Effect of TiO2 Concentration on Microstructure and Properties of Composite Cu–Sn–TiO2 Coatings Obtained by Electrodeposition

In this work, Cu–Sn–TiO2 composite coatings were electrochemically obtained from a sulfate bath containing 0–10 g/L of TiO2 nanoparticles. The effect of TiO2 particles on kinetics of cathodic electrodeposition has been studied by linear sweep voltammetry and chronopotentiometry. As compared to the Cu–Sn alloy, the Cu–Sn–TiO2 composite coatings show rougher surfaces with TiO2 agglomerates embedded in the metal matrix. The highest average amount of included TiO2 is 1.7 wt.%, in the case of the bath containing 5 g/L thereof. Composite coatings showed significantly improved antibacterial properties towards E. coli ATCC 8739 bacteria as compared to the Cu–Sn coatings of the same composition. Such improvement has been connected with the corrosion resistance of the composites studied by linear polarization and electrochemical impedance spectroscopy. In the bacterial media and 3% NaCl solutions, Cu–Sn–TiO2 composite coatings have lower corrosion resistance as compared to Cu–Sn alloys, which is caused by the nonuniformity of the surface.


Introduction
Bacterial infections and their complications cause a decline in the life quality and death of millions of patients around the world every year. The most common route of transferring pathogenic microorganisms is direct human contact with contaminated contact surfaces (fomites). That is an urgent problem in public places, for example, shopping centers, educational facilities, hospitals, and office buildings, since their microclimate promotes a rapid growth and transmission of microorganisms on metal handrails and doorknobs [1][2][3][4]. Moreover, many types of germs can survive on indoor surfaces for several days, with some of them being able to survive for longer than one month. In this regard, potentially contaminating surfaces must provide antibacterial and anticorrosive protection while maintaining high decorative and mechanical properties.

Electrodeposition of Composite Coatings
The electrochemical deposition of Cu-Sn-TiO 2 composite coatings was performed from a sulfuric acid bath of the composition listed in Table 1. All solutions were prepared with 18.2 MΩ cm deionized water (Polwater, Krakow, Poland) and reagents of chemically pure grade (Belreachim, Minsk, Belarus). The pH of the as-prepared electrolyte was <1. As a second phase, TiO 2 nanoparticles (Degussa aeroxide P25) were introduced into the electrolyte in amounts of 0, 1, 5 and 10 g/L. Hereafter, the coatings obtained from these electrolytes are labeled as Ti-0, Ti-1, Ti-5, and Ti-10, respectively. Figure 1 shows the scanning electron microscopy (SEM) image of the used TiO 2 powder with the particle sizes ranging from 30 to 50 nm. composition, physical-mechanical, antibacterial, and corrosion properties of the formed coatings was studied.

Electrodeposition of Composite Coatings
The electrochemical deposition of Cu-Sn-TiO2 composite coatings was performed from a sulfuric acid bath of the composition listed in Table 1. All solutions were prepared with 18.2 MΩ cm deionized water (Polwater, Krakow, Poland) and reagents of chemically pure grade (Belreachim, Minsk, Belarus). The pH of the as-prepared electrolyte was <1. As a second phase, TiO2 nanoparticles (Degussa aeroxide P25) were introduced into the electrolyte in amounts of 0, 1, 5, and 10 g/L. Hereafter, the coatings obtained from these electrolytes are labeled as Ti-0, Ti-1, Ti-5, and Ti-10, respectively. Figure 1 shows the scanning electron microscopy (SEM) image of the used TiO2 powder with the particle sizes ranging from 30 to 50 nm.  Before electrodeposition, as-prepared solutions were ultrasonically treated (power of 50 W) using an UP 200 Ht ultrasonic homogenizer (Hielscher Ultrasonics GmbH, Teltow, Germany) for 20 min to provide deagglomeration and better dispersion of TiO2 particles in the volume of the electrolyte. In the course of the deposition, the electrolyte was mechanically stirred every 5 min for 10 s (stirring rate 400 rpm). Cathodic deposition of coatings was performed in the potentiostatic mode at 20 °C. The deposition time varied depending on the applied potential to obtain coatings with a thickness of 10 μm. The values of the cathodic deposition potentials are indicated in the text of the contribution in the scale of a standard hydrogen electrode (SHE). A copper-foiled dielectric with a surface area of 8 cm 2 was used as the cathode and an M0 copper plate was used as the anode. The distance between the cathode and the anode was 40 mm. Before experiments, cathodes were chemically treated according to the State Standard GOST 9.305-84. The treatment Before electrodeposition, as-prepared solutions were ultrasonically treated (power of 50 W) using an UP 200 Ht ultrasonic homogenizer (Hielscher Ultrasonics GmbH, Teltow, Germany) for 20 min to provide deagglomeration and better dispersion of TiO 2 particles in the volume of the electrolyte. In the course of the deposition, the electrolyte was mechanically stirred every 5 min for 10 s (stirring rate 400 rpm). Cathodic deposition of coatings was performed in the potentiostatic mode at 20 • C. The deposition time varied depending on the applied potential to obtain coatings with a thickness of 10 µm. The values of the cathodic deposition potentials are indicated in the text of the contribution in the scale of a standard hydrogen electrode (SHE). A copper-foiled dielectric with a surface area of 8 cm 2 was used as the cathode and an M0 copper plate was used as the anode. The distance between the cathode and the anode was 40 mm. Before experiments, cathodes were chemically treated according to the State Standard GOST 9.305-84. The treatment included degreasing in the solution containing 15 g/L Na 2 CO 3 , 30 g/L Na 3 PO 4 ·12H 2 O, and 5 g/L Sintanol DS10 with further activation in 0.1 M H 2 SO 4 .
