Performance of Rice Husk Ash as Supplementary Cementitious Material after Production in the Field and in the Lab

Supplementary cementitious materials (SCM) can reduce the total amount of Portland cement clinker in concrete production. Rice husk ashes (RHA) can be converted from an agricultural by-product to a high-performance concrete constituent due to a high amount of reactive silica with pozzolanic properties if they are burnt under controlled conditions. The way and duration of combustion, the cooling process as well as the temperature have an effect on the silica form and thus, the chemical and physical performance of the RHA. Various studies on the best combustion technique have been published to investigate the ideal combustion techniques. Yet, the process mostly took place under laboratory conditions. Investigating the difference between the performance of RHA produced in a rural environment and laboratory conditions is useful for the assessment and future enhancement of RHA production, and its application both as building material, for example in rural areas where it is sourced in large quantities, and as additive for high performance concrete. Thus, the paper presents a comparison between RHA produced under rudimentary conditions in a self-made furnace in the rural Bagamoyo, Tanzania and under controlled laboratory conditions at the Technical University of Munich, Germany, with different combustion methods and temperatures. In a second step, RHA was ground to reach particle size distributions comparable to cement. In a third step, cement pastes were prepared with 10%, 20% and 40% of cement replacement, and compared to the performance of plain and fly ash blended cement pastes. The results show that controlled burning conditions around 650 °C lead to high reactivity of silica and, therefore, to good performance as SCM. However, also the RHA burnt under less controlled conditions in the field provided reasonably good properties, if the process took place with proper burning parameters and adequate grinding. The knowledge can be implemented in the field to improve the final RHA performance as SCM in concrete.


Introduction
Concrete production and construction contribute to global carbon emissions and therefore climate change in many ways. Without paying attention to further environmental effects like land use, each ton of cement thus emits 600-900 kg CO 2 due to the decomposition of calcium carbonate to calcium oxide, the energy demand, processing and grinding [1,2]. Thus, cement production accounts for 5-8% of the total global anthropogenic carbon dioxide emissions [3][4][5]. While processing techniques in cement mills are permanently optimized, carbon emissions due to calcination cannot be prevented unless Despite their potential as high-performance concrete constituent, approximately 115 Mio tonnes of rice husks stay unused agricultural waste annually [33], and at the same time, cement is the most cost-driving factor in Sub-Saharan Africa [34]. In addition to environmental aspects, the design of circular value chains from agro-wastes to building materials could also reduce material costs and, thus, strengthen the wealth of emerging areas, provide prospective sustainable building solutions, creating livelihoods and prevent depositing agricultural wastes.
This paper aims to compare and optimize the combustion and the grinding process of RH under controlled conditions in the laboratory, and easy combustion techniques on the countryside in a self-made furnace, to obtain more knowledge for producing amorphous silica of adequate particle size. Despite the extensive literature regarding the use of RHA as SCM, the direct comparison of one material after different treatments and, thus, possible building material in the field or high quality product after treatment in the lab is missing. Therefore, the study results serve as a basis for further studies on the use of RHA in concrete.

Previous Studies on the Use of RHA as SCM
Worldwide, there are approximately 22 species of rice with different chemical compositions [33]. With only two species being relevant for human consumption, the chemical composition, i.e., the alkalinity, salinity and acid-sulphur amount, depends on the water and soil supply during cultivation [35]. Thus, not only of the raw material, but also the produced ashes, contain various amounts of trace elements. During combustion, the organic parts of the husks are decomposed. After combustion ideally all organic components are removed, by weight 17-18% of ash remain from the husks [36]. The dominating remaining chemical components are silica (typically more than 85%, up to 98% [37]) and trace elements like potassium, calcium, aluminum, iron and magnesium. Even though the variation of trace elements can affect the final performance of RHA, pozzolanic activity is always given, due to these high amounts of reactive silica.

