Conservation Environments’ Effect on the Compressive Strength Behaviour of Wood–Concrete Composites

This paper addresses the issues in making wood–concrete composites more resilient to environmental conditions and to improve their compressive strength. Tests were carried out on cubic specimens of 10 × 10 × 10 cm3 composed of ordinary concrete with a 2% redwood- and hardwood-chip dosage. Superficial treatments of cement and lime were applied to the wood chips. All specimens were kept for 28 days in the open air and for 12 months in: the open air, drinking water, seawater, and an oven. Consequently, the compressive strength of ordinary concrete is approximately 37.1 MPa. After 365 days of exposure to the open air, drinking water, seawater, and the oven, a resistance loss of 35.84, 36.06, 42.85, and 52.30% were observed, respectively. In all environments investigated, the untreated wood composite concrete’s resistance decreased significantly, while the cement/lime treatment of the wood enhanced them. However, only 15.5 MPa and 14.6 MPa were attained after the first 28 days in the cases of the redwood and the hardwood treated with lime. These findings indicate that the resistance of wood–concrete composites depends on the type of wood used. Treating wood chips with cement is a potential method for making these materials resistant in conservation situations determined by the cement’s chemical composition. The current study has implications for researchers and practitioners for further understanding the impact of these eco-friendly concretes in the construction industry.


Introduction
The construction sector directly contributes to the expansion of economic activities while, at the same time, it is a major consumer of natural and physical resources. Unfortunately, this expansion has adverse environmental, social, and economic impacts. The environmental impact of construction activities has increased in recent decades due to the rapid increases in the population and greater industrial activity [1,2]. The building industry is responsible for around a quarter of all CO 2 emissions [3], not to mention the loss of non-renewable resources [4]. As a result, the building industry must innovate to ensure customer satisfaction, while also being environmentally sustainable, hence the interest in creating an eco-construction technique [5][6][7]. This unique design technique strives to the material's cement hardened (after 28 days in the open air). If they are to be employed as structural elements, their mechanical properties must be improved. They must also withstand the conditions imposed by the environments in which they will be utilized for as long as possible. Due to the complexities of the effects involved in this investigation, only compressive strength will be evaluated. Finally, this research will fill the gap in the literature regarding the effect of adding wood chips to concrete paste by addressing the following questions: 1.
How does ordinary concrete compressive strength behave in storage environments? 2.
What effects do treated/untreated wood chips have on this behaviour? 3.
Does the type of wood influence this behaviour? 4.
How does the chemical composition of the cement used in wood-chip treatments contribute to the composite's resistance to various storage conditions? Table 1. Treatment methods for wood.

Treatment Methods Advantage Techniques References
Thermal Thermal modifications are the chemical and physical changes that occur in natural fibres because of temperature applications, where different process factors substantially impact fibre qualities.

Hornification
Heat Hydrothermal [44,45] Chemical These treatments eliminate contaminants from the surface of natural fibres, enhancing fibre-matrix adhesion.
Alkali Saline Formaldehyde [25,46] Coating This reduces the impact of soluble compounds while increasing volume stability and surface roughness.
Linseed oil Cement Lime [47] Biological Environmentally friendly fibre modification approaches, low-energy processing, softer reaction conditions, the ability to deploy recycling systems, and enhanced fibre characteristics were accomplished.

Enzymes
Fungi Bacteria [47,48] Figure 1 depicts the itemized, strategic system for the development of the compressive strength investigation of cement materials made from redwood and hardwoods. After being preserved in multiple environments, specimens underwent compressive strength studies. Those specimens were made of ordinary concrete and treated/untreated woodconcrete composites. There were two types of wood used: redwood and hardwood. The treatment of wood chips can take several forms; in this investigation, the wood chips were coated with cement and lime. The duration and the conservation environments were as follows: 28 days in the open air and then 365 days in: (i) open air, (ii) seawater, (iii) drinking water, and (iv) an oven.

Research Methodology
The steps mentioned above were followed to develop the ordinary concrete and the treated/untreated-wood concrete using established concept development and strength analysis.

Materials
The shavings were by-products of woodworking processes. Redwood (W I ) was produced from the wood of a Scots pine tree. According to NF EN 1611 European classification standards, W I is classified as VI Scandinavian. Hardwood (W II ) was steamed beech sawn from Romania. European standard NF EN 975-1 classifies W II as a pedunculated oak species. Both of them have rapid growth and are cost-effective; these species of wood are widely employed in the construction sector. Both are distinguished by rapid development and low-cost aggregates. W II has higher mechanical properties than W I . The steps mentioned above were followed to develop the ordinary concrete and the treated/untreated-wood concrete using established concept development and strength analysis.

