The Effect of UV Irradiation on the Chemical Structure, Mechanical and Self-Healing Properties of Asphalt Mixture

Although huge numbers of investigations have been conducted for the ultraviolet (UV) aging of asphalt binder, research rarely focuses on the asphalt mixture. In order to evaluate the aging effect of UV radiation on the asphalt mixture, a dense grade of asphalt mixture was designated and aged by UV radiation for 7, 14 and 28 days respectively. After that, the chemical functional groups of asphalt binder were tested by Fourier transform infrared spectrometer (FTIR). The semi-circular bending strength and fatigue resistance of asphalt concrete were tested to characterize the mechanical properties of the asphalt concrete. To evaluate the self-healing effect of the macro-structure continuity of asphalt concrete intuitively, the computed tomography (CT) scanning machine was used to characterize the crack size of asphalt concrete samples both before and after self-healing. The results show that, with the increase of UV irradiation time, the relative ratios of the C=O and S=O bands’ areas of recovered asphalt binder increase significantly. UV radiation can significantly weaken the mechanical and self-healing properties of asphalt mixture, making the asphalt mixture to have worse macro-structure continuity, lower failure strength and worse fatigue resistance. Moreover, the longer the UV irradiation time is, the degradation effect of UV radiation on asphalt mixture becomes more obvious.


Introduction
For the complex work condition of asphalt pavement, there are many factors that can affect the service span, such as the vehicle, temperature [1], water and UV radiation [2][3][4]. Therefore, in general, the service time of asphalt pavement is always shorter than its designated life. UV radiation has attracted more and more focus for its significant aging effects on the asphalt materials [5]. After UV aging, the elemental ratios and chemical components of asphalt binder are changed [6], which results in the deterioration of physical and rheological performance of asphalt binder and the pavement performance of its concrete [7][8][9]. Especially for the areas with high intensity of UV radiation, the aging effect is more obvious [10].
In the previous work [11], the researchers conducted much work on the UV aging mechanism and aging effects on the technical performance of asphalt materials. For instance, Vallerga [12] used UV radiation and infrared light to irradiate the asphalt film in a film oven respectively and the results indicated that UV radiation could significantly affect the softening point and ductility of asphalt binder, therefore the UV radiation was an important factor causing the aging phenomenon of asphalt binder. Zhang [13] studied the aging effect of three types of aging methods namely thin film oven test (TFOT), pressure aging vessel (PAV), and UV radiation, the results showed that the UV aging and PAV aging have more obvious effects on the degradation of styrene-butadiene-styrene (SBS) polymer. Glotova [14] studied the effect of UV aging on asphalt binder by testing the chemical properties, structures and composition contents of asphalt binder before and after aging, and found that UV radiation has obvious degeneration effects on these properties, and the type of light irradiation also has a close relationship with the photo-oxidation aging speed. Wu et al. [15] used a high-pressure mercury lamp to irradiate both a base asphalt binder and a polymer modified asphalt binder; the results of the Fourier infrared test and dynamic shear rheometer (DSR) test also showed that UV radiation can obviously age the asphalt binder, and different intensities of UV radiations caused different aging effects. The above research verifies the degradation effects of UV radiation on the technical performance of asphalt materials, and it is truly important to investigate the degradation behaviors of this.
Compared with the asphalt binder, there was less work focused on the UV aging effect of UV radiation on the pavement performance asphalt mixture. In fact, the UV radiation always directly affects the asphalt mixture during the service period of pavement [16], so conducting the UV aging test on the asphalt mixture is better to simulate the true service situation of the asphalt road. In this research, a dense grade of asphalt mixture with the nominal maximum aggregate size of 13.2 mm (AC-13) was designated, and aged by UV radiation for 7, 14 and 28 days respectively. After UV aging, the mechanical performance of asphalt concrete was tested by a semi-circle bending test and the anti-fatigue properties of asphalt mixture were investigated by three-point bending fatigue test.
On the other hand, basing on Reference [17], it can be found that the thermal oxidative aging (85 • C for 240 h) can decrease the mechanical performance and healing levels of asphalt concrete obviously. Although the mechanism of thermal oxidative aging of asphalt material is not at all the same with UV aging, the effect tendency on the performance is somehow the same [18], so that UV aging may also cause a significant effect on the self-healing performance of asphalt concrete. In this research, the chemical functional groups of asphalt binder were tested by Fourier transform infrared spectrometer (FTIR). The healing index of the mechanical performance of asphalt concrete was investigated to characterize the self-healing performance. Meanwhile, a computed tomography (CT) scanning machine was also used to quantitatively test the crack size of asphalt concrete before and after self-healing. The results can be used to express the degradation behaviors of the chemical structure, mechanical and self-healing properties of asphalt mixture exposed during UV irradiation.