Combustion, Cooling and Grinding of RHA
Combustion techniques can be either direct or indirect. Direct burning, i.e., when used for energy supply, leads to ashes with varying qualities with regard to the chemical composition and the purity of the silica [36]. The indirect burning of the husks, i.e., combustion in a two-chamber-system, leads to a better control of combustion temperatures and thus more homogenous burning. The quality of these ashes is typically higher. Calcination temperature and heating rate determine the final reactivity, i.e., the pozzolanic index of the RHA [38]. Research on the most appropriate burning temperatures, combustion times and heating and cooling rates often found that appropriate combustion temperatures are between 500 and 800 • C [26,[39][40][41][42][43]. Below 500 • C, organic material remains in the ash. Above 800 • C, silica changes its structure from amorphous to crystalline which decreases the pozzolanic reactivity between remaining portlandite (C-H) from the first hydration reaction and silica from the RHA: with a crystalline structure of silica, a pozzolanic phase reaction of strength forming hydrates, i.e., C-S-H formation, is not possible. The heating rate, indeed, affects the porosity of the RHA: Chandrasekhar et al. investigated increasing pore volume with increasing heating rates [38]. Meanwhile, the reactivity increases with increasing porosity, due to higher inner specific surface area and, thus, has a positive effect on the final strength [38], but a negative effect on water adsorption and workability [34,44].
The combustion time depends on the amount of burnt ashes: in most ongoing research, combustion times under controlled conditions are below one hour [28]. On the other hand, Nair et al. reported that combustion temperatures at 1000 • C are possible if the combustion time is less than five minutes [44]. Moreover, the oxidation supply influences the silica form: with little oxidizing conditions, i.e., slow cooling with moderate oxygen supply, the silica appears in amorphous form. A highly oxidizing environment results in crystalline forms of the silica. In summary, the most appropriate combination of combustion temperature and time differs with changing furnace structures and geometries, the volume of burnt rice husks and the processing and control of heating and cooling rates. The production of RHA in controlled laboratories, where indirect burning under controlled temperatures and heating rates is possible in advanced muffle ovens and furnace systems, leads to the purest amorphous structures and, thus, the highest reactivity.
The grinding process determines the fineness of the RHA. With increasing grinding energy and time, the mean particle diameter of RHA decreases. For example, Le describes the decrease in mean diameter from 86.2 µm at 0 min grinding time to 5.7 µm to 540 min grinding time in a ball mill [31]. Due to its structure, sometimes described as a honeycomb structure, the specific surface area is normally 10 to 100 times higher than that of cement, and five to ten times higher than for silica fume [32]. Values from investigation via Brunauer-Emmett-Teller (BET) of properly burnt RHA are in the range of 100-150 m 2 /g [32,45]. With increasing fineness, the inner porosity of RHA decreases. A good overview of effects on chemical and physical composition induced by various parameter variations, such as combustion time, temperature and grinding technique, can be found in Fapohunda et al. [46].

Application of RHA in Practice: From Rural Combustion to High-Performance Concrete
The application possibilities of RHA in practice vary, depending upon existing infrastructure and material supply in different regions in the world, as well as the respective state of the art and research development. Rural combustion techniques offer the possibility of material performance increase, especially in areas where ordinary Portland cement (OPC) is scarce and expensive. Application-oriented furnace-systems besides the lab were invented i.e., by Pitt [47] and Zain et al. [48]: in 1976, Pitt invented a whole furnace system for proper combustion of agricultural wastes in a two-step-approach with a cyclone separator to prevent emerging flue gases. Zain et al. invented a furnace with either one or more steel pipes in the combustion chamber for an effective use of fuels and an exact adjustment of combustion temperatures [48]. Especially the invention by Zain et al. is applicable as an easy combustion method in rural areas. Further similar furnace inventions can be found in [39,42,44].
The subsequent use of RHA burnt under uncontrolled conditions leads to either improved or reduced concrete properties regarding strength and durability, depending on both the characteristics of the pozzolanic activity of RHA, the amount of replacement and the concrete mixture composition itself. The use of uncontrolled burnt RHA often also leads to a decrease in strength and durability properties [49][50][51].
Nevertheless, the production and application of RHA has advanced within the past years. Properly ground RHA, in combination with low w/c ratios and fluidizing admixtures, can lead to a highly reactive blended cementitious system and improved concrete properties [32]. In 2001, Bui developed a material concept for the use of RHA as mineral addition in high performance concrete [45]. In 2011, Nguyen et al. developed this approach further by investigating the use of RHA for ultra-high performance concrete (UHPC) [52]. In 2015, Le investigated especially fresh concrete properties of concrete containing RHA [31]: concerning rheology, Le designed self-compacting concrete (SCC) with RHA. Msinjili et al. investigated rheological properties of RHA blended cement mixtures containing various PCEs [34], whereas Schmidt et al. proposed SCC mixtures making use of the synergistic effect of RHA and limestone filler. While the RHA significantly increased the strength, the workability was drastically reduced. Limestone filler helped to improve the workability, but reduced the strength. A reasonable adjustment allows to significantly reduce the overall Portland cement clinker content without performanceloss. Finally, SCC with RHA was possible by using a combination of lignosulphonate plasticizer and cassava starch as rheology modifying admixtures [53,54].
However, the potentials for applications are lagging behind the research progress in this area: there is no approved and validated common production technique to gain pozzolanic material. Standards for concrete production with RHA do not exist, whereas common SCMs like fly ash or silica fume are mostly regulated all over the world.
The slow progress in implementing RHA in official standards might be caused by inhomogeneities in the material itself, but also the relatively low material amounts annually, compared to the material amounts of other additives. Moreover, big amounts of rice husks grow in countries with relatively low income and little possibilities and inadequate funding for basic infrastructure, further research and development of common building materials. At the same time, cities and communities deal with rapid growth of population and, thus, the need for increased construction and material supply, which leads to relocation, depletion, the emergence of low-income disadvantaged settlements and, consequently, a rapid exploitation of natural resources [55]. Locally available resources need to be investigated, combined with local traditional building techniques and improved for standardization and thus general building applications. RHA as product from a renewable resource can be a proper building material for both, rural production and application and extensive application in concrete production as addition with standardized procedures.
In summary, the production of RHA in research makes it a possible additive in modern concretes like UHPC and SCC. Combustion methods most often can be adopted from existing combustion systems and enhanced for the special needs of RHA. The presented experimental investigations reach to combine both rural combustion and advanced laboratory research to find the gap between the two methods of production and application. The results shall be used as the basis for the development of RHA production and application both for areas with cement supply shortage and low-cost housing and prospective cement reduction possibilities concerning the reduction of carbon emissions in more industrialized economies. These topics can be combined by considering the need for sustainable urban development and ongoing research regarding the circular economy and circular bio-based value chains, especially with the shift from rural to urban application [20].