Materials
The shavings were by-products of woodworking processes. Redwood (WI) was produced from the wood of a Scots pine tree. According to NF EN 1611 European classification standards, WI is classified as VI Scandinavian. Hardwood (WII) was steamed beech sawn from Romania. European standard NF EN 975-1 classifies WII as a pedunculated oak The density at RH 15% is typically 0.1 for redwood and 0.3 to 0.4 for hardwood. Both, measuring 0.5-12.5 mm, had an irregular form [49]. It should be ensured that the chips are evenly dispersed in the cement matrix throughout the mixing process.
The multiple grain sizes that make up a sample may be determined and seen via granulometric analysis. The granulometric analysis is performed using a LATEST SPA sieve machine set to moderate vibration. The study entailed sorting and categorising the grains based on their diameter using sieves piled one on top of the other, with the diameters of the holes decreasing from top to bottom. In general, the sample analysed in this study was placed on the top sieve, and the categorisation of the grains was acquired by the vibration of the sieve column. The column was stirred mechanically. The sieves were then agitated one by one, starting with the one with the widest opening, and using a bottom and a cover. When the residue did not change by more than 1% after one minute of sifting, the sieving was complete. The refuse was passed through each sieve, and the results were added together. Figure 2 shows the chip granulometric curves of W I and W II . It clearly shows that the wood chips had an irregular form, a higher granulometric limit of approximately 12.5 mm, and a lower granulometric limit of approximately 0.5 mm. Because of the chips' lack of stiffness and geometry, none of these characteristics was of any relative value. sifting, the sieving was complete. The refuse was passed through each sieve, and the results were added together. Figure 2 shows the chip granulometric curves of WI and WII. It clearly shows that the wood chips had an irregular form, a higher granulometric limit of approximately 12.5 mm, and a lower granulometric limit of approximately 0.5 mm. Because of the chips' lack of stiffness and geometry, none of these characteristics was of any relative value. The method appeared to be adequate for supplementing scanning electron microscopy (SEM) of surface features. Therefore, SEM analyses of wood-chip samples were performed using a JEOLJSM100F spectrophotometer. Figures 3 and 4 show SEM microstructural images of WI and WII for various view fields ranging from 10 µm to 500 µm. From Figure 3, we can see that WI chips have a fibrous texture with ordered distribution, while Figure 4 shows the ordered distribution of WII's fibrous texture. Despite this fact, the WI and WII are rather compact materials with fibres that run in the same direction. The method appeared to be adequate for supplementing scanning electron microscopy (SEM) of surface features. Therefore, SEM analyses of wood-chip samples were performed using a JEOLJSM100F spectrophotometer. Figures 3 and 4 show SEM microstructural images of W I and W II for various view fields ranging from 10 µm to 500 µm. From Figure 3, we can see that W I chips have a fibrous texture with ordered distribution, while Figure 4 shows the ordered distribution of W II 's fibrous texture. Despite this fact, the W I and W II are rather compact materials with fibres that run in the same direction.      The geometrical dimensions of the wood chips may also be seen in the SEM pictures. According to SEM examination, the wood chips had a low recovery property.
Portland cement (type II) class 45 (CPJ-CEM II/A) was utilized with the following physical characteristics: a specific surface area of 289 m 2 kg −1 , a specific density of 3078 kg m −3 , and a loss on ignition of 1.16%. Tables 2 and 3 show the mineralogical and chemical compositions of the cement, respectively. The Bogue method was used to determine both of these at the Hadjar Essoud (Skikda, Algeria) cement plant laboratory. Table 2 shows the chemical compositions as determined by the Hadjar Essoud [50] (Skikda, Algeria) cement plant laboratory (SCHS), from which the used Portland cement was obtained. On the other hand, Table 3 shows the mineralogical composition of the cement. It is derived from the data in Table 2 using the Bogue calculation [51]. In fact, the Bogue method was used to approximate the proportions of the four primary minerals in the Portland cement clinker [52]. Despite the fact that the results are only approximate, the computation is incredibly valuable and commonly used in the cement industry. The calculation assumes that the primary clinker minerals are pure minerals with the following compositions: (i) alite or tricalcium silicate (C 3 S); (ii) belite or dicalcium silicate (C 2 S); (iii) tricalcium aluminate (C 3 A); and (iv) tetracalcium aluminoferrite (C 4 AF) [53]. These clinkers may be computed using Equations (1)-(4) [54] where the oxides reflect the weight percentages (PW) [53]:   The concrete mixture contained 3 types of aggregates: rolling sand (2), fine aggregate (1), and coarse aggregate (3). Their mechanical and chemical characteristics are summarized in Tables 4 and 5 [49]. The aggregate characterization techniques are outlined by [55][56][57][58].  Regarding the treatment of the shavings, many treatments have been utilized in earlier studies, and it has been demonstrated that treatment by coating lime with cement yields satisfactory results, particularly in terms of mechanical strength and shrinkage [59,60]. Indeed, before adding these two types of wood chips to the composition, they were immersed in the combinations (cement + water) and then (lime + water). Lime milk was made from natural hydraulic lime (NHL5). The treated chips were left to dry in their natural state for more than 3 days before use. Indeed, for cement treatment of the W I and W II surfaces, they are immersed individually in cement milk or in water. The cement and lime used in this operation were Portland cement and natural hydraulic lime (NHL5). Similarly, the two types of wood were immersed in cement milk for the lime treatment. Cement and lime milks are cement-water and lime-water mixtures, respectively. Both of them were prepared, respectively, with water-cement (W/C) and water-lime (W/L) ratios equal to 1. After complete saturation, the treated chips were allowed to dry in the open air for 3 days before being used. Figure 5 shows the W I and W II before and after the cement and lime treatments.
Similarly, the two types of wood were immersed in cement milk for the lime treatment. Cement and lime milks are cement-water and lime-water mixtures, respectively. Both of them were prepared, respectively, with water-cement (W/C) and water-lime (W/L) ratios equal to 1. After complete saturation, the treated chips were allowed to dry in the open air for 3 days before being used. Figure 5 shows the WI and WII before and after the cement and lime treatments.  Seven different types of specimens will be discussed in this article:

Formulation of Concrete
Previous research [49] has provided the ideal compositions of the sand concrete examined without including wood shavings. Indeed, concrete is a glue-based material that holds the fillers together (fine aggregates, coarse aggregates, rolling sand, and wood chips). The paste and fillers combine to form the heterogeneous substance known as "concrete." The Dreux-Gorisse technique [33] is used to investigate the concrete composition. The compositions shown in Table 6 were used to prepare the mixtures. Figure 6 shows the results of a particle size study performed on the aggregates. The aim of this formulation was to generate a common concrete with a characteristic compression resistance of 30 MPa at 28 days. The maximum diameter (D max ) was set at 1, the average vibration speed was 1, and the proportion of aggregates was as follows: 35% rolling sand, 10% fine particles, and 55% coarse aggregates (3). The compositions shown in Table 6 were used to prepare the mixtures. results of a particle size study performed on the aggregates. The aim of this formulation was to generate a common concrete with a characteristic compression resistance of 30 MPa at 28 days. The maximum diameter (Dmax) was set at 1, the average vibration speed was 1, and the proportion of aggregates was as follows: 35% rolling sand, 10% fine particles, and 55% coarse aggregates (3). The compositions shown in Table 6 were used to prepare the mixtures.

Concrete Mixing
These procedures are sensitive because they are required to assure the status of the coating and the holding of the chips. Therefore, a well-defined procedure and low-speed mixing (about 50 turns mn −1 ) were adopted. The dry sand, cement, gravel, and wood chips were combined for 1 min at a slow speed. When the mixture was entirely homogenous, the mixing water was progressively added at a slow pace for 4 min. Using a vibrating table at a rate of 50 Hz and a vibrating time of 1 min resulted in the separation of distinct components. Finally, the moulds were manually filled.

Preparation of Specimens
The slump test for concrete was assessed using an Abrams cone after it had been mixed (AFNOR P 18-451). The Abrams cone slump was used to calculate handling. The new concrete was introduced into a cubic mould (10 × 10 × 10 cm 3 ) on a vibrating table for 1 min. The specimens were stored in an appropriate location for 24 h and then immersed in water according to the NFP18404 standard.

Experimental Methodology of Compressive Strength Test
Each reported result for the compressive strength tests was the average of 105 samples. The seven categories of samples were tested for each series. Each kind was tested three times to ensure that the results would be reproducible. As a consequence, the total number of specimens used for each series was 21. The dry compressive strength was tested using a Baratest AG hydraulic press built in Switzerland; the compressive strength loss (RL) and gain (RG) are computed using Formula (5): R SC is the control specimen's compressive strength (MPa), and R is the compressive strength of a specimen of the same type in each environment (MPa).

Density Determination
Density was calculated by multiplying the mass of each specimen and its envelope volume, as shown in Equation (6), where M 0 is the weight (g), V 0 is the volume (cm 3 ), and is the density (g cm −3 ). The average of five measurements was used to calculate the results.

Water Absorption Capacity Measurement
The water absorption capacity was calculated using ASTM D 1037-12. A total of 6 specimens were submerged in water at a temperature of 20 • C for each sample. After 2 h and 24 h, the mass measurements were obtained. Each specimen's water absorption was determined as a percentage of mass gain compared to the starting mass, as shown in Equation (7) where m sat (g) is specimen mass in a saturated state and m dry (g) is the specimen mass in a dry state:

XRD Characterization
A Rigaku Ultima IV multipurpose X-ray diffraction apparatus was used to analyse the crystalline structure of the treated and untreated wood chips. The diffractometer was equipped with an X-ray generator (maximum rated output: 3 kW, target: Cu) and a goniometer (maximum rated output: 3 kW, target: Cu). The high score application, in accordance with the International Centre for Diffraction Data (ICDD) PDF-4, was used to identify the phases and retrieve all of the crystalline structure characteristics.

