Investigation of Building Materials’ Radioactivity in a Historical Building—A Case Study

The paper investigates a possible hazard originating from natural radionuclides in building materials in a selected historical building being reconstructed for housing. Both outdoor and indoor risks were evaluated through the radiological indices and estimated doses, based on measured activities of natural radionuclides in stone and brick materials of the building. The average measured activity concentrations of radionuclides were 7.32 Bq/kg for 226Ra, 40.05 Bq/kg for 232Th, and 546.64 Bq/kg for 40K radionuclides. The average total activity concentration in building materials (594.0 Bq/kg) exceeded the world average value. A correlation was found between the potassium content in the building material samples and the total activity of radionuclides. The gamma indices, Iγ, calculated for the samples, ranged in an interval of 0.26–0.60, not exceeding the restricted limit for bulk materials Iγ = 1. The average annual effective dose due to building materials was 0.53 mSv/y, which does not exceed the limit (1 mSv/y), however, it contributes to a gamma dose excess that is higher than recommended (0.3 mSv/y at the most). The bricks were responsible for a higher level of natural radiation than natural stone material. Nevertheless, based on the radiation protection requirements, it can be concluded that the building can be used for residential purposes after the reconstruction, as no significant human health impact is expected due to the radioactivity of building materials.


Introduction
The radiation to which the human population is exposed comes from many diverse sources. Some of these sources are natural; others are the result of human activities. The radiation from natural sources includes cosmic radiation, external radiation from radionuclides in Earth's crust, and internal radiation from radionuclides inhaled or ingested and retained in the body [1,2]. The magnitude of these natural exposures depends on geographical location and on some human activities [1,2]. Height above sea level affects the dose rate from cosmic radiation; radiation from the ground depends on the local geology [3]. A significant part of the total dose contribution in the form of natural sources comes from terrestrial gamma radionuclides [2]. Nuclides with half-lives comparable with the age of the Earth or their corresponding decay products, existing in terrestrial materials, such as 40 K, 226 Ra, and 232 Th radionuclides, are of great interest [1,2]. The human population worldwide receives an average annual radiation dose of 2.4 mSv/y, about 80% of which comes from naturally occurring radionuclides, while the remaining part is largely due to artificial sources of which fallout radionuclides account for only 0.4% [2].
Since most people spend about 80% of their time indoors, controlling the natural ionizing radiation in buildings is of great importance. One of the main sources of the indoor radiation is represented by building materials as building materials contain natural radionuclides [4]. Natural radioactivity of building materials originating from natural sources (soil, rock) is connected mainly with the radium ( 226 Ra), thorium ( 232 Th), and potassium ( 40 K) radionuclides [5]. The built-in materials can cause both external and internal exposures indoors. The external exposure is caused by gamma radiation resulting from the decay of the radionuclides present in material; the internal exposure is caused by inhalation of the decay products of radionuclides present in materials, e.g., radon gas [6]. The level of radon concentrations, which can originate not only from building materials, but also from water and subsoil, is a non-negligible factor when evaluating indoor spaces. It is the subsoil that is often the most significant source of the presence of radon in the indoor environment [7,8]. Knowledge of hazards is required to take protective precautions to decrease the exposure of the population to ionizing radiation [9].
