Paper Doped with Polyacrylonitrile Fibres Modified with 10,12–Pentacosadiynoic Acid

This work reports a modification of a fibrous cellulose material (paper) by the addition of polyacrylonitrile (PAN) fibres doped with 10,12–pentacosadiynoic acid (PDA). The fibres are sensitive to ultraviolet (UV) light. When the paper containing PAN–PDA is irradiated with UV light it changes colour to blue as a consequence of interaction of the light with PDA. The colour intensity is related to the absorbed dose, content of PAN–PDA fibres in the paper and the wavelength of UV radiation. The features of the paper are summarised after reflectance spectrophotometry and scanning microscopy analyses. All the properties of the modified paper were tested in accordance with adequate ISO standards. Moreover, a unique method for assessing the unevenness of the paper surface and the quality of printing was proposed by using a Python script (RGBreader) for the analysis of RGB colour channels. The modification applied to the paper can serve as a paper security system. The modified paper can act also as a UV radiation indicator.


Introduction
Dynamic development of the industrial production and packaging of products exposed challenges regarding protection of copyrights and forgery of products. Modern security systems enhance the quality control and protection against illegal and uncontrolled trade of products. Securing products and packaging is the basic measure related to the quality of raw materials, correct application of production processes, determining the conditions of storage, transport, and distribution of products.
In the case of printed documents, the following forms of security can be highlighted: (i) overt-security on a product, visible and available to users; (ii) certified-a security set that is a trade secret and confirmed by a manufacturer for a specific group of users and (iii) hidden-a security set that can only be verified by certification laboratories without providing information about them to the user. Many markers are used for product protection against undesirable impact factors: changes in humidity and temperature, influence of oxygen, or exposure to light, mainly to ultraviolet (UV) radiation. Such markers provide information on climatic, biological, and mechanical factors, including information about product features such as quantitative losses, changes in shape, consistency, taste, and loss of functionality [1]. Absorbing systems, interacting with oxygen, water, odour, carbon dioxide, and ethylene, are also known [2]. On the commercial market the following are also available: TTI (Time and Temperature Indicators), MarkTM (3M), OnVu™, and CoolVu™ (Freshpoint) markers, which provide information on temperature differences in relation to the optimal value specified by the manufacturer. Such indicators are produced on the basis of thermochromic compounds that change their colour depending on temperature [3].

Preparation of Samples
The polyacrylonitrile microfibre (PAN) was prepared from a co-polymer of poly (acrylonitrile-co-methyl acrylate) (PAN, Zoltek, Nyergesújfalu, Hungary) with 10,12pentacosadiynoic acid (PDA, Sigma-Aldrich, Saint Louis, MI, USA) according to a procedure described elsewhere [15]. PDA was mixed with the PAN solution in DMF during the preparation of a spinning solution. For the fibre preparation, a 23% (w/w) solution of PAN in DMF was used, and the concentration of PDA was set to 1% (w/w of PAN). The microfibres were obtained as a multifilament-a bunch of 250 microfibres. After spinning, the fibres were cut into lengths of 3 mm and incorporated into cellulosic paper pulp. Bleached softwood kraft pine pulp (BSK) was used to prepare laboratory handsheets. The pulp parameters were as follows: initial moisture content: 6.37%, α-cellulose content: 86.6%, DP: 1081, initial Schopper-Riegler value: SR-12. Pulp was refined to SR-30 value. Different mixtures of refined cellulosic pulp with the addition of 0, 5, 10, and 20% PAN-PDA fibres were made, and an additional batch of a mixture of cellulosic pulp and 20% PAN-PDA fibres was refined together. All paper samples were prepared according to ISO 5263-1 standard [21], and one batch of 20% PAN-PDA fibres was refined together with cellulosic pulp to SR-30 value in a PFI mill according to TAPPI T 248 standard [22]. Drainability of refined pulps was tested in accordance with ISO 5267-1:1999 [23]. The laboratory sheets of cellulosic pulps with dopants of basis weight 65 g/m 2 and average thickness of 130 µm were formed in Rapid-Köthen apparatus according to ISO 5269-2:2005 standard [24].

