Organosulfur Materials with High Photo- and Photo-Oxidation Stability: 10-Anthryl Sulfoxides and Sulfones and Their Photophysical Properties Dependent on the Sulfur Oxidation State

While few studies show only symmetrical and poorly mono-SOn (n = 0–2) substituted acenes, in this study, we present a synthesis of a new group of unsymmetrical, significantly substituted derivatives, which revealed unique photophysical properties. Both sulfides (S), sulfoxides (SO) and sulfones (SO2) showed very high photochemical stabilities, unusual for these groups, during UV-irradiation at 254/365 nm (air O2 and Ar), which was higher than any found in the literature. For the (S)/(SO) series (254 nm), the stabilities of 80–519 min. (air O2 and Ar) were found. At 365 nm, stabilities of 124—812 min./(air O2) for (S)/(SO) and higher for (SO2) were observed. Photoluminescence lifetimes of (SOn) of the lower anthryl symmetry remained in the following order: (SO2) < (S) < (SO); those with full symmetry were in the following order: (S) < (SO) < (SO2). The enhanced photostability was explained with DFT/MS/Hammett’s constants, which showed the leading role of the SOn groups in stabilization of HOMO/LUMO frontier orbitals. The SOn (n = 0–2) substituted acenes turned out to be tunable violet/blue/green emitters by oxidation of S atoms and the introduction of rich substitution.

Due to the high electronegativity of oxygen, the sulfoxide S(O) and sulfone S(O)2 moieties are powerful electron-withdrawing groups in comparison to the sulfide precursors. Electron character of the latter deserves, however, a comment. The sulfide groups become quite strong electron donors when attached to electron-poor aromatic systems, while, when attached to electron-rich aromatics, they turn into weak acceptors [21]. The sulfur bridges between two (hetero)aromatic moieties exhibit tetrahedral geometry that can reduce the p-conjugation length to effectively develop blue emitters [25]. In polymeric materials, the limited conjugation endows the polymers with a weak optical absorption and a high transparency in the visible region [9]. The S(O) or S(O)2 bridges, between two (hetero)aromatic moieties, may deepen the frontier molecular orbital energy levels, and hence improve the electron collection and the hole blocking abilities of the resulting polymer solar cells [9]. A successive oxidation of the bridging sulfur atom in the SOn (n = 0, 1) bridges causes a large increase in photoluminescence yield (Φ) of the resulting chromophores [26]. Some studies conclude that the rapid intersystem crossing (ISC) to the triplet state is the main deactivation process limiting the photoluminescence (PL) quantum yield Φ, as in terthiophene dimers [27], but other investigations show that differently to the latter, the SOn bridged chromophores do not require competing ISC, as in binaphthyl systems, to limit the PL emission [28]. It is believed that these conclusions can be extrapolated to other sulfur-bridged conjugated chromophores [25]. In the above investigations, the different PL efficiencies upon oxidation of the sulfur bridge have been rationalized by the existence of energetically available non-radiative decays in the (S) and S(O) bridges. Both studies confirmed the generality of the electron lone-pair(s) screening concept, which assumed that electron lone-pair(s) on the sulfur atom in (S) and (SO) screened the electronic interactions between the two (hetero)aromatic chromophores. According to the concept, the Φ limiting ISC efficiency is reduced in the presence of the intramolecular charge transfer (CT), which can be tuned by the oxidation state of the SOn bridge. This causes a decrease in the CT and allows the efficient ISC in symmetrical (S) and (SO), which results in lower PL efficiencies in these systems and higher PL efficiencies in (SO2), with no electron lone pairs on the bridging sulfur atom. In other words, the formation of CT states in (SO2) can suppress ISC and lead to higher Φ values. Hence, the studies do not maintain the expectation that a greater electron density on the sulfur atom should facilitate electronic communication between bridged chromophores [27]. The origin of the anomalously low emission of aromatic (S)/ (SO) and high emission of (SO2) has also been rationalized by Finney et al. [29] on two sets of unsymmetrical 1-pyrenyl (S)/(SO)/(SO2); their study established that the excited states of benzylic aryl sulfoxides (SO) were deactivated not by the photoinduced electron transfer from the sulfur lone electron pair, but by the non-radiative, reversible α-cleavage of the C-S bond [29,30]. Further studies on the origin of the nonradiative excited state relaxation in aryl sulfoxides, including excited state pyramidal inversion and alternate formation of a twisted intramolecular charge transfer state (TICT), in which the radical cation/radical anion pair is twisted fully out of conjugation, have recently been described in the literature [13,28,31].
