Ternary Blends for Self-Compacting Mortars Production Composed by Electric Arc Furnace Dust and Other Industrial by-Products

This study is framed within the circular economy model through the valorisation of industrial by-products. This research shows the results of producing self-compacting mortars (SCMs) with electric arc furnace dust (EAFD) and other industrial by-products such as fly ash, conforming (FA) or not conforming (NcFA), from coal-fired power plants, or recovery filler (RF) from hot-mix asphalt plants. Three batches of SCMs, each with one industrial-by product (FA, NcFA, or RF), and three levels of EAFD ratio incorporation (0%, 10%, 20%), were tested. An extra batch with a greater amount of FA was manufactured. When the incorporation ratio of EAFD rose, the mechanical strength decreased, due to the presence of a calcium zinc hydroxide dihydrate phase; nevertheless, this decrease diminished over time. All SCM mixes, except the 40C 40FA 20 EAFD mix, were above 20 MPa at 28 days. All mixes named 70C and 40C reached 40 and 30 MPa, respectively, at 90 days. Mixes with EAFD showed less capillarity and no difference in water absorption by immersion with respect to mixes without EAFD after 91 days. The SCMs designed proved to be stable in terms of leaching of the heavy metals contained in EAFD, where all the hardened SCMs were classified as inert.


Introduction
The enormous amount of waste generated worldwide challenges global sustainability. Turning waste into a new raw material is one key way to achieve integrated ecological productivity in all economic sectors. This should avoid the negative impacts of waste disposal at the local level, such as landscape deterioration, and water and air pollution. These are two crucial and current demanding tasks for mankind. The construction sector could have a key role in incorporating waste in cement-based materials, such as concrete or mortar [1].
This industry is constantly evolving and searching for more efficient technologies that allow optimizing natural resources. Self-compacting concrete (SCC) has been one of the most important advances in construction materials, and its use has become widespread in also found a loss of mechanical properties in SCC with RF relative to the reference one. However, Shahidan et al. [31] found that compressive strength in SCC with RF presented greater values than SCC with natural aggregates.
On the other hand, the management of hazardous waste is one of the most complex current challenges, since incorrect management can have irreversible environmental impacts. World steel production in 2017 amounted to nearly 1.7 billion tonnes of crude steel, including carbon, stainless, and other alloys. The amount produced in electric furnaces (arc and induction) was above a quarter of the total. These figures represented the greatest numbers in the last decade [32]. One of the by-products generated in this industry is electric arc furnace dust (EAFD), which is generated as a result of the vaporization of molten iron with nonferrous metals, CO bursting bubbles, and the ejection and dragging of particles from the metal bath, slag, and other materials in the oven [33]. Its production ranges between 10 and 30 kg per tonne of steel for scrap smelting and direct reduced iron [34]. It is composed of heavy metals with leaching potential, which leads to negative impacts, such as Pb, Zn, Cd, Cr, and Ni [35]; because of this, it has been classified as hazardous waste in the European Waste Catalogue [36]. Therefore, its management implies a very high cost for steel mills since it cannot be deposited in landfills without prior treatment. The Spanish steelmaking industry generates an amount of 115,000 tonnes of EAFD per year [37]. Its particle size distribution matches the requirements for its use as filler. Different researchers have studied the influence of EAFD on mortars in terms of mechanical properties and leaching behaviour in the solid state [38][39][40][41]. In these studies, the heavy metals Zn, Se, Cd, Mo, and Pb, and the chloride anion were identified as the elements of EAFD that exceeded the limits to not be classified as hazardous waste. Additionally, it is said that the formation of the phase CaZn 2 (OH) 6 ·2H 2 O in mortars with EAFD was found, and it inhibited hardening during the early stages of curing [40]. Based on this issue, Massarwe et al. [42] confirmed their hypothesis of the addition of EAFD as a set retarder in concrete, and Magalhães et al. [43] successfully studied the possibility of applying a pre-treatment with a NaOH solution to enhance strength gain. Santamaría et al. [44] studied the use of another type of by-product in steelmaking, called electrical arc furnace slag, which presents a particle size distribution similar to a regular fine aggregate, in SCM. In this study, the gain of compressive strength over time was postponed when this by-product was used. Other authors have studied the solidification/stabilization of EAFD with different matrix compositions. Salihoglu & Pinarli [45] studied the use of paste samples based on cement, lime, or both for EAFD S/S. Samples with 35% of cement and lime and 30% of EAFD presented optimum composition for minimizing leaching test results. Fernández-Pereira et al. [46] studied the EAFD S/S with geopolymers based on low calcium fly ash. Fares et al. [47] compared the usage of EAFD and different conventional binders, such as silica fume and FA, with Portland cement in mortars. One of the features of SCMs that make it adequate for the encapsulation of potential harmful components is the higher density of the cement matrix than in regular mortars [40]. This, along with the need for filler material in SCMs, makes EAFD and the other industrial by-products excellent candidates for this purpose.
This study analyses the influence of incorporating different industrial by-products with a powdery size, such as EAFD, RF, FA, and NCFA, as fillers on the performance of self-compacting mortars (SCMs). To the extent of the authors' knowledge, none of the existing studies focused on the simultaneous use of FA, NcFA, or RF and EAFD as fillers in SCMs. This study addresses the topic regarding the use of ternary blends combining the use of EAFD and other industrial by-products, along with cement, to produce sustainable SCMs; this appears to be highly suitable due to its appropriateness as a filler and capability of limiting the release of potential pollutant elements. For this purpose, this investigation presents the characterization of the materials used, the performance of sustainable SCMs, and the leaching behaviour in the monolithic state. Therefore, this study contributes to the circular economy, since it avoids landfilling through its incorporation in SCMs and, consequently, reduces the consumption of raw materials.