Materials
The most commonly used asphalt mixture with the nominal maximum aggregate size of 13.2 mm (AC-13) was designated for the UV aging simulation test. The asphalt binder used in this research was base asphalt with penetration grade of 60/80. The physical performance and dynamic viscosity of asphalt binder are shown in Table 1.  [20] ASTM D113 [21] ASTM D4402 [22] The mix ratio of asphalt mixture was ensured with the Marshall method. The optimum oil-aggregate ratio of the asphalt mixture is 4.7%. The ratios of different grades of aggregate were 13.2-16.0 mm:9.5-13.2 mm:4.75-9.5 mm:2.36-4.75 mm:0-2.36 mm:filler = 3:15:33:13:32:4. The aggregate was basalt and the filler was the fine powder of limestone. The composite aggregate grading of the asphalt mixture is given in Figure 1. The volume parameters of asphalt concrete are shown in Table 2.
Materials 2019, 12, x FOR PEER REVIEW 3 of 16 [20] [21] The mix ratio of asphalt mixture was ensured with the Marshall method. The optimum oilaggregate ratio of the asphalt mixture is 4.7%. The ratios of different grades of aggregate were 13.2-16.0 mm:9.5-13.2 mm:4.75-9.5 mm:2.36-4.75 mm:0-2.36 mm:filler = 3:15:33:13:32:4. The aggregate was basalt and the filler was the fine powder of limestone. The composite aggregate grading of the asphalt mixture is given in Figure 1. The volume parameters of asphalt concrete are shown in Table  2.
. Figure 1. Composite aggregate grading of the asphalt mixture. The irradiation intensity of UV light used in the UV aging simulation test of asphalt mixture was 21 w/m 2 , which was produced by four UV lamps, the power of every UV lamp was 500 W. The aging time was 7 days, 14 days and 28 days respectively. The wavelength range of the UV radiation was from 200 nm to 400 nm. The temperature of chamber of the UV aging simulation instrument was 25 °C , it was tested by the temperature sensor in the chamber. The surface temperature of the asphalt mixture was about 50 °C , it was tested by an infrared temperature tester (SMART SENSOR AR-300+, SMART SENSOR, Hongkong, China). According to the thermal oxidative aging test (short term aging) of asphalt mixture, the spread density of asphalt mixture was 22 kg/m 2 . During the UV aging test, the asphalt mixture was mixed every 24 h. Figure 2 shows the UV aging test of loose asphalt mixtures.   The irradiation intensity of UV light used in the UV aging simulation test of asphalt mixture was 21 w/m 2 , which was produced by four UV lamps, the power of every UV lamp was 500 W. The aging time was 7 days, 14 days and 28 days respectively. The wavelength range of the UV radiation was from 200 nm to 400 nm. The temperature of chamber of the UV aging simulation instrument was 25 • C, it was tested by the temperature sensor in the chamber. The surface temperature of the asphalt mixture was about 50 • C, it was tested by an infrared temperature tester (SMART SENSOR AR-300+, SMART SENSOR, Hongkong, China). According to the thermal oxidative aging test (short term aging) of asphalt mixture, the spread density of asphalt mixture was 22 kg/m 2 . During the UV aging test, the asphalt mixture was mixed every 24 h. Figure 2 shows the UV aging test of loose asphalt mixtures.

Recovery of Asphalt Binder from Asphalt Mixtures
After different times of UV irradiation, the asphalt binders were recovered from the asphalt mixtures by dissolution-centrifugal separation method. The solvent was trichloroethylene (C2HCl3), the purity of which was higher than 99%. The detailed procedure was as follows. First, the asphalt mixture was placed into C2HCl3 for half an hour, and then the centrifugal separation method was used to get the asphalt-C2HCl3 solution; this step was repeated 2-3 times. Finally, the asphalt-C2HCl3 solution was placed in the fume hood and dried naturally for 72 h.
In order to detect whether the C2HCl3 would affect the Fourier transform infrared spectrometer (FTIR, Nexus, Thermo Nicolet, Columbus, OH, USA) result of recovered asphalt binder, after 72 h volatilization and drying, the chemical structures of the virgin asphalt binder, recovered 28 days aged asphalt binder and C2HCl3 were tested by FTIR respectively. The results are shown in Figure 3. From Figure 3, a special absorption band at the wavenumber of 932 cm −1 can be observed in the FTIR spectrum of C2HCl3, it is caused by the stretching vibration of C-Cl of C2HCl3. This absorption band was very obvious and could be found in the FTIR spectrum of the virgin asphalt binder. Therefore, it could be used to test whether the C2HCl3 volatilized completely by comparing the FTIR spectra differences of the virgin asphalt binder and recovered 28 days aged asphalt binder. It was found that, in the FTIR spectrum of 28 days aged asphalt binder, there was no absorption band at wavenumber 932 cm -1 , therefore the C2HCl3 volatilized completely after 72 h volatilization (at least, it did not obviously affect the FT-IR of recovered asphalt binder).