Irradiation of Samples
All paper samples were irradiated in UV-curing cabinets (UVP, Upland, CA, USA) to deliver doses up to 10 J/cm 2 at three wavelengths corresponding to UVA, UVB, and UVC. The instruments were equipped with five UV lamps of the following characteristics: UVA (8/W, type F8T5 black light, 369 nm, Hitachi, Tokyo, Japan), UVB (8/W, type G8T5E, 306 nm, Sankyo Denki, Tokyo, Japan) and UVC (8/W, type G8T5, 253.7 nm, Sankyo Denki, Tokyo, Japan). A given UV dose (J/cm 2 ) was delivered automatically using a built-in detector and the control system of the device. All samples were irradiated at room temperature (23 • C).

Spectrophotometric Measurements
Paper-PAN-PDA samples before and after irradiation were measured with a Spectraflashlight reflectance instrument (Spectraflash 300, DataColor, Lawrenceville, NJ, USA). The device was calibrated before the measurements. The light in the range of 190-400 nm was cut off in order to prevent exposure of the samples to UV light during the measurements. The samples were measured immediately after irradiation as well as post-irradiation in order to analyse their stability over time of storage. During storage, the samples were covered with aluminium foil to protect them against daylight. The measurements lead to the reflectance spectra (R [%], 400-700 nm with 10 nm resolution). Following this, a wavelength for which the change in reflectance was substantial was selected and analysed vs. absorbed dose for further analysis of the paper-PAN-PDA samples' doseresponse characteristics.

Scanning Electron Microscopy Measurements
The morphology of paper-PAN-PDA samples was analysed with the aid of a TES-CAN VEGA3-EasyProbe (TESCAN Brno, s.r.o., Brno, Czech Republic) scanning electron microscope equipped with VEGATG software (high vacuum mode (SE); accelerating voltage 7 kV). Before the measurements, all samples were coated by Au-Pd layers using a Cressington Sputter Coater 108 auto system (Watford, UK).

Paper Surface Unevenness
In order to assess the inhomogeneity of the paper surface and the possibility of printing on it, black text and graphical gradient patterns were printed on the samples. The prints were made with a digital inkjet printer (Epson L310, Nagano, Japan; Micro Piezo printhead; 5.760 × 1.440 dpi; CMYK printing system: dye-based inks). The printouts were made with the following parameters: document type, standard paper type, high print quality. In the next step, all samples were measured with an Epson Perfection V750 Pro scanner (Japan, Nagano; cold cathode fluorescent lamp; optical resolution Main 6.400 dpi × Sub 9.600 dpi; 48 bit/colour). The scanning was performed in the reflection mode and the colour depth was 24-bit RGB. All paper samples (30 × 30 mm 2 ) were scanned at a resolution of 300 dpi. Other scanning parameters such as brightness, colour saturation correction, colour regulation, and sharpness were switched off and were not taken into account in this study. Selected scans were used to calculate profiles across the paper samples. This was conducted with the aid of a prepared script for reading RGB channels (RGBreader; Python Script with Python Imaging Library; DosLab; [16]). Each sample was depicted using a three-colour RGB scale. For the channel that showed the highest changes in RGB values (from 0 to 255), further calculations were made. For the irradiated paper samples doped with PAN-PDA fibres, the green channel was selected. A detailed description of the RGBreader script is described elsewhere [14]. The obtained results of the analysis of the doped paper were compared with a commercial printer paper (POL Speed, Poland, Baruchowo; 80 g/m 2 ). Optical microscopy was performed (Biological microscope, NIKON, Japan, Tokyo) under a magnification of ×10 for the evaluation of the paper surface unevenness.

Dose Response of Paper-PAN-PDA Samples
All prepared papers doped with PAN-PDA fibres were UVA, UVB, and UVC irradiated at doses ranging from 0 to 10 J/cm 2 . The samples were first inspected with the naked eye, followed by spectrophotometric light reflectance measurements. A view of the samples as seen with the naked eye is presented in Figure 1. After UVB and UVC irradiation all doped paper samples changed their colour from white to blue. By exposure to UV light, blue PAN-PDA fibres emerged from the white paper sheets. The colour intensity was dose dependent; the higher the dose, the higher the intensity of the colour obtained. For all examined samples it was visible that they responded to UVC radiation at lower doses than for UVA and UVB irradiation.