The main effects of ionizing radiation on living organisms are cell death, loss of reproductive capacity, or mutation. However, such effects depend on several factors, with the dose rate and the linear energy transfer (LET) of the radiation being the most important. The dose rate is the delivery of dose per unit time and the absorbed dose is typically measured in Grays, Gy, where 1 Gy = 1 J/kg [10]. The higher the dose rate, the greater the cell damage. Exposure to gamma radiation in the indoor environment would result in low doses of radiation. Recent advances in the knowledge of the mechanisms underlying the biological effects of low doses have shown that low radiation dose effects are mechanistically different to high radiation dose effects, with low radiation dose effects being similar to those of some chemicals in the environment. Thus, results under mixed exposures to radiation and chemicals may not be predictable for human health, by the consideration of single agent effects. It has been observed that the risk of increase in cancer incidence caused by low-dose radiation is low, but recent epidemiological studies have indicated elevated risks of non-cancer diseases (e.g., perturbation of immune function or induction of inflammatory reactions with disease) at low doses below 1-2 Gy, and in some cases much lower, although the mechanisms are still unclear and the estimation of risks remains problematic [11].
Natural radioactivity in building materials is measured as the activity concentration of the 40 K, 226 Ra, and 232 Th radionuclides [12]. Since the distribution of 226 Ra, 232 Th, and 40 K in building materials is not uniform, the real radioactivity levels in building materials can be assessed in the form of a single quantity by using several radiological indices [13]. The activity concentration index (gamma index) Iγ, including activity concentrations of all three radionuclides, was proposed by the European Commission and it is most often used to assess the dose level of external gamma radiation from building materials [14]. The activity concentration index shall not exceed the defined values (e.g., for bulk materials Iγ = 1) to ensure that the annual dose criterion of 1 mSv is met [14]. However, based on the radiation protection principles in the EU, controls are recommended for building materials contributing to overall dose by the value of 0.3-1 mSv/y [14] which corresponds to Iγ = 0.5-1 for bulk materials. Besides the activity concentration index, several others have been developed over the years to evaluate the radiation exposure due to building material, e.g., alpha index [10], indoor and outdoor hazard indices [15], different dose parameters [16][17][18]. Several studies have been presented concerning the natural radioactivity of building materials [19][20][21][22][23][24], based on which it can be concluded that conventional building materials do not pose a radiological hazard due to gamma radiation and rarely exceed the EU annual dose criterion for radiation protection. The worldwide average activity concentrations in building materials are 35 Bq/kg for 226 Ra, 30 Bq/kg for 232 Th, and 400 Bq/kg for 40 K which correspond to a dose of 0.25 mSv/y [14]. However, a significantly higher level has been detected in some countries, such as Iran [25], Cameroon [26], or Chad [27].
On the other hand, the sustainability and circular economy principles require waste recycling or their re-use which leads to more significant incorporation of various industrial wastes into building materials. This is mainly connected with concrete and cement compos-ites, thus representing more sustainable materials [28][29][30][31]. Waste often has a higher level of radioactivity than natural materials and therefore there is a need to monitor not only conventional but also these new sustainable materials in order to guarantee their safety when applied to the indoor environment [32].
Currently, several studies are devoted to the natural radioactivity of building materials as well as to the monitoring of the occurrence of radon in the interior, but there is rarely information on radiation exposure in historical buildings or the study of the radioactivity of historical materials. At present, in terms of cultural heritage, great emphasis is placed on the protection and restoration of historical site buildings that can be found not only in the historical centers of regional, district towns and surrounding villages but also in remote places [33,34]. The fact is that in the past, one was forced to build dwellings of the materials that were available and they were not always investigated for the potential radiological risk [35].
In this research, natural radioactivity of building materials from a selected UNESCO historical building in Slovakia was studied in order to assess the radiological impact of the historical building materials. Determination of the activity levels of the radionuclides and consequent evaluation of the building materials were performed in a historical building which was reconstructed for the purpose of its further use for housing. Radiation measurements of building materials aimed to determine the dose of radiation exposure from materials, and to evaluate the possible health risks posed by radiation.