Cathodic polarization curves and chronopotentiograms in the studied electrolyte were recorded in a standard three-electrode glass electrochemical cell using an AUTOLAB PGSTAT302N potentiostat/galvanostat (Metrohm Autolab B.V., Utrecht, The Netherlands). The linear potential sweep rate during polarization measurements was 1 mV/s. The working electrode was a copper-foiled dielectric with an area of 1 cm 2 ; a silver/silver chloride was used as the reference electrode, and an M0 copper plate served as the counter electrode.

Morphology and Structural Analysis
The morphology and elemental composition of the formed coatings were determined using a JSM-5610 LV (JEOL Ltd., Tokyo, Japan) scanning electron microscope equipped with an EDX JED-2201 JEOL elemental analysis system. The recalculation of the mass content of titanium to the titanium dioxide was carried out according to the formula: where ω(TiO 2 ) is the mass content of titanium dioxide in the coating (wt.%); ω(Ti) is the weight content of titanium in the coating according to EDX data (wt.%); M(TiO 2 ) is the molar mass of TiO 2 (g/mol), and A(Ti) is the atomic mass of titanium (a. e. m.). The structural analysis of coatings was performed by X-ray diffraction (XRD) using a PANalytical Cubix X'Pert Pro X-ray (Malvern Panalytical B.V., Almelo, The Netherlands) diffractometer using CuKα radiation (λ = 1.5418 Å). Diffraction patterns were recorded at a scan rate of 2 deg/min with a 0.1 deg. step. The obtained diffraction patterns were processed using the Match! software and the COD (Crystallography Open Database) reference base.
The X-ray photoelectron spectroscopy (XPS) measurements were done using an ES-CALAB 220 XL XPS spectrometer (Thermo Fisher Scientific, Waltham, MA, USA) featuring a monochromatic Al Kα X-ray source (1486.6 eV). A pass energy of 20 eV was applied. The charge compensation was assured through low-energy electron and low-energy Ar+ ions bombardment of the sample, with the final peak calibration at adventitious carbon C1s (284.6 eV).

Antibacterial Performance
Antibacterial properties of the obtained coatings were determined using the classical Koch method by counting living bacteria colonies after their contact with the examined surfaces. The test cultures were the sanitary indicative Escherichia coli (E. coli) ATCC 8739. Before inoculation of the bacteria, the test samples were sterilized in ethanol (70%) for 1 h and then dried under UV irradiation. Overnight culture of E. coli was diluted to a concentration of~10 6 -10 7 CFU/mL and inoculated (50 µL) onto the surface of the studied samples. The samples were covered with a sterile film to ensure the spreading of the bacterial culture over the surface and incubated for 45 or 90 min. After incubation, the samples (with a film) were washed with 10 mL of saline solution containing Triton x-100 (0.001 vol.%). Undiluted wash liquid was plated on a solid medium (nutrient agar). The inoculations were incubated in such conditions for 24 h at a temperature of 30 • C, after which the colony-forming units were counted. All corrosion and antibacterial experiments reported in this paper were at least triplicated on independent samples.

Electrochemical Measurements
In electrochemical experiments, a platinum mesh was used as the counter electrode and a saturated silver/silver chloride electrode served as a reference. As a model corrosive medium, 3% NaCl solution and bacterial media were used. The composition of the bacterial media is provided in Table S3 in the Supplementary Information. The polarization curves of the obtained coatings were recorded in the potential range from −200 mV to +200 mV relative to the open-circuit potential (OCP). The electrochemical impedance spectroscopy (EIS) spectra were recorded at the OCP value in the frequency range from 10 5 to 10 -2 Hz, the ac potential amplitude of 10 mV, and 7 measured points per frequency decade. The consistency of the EIS data was evaluated using the Kramers-Kronig transformation procedure available in the potentiostat software. The analysis of the EIS spectra, selection of equivalent circuits, and fitting of their parameters were performed in the ZView 3.2c software.