Paper Surface Unevenness
In order to assess the inhomogeneity of the paper surface and the possibility of printing on it, black text and graphical gradient patterns were printed on the samples. The prints were made with a digital inkjet printer (Epson L310, Nagano, Japan; Micro Piezo printhead; 5.760 × 1.440 dpi; CMYK printing system: dye-based inks). The printouts were made with the following parameters: document type, standard paper type, high print quality. In the next step, all samples were measured with an Epson Perfection V750 Pro scanner (Japan, Nagano; cold cathode fluorescent lamp; optical resolution Main 6.400 dpi × Sub 9.600 dpi; 48 bit/colour). The scanning was performed in the reflection mode and the colour depth was 24-bit RGB. All paper samples (30 × 30 mm 2 ) were scanned at a resolution of 300 dpi. Other scanning parameters such as brightness, colour saturation correction, colour regulation, and sharpness were switched off and were not taken into account in this study. Selected scans were used to calculate profiles across the paper samples. This was conducted with the aid of a prepared script for reading RGB channels (RGBreader; Python Script with Python Imaging Library; DosLab; [16]). Each sample was depicted using a three-colour RGB scale. For the channel that showed the highest changes in RGB values (from 0 to 255), further calculations were made. For the irradiated paper samples doped with PAN-PDA fibres, the green channel was selected. A detailed description of the RGBreader script is described elsewhere [14]. The obtained results of the analysis of the doped paper were compared with a commercial printer paper (POL Speed, Poland, Baruchowo; 80 g/m 2 ). Optical microscopy was performed (Biological microscope, NIKON, Japan, Tokyo) under a magnification of ×10 for the evaluation of the paper surface unevenness.

Dose Response of Paper-PAN-PDA Samples
All prepared papers doped with PAN-PDA fibres were UVA, UVB, and UVC irradiated at doses ranging from 0 to 10 J/cm 2 . The samples were first inspected with the naked eye, followed by spectrophotometric light reflectance measurements. A view of the samples as seen with the naked eye is presented in Figure 1. After UVB and UVC irradiation all doped paper samples changed their colour from white to blue. By exposure to UV light, blue PAN-PDA fibres emerged from the white paper sheets. The colour intensity was dose dependent; the higher the dose, the higher the intensity of the colour obtained. For all examined samples it was visible that they responded to UVC radiation at lower doses than for UVA and UVB irradiation.