The materials with the S(O)2 group lower both the LUMO and HOMO energy levels. The electronic devices with the sulfone-based materials can be expected to have: (1) an efficient electron-injection and transport, an improved balance of holes and electrons allowing their effective recombination in emissive layers; (2) a high triplet energy for the efficient blue phosphorescent organic light-emitting diodes; (3) wide band gaps; and (4) good electrochemical and thermal stabilities [2,5,31]. To date, the sulfone-based materials have also been used as host or emitting materials in phosphorescent organic light-emitting diodes (PhOLEDs) and efficient, thermally activated delayed fluorescence (TADF) emitting materials [1][2][3][4][5][6][7][8].
In one of the few papers on photostability and photooxidation stability of the SOn bridged chromophores, Wolf et al. [31] reported that unsubstituted, symmetrical 9,9′-bianthryl sulfide (S) was stable in solution to irradiation at 365 nm for several hours, the sulfoxide (SO) underwent a rapid (seconds) loss of the bridging SO group followed by the quantitative formation of 9,9′-bianthryl, while the corresponding sulfone (SO2) underwent chemical reactions to give anthracene dimer containing a three-membered episulfone ring which, like the starting sulfone, could be converted to anthraquinone in the presence of oxygen upon overnight irradiation. There is a lack of studies on the photostability and photooxidation stability of these compounds at 254 nm.
In addition to the mentioned examples, a very limited number of other SOn bridged chromophores have been reported to date [29,30,32]. Moreover, the lack of studies on the synthesis and photochemical behavior of bulky, SOn (n = 0, 1, 2) bridged, non-symmetric chromophores, based on anthracene and larger acenes, is particularly noticeable in the literature. The present study fills this gap and investigates highly substituted (S), i.e., 10-RS-anthracenes, obtained in the thio-variant of the Friedel-Crafts-Bradsher cyclization [33,34], and the corresponding sulfoxides (SO) and sulfones (SO2).

Synthetic Procedures and Spectroscopic Techniques
m-Chloroperbenzoic acid (m-CPBA, Sigma-Aldrich, St. Louis, MO, USA) was used at ≥ 77%. Dry and oxygen free dichloromethane (DCM, JT Baker Chemicals, Deventer, The Netherlands) was taken from MB SPS-800 (MBRAUN Solvent Purification System, Garching, Germany). The 1 H NMR and 13 C NMR spectra ( Figure S1) were measured with a Bruker AV 200 or AV 500 spectrometer, (Billerica , USA) in CDCl3 with chemical shifts (δ) given in ppm relative to TMS as an internal standard. High-resolution mass spectrometry (HRMS) measurements were performed using Synapt G2-Si mass spectrometer (Waters, Milford, MA, USA) equipped with an APCI source and quadrupole-Time-of-Flight mass analyzer. The mass spectrometer was operated in the positive ion detection mode with discharge current set at 4.0 μA. The heated capillary temperature was 350 °C. The results of the measurements were processed using the MassLynx 4.1 software (Waters, Milford, MA, USA) incorporated with the instrument. Accurate mass measurements were performed by a peak matching technique using perfluorokerosene as an internal standard at a resolving power of 10,000 (10% valley definition). The HR(MS_MS)-(+)-APCI spectra were recorded at 15 eV, 25 eV and 35 eV. Melting points were measured using Boetius apparatus. Thin layer chromatography (TLC) was performed on precoated Merck 60 (F254 60, Darmstad, Germany) silica gel plates with fluorescent indicator, with detection by means of UV light at 254 and 360 nm. Column chromatography was done on Merck silica gel (Kieselgel 60, Darmstad, Germany, 230-400 mesh). The UV-Vis absorption spectra were recorded in 1 cm cuvettes on a Shimadzu UV-2700 spectrophotometer (Kioto, Japan) using two types of the light source: a D2 64604 deuterium lamp and a Wl L6380 halogen lamp (Kioto, Japan, 220-600 nm). Room temperature, steady-state emission spectra were obtained with the Horiba Jobin Yvon, Fluorolog-3 spectrofluorimeter (Glasgow, United Kingdom) using a xenon lamp as a light source. The fluorescence quantum yields Φ of the obtained compounds were determined in EtOH and toluene on excitation at their absorption maximum using an integrating sphere (Horiba, Jobin Yvon, Quanta-φ F-3029 Integrating sphere). Fluorescence lifetime values were measured by the Time Correlated Single Photon Counting (TCSPC, Glasgow, United Kingdom) analysis. The fluorescence decay curves were obtained by exciting the molecules at their emission maximum using a NanoLED laser at 374 nm ± 10 nm (<200 ps) as a light source. The photodegradation measurements were investigated by monitoring the absorbance decay of 10 −5 ethanolic solutions in a quartz cuvette stored in the dark at room temperature, under ambient atmosphere (O2) and inert atmosphere (Ar), and then exposed to a UVP-Hg-Pen-ray lamp (254 nm, 16.33 mW/cm 2 at distance 1 cm) and a VL-6.LC fluorescent lamp (6W) (365 nm, 27.4 mW/cm 2 at distance 1 cm).