Materials
For SCM production, two fractions of aggregates of siliceous nature were used: fine sand 0/1 (NS 0-1) and coarse sand 0/4 (NS 0-4). Figure 1 shows the particle sieve distribution of both sands. NS 0-1 and NS 0-4 presented water absorption after 24 h of 0.7% and 1.1% and specific gravity of 2.58 and 2.55, respectively. The cement used was CEM I-42.5 R (CEM) and it complied with NP EN 197-1. It had a specific gravity of 3.14. The high-performance/strong water reducer superplasticiser used, SikaPlast 898 (SP), is based on a combination of modified polycarboxylates in an aqueous solution that works by electrostatic and steric repulsion. tion of both sands. NS 0-1 and NS 0-4 presented water absorption after 24 h of 0.7% and 1.1% and specific gravity of 2.58 and 2.55, respectively. The cement used was CEM I-42.5 R (CEM) and it complied with NP EN 197-1. It had a specific gravity of 3.14. The highperformance/strong water reducer superplasticiser used, SikaPlast 898 (SP), is based on a combination of modified polycarboxylates in an aqueous solution that works by electrostatic and steric repulsion.
The different by-products used as fillers were conforming fly ash (FA), non-conforming fly ash (NcFA), recovery filler (RF), and electric arc furnace dust (EAFD). The FA was supplied by SECIL Company (Lisbon, Portugal) and complied with the NP EN 450-1 and NP EN 450-2 standards; on the contrary, the other FA used did not comply with the fineness standard UNE-EN 933-10: 2010, therefore named NcFA. It was obtained from the Puente Nuevo coal-fired power station (Córdoba, Spain) of Viesgo electric company. The origin of the RF was from waste powder from asphalt mixture sands supplied by PAMASA (Málaga, Spain). The hazardous waste, EAFD, came from a steelwork located in Zumárraga (Guipúzcoa, Spain) that uses an electric arc furnace (EAF) for steel production.

Test Methods for Materials Characterization
The chemical composition of CEM and EAFD was found by X-ray fluorescence (XRF) using 4 kW of power and S4PIONEER, BRUKER equipment, whereas for FA, NcFA, and RF it was done by analysis of the dispersive energy of X-rays (EDAX).
The mineralogical composition of the raw materials was determined by X-ray diffraction (XRD) using a Bruker D8 Discover A 25 with Cu Kα radiation (λ = 1.54050 A; tube voltage: 40 kV; Tube current 30 mA). For EAFD, goniometric scanning was used from 10° to 70° (2θ°) at a speed of 0.00625°/min, whereas for the rest of the materials, the speed was 0.05°/min. The identification of the main minerals was done by comparison with the JCPDS Powder Diffraction File database [48]. The different by-products used as fillers were conforming fly ash (FA), non-conforming fly ash (NcFA), recovery filler (RF), and electric arc furnace dust (EAFD). The FA was supplied by SECIL Company (Lisbon, Portugal) and complied with the NP EN 450-1 and NP EN 450-2 standards; on the contrary, the other FA used did not comply with the fineness standard UNE-EN 933-10: 2010, therefore named NcFA. It was obtained from the Puente Nuevo coal-fired power station (Córdoba, Spain) of Viesgo electric company. The origin of the RF was from waste powder from asphalt mixture sands supplied by PAMASA (Málaga, Spain). The hazardous waste, EAFD, came from a steelwork located in Zumárraga (Guipúzcoa, Spain) that uses an electric arc furnace (EAF) for steel production.