Ordinary Concrete
From the findings in Figure 7, RLs of the OCs were evident in all media, and they depended on the conservation context. The compressive strength of the control OC was about 37.1 MPa. The literature shows a mean compression strength of 37.3 MPa in moulded cement composites made using Portland cement and no wood [61]. The creation of gluewater-cement explains this result during the first 28 days of concrete setting. Le Chatelier (1887) [54] described a cement hydration process based on dissolution/precipitation. When water is supplied, the anhydrous reactants will gradually dissolve. These reactants are more soluble than the products after hydration. The solution becomes supersaturated, resulting in the precipitation of hydrates. As the concentration of reactants (Table 3) falls, more ions enter the solution, allowing other hydrates to precipitate. The primary phases of Portland cement are tricalcium silicates (C 3 S) and dicalcium silicates (C 2 S) ( Table 2). Their hydration products are hydrated calcium silicates (C-S-H) and Portlandite (Ca(OH) 2 ) [62,63]. saturated, resulting in the precipitation of hydrates. As the concentration of reactants (Table 3) falls, more ions enter the solution, allowing other hydrates to precipitate. The primary phases of Portland cement are tricalcium silicates (C3S) and dicalcium silicates (C2S) ( Table 2). Their hydration products are hydrated calcium silicates (C-S-H) and Portlandite (Ca(OH)2) [62,63].   36.06%, 42.85%, and 52.30%, after 12 months of exposure to outdoor air, drinking water, seawater, and an oven, respectively. Hardened concrete improves its compressive strength over time under normal conditions. However, it should be noted that environmental variables, particularly RH, temperature, and inorganic salts, might influence the evolution of compressive strength. Open air 28D (1) Open air 365D (2) drinking water 365D (3) seawater 365D (4) stove 365D (5) Compressive strength (MPa) OC UWI UWII  .85%, and 52.30%, after 12 months of exposure to outdoor air, drinking water, seawater, and an oven, respectively. Hardened concrete improves its compressive strength over time under normal conditions. However, it should be noted that environmental variables, particularly RH, temperature, and inorganic salts, might influence the evolution of compressive strength.
The evaluation of the impact of RH on the compressive strength of fresh and hardened cement is based on a concerted effort and is strongly connected to the phenomena of carbonation [64]. Carbonation, according to Mahmood et al. [65], is described as a regularly diffused phenomenon in ancient reinforced concrete structures, which are typically constructed without special design requirements preventing degradation. In the carbonation process, atmospheric carbon dioxide (CO 2 ) enters the concrete cover through the capillary pores and reacts with calcium hydroxide (Ca(OH) 2 ), which is a hydration product of calcium silicate compounds present in the clinker and which is responsible for pH value reduction, resulting in the formation of calcium carbonate, as depicted by Equation (8): Furthermore, CO 2 may react with the calcium silicate hydrate (C-S-H) network to produce additional CaCO 3 [66]. The proportion of Portlandite (Ca(OH) 2 ) in the concrete mass determines the pH of the recycled aggregate. Because of the dissolution of Ca(OH) 2 and the generation of OH-in water, the pH of the recycled aggregate increases to 12 and normally ranges from 11 to 13. According to Equation (9), the presence of water in the carbonation process is required for the mobility of hydrated cement products in the pore solution and allows CO 2 to dissolve and create carbonic acid (H 2 CO 3 ). Using the following process, this weak acid attacks Portlandite (Ca(OH) 2 ) and generates CaCO 3 : Elsalamawy et al. [67] established a direct proportionality between carbonation depth and concrete compressive strength. This is supported by Peng Liu et al. [25], who reinforced this conclusion, noting that cement type has a significant impact on concrete carbonation resistance. Metalssi et al. [67] report that, for genuine constructions exposed to natural carbonation, the concrete is saturated after demoulding and cannot be carbonated spontaneously owing to the low CO 2 content. Carbonation, on the other hand, might occur after a partial drying of the material, after several weeks, or even after several years (in the case of Portland cement, CEM I according to European standards) [68].
Elsalamawy et al. [67] demonstrate that RH is one of the most important elements influencing carbonation depth, with the carbonation depth increasing with increasing RH to reach a peak value at 65 percent RH, regardless of cement type. This discovery validates the importance of the electrified RL for open-air OC preservation (conditions: RH = 65%, T = 25 • C, pH [12][13][14]. In addition, the same authors [67] determined relative carbonation depth by dividing the value of carbonation depth by the maximum value of carbonation depth. They established the polynomial relationship between relative carbonation depth and relative humidity (40-80%). The graph demonstrates that at RH 50%, there is insufficient moisture for carbonation to occur, and at RH > 70%, there is insufficient moisture for carbonation to occur. Therefore, it can be inferred that the carbonation phenomenon has no effect on the conservation of OC in drinking water (RH 100%), seawater (RH 100%), or the oven (RH 50%).
In drinking water and seawater, inorganic ions, such as Cl − , SO 4 2− , Mg 2+ , K + , and Na + , occur in aqueous media. According to Chen et al. [69], Mg 2+ and SO 4 2− may be more damaging to the compressive strength of cement-based composites than other anions. The major damage caused by SO 4 2− to concrete is crystalline corrosion [6,70], which includes the conversion of thenardite crystals to mirabilite crystals [70,71] and the volume expansion of ettringite crystals and gypsum crystals. Both of the aforementioned factors may cause a sequence of physical and chemical reactions inside the concrete, which may result in additional concrete expansion and cracking [72][73][74]. Mg 2+ damage is mostly indicated by the weakening of mortar and aggregate on the concrete's surface [12,75]. This is due to Mg 2+ generating magnetic Mg(OH) 2 inside the concrete, which has low solubility. With the continuous precipitation of Mg(OH), C-S-H cementing material degrades and produces non-cementitious M-S-H [76,77]. These considerations support the RLs obtained during OC preservation in an aqueous medium. Furthermore, due to the high concentration of mineral salt in saltwater, the RL of OC preserved in seawater is larger than that in drinking water.
Previous research on the compressive behaviour of hardened concrete at various temperatures has been conducted. As the heating temperature increased, the compressive strength of concrete with the same moisture level decreased [78]. Concrete curing temperatures below 5 • C or over 100 • C resulted in an almost 20% drop in concrete strength [79]. When the gap between the ambient and concrete temperatures was small, the mechanical performance of concrete was ideal [80]. According to El-Zohairy et al. [81], after just 90 days, concrete lost 10-20% of its initial compressive strength when heated to 100 • C and 30-40% when heated to 260 • C. Therefore, in the current study, OC maintained in the oven had the lowest compressive strength (17.66 MPa). As a result, it displayed an RL value (52.30%) that was about twice as low as that of the OC after 28 days.