Photostability and Photooxidation Stability in Ethanol Solutions
The photodegradation was investigated by monitoring the absorbance decay of 10 −5 M ethanolic solutions in quartz cuvettes stored in the dark at room temperature, under ambient atmosphere and Ar atmosphere, and exposed to a UVP-Hg-Pen-ray lamp (254 nm, 16.33 mW/cm 2 at distance 1 cm) and a VL-6.LC fluorescent lamp (6W) (365 nm, 27.4 mW/cm 2 at distance 1 cm).

Chemical Synthesis
The (S) substrates, mono-RS-substituted anthracenes 1, used for the synthesis of two series of mono-RS(O)-and mono-RS(O)2-substituted anthracenes ((SO) 2 and (SO2) 3, respectively), were obtained from cyclisation of (o-S,S-dithioacetalaryl)arylmethyl thioethers in the presence of FeCl3/KI in boiling ethanol, according to the thio-Friedel-Crafts-Bradsher reaction, which has recently been elaborated in our lab [33,34]. Next, RS groups in (S)-1a-d were oxidized using one or two equivalents of m-chloroperbenzoic acid (m-CPBA) to give the corresponding (SO)-2a-d and (SO2)-3c, 3d, respectively (Scheme 1 and Table 1). The oxidation reaction of 1a and 1b gave 2a and 2b in 55% and 42% yields, respectively. In this series, the corresponding sulfones 3a and 3b, obtained directly from the reaction of 1a and 1b with 2 equiv. of m-CPBA, although detected in small quantities in the crude reaction mixture (mass spectra), could not be isolated. An attempted synthesis of 3a from the sulfoxide 2a with 1 equiv. of m-CPBA, carefully monitored by 1 H NMR for 5 days, resulted in the same outcome. The anthracene core in these two series has the highest electron donor character due to the presence of five alkoxy substituents and, most probably due to this reason, is unstable during oxidation. The oxidation of other sulfides 1c and 1d with 1 equiv. of m-CPBA gave sulfoxides 2c and 2d in 36% and 32% yields, respectively. In this series, synthesis of the corresponding sulfones 3c and 3d was successful and they were obtained from 2c and 2d with 2 equiv. of m-CPBA in 26% and 17% yields, respectively.

Photophysical Properties
Photophysical properties (absorption and PL spectra, PL quantum yields (Φ) as well as PL lifetimes (τ) of (S)-1a-d, ( nm with only two absorption maxima for 1a and for 1b at max abs  = 380 and 400 nm, respectively, and one absorption maximum for 2a and for 2b at max abs  = 380 nm with a shoulder at 405 nm for 2a and 2b. In the two a and b series of (S) and (SO), with five alkoxy substituents on the anthracene core, the higher oxidation state of sulfur atom ((S) versus SO)) had, astonishingly, no effect on the position of the absorption maxima (1a/2a and

Compound
Absorption   Figure S5). The spectra also showed relatively stronger dependence on the sulfur oxidation state, going from (S) to (SO) and from the latter to (SO2).