Materials and Methods
The research of radioactivity of building materials in this study was carried out in the historic building in Master Paul's Square of the UNESCO city Levoča, Slovakia. More detailed characteristics of the historical building are given in Section 2.1. Part of this building was undergoing reconstruction for residential purposes and building materials, represented by brick and stone samples, were collected during the reconstruction period as described in Section 2.2. After preparing the material samples (Section 2.3), chemical analysis was performed to determine the basic chemical composition of the brick and stone samples as well as to estimate the potassium radionuclide content based on the total potassium concentrations. The activity concentrations of radionuclides ( 226 Ra, 232 Th, and 40 K) were measured in powdered samples of stone and brick materials using gamma spectrometry (Section 2.5). Measured values of the activity concentrations of radionuclides were used for the estimation of the external gamma exposure due to building materials by calculation and evaluation of various radiological indices and doses as described in more detail in Section 2.5. The general diagram of the research procedure is given in Figure 1.

Historical Building under Study
The historical burgher house selected for the investigation, with the inventory number 43 and also known as the Mariássy Palace or the patrician house, has a rich history. The building is one of the largest and historically most important burgher houses in Master Paul's Square, Levoča, which falls under the strictest level of monument protection in Slovakia. The house is segmented into six main parts according to the diagram in Figure 2 [36,37]. The oldest building structures were realized in the 14th century. Since that period, the building has passed through a number of renovations and reconstructions. The results of detailed historical research that document the development phases of the building are illustrated in Figure 3.

Sampling
Three sampling points of building materials for the radioactivity analysis were chosen in the middle part of section 43-B1/a as seen in Figures 2 and 5. Although this was not the oldest part of the building, there were several reasons for choosing this part of the building in terms of authenticity [36,37], e.g., minimal or no changes in room layout during use for approx. 400 years, original or minimally modified building structures with historical materials: masonry, mortars, plasters, this part of the building was not affected by the fires, and the 43-B1/a part of the building includes a basement, so it was possible to take material from all three floors. The stone (S) and brick samples (B) were collected from each sampling point during spring. Indoor air temperature in the rooms was in the interval 19.3-20.6 • C, relative air humidity 57%. All spaces had only natural ventilation and the windows were closed during sampling. Therefore, ventilation was carried out only by infiltration through the old historical wooden double windows.

Basement
The basement in the courtyard at elevation 569.52 m a.s.l. has an entrance through a stone rectangular portal from the courtyard. The space, accessible by stairs, has a floor made of steamed clay and is vaulted with a barrel vault with lunettes; on the south wall there is a ventilation opening to the facade of the square. Samples of building stone (SB) and solid fired brick (BB) were taken from the northeastern wall, the construction of which dates back to around 1600 [36,37]. The sampling points were located about 1000 mm above the floor level.

First Floor
Yard wing 43-B1/a at elevation 573.15 m a.s.l. extends over an area of 84 m 2 . It consists of four rooms being accessible from the courtyard. Room No. 1.11 which was chosen for the sampling is vaulted with a barrel vault with lunette sections [36,37]. Samples of building stone (S1st) and solid fired bricks (B1st) were taken from the northeast wall of the room approximately 1000 mm above the floor level.

Second Floor
The courtyard wing 43-B1/a on the second floor at elevation 576.81 m a.s.l. was built in the early Baroque style [36,37]. It consists of four original rooms. Samples of building stone (S2nd) and solid fired bricks (B2nd) were taken from the northeast wall of room 2.15 approximately 1000 mm above floor level. Before removing the material, a modern lime-cement layer of plasters with painting was removed.

Sample Preparation for the Analysis
The samples were reduced to smaller sizes by a jaw crusher (BRIO BCD 3) and then ground using a planetary rotary mill (SFM-1) to a prescribed particle size of 0.5 mm. Consequently, the powders of material samples were homogenized and dried at 105 • C in a laboratory oven to a constant weight. Subsequently, the bulk samples were homogeneously dispersed into Marinelli type containers (450 mL volume), weighed, and, after closure, subjected to Rn equilibrium for more than 150 days.

Chemical Analysis
The chemical composition of bricks was determined by X-ray fluorescence analysis (XRF) using SPECTRO iQ II (Ametek, Weiterstadt, Germany). Samples were measured in powder form (4 g) for 10 min.