Untreated Redwood-Cement Concrete
Because of the nature of the untreated redwood chips, Figure 7 reveals an alarming rise in RL for all media. After 28 days, UW I was characterized by excessive water absorption and increased swelling (7.8 MPa). In general, vegetated concrete has a high porosity. Indeed, the SEM pictures of a significant variety of fibre cements in the literature exhibit several fields when compared to regular concrete [82][83][84][85][86]. As a result, the addition of wood fibres to concrete enhances its density. In addition, because of their porosity, these concretes are water-sensitive [87].
After 12 months of storage in the open air, 36.92%, 19.23%, and 65.76% of RLs were obtained. Wood-fibre-concrete's porous nature has a capacity to exchange moisture (or water) with the surrounding environment via the adsorption/desorption phenomena [14]. According to Mohr et al., the bulk of mechanical property losses occurred during the first five wet/dry cycles. However, ductile fibre failure was still identified using scanning electron microscopy (SEM) [88,89]. The sensitivity of vegetal concretes to humidity causes dimensional fluctuations that correspond to changes in relative humidity [90]. In addition, RH has been shown to influence at least four essential characteristics of electrospun fibres: surface morphology, interior porosity, structure, and mechanical qualities [91].
Wood-fibre-cement composites age in humid and aquatic environments, resulting in a reduction in strength and toughness. Wood composition in the specimens is often exposed to three distinct processes reducing their adherence to the matrix [41]: • Debonding of the plant particle/matrix interfaces because of wood-water swelling.

•
The degradation of plant particles is promoted by progressive alkali hydrolysis.

•
Mineralization of plant particles is caused by the deposition of cement hydration products, primarily calcium hydroxide, onto the plant particle surface. On the other hand, the adhesion problem can be enhanced by modifying the particle surface.
The RL of UW I in drinking water (19.23%) is insignificant compared to the nonaqueous environments after 28 and 365 days. In addition, The RL in drinking water was about 3.5 times more than the RL of UW I stored in saltwater (65.76%). The pH of the storage media explains this finding. In fact, the pH of drinking water (pH 6) is lower than that of saltwater (pH 8-9), and the non-aqueous environments (pH [12][13][14]. The lower the pH, the less alkaline the attack on the wood.
On the other hand, 68.84% of the RL was obtained after 12 months in the oven. Based on SEM images from the study by de Abreu Neto et al. [92], it is probable that increasing the temperature causes deformations and changes in the morphology of the wood fibres as a whole. Indeed, wood fibres exhibited a propensity for the thickness of their fibre walls to shrink with increasing temperatures. The study conducted by Dehghan et al. [93] supports this fact. Figure 7 depicts the variation of UW II resistance according to the storage medium. Compared to the UW I data, it is clear that the resistance improved considerably in all the selected environmental conditions. The discrepancy is explained by a difference in the absorption coefficient of the aggregates [12]. W I has a lower apparent density than W II . However, this structure results in a material with poor strength and stiffness after cure. W I has a very high water-absorption capacity because of its porous structure, which reduces the amount of water available for the binder to set in. Furthermore, the significant migration of water via capillarity results in the movement of Ca 2+ calcium ions, which are required for binding the binder with the plant particles.

Untreated Hardwood-Cement Concrete
In order to verify this, the effect of the ratio of W I and W II on the density and adsorption capacity of UW I and UW II after 28 days of hardening was explored. Figure 8 demonstrates the outcomes. Figure 8a demonstrates that the densities of UW I and UW II reduce when the ratios of W I and W II in the concrete composition increase. This demonstrates that the wood chips from W I and W II lighten the concrete. Furthermore, Figure 8b shows that the absorption capacities of UW I and UW II are proportional to the rate of the wood chips. When the densities and water-absorption capacities of the two concretes are compared, it is evident that the densities and water-absorption capacities of UW II are greater than those of UW I . This demonstrates that W I has a lower density and a higher water-absorption capacity than W II .
According to Mukhopadhyay et al. [94], the degrees of deterioration caused by an alkaline environment attack on the vegetal additive's composition vary. The loss of mechanical characteristics of various vegetables additives' composition determines the extent of the damage. The severity of the attack ranges from a severe loss of strength to almost no loss of strength. It is governed by the capacity of the vegetal additive's composition to absorb water. the wood chips from WI and WII lighten the concrete. Furthermore, Figure 8b shows that the absorption capacities of UWI and UWII are proportional to the rate of the wood chips. When the densities and water-absorption capacities of the two concretes are compared, it is evident that the densities and water-absorption capacities of UWII are greater than those of UWI. This demonstrates that WI has a lower density and a higher water-absorption capacity than WII. According to Mukhopadhyay et al. [94], the degrees of deterioration caused by an alkaline environment attack on the vegetal additive's composition vary. The loss of mechanical characteristics of various vegetables additives' composition determines the extent of the damage. The severity of the attack ranges from a severe loss of strength to almost no loss of strength. It is governed by the capacity of the vegetal additive's composition to absorb water.
The RG in all sectors, on the other hand, is lower than the OC. The result was that 15.67, 28.42, and 86.96% of RG were allocated when the UWII samples were in the open air, potable water, and seawater. However, soaking UWII in saltwater for 12 months yielded the best compressive strength results. Indeed, UWII increased in its compressive strength by 40.5%. Even though multiple investigations have yielded equivalent results [72], the behaviour of concrete loaded with wood augmentation methods in saline solutions is still poorly understood. The rise in its compressive strength in seawater is due to the high concentration of inorganic salts. The concentration of inorganic ions in saltwater The RG in all sectors, on the other hand, is lower than the OC. The result was that 15.67, 28.42, and 86.96% of RG were allocated when the UW II samples were in the open air, potable water, and seawater. However, soaking UW II in saltwater for 12 months yielded the best compressive strength results. Indeed, UW II increased in its compressive strength by 40.5%. Even though multiple investigations have yielded equivalent results [72], the behaviour of concrete loaded with wood augmentation methods in saline solutions is still poorly understood. The rise in its compressive strength in seawater is due to the high concentration of inorganic salts. The concentration of inorganic ions in saltwater is greater than that in drinking water [95,96]. However, the competition for OH − and Ca 2+ attachment to the surface of wood chips with other inorganic ions is more crucial.

