Sintering and Mechanical Properties of (SiC + TiCx)p/Fe Composites Synthesized from Ti3AlC2, SiC, and Fe Powders

Ceramic-particle-reinforced iron matrix composites (CPR-IMCs) have been used in many fields due to their excellent performance. In this study, using the fast resistance-sintering technology developed by our team, iron matrix composites (IMCs) reinforced by both SiC and TiCx particles were fabricated via the addition of SiC and Ti3AlC2 particles, and the resulting relative densities of the sintering products were up to 98%. The XRD and EDS analyses confirmed the in situ formation of the TiCx from the decomposition of Ti3AlC2 during sintering. A significant hybrid reinforcing effect was discovered in the (SiC + TiCx)p/Fe composites, where the experimental strength and hardness of the (SiC + TiCx)p/Fe composites were higher than the composites of monolithic SiCp/Fe and (TiCx)p/Fe. While, under the condition of constant particle content, the elongation of the samples reinforced using TiCx was the best, those reinforced by SiC was the lowest, and those reinforced by (SiC + TiCx) fell in between, which means the plastic response of (SiC + TiCx)p/Fe composites obeyed the rule of mixture. The successful preparation of IMCs based on the hybrid reinforcement mechanism provides an idea for the optimization of IMCs.


Introduction
With its advantages of high strength and elasticity modulus, excellent abrasion performance, and great heat resistance, ceramic particle reinforced iron matrix composites (CPR-IMCs) have shown great application prospects in machinery, mining, metallurgy, and other fields, and thus have attracted extensive attention from researchers [1][2][3][4][5]. Iron matrix composites (IMCs) are generally popularly fabricated using the liquid-phase process or conventional powder metallurgy [2,6,7]. The normal powder metallurgy and even hot isostatic press sintering both take a long time (usually lasts several hours) and result in severe interface reactions between the reinforcing particles and the matrix, which could weaken the reinforcing effect caused by the ceramic particles and reduce the properties of the IMCs [7]. As a result, the application of IMCs has been limited.
Our team has developed a fast resistance-sintering technology by which IMCs can be synthesized under a certain external pressure in the condition of a semi-molten state. This sintering process, which is normally done in a few minutes, makes manufacturing feasible with low costs and produces excellent material properties due to the short processing time [5,8]. With a good load-bearing effect in composites, SiC is a very common reinforcing agent in many metal base materials, such as iron [5,9], aluminum [10][11][12][13], magnesium [14,15], nickel [16,17], and zinc [18]. Our previous research results showed that SiC has the best enhancement effect compared with the common candidate reinforcements, such as TiC, TiN, and Cr 3 C 2 in IMCs [8]. Furthermore, IMCs reinforced using a low SiC content (≤10%) have been successfully prepared based on this technology [5,8,9,19,20]. Since the heat source of this technology is the joule heat generated by metal powders passing by an electric current, the electric conductivity of reinforcing particles has a very important effect on the sintering performance, and the electrical resistance of SiC particles is high (up to 5.3 × 10 −6 Ω·m under 293 K) [8]. As a result, it is reasonable to find that there is a decrease in electrical conductivity and joule heat, which causes a decline in the material performance when the SiC content exceeds 10% [5]. Generally, the hardness and the wear resistance of composites can be dramatically improved by increasing the amount of reinforced particles [1]. Thus, it is extremely challenging and interesting to add another reinforcing particle on the basis of IMCs reinforced by SiC without reducing the electrical conductivity of the as-prepared powder to further optimize the performance of IMCs. As we know, the reports on the effects are too few and too inconsistent to draw any conclusions. Ti 3 AlC 2 , one kind of MAX phase materials (M is a transition metal, A is an element from groups IIIA to VIA, and X is C or N), has a very high electrical conductivity ((2.87-3.45) × 10 −7 Ω·m under 293 K) [21][22][23][24][25][26]. Research has found that an exothermic reaction between Fe and Ti 3 AlC 2 is predominant above 763.1 • C, and Ti 3 AlC 2 totally disappears and transfers into TiC x and Fe (Al) when the temperature is up to 1045 • C [24]. Furthermore, TiC x is also a commonly used reinforcement agent in IMCs and has a good reinforcing effect for metal matrix composites (such as titanium [27], high entropy alloys [28,29], and iron [30]), as it has excellent hardness, a high melting temperature (3147 • C), wear resistance, and thermodynamic stability, according to previous work [8]. Meanwhile, it is predicted that there is better interface bonding between the matrix and TiC x that is formed by the decomposition of Ti 3 AlC 2 . Recently, Ti 2 AlC, which is another kind of MAX phase with similar physical properties and crystal structure to Ti 3 AlC 2 , has been used as the precursor to trigger in situ TiC x in Inconel718, where enhanced mechanical properties could be successfully obtained [25]. This is a very inspiring work, indicating the feasibility of the strengthening method using in situ TiC x decomposed by Ti 3 AlC 2 .