Recovery of Asphalt Binder from Asphalt Mixtures
After different times of UV irradiation, the asphalt binders were recovered from the asphalt mixtures by dissolution-centrifugal separation method. The solvent was trichloroethylene (C 2 HCl 3 ), the purity of which was higher than 99%. The detailed procedure was as follows. First, the asphalt mixture was placed into C 2 HCl 3 for half an hour, and then the centrifugal separation method was used to get the asphalt-C 2 HCl 3 solution; this step was repeated 2-3 times. Finally, the asphalt-C 2 HCl 3 solution was placed in the fume hood and dried naturally for 72 h.
In order to detect whether the C 2 HCl 3 would affect the Fourier transform infrared spectrometer (FTIR, Nexus, Thermo Nicolet, Columbus, OH, USA) result of recovered asphalt binder, after 72 h volatilization and drying, the chemical structures of the virgin asphalt binder, recovered 28 days aged asphalt binder and C 2 HCl 3 were tested by FTIR respectively. The results are shown in Figure 3. From Figure 3, a special absorption band at the wavenumber of 932 cm −1 can be observed in the FTIR spectrum of C 2 HCl 3 , it is caused by the stretching vibration of C-Cl of C 2 HCl 3 . This absorption band was very obvious and could be found in the FTIR spectrum of the virgin asphalt binder. Therefore, it could be used to test whether the C 2 HCl 3 volatilized completely by comparing the FTIR spectra differences of the virgin asphalt binder and recovered 28 days aged asphalt binder. It was found that, in the FTIR spectrum of 28 days aged asphalt binder, there was no absorption band at wavenumber 932 cm −1 , therefore the C 2 HCl 3 volatilized completely after 72 h volatilization (at least, it did not obviously affect the FT-IR of recovered asphalt binder).

Chemical Functional Group Test of Recovered Asphalt Binders
The chemical structures of recovered asphalt binders were characterized by FTIR, the procedure of the FTIR test was as follows. The asphalt was dissolved in carbon disulfide (CS2), the concentration of the asphalt binder was 5.0 wt%; then the asphalt-CS2 solution was dropped on a potassium bromide (KBr) window, and the potassium bromide window was set under an incandescent light bulb until the CS2 volatized completely. The sweep times was 32, the sweep range of wavenumber was from 4000 cm −1 to 400 cm −1 .

Mechanical Properties Tests of Asphalt Concrete
The mechanical properties tests of asphalt concretes before and after UV aging were investigated by both the semi-circular bending test and three-point bending fatigue test.
The machine used for the semi-circular bending test was UTM-25 (IPC, Sydney, Australia). The diameter of the sample was 100 mm, the thickness was 50 mm. In order to control the crack position during the test, a notch with depth of 10 mm and width of 2 mm was precut. The testing temperature was −10 °C , and the loading speed was 0.5 mm/min. The schematic diagram of semi-circular bending test of asphalt concrete is shown in Figure 4.
The fatigue tests of asphalt concretes were tested at both 0.4 and 0.6 stress ratios, which was conducted with UTM-25 machine as well. The testing temperature was 25 °C and the Poisson ratio was designated as 0.35. A semi-sine wave of loading was used, and the loading frequency was 1.0 Hz (loading time was 0.1 s, and interval was 0.9 s). To control the temperature of the samples, all of them were put in the UTM chamber under constant temperature (25 °C) for more than five h. For the same aging status, three samples of asphalt concretes were tested to calculate the average values and standard deviations of the fatigue lives.

Chemical Functional Group Test of Recovered Asphalt Binders
The chemical structures of recovered asphalt binders were characterized by FTIR, the procedure of the FTIR test was as follows. The asphalt was dissolved in carbon disulfide (CS 2 ), the concentration of the asphalt binder was 5.0 wt%; then the asphalt-CS 2 solution was dropped on a potassium bromide (KBr) window, and the potassium bromide window was set under an incandescent light bulb until the CS 2 volatized completely. The sweep times was 32, the sweep range of wavenumber was from 4000 cm −1 to 400 cm −1 .

Mechanical Properties Tests of Asphalt Concrete
The mechanical properties tests of asphalt concretes before and after UV aging were investigated by both the semi-circular bending test and three-point bending fatigue test.
The machine used for the semi-circular bending test was UTM-25 (IPC, Sydney, Australia). The diameter of the sample was 100 mm, the thickness was 50 mm. In order to control the crack position during the test, a notch with depth of 10 mm and width of 2 mm was precut. The testing temperature was −10 • C, and the loading speed was 0.5 mm/min. The schematic diagram of semi-circular bending test of asphalt concrete is shown in Figure 4.
The fatigue tests of asphalt concretes were tested at both 0.4 and 0.6 stress ratios, which was conducted with UTM-25 machine as well. The testing temperature was 25 • C and the Poisson ratio was designated as 0.35. A semi-sine wave of loading was used, and the loading frequency was 1.0 Hz (loading time was 0.1 s, and interval was 0.9 s). To control the temperature of the samples, all of them were put in the UTM chamber under constant temperature (25 • C) for more than five h. For the same aging status, three samples of asphalt concretes were tested to calculate the average values and standard deviations of the fatigue lives.