Test Methods for Materials Characterization
The chemical composition of CEM and EAFD was found by X-ray fluorescence (XRF) using 4 kW of power and S4PIONEER, BRUKER equipment, whereas for FA, NcFA, and RF it was done by analysis of the dispersive energy of X-rays (EDAX).
The mineralogical composition of the raw materials was determined by X-ray diffraction (XRD) using a Bruker D8 Discover A 25 with Cu Kα radiation (λ = 1.54050 A; tube voltage: 40 kV; Tube current 30 mA). For EAFD, goniometric scanning was used from 10 • to 70 • (2θ • ) at a speed of 0.00625 • /min, whereas for the rest of the materials, the speed was 0.05 • /min. The identification of the main minerals was done by comparison with the JCPDS Powder Diffraction File database [48].
The specific surface area of the CEM, FA, NcFA, RF, and EAFD samples was analysed by the Brunauer-Emmett-Teller method (BET), using Micromeritics ASAP 2010 equipment, Norcross, GA, USA. The single-point pore volume was determined from the amount adsorbed at a relative pressure of ∼0.99. The real particle density was estimated according to UNE 80103:2013. The particle size distribution of CEM, FA, NcFA, RF, and EAFD was measured using a Mastersizer S 2000 device (Malvern Instruments, Malvern, UK) with a previous ultrasonic homogenization for sample particle dispersions. Furthermore, the adsorption-desorption isotherms of nitrogen were determined to study the pore size distribution in CEM, FA, NcFA, RF, and EAFD by means of the DFT (density function theory).
Thermogravimetric and differential thermal analysis (TGA-DTA) was performed in a Setaram Setsys Evolution 16/18 apparatus under nitrogen at a heating rate of 5 • C/min in FA, NcFA, RF, and EAFD samples.
The standard UNE-EN 12457-4:2003 [49] is a basic characterization procedure which was conducted on 0.090 kg of each filler (FA, RF, NcFA, and EAFD), by means of a singlestep batch leaching test, in which the solution was shaken for 24 ± 0.5 h at an L/S ratio of 10 L/kg. After the contact phase, the samples were left to decant, then filtered and a subsample of 40 mL of eluate was collected for testing and analysed within 24 h, for several elements and/or anions using ICP-MS and ionic chromatography, respectively.

Mortar Mix Proportions
The composition of the mortar mixes (Table 1) was designed following the Nepomuceno method [5], separating powders (CEM, FA, RF, NcFA, and EAFD) and fine aggregates (NS-0/1 and NS-0/4). The self-compacting parameters used based on the absolute volume proportions were: powder materials and fine aggregates (V p /V s ), which were kept constant at 0.70 for all the mixes; and water and powder materials (V w /V p ), with a value of 0.83 and 0.78 for mixes with 70% and 40% of cement with respect to powder materials, respectively. The mass of the superplasticizer and mass of the powder materials ratio (Sp/%p) were adjusted for each mix. This increased as the EAFD ratio incorporation rose since the EAFD had finer particle size distribution and greater specific surface area than the powders replaced (RF, FA, and NcFA).
The self-compacting parameter regarding the fresh state of SCM was determined through the Gm. It is obtained by means of the slump-flow test; a truncated cone with a height of 60 mm and diameters of 70 and 100 mm at the top and bottom, respectively. It was filled up and then it was immediately lifted to let the fresh mortar spread out on a plate with a smooth and dampened surface. The average of the two perpendicular diameters of the spread mortar was used in the formula for Gm, provided by Nepomuceno et al. [5], to obtain the Gm parameter (Equation (1)). This value decreased when the EAFD content increased, even with the addition of superplasticiser. Above the amount used in mixes with EAFD incorporation (Table 1), the phenomena of segregation and water exudation were found. Although the Gm values in some mixes were lower than what is recommended [5], none of the aforementioned phenomena occurred.
where Dm is the mean of the diameters of the spread mortar, in mm, and D 0 stands for the initial diameter at the base of the cone, in mm. The designation of the mortars depends on the composition by volume of the powders as shown in Table 1.
To produce the SCM specimens, a standard mortar mixer was used. The constituents in solid state were homogenised 30 s after 80% of the water was poured in the mixer. Two minutes later, the remaining 20% of the water was added with the superplasticiser previously diluted. Then, the mixer was stopped for 1 min to ensure that all the constituents were mixed and to clean the mixer-blades. Finally, the mix went on for another 1 min and prismatic specimens, 40 × 40 × 160 mm 3 , were cast without agitation or mechanical compaction. Before 24 h, 48 h, and 72 h for mix specimens with no EAFD, with 10% EAFD, and with 20% EAFD, respectively, were demoulded, and afterwards stored in a climatic chamber at 50 ± 5% relative humidity and 20 ± 2 • C. This increasing time between manufacturing and demoulding as EAFD percentage rose was due to the retardation of hardening of cement matrixes in the presence of EAFD, as aforementioned in the introduction section.

