Influence of Laser Treatment on the Corrosion Resistance of Cr3C2-25(Ni20Cr) Cermet Coating

The influence of the laser treatment on the corrosion resistance of the Cr3C2-25(Ni20Cr) cermet coating on the Al7075 (EN, AW-7075) substrate (Cr3C2-25(Ni20Cr)/Al7075) was investigated. The coating was produced by the cold sprayed (CS) method. The tested coatings were irradiated with a laser spot speed of 600 mm/min, 800 mm/min, and 1000 mm/min. The mechanical properties of the Cr3C2-25(Ni20Cr)/Al7075 were characterized by microhardness (HV) measurements. The surface and microstructure of the specimens were observed by ascanning electron microscope (SEM) and other assistive techniques. The corrosion test of materials wascarried out by using the electrochemical method in the acidic chloride solution. Cermet coatings perfectly protect the Al7075 substrate against contact with an aggressive corrosion environment. The laser remelting process of the Cr3C2-25(Ni20Cr) layer caused the homogenization of the structure cermet coatings. The irradiation with the laser beam eliminates microcracks and pores on the Cr3C2-25(Ni20Cr) surface. However, the best effect of improving the anti-corrosion properties of cermet coating was obtained for the lowest laser spot speed (i.e., 600 mm/min). It was found that the corrosion rate of the Cr3C2-25(Ni20Cr) cermet coating was reduced by more than two times compared to the highest speed of the laser spot.


Introduction
Cold sprayed (CS) is the newest method of thermal spraying, which has found a number of unique applications in various industries. CS is a process in which solid powder particles are accelerated over the sonic velocity through a de Lavel nozzle with aconvergentdivergent geometry. Particles have ballistic impingement on a suitable substrate at speeds ranging between 300 and 1200 m/s. In the spraying process, the substrate material does not melt, and the sprayed coating is attached to the substrate mechanically with adhesion, and the connection of coating material is of metallurgical nature. In this case, the particles of material falling on the sprayed surface are flattened and adhering to each other in the form of successive layers and form a continuous coating [1,2]. The main advantages of coatings produced by the cold gas method are high purity and excellent mechanical properties, which are not achievable with the spraying methods used so far [3].
The Al7075 alloy is a high-strength aluminum alloy thatis comparable to many types of steel; it is applicable as aircraft fittings, shafts, gears valve components, and many other structural parts. However, this alloy has lower corrosion resistance than other aluminum alloys. This issue can be solved by the development of the ceramic coating with the improved corrosion resistance of the Al7075 alloy. The modern industry widely applies fabrication of different ceramic coating on metallic substrates to obtain a required property. Usually, these materials are implemented for wear and corrosion resistance. Good It seems that using the cold spray method for the production of the Cr 3 C 2 -NiCr coatings can be greatly reduced, such as thermally induced phase reactions and decomposition effects of fine Cr 3 C 2 -NiCr powders. There is still a lack of knowledge about CS spraying of fine Cr 3 C 2 -NiCr carbides, and it is yet unclear to what extent the final phase distribution and the coating crystallite sizes depend on the initial microstructure of the feedstock powder. On the other hand, various methods are used to remove the cermet coating defects, such as heat treatment, sealing, laser remelting, and others [19]. However, the laser remelting of the cermet coating surface is the most recommended because it can be largely eliminated the porosity, providing a more homogeneous and densified microstructure of coatings [20]. It is worth adding that as aresult of laser remelting, the hardness of the cermet coating also increases significantly.
Various methods were used to increase the mechanical and protective properties of metallic coatings. According to the literature reports, the laser treatment method has not been widely used so far. Therefore, laboratory tests were undertaken to determine the effect of laser remelting on the increase in mechanical and anti-corrosion properties of cermet coatings applied to the aluminum alloy substrate.
In the present study, the influence of the laser remelting process on the corrosion resistance of the Cr 3 C 2 -25(Ni20Cr) cermet coatings on the Al7075 substrate was investigated. The cermet coatings were produced by the cold sprayed method. The corrosion test of the materials in the acidic chloride solution (1.2 M Cl − ) was carried out by using the electrochemical method.

Materials and Methods
The chemical composition of the Al7075 (EN, AW-7075) alloy is as follows (wt%): 5.6% Zn, 2.5% Mg, 1.6% Cu, 0.22%, Cr < 0.50% are admixtures (i.e., Mn, Fe, and Si), the rest is aluminum. Fine irregular and broken of the Cr 3 C 2 -25(Ni20Cr) (Diamalloy 3004, Oerlikon Metco Inc., Westbury, NY, USA) were employed as feedstock material. However, it was amixture of Cr 3 C 2 and Ni2OCr powders in a weight ratio of 75% and 25%. A scanning electron microscopy (SEM) image of the powder morphology and the grain size distribution is illustrated in Figure 1.
distribution and the coating crystallite sizes depend on the initial microstructure of the feedstock powder. On the other hand, various methods are used to remove the cermet coating defects, such as heat treatment, sealing, laser remelting, and others [19]. However, the laser remelting of the cermet coating surface is the most recommended because it can be largely eliminated the porosity, providing a more homogeneous and densified microstructure of coatings [20]. It is worth adding that as aresult of laser remelting, the hardness of the cermet coating also increases significantly.
Various methods were used to increase the mechanical and protective properties of metallic coatings. According to the literature reports, the laser treatment method has not been widely used so far. Therefore, laboratory tests were undertaken to determine the effect of laser remelting on the increase in mechanical and anti-corrosion properties of cermet coatings applied to the aluminum alloy substrate.
In the present study, the influence of the laser remelting process on the corrosion resistance of the Cr3C2-25(Ni20Cr) cermet coatings on the Al7075 substrate was investigated. The cermet coatings were produced by the cold sprayed method. The corrosion test of the materials in the acidic chloride solution (1.2 M Cl − ) was carried out by using the electrochemical method.

