Ceramics, Glass and Glass-Ceramics for Personal Radiation Detectors

Different types of ceramics and glass have been extensively investigated due to their application in brachytherapy, radiotherapy, nuclear medicine diagnosis, radioisotope power systems, radiation processing of food, geological and archaeological dating methods. This review collects the newest experimental results on the thermoluminescent (TL) properties of crystalline and glassy materials. The comparison of the physico-chemical properties shows that glassy materials could be a promising alternative for dosimetry purposes. Furthermore, the controlled process of crystallization can enhance the thermoluminescent properties of glasses. On the other hand, the article presents information on the ranges of the linear response to the dose of ionizing radiation and on the temperature positions of the thermoluminescent peaks depending on the doping concentration with rare-earth elements for crystalline and glassy materials. Additionally, the stability of dosimetric information storage (fading) and the optimal concentration of admixtures that cause the highest thermoluminescent response for a given type of the material are characterized. The influence of modifiers addition, i.e., rare-earth elements on the spectral properties of borate and phosphate glasses is described.


Introduction
Thermoluminescent dosimetry is a science which deals with measuring doses of ionizing radiation with the use of TL detectors. Thermoluminescence (TL) dosimetric studies have significant impact on many fields useful in ordinary life such as: radiotherapy [1], nuclear medicine diagnosis [2], radioisotope power systems [3], radiation processing of food [4], geological and archaeological dating methods [5,6], radiation shielding materials [7,8]. Due to the increasing use of ionizing radiation in technology, it seems that we must search for better materials suitable for radiation shielding. The amorphous structure of the glass, which is characterized by exceptional chemical resistance, seems to be ideal for this type of application. Moreover, the thermoluminescent materials are used in measurements of terrestrial and cosmic radiation [9] or radionuclide sources [10]. The phenomenon of thermoluminescence depends on the light emission as a result of heating a sample that was previously exposed to ionizing radiation. The luminescence mechanism in this case can be considered as phosphorescence caused by increasing temperature. The light emission can be observed directly during the first heating process. Luminescence can also be observed again after radiation exposure of a specific wavelength. The phenomenon of thermoluminescence occurs mainly in dielectrics [11] but also in organic materials [12]. The thermoluminescence effect was firstly observed and described in 1663 by the English physicist Robert Boyle [13]. Thermoluminescence was acknowledged in a diamond which had been heated to the temperature of the human body. Then, in 1904 Maria Skłodowska-

Materials and Methods
The thermoluminescent detector was used in ionizing radiation dosimetry for the first time during nuclear testing as part of the Manhattan Project in the United States since 1942 [33]. Nowadays, we are observing a tremendous progress in the thermoluminescence dosimetry from that moment [34][35][36][37]. The most commonly used material in TL detectors is crystalline lithium fluoride. There are a several types of detectors based on this compound: MCP detector (LiF doped Mg, Cu and P), MTS detector (LiF doped Mg and Ti) or MTT detector (LiF doped Mg and Ti with ten times more titanium and almost three times less magnesium in comparison with the MTS detector) [38]. The most important advantages of these detectors are high sensitivity and a cross-section for interaction with ionizing radiation which are similar to that of human tissues. Natural lithium contains 92.5% of the 7 Li isotope and 7.5% of the 6 Li isotope. The TL detectors also use lithium depleted or enriched in the 6 Li isotope, which corresponds to three subtypes: MCP-N (natural abundance of lithium isotopes), MCP-6 ( 6 Li-enriched) and MCP-7 ( 7 Li-enriched) [39]. MTS-N detectors are characterized by a linear thermoluminescence response to approx. 1 Gy, and the reduction in the signal at room temperature is estimated at several percent per year. Moreover, they are characterized by good tissue similarity, therefore they are used in environmental and individual dosimetry. The MCP-N detector is characterized by thirty times greater sensitivity than the MTS-N detector and three times lower own background. This allows the measurement of radiation doses at the level of 200 nGy, which is a result 100 times lower in comparison with the MTS-N detector. The response of the MCP-N detector is linear up to a few Gy and has good stability over time. The spontaneous decrease in the stored radiation signal over time amounts to approx. 5% per year in the room temperature. The MTT-N detector is more efficient than the MTS-N detector, but its sensitivity is approximately 2.5 times lower. Therefore, the minimum measured dose is 1 mGy.