Fluorescence spectra of compounds 2a and 2b with 3-methoxy groups on the athracene moiety, both in toluene and EtOH, show large redshifts in relation to the spectra of 1a and 1b (Figure 1a,b and Figure S5). In contrast, in solid thin films, where conformational motions are limited relative to solutions, the spectra of 2a and 2b do not show such a shift and almost overlap (Figure 2, Figure S7). A similar increase can be seen for quantum yields and lifetimes, which are larger for sulfoxides than for sulfides (Table 2). These data provide arguments for the involvement of intramolecular CT processes in the excited state. Indeed, charge-transfer (CT) states have been observed previously for symmetrically substituted arenes bridged by sulfide at different oxidation levels [26]. For compounds 1c, 2c and 3c, with only one electron-donating methoxy substituent (EDG) on the methylene-1,3-dioxo-anthracene backbone (Figure 1c), a similar tendency for the fluorescence spectra to redshift with the degree of oxidation state is observed, although the absorption spectra reveal the vibronic structure of anthracene to a greater extent than in the case of 1a,b and 2a,b. The greatest shift shows the spectrum of 3c, while the spectrum of 2c, being broader, covers both the 1c and 3c fluorescence spectra, i.e., it contains localised emission from the anthracene molecule and long-wavelength emission from the CT state.
The observed quantum yields and fluorescence lifetimes of 1c and 2c show a similar increasing trend as for pair 1a-2a and 1b-2b, i.e., they are higher for sulfoxide analogues than for the sulfide ones. The sulfone derivative does not show the largest increase in φ and τ as in the case of symmetric chromophores [26]. On the contrary, a significant decrease in these parameters is observed for both studied solvents. Additionally, 3c in EtOH has a bi-exponential fluorescence decay.
For the symmetric bis(methylene-1,3-dioxo)-anthracene moiety, the decreases in quantum yields and lifetimes are more drastic (Table 2). There is no clear redshift of the fluorescence bands associated with expected increasing contribution of CT transitions in the fluorescence process due to oxidation of the sulfide bridge. The emission decays are 2-or 3-exponential with the slow components below 5.7 ns (for EtOH) and 9.5 ns (for toluene). This may indicate the presence of two or three chromophore populations in the excited state due to, among other factors, conformational strain of the five-membered methylene-1,3-dioxolane ring. Then, the non-radiative processes start to play an essential role in the deactivation of the excited state, as well as significantly reducing quantum efficiency.
In conclusion of this section, it should be stated that: (1) with the degree of oxidation of the sulfide bridge, the vibronic character of the anthracene absorption band disappears; (2) no increase in quantum yields as a function of bridge oxidation was observed as for symmetric arenes [26], but a clear increase was observed for sulfoxide derivatives; and (3) EDG substituents on the anthracene backbone have a significant influence on the photophysical processes. Their amount and size facilitate the participation of intramolecular CT processes in both polar and non-polar media.
The room-temperature PL lifetimes (τ) of compounds in series of 1-3 were dependent on the oxidation state of the bridging sulfur.  and d (1c, 1d, 2c, 2d and 3c, 3d), more than one lifetime was measured. For (SO2)-3d, three τ-components were recorded, of which two were very short (toluene/ethanol: τ = 0.47, 3.98 ns/0.16, 0.77 ns) and one relatively very long (toluene/ethanol: τ = 9.46/5.64 ns). For the symmetrically bridged (S), (SO) and (SO2) chromophores, Wolf et al. [31] showed that all of the compounds exhibited prompt lifetimes (<1 ns), while (SO) and (SO2) compounds had multi-exponential lifetimes with a substantially longer (about 30 ns) component, which was two-fold greater than the longest lifetimes, reported for 2a and 2b in the whole a-c series of unsymmetrically bridged chromophores (Table 2). It has been found in the literature that the longest-lived component for symmetrical SOn bridges increases with increasing oxi-dation state of the bridging sulfur atom, in the following order: (S) < (SO) < (SO2); this occurs under both air and argon [31]. The same order was observed in our case for the d series of unsymmetrical compounds, however with a much greater dispersion in the lifetime values. A comparison of the longest-lived components in the c series, showed a different order: (SO2) < (S) < (SO); this may be due to a lower symmetry of the unsymmetrically substituted anthryl core in comparison to the fully symmetrical one in the d series.
