Temperature Sensor Based on Surface Plasmon Resonance with TiO2-Au-TiO2 Triple Structure

Temperature sensors have been widely applied in daily life and production, but little attention has been paid to the research on temperature sensors based on surface plasmon resonance (SPR) sensors. Therefore, an SPR temperature sensor with a triple structure of titanium dioxide (TiO2) film, gold (Au) film, and TiO2 nanorods is proposed in this article. By optimizing the thickness and structure of TiO2 film and nanorods and Au film, it is found that the sensitivity of the SPR temperature sensor can achieve 6038.53 nm/RIU and the detection temperature sensitivity is −2.40 nm/°C. According to the results, the sensitivity of the optimized sensor is 77.81% higher than that of the sensor with pure Au film, which is attributed to the TiO2(film)-Au-TiO2(nanorods) structure. Moreover, there is a good linear correlation (greater than 0.99) between temperature and resonance wavelength in the range from 0 °C to 60 °C, which can ensure the detection resolution. The high sensitivity, FOM, and detection resolution indicate that the proposed SPR sensor has a promising application in temperature monitoring.


Introduction
Surface plasmon resonance (SPR) refers to the collective oscillation of electrons on the metal surface when incident light shines on the interface between metal and medium, and the coupling of light and electrons on the metal surface forms an electromagnetic wave propagating along the metal surface [1][2][3][4][5][6][7]. When the frequency of electron oscillation is consistent with the frequency of incident light, resonance is generated [4]. When resonance occurs, the electromagnetic field on the metal surface is enhanced. The SPR sensor made of surface plasmon resonance can subtly detect the change in the refractive index of the sensing medium. SPR sensors can be used to directly measure RI or indirectly detect any physical factor causing RI changes, such as temperature, concentration, strain, magnetic field, pressure, density, and molecular species [5,[8][9][10][11][12][13][14][15][16][17][18][19].
A number of applications of temperature sensors can be seen in daily life, industrial production, and scientific research [20,21]. Sensors can monitor the room temperature and can also be used in air conditioners, induction cookers, microwave ovens, water dispensers, and other household appliances. In firefighting, measuring temperature is very important. Monitoring the temperature can find the abnormal temperature so that fire can be prevented, detected, and located [22]. In agricultural production, taking greenhouses as an example, suitable temperature is an important parameter for the plant growth processes [23]. In industrial production, such as metal smelting, the petrochemical industry, light industry, textile manufacturing, and water treatment, temperature sensors are the most common elements to ensure the normal operation of equipment [24]. In the medical industry, to ensure the activity of vaccines and other biological products, the environmental temperature should be constantly monitored during production and transportation [25]. From the above point of view, with the development of science and technology, research on temperature sensors has become a hot topic of research. The temperature sensor is developing in the direction of high accuracy and automation.
Due to the advantages of unmarkedness, real-time monitoring, quick response, and high sensitivity, SPR sensors also have important applications in temperature sensors in environmental regulation, food safety, medicine, and biological detection [8,26].
In metals where the SPR phenomenon occurs (such as gold, silver, aluminum, and copper), the precious metal gold is chemically stable and can output persistent SPR signals in the visible region [27][28][29][30][31][32]. Although gold has good oxidation resistance and corrosion resistance and can remain effective, the surface of the gold film is too smooth to adsorb a great number of molecules, thus limiting the improvement of sensor sensitivity. Titanium dioxide (TiO 2 ), a nanostructured semiconductor metal oxide, has good absorbability, excellent chemical stability, loose molecular structure, wide band gap (i.e., 3.2 eV for anatase and 3.0 eV for rutile), and high RI (i.e., 2.5 for anatase and 2.7 for rutile) [33][34][35][36][37][38][39]. Owing to the above characteristics, the TiO 2 layer is added to induce field confinement and enhancement in the interface, which is favorable for sensitivity improvement [40].