Materials and Methods
The chemical composition of the Al7075 (EN, AW-7075) alloy is as follows (wt%): 5.6% Zn, 2.5% Mg, 1.6% Cu, 0.22%, Cr < 0.50% are admixtures (i.e., Mn, Fe, and Si), the rest is aluminum. Fine irregular and broken of the Cr3C2-25(Ni20Cr) (Diamalloy 3004, Oerlikon Metco Inc., Westbury, NY, USA) were employed as feedstock material. However, it was amixture of Cr3C2 and Ni2OCr powders in a weight ratio of 75% and 25%. A scanning electron microscopy (SEM) image of the powder morphology and the grain size distribution is illustrated in Figure 1. The Cr3C2 powder particles have an irregular shape, while the Ni20Cr particles have aspherical shape (Figure 1a). On the other hand, it is worth noting that in the Cr3C2-25(Ni20Cr) powder, the presence of alarge fraction of fine grains is noticeable ( Figure 1b). Moreover, in order to minimize agglomeration effects, the powder was heated up to 110 °C in a convection oven for 1 h before use in thefeeder system.
For the production of the Cr3C2-25(Ni20Cr) cermet coating on the Al7075 substrate (Cr3C2-25(Ni20Cr)/Al7075) was used of cold gas spraying system Impact Innovations 5/8 equipped with the Fanuc M-20iA robot (Fanuc Robotics Ltd., Oshino, Japan), Figure 2. The Cr 3 C 2 powder particles have an irregular shape, while the Ni20Cr particles have aspherical shape (Figure 1a). On the other hand, it is worth noting that in the Cr 3 C 2 -25(Ni20Cr) powder, the presence of alarge fraction of fine grains is noticeable (Figure 1b). Moreover, in order to minimize agglomeration effects, the powder was heated up to 110 • C in a convection oven for 1 h before use in thefeeder system.
For the production of the Cr 3 C 2 -25(Ni20Cr) cermet coating on the Al7075 substrate (Cr 3 C 2 -25(Ni20Cr)/Al7075) was used of cold gas spraying system Impact Innovations 5/8 equipped with the Fanuc M-20iA robot (Fanuc Robotics Ltd., Oshino, Japan), Figure 2. The following parameters were used for the production ofcermet coatings: n pressure-30 bar; nitrogen preheating temperature-800 °C; spraying distancetraverse speed-40 mm/s; the step size between 10 passes was 2 mm; the numbe ers-4. The Cr3C2-25(Ni20Cr) cermet coatings were deposited on the Al7075 all surface of Al7075 substrates wasprepared by blasting with corundum of size 30 ( μm). The specimen size was 310 × 110 × 5 mm 3 . The thicknesses of sprayed cerm ings were in the range from 108 μm to 158 μm. However, the test specimens shape of a cuboid with dimensions of 30 × 10 × 5 mm 3 .
The cold gas sprayed coatings were laser remelted with three different veloc means of a CO2 TRUMPF LASERCELL 1005 system (Trumpf GmbH, Ditzinge many) appointed with a three-axial table. The laser remelting parameters are g Table 1. The measurement of microhardness of the tested materials was measured Vickers method (HV), using the Falcon 500 hardness tester from the INNOV company (Maastricht, The Netherlands). An indenter was used in the form of a d pyramid with a square base, and an angle between opposite walls equal to 136 was load varied from 0.02 N to 20 N. The depth of indentation was about 2 μm. The microstructure and cross-section of the specimens were observed by photo camera andscanning electron microscope (SEM) Joel (JEOL Ltd., Tokyo, The following parameters were used for the production ofcermet coatings: nitrogen pressure-30 bar; nitrogen preheating temperature-800 • C; spraying distance-60 mm, traverse speed-40 mm/s; the step size between 10 passes was 2 mm; the number of layers-4. The Cr 3 C 2 -25(Ni20Cr) cermet coatings were deposited on the Al7075 alloy. The surface of Al7075 substrates wasprepared by blasting with corundum of size 30 (600-710 µm). The specimen size was 310 × 110 × 5 mm 3 . The thicknesses of sprayed cermet coatings were in the range from 108 µm to 158 µm. However, the test specimens had the shape of a cuboid with dimensions of 30 × 10 × 5 mm 3 .
The cold gas sprayed coatings were laser remelted with three different velocities by means of a CO 2 TRUMPF LASERCELL 1005 system (Trumpf GmbH, Ditzingen, Germany) appointed with a three-axial table. The laser remelting parameters are given in Table 1. The measurement of microhardness of the tested materials was measured by the Vickers method (HV), using the Falcon 500 hardness tester from the INNOVATEST company (Maastricht, The Netherlands). An indenter was used in the form of a diamond pyramid with a square base, and an angle between opposite walls equal to 136 • whose was load varied from 0.02 N to 20 N. The depth of indentation was about 2 µm.
The microstructure and cross-section of the specimens were observed by using a photo camera andscanning electron microscope (SEM) Joel (JEOL Ltd., Tokyo, Japan), type JSM-5400. The accelerating voltage of SEM was 20 kV. The chemical composition for the corroded surface was also measured by energy-dispersive spectrometer (EDS).
Additionally, to observe the surface topography was used an inverted metallographic microscope (MO) IM-100 (Delta Optical, Warszawa, Poland). The topography of the coatings and the shape of the profile were examined using the Talysurf CCl-Lite 3D noncontact profilograph (Taylor Hobson Ltd., Leicester, UK). Figure 3 shows the SEM image of the top surface of the Cr 3 C 2 -25(Ni20Cr) cermet coating on the Al7075 substrate.  The scanning electron microscope image of the cermet coating has indicated carbide particles (dark areas) in the metallic of the Ni-Cr matrix. However, the size of the carbides in the Cr3C2-25(Ni20Cr) layer did not exceed 3 μm.
X-ray diffraction (XRD) was applied to characterize the phase composition of powders and cold sprayed coatings before and after laser remelting using a Bruker D8 Discover diffractometer (Bruker Ltd., Malvern, UK), with Co K radiation of wavelength λ = 1.7889 Å .
The saturated calomel electrode (SCE(KCl)) was used as the reference, and the counter electrode (5 cm 2 ) was made of platinum foil (99.9% Pt).
The corrosion environment was obtained by mixing the sodium chloride and hydrochloric acid, so the concentration of Cl − ion was 1.2 M. The pH value was 1.5.
The electrolyte was not deoxygenated. The open-circuit potential (EOCP) in the corrosion environment was recorded within 60 min.
The potentiodynamic polarization (LSV) curves were recorded in the potential rangefrom −1000 mV to +200 mV vs. SCE(KCl), with a potential sweep of 1 mV/s. The LSV curves were used to designate the corrosion electrochemical parameters of the tested materials [21][22][23].
The chronoamperometric curves (ChA) were obtained for the potential values,which were selected on the basis of the potentiodynamic polarization curves.
All measurements were carried out at a temperature of 25 ± 0.5 °C, which were maintained using an air thermostat, home production. The scanning electron microscope image of the cermet coating has indicated carbide particles (dark areas) in the metallic of the Ni-Cr matrix. However, the size of the carbides in the Cr 3 C 2 -25(Ni20Cr) layer did not exceed 3 µm.
X-ray diffraction (XRD) was applied to characterize the phase composition of powders and cold sprayed coatings before and after laser remelting using a Bruker D8 Discover diffractometer (Bruker Ltd., Malvern, UK), with Co Kα radiation of wavelength λ = 1.7889 Å.
The saturated calomel electrode (SCE(KCl)) was used as the reference, and the counter electrode (5 cm 2 ) was made of platinum foil (99.9% Pt).
The corrosion environment was obtained by mixing the sodium chloride and hydrochloric acid, so the concentration of Cl − ion was 1.2 M. The pH value was 1.5.
The electrolyte was not deoxygenated. The open-circuit potential (E OCP ) in the corrosion environment was recorded within 60 min.
The potentiodynamic polarization (LSV) curves were recorded in the potential rangefrom −1000 mV to +200 mV vs. SCE(KCl), with a potential sweep of 1 mV/s. The LSV curves were used to designate the corrosion electrochemical parameters of the tested materials [21][22][23].
The chronoamperometric curves (ChA) were obtained for the potential values, which were selected on the basis of the potentiodynamic polarization curves.
All measurements were carried out at a temperature of 25 ± 0.5 • C, which were maintained using an air thermostat, home production.