The absorption spectra of (S)-1a-d, (SO)-2a-d and (SO2)-3c, 3d in thin films are presented in Figure 2 and their optical properties are summarized in Table 3. In thin films, lower-energy absorption bands are redshifted and broadened, compared with absorption bands in solution, which is attributed to the stronger intermolecular interactions in solid state. The positions of the absorption maxima for (S)-1 and (SO)-2 were practically identical, while the maxima for (SO2) were redshifted by 4-10 nm in comparison to 1 and 2. In PL spectra, slightly higher redshifts of 10-17 nm were observed for pairs of (S)/(SO)-1a/2a and 1d/2d, respectively, while for the pairs of 1b/2b and 1c/2c, a blueshift of 2-19 nm was found. Table 4 shows the CIE 1931 chromaticity coordinates for (S)-1a-1d, (SO)-2a-2d, (SO2)-3c and 3d in toluene and ethanol solutions. The CIE 1931 coordinates for the luminescent materials on the plane of color spaces define the relationship between emitted wavelengths of light and physiologically recognized by humans. The (S)-1a-d emitted blue light both in toluene and ethanol solutions. Only coordinates of the light emitted by the symmetrical (S)-1d, possessing four alkoxy substituents and the 4-methoxyphenylsulfenyl group on the anthracene core, were slightly shifted towards blue-violet part of the CIE 1931 color space chromaticity diagram (Table 2, Figure 3A).

The CIE 1931 Color Spaces-Luminosity Function Compound
Toluene (x, y) Ethanol (x, y) 1a x = 0.1534, y = 0.0891 x = 0.15148, y = 0.09148 2a Oxidation of (S)-1a-d caused a significant, sulfur oxidation state dependent effect, and chromaticity coordinates dispersion from deep blue and blue through blue-green to green color was observed in the resulting (SO)-2a-d (Table 2, Figure 3B). The sulfoxide group S(O), which may form a hydrogen bond with ethanol, caused a further dispersion in chromaticity coordinates for 2a-c, in relation to non-polar toluene. Only in the case of (SO)-2d, a weaker effect of the solvent polarity on wavelength of the emitted blue light was observed. In the series of (SO2)-3c, 3d, the distribution of the coordinates was similar as in the group of (SO), and again in 3d, with electron-donating 4-methoxyphenyl and four alkoxy-anthryl groups around the SO2 bridge, a weaker effect of the solvent polarity was observed (Table 2, Figure 3C). This confirms previous observations made for the series of (S)-1 and (SO)-2 that the increasing number of electron-rich groups at the anthracene core is the main factor responsible for color shifting of the emitted light towards the blue or blue-violet part of the spectrum.

Photochemical Stability
Optical materials should have a high photochemical stability; therefore, all three series of (S)-1a-d, (SO)-2a-d and (SO2)-3c, 3d were exposed to light under anaerobic and aerobic conditions, in ethanol solutions, using two different UV wavelengths of 254 and 365 nm. Photostability under anaerobic conditions and photooxidation stability under aerobic (ambient) conditions were examined by monitoring the 50% loss of absorbance intensity of 10 −5 M ethanol solutions of samples 1-3, first stored in the dark at room temperature, under inert (Ar) or ambient (O2) atmosphere, and next exposed to the UV light of 254 nm (UVP-Hg-Pen-ray lamp, 16.33 mW/cm 2 at a distance 1 cm) and 365 nm (fluorescent lamp VL-6.LC (6W), 27.4 mW/cm 2 at a distance 1 cm). The actual irradiation dose (J/cm 2 ) may be calculated by multiplication of the latter (W/cm 2 ) by exposure time (sec.). Both (S)-1, (SO)-2 and (SO2)-3 revealed enhanced photochemical stability in solution during UV-irradiation at both 254 and 365 nm. In the series of significantly substituted chromophores 1 and 2, the photooxidation stability in the range of 80-249 min. was measured at 254 nm under ambient atmosphere (O2), and even higher photostability in the range of 88-519 min. was found at 254 nm under