Changes in temperature can cause variations in the RI of alcohol, leading to the shift of the SPR spectrum. Nonetheless, the research on temperature sensors based on SPR film sensors has not attracted much attention. In this work, two SPR temperature sensors, i.e., TiO 2 -Au dual film structure and TiO 2 (film)-Au-TiO 2 (nanorods) triple structure, are proposed. The two sensors are simulated by the Finite Element Method (FEM). It is the purpose of this work to optimize the thickness of the TiO 2 film and the Au film, as well as the geometry of the TiO 2 nanorods, to maximize the sensitivity and FOM of the SPR temperature sensor. The optimized TiO 2 (film)-Au-TiO 2 (nanorods) triple structure SPR temperature sensor has a sensitivity of 6038.53 nm/RIU and performs −2.40 nm/ • C in temperature sensing. The sensitivity of the proposed sensor is improved by 77.81% compared with that of a traditional gold SPR sensor. This work is important not only for the enhancement of the SPR sensor but for the study of temperature measurement by the SPR sensor as well.

Theoretical Analysis
SPR is the collective oscillation phenomenon of metal particles caused by photons when light irradiates the surface of metal materials at a specific angle. The necessary condition for exciting surface plasmon (SP) is that the wave vector of the polarized incident light (k c ) should be equal to the wave vector of surface plasmon (k sp ) [41,42].
The wave vector of the polarized incident light (k c ) can be represented as [43]: where n p is the RI of the prism, λ is the incident wavelength, and α is the incident angle. The wave vector of surface plasmon (k sp ) is expressed as follows [44]: where n m represents the RI of the metal film and n s represents the RI of the sensing medium.
In this paper, the wavelength interrogation method was adopted; that is, the incident angle was fixed, and the incident wavelength was scanned in a certain range. At a particular wavelength, the reflected light intensity sharply decreases, displaying a sharp valley in the reflectance curve. The wavelength corresponding to the minimum reflectance point is the resonance wavelength. The resonance wavelength moves gradually as the RI of the sensing medium changes. The refractive index of metals varies with wavelength, and the corresponding functional relationship is as follows [45]: where n p is the RI of the prism, α is the incident angle, n m (λ) represents the RI of the metal film (varied with wavelength), and n s represents the RI of the sensing medium. The Kretschmann configuration (Figure 1a), a common SPR structure, consists of a prism, a thin metal film, and the sensing medium. When there is only gold film, Ppolarized light passes through the prism and undergoes attenuated total internal reflection at the prism/gold film interface. The evanescent wave penetrates the thin metal layer and resonates with propagating metal-dielectric surface plasmons, causing the absorption of the reflected light beam [26]. The electric field intensity is strongest at the intersection of gold film and sensing medium and declines exponentially with the increase in medium depth. After adding titanium dioxide, the high RI of TiO 2 leads to the enhancement of the interaction of the evanescent field and shifts the resonant wavelengths towards the near-infrared wavelengths [46,47]. is the resonance wavelength. The resonance wavelength moves gradually as the RI of the sensing medium changes. The refractive index of metals varies with wavelength, and the corresponding functional relationship is as follows [45]: where np is the RI of the prism, α is the incident angle, ( ) represents the RI of the metal film (varied with wavelength), and represents the RI of the sensing medium. The Kretschmann configuration (Figure 1a), a common SPR structure, consists of a prism, a thin metal film, and the sensing medium. When there is only gold film, P-polarized light passes through the prism and undergoes attenuated total internal reflection at the prism/gold film interface. The evanescent wave penetrates the thin metal layer and resonates with propagating metal-dielectric surface plasmons, causing the absorption of the reflected light beam [26]. The electric field intensity is strongest at the intersection of gold film and sensing medium and declines exponentially with the increase in medium depth. After adding titanium dioxide, the high RI of TiO2 leads to the enhancement of the interaction of the evanescent field and shifts the resonant wavelengths towards the nearinfrared wavelengths [46,47]. Sensitivity is an important parameter for evaluating the performance of SPR sensors and is generally calculated by the following formula: where ∆ is the swift of SPR wavelength and ∆ is the change in refractive index. The response sensitivity of SPR sensor to temperature is defined as: where ∆ is the change in temperature.
When it comes to evaluating sensor performance, sensitivity alone is not enough. The Sensitivity is an important parameter for evaluating the performance of SPR sensors and is generally calculated by the following formula: where ∆λ SPR is the swift of SPR wavelength and ∆n is the change in refractive index. The response sensitivity of SPR sensor to temperature is defined as: where ∆T is the change in temperature.