According to the features of electrical conductivity and decomposition in an iron matrix at elevated temperatures, Ti 3 AlC 2 was added into IMCs in this work. Meanwhile, SiC, which is one of the best reinforcing particles in IMCs, was also added to obtain IMCs with a higher particle content and better mechanical properties, such as tensile strength and hardness. The primary objective of this study was to investigate the feasibility of fabricating ICMs reinforced by both SiC and in situ TiC x based on the decomposition of Ti 3 AlC 2 . Three combinations (SiC + Fe, Ti 3 AlC 2 + Fe and SiC + Ti 3 AlC 2 + Fe) were designed for comparison and the total particle contents (vol.%) were chosen to be 15% and 20% (the ratio was 1:1 in a two-particle-type mixture). The microstructure and properties of the IMCs were also examined to evaluate the sintered products and reveal the strengthening mechanism.

Materials and Samples
The starting materials for the IMCs preparation were powders of iron, α-SiC, and Ti 3 AlC 2 . The powders of iron and SiC used in the experiment were all commercial powder products (iron was produced by Beipiao Shenglong Power Metallurgy Co., Ltd., Chaoyang, China, and the SiC was from Shanghai Colloid Chemical Plant, Shanghai, China) with a ≥99.85% purity rating. Ti 3 AlC 2 powder was synthesized using the fluctuation method and the synthesis details are described in [31,32]. The average particle sizes of the SiC and Ti 3 AlC 2 powders were~10 µm and~5 µm, respectively. The iron powders were commercial deoxidized powder with an average size of 50 µm and a maximum C content of 0.015 wt.%. Meanwhile, zinc stearate was added as a caking agent and lubricant. The ratios of powders in different samples are as follows (Table 1). Each mixture of powders was mixed for 15 h in a planetary high-energy ball mill and then compressed into a block with a size of 60 × 30 × 10 mm 3 . The grinding ball material was GCr15 and the mass ratio of the ball to the material was 5:1 with a speed of 300 r/min during the dry grinding process. The fast resistance-sintering technology, based on the equipment adapted from the traditional hot-pressing furnace [6,[9][10][11][12], was adopted for the sintering of the cold-pressed samples. The main parameters of the sintering process were pressure, voltage, heating, and holding time. An external pressure limited to 40 MPa was applied to obtain a product with a high relative density according to the performance of the ceramic die. A two-stage sintering process, during which the first stage can heat the powders into a semi-molten state and the second stage can hold the state under applied stress for a higher relative density, was adopted in this research. The heating time was 70 s, the holding time was 180 s in total, and the voltage was 6.0 V. The current was conducted and broken alternately during the holding stage, where the on-off ratio was 1 s:1.2 s.

Structure Characterization and Mechanical Testing
The microstructure of the composites was observed by means of optical microscopy (OM, GX71, Olympus, Tokyo, Japan) and scanning electron microscopy (SEM, JSM-6510A, JEOL, Tokyo, Japan). The distribution of elements, such as Fe, Ti, Si, and Al, were analyzed using an energy-dispersive X-ray spectrometer (EDXS, INCA 25X-Max50, Oxford, UK) mounted on the SEM. Meanwhile, phase analysis of the as-mixed powders and sintered samples was performed via X-ray diffraction (XRD, Smartlab 9, Rigaku, Tokyo, Japan) observations with Cu Kα radiation at 40 kV and 40 mA. Tensile tests were performed via an electronic universal testing machine (AG-XPLUS1000KN, Shimadzu, Kyoto, Japan) at room temperature with a crosshead separation rate of 0.3 mm/min. The specimens were machined into a dumbbell shape with a length of 60 mm, the gauge section was 25 mm and Φ5 mm, and the clamping parts had a size of nearly 17.5 mm and Φ8 mm at each end. The relative density of the sintered samples was tested using the Archimedes method with a density determination kit (OHAUS, Parsippany, NJ, USA) and Vickers hardness was measured using a digital Vickers hardness tester (DVH, HVS-1000A, Huayin, Laizhou, China) with a load of 200 gf for 15 s. Each relative density was tested more than three times to ensure the repeatability and reliability of the data.