Fluorides and calcium sulphates doped Tm or Dy and Al 2 O 3 doped carbon are also successfully used as thermoluminescent materials [40,41]. However, in practice, they are less often used items than crystalline doped LiF due to the different cross-section for interaction with radiation in comparison with human tissues. The most important technical parameters that prove the quality of thermoluminescent materials include: a wide range of energy of the measured doses, the linearity of the response to the radiation dose, potentially small geometric dimensions, the lack of need for power supply and chemical resistance to environmental factors. An undesirable feature of the thermoluminescent material is the high annealing temperature during the dose reading procedure. Thermoluminescent detectors are usually in the form of sintered bulk ceramics or powders. The most commonly used TL detectors are based on the doped: LiF, Al 2 O 3 , CaF 2 and CaSO 4 [40][41][42]. The comparison of the thermoluminescence glow curves for the same radiation dose for the crystalline TL materials is presented in the Figure 1.
The glass matrix with optically active dopants may also be of interest for developing dosimetric detectors. The borate glasses have a high transparency and high solubility for the rare-earth ions among other oxide glasses, i.e., silicates, phosphates and tellurite glasses [43]. However, due to their multiple phases, high phonon energy and low moisture resistance, borate glasses have some limitations to their optical gain medium. On the other hand, the borosilicate glasses have a better thermal stability, higher value of refractive index and lower dispersion as well as higher chemical resistance [44]. Therefore, these glasses are widely used for optoelectronics [45] and optical lenses applications [46] and also as glass cookware due to low thermal expansion coefficient [47]. The incorporation of rare-earth elements to the glass matrix can induce thermoluminescence effect and produce optical active materials [48]. These dopants act as luminescent centers what enables radiation processes. The glass matrix with optically active dopants may also be of interest for developing dosimetric detectors. The borate glasses have a high transparency and high solubility for the rare-earth ions among other oxide glasses, i.e., silicates, phosphates and tellurite glasses [43]. However, due to their multiple phases, high phonon energy and low moisture resistance, borate glasses have some limitations to their optical gain medium. On the other hand, the borosilicate glasses have a better thermal stability, higher value of refractive index and lower dispersion as well as higher chemical resistance [44]. Therefore, these glasses are widely used for optoelectronics [45] and optical lenses applications [46] and also as glass cookware due to low thermal expansion coefficient [47]. The incorporation of rare-earth elements to the glass matrix can induce thermoluminescence effect and produce optical active materials [48]. These dopants act as luminescent centers what enables radiation processes.
The incorporation of alkali ions in the borate network can reduce the risk of different phases formation in the glass by converting BO3 triangle borate units to BO4 tetrahedra [49]. The addition of fluoride ions to oxide glasses induces the special oxyfluoride properties which combine the low phonon energy and value of refractive index of fluorides with thermal stability towards devitrification of the oxide glasses. For example, after incorporation of lithium ions to borate glass network, the negative charge of the boron-oxygen tetrahedron is compensated by lithium cations [50]. Moreover, alkali fluoride (i.e., LiF, KF or NaF) can be introduced to borate network up to 45 mol%. The rearrangement of lithium ions due to its small radius can likewise be caused by irradiation or glass matrix imperfection. Therefore, it enables formation of negative point defects which play a role of hole traps. On the other hand, oxygen vacancy formed a positive point defect which play a role of electron traps. That explains why, after lithium oxide addition to borate matrix, boron-oxygen triangle attaches an additional oxygen atom forming boron-oxygen tetrahedron. The oxyfluoride glasses from the LiF-B2O3-SiO2 system are characterized by favorable thermoluminescent properties [51]. The increase in lithium fluoride The incorporation of alkali ions in the borate network can reduce the risk of different phases formation in the glass by converting BO 3 triangle borate units to BO 4 tetrahedra [49]. The addition of fluoride ions to oxide glasses induces the special oxyfluoride properties which combine the low phonon energy and value of refractive index of fluorides with thermal stability towards devitrification of the oxide glasses. For example, after incorporation of lithium ions to borate glass network, the negative charge of the boron-oxygen tetrahedron is compensated by lithium cations [50]. Moreover, alkali fluoride (i.e., LiF, KF or NaF) can be introduced to borate network up to 45 mol%. The rearrangement of lithium ions due to its small radius can likewise be caused by irradiation or glass matrix imperfection. Therefore, it enables formation of negative point defects which play a role of hole traps. On the other hand, oxygen vacancy formed a positive point defect which play a role of electron traps. That explains why, after lithium oxide addition to borate matrix, boron-oxygen triangle attaches an additional oxygen atom forming boron-oxygen tetrahedron. The oxyfluoride glasses from the LiF-B 2 O 3 -SiO 2 system are characterized by favorable thermoluminescent properties [51]. The increase in lithium fluoride contribution from 20 to 40 mol% in the borosilicate glass causes efficiency enhancement of the thermoluminescence signal. Moreover, the process of controlled crystallization based on DSC curves can increase TL sensitivity, narrowing and shifting the main TL peak to the lower temperatures. The glass-ceramics with 40 mol% LiF containing LiBF 4 optically active phase exhibits similar level of TL signal to commercially used doped LiF materials [52].