When it comes to evaluating sensor performance, sensitivity alone is not enough. The Figure of Merit (FOM) is another important factor, and the calculation is as follows: where S is the sensitivity of SPR sensor and FWHM is full width at half maxima of SPR reflectance spectrum. In this work, sensors for four kinds of structures were simulated. The prism material is BK7 glass, and the sensing medium is ethanol liquid, whose refractive index is affected by temperature. The four kinds of metal layers are pure gold film, pure titanium dioxide film, TiO 2 -Au film, and TiO 2 (film)-Au-TiO 2 (nanorods) triple film, respectively. The angle of incident light is 72 deg. Temperature changes linearly with RI of ethanol liquid [48]: where T is the test temperature and T 0 is the reference temperature (20 • C). Since ethanol is liquid at −144-78 • C, the performance of SPR sensors is explored at 0-60 • C (10 • C intervals), using the wavelength modulation method.

Results and Discussion
Firstly, the pure gold film SPR sensor was simulated. The sensor with a BK7 prism-Au thin film structure is shown in Figure 1b where S is the sensitivity of SPR sensor and FWHM is full width at half maxima of SPR reflectance spectrum. In this work, sensors for four kinds of structures were simulated. The prism material is BK7 glass, and the sensing medium is ethanol liquid, whose refractive index is affected by temperature. The four kinds of metal layers are pure gold film, pure titanium dioxide film, TiO2-Au film, and TiO2(film)-Au-TiO2(nanorods) triple film, respectively. The angle of incident light is 72 deg. Temperature changes linearly with RI of ethanol liquid [48]: where T is the test temperature and T0 is the reference temperature (20 °C). Since ethanol is liquid at −144-78 °C, the performance of SPR sensors is explored at 0-60 °C (10 °C intervals), using the wavelength modulation method.

Results and Discussion
Firstly, the pure gold film SPR sensor was simulated. The sensor with a BK7 prism-Au thin film structure is shown in Figure 1b   In addition to the shift in resonance wavelength, the minimum reflectance should also be noted. With the increase in the gold film thickness, the minimum reflectance decreases first and then increases. The minimum reflectance at 0 • C and 60 • C is plotted in Figure 3. When the thickness of the gold film is between 35 nm and 60 nm, the minimum reflectance is higher than 20%. In general, sensors with a minimum reflectance greater than 20% are not considered, because the sensing effect is not good enough. In the subsequent research on sensor performance improvement, sensors with a minimum reflectance of above 20% will no longer be considered. SPR sensors based on gold film thicknesses of 40 nm, 45 nm, 50 nm, and 55 nm are explored in the following study.
In addition to the shift in resonance wavelength, the minimum reflectance should also be noted. With the increase in the gold film thickness, the minimum reflectance decreases first and then increases. The minimum reflectance at 0 °C and 60 °C is plotted in Figure 3. When the thickness of the gold film is between 35 nm and 60 nm, the minimum reflectance is higher than 20%. In general, sensors with a minimum reflectance greater than 20% are not considered, because the sensing effect is not good enough. In the subsequent research on sensor performance improvement, sensors with a minimum reflectance of above 20% will no longer be considered. SPR sensors based on gold film thicknesses of 40 nm, 45 nm, 50 nm, and 55 nm are explored in the following study. Titanium dioxide is an oxide semiconductor and has the advantages of stable chemical properties and a high refractive index. Moreover, the molecular structure of titanium dioxide nanomaterials is dispersed and there is a large volume gap. These characteristics of TiO2 film make it more sensitive to refractive index changes than gold film. The prism structure with pure titanium dioxide film is shown in Figure 1c and SPR spectra are shown in Figure 4. It can be seen that the FWHM of the SPR curve of a pure TiO2 film SPR sensor is generally wide, up to 254.16 nm and 311.73 nm. In addition, there is no clear and definite SPR resonance wavelength. Therefore, TiO2 film alone is not a good choice. In order to obtain the excitation effect of gold film and the enhancement effect of titanium dioxide at the same time, a prism-TiO2-Au SPR sensor was designed. The structure is shown in Figure 1d. In order to obtain the best combination of TiO2 layer and gold nanolayer, the simulation results in the sensing performance of different combinations of TiO2 layer thickness in the range of 140-190 nm (increasing 10 nm each time) and gold Titanium dioxide is an oxide semiconductor and has the advantages of stable chemical properties and