Analysis of Mixed Powders
The mixed powders were ball-milled via the process introduced in Section 2.1 and the micro-morphologies of the mixed powders after ball-milling are shown in Figure 1. It can be seen that most of the iron powders were approximate ellipsoid and the reinforcements were uniformly distributed. No obvious particle agglomerating or iron powder breakage could be observed. According to Figure 1, no obvious size change happened during the ball milling. Most of the reinforcing agents were adsorbed onto the surface of the iron powder or embedded into them. Normally, SiC can be embedded in the iron powders because of its higher hardness and Ti 3 AlC 2 can be adsorbed on the surface of the iron powders (see Figure 1g,h). Meanwhile, a few individual SiC and Ti 3 AlC 2 particles were seen, which means that an appropriate ball milling process was chosen. Meanwhile, a phase analysis was carried out via XRD, where only Fe, SiC, and Ti 3 AlC 2 could be found according to Figure 1i. Thus, we are sure that there was no new phase formed during the milling process.

Microstructure and Phase Components of the IMCs
The distribution of the reinforcing particles in the iron matrix was observed using OM, where the microstructure is shown in Figure 2. The density of the reinforcing particles was similar under the same particle content and more reinforcing particles appeared in the sample with a higher particle content, i.e., the density in Figure 1a-c was 14.3-15.4% (area percentage) and the corresponding value in Figure 1d-f is 18.3-19.2%. In the samples, SiC exited in the form of granular particles with a size of ~10 μm (Figure 2a,d) and was dispersed randomly throughout the matrix, which is consistent with adding particles. There were distinct boundaries between the matrix and the SiC, which means a weak interface reaction [5,9]. Irregular-shaped islands could be seen in the samples with Ti3AlC2 (marked by red arrows in Figure 2b,c,e,f), which could have been caused by the decomposition of Ti3AlC2 (confirmed later). In addition, some decomposing products with a chain shape were also found in Figure 2b,c,e,f; the reason for this could be that the decomposing products were smaller and hence filled the gaps between iron powders easier under a certain pressure in the sintering process. In Figure 2c,f, both granular SiC and products decomposed by Ti3AlC2 can be observed.

Microstructure and Phase Components of the IMCs
The distribution of the reinforcing particles in the iron matrix was observed using OM, where the microstructure is shown in Figure 2. The density of the reinforcing particles was similar under the same particle content and more reinforcing particles appeared in the sample with a higher particle content, i.e., the density in Figure 1a and was dispersed randomly throughout the matrix, which is consistent with adding particles. There were distinct boundaries between the matrix and the SiC, which means a weak interface reaction [5,9]. Irregular-shaped islands could be seen in the samples with Ti 3 AlC 2 (marked by red arrows in Figure 2b,c,e,f), which could have been caused by the decomposition of Ti 3 AlC 2 (confirmed later). In addition, some decomposing products with a chain shape were also found in Figure 2b,c,e,f; the reason for this could be that the decomposing products were smaller and hence filled the gaps between iron powders easier under a certain pressure in the sintering process. In Figure 2c,f, both granular SiC and products decomposed by Ti 3 AlC 2 can be observed. Comparatively speaking, it could be speculated that SiC and Ti3AlC2 presented different behaviors in the sintering process. SiC remained in the microstructure after sintering, while Ti3AlC2 could decompose according to the morphological features. In order to verify the behavior of the SiC and Ti3AlC2 during the sintering, an XRD test was carried out. According to the XRD analysis results in Figure 3, no trace of Ti3AlC2 could be detected in the samples with Ti3AlC2, indicating the complete decomposition of Ti3AlC2 in this sintering condition. Compared with the XRD results in Figure 1, it can be known that no new phase appeared during both the ball-milling and sintering in the SiC case; however, Ti3AlC2 decomposed during the sintering process, although there was no new phase formed during the ball-milling. SiC and TiCx were the main phases in the sintered samples, which means that SiC was stable in the iron matrix and Ti3AlC2 decomposed to TiCx during the sintering process. Because the solubility limit of Al in Fe is nearly 20 at.%, no new phase between Fe and Al was detected, and this conclusion was true for all the samples prepared in our research. According to the enlarged range of 43-45° (2θ) in Figure 3, the 2θ locations of diffraction peaks for the iron matrix shifted to lower 2θ angles in the samples with Ti3AlC2. According to the Bragg formula, the 2θ displacement shifting to lower Bragg angles indicates an increase in distance between adjacent lattice planes, which can be ascribed to the distortion of the lattice due to the incorporation of entire Al atoms derived from Ti3AlC2 phases into the iron matrix lattice. The results agree well with previous studies showing that Al diffuses out from Ti3AlC2 to form an Fe (Al) solid solution and TiCx, with a theoretical composition of TiC0.625, which appears when the temperature exceeds 763.1 °C [24]. Comparatively speaking, it could be speculated that SiC and Ti 3 AlC 2 presented different behaviors in the sintering process. SiC remained in the