0%
5% 10% 20% The development of colour was related to the absorbed dose of UV light and concentration of PAN-PDA dopant in the paper structure. Therefore, we assessed the samples quantitatively through the measurements of light reflectance in relation to the absorbed UV dose and concentration of the PAN-PDA dopant. The colour change of the paper samples without the PAN-PDA dopant was also analysed in the range of 0−10 J/cm 2 (Figure 2a,b). It is known that a long-term exposure to UV radiation can degrade various materials, including paper. The papers exposed to light for a long time change their optical, mechanical, and physicochemical properties. The most visible sign of paper ageing is the change of its optical characteristics (yellowing or bleaching), which is associated with degradation of lignin, cellulose, and hemicelluloses after exposure to light, heat, radiation, pH, and oxidation processes at elevated temperature in the presence of atmospheric oxygen. A slight change in the value of the light reflectance ( Figure 2a) can be observed at 400−500 nm, which may result from the UV radiation exposure to 10 J/cm 2 . For instance, the difference in reflectance values at 430 nm for non-irradiated and 2 and 10 J/cm 2 irradiated paper samples was -1.29, -4.56 and -2.99, -5.72 and -3.63, -5.39%, for UVA, UVB, and UVC, respectively. In Figure 2b, the reflectance relations vs. absorbed UV dose are shown. Linear regressions were adapted to the experimental points. The extracted slopes from these regressions are as follows: -0.0001, -0.0003, -0.0003% cm 2 /J, for UVA, UVB, and UVC, respectively. This denotes that the paper samples without the PAN-PDA dopant are only slightly vulnerable to colour change after irradiation with UVA, UVB, and UVC. However, after irradiation, the samples were not yellow to the naked eye; no significant changes in the range of 550−600 nm were observed. Therefore, it was concluded that the applied UV doses slightly affected the non-modified paper samples in a blue range of Vis light. 2a,b). It is known that a long-term exposure to UV radiation can degrade various materials, including paper. The papers exposed to light for a long time change their optical, mechanical, and physicochemical properties. The most visible sign of paper ageing is the change of its optical characteristics (yellowing or bleaching), which is associated with degradation of lignin, cellulose, and hemicelluloses after exposure to light, heat, radiation, pH, and oxidation processes at elevated temperature in the presence of atmospheric oxygen. A slight change in the value of the light reflectance ( Figure 2a) can be observed at 400−500 nm, which may result from the UV radiation exposure to 10 J/cm 2 . For instance, the difference in reflectance values at 430 nm for non-irradiated and 2 and 10 J/cm 2 irradiated paper samples was -1.29, -4.56 and -2.99, -5.72 and -3.63, -5.39%, for UVA, UVB, and UVC, respectively. In Figure 2b, the reflectance relations vs. absorbed UV dose are shown. Linear regressions were adapted to the experimental points. The extracted slopes from these regressions are as follows: -0.0001, -0.0003, -0.0003% cm 2 /J, for UVA, UVB, and UVC, respectively. This denotes that the paper samples without the PAN-PDA dopant are only slightly vulnerable to colour change after irradiation with UVA, UVB, and UVC. However, after irradiation, the samples were not yellow to the naked eye; no significant changes in the range of 550−600 nm were observed. Therefore, it was concluded that the applied UV doses slightly affected the non-modified paper samples in a blue range of Vis light. The colour intensity increased with radiation dose and depended on the content of the PAN-PDA dopant ( Figure 3). In Table 1, CIE Lab parameters of the colours of the UVirradiated-doped paper samples are presented. CIE Lab parameters specify a colour using a 3-axis system. Accordingly, a* and b* are colour directions: +a* is the red axis, -a* is the green axis, +b* is the yellow axis, -b* is the blue axis, and L* is the lightness axis. The reflectance for the samples decreases between about 500 and 660 nm (Figure 3a,c,e). Regardless of the amount of added PAN-PDA fibres to the paper pulp, all paper samples are almost insensitive to UVA irradiation. As a consequence, exposure of the fibres to UVA did not cause colour saturation, even at high doses of over 10 J/cm 2 . In the case of the UVB irradiation of the paper-PAN-PDA, the reflectance versus dose relations at 500 and 600 nm corresponded to blue colour formation of PDA in the PAN fibres ( Figure  3b,d,f). The colour intensity increased with radiation dose and depended on the content of the PAN-PDA dopant ( Figure 3). In Table 1, CIE Lab parameters of the colours of the UV-irradiated-doped paper samples are presented. CIE Lab parameters specify a colour using a 3-axis system. Accordingly, a* and b* are colour directions: +a* is the red axis, -a* is the green axis, +b* is the yellow axis, -b* is the blue axis, and L* is the lightness axis. The reflectance for the samples decreases between about 500 and 660 nm (Figure 3a,c,e). Regardless of the amount of added PAN-PDA fibres to the paper pulp, all paper samples are almost insensitive to UVA irradiation. As a consequence, exposure of the fibres to UVA did not cause colour saturation, even at high doses of over 10 J/cm 2 . In the case of the UVB irradiation of the paper-PAN-PDA, the reflectance versus dose relations at 500 and 600 nm corresponded to blue colour formation of PDA in the PAN fibres (Figure 3b,d,f).     Upon UVB irradiation, blue colour saturation occurs at doses of 2-2.5 J/cm 2 . The sensitivity of the samples is higher than that for UVA light. Low sensitivity of the samples to UVA radiation is advantageous from the point of view of accidental exposure of the samples to daylight. However, the paper-PAN-PDA samples showed the highest colour change after UVC irradiation. If the paper-PAN-PDA samples were UVC irradiated, the saturation of the blue colour occurred at about 1 J/cm 2 . The dose sensitivity (expressed as a slope of quasi-linear part of the reflectance vs. dose relation) was −0.0074 (5% PAN-PDA dopant), −0.0117 (10% PAN-PDA dopant), and −0.0236 (20% PAN-PDA dopant), i.e., 23, 11, and 10% higher, respectively, than the dose sensitivity for UVB radiation. Elementary characteristics of all paper samples doped with PAN-PDA fibres including threshold dose, measuring range, dose sensitivity, and R 2 coefficient were determined and are presented in Table 2. Table 2. Elementary characteristics of UV-irradiated paper samples with PAN-PDA fibres dopant (non-refined paper) (A denotes the slope of the linear regression that is the dose sensitivity). The samples made of refined cellulose pulp had similar sensitivity to UVC radiation as the unrefined samples ( Figure 4). After analysis of the CIE Lab values obtained from the measurements of light reflectance at 500 nm for refined and unrefined samples, it can be concluded that the intensity of the blue colour for the refined paper visible after UVC irradiation (especially for the dose range 0.5-10 J/cm 2 ) was about 5% lower than that for the unrefined sample.