The addition of a heavy metal oxide to the borate network increases the transmission of light in the mid-infrared region and decreases the melting temperature and the phonon energy [53]. Alkali-heavy metal oxide borate glasses show high UV-vis-NIR transparency, low melting and glass transition temperatures, low phonon energy, low thermal expansion coefficient, good mechanical strength and chemical stability [54]. Among various glass hosts, a borate matrix is a proven good radiation absorber with a cheap processing [55]. The effective atomic number Z eff of network former B 2 O 3 is about 7.35 which is close to that of human tissue (Z eff = 7.42) [56]. Heavy metal oxides, such as BaO, decrease the phonon energy of the glass matrix, and simultaneously increase the efficiency of luminescence [57]. It has been observed that the addition of BaO up to 25 mol% to borate glass could help improve the thermoluminescence intensity.
In some cases, commercial borate glasses exhibit UV charge transfer absorption because of the trace iron impurities presence (largely Fe 3+ ions) [58]. It was proved that transition metal (TM) ions even for the ppm level in glasses could produce strong UV absorption. Moreover, the charge transfer mechanism for glasses has been thoroughly classified based on trace transition metal impurities content (such as Fe 3+ or Cr 6+ ) [59]. The increased absorption in the range of ultraviolet results from an electron transfer mechanism (electron transition from the orbital of a coordinating oxygen atom to an orbital of the metal ion). Abdelghany and ElBatal have observed charge transfer absorption bands in the UV range for a various undoped borate glasses [60,61]. Therefore, the trace iron impurities (largely Fe 3+ ions) which are present in the chemical reagents/raw materials can induce UV absorption mechanisms in different glass systems.
The first thermoluminescent material, based on lithium borate polycrystal Li 2 B 4 O 7 doped with manganese, was introduced in radiation dosimetry by J.H. Schulman in 1967 [62]. Unfortunately, the TL sensitivity of Li 2 B 4 O 7 :Mn was quite low and it was impossible to use this material for commercial purposes. Moreover, the reproducibility and the linearity of its dose-response for high energies were insufficient for strict environmental requirements. Subsequently, M. Takenaga significantly improved the TL sensitivity of lithium borate phosphor by using Cu dopants instead of Mn ions [63]. Nowadays, a high efficiency of fluorescence was obtained for borate glasses doped with europium ions [64]. The significant improvements of dosimetric features can be modified by using co-dopants such as transition metals [65]. However, to our present knowledge, the correct mechanism of the TL phenomenon for doped lithium tetraborate glasses is still under discussion. On the other hand, polycrystalline probes of lithium tetraborate exhibit two well-separated thermoluminescent peaks which are related to two different types of trapping points [66]. Electrons can be trapped by oxygen vacancies while holes are trapped by lithium vacancies in Li 2 B 4 O 7 matrix. The monotonous decrease in luminescence signal intensity with higher temperature is due to gradual release of trapped charge carriers. By the thermal energy absorption process, the trapped holes in borate network are freed and can combine with electrons released from the oxygen vacancies which results in emission of the light. The symmetry factors f for lithium tetraborate glasses irradiated with various radiation dose and measured with different heating rates are greater than 0.52, which suggests the second order kinetic of luminescence process [64]. It is widely known that higher order of luminescence kinetic means greater probability of re-trapping processes due to many trapping points in glassy matrix [67]. The main type of radiation damages in lithium borate glasses are Frenkel pairs in the form of vacancies of oxygen and boron with inter-nodal ions [68]. However, the thermal stability of the defect points produced by ionizing radiation has always been a topic of discussion. Unfortunately, electron and hole traps for lithium tetraborate glasses exhibit weak thermal stability with respect to ionizing radiation [69].