microstructure after sintering, while Ti 3 AlC 2 could decompose according to the morphological features. In order to verify the behavior of the SiC and Ti 3 AlC 2 during the sintering, an XRD test was carried out. According to the XRD analysis results in Figure 3, no trace of Ti 3 AlC 2 could be detected in the samples with Ti 3 AlC 2 , indicating the complete decomposition of Ti 3 AlC 2 in this sintering condition. Compared with the XRD results in Figure 1, it can be known that no new phase appeared during both the ball-milling and sintering in the SiC case; however, Ti 3 AlC 2 decomposed during the sintering process, although there was no new phase formed during the ball-milling. SiC and TiC x were the main phases in the sintered samples, which means that SiC was stable in the iron matrix and Ti 3 AlC 2 decomposed to TiC x during the sintering process. Because the solubility limit of Al in Fe is nearly 20 at.%, no new phase between Fe and Al was detected, and this conclusion was true for all the samples prepared in our research. According to the enlarged range of 43-45 • (2θ) in Figure 3, the 2θ locations of diffraction peaks for the iron matrix shifted to lower 2θ angles in the samples with Ti 3 AlC 2 . According to the Bragg formula, the 2θ displacement shifting to lower Bragg angles indicates an increase in distance between adjacent lattice planes, which can be ascribed to the distortion of the lattice due to the incorporation of entire Al atoms derived from Ti 3 AlC 2 phases into the iron matrix lattice. The results agree well with previous studies showing that Al diffuses out from Ti 3 AlC 2 to form an Fe (Al) solid solution and TiC x , with a theoretical composition of TiC 0.625 , which appears when the temperature exceeds 763.1 • C [24].
In order to further explore the reactions between the reinforcing particles and the iron matrix, an EDS analysis was carried out in the (Ti 3 AlC 2 + SiC)/Fe composites. According to the EDS results in Figures 4 and 5, it can be known that SiC was found, which agreed well with the OM observations and XRD results in Figures 2 and 3. There was no reaction between the iron matrix and SiC, and similar results were also found in other kinds of metal-based materials reinforced by SiC [12][13][14][15][16], which means SiC is a stable reinforcer. As to Figure 5b,d, it shows that Ti was detected in the reinforcing particle area; however, Al was found in the whole observation area. It is clear that Ti 3 AlC 2 decomposed according to the EDS map analysis results. This may be contributed to the diffusion relationship between Fe and Al, i.e., Al escaped from Ti 3 AlC 2 and dissolved into the matrix and Fe near the particle could permeate into the Ti 3 AlC 2 grains through the vacancy left by Al. A Materials 2021, 14, 2453 6 of 12 similar transformation was observed in a Cu-Ti 3 AlC 2 system at elevated temperatures in which the Al de-intercalated from Ti 3 AlC 2 along the (0001) basal plane to form a Cu (Al) solid solution [31]. Furthermore, in an Inconel718-Ti 2 AlC system, the Ti 2 AlC precursor completely transformed into an ultrafine TiC particulate via the dissolution of Al in the Ni matrix [25]. The decomposition reaction mechanisms of Ti 3 AlC 2 in iron can be described as follows [24]: Materials 2021, 14, 2453 In order to further explore the reactions between the reinforcing particles iron matrix, an EDS analysis was carried out in the (Ti3AlC2 + SiC)/Fe composites. ing to the EDS results in Figures 4 and 5, it can be known that SiC was found, which well with the OM observations and XRD results in Figures 2 and 3. There was no between the iron matrix and SiC, and similar results were also found in other metal-based materials reinforced by SiC [12][13][14][15][16], which means SiC is a stable re As to Figure 5b,d, it shows that Ti was detected in the reinforcing particle area; h Al was found in the whole observation area. It is clear that Ti3AlC2 decomposed ac to the EDS map analysis results. This may be contributed to the diffusion rela between Fe and Al, i.e., Al escaped from Ti3AlC2 and dissolved into the matrix and the particle could permeate into the Ti3AlC2 grains through the vacancy left by A ilar transformation was observed in a Cu-Ti3AlC2 system at elevated tempera which the Al de-intercalated from Ti3AlC2 along the (0001) basal plane to form a solid solution [31]. Furthermore, in an Inconel718-Ti2AlC system, the Ti2AlC p completely transformed into an ultrafine TiC particulate via the dissolution of A Ni matrix [25]. The decomposition reaction mechanisms of Ti3AlC2 in iron can scribed as follows [24]: Ti3AlC2 + Fe → TiC0.625 + Fe (Al) As a result, in situ TiCx formed during the sintering process, which is consist the XRD analysis results and caused the morphological change of adding partic sintering (Figure 2b,c,e,f).  