Self-Healing Performance Tests of Asphalt Concrete
The semi-circular bending strength and fatigue life of initial asphalt concrete and asphalt concrete after self-healing were tested respectively, which was to obtain the healing index of asphalt concrete. A higher value of healing index expresses the better self-healing performance of asphalt concrete, and vise versa.
Meanwhile, a CT scanning machine (Xradia 510 Versa, ZEISS, Oberkochen, Germany) was used to characterize the crack size of asphalt concrete samples before and after self-healing. Figure 5 shows the diagram of this test. The real spatial resolution of the machine was 0.7 microns, and the voxel size was as low as 70 nanometers. The self-healing time of the samples was 72 h, and the temperature in the environmental chamber was 50 °C.

Logic Map of Experimental Design
The logic map of experimental design is shown in Figure 6.

Self-Healing Performance Tests of Asphalt Concrete
The semi-circular bending strength and fatigue life of initial asphalt concrete and asphalt concrete after self-healing were tested respectively, which was to obtain the healing index of asphalt concrete. A higher value of healing index expresses the better self-healing performance of asphalt concrete, and vise versa.
Meanwhile, a CT scanning machine (Xradia 510 Versa, ZEISS, Oberkochen, Germany) was used to characterize the crack size of asphalt concrete samples before and after self-healing. Figure 5 shows the diagram of this test. The real spatial resolution of the machine was 0.7 microns, and the voxel size was as low as 70 nanometers. The self-healing time of the samples was 72 h, and the temperature in the environmental chamber was 50 • C.

Self-Healing Performance Tests of Asphalt Concrete
The semi-circular bending strength and fatigue life of initial asphalt concrete and asphalt concrete after self-healing were tested respectively, which was to obtain the healing index of asphalt concrete. A higher value of healing index expresses the better self-healing performance of asphalt concrete, and vise versa.
Meanwhile, a CT scanning machine (Xradia 510 Versa, ZEISS, Oberkochen, Germany) was used to characterize the crack size of asphalt concrete samples before and after self-healing. Figure 5 shows the diagram of this test. The real spatial resolution of the machine was 0.7 microns, and the voxel size was as low as 70 nanometers. The self-healing time of the samples was 72 h, and the temperature in the environmental chamber was 50 °C.

Logic Map of Experimental Design
The logic map of experimental design is shown in Figure 6.

Logic Map of Experimental Design
The logic map of experimental design is shown in Figure 6.

Characterization of the UV Aging Status of Recovered Asphalt Binder
The atoms that form the chemical bonds or functional group of organic molecules are always in a constant state of vibration, and the vibration frequency of that is equal to the vibration frequency of the infrared light [23]. When the infrared light irradiates on the organic molecules, the vibrational absorption of infrared light can be observed in the chemical bonds or functional groups in molecules [24]. The different chemical bonds or functional group have different absorption frequencies, the infrared spectrum will be reflected in different positions, thus the FTIR can be used to characterize the chemical bonds or functional molecules in organic molecules [25]. Because of the irradiation of UV light, the chemical groups such as C=C and C-H without oxygen can be oxidized, and form oxygen-containing functional groups, such as the carbonyl group (C=O) and sulfoxide functional group (S=O) [26]. Therefore, the content of C=O and S=O will increase after UV aging, the absorption band areas of these two chemical functional groups will increase as well, which can be used to characterize the aging status of asphalt binder. The bigger the absorption band areas of C=O and S=O, the more serious the UV aging status.
The FTIR spectra of asphalt binders recovered from aged mixtures are shown in Figure 7. From Figure 7, the absorption bands of the main chemical functional groups of asphalt binder were in the wavenumber range of 600-2000 cm −1 , the absorption bands at 1700 cm −1 and 1030 cm −1 were caused by the C=O and S=O respectively. However, the absorption bands of the C=O and S=O can also be observed in FTIR spectra of original asphalt binder. This is because thermo-oxidative aging happens during the production and storage of asphalt binder, and the mixing of asphalt mixture. From Figure 7, the absorption bands C=O and S=O increased with the increasing aging time, indicating the more serious aging status of asphalt binders recovered from asphalt mixtures under longer times of UV irradiation. AC-13 dense asphalt mixture exposed under UV radiation for 7, 14