Test Methods for SCM
The mineralogical composition of the SCM was determined using the equipment used for raw materials with 0.05 • /min of speed. For this purpose, samples were collected after testing compressive strength, and then immersed in ethylic alcohol and stored at least 72 h to inhibit any setting reaction and to dry by solvent replacement [6]. The XRD patterns of the crystalline mineral phases in SCM were compared with the JCPDS powder diffraction file database [50].
The mechanical properties of the SCM in hardened state were studied at 28 and 91 days of curing. The flexural strength was obtained using a standard three-point-bending test with a 100 mm span, and compressive strength was measured on perpendicular edges of each of the two residual pieces obtained from the flexural test, following the standard UNE-EN 1015-11:2000 [50]. The rate of loading for flexural and compressive strength were 0.04 kN/s and 0.4 kN/s, and their value corresponds to the average of the three tests.
The following physical properties related to the durability were studied: water absorption by immersion and capillarity, and dry bulk density; these tests were carried out after 91 days of curing in three specimens each. Water absorption by immersion was obtained by measuring the water absorbed after immersion until mass became constant, and its apparent volume was determined by subtracting the saturated mass and weighing the sample under water. To study the water absorption by capillary, the capillarity coefficient was obtained in accordance with UNE-EN 1015-18:2003 [51]. Dry bulk density was yielded in the relationship between the dry mass of the specimen and its apparent volume, following the standard UNE-EN 1015-10:2000 [52].
With the aim of analysing the capability of encapsulating heavy metals, with potential hazardous impacts to the environment, in SCM due to the presence of EAFD, the test conducted was the tank-leaching test according to XP X31-211:2012 [53]. It determines the leachability of a solid waste material, in this case generated in a solidification process. Prismatic sample halves were introduced in a PET container with a liquid to solid ratio of 10 with de-ionized water being agitated for 24 h. After that, the pH and electrical conductivity were measured and the amount of elements and anions was determined using ICP-MS and ionic chromatography, respectively. Tables 2 and 3 show the chemical composition of FA, NcFA, and RF by EDAX, and CEM and EAFD by XRF, respectively. Figure 2 shows the X-ray diffractograms of CEM, FA, NcFA, RF, and EAFD. The CEM sample presented a high content of larnite (Ca 2 SiO 4 , JCPDS no. 09-0351), hatrurite (Ca 3 SiO 5 , JCPDS no. 86-0402), gypsum (CaSO 4 ·2H 2 O, JCPDS no. 33-0311) and to a lesser extent, components such as gismondinea ((Ca, Na 2 )Al 2 Si 2 O 8 ·4H 2 O, JCPDS no. 21-0840) and calcite (CaCO 3 , JCPDS no. 80-0742) ( Figure 2). The XRF analysis agreed with the mineralogical phase found in the diffractograms.  The XRD patterns of the NcFA and FA fillers ( Figure 2) showed quartz (SiO 2 , JCPDS no. 33-1161) as the main phase; hematite (Fe 2 O 3 , JCPDS no. 33-0664) and mullite (Al 6 Si 2 O 13 , JCPDS no. 15-0776) were also found, the latter being in high quantity. The FA used presented almost identical chemical composition to the one used in da Silva et al.'s [6] research. The chemical composition determined by EDAX analysis of NcFA and FA (Table 2) implied that both samples exhibited a small amount of unburned coal particles and FA presented a greater quantity of Mg and Ca in carbonate forms. FA showed similar composition to the ones studied by Fernandez-Periera et al. [46]. According to the diffractogram, a greater presence of amorphous phase in NcFA than in FA was estimated, since a more dented hump was located between 15 • and 35 • [54,55]. Although the percentage of amorphous was not determined, the XRD pattern of RF filler showed a dolomitic nature (CaMg (CO 3 ) 2 , JCPDS no. 36-0426) as the only phase presented. The XRD patterns of EAFD showed that it was mainly composed of franklinite (ZnFe 2 O 4 , JCPDS no. 22-1012) and zincite (ZnO, JCPDS no.36-1451). Silva Magalhães et al. [56] and Dutra et al. [57] also found these main phases in EAFD. To a lesser extent, other minor phases were found as sodium (NaCl, halite, JCPDS no. 05-0628) and potassium (KCl, sylvite, JCPDS no. 73-0380) chloride [58]. These results are in agreement with the chemical composition determined by EDAX (Table 3). Table 4 shows the particle density (standard UNE-80103: 2013), the specific surface area by Brunauer-Emmett-Teller (BET), and single-point pore volume (Vp) of CEM, FA, NcFA, RF, and EAFD. The high particle density value in EAFD is due to the higher density of the phases presented, franklinite and zincite, with a greater density of 5 g/cm 3 . The RF presented a surface much greater than the rest of materials, between 10 times the EAFD and 40 times the NcFA in terms of BET surface, and between 25 times the EAFD and 90 times the NcFA in terms of Vp.  Table 4 shows the particle density (standard UNE-80103: 2013), the specific surface area by Brunauer-Emmett-Teller (BET), and single-point pore volume (Vp) of CEM, FA, NcFA, RF, and EAFD. The high particle density value in EAFD is due to the higher density of the phases presented, franklinite and zincite, with a greater density of 5 g/cm 3 . The RF presented a surface much greater than the rest of materials, between 10 times the EAFD and 40 times the NcFA in terms of BET surface, and between 25 times the EAFD and 90 times the NcFA in terms of Vp.   Figure 3 shows the particle size distribution of CEM, FA, NcFA, RF, and EAFD in percentage. CEM, FA, and RF presented a similar distribution curve and maximum peak: for CEM 27 µm, for FA 39 µm, and for RF 32 µm. NcFA showed a trimodal distribution with a majority presence of coarser particles, with a maximum peak of 48 µm. The percentage of medium-sized particles, from 1 to 10 µm, is much lower than that of the rest of the samples, although the amount of particles smaller than 1 µm is similar, except for CEM where it is slightly greater than the rest. The EAFD sample presented a bimodal curve, medium-sized and small particle fraction, with very pronounced peaks at 2.6 µm and 0.3 µm respectively. Thus, it is a material with very fine particles.  Figure 3 shows the particle size distribution of CEM, FA, NcFA, RF, and EAFD in percentage. CEM, FA, and RF presented a similar distribution curve and maximum peak: for CEM 27 μm, for FA 39 μm, and for RF 32 μm. NcFA showed a trimodal distribution with a majority presence of coarser particles, with a maximum peak of 48 μm. The percentage of medium-sized particles, from 1 to 10 μm, is much lower than that of the rest of the samples, although the amount of particles smaller than 1 μm is similar, except for CEM where it is slightly greater than the rest. The EAFD sample presented a bimodal curve, medium-sized and small particle fraction, with very pronounced peaks at 2.6 µm and 0.3 µm respectively. Thus, it is a material with very fine particles.  Figure 4 shows the pore size distribution (nm) versus its volume and the cumulative curve, both in cm 3 /g. The size of the pores is classified by the International Union of Pure and Applied Chemistry (IUPAC) as follows: pores with sizes above 50 nm are named macropores, those ranging between 2 and 50 nm are mesopores, and those under 2 nm are micropores. Similar distributions were obtained in CEM, FA, and NcFA, with a higher concentration of pores in the range of small mesopores (2-10 nm). The maximum pore volume peak is around 3 nm in these samples. FA exhibited a small amount of micropores (between 1.7 and 2 nm), which did not happen with NcFA.  Figure 4 shows the pore size distribution (nm) versus its volume and the cumulative curve, both in cm 3 /g. The size of the pores is classified by the International Union of Pure and Applied Chemistry (IUPAC) as follows: pores with sizes above 50 nm are named macropores, those ranging between 2 and 50 nm are mesopores, and those under 2 nm are micropores. Similar distributions were obtained in CEM, FA, and NcFA, with a higher concentration of pores in the range of small mesopores (2-10 nm). The maximum pore volume peak is around 3 nm in these samples. FA exhibited a small amount of micropores (between 1.7 and 2 nm), which did not happen with NcFA.