Vickers Hardness of Material
The microhardness (HV) values of the Cr 3 C 2 -25(Ni20Cr) cermet coatings on the Al7075 substrate without and with laser remelting are listed in Table 2. The cermet coatings were produced by the cold sprayed method. However, the laser spot speed was 600 mm/min, 800 mm/min, and 1000 mm/min. It was found that the laser remelting process changes the value of the surface hardness of the Cr 3 C 2 -25(Ni20Cr) cermet coating on the Al7075 substrate. Because using a laser spot that moved at 600 mm/min caused the hardness of the Cr 3 C 2 -25(Ni20Cr)/Al7075 surface to increase by about 60 HV10 units. It turned out that the surface hardness of the Cr 3 C 2 -25(Ni20Cr) cermet coatings for the higher values the laser spot speed (i.e., 800 mm/min, and 1000 mm/min) significantly decreased, reaching the value of 349 HV10 for the laser spot speed of 1000 mm/min (Table 2). Thus, the laser remelting of the Cr 3 C 2 -25(Ni20Cr) surface changes the structure of the alloy by smoothing and hardening the cermet coating, which is most pronounced for the laser spotspeed of 600 mm/min. It is worth adding that for the lower the laser spot speed values (i.e., 400 mm/min), a very deep melting of the Cr 3 C 2 -25(Ni20Cr) surface structure takes place, which causes deterioration of the mechanical properties of the cermet coating. On the other hand, for the high values of the laser spot speed (i.e., 1200 mm/min), no significant change in the value of the Cr 3 C 2 -25(Ni20Cr) surface hardness was observed. Figure 4 shows the scanning electron microscopy (SEM) imagesof the Cr 3 C 2 -25(Ni20Cr) cermet coatings on the Al7075 substrate after laser remelting for the different spot speeds.