a high refractive index. Moreover, the molecular structure of titanium dioxide nanomaterials is dispersed and there is a large volume gap. These characteristics of TiO 2 film make it more sensitive to refractive index changes than gold film. The prism structure with pure titanium dioxide film is shown in Figure 1c and SPR spectra are shown in Figure 4. It can be seen that the FWHM of the SPR curve of a pure TiO 2 film SPR sensor is generally wide, up to 254.16 nm and 311.73 nm. In addition, there is no clear and definite SPR resonance wavelength. Therefore, TiO 2 film alone is not a good choice. In addition to the shift in resonance wavelength, the minimum reflectance should also be noted. With the increase in the gold film thickness, the minimum reflectance decreases first and then increases. The minimum reflectance at 0 °C and 60 °C is plotted in Figure 3. When the thickness of the gold film is between 35 nm and 60 nm, the minimum reflectance is higher than 20%. In general, sensors with a minimum reflectance greater than 20% are not considered, because the sensing effect is not good enough. In the subsequent research on sensor performance improvement, sensors with a minimum reflectance of above 20% will no longer be considered. SPR sensors based on gold film thicknesses of 40 nm, 45 nm, 50 nm, and 55 nm are explored in the following study. Titanium dioxide is an oxide semiconductor and has the advantages of stable chemical properties and a high refractive index. Moreover, the molecular structure of titanium dioxide nanomaterials is dispersed and there is a large volume gap. These characteristics of TiO2 film make it more sensitive to refractive index changes than gold film. The prism structure with pure titanium dioxide film is shown in Figure 1c and SPR spectra are shown in Figure 4. It can be seen that the FWHM of the SPR curve of a pure TiO2 film SPR sensor is generally wide, up to 254.16 nm and 311.73 nm. In addition, there is no clear and definite SPR resonance wavelength. Therefore, TiO2 film alone is not a good choice. In order to obtain the excitation effect of gold film and the enhancement effect of titanium dioxide at the same time, a prism-TiO2-Au SPR sensor was designed. The structure is shown in Figure 1d. In order to obtain the best combination of TiO2 layer and gold nanolayer, the simulation results in the sensing performance of different combinations of TiO2 layer thickness in the range of 140-190 nm (increasing 10 nm each time) and gold In order to obtain the excitation effect of gold film and the enhancement effect of titanium dioxide at the same time, a prism-TiO 2 -Au SPR sensor was designed. The structure is shown in Figure 1d. In order to obtain the best combination of TiO 2 layer and gold nanolayer, the simulation results in the sensing performance of different combinations of TiO 2 layer thickness in the range of 140-190 nm (increasing 10 nm each time) and gold nanolayer thickness in the range of 40-55 nm (increasing 5 nm each time) are shown in Figure 5. As can be seen from Figure 5, in longitudinal comparison with the same gold film thickness, the sensitivity of the sensor first increases and then decreases with the increase in TiO 2 layer thickness. This proves that the addition of titanium dioxide can indeed make the SPR wavelength move a longer distance and improve the performance, but if the TiO 2 layer is too thick, the sensor's response to the RI change begins to decline. Table 1 shows the detailed data of the six most sensitive material structure combinations.
nanolayer thickness in the range of 40-55 nm (increasing 5 nm each time) are shown in Figure 5. As can be seen from Figure 5, in longitudinal comparison with the same gold film thickness, the sensitivity of the sensor first increases and then decreases with the increase in TiO2 layer thickness. This proves that the addition of titanium dioxide can indeed make the SPR wavelength move a longer distance and improve the performance, but if the TiO2 layer is too thick, the sensor's response to the RI change begins to decline. Table  1 shows the detailed data of the six most sensitive material structure combinations.  The maximum sensitivity occurs when the SPR sensor is combined with 160 nm TiO2 and 40 nm Au, but due to the wide FWHM, the FOM is not so good. Based on the sensitivity and FOM, the SPR sensor combined with 160 nm TiO2 and 45 nm Au was finally selected as the sensor with the best effect. The SPR reflectance curve is shown in Figure  6a. In the temperature range of 0-60 °C, the SPR wavelength initially decreases as temperature increases. The SPR wavelength at 0 °C is 814.80 nm and is 691.00 nm at 60 °C, resulting in a resonance wavelength shift of 123.80 nm, with a sensitivity of 5184.25 nm/RIU. The minimum reflectance of the resonance wavelength is 0.032. Figure 6b shows the relationship between the temperature and SPR resonance wavelength, and the fitting is performed. Temperature and wavelength are linearly dependent, and the correlation coefficient R 2 is 0.9754. The response of the sensor to temperature is −1.98 nm/°C.  