In order to further explore the reactions between the reinforcing particles and the iron matrix, an EDS analysis was carried out in the (Ti3AlC2 + SiC)/Fe composites. According to the EDS results in Figures 4 and 5, it can be known that SiC was found, which agreed well with the OM observations and XRD results in Figures 2 and 3. There was no reaction between the iron matrix and SiC, and similar results were also found in other kinds of metal-based materials reinforced by SiC [12][13][14][15][16], which means SiC is a stable reinforcer. As to Figure 5b,d, it shows that Ti was detected in the reinforcing particle area; however, Al was found in the whole observation area. It is clear that Ti3AlC2 decomposed according to the EDS map analysis results. This may be contributed to the diffusion relationship between Fe and Al, i.e., Al escaped from Ti3AlC2 and dissolved into the matrix and Fe near the particle could permeate into the Ti3AlC2 grains through the vacancy left by Al. A similar transformation was observed in a Cu-Ti3AlC2 system at elevated temperatures in which the Al de-intercalated from Ti3AlC2 along the (0001) basal plane to form a Cu (Al) solid solution [31]. Furthermore, in an Inconel718-Ti2AlC system, the Ti2AlC precursor completely transformed into an ultrafine TiC particulate via the dissolution of Al in the Ni matrix [25]. The decomposition reaction mechanisms of Ti3AlC2 in iron can be described as follows [24]: As a result, in situ TiCx formed during the sintering process, which is consistent with the XRD analysis results and caused the morphological change of adding particles after sintering (Figure 2b,c,e,f).   After the tensile test, an analysis of the characteristics of the particles on the fracture surfaces was carried out. Typical microstructures with a 20% particle content can be seen in Figure 6, which illustrates the principally brittle morphology in all the samples, although small dimples appeared on the fracture surfaces due to the iron matrix deformation features. Figure 6a shows that both the SiC and TiCx particles were dispersed on the fracture surface. According to the surface morphology and EDS analysis in Figure 6a,d,e, many TiCx particles were broken and most SiC particles were unbroken. During the tensile process, a "tear ridge" was formed by the plastic deformation around the particles and the particles were embedded in the surface in the form of "breakage" (most are TiCx) or "pull-out" (most are SiC) modes. It can be deduced that both kinds of particles served as the main contributors as load carriers when the fracture occurred, which means the reinforcing effect was achieved by the particles via a load transfer mechanism. As a result, in situ TiC x formed during the sintering process, which is consistent with the XRD analysis results and caused the morphological change of adding particles after sintering (Figure 2b,c,e,f).
After the tensile test, an analysis of the characteristics of the particles on the fracture surfaces was carried out. Typical microstructures with a 20% particle content can be seen in Figure 6, which illustrates the principally brittle morphology in all the samples, although small dimples appeared on the fracture surfaces due to the iron matrix deformation features. Figure 6a shows that both the SiC and TiC x particles were dispersed on the fracture surface. According to the surface morphology and EDS analysis in Figure 6a,d,e, many TiC x particles were broken and most SiC particles were unbroken. During the tensile process, a "tear ridge" was formed by the plastic deformation around the particles and the particles were embedded in the surface in the form of "breakage" (most are TiC x ) or "pull-out" (most are SiC) modes. It can be deduced that both kinds of particles served as the main contributors as load carriers when the fracture occurred, which means the reinforcing effect was achieved by the particles via a load transfer mechanism.   After the tensile test, an analysis of the characteristics of the particles on the fracture surfaces was carried out. Typical microstructures with a 20% particle content can be seen in Figure 6, which illustrates the principally brittle morphology in all the samples, although small dimples appeared on the fracture surfaces due to the iron matrix deformation features. Figure 6a shows that both the SiC and TiCx particles were dispersed on the fracture surface. According to the surface morphology and EDS analysis in Figure 6a,d,e, many TiCx particles were broken and most SiC particles were unbroken. During the tensile process, a "tear ridge" was formed by the plastic deformation around the particles and the particles were embedded in the surface in the form of "breakage" (most are TiCx) or "pull-out" (most are SiC) modes. It can be deduced that both kinds of particles served as the main contributors as load carriers when the fracture occurred, which means the reinforcing effect was achieved by the particles via a load transfer mechanism. It can be seen in Figure 6b that most of the SiC particles were unbroken and some ridges that formed via deformation around the particles can be seen, which means that the particles acted as a reinforcement, mainly by means of the "pull-out" mode. It can be concluded that decohesion occurred at the interfaces when the fracture strength in the particles exceeded the interfacial strength. Meanwhile, some small pores and cracks whose surrounding matrix did not deform were also observed, as shown in Figure 6b. This could have been caused by inadequate sintering. In Figure 6c, many TiCx particles are shown to be broken, which means the particles bore the load during the deformation. It is reported that the fracture mode depends on the relative strength of the interface and the reinforcing particles [30] in composites. The fracture of the particles occurred in this work, suggesting that the interfacial strength in the new composites was so high that it exceeded the threshold stress of TiCx particles for fracture. Thus, it can be concluded that the in situ TiCx composites had strong interfacial bonding forces, which resulted in a cleavage fracture of in situ TiCx particles rather than a "pull-out" fracture at the interfaces between the in situ TiCx particles and the iron matrix.