Scanning Electron Microscopy Images
It was found that the laser spot speed has a significant influence on the surface structure of the Cr 3 C 2 -25(Ni20Cr)/Al7075. For the lowest, the laser spot speed, i.e., 600 mm/min, the flattest, regular, and compact cermet surface was obtained (Figure 4a). Moreover, for the larger the laser spot speed (800 mm/min, and 1000 mm/min), a rougher of the Cr 3 C 2 -25(Ni20Cr)/Al7075 surfaces were obtained (Figure 4b,c). However, the main component is the Ni20Cr matrix, which is the light phase. Additionally, new phases in the form of chromium and nickel oxides appeared on the surface of the coatings (Figure 4). A significant proportion of the surface is covered by the dark phase, which is chromium oxide [24]. This oxide was formed as a result of direct contact with the surrounding atmosphere despite the use of argon as a shielding gas. The appearance of this oxide on the surface cermet coatings was also reported by Matthews et al. [25]. Graphite, which is the black phase, is very clearly visible, distributed on the surface in the form of small rounded areas. However, when the temperature reaches the melting point of the matrix, the boundaries between deformed Ni20Cr grains disappeared in it. At the same time, fine carbide grains begin to dissolve in it and take on more round shapes. This is visible in the case of large chromium carbide grains that have retained a partially retained shape. The dissolution process produces fine grains of transformed Cr 3 C 2 carbides that surround large grains [24]. The Cr 3 C 2 carbide decomposed by peritectic reaction and Cr 7 C 3 carbide under conditions of rapid cooling could probably then be formed. On the other hand, the laser melting process is a non-equilibrium process, and there are both types of chromium carbides in the melted layers. This analysis was confirmed by the carried-out investigations of the phase composition of all remelted coatings, which showed the presence of both chromium carbides in them, Figure 5. laser melting process is a non-equilibrium process, and there are both types of chromium carbides in the melted layers. This analysis was confirmed by the carried-out investigations of the phase composition of all remelted coatings, which showed the presence of both chromium carbides in them, Figure 5.   laser melting process is a non-equilibrium process, and there are both types of chromium carbides in the melted layers. This analysis was confirmed by the carried-out investigations of the phase composition of all remelted coatings, which showed the presence of both chromium carbides in them, Figure 5.   The influence of the speed of the laser beam is visible; at the lowest speed of 600 mm/min, the heat input is the highest on the peaks of Cr 7 C 3 are clearly higher, which means that more Cr 3 C 2 was transformed into Cr 7 C 3 . Irregular spaces in the cold sprayed coatings filled with graphite become spherical. Moreover, the microstructure of remelted layers seems to be homogenous and independent of the laser spot speed.
The scanning electron microscopy microstructure of the cross-section of the tested coatings is shown in Figure 6. The influence of the speed of the laser beam is visible; at the lowest speed of 600 mm/min, the heat input is the highest on the peaks of Cr7C3 are clearly higher, which means that more Cr3C2 was transformed into Cr7C3. Irregular spaces in the cold sprayed coatings filled with graphite become spherical. Moreover, the microstructure of remelted layers seems to be homogenous and independent of the laser spot speed.
The scanning electron microscopy microstructure of the cross-section of the tested coatings is shown in Figure 6. As a result of the laser treatment, the thickness of the Cr3C2-25(Ni20Cr) cermet coating was reduced. The lowest coating thickness was obtained for the laser spot speed of 600 mm/min (Figure 6a). The effect of a significant reduction in the thickness of the coating was obtained as a result of packing the structure of the tested coating. The obtained layer is very dense and homogenous because as a result of remelting the coating, the boundaries between the phases visible in the cold sprayed coating have disappeared (Figure 6b). Moreover, no cracks were observed in the obtained layer, which often occurs due to the relief of the accumulated thermal gradient stress during the laser remelting process. On the other hand, there is a significant visible change in the microstructure of the cold sprayed coatings after laser remelting for the spot speed of 800 mm/min or 1000 mm/min. As a result of the lower packing of the particles, the thickness of the cermet As a result of the laser treatment, the thickness of the Cr 3 C 2 -25(Ni20Cr) cermet coating was reduced. The lowest coating thickness was obtained for the laser spot speed of 600 mm/min (Figure 6a). The effect of a significant reduction in the thickness of the coating was obtained as a result of packing the structure of the tested coating. The obtained layer is very dense and homogenous because as a result of remelting the coating, the boundaries between the phases visible in the cold sprayed coating have disappeared (Figure 6b). Moreover, no cracks were observed in the obtained layer, which often occurs due to the relief of the accumulated thermal gradient stress during the laser remelting process. On the other hand, there is a significant visible change in the microstructure of the cold sprayed coatings after laser remelting for the spot speed of 800 mm/min or 1000 mm/min. As a result of the lower packing of the particles, the thickness of the cermet coatings on the Al7075 substrate is significantly greater (Figure 6c-e). The boundaries between the phases in both cermet shells are clearly visible (Figure 6d-f).
Therefore, it can be assumed that for the lowest speed of the laser spot (i.e., 600 mm/min), the Cr 3 C 2 -25(Ni20Cr) cermet coating was obtained, which should best protect the Al7075 substrate against contact with the corrosion environment. coatings on the Al7075 substrate is significantly greater (Figure 6c-e). The boundaries between the phases in both cermet shells are clearly visible (Figure 6d-f). Therefore, it can be assumed that for the lowest speed of the laser spot (i.e., 600 mm/min), the Cr3C2-25(Ni20Cr) cermet coating was obtained, which should best protect the Al7075 substrate against contact with the corrosion environment.  The average metal content (which are summarized in the Spectrum Label) in the Cr3C2-25(Ni20Cr) coatings was: 56.73%, 18.97%, and 3.50% for the elements Cr, Ni, and Al, respectively. The quantitative distribution of the elements along the cross-section of the coatings is not the same. The content of chromium and nickel increases systematically from the Al7075 substrate to the surface of the coatings. In addition, during the production of the Cr3C2-25(Ni20Cr) coatings by the cold sprayed method, aluminum and other elements (i.e., Zn, Mg, and Cu) permeated from the Al7075 substrate into the coatings. Figure 8 shows the surface topography and histogram roughness depth. The obtained results prove about high of the Cr3C2-25(Ni20Cr) surface roughness, which was produced by the cold gas method. The average metal content (which are summarized in the Spectrum Label) in the Cr 3 C 2 -25(Ni20Cr) coatings was: 56.73%, 18.97%, and 3.50% for the elements Cr, Ni, and Al, respectively. The quantitative distribution of the elements along the cross-section of the coatings is not the same. The content of chromium and nickel increases systematically from the Al7075 substrate to the surface of the coatings. In addition, during the production of the Cr 3 C 2 -25(Ni20Cr) coatings by the cold sprayed method, aluminum and other elements (i.e., Zn, Mg, and Cu) permeated from the Al7075 substrate into the coatings. In this case, the surface roughness coefficient (Ra) values were found to be within limits from 16.3 µ m to 160.3 µ m. On the other hand, for the higher the laser spot speed, the Ra values were much higher. Moreover, the tested coating has an asymmetric structure with anegative slope of the surface height. On the other hand, the value of the excess kurtosis was 3.2, which proves that the surface of the Cr3C2-25(Ni20Cr) cermet coating on the Al7075 substrate after laser remelting for the spot speed of 600 mm/min was free from extreme features of peaks and valleys. Therefore, the high roughness of the materials tested was due to the extensive grains diameter distribution that wasused to produce the Cr3C2-25(Ni20Cr) cermet coatings on the Al7075 substrate.