The phosphate glass dosimeters are currently of particular interest due to their high thermoluminescence (TL) yield and the simplicity of fabrication and modification for various applications in terms of their chemical and physical properties [70]. Phosphate glasses are often used as biomaterials because they are often similar in chemical composition to the natural bone [71]. However, pure phosphate glasses are often not chemically stable for practical applications [72]; they are characterized by low melting temperature, small value of refractive index and uniquely high thermal expansion coefficient when compared to silicate glasses. Therefore, they can be used as high-power lasers, sealing materials, glasses for medical uses and ionizing radiation dosimetric purposes. A typical network of phosphate glasses contains a polymeric structure dominated by linkages between the PO 4 tetrahedra. For vitreous P 2 O 5 , these groups are connected to adjacent units by three of their four vertices, while one place is occupied by a terminal double-bounded oxygen atom. The extent of glass formation in alkali and alkaline earth binary phosphates is generally larger than in silicates and the borates [73,74]. It is the responsibility of the phosphate rings by the modifier ions to form phosphate chains with varying chain lengths [75]. P 2 O 5 is often used in the optically active glasses due to the shift of the absorption cut-off wavelength to the near infrared region (NIR) [76,77]. The advantage of phosphate glass is its higher solubility of rare earths in its structure in comparison with silicate glasses. Moreover, the lithium fluoride added to phosphate glass causes a decrease in thermal fading at the room temperature [78]. Rare-earth ions, in their trivalent state, act as fluorescence activators when doped in the phosphate glass matrix and enhance TL emission. However, photo and thermoluminescence properties of the RE ions are sensitive to various solid-state hosts. They exhibit absorption bands in the near-UV to blue region and sharp emission bands in the entire visible region of the electromagnetic spectrum, which is expected for visible solid-state lasers and light emitting diodes [79]. The amorphous nature of the glasses makes them susceptible to accommodate radiation-induced defects what is also their advantage.
Pure phosphate glasses produce no TL signals [80]. However, lithium-doped phosphate glasses characterize a broad TL peak at the rage of 200-300 • C [81]. On the other hand, barium-doped phosphate glasses feature at least two TL peaks, approximately at 220 and 390 • C, which are attributed to Ba 2+ ions [82]. The observed TL peaks result from various defects generated by the modifier ions (Ba 2+ and Li + ) inserted into the glass matrix. The low temperature peak characterizes an average intensity loss of 57% after 2 days of storage and a reduction to 9% of the initial signal after 4 months of storage. Thus, thermal fading makes using this peak for dosimetry purposes difficult. The high temperature peak also fades in the short term, but it eventually stabilizes at 75% of the initial value [83]. They also give a fast-decaying OSL signal correlated with the low temperature of TL peak. The optically stimulated luminescence signal increases linearly with the received dose for phosphate glasses containing both barium and lithium ions [84]. On the other hand, a 100-h delay readout after irradiation shows the signal decrease to less than 50% of the initial dose value. The content of barium ions Ba 2+ allows linear characteristics of the dose response in phosphate glasses up to 100 Gy. Moreover, phosphate glass doped with barium oxide is at least one order of magnitude more sensitive to radiation than the glass doped with lithium oxides [85].
The article presents the thermoluminescent properties of mainly borate and phosphate glasses due to the similar cross-section on the interaction with ionizing radiation to human tissues [86,87]. Unfortunately, silicate and telluride glasses have Z eff significantly different than most human organs [88,89]. For this reason, the use of these materials in personal dosimetry is very difficult.
Another group are fluoride glasses, the development of which was initiated by the discovery of the glass-forming properties of zirconium fluoride-ZrF 4 . These glasses are based on heavy metal fluoride glasses (HMFG) and are characterized by-compared to oxide glasses-low attenuation of signals in the infrared range (up to approx. 3 µm). At the same time, fluoride glasses readily accept rare-earth elements into their structure, which makes it possible to use them as optical amplifiers in telecommunications bands operating in the near infrared. Figure 2 shows the values of the highest phonon energy together with ultraviolet cut-off wavelength in various glass systems.
based on heavy metal fluoride glasses (HMFG) and are characterized by-compared to oxide glasses-low attenuation of signals in the infrared range (up to approx. 3 μm). At the same time, fluoride glasses readily accept rare-earth elements into their structure, which makes it possible to use them as optical amplifiers in telecommunications bands operating in the near infrared. Figure 2 shows the values of the highest phonon energy together with ultraviolet cut-off wavelength in various glass systems.

Discussion of the Results
Rare-earth (RE) doped glasses are characterized by promising physical and chemical properties, inclduing: higher thermal stability [90], greater chemical durability [91], superior hardness and elastic modulus than traditional glass network modified by cationic dopants [92]. In general, the rare-earth elements are considered as network modifiers of the glass structure [93,94]. For the phosphate glasses, they are incorporated in the voids between [PO4] tetrahedra [95]. The cationic field strength changes with atomic number due to continuous decrease in the ionic radii for the lanthanide elements [96]. Therefore, this phenomenon has a significant effect on the physico-chemical properties of rare-earth doped phosphate glasses.