According to Figure 6a-c, the difference in the particle morphology could be attributed to the strength of the particle and its combination with the iron matrix. A weaker strength and firm bond would cause a breakage, such as in the case of the TiCx particles. As to the SiC particles, a "pull-out" effect means a higher strength and weaker bond with the matrix. Figure 7 shows the relative density of samples with different particle types and contents. It can be seen that the relative density decreased with an increasing particle content in the samples that were reinforced only by SiC (from 95 to 93%). In the cases of samples that were created by adding Ti3AlC2, the relative densities were high and up to 98%. The reason was that the heat mainly came from the joule heat produced by the current through the iron powders. With the increasing content of reinforcing particles, the electrical resistance of the samples that were reinforced only by SiC decreased and the heating effect became weak. In contrast, Ti3AlC2 has a lower electrical resistance and thus a better sintering effect can be achieved. Meanwhile, the worse sintering effect means more sintering defects, such as pores, which can be seen in Figure 6b [5]. It can be seen in Figure 6b that most of the SiC particles were unbroken and some ridges that formed via deformation around the particles can be seen, which means that the particles acted as a reinforcement, mainly by means of the "pull-out" mode. It can be concluded that decohesion occurred at the interfaces when the fracture strength in the particles exceeded the interfacial strength. Meanwhile, some small pores and cracks whose surrounding matrix did not deform were also observed, as shown in Figure 6b. This could have been caused by inadequate sintering. In Figure 6c, many TiC x particles are shown to be broken, which means the particles bore the load during the deformation. It is reported that the fracture mode depends on the relative strength of the interface and the reinforcing particles [30] in composites. The fracture of the particles occurred in this work, suggesting that the interfacial strength in the new composites was so high that it exceeded the threshold stress of TiC x particles for fracture. Thus, it can be concluded that the in situ TiC x composites had strong interfacial bonding forces, which resulted in a cleavage fracture of in situ TiC x particles rather than a "pull-out" fracture at the interfaces between the in situ TiC x particles and the iron matrix.

Properties of the IMCs
According to Figure 6a-c, the difference in the particle morphology could be attributed to the strength of the particle and its combination with the iron matrix. A weaker strength and firm bond would cause a breakage, such as in the case of the TiC x particles. As to the SiC particles, a "pull-out" effect means a higher strength and weaker bond with the matrix. Figure 7 shows the relative density of samples with different particle types and contents. It can be seen that the relative density decreased with an increasing particle content in the samples that were reinforced only by SiC (from 95 to 93%). In the cases of samples that were created by adding Ti 3 AlC 2 , the relative densities were high and up to 98%. The reason was that the heat mainly came from the joule heat produced by the current through the iron powders. With the increasing content of reinforcing particles, the electrical resistance of the samples that were reinforced only by SiC decreased and the heating effect became weak. In contrast, Ti 3 AlC 2 has a lower electrical resistance and thus a better sintering effect can be achieved. Meanwhile, the worse sintering effect means more sintering defects, such as pores, which can be seen in Figure 6b  Then, the hardness and strength, as important properties of wear-resisting materials, were tested and the results are shown in Figure 8. For the same volume content, samples reinforced by both SiC and TiCx had the highest hardness and strength, which were 550 HV and 720 MPa and 635 HV and 683 MPa on average, respectively. Both of these properties exhibit a hybrid reinforcement effect, i.e., samples reinforced by SiC and TiCx were better than samples with a single reinforcing agent. As to the effect of particle content, the IMCs with different reinforcing agents exhibited varied performance trends in our research. In the case of samples reinforced by SiC, the hardnesses and strengths were 450 HV and 600 MPa and 438 HV and 500 MPa on average, respectively, which showed a decrease with increasing content. For the samples reinforced by TiCx, the properties increased with a content increase, i.e., their values were 400 HV and 649 MPa and 475 HV and 670 MPa on average, respectively. With regard to the samples reinforced by both SiC and TiCx, the hardness increased and the strength decreased with increasing content. This interesting phenomenon was mainly determined by the characteristics of the fast resistance-sintering technology. During the sintering process, there are two critical factors contributing to the mechanical performance: the types of reinforcing particles and electrical conductivity. On the one hand, the improvement in hardness and strength requires stronger particles with a better load-bearing ability and higher content [8]. A load can be transferred from the matrix to the SiC and TiCx reinforcements, which is expected to produce high strength and hardness in the composites [11]. On the other hand, high