Open-Circuit Potential Measurements
As the potential measured at each time was not locally measured, itonly represents an average potential value of all contributions of the sample in contact with the electrolyte and can provide information on the evolution and degrading of the coating. The open-circuit potential (EOCP) vs. time curves of the Cr3C2-25(Ni20Cr) cermet coatings on the Al7075 substrate are showed in Figure 9. In this case, the surface roughness coefficient (R a ) values were found to be within limits from 16.3 µm to 160.3 µm. On the other hand, for the higher the laser spot speed, the Ra values were much higher. Moreover, the tested coating has an asymmetric structure with anegative slope of the surface height. On the other hand, the value of the excess kurtosis was 3.2, which proves that the surface of the Cr 3 C 2 -25(Ni20Cr) cermet coating on the Al7075 substrate after laser remelting for the spot speed of 600 mm/min was free from extreme features of peaks and valleys. Therefore, the high roughness of the materials tested was due to the extensive grains diameter distribution that wasused to produce the Cr 3 C 2 -25(Ni20Cr) cermet coatings on the Al7075 substrate.

Open-Circuit Potential Measurements
As the potential measured at each time was not locally measured, itonly represents an average potential value of all contributions of the sample in contact with the electrolyte and can provide information on the evolution and degrading of the coating. The open-circuit potential (E OCP ) vs. time curves of the Cr 3 C 2 -25(Ni20Cr) cermet coatings on the Al7075 substrate are showed in Figure 9.
For all specimens, a slower change of potential was observed after ten minutes of immersion in the corrosion solution. By extrapolating the potential to zero time, the opencircuit potential values were determined of the Cr 3 C 2 -25(Ni20Cr) cermet coatings on the Al7075 substrate (Figure 9). It turned out that as the laser spot speed was decreased, the E OCP values move towards positive values (i.e., from −682 mV to −386 mV vs. SCE(KCl)). Thus, it can be assumed that the Cr 3 C 2 -25(Ni20Cr) cermet coating on the Al7075 substrate becomes more resistant to electrochemical corrosion in the chloride environment for the lowest laser spot speed (i.e., 600 mm/min).