Measurement of Radionuclides' Activity Concentration
The activity concentrations of radionuclides ( 226 Ra, 232 Th, and 40 K) in studied materials were measured using gamma ray spectrometry. Measurements were carried out using an EMS-1A SH (Empos, Prague, Czech Republic) detection system equipped with a NaI/Tl scintillation detection probe and an MC4K multichannel analyzer with optimized resolution of 818 V, 4.096 channels, and with 9 cm of lead shielding and internal lining of 2 mm tinned copper.
The specific activity concentrations of 226 Ra, 232 Th, and 40 K were determined in Bq/kg using the count spectra. The 40 K radionuclide was measured directly through its gamma ray energy peak at 1461 keV, while activities of 226 Ra and 232 Th were calculated based on the mean value of their respective decay products. Activity of 226 Ra was measured using the 351.9 keV gamma rays from 214 Pb and the activity of 232 Th was measured using the 238.6 keV gamma rays of 212 Pb. The same counting time of 86.400 s (24 h) was used for all measured samples. The characteristics of the measured radiation quantities of particular radionuclides are given in Table 1. To assess the collective impact of activity concentrations of the radionuclides in a single quantity, the radiological indices and dose parameters selected are given in Table 2. The gamma activity concentration Iγ has been defined by the European Commission according to Formula (1) [38][39][40]. Alpha index Iα (2) [41] was used to estimate exposure due to the radon gas emanation from building materials. Activity utilization index AUI was calculated using Formula (3) [42].
where the values 0.00809, 0.4798, and 0.4392 represent fractional percentages of the total dose from 226 Ra, 232 Th, and 40 K (f Ra = 8.09%, f Th = 47.98%, and f K = 43.92%) The hazard indices were represented by external H ex and internal H in hazard risk indices, which are necessary to assess the potential risk resulting from the construction materials used. In principle, the external hazard index H ex is used to estimate the radiological risk caused by exposure to the external natural radioactive gamma source. The equation is based on the assumption that the activity of 370 Bq/kg of 226 Ra, 259 Bq/kg of 232 Th, and 4810 Bq/kg of 40 K produce the same gamma ray dose rate. H ex maximum allowable level is expressed based on the corresponding maximum acceptable Ra eq limit (370 Bq/kg). Ra eq is expressed by (6) [43][44][45]. Since radon and its short-lived decay products are also hazardous to the respiratory organs, the internal hazard index H in has been introduced. Both indices were calculated using the expressions (4) and (5) Outdoor external dose D out was calculated using Formula (7) [49,50]. The European Commission, in 1999 [43], introduced the indoor external dose D in described by Formula (8). The quantitative coefficients used in D out and D in calculations are expressed in nGy/h per 1 Bq/kg. The annual effective dose equivalent is used to estimate the health risk associated with exposure of an individual. The annual effective doses are defined for outdoor, E out (9), and indoor, E in (10), exposures [2,51,52]. To estimate the E in and E out , the conversion factor (0.7) from absorbed dose rate in air in Sv/Gy to effective dose rate in mSv/yr is used. The occupancy factor represents the proportion of time spent in the indoor and outdoor environments and differs for the outdoor dose E out (occupancy factor of 0.2) and indoor dose E in (occupancy factor of 0.8). The excess lifetime cancer risk (ELCR) indicator estimates the potential of cancer development over a lifetime, caused by irradiation from building materials. ELCR was calculated based upon values of E out and E in using Formulas (11) and (12), where LE is life expectancy (70 years) [2,53] and RF is fatal risk factor per Sievert, which is 0.05 according to [54]. The annual dose equivalent of gonads AGDE due to the specific activities of 226 Ra, 232 Th, and 40 K was estimated using Formula (13) [51,55]. The annual effective dose equivalent represents the degree of genetic significance of the annual dose that the reproductive organs of a population receive. Organs with rapidly dividing cells, such as gonads, active bone marrow cells, lungs, testes, ovaries, and bone surface cells, are considered interesting by the UN Scientific Committee on the Effects of Atomic Radiation. The effective dose rate D organs delivered to a particular organ can be calculated using the relation in (14) [56], where f is the conversion factor of organ dose from air dose. The conversion factor for lungs, ovaries, bone marrow, testes, and the whole body are 0.64, 0.58, 0.69, 0.82, 0.68, respectively [39].