Then, the hardness and strength, as important properties of wear-resisting materials, were tested and the results are shown in Figure 8. For the same volume content, samples reinforced by both SiC and TiC x had the highest hardness and strength, which were 550 HV and 720 MPa and 635 HV and 683 MPa on average, respectively. Both of these properties exhibit a hybrid reinforcement effect, i.e., samples reinforced by SiC and TiC x were better than samples with a single reinforcing agent. As to the effect of particle content, the IMCs with different reinforcing agents exhibited varied performance trends in our research. In the case of samples reinforced by SiC, the hardnesses and strengths were 450 HV and 600 MPa and 438 HV and 500 MPa on average, respectively, which showed a decrease with increasing content. Then, the hardness and strength, as important properties of wear-resisting materials, were tested and the results are shown in Figure 8. For the same volume content, samples reinforced by both SiC and TiCx had the highest hardness and strength, which were 550 HV and 720 MPa and 635 HV and 683 MPa on average, respectively. Both of these properties exhibit a hybrid reinforcement effect, i.e., samples reinforced by SiC and TiCx were better than samples with a single reinforcing agent. As to the effect of particle content, the IMCs with different reinforcing agents exhibited varied performance trends in our research. In the case of samples reinforced by SiC, the hardnesses and strengths were 450 HV and 600 MPa and 438 HV and 500 MPa on average, respectively, which showed a decrease with increasing content. This interesting phenomenon was mainly determined by the characteristics of the fast resistance-sintering technology. During the sintering process, there are two critical factors contributing to the mechanical performance: the types of reinforcing particles and electrical conductivity. On the one hand, the improvement in hardness and strength requires stronger particles with a better load-bearing ability and higher content [8]. A load can be transferred from the matrix to the SiC and TiCx reinforcements, which is expected to produce high strength and hardness in the composites [11]. On the other hand, high This interesting phenomenon was mainly determined by the characteristics of the fast resistance-sintering technology. During the sintering process, there are two critical factors contributing to the mechanical performance: the types of reinforcing particles and electrical conductivity. On the one hand, the improvement in hardness and strength requires stronger particles with a better load-bearing ability and higher content [8]. A load can be transferred from the matrix to the SiC and TiC x reinforcements, which is expected to produce high strength and hardness in the composites [11]. On the other hand, high electrical conductivity is also needed to generate sufficient joule heat for the sintering effect. For the case of adding only SiC, the joule heat will decrease with an increasing SiC content because of its high electrical resistance. Based on our previous results, the hardness and strength of the IMCs reinforced by SiC first increased and then decreased with an increasing SiC content, and the optimal content was 10% [5]. The electric resistance of Ti 3 AlC 2 was much lower than SiC, which meant that effective sintering could be obtained. Furthermore, an exothermic reaction was predominant in the process when the temperature was above 763.1 • C [24], which could also provide the energy required for sintering. Thus, the hardness and strength of samples supplemented with Ti 3 AlC 2 increased with increasing content when the content was 15-20%, as was the case in this research. TiC x leads to an inferior strengthening effect compared to SiC, as confirmed by the experimental data when the content is not more than 10%. When the content was 15-20% as was the case in this research, the strength and hardness of the samples supplemented with Ti 3 AlC 2 were higher than with SiC, which means that the particle reinforcement was determined by the combined effect of both the particle strength and electrical resistance, as mentioned above. Therefore, the addition of SiC ensured the strength of the IMCs. The addition of Ti 3 AlC 2 ensured that there was enough joule heat caused by the electrical current and strengthening of both particles and the solid solution. As a result, a hybrid strengthening feature caused by TiC x and SiC could be achieved using this sintering technology. Moreover, the strengthening mechanism based on the decomposition of Ti 3 AlC 2 has multiple effects. According to the first-principles calculation of sub-stoichiometric TiC x [33], the bulk modulus of relaxed TiC 0.625 is 226 GPa, which is much higher than that of Ti 3 AlC 2 (160 GPa). After the decomposition, there was a large amount of bulky TiC x , as seen in Figure 6, which could play the role of transferring the load in the composites. Meanwhile, the strength of the Fe (Al) solid solution could be better than the Fe matrix due to solution strengthening. In addition, the interfacial layer formed in this way provided a high-strength transient zone between the Fe matrix and TiC x , favoring the load transfer in the composite during deformation. As a result, a better interface bonding between the in situ TiC x and the matrix was expected because of the formation mechanism of TiC x discussed above, which could benefit the tensile strength and hardness.