A thermoluminescent detector should have a wide linear relationship between the integrated TL intensity and the received radiation dose [112]. It enables greater potential of the material for various applications. Many researchers have noticed an enhancement in the TL intensity of glasses after the addition of rare-earth ions to the glass. The ranges of the linear thermoluminescent dose response for selected glasses doped with rare-earth elements are presented in Table 1. The rare-earth ions usually convey a significant amount of the absorbed radiation energy as heat in the glass matrix what can stimulate thermoluminescence effect.

Discussion of the Results
Rare-earth (RE) doped glasses are characterized by promising physical and chemical properties, inclduing: higher thermal stability [90], greater chemical durability [91], superior hardness and elastic modulus than traditional glass network modified by cationic dopants [92]. In general, the rare-earth elements are considered as network modifiers of the glass structure [93,94]. For the phosphate glasses, they are incorporated in the voids between [PO 4 ] tetrahedra [95]. The cationic field strength changes with atomic number due to continuous decrease in the ionic radii for the lanthanide elements [96]. Therefore, this phenomenon has a significant effect on the physico-chemical properties of rare-earth doped phosphate glasses.
A thermoluminescent detector should have a wide linear relationship between the integrated TL intensity and the received radiation dose [112]. It enables greater potential of the material for various applications. Many researchers have noticed an enhancement in the TL intensity of glasses after the addition of rare-earth ions to the glass. The ranges of the linear thermoluminescent dose response for selected glasses doped with rareearth elements are presented in Table 1. The rare-earth ions usually convey a significant amount of the absorbed radiation energy as heat in the glass matrix what can stimulate thermoluminescence effect. For most TL detectors, the dose response is linear to about a few Gy when it becomes super-linear or sublinear until the detector signal is saturated. The TL response as a function of dose can be described by the function:  Figure 3 shows the linearity, super-linearity and sub-linearity of the exemplary thermoluminescence signal as a function of the absorbed dose. For most TL detectors, the dose response is linear to about a few Gy when it becomes super-linear or sublinear until the detector signal is saturated. The TL response as a function of dose can be described by the function:  Figure 3 shows the linearity, super-linearity and sub-linearity of the exemplary thermoluminescence signal as a function of the absorbed dose.  Phosphate glass doped with 0.5 mol% of lanthanum oxide exhibits 2 luminescence regions in the ranges of blue and red light [125]. The main thermoluminescence peaks appear between 100 and 140 • C for the temperatures up to 300 • C. The deconvolution process of the TL spectrum into Gaussian shape peaks in the range of 100-140 • C reveals two emission energies at 2.01 eV and 2.70 eV (~615 and~460 nm, respectively). After one day of storage (24 h) in the black box, the initial TL intensity is reduced to 50.8% for the phosphate glass doped with La 2 O 3 . It is worth noting that for a phosphate glass doped with yttrium oxide, the glow curves are characterized by TL peaks in the similar range (100-140 • C) but with lower intensities [126]. These TL spectra comparison indicates that La and Y, in contrast to other rare-earth or transition metal dopants, do not directly act as a recombination center for phosphate glass but possibly enhance luminescence efficiency stabilizing other point defects such as vacancies by the charge compensation mechanism.
The energy transfer processes lead to higher TL yield in Ce 3+ /Tb 3+ doped phosphate glasses [127]. A new concept of energy transfer, based on nearly resonant energy migration through a rare-earth-ion subsystem in the glass matrix followed by a single-step transfer to an emission centre, was observed. Gadolinium ions Gd 3+ at a sufficiently high concentration enable effective energy migration in the phosphate glasses matrices followed by single-step energy transfer towards emission centers created by Ce 3+ and Tb 3+ doping ions. Moreover, it has been observed that strongly increasing efficiency of Ce 3+ emission in the Gd-containing Na 67 Gd 30 Ce 3 sample with respect to Gd-free Na 97 Gd 0 Ce 3 one. Furthermore, an increase in the TL signal is observed by increasing the concentration of Tb 3+ ions. On the other hand, a lower signal is detected by increasing the concentration of Gd 3+ . The thermoluminescence measurements above room temperature show the presence of two types of traps with concentrations strongly dependent on the glass composition. Cerium-doped barium borate glasses exhibit both thermoluminescence (TL) and optically stimulated luminescence (OSL) phenomenon [114]. The increase in the cerium dopant concentration from 1 to 5 mol% causes the efficiency enhancement of TL by more than ten times and OSL by more than one hundred times. Moreover, the process of controlled crystallization leads to formation of the optically active BaCeB 9 O 16 phase and higher TL and OSL signals at lower temperature. The shape of the glow curves confirms the linearity of the recorded TL signal as a function of the increasing radiation dose [128]. Unfortunately, barium borate glasses are not the most chemically resistant among wide variety of glass systems. The main disadvantages include the lack of resistance to the presence of moisture in the air. Currently, attempts are being made to increase the resistance to dissolution of borate glasses by adding, e.g., silica SiO 2 [129]. As the amount of silica increases, the chemical resistance increases, but at the expense of the amount of optically active phase, which reduces the value of the luminescence signal. Therefore, it is crucial to choose the optimum amount of SiO 2 to maintain a balance between luminescent properties and thermal stability.