Concept of Investigation
Rice husks were collected by the authors in Bagamoyo, Tanzania. They were washed with pure water, sundried and not treated further. Combustion possibilities of the rice husks for the application as SCM in concrete were investigated both under rural conditions in Bagamoyo, Tanzania and laboratory conditions in the Center for Building Materials in Munich, Germany. The production of the ashes focused on changing the parameters combustion temperatures and grinding values. The main goal of the investigations was to (1) examine the physical and chemical parameters of produced RHA under controlled and uncontrolled conditions, (2) determine the most appropriate combustion and grinding technique and (3) estimate the application possibilities of controlled laboratory treatment to the field. The physical and chemical parameters of the RHA were investigated using laser granulometry for the investigation of particle size distribution, BET analysis for the estimation of specific surface area, scanning electron microscopy (SEM) for the investigation of the surface structure, inductively coupled plasma optical emission spectrometry (ICP-OES) for the chemical composition and X-ray diffraction (XRD) for the quantitative investigation of amorphous phase content.
In a second step, cement pastes were prepared with varying substitution ratios of cement with RHA or fly ash: in three test series, pastes were prepared with 10%, 20% and 40% RHA by weight of cement (bwoc) cement replacement, respectively. Strength tests were conducted after 28 and 56 days.

Combustion Variation
RH were burnt both under uncontrolled conditions with a self-made furnace (Figures 1 and 2a) and for comparison under controlled conditions in a muffle oven in a laboratory (Figure 2c). The sample designation, given by the variation of controlled and uncontrolled combustion conditions, is shown in Table 1.   Combustion under rural conditions took place in a simple self-made furnace, shown in Figure 1: the furnace consisted of a two-chamber system for indirect burning of the husks (Figure 1a). Husks were filled until 0.75 m height in the chamber above the combustion chamber (Figure 1b). Five steel pipes were installed with a diameter of 7.0 cm (Figure 1c). The steel pipes ensured an even heat distribution within the chamber. Fuel could be either charcoal or timber. Charcoal possesses a higher caloric value and, thus, reaches higher temperatures and longer burning times. Tests were conducted with both timber and charcoal: with timber, temperatures around 500 • C were reached. With charcoal, higher constant temperatures between 800 and 1000 • C could be reached. The temperature measurements were conducted with a high temperature thermometer from Professional Instruments, China. Controlled combustion was achieved with a muffle oven in Figure 2c. Temperatures of 450 • C and 650 • C were chosen, following the recommendations of existing studies [30]. For each combustion process, in Figure 2d, only a small amount of husks were burnt, to ensure homogeneous combustion and oxidizing environment. The small sample amount allowed short combustion durations of 30 min, respectively. The husks were only stored in the muffle oven after it reached the combustion temperature. The combustion procedure created homogeneously burnt ash of white color (Figure 2d). After combustion, the RHA was directly cooled down without monitoring the cooling rate.

