In Situ Generation of Fluorescent Copper Nanoclusters Embedded in Monolithic Eggshell Membrane: Properties and Applications

Luminescent metal nanoclusters have attracted considerable research attention in recent years due to their unique properties and extensive usage in many fields. Three different synthetic routes were developed to in situ generate orange and red emitting copper nanoclusters embedded in monolithic eggshell membrane (Cu NCs@ESM) using different reducing reagents including N2H4·H2O, NH2OH·HCl and Vitamin C at room temperature for the first time. The routes are extremely facile, low-cost and versatile. The obtained Cu NCs@ESM nanocomposites exhibit excellent photostability and chemical stability, laying the foundation for various practical applications. Fluorescent surface patterning was demonstrated based on the proposed strategy easily. Significantly, the Cu NCs@ESM shows selective fluorescence quenching response to Hg2+ ions and good catalytic activity for methylene blue (MB) reduction degradation making it ideal as portable sensing strip and recyclable catalyst. The work provides a general strategy for the fabrication of other various monolithic nanomaterials with potential applications.


Introduction
Metal nanoclusters (NCs) consisting of several to tens of atoms have drawn considerable research interest due to their low toxicity, good biocompatibility, multifunctional surface chemistry, and excellent fluorescence behaviors such as emitting tunability, large Stokes shift, and photo stability [1][2][3][4]. The NCs have been wildly applied in bioimaging [5][6][7], sensing [8][9][10], catalysis [11][12][13][14], nanodevices [15][16][17] and many other fields [18,19]. However, to date, extensive research on fluorescent metal nanoclusters has mainly focused on the noble metal nanoclusters (especially Au and Ag NCs). The studies on tiny Cu NCs are still deficient owing to their inherent instability [17,20]. The less use of noble metals has attracted ever increasing attention due to their scarce natural resources and high cost. Researchers turned to the studies of the first transition metals such as Cu, Fe, Ni, which can be regarded as alternatives to Au and Ag. Copper is frequently used in industry because of its high conductivity, similar properties to gold and silver and especially much lower cost. Therefore, the development of various synthetic routes and extensive properties investigations of Cu NCs will be of great practical significance [21,22].
Recently, many efforts have led to some approaches for Cu NCs syntheses such as polymer and biomolecule templated methods [23][24][25][26][27][28][29][30][31], electrochemical reduction [32], sonochemical synthesis [33], microwave-assisted [34][35][36] and microemulsion technology [37,38]. However, those as-prepared Cu NCs are mostly dispersed in homogeneous solution. Agglomeration, precipitation and recycling during practical applications are the chief drawbacks of solution-dispersed fluorescent Cu NCs. Additionally, Additionally, these aqueous Cu NCs might hinder their potential applications as solid state materials in chemical sensing strips, surface patterning, light-emitting devices and other fields. However, to date, there are only few reports on the syntheses of solid state Cu NCs. Zhang et al. reported the synthesis of solid fluorescent Cu NCs in supramolecular hydrogels via employing a series of bile acid derivatives as pre-gelators [39]. Qing et al. proposed the fluorescent Cu NPs templated by poly(thymine) in the agarose hydrogel [40]. Very recently, composite polymer films incorporating luminescent Cu NCs were fabricated in a hydrogel by the precursors of polyvinylpyrrolidone and poly(vinyl alcohol) by Wang et al. [41]. In the mentioned work, the solid Cu NCs were all generated based on pre-formed or simultaneously polymerized hydrogel network. Obviously, sometimes poor dispersion of NCs in hydrogel would lead to the phase segregation making it difficult to fabricate large-area, uniform, photo-stable luminescent films. Thus, developing some facile and practical strategies to fabricate novel solid state Cu NCs is a very urgent and fascinating task.
Eggshell membrane (ESM), generally abandoned in daily life, has been demonstrated to be one of natureʼs gifts for nanomaterial preparation [42]. ESM, a double-layer water-insoluble biomembrane with interwoven fibrous structure attached inside the hen eggshell, is composed of highly cross-linked and cystine-abundant proteins, which make ESM a good reducing agent and stabilizer in nanoscience. Importantly, the three-dimensional monolithic structure could serve as an ideal platform, providing rich sites and making sure there is uniform loading. For instance, previous research by Shao et al. demonstrated that ESM was an efficient solid state platform for generating Au and Ag NCs [43]. Also, Devi reported the formation of Ag NPs by ESM [44]. Again, Pramanik proposed the formation of fluorescent AuAg alloy nanoparticles immobilized in solid ESM [45]. Nevertheless, to the best of our knowledge, the in situ synthesis of fluorescent Cu NCs embedded in monolithic ESM hasn't been reported yet. Additionally, the ease of oxidation of Cu (E 0 , 0.34 V), in comparison to that of Ag (E 0 , 0.80 V) and Au (E 0 , 1.50 V) makes related study remain a challenge. In this work, we established several facile routes for the in situ generation of fluorescent Cu NCs embedded in solid state ESM (Cu NCs@ESM), employing different reducing agents at room temperature for the first time (Scheme 1), and the reaction conditions and properties of obtained Cu NCs@ESM nanocomposites were investigated in detail. Theoretical and experimental studies have shown that Cu NCs possess unique size-and composition-dependent catalysis properties [1,13,14]. With many attractive features of the in situ generated Cu NCs-incorporated nanocomposite, including monolith, low cost, convenient tailoring, good stability, easy storage and transport, and large Stokes-shift, the as-prepared Cu NCs@ESM nanocomposite is expected to exhibit significant catalytic and sensing performance. Herein, their applications in visual Hg 2+ strips sensing based on fluorescence quenching and catalysis for methylene blue reduction degradation have been demonstrated.
Fresh eggs were purchased from ZhenBang supermarket near the HuaiBei Normal University (Huaibei, China). The ESMs were peeled off from the natural eggshells manually and cleaned with copious amount of deionized water carefully. The resultant ESMs were cut into proper rectangular pieces (about 1 × 1.5 cm 2 ) and stored in deionized water before use.

