and biodiversity. Researchers use both biological and chemical methods to remove p-CNB from the environment [5,8]. However, the biological method that included the use of an anaerobic sludge system to facilitate reduction of the p-CNB is not efficient due to its strong recalcitrance to biodegradation as well as its high biological toxicity [2,5]. The chemical methods, including photocatalytic oxidation [9], Fenton oxidation [10,11] and nanotechnology [2,12], have been widely used to reduce p-CNB. Among these chemical methods, nanotechnology (nanoscale zerovalent iron (Fe 0 )) has been identified as the most effective due to its relatively low cost, high adsorption capacity, strong reactivity and high reductivity [13][14][15][16][17].

Materials and Chemicals
The chemicals used in this study included p-chloronitrobenzene, nickel sulphate (NiSO 4 ·6H 2 O), ferrous sulphate (FeSO 4 ·7H 2 O), sodium hydroxide (NaOH), hydrochloric acid (HCl) and sodium borohydride (NaBH 4 ). All chemicals were of analytical grade and obtained from Sinopharm Chemical Reagent Co. Ltd. in Shanghai, China. Chromatographic methanol was acquired from Tianli Chemical Reagent Company (Tianjin, China). Deionized water was used in the preparation of the chemical solutions.

Preparation of Materials
The n-Fe/Ni was prepared by the liquid-phase reduction method. It involves the conventional reduction of Fe 2+ with NaBH 4 in a nitrogen (N 2 ) atmosphere. Specifically, 40 mL of 1 M FeSO 4 solution was put into a 500 mL three-necked round bottom flask. Then, 80 mL of 1 M NaBH 4 solution was added to the FeSO 4 solution dropwise (2 drop/s), under ambient temperature and mechanical stirring (150 rpm) to remove dissolved oxygen throughout the preparation process. N 2 was purged into the three-necked round bottom flask during the synthesis. After the dripping, 3.2 mL of 1 M NiSO 4 solution was added. The resulting mixture was mechanically stirred for 30 min to ensure uniform distribution of the Ni 2+ on the surface of the nano-iron. The as-prepared material was filtered and washed with deionized water. It was later dried under vacuum at −30 • C for about 15 h in a freeze dryer and vacuum-packed and preserved in a refrigerator. The synthesized n-Fe/Ni was analyzed using an inductively coupled plasma emission spectrometer (Thermo Elemental, IRIS Advantage ER/5, Thermo Elemental Inc., Waltham, MA, USA). The result shows that the Ni:Fe mass ratio is 2.17:97.83.

Batch Experiments
Batch experiments for the coupling removal of the p-CNB and its reduction products (p-CAN and AN) were carried out in a 500 mL Erlenmeyer bottle. First, 0.5 g of freshly prepared n-Fe/Ni was added to 200 mL of the prepared p-CNB solution (10 mg/L, pH = 5-6) in a 500 mL Erlenmeyer bottle. The reaction was performed under ambient temperature and in a shaking incubator (200 rpm) to ensure adequate contact between the n-Fe/Ni and p-CNB solution. In order to determine the concentration of the p-CNB, p-CAN and AN, 2 mL of the supernatant was collected with a 5 mL syringe at pre-selected time intervals and filtered through a 0.45 µm nitrocellulose membrane. The batch experiments were performed in triplicate to ensure precision in the results obtained.
The filter liquors were analyzed by high-performance liquid chromatography (HPLC) (Ultimate 3000, Dionex, Sunnyvale, CA, USA) embedded with a C18 column (4.6 mm × 250 mm, 5 µm). The mobile phase of the HPLC contained chromatographic methanol and H 2 O at a volume ratio of 75:25 and operated at a flowrate of 1.0 mL/min. The detector wavelengths were set at 270 nm for p-CNB, at 240 nm for p-CAN and at 230 nm for AN.