inert atmosphere (Ar), which turned out to be the highest stability values reported for the π-extended (SO) and (SO2) (Table 5, Figure 4). Surprisingly, there were no significant differences in the 50% loss of absorbance between aerobic and anaerobic conditions at 254 nm for the tested series of (S)-1a-d and (SO)-2ad (e.g., 1a: 254 nm-166 (O2)/175 (Ar) min.; 2a: 254 nm-80 (O2)/88 (Ar) min.), and for 2c and 2d at 254 and 365 nm (e.g., 2c: 254 nm (O2)/254 nm (Ar)/365 nm (O2) = 247/245/254 min.). Only in case of (S)-1b, a significant two-fold increase in photostability was observed at 254 nm under inert versus ambient atmosphere (1b: 254 nm-249(O2)/519 (Ar) min). Another (S)-1d showed the highest photostability at 254 nm (Ar, absorption decay not observed) and photooxidation stability at 365 nm (O2, 812 min.) ( Table 5).  A further detailed analysis shows that the photostability and photooxidation stability of (SO)-2a, 2b and 2d are lower than the corresponding (S)-1a, 1b and 1d, both under ambient and inert atmosphere, but are still much higher than the values, reported in the literature, of unsubstituted, symmetrical 9,9′-bianthryl analogs [31]. Only the (SO)-2c was slightly more stable under ambient atmosphere at 254 nm than its (S) precursor 1c (2c/1c-247 min./210 min.). The highest stability at 254 nm among the (SO) family presented 2b and 2c (251, 245 nm, respectively) with the bulky naphthyl substituent at the S(O) bridge. The compounds (S)-1a-c and (SO)-2a, 2b deserve a special mention due to their extreme photooxidation stability at 365 nm under ambient conditions, which has not been reported in the literature so far. A similar, very high stability showed (SO2)-3c and 3d at 365 nm under the same conditions, for which the absorbance decay was not observed as well (see SM, Figure S8).
Analysis of the UV/Vis spectra of (S)-1a-1d and (SO)-2a-2d (254 nm, air O2/Ar) showed a presence of several isosbestic points, which indicated the co-existence in solution of the starting materials and photo-products. For 1b-1d and 2a, 2b (365 nm, air O2), isosbestic points were not observed, as was also the case for all (SO2)-3 both at 254 and 365 nm (air O2/Ar). For 1a, a weak 50% absorbance decay was observed and only two isosbestic points in a lower part of the UV spectrum could be detected (see SM, Figure S7).
The HRMS-(+)-APCI analysis of the crude reaction mixtures obtained by irradiation of ethanolic solutions of 1-3 for 3 h (air O2, 254 nm, Hg lamp, irradiation dose: 176 J/cm 2 ), did indeed confirm the formation of the oxidized, deoxidized or degraded products, which accompanied the starting acenes, as minor components of the mixtures (see SM, Figures S9-S15).
The characteristic feature for all starting acenes 1-3 was the maintenance of the integrity of anthracene rings without the ring C-C bonds' cleavage. However, in case of (S) 1, aromatic character of the products was destroyed by the oxidation of one or two peripherial or middle ring carbon atoms to ketone groups, while the aromatic character of (SO)-2 and (SO2)-3 was preserved. Thus, in the HRMS-(+)-APCI spectra of (S)-1a, 1b and 1d, two main groups of photo-products were found in the mixtures, which originated from: 1) the addition of oxygen to anthracene rings to initially form endoperoxides or hydroperoxides (not detected), which were subsequently cleaved to phenolic derivatives and further oxidized to 10-ketones or 1,4-anthraquinones; 2) the oxidation of sulfur atoms to sulfoxide [33]. Contrary to (S)-1, (SO)-2a, 2d and (SO2)-3c, 3d preserved aromatic character of photo-products after the 3h irradiation at 254 nm under air O2 in EtOH. Thus, (SO)-2a was photo-deoxygenated to the corresponding (S)-1a, as the main product. This unexpected reduction that occurred under photochemical, aerobic conditions, has earlier been observed for aromatic sulfides by Posner and Gurria under nitrogen atmosphere [35].