Long-Term Stability of the Doped Paper
The stability of the paper samples with and without the PAN-PDA fibre dopant irradiated to different doses of UVA, UVB, and UVC was assessed by spectrophotometric light reflectance measurements ( Figure 5). The measurements were performed for one month. From the results obtained it was concluded that the fibres were stable, independent of the absorbed dose. All samples kept in a dark place did not change during the storage period. Figure 5 shows example measurements of the paper samples with 20% PAN-PDA dopant irradiated with UVC light in the range of 0−10 J/cm 2 . These observations for UVC light-irradiated samples are analogous to those for UVA-and UVB-irradiated samples. On this basis, it was concluded that the samples both non-irradiated and after UV irradiation are very stable during storage. This feature is important if the doped paper is to serve as a radiation sensor/indicator or if a permanent colour effect is required for marking the originality of a paper product.

Long-Term Stability of the Doped Paper
The stability of the paper samples with and without the PAN-PDA fibre dopant irradiated to different doses of UVA, UVB, and UVC was assessed by spectrophotometric light reflectance measurements ( Figure 5). The measurements were performed for one month. From the results obtained it was concluded that the fibres were stable, independent of the absorbed dose. All samples kept in a dark place did not change during the storage period. Figure 5 shows example measurements of the paper samples with 20% PAN-PDA dopant irradiated with UVC light in the range of 0−10 J/cm 2 . These observations for UVC light-irradiated samples are analogous to those for UVA-and UVB-irradiated samples. On this basis, it was concluded that the samples both non-irradiated and after UV irradiation are very stable during storage. This feature is important if the doped paper is to serve as a radiation sensor/indicator or if a permanent colour effect is required for marking the originality of a paper product.

Long-Term Stability of the Doped Paper
The stability of the paper samples with and without the PAN-PDA fibre dopant irradiated to different doses of UVA, UVB, and UVC was assessed by spectrophotometric light reflectance measurements ( Figure 5). The measurements were performed for one month. From the results obtained it was concluded that the fibres were stable, independent of the absorbed dose. All samples kept in a dark place did not change during the storage period. Figure 5 shows example measurements of the paper samples with 20% PAN-PDA dopant irradiated with UVC light in the range of 0−10 J/cm 2 . These observations for UVC light-irradiated samples are analogous to those for UVA-and UVB-irradiated samples. On this basis, it was concluded that the samples both non-irradiated and after UV irradiation are very stable during storage. This feature is important if the doped paper is to serve as a radiation sensor/indicator or if a permanent colour effect is required for marking the originality of a paper product.