Open-Circuit Potential Measurements
As the potential measured at each time was not locally measured, itonly represents an average potential value of all contributions of the sample in contact with the electrolyte and can provide information on the evolution and degrading of the coating. The open-circuit potential (EOCP) vs. time curves of the Cr3C2-25(Ni20Cr) cermet coatings on the Al7075 substrate are showed in Figure 9.

Potentiodynamic Polarization Measurements
Potentiodynamic polarization (LSV) measurements were carried out in order to gain knowledge concerning the impact of laser remelting on the anti-corrosion properties of the Cr 3 C 2 -25(Ni20Cr) cermet coating on the Al7075 substrate and kinetics of the cathodic and anodic reactions. Figure 10 shows potentiodynamic polarization curves of the Cr 3 C 2 -25(Ni20Cr)/Al7075, before and after laser remelting for the different spot speeds, i.e., 600 mm/min, 800 mm/min, and 1000 mm/min. For all specimens, a slower change of potential was observed after ten minutes of immersion in the corrosion solution. By extrapolating the potential to zero time, the open-circuit potential values were determined of the Cr3C2-25(Ni20Cr) cermet coatings on the Al7075 substrate ( Figure 9). It turned out that as the laser spot speed was decreased, the EOCP values move towards positive values (i.e., from −682 mV to −386 mV vs. SCE(KCl)). Thus, it can be assumed that the Cr3C2-25(Ni20Cr) cermet coating on the Al7075 substrate becomes more resistant to electrochemical corrosion in the chloride environment for the lowest laser spot speed (i.e., 600 mm/min).

Potentiodynamic Polarization Measurements
Potentiodynamic polarization (LSV) measurements were carried out in order to gain knowledge concerning the impact of laser remelting on the anti-corrosion properties of the Cr3C2-25(Ni20Cr) cermet coating on the Al7075 substrate and kinetics of the cathodic and anodic reactions. Figure 10 shows potentiodynamic polarization curves of the Cr3C2-25(Ni20Cr)/Al7075, before and after laser remelting for the different spot speeds, i.e., 600 mm/min, 800 mm/min, and 1000 mm/min. where Me means the Cr, Ni, and other metals. The process of hydrogen depolarization occurs in the cathode region of the potentiodynamic polarization curves. In the acid corrosion environment, the cathodic branches of the LSV curves correspond to the simplified reduction of hydrogen ions [21][22][23]: where Me means the Cr, Ni, and other metals. The oxidation process (anode region) of the surface of the Cr 3 C 2 -25(Ni20Cr) cermet coating on the Al7075 substrate depends on the laser spot speed. The shift of the LSV curves towards the positive potentials may indicate an increase in the corrosion resistance of the Cr 3 C 2 -25(Ni20Cr) cermet coatings, especially for the lowest laser spot speed, i.e., 600 mm/min ( Figure 10, curve (d)). Moreover, when Al7075 was covered with Cr 3 C 2 -25(Ni20Cr) cermet coating, the anodic reaction was as follows [21][22][23]: where (MeO) ads means (Cr 2 O 3 ) ads , (NiO) ads , and other oxides. In this case, the working electrode surface was covered mainly with a layer of (Cr 2 O 3 ) ads , (NiO) ads oxides. However, oxides adhered well to the electrode surface. Thus, the Cr 3 C 2 -25(Ni20Cr) coating was passivated under the experimental conditions.The characteristic peaks related to the passivation process of the Cr 3 C 2 -25(Ni20Cr) coating appeared in the LSV curves. Passivation peaks are observed in a wide range of electrode potential, i.e., from −510 mV to −190 mV vs. SCE(KCl)) for the tested materials ( Figure 10). Therefore, a clear inhibition of the corrosion process of the protective coating was observed. It seems that under these conditions, the adsorbed oxide layer can be additionally sealed by adsorption of Cl − ions [22]: The adsorption layer (MeClOH) ads in the acidic chloride solution weredissolved in accordance with a chemical reaction [21][22][23]: Thus, a further sharp increase in the current intensity is observed due to the oxidation of the electrode surface ( Figure 10). However, for a more positive electrode potential of the Cr 3 C 2 -25(Ni20Cr), coatings were depassivated, and further oxidation of the tested materials was observed (Figure 10, curves (a)-(d)). This problem will be discussed extensively later in the article.