Characterization of the UV Aging Status of Recovered Asphalt Binder
The atoms that form the chemical bonds or functional group of organic molecules are always in a constant state of vibration, and the vibration frequency of that is equal to the vibration frequency of the infrared light [23]. When the infrared light irradiates on the organic molecules, the vibrational absorption of infrared light can be observed in the chemical bonds or functional groups in molecules [24]. The different chemical bonds or functional group have different absorption frequencies, the infrared spectrum will be reflected in different positions, thus the FTIR can be used to characterize the chemical bonds or functional molecules in organic molecules [25]. Because of the irradiation of UV light, the chemical groups such as C=C and C-H without oxygen can be oxidized, and form oxygen-containing functional groups, such as the carbonyl group (C=O) and sulfoxide functional group (S=O) [26]. Therefore, the content of C=O and S=O will increase after UV aging, the absorption band areas of these two chemical functional groups will increase as well, which can be used to characterize the aging status of asphalt binder. The bigger the absorption band areas of C=O and S=O, the more serious the UV aging status.
The FTIR spectra of asphalt binders recovered from aged mixtures are shown in Figure 7. From Figure 7, the absorption bands of the main chemical functional groups of asphalt binder were in the wavenumber range of 600-2000 cm −1 , the absorption bands at 1700 cm −1 and 1030 cm −1 were caused by the C=O and S=O respectively. However, the absorption bands of the C=O and S=O can also be observed in FTIR spectra of original asphalt binder. This is because thermo-oxidative aging happens during the production and storage of asphalt binder, and the mixing of asphalt mixture. From Figure 7, the absorption bands C=O and S=O increased with the increasing aging time, indicating the more serious aging status of asphalt binders recovered from asphalt mixtures under longer times of UV irradiation.
To quantificationally characterize the aging status of UV aging status of recovered asphalt binder, the relative ratios of the areas of C=O absorption band and S=O absorption band were calculated based on Equations (1) and (2) respectively. To quantificationally characterize the aging status of UV aging status of recovered asphalt binder, the relative ratios of the areas of C=O absorption band and S=O absorption band were calculated based on Equation (1) and Equation (2) respectively.
where, the (CRR) and (SRR) are the C=O relative ratio and S=O relative ratio respectively, 1700cm −1 and 1030cm −1 are the areas of C=O absorption band and S=O absorption band respectively, ∑ 2000 cm −1 ~ 600 −1 is the sum of areas of all bands in the wavenumber range of 2000 cm −1 ~ 600 −1 .
The relative ratios of the areas of C=O and S=O absorption bands are shown in Table 3. The bigger the CRR and SRR values are, the more serious the aging status of asphalt binder is [27]. From Table 3, after 7 days, 14 days and 28 days of UV irradiation, the CRR value of which increased by 128.6%, 226.2% and 358.3% respectively, the SRR value of which increased by 21.7%, 34.5% and 40.4% respectively. The CRR and SRR values of recovered asphalt binder increased significantly with the increase of UV irradiation time, the content of oxygen-containing functional groups in asphalt binder increased obviously as well, indicating that the aging status of asphalt binder was more serious with longer UV irradiation time.  The relative ratios of the areas of C=O and S=O absorption bands are shown in Table 3. The bigger the CRR and SRR values are, the more serious the aging status of asphalt binder is [27]. From Table 3, after 7 days, 14 days and 28 days of UV irradiation, the CRR value of which increased by 128.6%, 226.2% and 358.3% respectively, the SRR value of which increased by 21.7%, 34.5% and 40.4% respectively. The CRR and SRR values of recovered asphalt binder increased significantly with the increase of UV irradiation time, the content of oxygen-containing functional groups in asphalt binder increased obviously as well, indicating that the aging status of asphalt binder was more serious with longer UV irradiation time.

UV Radiation Effects on the Semi-Circular Bending Strength of Asphalt Concrete
Asphalt concrete is granular in nature, and its macroscopic behavior is mainly a function the interactions of asphalt binder and aggregate and the UV aging of asphalt binder may significantly influence the mechanical property of asphalt concrete [28,29]. The semi-circular bending test was conducted on the asphalt concrete before and after UV aging. Three parallel tests were performed at each aging time, the bending strength of asphalt concrete was calculated according to Equation (3), the average bending strength of these three specimens were taken as the final result.
where, S t is the semi-circular bending strength of asphalt concrete, MPa; P is the maximum loading of every specimen, N; d is the diameter of every specimen, mm; h is the thickness of every specimen, mm. Figure 8 gives the average bending strengths of all asphalt concretes. From Figure 8, when after 7, 14 and 28 days of UV aging, the semi-circular bending strengths of asphalt concretes at −10 • C decreased by 10.8%, 15.6% and 31.4% respectively; while the semi-circular bending strengths of asphalt concretes at 25 • C increased by 97.6%, 110.0% and 118.6% respectively. Therefore, after different times of UV aging, the semi-circular bending strengths of asphalt concretes at −10 • C tended to decrease, while they showed an opposite tendency at 25 • C. With the extension of UV exposure time, the tendencies were more obvious. The reason is that, after aging the asphalt binder tends to be stiffer and harder, the asphalt binder is inherently brittle at low temperature condition (−10 • C); the comprehensive action of UV aging and low temperature causes the degradation of the three bending strengths of asphalt concretes. However, at relative high temperature (25 • C), the harder effect of UV aging on asphalt binder can partially offset the softening effect of high temperature, therefore the 25 • C semi-circular bending strengths of asphalt concretes were increased. This results also the same as other research work [30].