Morphology and Mechanical Properties of Paper-PAN-PDA Samples
Manufacturing a paper sheet requires several steps, and many factors affect the properties of the final paper. The choice of raw material composition, degree of refining, types, and amounts of additives influence the final product. The most commonly used additives include sizing agents, fillers, dyes, optical brighteners, additives improving the strength of the paper web, and special additives, e.g., natural or synthetic fibres with special properties. In our experiment, two types of paper were produced: a mixture of refined cellulosic BSK pulp with the addition of 0, 5, 10, and 20% PAN-PDA fibres and a mixture of cellulosic BSK pulp refined together with 20% PAN-PDA fibres. The micro-and macro-structure of the paper plays important roles in the mechanical properties. Thus, the morphology of the paper was evaluated with scanning electron microscopy for nonirradiated, UVA, UVB, and UVC irradiated papers without and with PAN-PDA fibres. The results of the scanning electron microscopy measured papers are presented in Figure 6 for non-irradiated and 5 J/cm 2 (UVC) irradiated samples. PAN-PDA fibres are marked in blue colour to be more visible in the SEM images. In the case of paper without the addition of PAN-PDA fibres, a typical structure of the natural cellulose paper can be seen in the form of elongated, flattened objects with an uneven surface. PAN-PDA fibres are seen as smooth and round objects incorporated into the structure of cellulose fibres.
Based on the analysis of the elementary parameters of the paper, it was found that tensile index, elongation, tear index, and bursting index decreased as the content of PAN-PDA fibres increased (Table 3). At the same time, the roughness of the paper increased, which is typical for such modifications of paper. However, in the case of the refining of cellulosic pulp with 20% addition of PAN-PDA fibres, it was found that the decrease in the mechanical properties of the paper was lower than that in the case of paper with the addition of the same amount of fibres that had not been exposed to refining process. This can be explained by the fact that the synthetic fibres were deformed during the refining operation, thanks to which they better fit into the fibrous structure of the paper. These conclusions were confirmed by the apparent density results (Table 3). With an increase in the addition of unrefined synthetic fibres, the apparent density decreased. In the case of the pulp refined together with 20% of PAN-PDA fibres, the value of apparent density was higher-practically the same as for paper without the addition of synthetic fibres. The presence of fibre deformation was also confirmed after analysis of Figure 7d. Table 3. Basic parameters of the paper samples doped with different amounts of PAN-PDA fibres (SD denotes the standard deviation and COV denotes the coefficient of variation).  The mechanical mixing of the PAN-PDA fibres with the cellulose pulp resulted in a homogeneous paper surface and did not significantly change its structure. The straight lengths (3 mm) of PAN-PDA fibres penetrate into the cellulose pulp structure at various depths. After preparation of the doped paper, the samples containing PAN-PDA fibres showed no changes in optical properties and the surface texture appeared uniform. Mechanical mixing of the cellulose pulp ensured homogeneous distribution of PAN-PDA fibres. However, when irradiated with higher doses of UV radiation, bunches of blue fibres were visible on the paper surface (Figure 7). PAN-PDA fibres were distributed randomly, and their visibility on the surface increased with an increase in their amount. Mechanical mixing of the fibre dopant did not damage them. They were straight and smooth without visible changes such as bends, fractures or fibrillation.

PAN-PDA
To improve the uniformity of PAN-PDA fibre dispersion, refined paper samples were prepared. Refining is required in order to improve papermaking ability and paper properties, among others the structure, flexibility, and strength. Refined pulp was more homogeneous and filled, which is related to the fibrillization of cellulose fibres ( Figure  7b). As a result of refining, PAN-PDA fibres were tangled and better bonded to the paper fibres bunches The mechanical mixing of the PAN-PDA fibres with the cellulose pulp resulted in a homogeneous paper surface and did not significantly change its structure. The straight lengths (3 mm) of PAN-PDA fibres penetrate into the cellulose pulp structure at various depths. After preparation of the doped paper, the samples containing PAN-PDA fibres showed no changes in optical properties and the surface texture appeared uniform. Mechanical mixing of the cellulose pulp ensured homogeneous distribution of PAN-PDA fibres. However, when irradiated with higher doses of UV radiation, bunches of blue fibres were visible on the paper surface (Figure 7). PAN-PDA fibres were distributed randomly, and their visibility on the surface increased with an increase in their amount. Mechanical mixing of the fibre dopant did not damage them. They were straight and smooth without visible changes such as bends, fractures or fibrillation.
To improve the uniformity of PAN-PDA fibre dispersion, refined paper samples were prepared. Refining is required in order to improve papermaking ability and paper properties, among others the structure, flexibility, and strength. Refined pulp was more homogeneous and filled, which is related to the fibrillization of cellulose fibres (Figure 7b). As a result of refining, PAN-PDA fibres were tangled and better bonded to the paper surface ( Figure 7d). However, they were not damaged. There were no visible cracks or fibrillation of PAN-PDA fibres. The obtained samples were smoother and the fibre bunches were hardly seen on the paper surface with the naked eye after UV irradiation.