Chemical Composition of Samples
The chemical analysis of the collected materials, measured by an X-ray fluorescence analyzer (XRF) (Ametek, Germany), are given in Table 3. The chemical composition of brick samples in Table 3 corresponds to the usual contents of the main elements in brick clay [57]. According to the chemical composition of the stone samples, the stones could probably belong to granite type [58]. However, the chemical composition of the stone samples in the basement differs slightly from those collected from the 1st and 2nd floor. To compare the similarity of the samples, the expression of the concentration ratio of CaO to SiO 2 is commonly used. While for brick samples the CaO/SiO 2 concentration ratio varies in a relatively narrow interval of 15-20, in the case of stone samples the differences are significantly larger. The CaO/SiO 2 ratio of stone samples from the basement reached the value of 26.8, which is several times higher than the CaO/SiO 2 ratio of stone samples from the 1st and 2nd floor (4.9 and 2.6, respectively). This finding points to non-identical stone materials analyzed.
Granite, widely used as a cladding on city buildings and also architecturally in homes, contains an average of 3 ppm (40 Bq/kg) uranium and 17 ppm (70 Bq/kg) thorium [59]. Based on the contents of natural potassium, uranium, and thorium, the activity of radioactive isotopes should be estimated in particular samples. As seen in Table 1, higher activity concentrations of 40 K can be expected in brick samples since the total potassium content in bricks was higher than in stone samples. Content of 1% of natural potassium in rock minerals corresponds to 313 Bq/kg of 40 K radionuclide as reported in [60]. It is assumed that 40 K concentrations could range from 376 to 761 Bq/kg for the individual samples analyzed. Radium and thorium radioisotope concentrations are difficult to estimate as the measured XRF concentrations are below the detection limit.

Activity Concentrations of Radionuclides
The measured activity concentration of 226 Ra, 232 Th, and 40 K radionuclides in the stone and brick samples varied from 6.78 ± 2.1 to 8.98 ± 1.8, 22.96 ± 7.3 to 61.62 ± 7.6, 341.04± 10.2 to 781.19 ± 10.9 Bq/kg, respectively, as shown in Table 4. Profiles of the activity concentration of various radionuclides in building material samples and world averages are shown in Figure 5. The total activity concentrations varied from 372.97 to 850.01 Bq/kg. The activity concentration of 226 Ra for bricks and stones and activity concentrations of 232 Th and 40 K for stone samples were lower than the world average concentrations of these radionuclides in building materials that are 25, 25, and 370 Bq/kg, respectively, as per [61]. The values of stone samples radioactivity were lower than in Gupta, 2011 [62], likewise for brick activity concentrations compared to Turhan, 2008 [63] and Raghu, 2016 [64]. The average of total activity concentration (594.01 Bq/kg) expressed as sum of 226 Ra and 232 Th and 40 K concentrations is higher than the world average of total activity concentration of these radionuclides in building material samples (420 Bq/kg). The total activity concentrations of 226 Ra, 232 Th, and 40 K of building material samples are shown in Figure 6.  As assumed, the measured concentrations of 40 K were almost twice as high in brick samples than in stone samples.
A correlation was found between the chemical composition, specifically the potassium content in the building material samples and the total activity of radionuclides (Figure 7a) with the correlation coefficient R = 0.85, as well as the dependence between the gamma index and the potassium content ( Figure 7b) with a correlation coefficient of R = 0.88. The correlation was even more significant for the brick materials themselves. The measured activity concentrations of samples were also analyzed in terms of the samples' location from the basement to the second floor. No fundamental difference was detected in the radioactivity of the materials taken from the individual floors. The radioactivity of the materials of the stone samples slightly decreased with increasing floor as can be seen in Figure 8a. This was not observed for the brick samples. The differences between the particular values of total activities per samples collected from the basement, 1 st , and 2nd floor ranged from 0.6 to 12% (Figure 8b).