According to the authors' suggestions, the reaction most probably occurred via the triplet excited state. Interestingly, reoxidation of (S)-1a back to (SO)-2a and a cleavage of the Ar-S bond were observed to be the main pathways after prolonged contact with air O2 and irradiation of the sample for 9 h under the same reaction conditions (254 nm, EtOH, irradiationdose of 528 J/cm 2 ). On the other hand, (SO)-2d underwent a cleavage of both An-S and Ar-S bonds to a minor extent. After prolonged irradiation for 9 h, the fragmentation of 2d slightly deepened; however, the parent peak remained as the main one in the spectrum, which meant that there was still a good stability of this compound after a threefold increase in the irradiation time. Sulfones (SO2)-3c, 3d, for which isosbestic points were not observed in UV spectra, were stable under the irradiation conditions (3 h, 254/365 nm, air O2/Ar, EtOH). The HRMS-(+)-APCI spectra of (SO2)-3c, 3d were almost identical before and after irradiation, with the main fragmentation leading to desulfonylated species derived from 3c, 3d due to the An-S cleavage. The predominant fragmentation of An-S bonds over Ar-S ones in 3c and 3d may be explained by a relatively large bond lengths and a large An-S /Ar-S difference in DFT calculated bond lengths of the optimized molecules (An-S/Ar-S: 3c-1.82954/1.81225 Å; 3d-1.83695/1.80460 Å). For a comparison, the corresponding bonds in 1 are shorter and stronger, and the An-S /Ar-S difference is negligible (1c-1.79759/1.79689 Å; 1d-1.79941/1.79978 Å). After prolonged exposure to the UV light at 254 nm for 9 h, both sulfones 3c and 3d showed still a good photooxidation stability with the increased cleavage of the Ar-S bond. In order to distinguish fragmentation peaks from the peaks due to the photo-products in the irradiated mixture, a HR(MS_MS)-(+)-APCI fragmentation of single peaks, in the whole spectra, was carried out to conclude that the detected peaks for all investigated compounds were due to the real photoproducts in the mixture.
The stability to photooxidation of the tested compounds 1-3 upon exposure to the UV light at 365 nm (air O2) was obviously much higher than the stability upon exposure to the UV light at 254 nm and no isosbestic points were detected for these compounds in UV spectra.
Due to the lack of broader investigations on photostability and photooxidation stability of SOn (n = 0, 1, 2) bridged chromophores, the stability of the investigated compounds in this study may be compared with photooxidation results obtained at 365 nm for the unsubstituted 9,9′-bianthryl (S), (SO) and (SO2) [31], which are structurally the most similar compounds to the series of significantly substituted mono-anthryl derivatives 1, 2 and 3. While the high photooxidation stability (hours) at 365 nm of the 9,9′-bianthryl (S) was comparable with the high stability of 1, the stability of 2 was many times greater than the stability (seconds) of the 9,9′-bianthryl (SO) [31]. The (SO2)-3 were similarly very stable, while the 9,9′-bianthryl (SO2) underwent chemical reactions (first the episulfone and then the anthraquinone formation) [31]. To our knowledge, unsymmetrical, significantly substituted 1-, 2-and 3-SOn bridged chromophores, obtained by electron-donating alkoxy substituents, are the most stable sulfur compounds of this kind reported to date. At the same time, a lack of photostability and photooxidation stability tests of such compounds at 254 nm should be noted.