Results and Discussion
3.1. Electrodeposition of Cu-Sn-TiO 2 Composite Coatings Figure 2 presents polarization curves of the copper electrode obtained in the studied electrolytes containing 0-10 g/L TiO 2 . The introduction of TiO 2 nanoparticles into the electrolyte leads to a shift of the polarization curves to the electronegative region. All the obtained polarization dependences can be divided into three areas. In the range of potentials from 0.30 to 0.00 V, only copper(II) ions are discharged at the cathode. When potentials more negative than 0.04-0.00 V are reached, the polarization curves show a monotonic increase in the current density, which is caused by the UPD of Sn. At potentials lower than −0.20 V, the slope of the current-voltage dependence changes, which is caused by the onset of the discharge of stannous ions under the overpotential deposition (OPD). The obtained polarization curves revealed that the introduction of TiO 2 particles into the studied bath leads to only slight inhibition of the discharge of copper(II) ions and a decrease in the overall rate (current density) of processes occurring on the electrode in the potential range from 0.00 to −0.20 V. curves of the obtained coatings were recorded in the potential range from −200 mV to +200 mV relative to the open-circuit potential (OCP). The electrochemical impedance spectroscopy (EIS) spectra were recorded at the OCP value in the frequency range from 10 5 to 10 -2 Hz, the ac potential amplitude of 10 mV, and 7 measured points per frequency decade. The consistency of the EIS data was evaluated using the Kramers-Kronig transformation procedure available in the potentiostat software. The analysis of the EIS spectra, selection of equivalent circuits, and fitting of their parameters were performed in the ZView 3.2c software. Figure 2 presents polarization curves of the copper electrode obtained in the studied electrolytes containing 0-10 g/L TiO2. The introduction of TiO2 nanoparticles into the electrolyte leads to a shift of the polarization curves to the electronegative region. All the obtained polarization dependences can be divided into three areas. In the range of potentials from 0.30 to 0.00 V, only copper(II) ions are discharged at the cathode. When potentials more negative than 0.04-0.00 V are reached, the polarization curves show a monotonic increase in the current density, which is caused by the UPD of Sn. At potentials lower than −0.20 V, the slope of the current-voltage dependence changes, which is caused by the onset of the discharge of stannous ions under the overpotential deposition (OPD). The obtained polarization curves revealed that the introduction of TiO2 particles into the studied bath leads to only slight inhibition of the discharge of copper(II) ions and a decrease in the overall rate (current density) of processes occurring on the electrode in the potential range from 0.00 to −0.20 V. The electrochemical deposition of copper and tin in sulfuric acid electrolytes occurs under the diffusion control of the discharge of copper(II) ions [20,21,30,35,40]. For this reason, a decrease in the cathodic current densities in the electrolytes containing TiO2 nanoparticles seen in Figure 2 can be due to the following reasons: The electrochemical deposition of copper and tin in sulfuric acid electrolytes occurs under the diffusion control of the discharge of copper(II) ions [20,21,30,35,40]. For this reason, a decrease in the cathodic current densities in the electrolytes containing TiO 2 nanoparticles seen in Figure 2 can be due to the following reasons:

Electrodeposition of Cu-Sn-TiO2 Composite Coatings
(i) according to the Guglielmi model of the electrochemical deposition of composite coatings [40], TiO 2 nanoparticles can physically adsorb on the electrode surface during electrolysis, thereby reducing the active electrode area involved in the electrochemical process. This leads to a decrease in the current response at an applied potential; (ii) since diffusion is the limiting stage of the discharge of copper(II) ions in acidic electrolytes, TiO 2 particles dispersed in the electrolyte could prevent diffusion and migration of copper and stannous ions from the bulk solution to the electrode surface.
To study the effect of TiO 2 nanoparticles on the galvanostatic deposition of Cu-Sn-TiO 2 coatings, chronopotentiograms of the copper electrode in the examined solutions were obtained at a cathodic current density of −0.015 A/cm 2 ( Figure 3). (i) according to the Guglielmi model of the electrochemical deposition of composite coatings [40], TiO2 nanoparticles can physically adsorb on the electrode surface during electrolysis, thereby reducing the active electrode area involved in the electrochemical process. This leads to a decrease in the current response at an applied potential; (ii) since diffusion is the limiting stage of the discharge of copper(II) ions in acidic electrolytes, TiO2 particles dispersed in the electrolyte could prevent diffusion and migration of copper and stannous ions from the bulk solution to the electrode surface.
To study the effect of TiO2 nanoparticles on the galvanostatic deposition of Cu-Sn-TiO2 coatings, chronopotentiograms of the copper electrode in the examined solutions were obtained at a cathodic current density of −0.015 A/cm 2 ( Figure 3). At the initial moment of deposition (from 1 to 2 s), the chronopotentiograms exhibit potential maxima corresponding to the overvoltage of the formation of the first copper clusters [20]. After reaching the maximum, the electrode potential gradually shifts to the electronegative region, which is caused by a progressive reduction of copper ions in the cathode interface. The subsequent plateau of the electrode potential indicates that copper ions discharge at the limiting diffusion current and the UPD of tin is initiated [20,41]. As the content of TiO2 nanoparticles in the electrolyte increases, the dependences shift to more negative potentials, which may indicate a decrease in the fraction of the current consumed to the discharge of copper(II) ions and subsequent increase in the partial current of the tin deposition. Therefore, this effect of TiO2 particles must be considered during electrodeposition under galvanostatic conditions, since increasing the electrode potential will lead to an increase in the tin content in the alloy. This may complicate a comparative assessment of the corrosion and antibacterial properties of Cu-Sn and Cu-Sn-TiO2 coatings.