The maximum sensitivity occurs when the SPR sensor is combined with 160 nm TiO 2 and 40 nm Au, but due to the wide FWHM, the FOM is not so good. Based on the sensitivity and FOM, the SPR sensor combined with 160 nm TiO 2 and 45 nm Au was finally selected as the sensor with the best effect. The SPR reflectance curve is shown in Figure 6a. In the temperature range of 0-60 • C, the SPR wavelength initially decreases as temperature increases. The SPR wavelength at 0 • C is 814.80 nm and is 691.00 nm at 60 • C, resulting in a resonance wavelength shift of 123.80 nm, with a sensitivity of 5184.25 nm/RIU. The minimum reflectance of the resonance wavelength is 0.032. Figure 6b shows the relationship between the temperature and SPR resonance wavelength, and the fitting is performed. Temperature and wavelength are linearly dependent, and the correlation coefficient R 2 is 0.9754. The response of the sensor to temperature is −1.98 nm/ • C. To further improve the sensitivity, FOM, and linear correlation of resonance wavelength and temperature, titanium dioxide nanorods were added to form the TiO2(film)-Au-TiO2(nanorods) triple structure SPR sensor (Figure 7). In this structure, three factors need to be considered, namely the height, radius, and the distance between the nanorods. The influence of the above three factors on the sensing effect is presented in Tables 2-4.   To further improve the sensitivity, FOM, and linear correlation of resonance wavelength and temperature, titanium dioxide nanorods were added to form the TiO 2 (film)-Au-TiO 2 (nanorods) triple structure SPR sensor (Figure 7). In this structure, three factors need to be considered, namely the height, radius, and the distance between the nanorods. The influence of the above three factors on the sensing effect is presented in Tables 2-4. To further improve the sensitivity, FOM, and linear correlation of resonance wave length and temperature, titanium dioxide nanorods were added to form the TiO2(film) Au-TiO2(nanorods) triple structure SPR sensor (Figure 7). In this structure, three factor need to be considered, namely the height, radius, and the distance between the nanorods The influence of the above three factors on the sensing effect is presented in Tables 2-4.     To further study the performance of the sensor, the structure of TiO 2 nanorods was changed, including height, radius, and spacing. The original geometric size of TiO 2 nanorods is 50 nm in height, 15 nm in radius, and 20 nm in spacing. The control variable method was used in subsequent studies. In order to explore the influence of the height of TiO 2 nanorods on the sensing performance (Table 2), the height was changed while keeping other parameters unchanged. It can be seen that the sensitivity of the sensor is improved while the height increases from 30 to 60 nm. When the height of the TiO 2 nanorods is 60 nm, the sensitivity is the highest. However, the FWHM and FOM are poor at this time. When measuring the performance of a sensor, the sensitivity and the FOM should be considered comprehensively. As can be seen from the detailed data in Table 2, the FOM of the sensor is the largest and has a high sensitivity when the height is 50 nm.
Furthermore, the effect of the radius of the TiO 2 nanorods and the spacing between the nanorods on the sensitivity of the sensor were investigated. The sensitivity of the sensor increases first and then slightly decreases as the radius increases from 5 to 20 nm. The value of FOM also increases first and then decreases, as shown in Table 3. When the radius of TiO 2 nanorods is 15 nm, the sensitivity and FOM are both maximized.
In this study, the spacing range between TiO 2 nanorods was 10-30 nm. With the increase in the spacing between nanorods, the sensor sensitivity shows a downward trend and the value of FOM first rises and then falls. Based on the data in Table 4, it can be concluded that the sensor with a 20 nm distance has the largest FOM and higher sensitivity and is the best choice.
In terms of geometric size, the optimized TiO 2 nanorods in the sensor have a height of 50 nm, a radius of 15 nm, and a spacing distance of 20 nm. The sensitivity of the SPR sensor is 6038.53 nm/RIU. The reflectance curve is shown in Figure 8a. The SPR dip shifts towards shorter wavelengths with the increase in temperature. As shown in Figure 8b, the relationship between SPR resonance wavelength and temperature shows a good linear relationship with a correlation coefficient of 0.9990.