UV Radiation Effects on the Semi-Circular Bending Strength of Asphalt Concrete
Asphalt concrete is granular in nature, and its macroscopic behavior is mainly a function the interactions of asphalt binder and aggregate and the UV aging of asphalt binder may significantly influence the mechanical property of asphalt concrete [28,29]. The semi-circular bending test was conducted on the asphalt concrete before and after UV aging. Three parallel tests were performed at each aging time, the bending strength of asphalt concrete was calculated according to Equation (3), the average bending strength of these three specimens were taken as the final result.
where, St is the semi-circular bending strength of asphalt concrete, MPa; P is the maximum loading of every specimen, N; d is the diameter of every specimen, mm; h is the thickness of every specimen, mm. Figure 8 gives the average bending strengths of all asphalt concretes. From Figure 8, when after 7, 14 and 28 days of UV aging, the semi-circular bending strengths of asphalt concretes at −10 °C decreased by 10.8%, 15.6% and 31.4% respectively; while the semi-circular bending strengths of asphalt concretes at 25 °C increased by 97.6%, 110.0% and 118.6% respectively. Therefore, after different times of UV aging, the semi-circular bending strengths of asphalt concretes at −10 °C tended to decrease, while they showed an opposite tendency at 25 °C. With the extension of UV exposure time, the tendencies were more obvious. The reason is that, after aging the asphalt binder tends to be stiffer and harder, the asphalt binder is inherently brittle at low temperature condition (−10 °C ); the comprehensive action of UV aging and low temperature causes the degradation of the three bending strengths of asphalt concretes. However, at relative high temperature (25 °C ), the harder effect of UV aging on asphalt binder can partially offset the softening effect of high temperature, therefore the 25 °C semi-circular bending strengths of asphalt concretes were increased. This results also the same as other research work [30].

UV Radiation Effects on the Fatigue Resistance of Asphalt Concrete
The fatigue tests of asphalt concretes before and after UV aging were conducted at 0.4 and 0.6 stress ratios respectively. The results are shown in Figure 9.
It can be found from Figure 9 that, after UV aging, the fatigue lives of asphalt concretes at both 0.4 and 0.6 stress ratios decreased, and with prolonging UV irradiation time, the decreased range was more significant. In detail, after being aged for 7, 14 and 28 days, the fatigue lives of asphalt concrete under 0.4 stress ratio of loading decreased by 42.2%, 58.9% and 66.2% respectively, and

UV Radiation Effects on the Fatigue Resistance of Asphalt Concrete
The fatigue tests of asphalt concretes before and after UV aging were conducted at 0.4 and 0.6 stress ratios respectively. The results are shown in Figure 9.
It can be found from Figure 9 that, after UV aging, the fatigue lives of asphalt concretes at both 0.4 and 0.6 stress ratios decreased, and with prolonging UV irradiation time, the decreased range was more significant. In detail, after being aged for 7, 14 and 28 days, the fatigue lives of asphalt concrete under 0.4 stress ratio of loading decreased by 42.2%, 58.9% and 66.2% respectively, and under 0.6 stress ratio of loading decreased by 32.3%, 58.2% and 69.6% respectively. Therefore, UV radiation decreased the fatigue resistance of asphalt concretes; the longer the UV irradiation time was, the more significant the aging effect. under 0.6 stress ratio of loading decreased by 32.3%, 58.2% and 69.6% respectively. Therefore, UV radiation decreased the fatigue resistance of asphalt concretes; the longer the UV irradiation time was, the more significant the aging effect.

Healing Percentages of Semi-Circular Bending Strengths
The healing percentages of semi-circular bending strengths of asphalt concretes were calculated according to Equation (4). The healing percentages of semi-circular bending strengths (HPBS) values of asphalt concretes before and after UV irradiation are listed in Figures 10 and 11.
where, the HPBS is the healing percentages of semi-circular bending strengths of asphalt concretes, %; BSbefore aging and BSafter aging are the healing percentages of semi-circular bending strengths of asphalt concretes before and after UV aging respectively, MPa. From Figure 10, for the −10 °C bending strengths, the self-healing effects of asphalt concretes had time sensitivity: the HPBS values of asphalt concretes increased with the increase of healing time. When the healing times were 24 h and 72 h, the HPBS values of asphalt concretes before UV aging were 40.0% and 53.2% respectively. Compared with asphalt concrete without UV irradiation, after self-healing, the HPBS values of asphalt concretes after 7, 14 and 28 days UV irradiation decreased significantly; the HPBS decrement of asphalt concretes after different times of UV irradiation are listed in detail in Table 4. From Figure 11 and Table 4, after 72 h of self-healing, the same tendency could also be observed for the 25 °C bending strengths of asphalt concrete. Therefore, the UV irradiation could weaken the self-healing performance of asphalt concrete obviously, and the longer the irradiation time was, the worse the self-healing performance of asphalt concrete.

Healing Percentages of Semi-Circular Bending Strengths
The healing percentages of semi-circular bending strengths of asphalt concretes were calculated according to Equation (4). The healing percentages of semi-circular bending strengths (HPBS) values of asphalt concretes before and after UV irradiation are listed in Figures 10 and 11. HPBS = BS a f ter aging BS be f ore aging × 100% (4) where, the HPBS is the healing percentages of semi-circular bending strengths of asphalt concretes, %; BS before aging and BS after aging are the healing percentages of semi-circular bending strengths of asphalt concretes before and after UV aging respectively, MPa.

