Establishing the Relationship between Cutting Speed and Output Parameters in Belt Grinding on Steels, Aluminum and Nickel Alloys: Development of Recommendations

This paper presents the research results of one of the main technological parameters of belt grinding, i.e., the cutting speed while machining corrosion- and heat-resistant, structural carbon and structural alloy steels, aluminum, and heat-resistant nickel alloys. Experimental and analytical methods are used to establish the dependence of the output parameters of surface belt grinding on the cutting speed and tool characteristics. An analytical model, considering the physical and mechanical properties of the grinding belt (strength depending on the base and bond; the thermal conductivity; the type of grinding operation) and the machined material, is created to determine the belt grinding speed. The output parameters, such as the arithmetic mean of the surface roughness (Ra) and the material removal rate (MRR) during the belt grinding of steels, heat-resistant and light alloys, have been studied. Based on the empirical dependencies of the belt grinding parameters, the model was developed for the selection and setting of the cutting speed of belt grinding for the aforementioned alloys, taking into account the type of operation, the type of the machined material, and the main characteristics of the sanding belt.


Introduction
The use of abrasive tools on a flexible base, including grinding belts, in leading industries (aerospace [1], machinery [2,3], automotive [4], etc.) is significant and accounts for about 40% of the total volume of abrasive tool use. Cloth grinding belts are most widely used, with a prevalence of up to 80% [5,6]. The most important precision parameter for belt grinding is surface roughness. Wang et al. [7] evaluated grain wear by the parameters of 3D surface roughness Sz (maximum height), Sdq (root-mean-square gradient) and Spc (arithmetic mean peak curvature) for dry belt grinding on AISI52100 hardened steel. Luo et al. [8] studied the influence of the grinding force, grinding speed, feed rate, and grain size on the surface roughness during the belt grinding of a titanium alloy. Li et al. [9] obtained the optimal values of surface roughness and material removal rate (MRR) for the belt grinding of 45 steel. Xie et al. [10] proposed a method for predicting and modeling the topography of a grinding surface based on a graphics processor (GPU). Van Gorp et al. [11] • To study and establish the dependences on the cutting speed of grinding belts and the most widely used characteristics in metalworking; • To develop and select the resulting surface roughness and material removal rate, reflecting the influence of the cutting speed on grinding different alloys with cloth grinding belts; • To develop recommendations for the selection and setting of the cutting speed during metalworking with cloth grinding belts.