The presence of trivalent cations (dopants) results in a more stable (less hygroscopic) glass structure in all of the glass samples. However, the solubility limit related to the overall concentration of trivalent ions in phosphate glasses seems to be round 50 mol% [130]. The tellurite glasses doped with praseodymium ions Pr 3+ exhibit reddish-orange luminescence under blue wavelength excitation [131]. This phenomenon suggests its possible application in tri-color white light emitting diodes as a red component. Praseodymium is also used with success in various types of phosphors due to the efficient reddish-orange emission of light [132]. For example, CdGeO 3 phosphor exhibits long persistent luminescence (LPL) after the short UV-irradiation. The reddish-orange photostimulated luminescence (PSL) is also observed upon near infrared stimulation at 980 nm after per-exposure into UV light. The light emission is caused by the presence of Pr 3+ ions in trapped states in the structure of the lattice. The most effective concentrations of Pr 3+ ions for the brightest photoluminescence (PL) emission and the best LPL characteristic are about 3 mol% and 0.5 mol%, respectively. The incorporation of 0.3 mol% Pr 6 O 11 to germano-tellurite glasses enhances the intensity of the thermoluminescence response, but in different ways for series with and without Ga 2 O 3 [133]. The inversion of the maxima of the main TL peaks between both series is noticeable. The additive of Ga 2 O 3 inhibits phase separation of Te-Ge oxide network. The Ga 3+ ions play a role of the modifier and facilitate connection between structural units of two glass-formers, preventing phase separation.
The zinc phosphate glass doped with Y 2 O 3 :Eu 3+ powder is characterized by good transparency above 90% for the range 400-700 nm [125]. The bimetallic nanoparticles (BMNPs) of Y 2 O 3 were synthesized by evaporation method at 1100 • C with 4.3 mol% admixture content of Eu 3+ . The doped glasses exhibit an intense thermoluminescence emission, characteristic for intra-electronic transition energy levels of Eu 3+ ion. The main luminescence emission wavelength is about 613 nm, which corresponds to the 5 D 0 to 7 F 2 transition. Meanwhile, the main excitation wavelength which was observed was approximately λ exc = 395 nm. Thus, it is possible to induce luminescence in these glasses with a standard blue laser (400-410 nm). The chromaticity diagram (CIE) confirmed that synthesized glasses with BMNPs have emission of light in the red range [125].
The addition of Dy 2 O 3 to borate glasses acts as a network modifier which also exhibits luminescence properties. The small amount of dysprosium oxide can change the coordination number of boron atoms from 3 to 4, which results in greater number of nonbridging oxygens [134]. It provides better efficiency of thermoluminescence processes in the borate glasses. The presence of Dy 3+ ions in lithium borate network plays a crucial role for the luminescence process due to onefold trapping point behavior [135]. As a result, the probability of the hole-electron recombination process increases because of re-trapping mechanisms are negligibly small. Moreover, the indirect and direct optical bandgap energy of doped lithium borate glass decreases with higher amount of dysprosium ions [136]. Mainly, it is caused by the presence of bonding defects and increasing number of nonbridging oxygens in the glass network. Simultaneously, the incorporation of dysprosium oxide to the glass matrix induces the higher amount of donor energy levels and the average value of Urbach energy increases with greater amount of Dy 2 O 3 content. This tendency also confirms that dysprosium ions can induce trapping defects in the glass network which results in higher glass disordering. The minimal value of Urbach energy is obtained for lithium borate glass with no dysprosium addition. The lack of interstitial defects in the glass network exhibits in better alignment of the structure [137].