To assess the effect of the TiO2 nanoparticles in the electrolyte on the microstructure and grain size of the formed coatings, electrolysis was carried out in the potentiostatic mode at a deposition potential of −0.05 V. At the initial moment of deposition (from 1 to 2 s), the chronopotentiograms exhibit potential maxima corresponding to the overvoltage of the formation of the first copper clusters [20]. After reaching the maximum, the electrode potential gradually shifts to the electronegative region, which is caused by a progressive reduction of copper ions in the cathode interface. The subsequent plateau of the electrode potential indicates that copper ions discharge at the limiting diffusion current and the UPD of tin is initiated [20,41]. As the content of TiO 2 nanoparticles in the electrolyte increases, the dependences shift to more negative potentials, which may indicate a decrease in the fraction of the current consumed to the discharge of copper(II) ions and subsequent increase in the partial current of the tin deposition. Therefore, this effect of TiO 2 particles must be considered during electrodeposition under galvanostatic conditions, since increasing the electrode potential will lead to an increase in the tin content in the alloy. This may complicate a comparative assessment of the corrosion and antibacterial properties of Cu-Sn and Cu-Sn-TiO 2 coatings.
To assess the effect of the TiO 2 nanoparticles in the electrolyte on the microstructure and grain size of the formed coatings, electrolysis was carried out in the potentiostatic mode at a deposition potential of −0.05 V. Figure 4 shows SEM images of the obtained coatings. Homogeneous fine-grained coatings were formed from the electrolyte without TiO 2 particles (Figure 4a). Obtained coatings have good adhesion to the substrate without visible delamination at the coating/substrate interface (cross-sectional images, Figure S1 in the Supplementary Information). The grain size of the formed alloy varies from 20 to 70 nm. The introduction of TiO 2 particles in the electrolyte did not significantly change the grain size of the metal matrix, however, it did noticeably change the microstructure (Figure 4b-d). It is clearly seen that many sphere-shaped features with sizes between 1 and 10 µm were formed on the surface of Ti-1, Ti-5, and Ti-10 coatings ( Figure S1 in the Supplementary Information). Nonuniform inclusions of 200-700 nm in size, which were not observed in the case of Cu-Sn coating, are also noticeable in the microstructure. An increase in the content of TiO 2 particles in the electrolyte resulted in higher inhomogeneity of the surface and an increased number of agglomerates in the alloy matrix. The formation of globular deposits could be ascribed either to theTiO 2 particles embed into the metal matrix and then covered by a next layer of the coating or to the negative effect of the second-phase particles on the current distribution over the electrode surface. Introduction of TiO 2 also decreased luster of the coatings but significantly improved their microhardness (Table S1 in the Supplementary Materials). Figure 4 shows SEM images of the obtained coatings. Homogeneous fine-grained coatings were formed from the electrolyte without TiO2 particles (Figure 4a). Obtained coatings have good adhesion to the substrate without visible delamination at the coating/substrate interface (cross-sectional images, Figure S1 in the Supplementary Information). The grain size of the formed alloy varies from 20 to 70 nm. The introduction of TiO2 particles in the electrolyte did not significantly change the grain size of the metal matrix, however, it did noticeably change the microstructure (Figure 4b-d). It is clearly seen that many sphere-shaped features with sizes between 1 and 10 μm were formed on the surface of Ti-1, Ti-5, and Ti-10 coatings ( Figure S1 in the Supplementary Information). Nonuniform inclusions of 200-700 nm in size, which were not observed in the case of Cu-Sn coating, are also noticeable in the microstructure. An increase in the content of TiO2 particles in the electrolyte resulted in higher inhomogeneity of the surface and an increased number of agglomerates in the alloy matrix. The formation of globular deposits could be ascribed either to theTiO2 particles embed into the metal matrix and then covered by a next layer of the coating or to the negative effect of the second-phase particles on the current distribution over the electrode surface. Introduction of TiO2 also decreased luster of the coatings but significantly improved their microhardness (Table S1 in the Supplementary Materials).  The point EDX analysis of the two characteristic morphology regions on the surface of Ti-1 coating is shown in Figure 5. The results confirmed that fine smooth areas of the surface are Cu-Sn alloy with the stacked granules being TiO 2 particles. a deposition potential of −0.05 V (region of Sn UPD). As expected from the selected electrodeposition mode (Figure 3), coatings have almost equal content of tin (11.3-11.5 wt.%) with the Ti-1 coating containing 10.8 wt.% of tin. The maximum average amount of TiO2 was observed in the Ti-5 coating (1.7 wt.%). It can be explained by higher agglomeration and, consequently, lower sedimentation stability of the electrolyte containing 10 g/L TiO2. However, we cannot exclude some variation of the TiO2 content in the bulk of the examined coatings.  The EDX element distribution maps over the surface of the electrodeposited composite coatings are shown in Figure 6. They illustrate that Cu and Sn are uniformly distributed over the surface regardless of the concentration of TiO2 particles in the electrolyte. During the electrodeposition process, TiO2 particles are embedded into the metal matrix as agglomerates with sizes varying from sub-to several microns.  