x FOR PEER REVIEW To compare the sensing performance of the pure Au SPR sensor, the TiO2-Au SPR sensor, the TiO2(film)-Au-TiO2(nanorods) triple SPR sensor, the SPR wavelengths, and their corresponding temperatures are presented in Figure 9. The sensitivity of the TiO2(film)-Au-TiO2(nanorods) triple SPR sensor is 16.48% higher than that of the TiO2-Au SPR sensor and 77.81% higher than that of the pure Au SPR sensor. This can be seen by comparing the slopes of the three fitted lines. In addition to the significant increase in sensitivity, the correlation coefficient of the TiO2(film)-Au-TiO2(nanorods) triple SPR sensor fitting line is also significantly higher than the other two fitting lines. In summary, the proposed TiO2(film)-Au-TiO2(nanorods) triple SPR sensor has high sensitivity and excellent FOM, with a good linear correlation between resonance wavelength and temperature. Figure 9. SPR wavelengths corresponding to temperature of three proposed SPR temperature sensors and linear fitting curves. To compare the sensing performance of the pure Au SPR sensor, the TiO 2 -Au SPR sensor, the TiO 2 (film)-Au-TiO 2 (nanorods) triple SPR sensor, the SPR wavelengths, and their corresponding temperatures are presented in Figure 9. The sensitivity of the TiO 2 (film)-Au-TiO 2 (nanorods) triple SPR sensor is 16.48% higher than that of the TiO 2 -Au SPR sensor and 77.81% higher than that of the pure Au SPR sensor. This can be seen by comparing the slopes of the three fitted lines. In addition to the significant increase in sensitivity, the correlation coefficient of the TiO 2 (film)-Au-TiO 2 (nanorods) triple SPR sensor fitting line is also significantly higher than the other two fitting lines. In summary, the proposed TiO 2 (film)-Au-TiO 2 (nanorods) triple SPR sensor has high sensitivity and excellent FOM, with a good linear correlation between resonance wavelength and temperature. To compare the sensing performance of the pure Au SPR sensor, the TiO2-Au SPR sensor, the TiO2(film)-Au-TiO2(nanorods) triple SPR sensor, the SPR wavelengths, and their corresponding temperatures are presented in Figure 9. The sensitivity of the TiO2(film)-Au-TiO2(nanorods) triple SPR sensor is 16.48% higher than that of the TiO2-Au SPR sensor and 77.81% higher than that of the pure Au SPR sensor. This can be seen by comparing the slopes of the three fitted lines. In addition to the significant increase in sensitivity, the correlation coefficient of the TiO2(film)-Au-TiO2(nanorods) triple SPR sensor fitting line is also significantly higher than the other two fitting lines. In summary, the proposed TiO2(film)-Au-TiO2(nanorods) triple SPR sensor has high sensitivity and excellent FOM, with a good linear correlation between resonance wavelength and temperature. To confirm the temperature sensing performance, the optimized TiO2(film)-Au-TiO2(nanorods) triple SPR sensor was simulated to determine whether it can respond clearly to temperature changes. Within the range of 10-30 °C, an SPR reflectance curve was calculated and drawn for every 1 °C, as shown in Figure 10a. The resonance wavelength at each temperature is plotted in Figure 10b and then fitted. The fitting results show To confirm the temperature sensing performance, the optimized TiO 2 (film)-Au-TiO 2 (nanorods) triple SPR sensor was simulated to determine whether it can respond clearly to temperature changes. Within the range of 10-30 • C, an SPR reflectance curve was calculated and drawn for every 1 • C, as shown in Figure 10a. The resonance wavelength at each temperature is plotted in Figure 10b and then fitted. The fitting results show that the resonance wavelength is linearly correlated with the temperature and the correlation coefficient is 0.9957. TiO 2 (film)-Au-TiO 2 (nanorods) triple SPR sensor can clearly distinguish the temperature change of 1 • C in the 10-30 • C range and the correlation is good. Therefore, when the resonance wavelength is known, the temperature can be determined according to the fitted curve.