Borate glasses doped with erbium ions Er 3+ have promising thermoluminescence properties in view of high-dose radiation detectors [123]. This type of glass exhibited a good linearity in the 0.25 kGy to 3 kGy range, with a high sensitivity of 27 thousand counts·g −1 ·kGy −1 and a minimum detectable dose of 0.2 kGy. After 7 days of storage, the integrated TL intensity of erbium-doped borate glasses reduced by just 4% in comparison with the standard response. However, the reduction was 21% and 50% of its standard value after 15 days and 30 days, respectively. Beyond 30 days, stability was observed as the residual signal remained almost the same even up to 90 days [137]. The erbium rare-earth ion (Er 3+ ) has notable emission bands in MIR, NIR, red, green, and violet light. Therefore, erbium ions are often used in phosphate glasses as application in optical fibers, lasers, and emission devices [138,139].
Thermoluminescence measurements for several materials show that there are measurable differences between signals from materials in the powder and bulk forms [137]. For example, powdered calcium fluoride, crystalline calcite, aragonite, and Iceland Spar have altered thermoluminescence signal in comparison with the bulk form. For example, particle size selection of rare-earth oxides can increase thermoluminescence emission in the doped phosphate glasses [118]. Studies have shown that the efficiency of TL is the higher the larger particles of Gd 2 O 3 or Dy 2 O 3 . The use of 500-1000 µm Gd 2 O 3 as well as Dy 2 O 3 particles allows a linear thermoluminescent response to doses up to 0.9 kGy. The application of smaller particles up to 25 µm gradually reduces the luminescence efficiency. Thus, the incorporation of dysprosium or gadolinium ions into the glass matrix affects both the structure of the electron traps energy levels in the glass matrix and TL emission intensity with respect to particles size. The obtained phosphate glasses exhibit good thermoluminescence properties for the high energy beta radiation dose measurement applications [118].
The temperature of the TL peak for different glass systems is presented in the Figure 4. The colors of the symbols, with which the appropriate dopants from the lanthanide group are marked, correspond to the luminescence emission colors. thermoluminescence properties for the high energy beta radiation dose measurement applications [118].
The ranges of rare-earth dopant concentration for various glass systems from Figure  4 are presented in the Figure 5. The legend markings correspond to the concentration that induces the maximum luminescence signal for a given glass.
Fading is a process during which the radiation dose information stored by thermoluminescent detector is lost, mainly due to the thermal influence of external environment. The thermal stability of the stored TL signals under influence of some environmental conditions is specified by fading parameters. Therefore, the developed TL materials are stored in the black boxes at an ambient temperature, while all measurements are taken in the red lighted rooms. It means that only storage time between irradiation and TL readout can influence on the intensity of luminescence response. The characteristic parameters of thermal fading for different glass systems doped with rare-earth elements are presented in Table 2.  [48,[114][115][116][117][118][119][120][121][122][123]134,140,141].
The ranges of rare-earth dopant concentration for various glass systems from Figure 4 are presented in the Figure 5. The legend markings correspond to the concentration that induces the maximum luminescence signal for a given glass.
Fading is a process during which the radiation dose information stored by thermoluminescent detector is lost, mainly due to the thermal influence of external environment. The thermal stability of the stored TL signals under influence of some environmental conditions is specified by fading parameters. Therefore, the developed TL materials are stored in the black boxes at an ambient temperature, while all measurements are taken in the red lighted rooms. It means that only storage time between irradiation and TL readout can influence on the intensity of luminescence response. The characteristic parameters of thermal fading for different glass systems doped with rare-earth elements are presented in Table 2.