Grinding Variation
The RHA were ground in a ball mill (Cryomill, Retsch, Germany) with varying grinding times and frequencies. The chosen grinding parameters are given in Table 2. The parameters were adjusted in a stepwise approximation. After grinding, particle size distribution was investigated using laser granulometry with a Mastersizer 2000, Malvern, UK. The specific surface area (SSA) was calculated using the Blaine method. The particle size distribution (PSD) as well as the mean diameter (d 50 ) were investigated. Furthermore, the specific surface area (SSA) of the ground RHA was measured by BET nitrogen adsorption method using a Belsorp II Mini (Microtrac BEL, Haan, Germany).

Characterization Methods
Chemical and phase composition was conducted through X-ray diffraction measurements (XRD). The measurements were conducted with a Bruker D8 Advance Diffractometer (Bruker Corporation, Billerica, MA, USA) with Cu Kα radiation and a high-resolution energy-dispersive detector LYNXEYE-XE. The analysis was carried out with automatic divergence slit; 5-70 • 2Theta angle range; 0.02 • 2Theta step size; 0.2 s measurement time per step; 40 kV voltage and 40 mA current intensity. The resulting peaks were identified based on existing data bases. The Rietveld refinement was used for the quantitative analysis of the results.
XRD can only detect crystalline phases. Accordingly, the amorphous content was investigated by measuring the remaining crystalline amount. The RHA powder for XRD samples was prepared using a ball mill (Cryomill Retsch, Haan, Germany) at 20 HZ and grinding for 20 s. Scanning electron microscopy (SEM) with coupled energy dispersive X-ray spectroscopy (EDS) was conducted on the RHA powder using the FlexSEM 1000 from Hitachi, Japan. ICP-OES analysis using the Avio 500 (PerkinElmer, Germany) finally showed the elementary distribution of RHA.

Compressive Strength Tests: Mixture Composition
For compressive strength tests, cement paste prisms with both pure cement and cement with fly ash of 15 mm × 15 mm × 60 mm were prepared. Cement pastes were mixed containing OPC (CEM I 42.5 R, Heidelberg Cement, Heidelberg, Germany; technical characteristics given in data in brief by Lu et al. [56]) and demineralized water. Fly ash was supplied by Powerment GmbH, Germany. The chemical composition is given in Table 3. The cement was stored at 20 • C without solar irradiation; the added water temperature was 8 • C for a controlled paste temperature at 20 • C. The mixture proportions of all test series for compressive strength tests are given in Table 4. Pure cement paste with a water/cement ratio (w/c ratio) of 0.5 was prepared as reference series (100CEM). Five further test series were conducted. Outgoing from the combustion and grinding analysis, two RHA from the field in Bagamoyo, Tanzania (Uncontrolled U1 and U2) and two RHA after controlled combustion at 450 • C and 650 • C (C450 and C650) were chosen. For an estimation of RHA as SCM in comparison to other pozzolanic SCMs, cement paste containing fly ash (FA) was prepared. For all testing series, the cement amount was stepwise replaced by 10%, 20% and 40% of FA and RHA, respectively. The cement replacement was chosen by the weight of cement for a controlled water/binder ratio (w/b) of 0.5 at all test series. In accordance with different material densities (measured by helium pycnometry, AccuPyc 1330 pycnometer, Micromeritics, Norcross, GA, USA; values are given in Table 3), the fresh paste densities and therefore the hardened paste densities varied.  The pastes were prepared in a bucket with a standard drilling machine and a four-bladed stirrer at a shear of 1700 min −1 to ensure a homogeneously mixed paste. For each mixture, a paste volume of 300 mL was prepared. The mixing time was 90 s. The produced cement prisms were stored for one day before striking and subsequently stored for 28 days, respectively, under water at 20 • C room temperature and 65% rel. air humidity. The compressive strength tests were conducted using a testing machine from Walter+Bai, Germany. For each mixture, six cement prisms were tested on compressive strength. The mean values and their standard deviation were calculated from six values for each mixture.