FOR PEER REVIEW 10 of 13 that the resonance wavelength is linearly correlated with the temperature and the correlation coefficient is 0.9957. TiO2(film)-Au-TiO2(nanorods) triple SPR sensor can clearly distinguish the temperature change of 1 °C in the 10-30 °C range and the correlation is good. Therefore, when the resonance wavelength is known, the temperature can be determined according to the fitted curve.  Figure 11 shows the electric field |E| of the optimized TiO2(film)-Au-TiO2(nanorods) triple structure SPR temperature sensor at different interfaces of resonance wavelength when the temperature is 60 °C. When the reflectance is at its minimum, the intensity of the electric field approaches its maximum. In Figure 11, we can see the maximum electric field is obtained at the interface between the TiO2 nanorods and the sensing medium. The intensity field decays exponentially in the sensing medium. The electric field distribution indicates that the reduced reflectance is caused by the SPR phenomenon. In the preparation experiment, TiO2 films can be manufactured via a sol-gel process [36,37], Au film can be manufactured via magnetron sputtering, and TiO2 nanorods can be manufactured via a hydrothermal method [49]. The optimized TiO2(film)-Au-TiO2(na- Figure 10. (a) The reflectance curve of optimized TiO 2 (film)-Au-TiO 2 (nanorods) triple SPR sensor in the 10-30 • C range and (b) SPR wavelength corresponding to temperature for every 1 • C in the 10-30 • C range and linear fitting. Figure 11 shows the electric field |E| of the optimized TiO 2 (film)-Au-TiO 2 (nanorods) triple structure SPR temperature sensor at different interfaces of resonance wavelength when the temperature is 60 • C. When the reflectance is at its minimum, the intensity of the electric field approaches its maximum. In Figure 11, we can see the maximum electric field is obtained at the interface between the TiO 2 nanorods and the sensing medium. The intensity field decays exponentially in the sensing medium. The electric field distribution indicates that the reduced reflectance is caused by the SPR phenomenon. that the resonance wavelength is linearly correlated with the temperature and the correlation coefficient is 0.9957. TiO2(film)-Au-TiO2(nanorods) triple SPR sensor can clearly distinguish the temperature change of 1 °C in the 10-30 °C range and the correlation is good. Therefore, when the resonance wavelength is known, the temperature can be determined according to the fitted curve.  Figure 11 shows the electric field |E| of the optimized TiO2(film)-Au-TiO2(nanorods) triple structure SPR temperature sensor at different interfaces of resonance wavelength when the temperature is 60 °C. When the reflectance is at its minimum, the intensity of the electric field approaches its maximum. In Figure 11, we can see the maximum electric field is obtained at the interface between the TiO2 nanorods and the sensing medium. The intensity field decays exponentially in the sensing medium. The electric field distribution indicates that the reduced reflectance is caused by the SPR phenomenon. In the preparation experiment, TiO2 films can be manufactured via a sol-gel process [36,37], Au film can be manufactured via magnetron sputtering, and TiO2 nanorods can be manufactured via a hydrothermal method [49]. The optimized TiO2(film)-Au-TiO2(nanorods) triple structure SPR temperature sensor prepared through the above methods can obtain the theoretically expected sensing effect and can be put into application. In the preparation experiment, TiO 2 films can be manufactured via a sol-gel process [36,37], Au film can be manufactured via magnetron sputtering, and TiO 2 nanorods can be manufactured via a hydrothermal method [49]. The optimized TiO 2 (film)-Au-TiO 2 (nanorods) triple structure SPR temperature sensor prepared through the above methods can obtain the theoretically expected sensing effect and can be put into application.

Conclusions
Temperature changes often cause variations in the RI of alcohol, thus leading to the shift of the SPR spectrum. However, the research on temperature sensors based on SPR film sensors has not attracted much attention. In this work, an SPR sensor with a TiO 2 (film)-Au-TiO 2 (nanorods) triple structure was proposed through a comparative study with a traditional pure Au film SPR sensor and a TiO 2 -Au dual film sensor. It was found that the triple combination of TiO 2 and Au could not only excite SPR with Au but also enhance the performance with TiO 2 . The sensitivity of the SPR temperature sensor can achieve 6038.53 nm/RIU with 160 nm TiO 2 film, 45 nm Au film, and 50 nm high TiO 2 nanorods (5 nm in radius, 20 nm in spacing), and the detection temperature sensitivity is −2.40 nm/ • C. The sensitivity of the TiO 2 (film)-Au-TiO 2 (nanorods) triple SPR sensor is 16.48% higher than that of the TiO 2 -Au SPR sensor and 77.81% higher than that of the pure Au SPR sensor. Good sensing characteristics show the application potential of the device in the field of temperature sensing. Owing to the high-temperature sensitivity, quick and clear response, simple structure, convenient operation, and environmental protection, the proposed TiO 2 (film)-Au-TiO 2 (nanorods) triple structure SPR sensor has great advantages in application.