Instruments
Fluorescence spectra of Cu NCs@ESMs were recorded with a FP-8300 spectrophotometer equipped with solid sample holder (Jasco, Tokyo, Japan). The photos of all samples were taken with a MeiZu mobile phone (Zhuhai, China). The fluorescent photos under 365 nm UV light were taken under a ZF-20D black-box-style UV based analyzer (YuHua, GongYi, China). Surface morphology of fluorescent Cu NCs@ESMs were observed under an Olympus IX71 fluorescence microscope (Tokyo, Japan). The X-ray photoelectron spectra (XPS) were obtained on an ULVAC-PHI X-ray photoelectron spectrometer (PHI Quantera, Tokyo, Japan) using Al K α radiation. Quantitative analyses of the copper contents in Cu NCs@ESMs were performed on Perkin Elmer Opyima 7300 ICP-AES (Waltham, MA, USA). The UV-vis absorption spectra and diffuse reflectance spectra (DRS) measurements were carried out using a PGENERAL TU-1901 UV-vis spectrophotometer (Purkinje General Instrument, Beijing, China). The time-resolved fluorescence decay was investigated by time correlated single photon counting (TCSPC) technique on FLS 920 (Edinburgh Instrument, Edinburgh, UK).

Synthesis of Cu NCs@ESM Using N 2 H 4 ·H 2 O
A cleaned piece of ESM platform was incubated in an aqueous of CuSO 4 solution (1 mL, 50 mM) for 10 min. Then, excessive CuSO 4 was removed, and the Cu 2+ impregnated ESM (Cu 2+ /ESM) was transferred into 1 mL N 2 H 4 solution (85%) to initialize the reduction. The process typically took approximately 5~7 h at ambient temperature to get strongly orange emitting Cu NCs@ESM.