Material Characterizations
The morphological characteristics of n-Fe/Ni and iron oxides were analyzed using a transmission electron microscope (TEM) (Tecnai G2 F30, S-Twin, FEI, Hillsboro, OR, USA). The crystallinity of the materials was determined using an X-ray diffractometer (XRD) (D/MAX-2500, Science Corporation, Tokyo, Japan) operated at 45 kV and 250 mA with CuKα. Figure 1 presents the TEM images of pristine and reacted Fe 0 in n-Fe/Ni. The Fe 0 nanoparticles in Figure 1a appear to be spherical and aggregated, thus forming chains [20,21]. This spherical and chain-like pattern has been attributed to the magnetic attraction of the iron [22,23]. After the 1 h reaction, the core of the Fe 0 particles became hollowed and corroded (Figure 1b), indicating that the Fe 0 in the inner core had almost completely reacted. Figure 1c displays the transformation of the spherical and chain-like pattern of the Fe 0 nanoparticles into laths and needles, which are characteristic of lepidocrocite and goethite [24].

Batch Experiments
Batch experiments for the coupling removal of the p-CNB and its reduction products (p-CAN and AN) were carried out in a 500 mL Erlenmeyer bottle. First, 0.5 g of freshly prepared n-Fe/Ni was added to 200 mL of the prepared p-CNB solution (10 mg/L, pH = 5-6) in a 500 mL Erlenmeyer bottle. The reaction was performed under ambient temperature and in a shaking incubator (200 rpm) to ensure adequate contact between the n-Fe/Ni and p-CNB solution. In order to determine the concentration of the p-CNB, p-CAN and AN, 2 mL of the supernatant was collected with a 5 mL syringe at pre-selected time intervals and filtered through a 0.45 µm nitrocellulose membrane. The batch experiments were performed in triplicate to ensure precision in the results obtained.
The filter liquors were analyzed by high-performance liquid chromatography (HPLC) (Ultimate 3000, Dionex, Sunnyvale, CA, USA) embedded with a C18 column (4.6 mm × 250 mm, 5 µm). The mobile phase of the HPLC contained chromatographic methanol and H2O at a volume ratio of 75:25 and operated at a flowrate of 1.0mL/min. The detector wavelengths were set at 270 nm for p-CNB, at 240 nm for p-CAN and at 230 nm for AN.

Material Characterizations
The morphological characteristics of n-Fe/Ni and iron oxides were analyzed using a transmission electron microscope (TEM) (Tecnai G2 F30, S-Twin, FEI, Hillsboro, OR, USA). The crystallinity of the materials was determined using an X-ray diffractometer (XRD) (D/MAX-2500, Science Corporation, Tokyo, Japan) operated at 45 kV and 250 mA with CuKα. Figure 1 presents the TEM images of pristine and reacted Fe 0 in n-Fe/Ni. The Fe 0 nanoparticles in Figure 1a appear to be spherical and aggregated, thus forming chains [20,21]. This spherical and chain-like pattern has been attributed to the magnetic attraction of the iron [22,23]. After the 1 h reaction, the core of the Fe 0 particles became hollowed and corroded (Figure 1b), indicating that the Fe 0 in the inner core had almost completely reacted. Figure 1c displays the transformation of the spherical and chain-like pattern of the Fe 0 nanoparticles into laths and needles, which are characteristic of lepidocrocite and goethite [24].    the morphology of the iron hydroxides in the shape of a lath ( Figure 2a) and needle ( Figure  2c) can be clearly observed. This is consistent with the TEM observations ( Figure 1c). The measured crystal plane spacings of lath iron hydroxideare 0.246 nm and 0.323 nm ( Figure  2b), which are in line with the crystal planes (120) and (031) of rhombic structured lepidocrocite. The measured crystal plane spacing of needle-rod iron hydroxide is 0.492 nm ( Figure  2d). This is consistent with the (020) crystal plane of rhombic goethite. HR-TEM analyses further proved that the iron hydroxides formed by n-Fe/Ni reaction with p-CNB for 8 h are lepidocrocite and goethite.