Materials Characterization
EAFD had a more uniform distribution throughout the range of pore sizes, although a large part of these pores were concentrated in the range of small mesopores. Micropores were also observed between 1.7 and 2 nm and its maximum peak in pore volume was around 3 nm in diameter.
The RF sample had no micropores and a few small mesopores. The largest number of pores was found between medium-large mesopores (20-50 nm) and macropores. The EAFD's highest volume peak was near 31 nm, with a large dispersion of the curve. The RF presented the highest porosity, in agreement with the data in Table 2. Figure 5 shows the thermogravimetric analysis (TGA) and differential thermal analysis (DTA) of FA, NcFA, RF, and EAFD. A loss of mass of around 3.2% occurs between 440 and 700 • C in FA, mainly due to the decomposition of calcium and magnesium carbonates and the formation of CO 2 thanks to the combustion of unburned ones. This process shows in the thermal curve as an exothermic peak at around 600 • C. Fernández Pereira et al. [46] obtained a loss of mass of 3.32% at 750 • C in a FA sample. For NcFA, the loss was 1.5%, mainly due to the unburned carbonates. This is reflected in the peak of the DTA of NcFA, which is more defined than that of FA. The RF mass loss is around 48% (600-800 • C), and is due to the decomposition of the dolomite carbonate. The complexity of the EAFD makes it difficult to interpret its diagram. The changes in mass produced up to 650 • C are due to losses of hydration products and oxidative processes. After 650 • C, the loss of mass is due to sintering and melting of the chlorides present as sylvite and halite ( Figure 2). EAFD had a more uniform distribution throughout the range of pore sizes, although a large part of these pores were concentrated in the range of small mesopores. Micropores     Table 5 shows the 12 heavy metal elements and the three anions determined by the waste acceptance criteria, EU LD 2003/33/EC [59], at landfills. This so-called European Landfill Directive classifies waste as hazardous, non-hazardous, and inert materials, according to the release levels. EAFD was classified as hazardous; the fluoride anion, Cu, Cr, Zn, Cd, and Hg heavy metals exceeded the limit for inert materials; Se, Mo, and the sul-phate anion did so for non-hazardous limits; and Pb and the chloride anion for hazardous waste. The high release level of Pb in EAFD excludes its disposal at landfills without any treatment [60]. FA and NcFA were classified as non-hazardous materials due to the Cr, Mo, and sulphate anion content exceeding the corresponding limits. FA and NcFA release levels are in accordance with those exposed by Tsiridis et al. [61], who studied six different fly ash from Europe and in all of them Cr, Mo, and the sulphate anion exceeded the inert limit. RF was classified as inert, as expected. The fillers used (FA, RF, and NcFA) are not treated as potentially harmful to the environment, since its use as a new raw material construction is widely extended, unlike EAFD.