DFT Calculations of Molecular and Electronic Structures of 1, 2 and 3. Influence of Sulfur Oxidation State on Stabilization of Frontier Orbitals
The above studies were supported by DFT calculations of molecular and electronic structures of (S)-1a-d, (SO) -2a-d and (SO2)-3a-d in the gas phase, and at the ground state, using the gradient corrected three-parameter hybrid function (B3LYP) with the 6-311++G(d,p) basis set. Full geometry optimizations of these compounds were performed using the GAUSSIAN 09 quantum chemistry package (coordinates of atoms for all optimized geometries are given in Tables S1-S12). Analysis of shape and values of the HOMO-LUMO energy was carried out for twelve RS-, RS(O)-and RS(O2)-acene derivatives, organized in three a-c series. (Figure 5). The analysis showed that HOMO and LUMO orbitals, for each molecule, were mainly located on the system of fused aromatic rings with exception of 1d, for which the HOMO orbital was located also on the 4-methoxyphenylthio group. A comparison of the HOMO and LUMO energy values (Figure 6a) (in 3a) caused a further orbital stabilization and decrease in the HOMO and LUMO energies to −5.607 eV and −2.160 eV, respectively. The same trend was observed in all three a-c series of compounds (Figure 6a-d). The decrease and stabilization in the HOMO and LUMO energies are correlated well with the increase in the sulfur oxidation degree in the following order: (S) < (SO) < (SO2); in addition, the electron-acceptor character of the SOn bridge increased in the same order. The measure of the latter effect is the Hammett σp constant. For instance, the σp values calculated using ACD/Percepta [36] were 0.07, 0.44 and 0.68 for PhS, PhS(O) and PhS(O2) substituents, respectively, and 0.13, 0.39 and 0.77 for 4-MeOC6H4-S, 4-MeOC6H4-S(O) and 4-MeOC6H4-S(O2) substituents, respectively. The small but positive values of σp constants confirm a weak electron-acceptor character of the RS groups in all cases, when attached to electron-rich anthracenes substituted by five (a, b series), four (d series) and three (c series) electron-donating alkoxy groups [16]. Analysis of the σind and σres components shows that a mostly negative inductive effect (-I) is responsible for the electron-withdrawing character of the RS-groups in the electron-rich aromatics (e.g., SPh: σind/σres = 0.31/−0.24; S-Naphth: σind/σres = 0.3/−0.15). The (-I)  The final conclusion is that the observed high photochemical stability of 1-3 comes from the lowering of the LUMO energy level. The lower LUMO makes the compounds more resistant to photooxidation, which usually occurs via electron transfer (Type-I) or/and energy transfer (Type-II) mechanisms [37,38].

Conclusions
The most striking result obtained in this study is related to the very high, hitherto unrecorded photostability and photooxidation stability of the significantly ring substituted acenes, (S), (SO) and (SO2), under both anaerobic and aerobic conditions, at 254 and 365 nm. These stabilities are many times higher than stabilities under similar conditions of less sterically hindered or unsubstituted analogs that are known in the literature, which makes them promising materials for optoelectronics, photocatalysis and other areas requiring photostable compounds. The high photochemical stability is associated with the effect of the sulfur oxidation state and a significant substitution at the aromatic core by electron-donating groups. This leads to the formation of stable donor-acceptor systems, in which a negative, inductive effect (-I) from the RS(On) groups is responsible for electronaccepting properties, and the (+M) effect of alkoxy substituents is due to electron-donating properties (Hammett's constants, vide supra). The enhanced photooxidation stability (hours) of the obtained, unsymmetrical, significantly substituted (SO) was particularly striking, compared to the literature photooxidation stability results (seconds) in symmetrical, unsubstituted bianthryl (SO) at 365 nm [31]. The high stabilities in the obtained (S), (SO) and (SO2) series was supported by DFT calculations, which revealed the leading role of the SOn groups in lowering and stabilization of HOMO and LUMO frontier orbitals, making the mechanisms responsible for the anthracene oxidation more difficult [37,38].
This study also shows other photophysical/photochemical properties of the new groups of bridged, unsymmetrical, donor-acceptor SOn (n = 0, 1, 2) chromophores of a dominant electron-rich character, based on a significantly substituted anthracene core. The study complements the literature investigations on symmetrically SOn bridged, unsubstituted analogs. The (S) substrates were synthesized via the thio-Friedel-Crafts-Bradsher (thio-F-C-B) cyclization [33] as an extension of the oxo-variant of this reaction [39][40][41][42][43][44][45][46][47], while (SO) and (SO2) were obtained by a successive oxidizing of the sulfide bridge. The thio-F-C-B reaction is also a tool to introduce a significant substitution on the mono-RS-acene (anthracene) core, which also remains in the (SO) and (SO2) products after oxidation. This makes all three groups of compounds easily tunable optoelectronic materials that are of high photostability and high photooxidation stability. For instance, the colour of the emitted light can be tuned from blue-violet to green depending on the sulfur oxidation state, the number of electron-donating groups on anthracene, and the kind of solvent.
We believe that the findings herein will spur further interest and development in the unexplored area of photochemical behaviour of significantly substituted, SOn (n = 0, 1, 2)bridged chromophores, both symmetrical and unsymmetrical, based on larger acenes than anthracene.

Data Availability Statement:
The datasets generated and analyzed during the current study are available from the corresponding author on reasonable request.