Theoretical Provisions
Belt grinding in abrasive machining holds a specific place. The kinematics and dynamics of abrasive machining with grinding belts, and the accompanying physical phenomena, occupy an intermediate position between grinding with abrasive (i.e., hard, almost non-deformable) wheels and machining with loose abrasive [19] (see Table 1).
A distinctive feature of grinding belts is that during the cutting process, their design and properties provide for a significant elastic movement of abrasive grains from their static position in a direction perpendicular to the working surface of the tool. Due to the flexibility of grinding belts during machining, it is often impossible to preset a certain cutting depth, such as, for example, when grinding with abrasive wheels on a ceramic or bakelite bond. The necessary cutting conditions are created by setting the correct machining modes and, first of all, the main technological parameter-the cutting speed [19]. In studies of the grinding process, a significant inconsistency in the information on the selection of technological parameters of the grinding of steels and alloys, including the selection of the cutting speed, was observed. In [16,20], the recommended speed of grinding stainless steels is 17.5-25 m/s for roughing and 20-29 m/s for finishing; in [21], the recommended speed is 10-25 m/s for roughing and 0.5 m/s for finishing. In [22], identical speeds of 20-35 m/s are recommended for grinding heat-resistant steels, aluminum alloys, and hardened steels. In [9], a grinding speed of 3-9 m/s is proposed for belt grinding of steel 45.
Abrasive belts, made of new grinding materials (Cubitron [23], Cubicut [24], Alundum [25,26], etc.) with wear-resistant bonds and new polyester bases, allowing one to bring belt grinding closer to milling, are widely advertised. The main methodological provisions for the selection of the quality content of the indicators necessary to assess the performance properties of the grinding belt are given in [19,27]. The methodology includes taking into account the main factors, namely the grinding scheme, the type of machined material, the type of belt grinding stage, the parameters of the characteristics of the grinding belt, and the parameters of the grinding mode. The indicators are given for a unit of the belt's working surface (or the contact between the belt and the workpiece), making the output parameters comparable.
When developing output parameters, the selected indicators were differentiated by the designation of the tool to correctly reflect the physical essence of belt grinding. Thus, the assessment of the operating properties of the tool for the roughing and finishing operations, and for polishing, were differentiated based on the requirements for these operations, as the main purpose of roughing is to remove the allowance in the optimum minimum time. The main purpose of finishing and polishing is to achieve the required surface quality in the optimum minimum time. On this basis, we selected indicators per the type of operation.
The physical laws of abrasive machining established by Korchak are reflected in the analytical relationship between the output parameters and the volume of the material removed when machining a workpiece (Q mach ) [28]: where: P y is the cutting force directed along the normal to the machinable surface; v c is the cutting speed; τ is the time of machining; σi is the stress intensity in the shear zone of the material being machined (the stress intensity is a function of the strain intensity, ε, the strain rate, . ε, and the temperature, T 0 , of the material-σ i = f ε, . ε, T 0 ) [29,30]; K 1 and K 2 are the coefficients taking into account the geometry of the abrasive grains; f (τ) is the actual contact area between the tool and the workpiece, which changes during machining.
It follows from Formula (1) that the process of material removal is a function of the radial force, the cutting speed, the characteristics of the tool, and the machinable material. That is, the first requirement for the indicators is met if they reflect such basic indicators as material removal, the tool durability (and wear), and the limiting parameters: the cutting speed and the quality of machining. The second requirement for the indicators is met if the formulas take into account the dominant factors and the parameters, given the operating conditions of the tool. That is, to ensure the comparability of the indicators, it is necessary to have a unit of contact and make them speed-specific. The complex of indicators of the grit paper and the belt for roughing and finishing operations include comparable quantitative characteristics of machining, which reflect the high-speed interaction of contacting surfaces; for example, the reduced cutting ability (performance index) (q Per ) [19,27,31]. The physical meaning of the characteristic is q Per stock removal (materials rate removal (MRR)) from the workpiece per unit of work, which is given by the formula: where: q i is the material removal over the i-th grinding period; P c is the force of clamping the tool to the workpiece. To ensure the comparability of the indicators of the tool processes parameters for the pressure, the workpiece speed, the characteristics of the machinable workpiece, and the initial roughness, were investigated. Many influencing factors affect the results of the grinding operation. In this study, several of those factors have been selected, namely: the grinding scheme (surface belt grinding with a contact roller), the type of material being processed (steels, aluminum and nickel alloys used in the same type of mechanical engineering operations and other leading industries), the type of processing (preliminary and the final allowance), parameters of the characteristics of the sanding skin of the belt (grain size, bond, base, and abrasive material), parameters of the grinding mode (clamping force of the tool and workpiece, belt speed, workpiece speed, etc.). The methodological provisions of the work were tested in laboratory conditions on an experimental stand, simulating manufacturing conditions. Approximate experimental dependences were obtained, recommendations were developed depending on the above parameters. Production tests were carried out to validate the established dependencies and recommendations. The convergence of production and laboratory tests has been determined.

Experimental Details
The grinding belts were tested with operations according to the belt grinding scheme most common for machining-a surface belt grinder with a contact roller (see Figure 1). The experiments were carried out on a cloth sanding belt of the most widely used characteristics with a natural and synthetic bond when grinding metals of different machinability set in [27]. The experiment used a range of grinding speeds limited by the strength of the belt and reasonable durability. The restrictions allowed the application of the following full factorial experiment (FFE) method: where: N is the number of experiments; q y is the number of levels; k is the number of factors. The design matrix for the selected case of FFE = 2 3 is presented in Table 2.   wos-vertical oscillation frequency.
The design matrix for the selected case of FFE = 2 3 is presented in Table 2.