Table 2 reports the EDX chemical composition of the coatings electrodeposited from the electrolytes with varying TiO 2 content. High-quality yellow coatings were formed at a deposition potential of −0.05 V (region of Sn UPD). As expected from the selected electrodeposition mode (Figure 3), coatings have almost equal content of tin (11.3-11.5 wt.%) with the Ti-1 coating containing 10.8 wt.% of tin. The maximum average amount of TiO 2 was observed in the Ti-5 coating (1.7 wt.%). It can be explained by higher agglomeration and, consequently, lower sedimentation stability of the electrolyte containing 10 g/L TiO 2 . However, we cannot exclude some variation of the TiO 2 content in the bulk of the examined coatings. The EDX element distribution maps over the surface of the electrodeposited composite coatings are shown in Figure 6. They illustrate that Cu and Sn are uniformly distributed over the surface regardless of the concentration of TiO 2 particles in the electrolyte. During the electrodeposition process, TiO 2 particles are embedded into the metal matrix as agglomerates with sizes varying from sub-to several microns. Figure 7 shows XRD patterns of the obtained coatings. As can be seen from the data obtained, the main reflections of the obtained coatings are shifted to smaller angles as compared to the pure Cu phase (JCPDS 4-368). This indicates an increase in the intercrystallite distance of the metal matrix due to the introduction of tin atoms into the copper crystal lattice. This shift was lower for the Ti-1 coating, as it has the lowest amount of tin ( Table 2). All coatings have the fcc crystal structure with the preferred orientation in (111) plane. The formation of a single-phase solid solution is consistent with our previous studies [20].  Figure 7 shows XRD patterns of the obtained coatings. As can be seen from the data obtained, the main reflections of the obtained coatings are shifted to smaller angles as compared to the pure Cu phase (JCPDS 4-368). This indicates an increase in the intercrystallite distance of the metal matrix due to the introduction of tin atoms into the copper crystal lattice. This shift was lower for the Ti-1 coating, as it has the lowest amount of tin ( Table 2). All coatings have the fcc crystal structure with the preferred orientation in (111) plane. The formation of a single-phase solid solution is consistent with our previous studies [20].

XRD and XPS Analysis
The XPS analysis was performed to analyze the modification of Cu-Sn surface chemistry through TiO2 embedding into the coating. The results of high-resolution XPS analysis recorded in the core-level binding energy range of Cu2p, Sn3d, and Ti2p spectra are summarized in Figure 8.
The recorded Cu2p spectra reveal complex copper chemistry, two peak doublets were used for the deconvolution process with Cu2p3/2 peaking at 932.7 and 934.1 eV, respectively. The primary of the two components, located at lower binding energies lies in the energy range characteristic of metallic copper and copper (i) oxides. To distinguish them further, the supplementary CuLMM Auger electron spectra were recorded with the kinetic energy peaking at 916.8 eV for both studied samples. These results suggest that Cu2O is the primary copper constituent within the discussed XPS spectra, confirming the proposed corrosion mechanism (see Equation (6)). The second Cu2p component is located at the binding energies typical for Cu 2+ and is most likely present in the form of Cu(OH)2, a conclusion drawn based on the peak binding energy value and characteristic shape of the Cu 2+ satellite features [42]. Interestingly, the addition of TiO2 does not significantly alter the Cu + :Cu 2+ ratio. The XPS analysis was performed to analyze the modification of Cu-Sn surface chemistry through TiO 2 embedding into the coating. The results of high-resolution XPS analysis recorded in the core-level binding energy range of Cu2p, Sn3d, and Ti2p spectra are summarized in Figure 8.
The recorded Cu2p spectra reveal complex copper chemistry, two peak doublets were used for the deconvolution process with Cu2p 3/2 peaking at 932.7 and 934.1 eV, respectively. The primary of the two components, located at lower binding energies lies in the energy range characteristic of metallic copper and copper (i) oxides. To distinguish them further, the supplementary Cu LMM Auger electron spectra were recorded with the kinetic energy peaking at 916.8 eV for both studied samples. These results suggest that Cu 2 O is the primary copper constituent within the discussed XPS spectra, confirming the proposed corrosion mechanism (see Equation (6)). The second Cu2p component is located at the binding energies typical for Cu 2+ and is most likely present in the form of Cu(OH) 2 , a conclusion drawn based on the peak binding energy value and characteristic shape of the Cu 2+ satellite features [42]. Interestingly, the addition of TiO 2 does not significantly alter the Cu + :Cu 2+ ratio.
The XPS data confirmed the presence of Ti 4+ species at the surface of the analyzed Cu-Sn-TiO 2 sample, through the appearance of Ti2p3/2 peak at approx. 458.4 eV. Furthermore, tin oxidation in line with Equation (3) was confirmed through identification of Sn 4+ Sn3d 5/2 peak at 486.6 eV. The addition of TiO 2 to the studied Cu-Sn coating did not alter tin surface chemistry, but, interestingly, a consequence was a higher surface Sn:Cu ratio (12.4% in the case of Cu-Sn-TiO 2 compared to 2.6% for Cu-Sn coating). This can suggest that the surface of composite coatings is enriched in the corrosion products of tin, which is anodic component in the Cu-Sn system. The detailed surface composition examined by XPS is summarized in Table S2 in the Supplementary Information.  Materials 2021, 14, 6179 10 of 18  The XPS data confirmed the presence of Ti 4+ species at the surface of the analyzed Cu-Sn-TiO2 sample, through the appearance of Ti2p3/2 peak at approx. 458.4 eV.  The XPS data confirmed the presence of Ti 4+ species at the surface of the analyzed Cu-Sn-TiO2 sample, through the appearance of Ti2p3/2 peak at approx. 458.4 eV.