Properties of the IMCs
According to Figure 9, the elongation of samples that were supplemented with Ti 3 AlC 2 was the highest, followed by samples with SiC + Ti 3 AlC 2 and the sample with SiC was the lowest with the same content, which means the elongation followed the rule of mixture. When reinforced by the same particle type, the plasticity of the IMCs became worse with an increase in the content. As a result, the plasticity of the IMCs also mainly relied on the particle content and electrical resistance, where a high content meant more interfaces between the particles and the matrix, inevitable agglomeration, and more sintering defects, such as pores and cracks. With a certain content, different particles meant varied electrical resistances of the samples, where a lower powder electrical resistance would produce a better sintering effect with fewer defects. electrical conductivity is also needed to generate sufficient joule heat for the sintering effect. For the case of adding only SiC, the joule heat will decrease with an increasing SiC content because of its high electrical resistance. Based on our previous results, the hardness and strength of the IMCs reinforced by SiC first increased and then decreased with an increasing SiC content, and the optimal content was 10% [5]. The electric resistance of Ti3AlC2 was much lower than SiC, which meant that effective sintering could be obtained. Furthermore, an exothermic reaction was predominant in the process when the temperature was above 763.1 °C [24], which could also provide the energy required for sintering. Thus, the hardness and strength of samples supplemented with Ti3AlC2 increased with increasing content when the content was 15-20%, as was the case in this research.
TiCx leads to an inferior strengthening effect compared to SiC, as confirmed by the experimental data when the content is not more than 10%. When the content was 15-20% as was the case in this research, the strength and hardness of the samples supplemented with Ti3AlC2 were higher than with SiC, which means that the particle reinforcement was determined by the combined effect of both the particle strength and electrical resistance, as mentioned above. Therefore, the addition of SiC ensured the strength of the IMCs. The addition of Ti3AlC2 ensured that there was enough joule heat caused by the electrical current and strengthening of both particles and the solid solution. As a result, a hybrid strengthening feature caused by TiCx and SiC could be achieved using this sintering technology. Moreover, the strengthening mechanism based on the decomposition of Ti3AlC2 has multiple effects. According to the first-principles calculation of sub-stoichiometric TiCx [33], the bulk modulus of relaxed TiC0.625 is 226 GPa, which is much higher than that of Ti3AlC2 (160 GPa). After the decomposition, there was a large amount of bulky TiCx, as seen in Figure 6, which could play the role of transferring the load in the composites. Meanwhile, the strength of the Fe (Al) solid solution could be better than the Fe matrix due to solution strengthening. In addition, the interfacial layer formed in this way provided a high-strength transient zone between the Fe matrix and TiCx, favoring the load transfer in the composite during deformation. As a result, a better interface bonding between the in situ TiCx and the matrix was expected because of the formation mechanism of TiCx discussed above, which could benefit the tensile strength and hardness.
According to Figure 9, the elongation of samples that were supplemented with Ti3AlC2 was the highest, followed by samples with SiC + Ti3AlC2 and the sample with SiC was the lowest with the same content, which means the elongation followed the rule of mixture. When reinforced by the same particle type, the plasticity of the IMCs became worse with an increase in the content. As a result, the plasticity of the IMCs also mainly relied on the particle content and electrical resistance, where a high content meant more interfaces between the particles and the matrix, inevitable agglomeration, and more sintering defects, such as pores and cracks. With a certain content, different particles meant varied electrical resistances of the samples, where a lower powder electrical resistance would produce a better sintering effect with fewer defects. Figure 9. The elongation of the as-prepared samples. Figure 9. The elongation of the as-prepared samples.
To sum up, we aimed to increase the content of reinforcing particles in IMCs prepared using the fast resistance-sintering technology in this study. Ti 3 AlC 2 , with excellent electrical conductivity and a feature of decomposition into TiC x at elevated temperatures, was chosen, together with SiC, to be added into an iron matrix. The present approach provides an effective route for fabricating IMCs that are reinforced by SiC and in situ TiC x particulates. The experimental results show that the addition of SiC and Ti 3 AlC 2 could achieve the hybrid strengthening effect and the IMCs products reinforced by SiC and TiC x , formed by the decomposition of Ti 3 AlC 2 , could be obtained. The successful preparation of IMCs based on the hybrid reinforcement mechanism provides an idea for the optimization of IMCs.

1.
IMCs reinforced by both SiC and TiC x were prepared successfully through the addition of SiC and Ti 3 AlC 2 particles with volume fractions of 15% and 20% via the fast resistance-sintering technology, where the relative density of the samples was up to 98%.

2.
The in situ formation of the TiC x from the decomposition of Ti 3 AlC 2 during sintering was confirmed based on the XRD and EDS analysis results. 3.
The hybrid reinforcing effect, i.e., the tensile strength and hardness of samples reinforced by the mixture of SiC and TiC x were better than using a single reinforcing agent with the same volume content, was achieved. The elongation of the samples reinforced by TiC x was the best, followed by SiC and TiC x , and those reinforced by SiC were the lowest, which means the elongation obeyed the rule of mixture.