Evaluation of Paper Surface Unevenness
Based on the analysis of the basic parameters of the paper, the surface unevenness of the manufactured papers was examined in relation to the commercial ones. For this purpose, the RGBreader script described in Section 2.6 was used, which enabled the graphical visualization of the sample in the RGB colour space. Each paper sample was imaged with a flat-bed scanner and saved as an bmp file. Then, the image was analysed with the RGBreader script, which decomposed the graphics file into RGB channels. For the paper samples, significant changes in RGB values were recorded in the green channel. Therefore, it was selected for further analysis (Figure 8). The paper with the addition of 10% PAN-PDA fibres showed the greatest surface unevenness. Moreover, the refining of cellulosic pulp with PAN-PDA fibres led to a more filled (less uneven) surface of the paper (Figure 9). pose, the RGBreader script described in Section 2.6 was used, which enabled the graphical visualization of the sample in the RGB colour space. Each paper sample was imaged with a flat-bed scanner and saved as an bmp file. Then, the image was analysed with the RGBreader script, which decomposed the graphics file into RGB channels. For the paper samples, significant changes in RGB values were recorded in the green channel. Therefore, it was selected for further analysis (Figure 8). The paper with the addition of 10% PAN-PDA fibres showed the greatest surface unevenness. Moreover, the refining of cellulosic pulp with PAN-PDA fibres led to a more filled (less uneven) surface of the paper ( Figure  9).
The developed paper is intended to be used as a substrate for inkjet digital printing, e.g., as packaging. Therefore, it was interesting to see if the samples could be printed similarly to the commercial printer paper. It is known that the print quality depends on the basis weight, roughness, structure, and surface properties of the paper. Chemical and physical properties of the printed surface play an important role in paper interaction with liquids. Commercial printer papers are enhanced by the addition of surface sizing to control the wetting and penetration of the liquid. The behaviour of ink drops on the paper surface depends on the surface and interface tension and thus the wetting conditions and the flow of ink during the wetting process. In the digital printing process, the colorant part of the ink fixes in the top layer of paper and the ink vehicle part penetrates deeper into the structure [32]. In assessing the quality of inkjet digital printing, the most important factors are colour reproduction and print sharpness. Assessment of print quality is usually subjective and based on experience with printing. The instrumental measurements must relate to the subjective perceptual impressions to be meaningful. Therefore, a method for assessing the print quality using RGBreader script has been proposed. For this purpose, a text and a graphic pattern (black and colour) were inkjet printed on a commercial printer paper and refined paper doped with 20% PAN-PDA fibres ( Figure 10). The naked eye analysis of the samples indicated a visible difference between the saturation of printed colours for com- mercial printer paper and the paper doped with 20% PAN-PDA fibres. In the case of c mercial paper, the colour and black prints were less intense (Figure 10a,d,g), which m be related to the basic parameters of paper. For paper doped with PAN-PDA fibres, turbances in the green channel caused by the paper surface structure were visible, they did not significantly affect the shape and sharpness of the printed patterns (Fig  10b,e,h). Moreover, the samples looked similar after UVC irradiation (Figure 10c,f,i). colour change of the paper was related to the PAN-PDA fibre dopant, but had no ef on the printed pattern. It was found that after UV irradiation, the print quality of the fined paper with 20% PAN-PDA fibres was almost the same as that for commercial pa due to the colour intensity and the mapping of the printed shape (Figure 11a). It was possible to determine significant differences in the structure of the paper or the qualit prints following the analysis of the photos from an optical microscope (Figure 11b,c). Additionally, SEM measurements were performed and the obtained results are p sented in Figure 12. As expected, no traces of dye or aggregation of ink particles w visible on the surface of the papers. However, the commercial printer paper had filler Figure 9. Comparison of surface unevenness of paper samples (commercial paper, unrefined paper with 20% PAN-PDA fibres, and refined paper with 20% PAN-PDA fibres).
The developed paper is intended to be used as a substrate for inkjet digital printing, e.g., as packaging. Therefore, it was interesting to see if the samples could be printed similarly to the commercial printer paper. It is known that the print quality depends on the basis weight, roughness, structure, and surface properties of the paper. Chemical and physical properties of the printed surface play an important role in paper interaction with liquids. Commercial printer papers are enhanced by the addition of surface sizing to control the wetting and penetration of the liquid. The behaviour of ink drops on the paper surface depends on the surface and interface tension and thus the wetting conditions and the flow of ink during the wetting process. In the digital printing process, the colorant part of the ink fixes in the top layer of paper and the ink vehicle part penetrates deeper into the structure [32].
In assessing the quality of inkjet digital printing, the most important factors are colour reproduction and print sharpness. Assessment of print quality is usually subjective and based on experience with printing. The instrumental measurements must relate to the subjective perceptual impressions to be meaningful. Therefore, a method for assessing the print quality using RGBreader script has been proposed. For this purpose, a text and a graphic pattern (black and colour) were inkjet printed on a commercial printer paper and refined paper doped with 20% PAN-PDA fibres ( Figure 10). The naked eye analysis of the samples indicated a visible difference between the saturation of printed colours for commercial printer paper and the paper doped with 20% PAN-PDA fibres. In the case of commercial paper, the colour and black prints were less intense (Figure 10a,d,g), which may be related to the basic parameters of paper. For paper doped with PAN-PDA fibres, disturbances in the green channel caused by the paper surface structure were visible, but they did not significantly affect the shape and sharpness of the printed patterns (Figure 10b,e,h). Moreover, the samples looked similar after UVC irradiation (Figure 10c,f,i). The colour change of the paper was related to the PAN-PDA fibre dopant, but had no effect on the printed pattern. It was found that after UV irradiation, the print quality of the refined paper with 20% PAN-PDA fibres was almost the same as that for commercial paper due to the colour intensity and the mapping of the printed shape ( Figure 11a). It was impossible to determine significant differences in the structure of the paper or the quality of prints following the analysis of the photos from an optical microscope (Figure 11b,c).
Additionally, SEM measurements were performed and the obtained results are presented in Figure 12. As expected, no traces of dye or aggregation of ink particles were visible on the surface of the papers. However, the commercial printer paper had fillers in its structure to even out its surface, which was not the case for the paper modified with PAN-PDA fibres. Distance (pix) Figure 9. Comparison of surface unevenness of paper samples (commercial paper, unrefined paper with 20% PAN-PDA fibres, and refined paper with 20% PAN-PDA fibres).