Mechanical Strength
The compressive strength test results are presented in Figure 10. Firstly, regarding the mixes without EAFD, taking the 70C 30FA mix as the reference one, 70C 30NcFA showed a gain of 21.2% at 28 days of curing, whereas this gain was 10.7% at 91 days, and mixes with RF presented no loss or gain at the corresponding age. This result may be justified by the following reasons: the presence of coarser particles in NcFA (maximum distribution peak at 48 µm) than in FA and RF (maximum distribution peak at 39 µm and 32 µm respectively) ( Figure 3), which led to a better skeleton filler with cement; the ratio mass of filler to mass of cement is lower in the 70C 30NcFA mix; or/and the admixture content has been lower in the 70C 30NcFA mix. The chemical composition and mineralogical phases presented in mortars with FA and NcFA fillers were alike, except the fact that NcFA presented a greater amount of amorphous phase, which could be another factor for justifying the higher compressive strength found. The 70C 30RF mix presented a loss of compressive strength of 4.2% relative to the reference mix (70C 30FA) at 28 days and 9.8% at 91 days, due to the non-pozzolanic nature of RF. The compressive strength values of 70C 30RF and 70C 30FA at 28 days were similar to the corresponding ones of Nguyen [8] and Türkel & Altuntas [65], respectively. 40C 60FA showed a decrease of 39.4% relative to the reference mix (70C 30FA) at 28 days, and 46.5% at 91 days due to the lower amount of cement used.
Secondly, the incorporation of EAFD in SCM resulted in a significant decrease in compressive strength, as expected. The compressive strength values at 28 days presented for all the mixes were above 20 MPa, except for the 40C 40FA 20EA mix (15.8 [38] research, the mechanical strength decrease as EAFD incorporation rose was justified by, among other reasons, the high amount of Zn that prevented the regular hydration of cement. This is in accordance with the finding of CaZn 2 (OH) 6 ·2H 2 O instead of the portlandite phase in the mineralogical study of the SCM (Figures 6-9). The gain of compressive strength over time in mixes with 20% of EAFD incorporation was greater than in mixes with no EAFD; these gains were 29.3%, 21.8%, 18.1%, and 14.0% for 70C 30FA, 70C 30RF, 70C 30NcFA, and 40C 60FA mixes; and 63.7%, 162.5%, 54.8%, and 90.0%, respectively. This has been reported by other authors [63,67] and has been attributed to the delay in the hydration of cement.
Despite the fact that the flexural strength ( Figure 11) results presented similar trends to the compressive strength ones, when comparing mixes with no EAFD incorporation with the reference mix (70C 30FA) at 28 days, mixes with RF and NcFA presented a gain of 12.7% and 17.3%, respectively, and the 40C 60FA mix showed a drop of 25%. In the rest of the mixes, a lower reduction was found between the values with EAFD incorporation and those corresponding to the mixes without EAFD (with the same filler), at 44.5 ± 6.5%. At 91 days of curing, mixes with no EAFD presented similar values to those at 28 days, whereas mixes with EAFD presented a great gain of flexural strength. Conversely, Lozano-Lunar et al. [40] found that the flexural strength results in mixes without EAFD did not differ from mixes with a similar amount and nature of EAFD to this study. It has been reported [68] that an increase in compressive and flexural strength results from EAFD incorporation up to 15% in conventional concrete, relative to mixes without any addition. A linear regression between the flexural, x axis, and the compressive, y axis, strength values was carried out (intercept or constant value equals 0), and a strong correlation was found (R 2 = 0.97). The compressive strength of all mixes resulted in 5.52 times the flexural strength; this is in agreement with da Silva et al. [43], who found an almost identical relationship for the same percentage of EAFD incorporation in mortars with cement and EAFD as binders.