Estimation of External Gamma Exposure Due to Building Materials
Potential radiological risk of the bricks and stones from a historical building in Levoča was estimated on the basis of calculated radiological indicators and doses given in the following Figures 9-12.  The calculated gamma indices, Iγ, observed for the samples, ranged in an interval of 0.26-0.60, not exceeding the restricted limit for bulk materials Iγ = 1. However, when considering the recommended unrestricted value Iγ = 0.5 which corresponds to the annual dose of 0.3 mSv/year, 33% of samples did not meet this dose criterion (Figure 9). According to activity concentration index (ACI) approach, the materials having the Iγ in the interval 0.5-1 can be classified for restricted use, e.g., in bridges or roads or only for low-occupancy buildings. The highest value was found for the B1st sample (Iγ = 0.590). The gamma indices for bricks were higher compared to Amiri et al., 2014 [65], who reported six times lower Iγ found for bricks, and two times higher than in Lima, 2015 [53].
Alpha index Iα was in the range 0.03 to 0.05 ( Figure 9). Iα should be lower than permissible value (Iα = 1) which relates to 200 Bq/kg. Materials with 226 Ra concentration lower than 200 Bq/kg cannot cause indoor radon activity higher than 200 Bq/kg, therefore, it can be assumed that building materials in this study will not pose a risk to exceeding the limit value of Rn emanation from building materials. The Iα values were similar compared to [66] but lower compared to [67]. Values of Iα were lower for stones and higher for brick samples compared to Lyngkhoi, 2020 [67]. Activity utilization indices AUI ranged from 0.53 to 1.29, and were less than the recommended value (I ≤ 2). The AUI values in this study were comparable with those in the study by Ademila, 2020 [68].
Both H in and H ex risk indicators of all samples studied were lower than 1. These results correspond to the studies by Fares, 2019 [69] and Tuo, 2020 [70] for bricks and Ajayi, 2013 [71] for stones. The total gamma output from the combination of 226 Ra, 232 Th, and 40 K radionuclide activities represented through the radium equivalent activity indicator (Ra eq ) was under the limit value (370 Bq/kg), ranging from 68.067 to 155.459 Bq/kg ( Figure 10).
The calculated dose parameters resulting from the activity concentrations of measured radionuclides are presented and compared to the world average values in Figure 11. Outdoor external dose D out ranged from 31.887 to 72.621 nGy/h. The values linked to brick samples were found to be higher than the world average value of 59 nGy/h. The values of calculated indoor external dose D in ranged from 61.138 to 137.675 nGy/h with an average 95.06 nGy/h, which is 1.13 times more than the world average of 84 nGy/h as per [2].
The value of the annual indoor effective dose E in ranged from 0.30 to 0.68 mSv/y, and in the case of the brick samples, exceeded the world average of 0.41 mSv/y ( Figure 11). The annual outdoor effective dose E out for the building material samples was identified in the interval 0.04 to 0.09 mSv/y, and, similarly to E in , was higher than the world average of 0.07 mSv/y for the brick samples. These findings correspond to the results reported by [72]. The total annual effective dose E total (0.53 mSv/y) was similar to the world average value (0.52 mSv/y) and does not exceed the criterion limit of 1 mSv/y as per ICRP-60 [54]. However, the total annual effective dose E total for brick samples was significantly higher than that of the stone samples.
The ELCR total for outdoor and indoor exposure reached values from 1.05 to 2.36 with an average of 1.85, which is 27% higher than the world average (1.45). However, the results in this study are lower compared to [73], who reported the value of 3.21. The calculated annual gonadal equivalent dose AGDE connected to the samples ranged in an interval of 230.97-525.09 µSv/y. The world average of AGDE for houses was reported to be about 370 mSv/yr whereas the standard UNSCEAR value for AGDE is 300 mSv/yr. Darwish [66] presents the value of 520 µSv/y in stone houses. The highest value was found for the B1st sample. The AGDE values for bricks exceeded the world average value reported in an OECD report [26]. AGDE results for the samples were double those for stone and four times higher for bricks than reported in [67]. The application of waste materials as replacement for cement in the production of concrete could represent another risk of increasing the activity of radionuclides and subsequently their negative effects on the human body [74].  Figure 12 shows the estimation of the absorbed dose by individual organs. The highest sensitivity has been proved in the case of testes and the lowest for ovaries. These results are a little bit lower compared to [75]. However, it should be noted here that some experts do not recommend using low values of radionuclides' activity for cancer risk estimation. At the same time, the authors of the present study would like to point out that the results refer only to the study of external exposure due to built-in materials and not to the assessment of the radon levels.