Physical and Chemical Properties of RHA
The produced RHA are shown in Figure 3a-d. Table 4 shows the material and chemical properties of produced RHA. The density p in [g/cm 3 ] was measured by helium pycnometry. The CEM I 42.5 R possesses a mean raw density of 3.11 g/cm 3 . The density for the RHA varies between 2.25 and 2.32. The grinding results for different grinding parameters are given in Table 5; the particle size distribution (PSD) for each presented grinding series is given in Figure 4, together with the PSD of cement and fly ash. Whereas RHA_f15 contains higher volume fractions at large particle size diameters, the PSD of RHA_f25 shows a significant shift to the smaller particle size diameters. RHA_f20 possesses similar particle size diameters as the used OPC CEM I 42.5 R. Still, the inner surface of RHA cannot be detected using Blaine method or laser granulometry. Therefore, BET analysis of the ground RHA represents the difference in specific surface area for the used cement and the RHA_f20, considering the inner surface of the material: even if the particle size distribution seems to be similar (cf. Figure 4), the BET for RHA is the tenfold.    Figure 5c with 300 SE to present the unground RHA structure). Whereas the cement possesses its well-known dense crystalline structure (Figure 5a), RHA is visibly porous. The morphology of the samples U1 and U2 is shown before it was ground. As well as the apparent porosity, especially in Figure 5d, the SEM of U1 in Figure 5c also demonstrates the partly kept husk structure with honey-comb like texture on the husks' inner surface. Nevertheless, the appearance after proper grinding are given in Figure 5e,f. They present lower porosity but ash patterns and similar outer morphology as cement particles.
SEM-EDS and ICP-OES show the silica phases that are contained in all test samples. The chemical composition from ICP-OES analysis is given in Table 4. The silica content is above 90 M-% for all test samples. C650 contains the highest silica content with about 95% and at the same time very low remaining carbon (0.59%). Even if the C650 contains the highest silica content, the RHA from uncontrolled burning contains only 1% less silica and slightly higher carbon values. For the verification of an amorphous structure of the silica phases, XRD in conducted. The XRD patterns for all RHA samples are given in Figure 6. Except for slight amounts of remaining crystalline quartz and further mineral phases, the whole structure is amorphous. The samples U1 and U2 contain slightly more crystalline phases, with a broader variety of mineral structures. Comparing the combustion process and the results on the chemical composition, it can be concluded that temperatures around and higher than 450 • C lead to high silica contents if the husks are accumulated, oxidized and burnt homogeneously. Uncontrolled combustion leads to broader chemical distributions within one batch. Controlled combustion, nevertheless, enables a uniform supply of oxygen and, thus, an equal batch with high amorphous silica content.
The presented results show the effect of treatment parameters on the resulting chemical and physical performance. The literature review on the treatment of RHA already described the effect of combustion, grinding and cooling on the performance as SCM. Based on this review of the literature, the treatment parameters for the rice husks were chosen. Generally, the results of the experimental program show a good correspondence with the theoretical background. Particle size distributions similar to cement paste with at the same time high porosity (investigated by BET gas adsorption) could be reached through tuned grinding parameters. With the adjustment of combustion temperature and time, amorphous silica phases were produced. RHA with high amounts of amorphous silica could be obtained if the burning temperature was within a proper range. all RHA samples are given in Figure 6. Except for slight amounts of remaining crystalline quartz and further mineral phases, the whole structure is amorphous. The samples U1 and U2 contain slightly more crystalline phases, with a broader variety of mineral structures. Comparing the combustion process and the results on the chemical composition, it can be concluded that temperatures around and higher than 450 °C lead to high silica contents if the husks are accumulated, oxidized and burnt homogeneously. Uncontrolled combustion leads to broader chemical distributions within one batch. Controlled combustion, nevertheless, enables a uniform supply of oxygen and, thus, an equal batch with high amorphous silica content.
The presented results show the effect of treatment parameters on the resulting chemical and physical performance. The literature review on the treatment of RHA already described the effect of combustion, grinding and cooling on the performance as SCM. Based on this review of the literature, the treatment parameters for the rice husks were chosen. Generally, the results of the experimental program show a good correspondence with the theoretical background. Particle size distributions similar to cement paste with at the same time high porosity (investigated by BET gas adsorption) could be reached through tuned grinding parameters. With the adjustment of combustion temperature and time, amorphous silica phases were produced. RHA with high amounts of amorphous silica could be obtained if the burning temperature was within a proper range.    The compressive strength for pure cement paste is given as light grey dashed reference line in Figure 7; the values are 62. 5  A comparison of the strength values and the corresponding dotted reference lines of percental cement amount gives an intention of the additional pozzolanic strength gain. Except for the fly ash, nearly all test series with RHA possess higher strength values than a theoretical corresponding mixture with the same amount cement and inert material. Still, there is no overall consistency in cement replacement and strength test results. Generally, 40% replacement lead to a strong decrease in compressive strength, whereas 20% replacement can even improve the performance. At the same time, especially mixtures with 40% RHA show much higher values than their corresponding dashed line of 60% cement-the additional reactivity due to RHA is especially high for C450 and C650. The strength performance of cement with RHA nevertheless is not only dependent on additional strength gain due to pozzolanic activity, but on various additional factors. This material behavior can be explained considering the differing chemical and physical properties. Generally, high silica amounts improve the pozzolanic activity. As could be shown by the chemical analysis, ashes with high purity of amorphous silica and low carbon contents could be reached. C-S-H nevertheless is only formed with remaining portlandite from the first hydration reaction of cement with water. Cement replacement values of 40%, thus, could lead to lower strength, because not all silica from the husks can react with free portlandite. Results of 40% cement replacement, however, could be possible by considering physical factors like increased and optimized packing density compared to pure cement paste, or cement paste with fly ash. A proper amount of fine ground RHA could result in the most appropriate packing density and, thus, the highest reactivity environment.