XRD Analyses
The XRD spectra of the n-Fe/Ni reacting with p-CNB at different times are shown in Considering that the Fe 0 transforms into lepidocrocite, goethite and magnetite, it represents that the Fe 0 converts into Fe 2+ and then changes further to Fe 3+ products with the help of H2O and the dissolved oxygen [14]. The XRD results are consistent with the HR-TEM results in terms of the

XRD Analyses
The XRD spectra of the n-Fe/Ni reacting with p-CNB at different times are shown in Considering that the Fe 0 transforms into lepidocrocite, goethite and magnetite, it represents that the Fe 0 converts into Fe 2+ and then changes further to Fe 3+ products with the help of H 2 O and the dissolved oxygen [14]. The XRD results are consistent with the HR-TEM results in terms of the reaction under 8 h. Although the characteristic peak of magnetite appears in the XRD pattern of n-Fe/Ni reaction for 8 h as well, its peak intensity is very weak, thus indicating that the content is small. This justifies the non-observance of magnetite in the HR-TEM results. reaction under 8 h. Although the characteristic peak of magnetite appears in the XRD pattern of n-Fe/Ni reaction for 8 h as well, its peak intensity is very weak, thus indicating that the content is small. This justifies the non-observance of magnetite in the HR-TEM results.  Figure 4 shows the XPS spectrum of n-Fe/Ni before the reaction with p-CNB. It can be seen that the peak representing Fe 0 at 706.7 eV is higher, which further confirms that the main content in n-Fe/Ni (0h) is Fe 0 . The intensity of the two peaks at 709.8 and 711.5 eV is relatively weak, indicating that only a small amount of iron exists in the forms of Fe 2+ and Fe 3+ .   Figure 4 shows the XPS spectrum of n-Fe/Ni before the reaction with p-CNB. It can be seen that the peak representing Fe 0 at 706.7 eV is higher, which further confirms that the main content in n-Fe/Ni (0h) is Fe 0 . The intensity of the two peaks at 709.8 and 711.5 eV is relatively weak, indicating that only a small amount of iron exists in the forms of Fe 2+ and Fe 3+ . reaction under 8 h. Although the characteristic peak of magnetite appears in the XRD pattern of n-Fe/Ni reaction for 8 h as well, its peak intensity is very weak, thus indicating that the content is small. This justifies the non-observance of magnetite in the HR-TEM results.  Figure 4 shows the XPS spectrum of n-Fe/Ni before the reaction with p-CNB. It can be seen that the peak representing Fe 0 at 706.7 eV is higher, which further confirms that the main content in n-Fe/Ni (0h) is Fe 0 . The intensity of the two peaks at 709.8 and 711.5 eV is relatively weak, indicating that only a small amount of iron exists in the forms of Fe 2+ and Fe 3+ .   The pH of the solution was adjusted to 3, 4, 5, 6, 7, 8, 9, 10 and 11 with dilute HCl or NaOH; then, n-Fe/Ni was added to the solution at a dose of 2.5 g/L. The variation in pH during the reaction is shown in Figure 5. As can be seen from Figure 5, when the initial pH was ≤ 6, the pH of the solution increased with the extension of the reaction time and rose to about 6.0 after 28 h. When the initial pH of solution was 7, 8 and 9, the final pH of the solution decreased to between 6.1 and 6.4 afer 28 h. However, when the initial pH was 10 Materials 2022, 15, 1928 6 of 11 and 11, the pH of the solution decreased to 7.7 and 8.8 after 28 h of reaction, respectively. The reason may be that in the reaction between Fe 0 and p-CNB, both H + consumption and H + generation occur (see Equations (1)- (6)). When initial pH was ≤ 6, H + consumption was dominant; however, when initial pH was > 6, H + generation prevailed. Since the pH of the reaction was stable at around 6 for all initial pH conditions (except for initial pH 10 and 11), no buffer solution was employed to maintain the pH of the solution during the reaction.
A number of 200 mL p-CNB solutions with a concentration of 10 mg/L were taken. The pH of the solution was adjusted to 3, 4, 5, 6, 7, 8, 9, 10 and 11 with dilute HCl or NaOH; then, n-Fe/Ni was added to the solution at a dose of 2.5 g/L. The variation in pH during the reaction is shown in Figure 5. As can be seen from Figure 5, when the initial pH was ≤ 6, the pH of the solution increased with the extension of the reaction time and rose to about 6.0 after 28 h. When the initial pH of solution was 7, 8 and 9, the final pH of the solution decreased to between 6.1 and 6.4 afer 28 h. However, when the initial pH was 10 and 11, the pH of the solution decreased to 7.7 and 8.8 after 28 h of reaction, respectively. The reason may be that in the reaction between Fe 0 and p-CNB, both H + consumption and H + generation occur (see Equations (1)-(6)). When initial pH was ≤ 6, H + consumption was dominant; however, when initial pH was > 6, H + generation prevailed. Since the pH of the reaction was stable at around 6 for all initial pH conditions (except for initial pH 10 and 11), no buffer solution was employed to maintain the pH of the solution during the reaction. The influence of pH on the coupling removal of p-CNB, p-CAN and AN by n-Fe/Ni-FeOOH is shown in Figure 6. It is prudent to include that the p-CNB was quickly converted to its reduced form (p-CAN) within 2 min (except at pH 10 and 11) of reaction with the n-Fe/Ni. Therefore, the curve of the change in the concentration of p-CNB is not shown. The influence of pH on the coupling removal of p-CNB, p-CAN and AN by n-Fe/Ni-FeOOH is shown in Figure 6. It is prudent to include that the p-CNB was quickly converted to its reduced form (p-CAN) within 2 min (except at pH 10 and 11) of reaction with the n-Fe/Ni. Therefore, the curve of the change in the concentration of p-CNB is not shown.  