Antibacterial Performance
The antibacterial activity of the studied coatings was determined relative to the sanitary indicative bacteria E. coli ATCC 8739. Stainless-steel coupons (AISI 304) were used as a reference. The results of the bacterial tests are summarized in Figure 9. The concentration of viable cells in the initial suspension was 9.8 × 10 6 CFU/mL. In the case of the reference sample, an increase in the number of bacteria colonies to 8.6 × 10 7 CFU/mL was observed after 45 min of the sample contact with the bacteria without UV treatment. This indicates that the stainless-steel surface provides favorable conditions for the reproduction of microorganisms. In turn, all obtained copper-based coatings showed pronounced antibacterial effect. The concentration of bacteria decreased by 1-2 orders of magnitude after 45 min of the contact with the Ti-0 sample. Coatings modified with TiO 2 particles showed improved antibacterial properties in comparison with Cu-Sn coatings. After 45 min of contact with the surface of Cu-Sn-TiO 2 coatings, the number of active E. coli colonies decreased by 3 orders of magnitude, and after 90 min of testing, it was below the detection limit.
Furthermore, tin oxidation in line with Equation (3) was confirmed through identification of Sn 4+ Sn3d5/2 peak at 486.6 eV. The addition of TiO2 to the studied Cu-Sn coating did not alter tin surface chemistry, but, interestingly, a consequence was a higher surface Sn:Cu ratio (12.4% in the case of Cu-Sn-TiO2 compared to 2.6% for Cu-Sn coating). This can suggest that the surface of composite coatings is enriched in the corrosion products of tin, which is anodic component in the Cu-Sn system. The detailed surface composition examined by XPS is summarized in Table S2 in the Supplementary Information.

Antibacterial Performance
The antibacterial activity of the studied coatings was determined relative to the sanitary indicative bacteria E. coli ATCC 8739. Stainless-steel coupons (AISI 304) were used as a reference. The results of the bacterial tests are summarized in Figure 9. The concentration of viable cells in the initial suspension was 9.8 × 10 6 CFU/mL. In the case of the reference sample, an increase in the number of bacteria colonies to 8.6 × 10 7 CFU/mL was observed after 45 min of the sample contact with the bacteria without UV treatment. This indicates that the stainless-steel surface provides favorable conditions for the reproduction of microorganisms. In turn, all obtained copper-based coatings showed pronounced antibacterial effect. The concentration of bacteria decreased by 1-2 orders of magnitude after 45 min of the contact with the Ti-0 sample. Coatings modified with TiO2 particles showed improved antibacterial properties in comparison with Cu-Sn coatings. After 45 min of contact with the surface of Cu-Sn-TiO2 coatings, the number of active E. coli colonies decreased by 3 orders of magnitude, and after 90 min of testing, it was below the detection limit. Evaluation of antibacterial properties under UV irradiation showed that this type of treatment decreased the number of active colonies on the surface of Cu-Sn coatings almost two times as compared to the data without UV treatment after 90 min of contact. In the case of Cu-Sn-TiO2 composite coatings, the number of bacteria colonies was below the detection limit after 45 min of UV treatment. High antibacterial activity of Cu-Sn-TiO2 coatings under UV treatment is explained by the presence of TiO2 particles on their surface. These particles, being photocatalytically active, generate active forms of oxygen, which have a strong oxidation stress on the bacteria cells [43].
The antibacterial properties of copper and its alloys are usually connected to the release of copper ions, which have a strong oxidative effect on the membrane and/or wall of the bacterial cell [7][8][9][10]. It leads to the damage of the cell membrane and further to disruption of the expression of genetic material. In this regard, the antibacterial activity of the coatings is mainly connected with the concentration of copper ions at the coating/electrolyte interface. In turn, concentration of copper ions will strongly depend on the Evaluation of antibacterial properties under UV irradiation showed that this type of treatment decreased the number of active colonies on the surface of Cu-Sn coatings almost two times as compared to the data without UV treatment after 90 min of contact. In the case of Cu-Sn-TiO 2 composite coatings, the number of bacteria colonies was below the detection limit after 45 min of UV treatment. High antibacterial activity of Cu-Sn-TiO 2 coatings under UV treatment is explained by the presence of TiO 2 particles on their surface. These particles, being photocatalytically active, generate active forms of oxygen, which have a strong oxidation stress on the bacteria cells [43].
The antibacterial properties of copper and its alloys are usually connected to the release of copper ions, which have a strong oxidative effect on the membrane and/or wall of the bacterial cell [7][8][9][10]. It leads to the damage of the cell membrane and further to disruption of the expression of genetic material. In this regard, the antibacterial activity of the coatings is mainly connected with the concentration of copper ions at the coating/electrolyte interface. In turn, concentration of copper ions will strongly depend on the corrosion rate of the coating in the operating environments. For this reason, a detailed evaluation of the corrosion resistance of the formed composites was performed in 3% NaCl solutions and bacterial media.