As mentioned before, there is a different TL response of the as-made glass and glassceramics [51,114]. Figure 6 shows the influence of heat treatment on the intensity of TL signal and temperature of the glow peak. The effect was studied on samples from CeO 2 -BaO-B 2 O 3 [114] and LiF-B 2 O 3 -SiO 2 systems [40]. Glass-ceramic materials have been obtained by a heat treatment for 1 h at the temperatures of 720 • C and 840 • C for borate glass, and 600 • C and 720 • C for borosilicate glass, respectively. The significant increase in TL response was observed for glass-ceramics in both cases. Simultaneously, the glow peaks shift to lower temperature. This was caused by crystallization of BaCeB 9 O 16 and LiF phase, respectively. As an example, the peak intensity of TL signal and temperature of TL peak for the same heating rate were summarized for different kind of materials exposed to 10 Gy in the Table 3. It should be noted that the intensity of the thermoluminescence signal and the shape of the glow curve depend on the sample heating rate. Figure 5. The ranges of rare-earth dopant concentration for various glass systems data. The legend's markings correspond to the concentration that induces the maximum luminescence signal for a given glass [48,[114][115][116][117][118][119][120][121][122][123]134,140,141]. As mentioned before, there is a different TL response of the as-made glass and glassceramics [51,114]. Figure 6 shows the influence of heat treatment on the intensity of TL signal and temperature of the glow peak. The effect was studied on samples from CeO2-BaO-B2O3 [114] and LiF-B2O3-SiO2 systems [40]. Glass-ceramic materials have been obtained by a heat treatment for 1 h at the temperatures of 720 °C and 840 °C for borate glass, and 600 °C and 720 °C for borosilicate glass, respectively. The significant increase in TL Figure 5. The ranges of rare-earth dopant concentration for various glass systems data. The legend's markings correspond to the concentration that induces the maximum luminescence signal for a given glass [48,[114][115][116][117][118][119][120][121][122][123]134,140,141].  [142] response was observed for glass-ceramics in both cases. Simultaneously, the glow peaks shift to lower temperature. This was caused by crystallization of BaCeB9O16 and LiF phase, respectively. As an example, the peak intensity of TL signal and temperature of TL peak for the same heating rate were summarized for different kind of materials exposed to 10 Gy in the Table 3. It should be noted that the intensity of the thermoluminescence signal and the shape of the glow curve depend on the sample heating rate.

Conclusions
The crystalline and amorphous materials were described and compared due to their termoluminescence properties and their application as dosimeters for high energy radiation. This work shows that glassy materials can be as beneficial in dosimetry as commercially used crystalline ceramics. Especially considering lower content of active compounds (i.e., LiF) in the glass, the amorphous materials can provide a similar intensity to the thermoluminescent response. The temperature of the glow peak is generally lower in glassy materials. The chemical resistance of glass to environmental conditions (and even biocompatibility of phosphate glasses) means that they could be used in biological conditions, i.e., in brachytherapy. Furthermore, the glass allows easy fabrication and implementation of rare-earth elements into the more open structure then crystals and in a wider   [38] 0.51 205 CeO 2 -BaO-B 2 O 3 glass-ceramics (treated at 840 • C) [114] 1.05 120 CeO 2 -BaO-B 2 O 3 glass-ceramics (treated at 720 • C) [114] 0.78 120 CeO 2 -BaO-B 2 O 3 glass [114] 0.76 235 LiF-B 2 O 3 -SiO 2 glass-ceramics (treated at 720 • C) [51] 0.52 160 LiF-B 2 O 3 -SiO 2 glass-ceramics (treated at 600 • C) [51] 0.29 175 LiF-B 2 O 3 -SiO 2 glass [51] 0.28 200

Conclusions
The crystalline and amorphous materials were described and compared due to their termoluminescence properties and their application as dosimeters for high energy radiation. This work shows that glassy materials can be as beneficial in dosimetry as commercially used crystalline ceramics. Especially considering lower content of active compounds (i.e., LiF) in the glass, the amorphous materials can provide a similar intensity to the thermoluminescent response. The temperature of the glow peak is generally lower in glassy materials. The chemical resistance of glass to environmental conditions (and even biocompatibility of phosphate glasses) means that they could be used in biological conditions, i.e., in brachytherapy. Furthermore, the glass allows easy fabrication and implementation of rare-earth elements into the more open structure then crystals and in a wider range of concentration, thereby increasing the efficiency of the luminescence. However, it is worth noting that the transformation from glass to glass-ceramics enhance the thermoluminescent properties.
The aim of the review article was to summarize the current knowledge about the thermoluminescent properties of glassy and glass-crystalline materials. Unfortunately, due to the small amount of fading data for glass-ceramic materials, it was not possible to make a complete comparison of glassy and crystalline materials. In addition, the properties of materials whose cross-section for interaction with radiation is similar to that of human tissues dominated the review. It should be noted that there are many other glass systems, such as: silicate, telluride, and germanium, which were only mentioned in the article.
Perhaps the above-mentioned shortcomings will be the goal of another review article on the thermoluminescent properties of solids in the near future.
Author Contributions: S.Ś., M.Ś. and W.G. equally contributed to this review article, collecting data from literature and writing the manuscript. All authors have read and agreed to the published version of the manuscript.
Funding: This research has been supported by the EU Project POWR.03.02.00-00-I004/16 and financed by the Polish Ministry of Science and Education-the subsidy no 16.16.160.557.

Institutional Review Board Statement:
This article does not contain any studies with human participants or animals performed by any of the authors.

Data Availability Statement:
The data that support the findings of this study are available on request from the corresponding author; swiontek@agh.edu.pl.

Conflicts of Interest:
We hereby declare that we have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this review article.