It is evident in Figure 6a that the reaction from pH 2 to 9 results in rapid dechlorination of the p-CAN within 20 min. This may be because the weak acid-weak base condition is favorable for n-Fe corrosion, thus providing sufficient H2 and further producing more H* under the action of Ni [25]. On the other hand, when pH = 2-9, the passivated layer on the n-Fe surface will be dissolved and thinned to some extent. Therefore, the activity of Fe 0 at the reaction site can be better developed. When pH > 9, the dechlorination efficiency of n-Fe/Ni for p-CAN becomes slower, eventually dechlorinating by 60 min and remaining constant until 120 min. When pH = 11, the dechlorination performance of n-Fe/Ni reduces drastically and the dechlorination of the p-CAN is still not completed within 120 min (Figure 6a). The reason is that Fe (OH)2 and Fe (OH)3 precipitated on the n-Fe/Ni nanoparticles to cover the reaction site of Fe 0 under alkaline conditions, making it difficult It is evident in Figure 6a that the reaction from pH 2 to 9 results in rapid dechlorination of the p-CAN within 20 min. This may be because the weak acid-weak base condition is favorable for n-Fe corrosion, thus providing sufficient H 2 and further producing more H* under the action of Ni [25]. On the other hand, when pH = 2-9, the passivated layer on the n-Fe surface will be dissolved and thinned to some extent. Therefore, the activity of Fe 0 at the reaction site can be better developed. When pH > 9, the dechlorination efficiency of n-Fe/Ni for p-CAN becomes slower, eventually dechlorinating by 60 min and remaining constant until 120 min. When pH = 11, the dechlorination performance of n-Fe/Ni reduces drastically and the dechlorination of the p-CAN is still not completed within 120 min (Figure 6a). The reason is that Fe (OH) 2 and Fe (OH) 3 precipitated on the n-Fe/Ni nanoparticles to cover the reaction site of Fe 0 under alkaline conditions, making it difficult for the Fe 0 to exert its activity [26][27][28].
In Figure 6b, the adsorption rate of the AN by FeOOH, which is formed after the transformation of the Fe 0 reacted for 8 h, is relatively fast when the pH is 2 and 3. Complete adsorption of the AN by the FeOOH occurs within 24 h of reaction. When the pH is between 4 and 9, the adsorption rate of the AN by FeOOH becomes slow, yet it is eventually completely adsorbed within 36 h of the reaction. However, when the pH is 10, the adsorption rate of the AN by FeOOH is only 21.1% for 48 h. At pH = 11, FeOOH completely loses its adsorption capacity for AN since the concentration of the AN does not decrease between 10 and 48 h. Therefore, only in acidic or slightly alkaline environments can FeOOH have a good adsorption capacity for AN [29]. Furthermore, the lower the pH, the faster the adsorption rate of AN by FeOOH [30]. Figure 7 indicates the effect of temperature on the coupling removal of p-CAN and AN by n-Fe/Ni-FeOOH. It can be observed from Figure 7a that there is a positive proportional relationship between temperature and the dechlorination of p-CAN by n-Fe/Ni. The reason is that the mass transfer rate in the reaction system accelerates with the increase in temperature and promotes dechlorination [31]. In addition, the changes in temperature lead to changes in the concentration of the dissolved oxygen (Table 1). Specifically, there is a negative correlation between the temperature and the solubility of oxygen in water, which is not conducive to the formation of the passivation layer on the n-Fe/Ni surface. Therefore, the active site of the Fe 0 on the n-Fe/Ni surface is fully utilized. Although the dechlorination rates are slightly varying with different temperatures, p-CAN is completely dechlorinated within 40 min by the n-Fe/Ni at 15, 25 and 35 • C. The test results illustrate that temperature has little influence on the dechlorination of p-CAN.  Figure 7b demonstrates that AN can be adsorbed by the FeOOH formed after the reaction between n-Fe/Ni and p-CNB at different temperatures. However, the adsorption rate of the AN by FeOOH is much faster at 25 °C than the other two scenarios. The reason is that Fe 0 can be converted into the more crystalline FeOOH at such temperatures [32][33][34].     Figure 7b demonstrates that AN can be adsorbed by the FeOOH formed after the reaction between n-Fe/Ni and p-CNB at different temperatures. However, the adsorption rate of the AN by FeOOH is much faster at 25 • C than the other two scenarios. The reason is that Fe 0 can be converted into the more crystalline FeOOH at such temperatures [32][33][34].