Mechanical Strength
The compressive strength test results are presented in Figure 10. Firstly, regarding the mixes without EAFD, taking the 70C 30FA mix as the reference one, 70C 30NcFA showed a gain of 21.2% at 28 days of curing, whereas this gain was 10.7% at 91 days, and Secondly, the incorporation of EAFD in SCM resulted in a significant decrease in compressive strength, as expected. The compressive strength values at 28 days presented for all the mixes were above 20 MPa, except for the 40C 40FA 20EA mix (15.8 [38] research, the mechanical strength decrease as EAFD incorporation rose was justified by, among other reasons, the high amount of Zn that prevented the regular hydration of cement. This is in accordance with the finding of CaZn2(OH)6·2H2O instead of the portlandite phase in the mineralogical study of the SCM (Figures 6-9). The gain of compressive strength over time in mixes with 20% of EAFD incorporation was greater than in mixes with no EAFD; these gains were 29.3%, 21.8%, 18.1%, and 14.0% for 70C 30FA, 70C 30RF, 70C 30NcFA, and 40C 60FA mixes; and 63.7%, 162.5%, 54.8%, and 90.0%, respectively. This has been reported by other authors [63,67] and has been attributed to the delay in the hydration of cement.
Despite the fact that the flexural strength ( Figure 11) results presented similar trends to the compressive strength ones, when comparing mixes with no EAFD incorporation  Table 6 shows the physical properties studied related to durability at 91 days of curing and the dry bulk density of the SCM produced. With regards to density, there were no relevant differences when comparing mixes with the same amount of cement and EAFD but different filler. As expected, the dry bulk density increased as the EAFD incorporation ratio rose, due to the greater particle density of EAFD, as seen in Table 4. Similarly, mixes with 40% of cement presented lower density relative to the corresponding ones with the same EAFD incorporation ratio and 70% of cement, since FA had a lower particle density than cement. The results of the water absorption by immersion at 91 days did not show significant differences among the mixes with 70% of cement, whereas mixes named 40C had slightly greater values. Regarding the capillarity coefficient, mixes with 70% of cement with EAFD and no EAFD were clearly presented into two groups, because of the strong influence of EAFD. The mixes with EAFD presented lower capillarity than the ones without EAFD. These results could be justified by the findings of Lozano-Lunar et al. [41], who found lower large capillaries in a mix with a similar amount of EAFD relative to the reference one. It has been also reported [69] that the incorporation of steel by-products with powder size can worsen, or at least not improve, the porous structure in the cementitious matrix, due to the capacity of these finer particles to fulfil voids.