Synthesis of Cu NCs@ESM Using NH 2 OH·HCl or VC
In a typical process, a piece of ESM was incubated in a solution of CuSO 4 (1 mL, 50 mM) for 10 min. After that, the obtained Cu 2+ /ESM was treated with NaOH solution (1 mL, 10 M) for 20 min, and then transferred into 1 mL 1 M NH 2 OH·HCl or 2 M VC solution, immediately. The reaction took 5 h to generate intense red fluorescent Cu NCs@ESM at ambient temperature.

Surface Patterning on ESM Substrate
Firstly, "Cu-N-C-s" letters or the pattern of smiling face were written directly on an ESM substrate with 50 mM CuSO 4 solution as "ink". Then, the ESM with the impregnated letters or pattern was soaked into 10 M NaOH solution for 20 min. Finally, the treated ESM was transferred into 2 M VC solution for 5 h, and the fluorescent letters or pattern were fabricated embedded in the ESM substrate.

Response of Cu NCs@ESM Strips to Hg 2+ Ions
In a typical procedure, the as-prepared monolithic Cu NCs@ESM was cut into small pieces. Then, the small pieces were added into 1 mL Hg(NO 3 ) 2 solution with different concentrations and incubated at ambient temperature. After that, the fluorescence was observed under 365 nm UV light. Meanwhile, the influence of other interferences was also investigated with the concentrations of 500 µM.

Catalytic Activity of Cu NCs@ESM for MB Reduction
Typically, the as-prepared Cu NCs@ESM nanocomposite was briefly thrown into 1 mL 30 µM methylene blue (MB) solution in the sunlight. The catalytic degradation of MB dye in the presence of Cu NCs@ESM was monitored by the UV-vis spectrometer.

Synthesis and Characterization of Cu NCs@ESM Using N 2 H 4 ·H 2 O
Previous research demonstrated the formation of noble Au and Ag NCs based on the reductive ability of ESM itself in alkaline solution [43,45,46]. What about the in situ synthesis of Cu NCs employing ESM as the solid state platform? Herein, in initial experiments the ESMs were treated by these similar ways with curiosity [43] (Figures S1-S3). The results show the color of ESMs incubated with Cu 2+ rapidly changed from blue to purplish red in alkaline solution, as described in other literatures [20,47], which indicated the formation of Cu-ESM complex. However, no fluorescent Cu NCs were further formed, even if the reaction was prolonged to several days or the reaction was allowed to proceed at elevated temperature (55 • C) employing ESM itself as the reducer in alkaline solution, which was greatly different from that of Au-ESM and Ag-ESM. Therefore, new different routes would be needed to generate fluorescent Cu NCs embedded in monolithic ESM. We then attempted to introduce an external reductant, N 2 H 4 ·H 2 O, to initialize the reduction process. Typically, the ESM displayed a blue color after treating with CuSO 4 solution for 10 min, indicating that Cu 2+ was adsorbed onto ESM due to the coordination between Cu 2+ and the functional groups (amines, amides, and carboxylic groups) of the ESM fibers [47]. Exhilaratingly, after the introduction of N 2 H 4 ·H 2 O, the absorbed Cu 2+ could be reduced to Cu(0) and thus induced simultaneous nucleation and size-regulating growth of fluorescent Cu NCs embedded in ESM platform. Figure 1a shows the obtained Cu NCs@ESM had a yellowish color under room light characteristic of ultrafine Cu NCs and emitted intense orange fluorescence centered at 602 nm excited with 365 nm UV light ( Figure 1b). Separate control experiments were simultaneously performed by treating ESMs with N 2 H 4 ·H 2 O and CuSO 4 , respectively, and no orange fluorescence was observed. Additionally, the in situ generated Cu NCs showed an excitation maximum at 317 nm ( Figure S4). Besides, the excitation dependence property of Cu NCs embedded in ESM was also investigated, and no obvious excitation-dependent behavior was observed when the excitation wavelengths changed from 260 to 420 nm, indicating that the size distribution of in situ generated Cu NCs is equally uniform (Figure 1c). Fluorescence microscope images (Figure 1a) show the characteristic interwoven fibrous structure of ESM remained almost unchanged after the surface and inside loading of orange emitting Cu NCs, when compared with the natural blue emitting ESM substrate. It is noteworthy that the blue fluorescence was dramatically suppressed after the in situ generation of Cu NCs compared with the ESM itself (inset in Figure 1b). One possible reason was that the oxidation and reduction of some components in the natural ESM substrate occurred during the reaction process. On the other hand, the energy transfer between the blue emission from ESM itself and the clusters or other products was not unexpected when exited with the 365 nm UV light [43]. The content of copper in monolithic Cu NCs@ESM was determined to be 1.2% by inductively coupled plasma atomic emission spectroscopy (ICP-AES). XPS analysis also verified the existence of Cu(0) on the ESM, which showed two strong peaks at 932.2 eV and 952.2 eV in the spectrum, corresponding to the Cu2p 3/2 and Cu2p 1/2 of Cu(0), respectively. The absence of Cu2p3/2 satellite peak around 942 eV indicated the absence of Cu(II) in the prepared Cu NCs@ESM ( Figure 1d). As we know, the 2p 3/2 binding energy of Cu(0) is only~0.1 eV away from that of Cu(I) species. Therefore, the valence state of the Cu in protein matrix most likely lies between 0 and +1 [13,20]. the prepared Cu NCs@ESM ( Figure 1d). As we know, the 2p3/2 binding energy of Cu(0) is only ~0.1 eV away from that of Cu(I) species. Therefore, the valence state of the Cu in protein matrix most likely lies between 0 and +1 [13,20]. In the synthetic route, the concentrations of CuSO4 precursor and N2H4·H2O reducer played crucial roles in generating fluorescent Cu NCs. Additional experiments were performed (Figures S5 and S6) and the results show more than 5 mM Cu 2+ and 85% N2H4·H2O solution (~17 M) were effective to form strongly orange emitting Cu NCs embedded in ESM after the reaction duration of 5 h at room temperature. Interestingly, when the prepared monolithic Cu NCs@ESM was always immersed in N2H4·H2O reaction solution until several days at 4 °C, the membrane gradually dissolved due to the alkaline hydrolysis and a homogeneous solution with brownish yellow was obtained, suggesting the immobilized Cu NCs were released into aqueous solution and dispersed homogeneously. The maximum excitation and emission peaks were observed at 337 nm and 606 nm, and the aqueous Cu NCs was excitation-independent as the parent Cu NCs@ESM ( Figure S7). The large Stokes shift up to 269 nm of the Cu NCs makes it actually applicable with very low background and light scattering interference, which is ideal for bioimaging and biosensing.