The Effect of Temperature on Removal Efficiency
3.4. Process and Mechanism of Coupling Removal of p-CNB, p-CAN and AN by n-Fe/Ni-FeOOH Figure 8 shows the variation in the concentration of p-CNB, p-CAN and AN over time. In Figure 8a, p-CNB is completely removed within 2 min after n-Fe/Ni is added. This is because Fe 0 , as an electron donor, reduces -NO 2 on p-CNB into the -NH 2 group (Equation (1)), so that p-CNB is converted to p-CAN. Meanwhile, Ni and Fe 0 form the Fe-Ni galvanic cell, which accelerates the electron loss in Fe 0 corrosion and further hastens the electron transfer rate. The concentration of p-CAN reaches its peak (6.8 mg/L) at 2 min and then decreases to close to 0 at 20 min (Figure 8b). In the meantime, Figure 8c indicates that the concentration of AN reaches its peak (5.2 mg/L) at 20 min. This demonstrates that p-CAN has been completely converted to AN. In the dechlorination process, only Fe 0 cannot provide electrons to achieve dechlorination [18]. Fe 0 reacts with water to form H2 (Equation (2)). And then H2 is converted by the catalyst Ni into active hydrogen atom (H*) (Equation (3)) [35][36][37]. Immediately, H* acts on the C-Cl bond of the benzene ring to hydrochlorinate p-CAN into AN [38,39].The removed chlorine atom gains electrons to become the chloride ion (Equation (4)).
When p-CNB is nitro-reduced and dechlorinated by n-Fe/Ni, Fe 0 reacts with the dissolved oxygen and water to transform into FeOOH (Equation (5)), which can form a complex with AN to adsorb AN (Equation (6)) [40,41]. As can be seen from Figure 8c, AN can be completely adsorbed by FeOOH after 28h and the adsorption rate of AN is fastest between 8 and 28 h. 0 + ─ ─ 2 + 6 + → 2+ + ─ ─ 2 + 2 2 (1) In the dechlorination process, only Fe 0 cannot provide electrons to achieve dichlorination [18]. Fe 0 reacts with water to form H 2 (Equation (2)). And then H 2 is converted by the catalyst Ni into active hydrogen atom (H*) (Equation (3)) [35][36][37]. Immediately, H* acts on the C-Cl bond of the benzene ring to hydrochlorinate p-CAN into AN [38,39].The removed chlorine atom gains electrons to become the chloride ion (Equation (4)).
When p-CNB is nitro-reduced and dechlorinated by n-Fe/Ni, Fe 0 reacts with the dissolved oxygen and water to transform into FeOOH (Equation (5)), which can form a complex with AN to adsorb AN (Equation (6)) [40,41]. As can be seen from Figure 8c, AN can be completely adsorbed by FeOOH after 28 h and the adsorption rate of AN is fastest between 8 and 28 h.
Considering that during the reaction of n-Fe/Ni with p-CNB, Ni deposited on the surface of Fe 0 may react with dissolved oxygen to form Ni 2+ and enter the solution, the concentration of Ni 2+ in the solution after the reaction for 48 h was determined by an inductively coupled plasma emission spectrometer. The concentration of Ni 2+ was 0.073 mg/L. Therefore, the heavy metal Ni in n-Fe/Ni will not cause secondary pollution in the coupling removal of p-CNB, p-CAN and AN by n-Fe/Ni-FeOOH.
Based on these analyses, a schematic representation of the process and mechanism of the coupling removal of p-CNB, p-CAN and AN by n-Fe/Ni-FeOOH is shown in Figure 9.
Considering that during the reaction of n-Fe/Ni with p-CNB, Ni deposited on the surface of Fe 0 may react with dissolved oxygen to form Ni 2+ and enter the solution, the concentration of Ni 2+ in the solution after the reaction for 48 h was determined by an inductively coupled plasma emission spectrometer. The concentration of Ni 2+ was 0.073 mg/L. Therefore, the heavy metal Ni in n-Fe/Ni will not cause secondary pollution in the coupling removal of p-CNB, p-CAN and AN by n-Fe/Ni-FeOOH.
Based on these analyses, a schematic representation of the process and mechanism of the coupling removal of p-CNB, p-CAN and AN by n-Fe/Ni-FeOOH is shown in Figure 9.