Cementitious Paste Results
Finally, it also should be noted that the standard deviations for all test series are quite high compared to standardized mortar or concrete tests. The reason could be either inhomogeneities in the material due to processing, but also the geometry factor of the tested blocks: with only 15 mm × 15 mm × 60 mm, deviations due to boundary conditions might lead to increased scatter.

Conclusions
The contribution of this paper focuses on the effective treatment and final performance of rice husks under controlled and uncontrolled environments. The investigations present a comparison between uncontrolled and controlled burnt rice husk ashes. The chemical composition of differently burnt husks in dependence of burning conditions and temperature in the field were compared to RHA produced under set conditions in the lab. The grinding process was optimized for rice husk ash compared to cement. Due to its inner porosity, RHA contains the tenfold specific surface area compared to cement under similar particle size distributions.
Comparing the results of RHA production in the field and in the lab, the following concluding remarks can be made: (1) Rice husk ash production in the field under rural conditions is possible in comparable qualities as controlled laboratory production if the furnace geometry is advanced and production parameters like burning temperature, time, heating and cooling rate and especially heat supply and distribution during the burning are controlled. The grinding value and thus physical characteristics affect the final pozzolanic performance strongly: the extremely high surface area values of RHA lead to more reactive sites for a pozzolanic reaction. Still, its high porosity leads to increased water demand. (2) The first furnace approach in this study worked out for a proper heat supply for the produced amount of RHA with the system of five steel pipes. Various researchers have investigated and successfully implemented burning systems for agro-wastes, and our very cost-efficient and easy to implement furnace development could show adequate final chemical and physical properties for a pozzolanic ash as well. (3) Controlled combustion and grinding methods lead to homogeneous RHA with high amorphous silica amounts. With changing material amounts and furnace geometries, these parameters need to be adjusted. In particular, the most effective burning temperature and time needs to be assessed for low-energy production.
Nevertheless, the present investigations contain gaps in efficient production and use of RHA as supplementary cementitious materials. Still, the possibilities for more effective and ecological use both for rural areas and for acceptance as common building material could be shown. Therefore, as a first approach, the following indications can be made: (a) For efficient energy use, rice husks could be burnt directly. If only low external incinerating energy is needed for a subsequent self-combustion, processing costs and emissions can be reduced. Furthermore, the gained thermal energy from combustion should be stored and supplied e.g., in surrounding households, for continuing the incineration of the RHA furnace or supplied to an outer energy network. Especially for low-income areas, the implementation of a full production line from agro wastes to building materials under energy production will lead to increased wealth. (b) Rice is globally available and among the most used crops in the world. As renewable resource its husks provide material for the construction sector constantly. Even if the final RHA amounts are not comparable to those of limestone, clays or finally produced clinker, the possibility of each ecologically friendly building material needs to be investigated internationally for common use. This requires international standards and quality production both of RHA and concrete containing RHA. Thus, further investigations need to be made regarding strength, and especially durability performance.
Finally, the investigations regarding the proper treatment of rice husks and the subsequent use of RHA as SCM could show good results, especially regarding the performance of RHA produced in the field. Ongoing research focuses on both microstructural and application improvements. Performance tests according to existing standards together with material development might lead to both better knowledge about various rural application methods, as well as high-performance material and admission and thus broad use as prospective concrete addition. Various leading institutions, like RILEM, fib, etc., recently described the urgent need of sustainable material solutions for the growing demand of concrete [57]. RHA could be one of them.