Corrosion Properties
The corrosion performance of the obtained Cu-Sn and Cu-Sn-TiO 2 coatings in the 3% NaCl solution was evaluated by polarization and EIS studies. The polarization curves obtained after 15 min exposure of the coatings to the 3% NaCl solution are shown in Figure 10a. The electrochemical parameters of the corrosion process calculated from the potentiodynamic polarization data are summarized in Table 3.
tentiodynamic polarization data are summarized in Table 3.
Analysis of the polarization curves showed that the corrosion potential, Ecorr, for Ti-0 sample is 0.030 V. For the Ti-1 and Ti-10 coatings Ecorr it slightly shifted to the cathodic region reaching the value of ca. 0.020 V. Oppositely, for the Ti-5 coating, a shift to a more noble potential of 0.043 V was observed. Such a small variation in Ecorr can be caused by the surface passivation and almost equal Cu-to-Sn ratio in the coatings. The calculated value of the corrosion current density, icorr, for the Ti-0 sample is 1.2 × 10 -7 A/cm 2 . The introduction of TiO2 nanoparticles into the deposition bath deteriorated the corrosion stability of all TiO2-containing composites, which are characterized by 7-9 times higher icorr values as compared to the Ti-0 coating. Furthermore, the solution used for bacterial testing has a different composition (Table S3 in the Supplementary Information). The results of the corrosion experiments in this medium showed that the corrosion rate was generally lower than in 3% NaCl solution (Figure 10b and Table 3). Thus, it can be expected that the antibacterial performance of the obtained composites in the exploitation conditions could be further improved due to a faster release of copper ions from the coating.
To further evaluate the dynamics of the corrosion performance of the examined coatings, EIS spectra were obtained after 15 min (Figure 11a) and 168 h (Figure 11b) of their corrosion in 3% NaCl solution. In both cases, two time constants in the form of suppressed semicircles can be distinguished in the Nyquist plots of all samples. The semicircle at high and medium frequencies characterizes the coating surface and the semicircle at low frequencies characterizes the coating/substrate interface. The presence of two time constants implicitly confirmed the heterogeneity of the formed coatings. Analysis of the EIS spectra showed that the Ti-0 coating has higher values of the impedance modulus than the coatings modified with TiO2 particles. A significant increase in the impedance modulus of all the samples was observed after 168 h of exposure to the corrosive environment ( Figure   Figure 10. Potentiodynamic polarization curves of Cu-Sn and Cu-Sn-TiO 2 coatings after 15 min exposure to 3% NaCl solution (a) and bacterial media (b). Analysis of the polarization curves showed that the corrosion potential, E corr , for Ti-0 sample is 0.030 V. For the Ti-1 and Ti-10 coatings E corr it slightly shifted to the cathodic region reaching the value of ca. 0.020 V. Oppositely, for the Ti-5 coating, a shift to a more noble potential of 0.043 V was observed. Such a small variation in E corr can be caused by the surface passivation and almost equal Cu-to-Sn ratio in the coatings. The calculated value of the corrosion current density, i corr , for the Ti-0 sample is 1.2 × 10 -7 A/cm 2 . The introduction of TiO 2 nanoparticles into the deposition bath deteriorated the corrosion stability of all TiO 2 -containing composites, which are characterized by 7-9 times higher i corr values as compared to the Ti-0 coating. Furthermore, the solution used for bacterial testing has a different composition ( Table S3 in the Supplementary Information). The results of the corrosion experiments in this medium showed that the corrosion rate was generally lower than in 3% NaCl solution (Figure 10b and Table 3). Thus, it can be expected that the antibacterial performance of the obtained composites in the exploitation conditions could be further improved due to a faster release of copper ions from the coating.
To further evaluate the dynamics of the corrosion performance of the examined coatings, EIS spectra were obtained after 15 min (Figure 11a) and 168 h (Figure 11b) of their corrosion in 3% NaCl solution. In both cases, two time constants in the form of suppressed semicircles can be distinguished in the Nyquist plots of all samples. The semicircle at high and medium frequencies characterizes the coating surface and the semicircle at low frequencies characterizes the coating/substrate interface. The presence of two time constants implicitly confirmed the heterogeneity of the formed coatings. Analysis of the EIS spectra showed that the Ti-0 coating has higher values of the impedance modulus than the coatings modified with TiO 2 particles. A significant increase in the impedance modulus of all the samples was observed after 168 h of exposure to the corrosive environment (Figure 11b), which is due to the formation and compaction of a passive film of the corrosion products on the surface. element is given by: where Y is the CPE constant and n is the mathematical factor.