Conclusions
Coupling removal of p-CNB and its nitro-reduction products (p-CAN) and dechlorination products (AN) by n-Fe/Ni-FeOOH were investigated. XRD and TEM results show that after 8 h of reaction, the transformation products of Fe 0 are mainly lath-like lepidocrocite (γ-FeOOH) and needle-like goethite (α-FeOOH). The dechlorination efficiency of n-Fe/Ni for p-CAN and the adsorption rate of FeOOH for AN are both high, with pH between 2.0 and 9.0, while the efficiency is poor at pH > 9.0. The dechlorination of p-CAN and the adsorption of AN are less affected by temperature. The process and mechanism of n-Fe/Ni-FeOOH coupling removal of p-CNB and its reduction products are as follows: Fe 0 in n-Fe/Ni provides electrons to reduce p-CNB to p-CAN and then dechlorinates p-CAN to AN under the catalysis of Ni. Meanwhile, it is oxidized to FeOOH by dissolved O2 and H2O. AN is then adsorbed by FeOOH, so that p-CNB, p-CAN and AN are completely removed.
Author Contributions: J.L., Z.L., E.A., H.L. and X.F. conceived and designed the methodology; J.L. and Z.L. performed the experiment and prepared the composite materials; E.A., H.L. and X.F. analyzed the data. All authors evaluated and discussed the results, and wrote the paper together. All authors have read and agreed to the published version of the manuscript.

Conclusions
Coupling removal of p-CNB and its nitro-reduction products (p-CAN) and dechlorination products (AN) by n-Fe/Ni-FeOOH were investigated. XRD and TEM results show that after 8 h of reaction, the transformation products of Fe 0 are mainly lath-like lepidocrocite (γ-FeOOH) and needle-like goethite (α-FeOOH). The dechlorination efficiency of n-Fe/Ni for p-CAN and the adsorption rate of FeOOH for AN are both high, with pH between 2.0 and 9.0, while the efficiency is poor at pH > 9.0. The dechlorination of p-CAN and the adsorption of AN are less affected by temperature. The process and mechanism of n-Fe/Ni-FeOOH coupling removal of p-CNB and its reduction products are as follows: Fe 0 in n-Fe/Ni provides electrons to reduce p-CNB to p-CAN and then dechlorinates p-CAN to AN under the catalysis of Ni. Meanwhile, it is oxidized to FeOOH by dissolved O 2 and H 2 O. AN is then adsorbed by FeOOH, so that p-CNB, p-CAN and AN are completely removed.
Author Contributions: J.L., Z.L., E.A., H.L. and X.F. conceived and designed the methodology; J.L. and Z.L. performed the experiment and prepared the composite materials; E.A., H.L. and X.F. analyzed the data. All authors evaluated and discussed the results, and wrote the paper together. All authors have read and agreed to the published version of the manuscript. Data Availability Statement: All relevant data presented in the article are stored according to institutional requirements and as such are not available online. However, all data used in this manuscript can be made available upon request to the authors.