Conclusions
In this work we reported the first results from the preparation and characterization of papers modified with PAN-PDA fibres. Preliminary studies have shown that PAN-PDA fibres can be used as a modifier for paper products. Modified papers respond to UV radiation by colour change. The intensity of the blue colour increases with increasing dose of UVB and UVC light. The micro-and macro-structure of the papers depends on the preparation method applied. It was also found that carrying out the joint pulp refining with the addition of the PAN-PDA fibres resulted in a smaller decrease in the mechanical properties of the paper. The refined synthetic fibres were not damaged to such an extent that they lost their optical properties. Moreover, it has been shown that the developed refined paper with 20% PAN-PDA fibre is suitable as a substrate for inkjet printing and the print quality is comparable to that of a commercial printer paper. An application of the modified papers would be marking products against copying and counterfeiting, e.g., packaging with markers for the pharmaceutical industry. The proposed method provides uniform distribution of fibres in the product structure and a smooth surface that may be printed. An advantage of the solution presented is an intensive development of a colour when exposed to UV radiation of a specific wavelength. This can be used as a radiation "on-off" marker and effective identifier of paper products, documents, banknotes, and securities. This can also be helpful in management, control of production, transport, and storage of products. The subject of manufacturing paper modified with PAN-PDA fibres is not exhaustive and requires further research including (i) light properties (fluorescent and absorption spectra) of the papers [33][34][35], (ii) the influence of additives on the surface quality of the paper and UV dose response of PAN-PDA fibres dopant, (iii) the influence of paper refining methods: plasma, high temperature, calendaring.