Cement Treatment of Wood
To improve some of the properties of the investigated compositions, such as water sensitivity and wood-matrix adhesion, treating the wood pieces before incorporating them into the concrete was considered. Various treatments have been used in previous works, and it has been demonstrated that coating with cement produces satisfactory results, particularly in terms of compressive strength. Because of this impact, W I and W II were treated with cement before being included in the concrete mixture. Figure 9 depicts the findings of the compressive strength of TW IC and TW IIc , respectively, preserved in different media. The shaving treatment significantly enhanced the compressive strength of TW IC and TW IIc in all tested media, resulting in a suitably light structural weight. These findings are consistent with Bedirinan's study [28]. is greater than that in drinking water [95,96]. However, the competition for OH − and Ca 2+ attachment to the surface of wood chips with other inorganic ions is more crucial.

Cement Treatment of Wood
To improve some of the properties of the investigated compositions, such as water sensitivity and wood-matrix adhesion, treating the wood pieces before incorporating them into the concrete was considered. Various treatments have been used in previous works, and it has been demonstrated that coating with cement produces satisfactory results, particularly in terms of compressive strength. Because of this impact, WI and WII were treated with cement before being included in the concrete mixture. Figure 9 depicts the findings of the compressive strength of TWIC and TWIIc, respectively, preserved in different media. The shaving treatment significantly enhanced the compressive strength of TWIC and TWIIc in all tested media, resulting in a suitably light structural weight. These findings are consistent with Bedirinan's study [28]. Wood treatment lowers the porosity of TWIC and TWIIC structures, increasing the composites densities and decreasing the water capacities. This perspective is supported by Figure 10. It shows the findings of the change in the density and water absorption capacity of TWIc and TWIIc as a function of the mass of WI and WII treated with cement and   Wood treatment lowers the porosity of TW IC and TW IIC structures, increasing the composites densities and decreasing the water capacities. This perspective is supported by Figure 10. It shows the findings of the change in the density and water absorption capacity of TW Ic and TW IIc as a function of the mass of W I and W II treated with cement and lime. When the equations of Figures 8a and 10a are compared, the tangents of the density plots of TW IC and TW IIC are higher than those of UW I and UW II . Similarly, the tangents of the water-absorption capacity graphs of TW IC and TW IIC are lower than those of U WI and U WII (Figures 8b and 10b). These are the results of the wood-chip treatment. This finding demonstrates that treating wood chips with cement is an efficient way to create a more durable wood-cement composite. In addition, it improves wood-matrix adhesion since the coating of the chips in a layer of cement is likely to reinforce the adhesion with the cementitious matrix. It is possible that the pre-coating of the chips minimizes the hygroscopic effect and increases the wood-matrix adhesion. The images of the SEM of treated and untreated wood chips (WI and WII) in Figure 11 indicated that the cement matrix takes the shape of plates, and the distribution is random. They are more frequent in less inhabited places and specimens made of cement-treated chips. They can be seen clearly on the surface of the treated chips and do not exist on the untreated chips. These findings support the notion that the adhesion between wood and cement is poor. Furthermore, if the cement concentration in the treatment product is high, the paste layer coating the wood grains may be thicker, resulting in higher wood rigidity [72]. Consequently, significant compressive strength is attained in all of the investigated media. In addition, it improves wood-matrix adhesion since the coating of the chips in a layer of cement is likely to reinforce the adhesion with the cementitious matrix. It is possible that the pre-coating of the chips minimizes the hygroscopic effect and increases the wood-matrix adhesion. The images of the SEM of treated and untreated wood chips (W I and W II ) in Figure 11 indicated that the cement matrix takes the shape of plates, and the distribution is random. They are more frequent in less inhabited places and specimens made of cement-treated chips. They can be seen clearly on the surface of the treated chips and do not exist on the untreated chips. These findings support the notion that the adhesion between wood and cement is poor. Furthermore, if the cement concentration in the treatment product is high, the paste layer coating the wood grains may be thicker, resulting in higher wood rigidity [72]. Consequently, significant compressive strength is attained in all of the investigated media.