Corrosion Electrochemical Parameters
The potentiodynamic polarization curves ( Figure 10) were used to designate the corrosion parameters of the tested materials, i.e., Cr 3 C 2 -25(Ni20Cr) cermet coatings on the Al7075 substrate before and after laser remelting. For this purpose, the method of the extrapolation of rectilinear sections of the Tafel LSV curves wasused [21][22][23]. The values of the corrosion parameters of the tested materials are listed in Table 3. The corrosion potential (E corr ) of the investigated materials has shifted significantly towards the positive values compared to the Cr 3 C 2 -25(Ni20Cr) cermet coating on the Al7075 substrate without laser treatment. This means that the use of laser remelting increases the corrosion resistance of Cr 3 C 2 -25(Ni20Cr)/Al7075 in an acid chloride solution. It seems that the most corrosion-resistant coating was obtained for the lowest laser spot speed, i.e., 600 mm/min (Table 3). However, as the laser spot speed decreases, the slope of the cathodic (−b c ) and anodic (b a ) sections of the potentiodynamic polarization curves systematically decreases in a narrow range (about 100 mV). Therefore, the change of the laser spot speed does not significantly change the mechanism of the cathode and anode process on the surface of the Cr 3 C 2 -25(Ni20Cr) cermet coating. It is worth noting that the corrosion current density (j corr ) systematically decreases as the laser spot speed slows down (Table 3). It can be assumed that for the laser spot speed, i.e., 600 mm/min, the Cr 3 C 2 -25(Ni20Cr) cermet coating will have the lowest rate of electrochemical corrosion in aggressive chloride environments.

Polarization Resistance and Corrosion Rate
In order to determine the values of the polarization resistance (Rp) of the Cr 3 C 2 -25(Ni20Cr) cermet coatings without and with laser treatment in an aggressive chloride environment, fragments of potentiodynamic polarization curves (Figure 10), which relate to the active dissolution area of the tested materials were selected. The polarization resistance of the electrode is described by the equation [21][22][23]: (6) and: The R p valuesdepending on the laser spot speed are summarized in Table 4. It was found that the polarization resistance of the Cr 3 C 2 -25(Ni20Cr)/Al7075 electrode surface increases as the laser spot speed decreases (Table 4). Moreover, the polarization resistance of the Cr 3 C 2 -25(Ni20Cr) laser, treated with the spot speed of 600 mm/min, doubled compared to the Cr 3 C 2 -25(Ni20Cr)/Al7075,which was not subjected to laser irradiation.Thus, in the case of the protective coating irradiated with the laser spot speed of 600 mm/min, the mass and electric charge exchange between the Cr 3 C 2 -25(Ni20Cr) electrode and the chloride electrolyte solution was difficult.
The corrosion rate of the Cr 3 C 2 -25(Ni20Cr) cermet coatings on the Al7075 substrate without and with laser treatment was calculated based on the equation: CR (mm/year) = 1.16 j corr (8) which by authors [26][27][28] was proposed. The values of the corrosion rate of the Cr 3 C 2 -25(Ni20Cr) cermet coatings are listed in Table 5. The laser spot speed of the cermet coating has a significant influence on the values of the corrosion rate (CR) of the Cr 3 C 2 -25(Ni20Cr) coatings on the Al7075 substrate. It turned out that for the laser spot speed of 600 mm/min, the lowest CR, i.e., 0.46 mm/year, was observed for the Cr 3 C 2 -25(Ni20Cr)/Al7075. However, for a laser spot speed of 1000 mm/min, the corrosion rate of the Cr 3 C 2 -25(Ni20Cr) cermet coating is more than twice as high as the CR of the tested coatings for the lowest laser spot speed (Table 5). Figure 11 shows the chronoamperometric (ChA) curves of the Cr 3 C 2 -25(Ni20Cr) cermet coating on the Al7075 substrate after laser remelting for the spot speed of 600 mm/min. However, similar ChA curves were obtained for the remaining laser spot speed but are not quoted in this work. All curves were recorded in the acid chloride (1.2 M Cl − ) environment.

Chronoamperometric Measurements
The potentials of the working electrode were selected based on the potentiodynamic polarization curve ( Figure 10, curve (d)), i.e., for the laser spot speed of 600 mm/min. However, for the potential of −900 mV vs. SCE(KCl), the H + ions reduction process (reaction (2) took place on the surface of the working electrode ( Figure 11, curve (a)).
On the other hand, for the potentials of −190 mV and −40 mV vs. SCE(KCl), oxidation of the surface of the Cr 3 C 2 -25(Ni20Cr) cermet coating was observed (reactions (3)-(5)). It is worth noting that for the peak potential of −190 mV, the oxidation current density of the electrode material systematically decreases with the passage of electrolysis time ( Figure 11, curve (b)). Thus, during the electrolysis process, as a result of the reaction (3), the oxide layer on the Cr 3 C 2 -25(Ni20Cr)/Al7075 surface was sealed due to the adsorption of (Cr 2 O 3 ) ads and (NiO) ads oxides. Moreover, the adsorbed layer of nickel, chromium oxides, and other element oxides could be additionally sealed in the form of the adsorbed of (MeClOH) ads layer (reaction (4)) on the Cr 3 C 2 -25(Ni20Cr)/Al7075 surface. Figure 11 shows the chronoamperometric (ChA) curves of the Cr3C2-25(Ni20Cr) cermet coating on the Al7075 substrate after laser remelting for the spot speed of 600 mm/min. However, similar ChA curves were obtained for the remaining laser spot speed but are not quoted in this work. All curves were recorded in the acid chloride (1.2 M Cl − ) environment. The potentials of the working electrode were selected based on the potentiodynamic polarization curve ( Figure 10, curve (d)), i.e., for the laser spot speed of 600 mm/min. However, for the potential of −900 mV vs. SCE(KCl), the H + ions reduction process (reaction (2) took place on the surface of the working electrode ( Figure 11, curve (a)).