Experiment Number
The transition from the code expression of the factor to the natural value of the i-th factor (Xn) is set by the formula [19]: where: is the natural value of the factor at the zero level; is the code value of the ith factor; is the natural value of the variation interval. For the experimental studies, an IS-78 model stand (Russia, Chelyabinsk, ChOZ plant (Chelyabinsk Experimental Plant)), designed based on an upgraded 3110M circular grinder (Tbilisi Grinding Machine Plant, Tbilisi, Georgia)), was used (see Figure 1). The contact length depends on the machinability group, the type of machining (primary machining or finishing), the material, and the type The transition from the code expression of the factor to the natural value of the i-th factor (X n ) is set by the formula [19]: where: X 0 is the natural value of the factor at the zero level; X i is the code value of the i-th factor; δ is the natural value of the variation interval. For the experimental studies, an IS-78 model stand (Russia, Chelyabinsk, ChOZ plant (Chelyabinsk Experimental Plant)), designed based on an upgraded 3110M circular grinder (Tbilisi Grinding Machine Plant, Tbilisi, Georgia)), was used (see Figure 1). The contact length depends on the machinability group, the type of machining (primary machining or finishing), the material, and the type of contact roller (grooved, smooth). A grinding belt was a cloth-based grit paper made of 15A Brown Aluminum Oxide with F60 grain size on a synthetic bond as per GOST 27181 (Russian Standard). The experimental studies provided for grinding materials of different groups, including cast aluminum alloy AK5M2/AL3V (an analog of A319.0) as per GOST 1583, structural alloy steel 30KhGSN2/30KhGSNA as per GOST 1583, structural carbon steel 45 (an analog of AISI 1045) as per GOST 1050, corrosion-resistant and heat-resistant stainless steel Kh18N10T (an analog of AISI 321) as per GOST 5632, and heat-resistant nickel alloy KHN77TYUR (an analog of AISI 321) as per GOST 5632. Table 3 shows the chemical composition and physical and mechanical properties of these alloys [27]. The experimental study of the belt operation depending on the cutting speeds was carried out in the range of 9-35 m/s. The tests were carried out with a constant radial force, at pressures of 0.2, 0.4, and 0.8 MPa, when machining materials with a large machinability difference: steels 45, 30 KhGSN2, and Kh18N10T; alloys AK5M2 and KhN77TYuR. The following conditions were used in the experiment: the vertical oscillation frequency (ω os = 200 rpm), the longitudinal feed rate (v s = 0.058 m/s), and the oscillation value (A os = 3 mm). The roughness of the machined surface (arithmetic mean deviation of the assessed profile R a ) was measured using a surface roughness profilometer with a unified electronic AP system, model 263 (Proton JSC, Orel, Russia). An analysis of the data allowed showed that the performance index (cutting ability) q Per , mm 3 /min for the durability period is higher at v c = 35 m/s, but the grinding belt loses its cutting properties faster than at a speed of 25 m/s. The performance index q Per at a machining speed v c = 25 m/s is higher than when grinding at a speed v c = 35 m/s. Besides, as shown by the analysis, the highest achieved surface roughness corresponds to the lowest grinding speeds. A comparison of the experimental dependences of q Per overtime for the grinding belts on C and M bonds showed that the dependences of q Per for the grinding belts with C bonds have a flatter arrangement, are longer, and reach higher values. These indicators are explained by the stronger retention of the abrasive grain by the synthetic C bond and, therefore, during grinding, the abrasive grains can work for longer, and the belt loses its performance mainly due to the dulling of the abrasive layer. Figure 3 illustrates changes in the material removal rate (MRR) depending on the grinding speed (at a pressure of 0.4 MPa) of various materials with the 14A25C belt. The results indicated that an increase in the cutting speed leads to an increase in the number of the grain contacts with the machinable surface per unit of time, and to an increase in the MMR. When grinding different metals, the maximum MRR is observed at the highest tested speed of 35 m/s (at pressures of 0.4 and 0.2 MPa) [27]. This is explained as follows: with an increase in the grinding speed, the cutting ability of the belt increases because more working grains take part in the material removal per unit of time [27,32,33]. A possible factor which is affecting the decrease in MRR of the belt at a grinding speed of 35.3 m/s could be the increased wear of the belt [34]. With an increase in the speed, there is a sharp increase in the specific loads on single grains, which wear out more quickly, and the wear on the binder also increases [3,35]. The M bond, being relatively softer (with lower hardness values (N max )), does not offer sufficient resistance to wear with increasing speed [36]. Table 4 gives the values of the output parameters determined during the testsmaterial removal rate (MRR, cm 3 /min), performance index (q Per , mm 3 /mJ), and tool wear (V B , g)-during the belt grinding of various materials at different cutting speeds (v c ). The data confirm the above dependences of the output parameters during belt grinding of various materials on the cutting speed. The changes in the surface roughness (Ra), when machining different materials at different cutting speeds, after the first grinding cycle (Ra 1 ) and after the n-th grinding cycle (Ra n ), are shown in Figure 4 and correspond to the changes in q: the worst roughness is obtained at the lowest speed (v c = 9.4 m/s), the best at the highest speed (v c = 35.3 m/s). The experimental dependences were obtained during grinding with a 14A25M belt and at a pressure of 0.2 MPa. The analysis showed that the influence of the belt speed on the roughness (Ra 1 and Ra n ) is significant and expressed Materials 2021, 14,1974 8 of 17 by a correlation dependence with a high correlation coefficient from νR = −0.94 ± 0.02 to νR = 0.97 ± 0.02, and is described by:

Results and Discussion
Ra n = a n − b n ·v c (6) profile Ra) was measured using a surface roughness profilometer with a unified electronic AP system, model 263 (Proton JSC, Orel, Russia). Figure 2 shows the change in the cutting ability (see Figure 2a) and roughness of the machined surface (see Figure 2b)   sible factor which is affecting the decrease in MRR of the belt at a grinding speed of 35.3 m/s could be the increased wear of the belt [34]. With an increase in the speed, there is a sharp increase in the specific loads on single grains, which wear out more quickly, and the wear on the binder also increases [3,35]. The M bond, being relatively softer (with lower hardness values (Nmax)), does not offer sufficient resistance to wear with increasing speed [36].  Table 4 gives the values of the output parameters determined during the tests-material removal rate (MRR, cm 3 /min), performance index ( , mm 3 /mJ), and tool wear ( g)-during the belt grinding of various materials at different cutting speeds ( ). The data confirm the above dependences of the output parameters during belt grinding of various materials on the cutting speed. The changes in the surface roughness ( ), when machining different materials at different cutting speeds, after the first grinding cycle ( ) and   Table 5 gives the values of the coefficients a 1 , a n , b 1 and b n in Formulas (5) and (6) for representatives of the material groups, depending on their machinability with a grinding belt (defined in [19]), and the correlation coefficients.

Results and Discussion
The dependences of the output parameters on the change in the grinding speed remain for the entire range of the tested pressures p = 0.    Table 5 gives the values of the coefficients , , and in Formulas (5) and (6) for representatives of the material groups, depending on their machinability with a grinding belt (defined in [19]), and the correlation coefficients. Table 5. Coefficients of the empirical function of the initial and final surface roughness depending on the cutting speed.  The experiments show that the tool durability decreases by 10-60%, depending on the characteristics of the belt grit paper and the machinable material, with a grinding speed 1.4 times above 25 m/s. When testing at speeds of over 35.3 m/s, depending on the material and the pressure, thermal damage and burnout of the natural glue occur due to the increased wear and a sharp increase in the temperatures in the contact zone. To differentiate groups of grit paper strength by the breaking strength, which changes with the grain size, in this study, the base of the grit paper was, first of all, technologically selected according to its grain size [37]. The processing of a significant amount of the experimental data obtained during the tests allowed us to derive an empirical formula:

Grade of Metal
where: a b and b b are the coefficients of the group of material machinability with a belt for roughing and finishing; N is the grain size. The coefficients a b and b b change depending on the material machinability group and the type of machining (roughing, finishing); the latter is determined by the size of the allowance (A), and depends on the change in N and the strength group of the grit paper. Table 6 gives examples of Formula (6) for each group of machinable materials and the machining type with the correlation coefficients of the function ρ = f (N). The correlation coefficients show the influence of N on v c and are in the range ρ = 0.92 ± 0.006. To develop recommendations for the belt grinding speed, we proceeded primarily from the physical and mechanical properties of the grinding belt (the strength depending on the base and bond) the thermal conductivity, the type of grinding operation, and the machinable material. An analysis of the experimental data made it possible to derive an empirical design model to determine the belt grinding speed (v c ) depending on these factors, represented by the following exponential function [37]: where, σ p is the tensile strength of the grinding belt, N/mm 2 , k v is an exponent taking into account the machinable material, the type of operation, the properties of the grit paper (bond type and thermal conductivity), depending on the base, the grain size, and the belt grinding speed.
The tensile strength of the grinding belt in the longitudinal direction (σ p ) (Formula (7)) formed eight groups for standard cloth bases, taking into account the data of national standards (GOST 5009, GOST 13344, GOST 27181), and is shown in Table 7. The error of approximating the set dependences is 3.3-5.7%, which is acceptable and simplifies the calculations. The permissible belt grinding speeds, v c , were taken as the basis to develop the recommendations. Figure 5 shows the sequence setting the speed of the grinding belt in the developed recommendations.
The block diagram in Figure 5 illustrates the process of choosing the speed of the sanding belt (v c , m/s) as a function of Y = f (X 1 ,X 2 ,X 3 ), where: X 1 -groups of the machined material (according to the machinability factor (Co), set in work [27]); X 2 -the type of machining determined by the size of the allowance P up to 1.00 mm and 0.05 mm; X 3strength groups of the grinding belt (see Table 6). The group of the processed material (X 1 ) and the type of processing (X 2 ), as well as the belt speed (v c , m/s), is determined for a specific belt characteristic, namely, with the set X 3 -the belt strength group (eight groups). At stage 5 of the block diagram, we obtain the belt speed Y = f (X 1 ,X 2 ,X 3 ) for the next type of processing X = X 1 − X 2 . In parts six to eight of the block diagram, we determine the belt speed (v c , m/s) for this group (X 1 ) and separately for each type of processing (X 2 ), depending on the specific characteristics of the belt, namely, with the set X 3 -belt strength group (≤8 groups). At stages 9-14, the transition to the determination of v c , m/s of the next group of processed material (X 1 = X 1 + 1) and for a certain type of processing (X 2 ) is carried out. At stage 15, we determine v c , in m/s, for the next type of processing (X 2 = 0.5), and also for each of the groups of the processed material (X 1 ≤ 5). So, for example, for X 1 (the third group of materials) and X 2 (preliminary grinding at X 3 -the first group of strength v c = 14.9 m/s), if X = X 1 − X 2 , we get v c = 19.8 m/s, and for the second group of strength X 3 = X 3 + 1, we get v c = 15.0 m/s and X = X 1 − X 2 is determined by v c = 20.0 m/s. The block diagram in Figure 5 illustrates the process of choosing the speed of the sanding belt (vc, m/s) as a function of Y = f(X1,X2,X3), where: X1-groups of the machined material (according to the machinability factor (Co), set in work [27]); X2-the type of machining determined by the size of the allowance P up to 1.00 mm and 0.05 mm; X3strength groups of the grinding belt (see Table 6). The group of the processed material (X1) and the type of processing (X2), as well as the belt speed (vc, m/s), is determined for a specific belt characteristic, namely, with the set X3-the belt strength group (eight groups). At stage 5 of the block diagram, we obtain the belt speed Y = f(X1,X2,X3) for the next type of processing X = X1 − X2. In parts six to eight of the block diagram, we determine the belt speed (vc, m/s) for this group (X1) and separately for each type of processing (X2), depending on the specific characteristics of the belt, namely, with the set X3-belt strength group (≤8 groups). At stages 9-14, the transition to the determination of vc, m/s of the next group of processed material (X1 = X1 + 1) and for a certain type of processing (X2) is carried out. At stage 15, we determine vc, in m/s, for the next type of processing (X2 = 0.5), and also for each of the groups of the processed material (X1 ≤ 5). So, for example, for X1 (the third group of materials) and X2 (preliminary grinding at X3-the first group of strength vc = 14.9 m/s), if X = X1 − X2, we get vc = 19.8 m/s, and for the second group of strength X3 = X3 + 1, we get vc = 15.0 m/s and X = X1 − X2 is determined by vc = 20.0 m/s. Figure 5. A block scheme of selecting the belt grinding speed: Y is the speed of the grinding belt v c , m/s; Y = f (X 1 ,X 2 ,X 3 ); X 1i are material machinability groups (k m ); X 2 is the type of machining (allowance up to 1 mm or 0.05 mm); X 3i is the belt strength groups (σ p ).