Mechanism of Cement-Wood Treatment
Based on Table 2, it is possible to conclude that the cement was constituted chiefly of lime (60.41%). Given this fact, W I and W II were subjected to lime treatment to understand better the influence of cement treatment chemistry on compressive strength. Figure 12 shows the results of TW IL and TW IIL compression strength in relation to the conservation medium. Figure 13 shows that TW IL and TW IIL were less resistive after 28 days than were TW IC and TW IIC . The compression strengths of TW IL and TW IIL were 14.60 MPa and 15.05 MPa, respectively. The findings indicate that the strength of the concrete is only affected by the cement's composition after 28 days in open air. distribution is random. They are more frequent in less inhabited places and specimens made of cement-treated chips. They can be seen clearly on the surface of the treated chips and do not exist on the untreated chips. These findings support the notion that the adhesion between wood and cement is poor. Furthermore, if the cement concentration in the treatment product is high, the paste layer coating the wood grains may be thicker, resulting in higher wood rigidity [72]. Consequently, significant compressive strength is attained in all of the investiated media.

Mechanism of Cement-Wood Treatment
Based on Table 2, it is possible to conclude that the cement was constituted chiefly of lime (60.41%). Given this fact, WI and WII were subjected to lime treatment to understand better the influence of cement treatment chemistry on compressive strength. Figure 12 shows the results of TWIL and TWIIL compression strength in relation to the conservation medium. Figure 13 shows that TWIL and TWIIL were less resistive after 28 days than were TWIC and TWIIC. The compression strengths of TWIL and TWIIL were 14.60 MPa and 15.05 shows the results of TWIL and TWIIL compression strength in relation to the conserva medium. Figure 13 shows that TWIL and TWIIL were less resistive after 28 days than w TWIC and TWIIC. The compression strengths of TWIL and TWIIL were 14.60 MPa and 1 MPa, respectively. The findings indicate that the strength of the concrete is only affe by the cement's composition after 28 days in open air.    Figure 12 shows clear improvements in the specimens' compression strength after 365 days of conservation in all environments investigated. This finding is supported by the fact that both TWIL and TWIL resistances were improved by 8.5 MPa compared to UWI and UWII resistances. The enhanced resistance was due to the lime's ability to act as a surface layer for the wood chips [97]. This finding indicates that the improvement in compression strength of the TWIC and TWIIC was primarily attributable to the lime.  Figure 13 shows the findings regarding TWIL and TWIIL density and water-absorption capacity in relation to the mass of the wood chips. The tangents of the density plots of TWIL compared to TWIc, as well as TWIIL compared to TWIIC, are almost identical. This means that the lime in the cement maintains the impermeability of water in the wood. However, TWIL acquired resistance in all of the storage media except saltwater according to  The XRD patterns of WII, WIIc, and WIIL are shown in Figure 14. Tables 8 and 9 present structural characteristics derived from XRD characterizations of WI and WII, respectively.  Figure 12 shows clear improvements in the specimens' compression strength after 365 days of conservation in all environments investigated. This finding is supported by the fact that both TW IL and TW IL resistances were improved by 8.5 MPa compared to UW I and UW II resistances. The enhanced resistance was due to the lime's ability to act as a surface layer for the wood chips [97]. This finding indicates that the improvement in compression strength of the TW IC and TW IIC was primarily attributable to the lime. Figure 13 shows the findings regarding TW IL and TW IIL density and water-absorption capacity in relation to the mass of the wood chips. The tangents of the density plots of TW IL compared to TW Ic , as well as TW IIL compared to TW IIC , are almost identical. This means that the lime in the cement maintains the impermeability of water in the wood. However, TW IL acquired resistance in all of the storage media except saltwater according to Table 7 (−24.59%). Similarly, besides the oven (−30.88%), all conservation zones in TW IIL exhibited a grain in strength. The LRs collected are not related to the W IL and W IIL lime treatments. The XRD patterns of W II , W IIc, and W IIL are shown in Figure 14. Tables 8 and 9 present structural characteristics derived from XRD characterizations of W I and W II , respectively.  , a derivative of cellulose crystal planes (C6H10O4) in wood fibres (WI and WII) [98,99]. Thus, according to    , a derivative of cellulose crystal planes (C 6 H 10 O 4 ) in wood fibres (W I and W II ) [98,99]. Thus, according to Camargo et al. [41], the major component of plant fibres is cellulose. In addition, no typical peaks at 16.85 • and 22.60 • were detected, as shown in Figure 14. A previous study of bamboo surfaces, investigated by Bao et al. [100], supports this fact. On the other hand, the XRD data of cement-treated wood (W IC and W IIC ), are differentiated by 3 peak ranges, namely: (i) 5   .