Healing Percentages of Fatigue Performance
Initial fatigue lives and the fatigue lives after self-healing of asphalt concretes are shown in Table 5. From Table 5, after UV aging, the fatigue lives of all asphalt concretes before and after healing decreased obviously, with the increase of aging time, the reductions were more significant.
To quantificationally compare the abilities of the self-healing performance of asphalt concretes, the healing percentages of fatigue lives (HPFL) were calculated according to Equation (5). From Figure 10, for the −10 • C bending strengths, the self-healing effects of asphalt concretes had time sensitivity: the HPBS values of asphalt concretes increased with the increase of healing time. When the healing times were 24 h and 72 h, the HPBS values of asphalt concretes before UV aging were 40.0% and 53.2% respectively. Compared with asphalt concrete without UV irradiation, after self-healing, the HPBS values of asphalt concretes after 7, 14 and 28 days UV irradiation decreased significantly; the HPBS decrement of asphalt concretes after different times of UV irradiation are listed in detail in Table 4. From Figure 11 and Table 4, after 72 h of self-healing, the same tendency could also be observed for the 25 • C bending strengths of asphalt concrete. Therefore, the UV irradiation could weaken the self-healing performance of asphalt concrete obviously, and the longer the irradiation time was, the worse the self-healing performance of asphalt concrete.

Healing Percentages of Fatigue Performance
Initial fatigue lives and the fatigue lives after self-healing of asphalt concretes are shown in Table 5. From Table 5, after UV aging, the fatigue lives of all asphalt concretes before and after healing decreased obviously, with the increase of aging time, the reductions were more significant.
To quantificationally compare the abilities of the self-healing performance of asphalt concretes, the healing percentages of fatigue lives (HPFL) were calculated according to Equation (5).
HPFL = FL a f ter aging FL be f ore aging × 100% (5) where, the HPFL is the healing percentages of fatigue lives of asphalt concretes, %; FL before aging and FL after aging are the healing percentages of fatigue lives of asphalt concretes before and after UV aging respectively, times. The HPFL values of asphalt concrete after different times of UV irradiation are listed in Figure 12. From Figure 12, for the 0.4 stress ratio, the HPFL values of asphalt concretes before UV aging was 65.7%, it decreased to 21.4%, 72.9% and 87.5% after 7, 14, and 28 days of UV irradiation respectively; for the 0.6 stress ratio, the HPFL values of asphalt concretes also showed a decreasing tendency. The lower HPFL values meant a worse self-healing effect, so the self-healing effect of asphalt concretes after UV irradiation decreased, the self-healing performance of asphalt concrete decreased with increasing UV irradiation time. The reason is that the self-healing of asphalt concrete is accomplished mainly based on two patterns, firstly, due to the drain of asphalt binder into the cracks [31], it can fill the cracks and recover the structural continuity of asphalt concrete [32]; secondly, the thermal expansion of asphalt binder also plays an important role in the self-healing of asphalt concrete [33]. However, after UV aging, the viscosity of asphalt binder in its concrete is much higher than that of before aging [26]. At the same temperature, the asphalt binder in asphalt concrete after UV aging flows more slowly than that of initial asphalt concrete, the relative high viscosity limits the flow of asphalt binder [34][35][36], therefore results in a lower self-healing ratio.
where, the HPFL is the healing percentages of fatigue lives of asphalt concretes, %; FLbefore aging and FLafter aging are the healing percentages of fatigue lives of asphalt concretes before and after UV aging respectively, times.
The HPFL values of asphalt concrete after different times of UV irradiation are listed in Figure  12. From Figure 12, for the 0.4 stress ratio, the HPFL values of asphalt concretes before UV aging was 65.7%, it decreased to 21.4%, 72.9% and 87.5% after 7, 14,and 28 days of UV irradiation respectively; for the 0.6 stress ratio, the HPFL values of asphalt concretes also showed a decreasing tendency. The lower HPFL values meant a worse self-healing effect, so the self-healing effect of asphalt concretes after UV irradiation decreased, the self-healing performance of asphalt concrete decreased with increasing UV irradiation time. The reason is that the self-healing of asphalt concrete is accomplished mainly based on two patterns, firstly, due to the drain of asphalt binder into the cracks [31], it can fill the cracks and recover the structural continuity of asphalt concrete [32]; secondly, the thermal expansion of asphalt binder also plays an important role in the self-healing of asphalt concrete [33]. However, after UV aging, the viscosity of asphalt binder in its concrete is much higher than that of before aging [26]. At the same temperature, the asphalt binder in asphalt concrete after UV aging flows more slowly than that of initial asphalt concrete, the relative high viscosity limits the flow of asphalt binder [34][35][36], therefore results in a lower self-healing ratio.