Conclusions
The paper presents a radioactivity study on building materials (stone and bricks) of a historical building in the city of Levoča, Slovakia. The research was aimed at examining the possible risks originating from specific activities of radionuclides in building materials in the building after reconstruction. Building materials of three floors-basement, 1st floor, and 2nd floor-show some variation in activity concentration of three radionuclides ( 226 Ra, 232 Th, and 40 K) from site to site. The average measured activity concentrations of radionuclides were 7.32 Bq/kg for 226 Ra, 40.05 Bq/kg for 232 Th, and 546.64 Bq/kg for 40 K radionuclides. The average total activity concentration in building materials of 594.1 Bq/kg exceeded the world average value (420 Bq/kg).
The potential outdoor and indoor risks were evaluated through the various radiological indices and estimated doses based on the measured activity concentrations of 226 Ra, 232 Th, and 40 K radionuclides in the samples. The calculated gamma indices, Iγ, ranged from 0.26 to 0.60, not exceeding the EU limit for bulk materials Iγ = 1. Radiation values slightly higher than world average were noticed in the case of the outdoor external dose and outdoor annual effective dose and indoor annual effective dose which were identified to be 13 and 14% higher, respectively, than the average world values. Total annual effective dose of 0.53 mSv/y was almost identical to the average world value (0.52 mSv/y). Exceeding of the average world values was also observed for the total ELCR (by 27%) and for the annual gonadal dose equivalent (by 21%).
The results obtained in this study confirmed that bricks are responsible for a higher level of natural radiation than the used natural stone material. The radiological parameters related to bricks were more than double compared to building stone.
The observed strong correlation between the potassium content in the building materials, measured by XRF, and total activity concentration of radionuclides (R = 0.85) confirm the possibility to estimate the radioactivity of brick and stone materials based on chemical analysis. The results of this case study underline that, based on the chemical analysis and determination of the total potassium content, it is possible not only to estimate the activity concentrations of 40 K but also the total activity of radionuclides. During the reconstruction of buildings, external gamma radiation should be controlled in relation to the building materials used. The chemical analysis of materials, which can be performed in a shorter time frame than the determination of activity concentrations of radionuclides, which takes more than 40 days, could serve as input screening information on the need for detection of activity of radionuclides.
Although some radiological parameters were higher than the world average, no exceeding of the established limits for gamma index and annual dose was recorded. Thus, the analyzed materials cannot pose any significant risk in a long-term horizon and therefore the building could be recommended for residential purposes after the reconstruction. Since only external exposure to gamma radiation was evaluated in this study, further radon monitoring should be performed to confirm the safety of the indoor spaces considered for residential purposes.