Method
In comparison to Tables 2 and 3, the elements of cement with the largest weight percentages are CaO, SiO 2 , and Al 2 O 3 , in that order. They are also prominent components of clinkers, with FeO 2 , in low proportion, being the most abundant. This allows us to state that the cement has attached to the surface of the wood because the clinkers act as a glue. [101]. Similarly, there are 3 distinct sets of peaks in the lime-treated wood (W IL and W IIL ) spectra, namely: (i) 4 peaks at 28 Based on these findings, it is possible to deduce that the adherence of the lime on the surface of the wood is only made by Ca(OH) 2 . The existence of CaCO 3 on the surface of the wood is supported by the attack on Ca(OH) 2 by humidity and CO 2 in the air. According to Okayinkwa et al. [102], calcium carbonate significantly boosts the compressive strength of wood-cement concrete by decreasing its permeability. Furthermore, an SEM image of CaCO 3 /Wood-concrete, investigated by Merk et al. [103], shows that CaCO 3 may be introduced deep into the wood structure using alternating solution-exchange cycles of extremely concentrated electrolytes NaHCO 3 in water. Despite this fact, in the work conducted by Mejri et al. [104], it was demonstrated that the presence of sulphate and magnesium ions lowered the crystal development rate and decreased the quantity of CaCO 3 precipitates obtained at a constant temperature and ionic strength. Magnesium caused the production of aragonite rather than calcite or vaterite. The presence of magnesium and sulphate ions caused changes in the effect of magnesium on the kinetics of CaCO 3 precipitation, resulting in the incorporation of Mg 2+ ions in the CaCO 3 lattice. This explains the RL for TW IL obtained after 365 days in sea water (Table 7).
On the other hand, according to Cheng Bencedira et al. [105], the increase in temperature increases CaCO 3 precipitation in water (RH 100%). However, the CaCO 3 precipitation depends on the percentage of RH in the medium. Indeed, according to Pondelak et al. [106], After one year of exposure at RH 33% and T = 45 • C, the CaCO 3 does not precipitate. As a consequence, TW IL loses 30.88% of its compression resistance. It is hypothesized that CaCO 3 's stability is owing to the restricted quantity of water physiosorbed on the surface of the wood fibres, which is thought to be the driving factor for its precipitation.
According to Graine et al. [107], the average diameter of treated/untreated samples is calculated by measuring the width at half-height of the respective XRD peaks and by employing two methods, Scherrer's and Williamson-Hall. Scherrer's principle indicates that the widening of the XRD peaks is solely attributable to particle size. Using Equation (10), we can calculate the average crystallite size from the X-ray patterns: where D is the mean crystallite size, K is the crystallite form factor (12), is the X-ray wavelength, corrected is the full width at half the maximum of the peak, and is the diffraction angle. For correct calculations, the instrumental broadening effect and the observed XRD pattern peaks must be separated. As a result, Equation (11) can be used to estimate the corrected broadening, which is simply influenced by particle size.
However, the broadening of the XRD peaks might also be attributable to the lattice's micro-strain impact. As a result, for greater precision, we must also separate the crystallite size effect and the micro-strain impact. In this paper, the Williamson-Hall approach was employed, which assumes Equation (12) where is ε is the micro-strain in the lattice: D variation is shown in  (Figure 15a) and 1.30 nm, 8.16nm, and 15.77 nm, respectively, according to the Scherrer method ( Figure 15b). These data indicate that the wood chips' Ds before treatment are the same. This supports the wood chip diameter results using granulometric analysis. In addition, the two approaches' calculations demonstrate that the diameter of the wood particles increases when they are treated. In fact, D of cement-treated wood is larger than D of lime-treated particles. As a result, when the wood surfaces are treated, the lattice strain decreases. Indeed, the best lattice strain findings are attributable to W IC and W IIC . The reduction in lattice strain is reflected in the reduction in spacing within the minimum wood width. As a result, the density of the wood rises, while its capacity to absorb water diminishes. The study conducted by Zhang et al. [108] supports this argument.

Conclusions and Limitations
This work contributes to the broader challenge of sustainable development by improving wood-concrete composites' physical characteristics to expand their range of use. As a result, this work aimed to investigate the influence of various environments on the compression strength of concrete containing hardwood or redwood shavings. The studied storage environments were: open-air (T = 25 • C, RH 55%, pH [12][13][14], drinking water (T = 25 • C, RH 100%, pH 6-7), seawater (T = 25 • C, RH 100%, pH 7-9) and an oven (T = 75 • C, RH < 50%, pH [12][13][14]. Due to the complex mechanisms involved in this study, only the compressive strength was experimentally measured. The main findings obtained are: -Ordinary concrete strength diminishes after 365 days of storage in every medium investigated compared to its strength after 28 days. Depending on the environment studied, this decrease is significant. -In all conditions investigated, the addition of wood (redwood or hardwood) to the concrete reduces its resistance. The low mechanical resistance of vegetable concretes is partly due to the high water-absorption of wood chips and the poor wood-matrix adhesion. -Concrete made of untreated hardwood is more resistant, in all preservation media, than concrete made of redwood due to its high apparent density. -Seawater enhances the strength of hardwood-based concrete. Indeed, compressive strength results for ordinary concrete and hardwood-based concrete are comparable. - The treatment of wood enhances the compressive strength after 365 days in all conservation media. The lime in cement acts on wood chips by (i) coating the surface of the wood, which lowers the porosity subtract of wood-based concrete, (ii) and reinforces the wood-matrix adhesion. The other cement constituents are only involved during the curing step (the first 28 days).
Even though treating wood with cement coating improves its resistance in watery environments, its resistance in dry and wet environments remains lower. The resistance of OC surpasses that of TW IIc by 11.7 MPa, 12.51 MPa, and 8.86 MPa, respectively, after 28 days in the open air and 365 days in the open air and the oven. However, OC and TW IIC resistance after 365 days in drinking water and saltwater are comparable. This enables us to conclude that the efficiency of cement treatment of wood for boosting compressive strength is restricted solely to watery conservation conditions. The research has implications for academics where the results of the study can be used to understand the wood-concrete composite material further. Some of the remedies to enhance its performance can include (a) describing the failure mode of each series using a variety of analytic methods, (b) changing the treatment of the surface of wood chips to linseed oil, (c) changing the type of surface treated, or (d) combining two forms of therapies.

Data Availability Statement:
The data presented in this study are available upon request from the corresponding author.