Fracture Healing Characteristics Analysis by CT Scanning Test
The CT scanning figures of asphalt concretes before and after UV irradiation are shown in Figure 13 and Figure 14 respectively, where the self-healing effect of the cracks in the asphalt concrete intuitively can be observed. From Figure 13, the asphalt concrete had an obvious crack

Fracture Healing Characteristics Analysis by CT Scanning Test
The CT scanning figures of asphalt concretes before and after UV irradiation are shown in Figures 13 and 14 respectively, where the self-healing effect of the cracks in the asphalt concrete intuitively can be observed. From Figure 13, the asphalt concrete had an obvious crack before self-healing, while, after self-healing, the crack almost disappeared, and the crack could not be found unless we observed very carefully, which indicated that the crack healed very well. From Figure 14, after self-healing, the crack of asphalt concrete after 28 days of UV irradiation also decreased obviously, especially the lower part of sample almost healed completely, but a small crack could still be observed in the upper part (marked in Figure 14 by the red arrow), the continuity of macro structure of asphalt concrete was not completely repaired. Therefore, despite being under the same self-healing condition, the self-healing effect of asphalt concrete before UV irradiation was much better than that of asphalt concrete after 28 days of UV irradiation. The results indicated that the asphalt concrete after UV irradiation still had a certain self-healing ability, but the self-healing ability of which was reduced obviously during UV irradiation, therefore UV radiation can significantly decrease the self-healing performance of asphalt concrete. before self-healing, while, after self-healing, the crack almost disappeared, and the crack could not be found unless we observed very carefully, which indicated that the crack healed very well. From Figure 14, after self-healing, the crack of asphalt concrete after 28 days of UV irradiation also decreased obviously, especially the lower part of sample almost healed completely, but a small crack could still be observed in the upper part (marked in Figure 14 by the red arrow), the continuity of macro structure of asphalt concrete was not completely repaired. Therefore, despite being under the same self-healing condition, the self-healing effect of asphalt concrete before UV irradiation was much better than that of asphalt concrete after 28 days of UV irradiation. The results indicated that the asphalt concrete after UV irradiation still had a certain self-healing ability, but the self-healing ability of which was reduced obviously during UV irradiation, therefore UV radiation can significantly decrease the self-healing performance of asphalt concrete.

Conclusions
In this research, the AC-13 asphalt mixture was exposed under UV radiation for 7, 14 and 28 days to investigate the degradation behaviors of the chemical structure, mechanical and self-healing properties of asphalt mixture exposed under the UV radiation, the flowing conclusions can be obtained. before self-healing, while, after self-healing, the crack almost disappeared, and the crack could not be found unless we observed very carefully, which indicated that the crack healed very well. From Figure 14, after self-healing, the crack of asphalt concrete after 28 days of UV irradiation also decreased obviously, especially the lower part of sample almost healed completely, but a small crack could still be observed in the upper part (marked in Figure 14 by the red arrow), the continuity of macro structure of asphalt concrete was not completely repaired. Therefore, despite being under the same self-healing condition, the self-healing effect of asphalt concrete before UV irradiation was much better than that of asphalt concrete after 28 days of UV irradiation. The results indicated that the asphalt concrete after UV irradiation still had a certain self-healing ability, but the self-healing ability of which was reduced obviously during UV irradiation, therefore UV radiation can significantly decrease the self-healing performance of asphalt concrete.

Conclusions
In this research, the AC-13 asphalt mixture was exposed under UV radiation for 7, 14 and 28 days to investigate the degradation behaviors of the chemical structure, mechanical and self-healing properties of asphalt mixture exposed under the UV radiation, the flowing conclusions can be obtained.

Conclusions
In this research, the AC-13 asphalt mixture was exposed under UV radiation for 7, 14 and 28 days to investigate the degradation behaviors of the chemical structure, mechanical and self-healing properties of asphalt mixture exposed under the UV radiation, the flowing conclusions can be obtained.
(1) With the increase of UV irradiation time, the CRR and SRR values of recovered asphalt binder increased significantly, meanwhile, the fatigue life of asphalt concrete under both the 0.4 and 0.6 stress ratios decreased gradually, indicating that the UV radiation could weaken the chemical structure and fatigue resistance of asphalt concrete. (2) UV radiation significantly affected the asphalt semi-circular bending strength of asphalt concrete, it decreased the −10 • C bending strength of asphalt concrete, while increased the 25 • C bending strength, and the longer the exposure duration was, the more obvious the aging effect. (3) After UV aging, the HPBS and HPFL values of asphalt concrete decreased obviously; the CT scanning figures also showed the same tendency with HPBS and HPFL values, under the same self-healing condition. The self-healing effect of the crack in the asphalt concrete after UV irradiation was worse than that of initial asphalt concrete-a crack could still be observed in the asphalt concrete after UV irradiation. The results indicated the UV radiation could significantly reduce the self-healing performance of asphalt concrete, causing a worse macro-structure continuity, lower failure strength and worse fatigue resistance.