Physical Properties Related to Durability
EAFD incorporation up to 15% in conventional concrete, relative to mixes without any addition. A linear regression between the flexural, x axis, and the compressive, y axis, strength values was carried out (intercept or constant value equals 0), and a strong correlation was found (R 2 = 0.97). The compressive strength of all mixes resulted in 5.52 times the flexural strength; this is in agreement with da Silva et al. [43], who found an almost identical relationship for the same percentage of EAFD incorporation in mortars with cement and EAFD as binders. Figure 11. Flexural strength at 28 and 91 days. Table 6 shows the physical properties studied related to durability at 91 days of curing and the dry bulk density of the SCM produced. With regards to density, there were no relevant differences when comparing mixes with the same amount of cement and EAFD but different filler. As expected, the dry bulk density increased as the EAFD incorporation ratio rose, due to the greater particle density of EAFD, as seen in Table 4.   Table 7 shows the results of carrying out the leaching tank test XP X31-211:2012 in SCM samples. The levels of Zn, Cd, and Hg were below the detection limit and fluoride contents were under 0.2 mg/L for all the samples; hence, not included in Table 5. Fernández-Olmo et al. [70] found that the release of Zn in EAFD solidified in mortars was at a minimum when the pH was above 8, which agrees with the results. According to the release of pollutant elements listed by the European Landfill Directive [59] and the legal limits imposed by this regulation, despite the EAFD incorporation, all the SCM samples were classified as inert regarding the Directive. In Lozano-Lunar et al.'s [40] study, mixes with a similar ratio binder/EAFD were also classified as inert, even though the EAFD incorporation in the SCM mortar increased the release levels of Cr, Cu, Se, Mo, Ba, and Pb elements, and the conductivity and pH as well. Despite the low value presented, Pb (which was the most critical heavy metal) release decreased in the 40C 50FA 10EA and 40C 40FA 20EA mortars relative to those with a higher amount of cement. Some researchers have found that Pb release in an alkaline medium, such as cement-based materials, could ease its mobility. Ledesma et al. [39] reported an increase in Pb release starting at 11.5 pH, and Salihoglu & Pinarli [45] above 11. This is in line with the low pH values obtained in this research.

Conclusions
The aim of this research was to produce self-compacting mortars (SCMs) with electric arc furnace dust (EAFD) and other industrial by-products, such as fly ash, conforming (FA) or not conforming (NcFA), from coal-fired power plants, or recovery filler (RF) from hot-mix asphalt plants, used as fillers. A wide physical-chemical characterization of these industrial by-products was conducted, as well as the determination of its influence on the mineral phases formed and mechanical properties of the hardened SCM. The leaching stability of the hardened SCM samples was also evaluated. The main conclusions were as follows: 1.
FA and NcFA presented similar composition in the elemental analysis, with a high presence of quartz. RF presented a dolomitic nature. EAFD presented mainly oxides of zinc and/or iron. The maximum percentage of particle size of CEM, FA, and RF ranged between 27 and 39 µm, whereas RF presented the greatest value (48 µm). EAFD distribution particles presented a maximum size near 20 µm and two peaks at 2.6 µm and 0.3 µm. Regarding the pore size distribution, RF presented large mesopores and the others small mesopores and/or micropores.

2.
To produce SCM with similar self-compacting characteristics in the fresh state, EAFD incorporation required much higher superplasticiser contents to keep constant the water to powder volume ratio. This is due to the greater content in particles with a size below 1 µm.

3.
In terms of mechanical properties, the EAFD incorporated implied a decrease as the incorporation increased. The appearance of the phase CaZn 2 (OH) 6 ·2H 2 O in SCM with EAFD at the expense of the portlandite phase caused a reduction of the mechanical strength of SCM. This detrimental effect was reduced over time. Nevertheless, all SCM mixes produced, except for the 40C 40FA 20 EAFD mix, were above 20 MPa at 28 days, which is the minimum established by the Spanish Structural Code for structural concrete with no reinforcement. This structural code allows the use of the compressive strength at 90 days if no load is applied on concrete after placing; all mixes named 70C reached 40 MPa, and the ones named 40C reached 30 MPa at that age, hence, the SCM produced could be suitable for higher requirements than at 28 days if the previous condition is set. 4.
The study on the physical properties at 91 days of curing showed that the incorporation of fillers FA, NcFA, and RF did not significantly affect their performance. Regarding EAFD incorporation, these properties were not negatively affected. In fact, the capillarity was lower for mixes with EAFD incorporation, which could be attributed to its finer particle size.

5.
The leaching test of SCM in the monolithic state did not show a relevant release of any potentially harmful element. All SCMs with EAFD produced were classified as inert, according to criteria established by the European Landfill Directive. The ternary blend mixes with lower amounts of cement (40%) and greater amounts of FA performed even better than with greater amounts of cement. These results imply the feasibility of increasing the amount of filler in SCMs with EAFD, in terms of EAFD harmfulness encapsulation for future research.
The findings of this study show viable solutions of combining different industrial by-products as new secondary raw fillers to produce ternary blends for cement-based materials such as SCMs.