Chronoamperometric Measurements
On the other hand, for the potentials of −190 mV and −40 mV vs. SCE(KCl), oxidation of the surface of the Cr3C2-25(Ni20Cr) cermet coating was observed (reactions (3)-(5)). It is worth noting that for the peak potential of −190 mV, the oxidation current density of the electrode material systematically decreases with the passage of electrolysis time ( Figure 11, curve (b)). Thus, during the electrolysis process, as a result of the reaction (3), the oxide layer on the Cr3C2-25(Ni20Cr)/Al7075 surface was sealed due to the adsorption of (Cr2O3)ads and (NiO)ads oxides. Moreover, the adsorbed layer of nickel, chro- In the case of a more positive potential of the working electrode (i.e., −40 mV), the oxidation current density of the Cr 3 C 2 -25(Ni20Cr)/Al7075 surface initially decreases (up to 20 s) and then increases with increasing electrolysis time ( Figure 11, curve (c)). This means that the protective layer adsorbed on the surface of the working electrode in the acid chloride solution was partially dissolved. Thus, the exposureof the Cr 3 C 2 -25(Ni20Cr) coating was corroded in the aggressive corrosion environment of chlorides (reaction (5)). Figure 12 shows the inverted metallographic microscope (MO) images of the Cr 3 C 2 -25(Ni20Cr) cermet coatings on the Al7075 substrate after laser remelting for the spot speed of 600 mm/min, 800 mm/min, and 1000 mm/min. The Cr 3 C 2 -25(Ni20Cr)/Al7075 surface was subjected to the corrosion test in an acid chloride solution (1.2 M Cl − ). The exposure time of the specimen was five hours. However, the oxide layer from the surface of the tested specimen was removed with diluted nitric acid. In this case, the exposure time was about three minutes. On the other hand, for the higher laser spot speed, i.e., 800 mm/min or were much greater damage to the Cr3C2-25(Ni20Cr)/Al7075 surfaces due the aggressive environment of chloride (Figure 12b,c).

Conclusions
The influence of the laser treatment on the corrosion resis Cr3C2-25(Ni20Cr) cermet coating on the Al7075 substrate was inve Cr3C2-25(Ni20Cr)/Al7075 coating was produced by the cold sprayed (CS speed of the laser remelting of the Cr3C2-25(Ni20Cr) was varied from 600 m mm/min. Laser remelting has a significant influence on the surface struct met coatings. For the lowest speed (i.e., 600 mm/min), the flattest, regular cermet surface on the Al7075 substrate was obtained. However, the Vicke The surfaces of the Cr 3 C 2 -25(Ni20Cr) cermet coatings were subject to corrosion as aresult of long contact with a strong electrolyte. As a result of the corrosion process, numerous pits appeared on the surface of all samples, which reduced the mechanical and aesthetic properties of the tested materials ( Figure 12). The lowest corrosion damage was observed for the Cr 3 C 2 -25(Ni20Cr)/Al7075 surface, which was subjected to laser processing with alaser spot speed of 600 mm/min (Figure 12a). In this case, the Cr 3 C 2 -25(Ni20Cr) coating was hardened and sealed as a result of the laser treatment, and the corrosion process of the investigated material was significantly slowed down. Thus, the Cr 3 C 2 -25(Ni20Cr) coating protects the Al7075 substrate well against contact with a corrosion environment, i.e., 1.2 M Cl − .
On the other hand, for the higher laser spot speed, i.e., 800 mm/min or 1000 mm/min were much greater damage to the Cr 3 C 2 -25(Ni20Cr)/Al7075 surfaces due to corrosion in the aggressive environment of chloride (Figure 12b,c).

Conclusions
The influence of the laser treatment on the corrosion resistance of the Cr 3 C 2 -25(Ni20Cr) cermet coating on the Al7075 substrate was investigated. The Cr 3 C 2 -25(Ni20Cr)/Al7075 coating was produced by the cold sprayed (CS) method. The speed of the laser remelting of the Cr 3 C 2 -25(Ni20Cr) was varied from 600 mm/min to 1000 mm/min. Laser remelting has a significant influence on the surface structure of the cermet coatings. For the lowest speed (i.e., 600 mm/min), the flattest, regular, and compact cermet surface on the Al7075 substrate was obtained. However, the Vickers microhardness of the cermet coatings was decreased as the speed of laser irradiation was increased. The highest polarization resistance (R p ) was observed for the Cr 3 C 2 -25(Ni20Cr) coating after remelting for the speed of 600 mm/min. Therefore, in this case, the lowest corrosion rate (CR) of the Cr 3 C 2 -25(Ni20Cr) surface in the chloride environment was recorded. The protective, homogeneous oxide layer was formed on the Cr 3 C 2 -25(Ni20Cr) surface, which very effectively protects the tested materials against corrosion. Moreover, for the higher speeds, laser remelting (i.e., 800 mm/min or 1000 mm/min) significantly reduces the mechanical and anti-corrosion properties of the cermet coatings.