Summary
The research carried out allowed us to obtain the following results. The developed set of performance indicators, including those previously used in practice (material removed rate (MRR), tool life, roughness and wear) and those proposed in this work (material removed rate (MRR), reduced cutting ability (performance index), roughness for the first cycle and roughness for the n-th cycle) makes it possible to objectively evaluate the processing results of the belt grinding process. Significant statistical data of tests made it possible to derive an empirical model for calculating the speed of belt grinding from the grain size of the belt, as well as the group of metal machinability for roughing and finishing. Processing of statistical data on the dependence of the belt grinding speed on the physical and mechanical properties of the grinding belt, such as strength, depending on the base and bond, thermal conductivity, the type of grinding operation and the type of material being processed, made it possible to derive an empirical design model for determining the cutting speed of a tape from these factors in the form of an exponential function. Through the equations used for calculating the dependence of the cutting speed on the grain size of the tape, the type of operation, properties of the skin, and the type of bond and thermal conductivity, were obtained for five groups of machinability. The results of experimental studies revealed the presence of dependences of the main parameter of the grinding process-the cutting speed of the belts on the characteristics of the grinding paper, the type of material being processed, and the type of operation. The established dependencies and their approximation determined the mathematical models for calculating the function of the initial and final roughness of the machined surface on the grinding speed for each group of machinability of steels and alloys and the type of belt grinding.
The dependencies of the output parameters of the belt on the main parameter of belt grinding modes-the cutting speed-are complex but mainly have extreme ranges of values. The output parameters (operating time, cutting ability, etc.) are linked by a direct functional dependence with the grinding speeds (i.e., performance increases as speeds grow) to certain values, after which the increase stops. The roughness of the machined surface is inversely related to the grinding speed; the roughness decreases with an increase in the grinding speed.
The experiments established the maximum values of the output parameters at the optimal values of the grinding speed in combination with certain set test conditions.
The influence of the belt speed on the output parameters during grinding, depending on a combination of factors and developed recommendations for setting the grinding belt speed, was established. For rough grinding, the recommended belt speed is generally 20-30% lower than for finishing. With a decrease in the allowance, the recommended machining speed increases, which allows us to increase the productivity of the grinding and reduce the roughness of the machined surface, but belt wear also increases. The shape of the machinable workpiece also affects the change in the speed. It is recommended to grind flat workpieces at slightly lower speeds than cylindrical ones.
As a result of studying surface belt grinding, we developed recommendations for the belt speed based on the requirements for the type of operation and depending on the type of the material, to achieve the best output parameters and optimal combinations of material removal rate (MMR), belt wear, and the roughness of the machined surface.

Conclusions
The relevance of the work is justified by the aggravation of competition in market conditions, which requires manufacturers of machine-building products to look for reserves in order to increase production efficiency. The measures developed in this study are aimed at increasing the efficiency of the enterprise, namely, the operation of belt grinding, paying particular attention to the issue of choosing reasonable and rational technological conditions for their implementation. The successful solution of this problem allows the creation of a reserve for further increasing the technical and economic efficiency of manufacturing without additional labor-intensive and material costs.
As a result, the optimal main technological parameter of belt grinding-belt speedwas identified based on experimentally established dependences on real process factors.
An analytical model for determining the value of the belt grinding speed was created, taking into account the physical and mechanical properties of the grinding belt (the strength depending on the base and bond), thermal conductivity, the type of the grinding operation, and the machinable material.
Groups of values were formed for the tensile strength of the grinding belt in the longitudinal direction for standard cloth-based grit paper, taking into account national (Russian) standards, and they were included in the recommendations for the belt grinding speed.
The provisions for the calculation, selection, and application of the output parameters were determined to assess belt grinding. Based on the results, we collected the statistics of the output parameters according to the dependences on the cutting speed of the characteristics of the grinding belt, the type of machining, and the machinable material. The experimental studies determined the empirical dependences of the belt grinding speed for groups of steels and alloys with a grinding belt on the characteristics of the grinding belt, the type of machining. The error in approximating the dependences was 3.3-5.7%. We determined the significant influence of the belt speed on the roughness of the machined surface and described it by linear functions and the correlation dependence with a high correlation coefficient (from 0.94 ± 0.02 to 0.97 ± 0.02).
Based on these empirical dependences, we developed recommendations for the belt speed in ranges covering the most widely used grinding schemes (primarily, surface grinding), for the machinability groups of steels and alloys, the main characteristics of the tool, and the type of operation provided by the technical parameters of the equipment.
The recommendations for the belt speed for grinding and finishing allow us to guarantee the optimal performance of grinding operations while ensuring a specified surface quality under variable machining conditions.
The recommendations are of significant practical value and can be used at leading abrasive enterprises and enterprise consumers. Data Availability Statement: All data generated or analysed during this study are included in this article. Groups of the machined material

Conflicts of
The type of machining determined by the size of the allowance P up to 1.00 mm and 0.05 mm X 3 Strength groups of the grinding belt