The results of the data fitting are presented in Table 4. Comparison of the corrosion resistance of the coatings was performed based on the values of the polarization resistance, Rp, which for the used equivalent circuit was calculated as Rp = R2 + R3. It was found that regardless of the exposure duration, the composite coatings have lower Rp values than the Ti-0 coating. This result is in good agreement with the polarization studies ( Figure 10).   To quantitatively describe the obtained impedance spectra, the equivalent circuit shown in Figure 11a was used. Here, R 1 corresponds to the electrolyte resistance; R 2 is the resistance of the surface layer of corrosion products; CPE 1 describes the capacitive response of the layer of corrosion products; R 3 is the charge transfer resistance; CPE 2 is the capacitive response of the electric double layer. The constant phase element (CPE) was used due to the significant heterogeneity of the coating surface. The impedance of the CPE element is given by: where Y is the CPE constant and n is the mathematical factor. The results of the data fitting are presented in Table 4. Comparison of the corrosion resistance of the coatings was performed based on the values of the polarization resistance, R p , which for the used equivalent circuit was calculated as R p = R 2 + R 3 . It was found that regardless of the exposure duration, the composite coatings have lower R p values than the Ti-0 coating. This result is in good agreement with the polarization studies ( Figure 10). SEM micrographs of the Cu-Sn and Cu-Sn-TiO 2 coatings after 168 h of immersion corrosion tests in the 3% NaCl solution are shown in Figure 12. Numerous adsorbed particles, most probably insoluble corrosion products, were seen on the surface of the Ti-0 coating (Figure 12a). Despite this noticeable uniform change, no pronounced local corrosion attack was observed. In the case of Cu-Sn-TiO 2 composites (Figure 12b-d), the local corrosion attack was mostly concentrated around globular formations in the microstructure of the coatings. Our SEM/EDX analysis (Figures 5 and 6) confirmed that those are surface areas where TiO 2 particles are embedded into the alloy matrix. Such microstructure is characterized by significant heterogeneity and microdefects, which, in turn, can act as initiation sites of the local corrosion attack. The EDX analysis confirmed the presence of insoluble chloride-containing corrosion products on their surface ( Figure S1 in the Supplementary Information). Summarizing, the results of corrosion tests in 3% NaCl solution indicated that TiO 2 particles can slightly decrease the corrosion resistance of the Cu-Sn matrix.  Figure 12. Numerous adsorbed particles, most probably insoluble corrosion products, were seen on the surface of the Ti-0 coating (Figure 12a). Despite this noticeable uniform change, no pronounced local corrosion attack was observed. In the case of Cu-Sn-TiO2 composites (Figure 12b-d), the local corrosion attack was mostly concentrated around globular formations in the microstructure of the coatings. Our SEM/EDX analysis (Figures 5 and 6) confirmed that those are surface areas where TiO2 particles are embedded into the alloy matrix. Such microstructure is characterized by significant heterogeneity and microdefects, which, in turn, can act as initiation sites of the local corrosion attack. The EDX analysis confirmed the presence of insoluble chloride-containing corrosion products on their surface ( Figure S1 in the Supplementary Information). Summarizing, the results of corrosion tests in 3% NaCl solution indicated that TiO2 particles can slightly decrease the corrosion resistance of the Cu-Sn matrix.  The corrosion process of copper-tin alloys in chloride-containing media can be described by the following mechanism [38,[44][45][46]. Tin is a more electronegative component of the Cu-Sn alloy. Therefore, oxidation of tin at the Cu-Sn alloy/electrolyte interface will occur first with the formation of a SnO 2 layer [44,45]: After this, the dissolution of the main component of the alloy (copper) in a chloridecontaining medium can proceed through the stage of the Cu + ion formation according to the reactions [44,45]: Cu + +Cl − → CuCl.
These corrosion products form a low-soluble dense adsorbed surface film [46]. At high concentrations of chloride ions in the near-electrode layer, the formation of CuClions is also possible. They can further interact with water molecules, forming a layer of poorly soluble Cu 2 O on the sample surface [44,45]: In general, the incorporation of particles into electrodeposited metal coatings is reported to improve their corrosion resistance [23,47,48]. However, contradicting results on the corrosion resistance of the electrochemically deposited Cu-Sn-TiO 2 composite coatings are reported in the literature. Ying et al. reported significantly improved corrosion resistance of Cu-Sn-TiO 2 coatings due to the improved coating structure [30]. In turn, Gao et al. observed slightly improved corrosion resistance of Cu-Sn-Zn-1 g/L TiO 2 coatings, while those deposited from the bath containing 5 g/L TiO 2 were characterized by higher i corr [32]. Our results showed that all TiO 2 -containing composites are characterized by lower corrosion resistance as compared to the Cu-Sn alloy, probably due to the agglomeration of TiO 2 particles. This results in the nonuniformity of the coating surface. The highest corrosion resistance among the composite coatings was shown by the Ti-5 sample, for which the R p values are comparable with those for the Ti-0 coating. This composite is also characterized by the best uniformity of the second-phase particles distribution over the surface. Another important factor is that TiO 2 agglomerates embedded in the Cu-Sn matrix can form local microcathodes on the surface of the alloy, causing selective dissolution of the metal matrix around them. However, the main corrosion parameters of the obtained composites were still acceptable for their industrial application. Moreover, such corrosion behavior is favorable in terms of their antibacterial performance.
Furthermore, the solution used for bacterial testing has a different composition ( Table S3 in the Supplementary Information). The results of the corrosion experiments in this medium showed that the corrosion rate was generally lower than in 3% NaCl solution ( Figure 10 and Table 3). Thus, it can be expected that the antibacterial performance of the obtained composites in the exploitation conditions could be further improved due to a faster release of copper ions from the coating. Summarizing, the use of topcoat Cu-Sn-TiO 2 coatings in public areas can significantly reduce their bacterial load.