Synthesis and Characterization of Cu NCs@ESM Using NH2OH·HCl
In the above case, the fluorescent Cu NCs were successfully in situ generated in ESM by externally introduced N2H4·H2O as the reducer. In order to develop diverse synthetic routes, other reducing agents, NaBH4 and NH2OH·HCl were also tried to prepare fluorescent Cu NCs@ESM employing the similar synthetic route. However, very weakly red emitting Cu NCs could be obtained via NaBH4 reduction. In particular, the reaction condition was relatively harsh, and it seemed very difficult to control a good nucleation and growth of copper clusters due to the strong reducing In the synthetic route, the concentrations of CuSO 4 precursor and N 2 H 4 ·H 2 O reducer played crucial roles in generating fluorescent Cu NCs. Additional experiments were performed (Figures S5 and S6) and the results show more than 5 mM Cu 2+ and 85% N 2 H 4 ·H 2 O solution (~17 M) were effective to form strongly orange emitting Cu NCs embedded in ESM after the reaction duration of 5 h at room temperature. Interestingly, when the prepared monolithic Cu NCs@ESM was always immersed in N 2 H 4 ·H 2 O reaction solution until several days at 4 • C, the membrane gradually dissolved due to the alkaline hydrolysis and a homogeneous solution with brownish yellow was obtained, suggesting the immobilized Cu NCs were released into aqueous solution and dispersed homogeneously. The maximum excitation and emission peaks were observed at 337 nm and 606 nm, and the aqueous Cu NCs was excitation-independent as the parent Cu NCs@ESM ( Figure S7). The large Stokes shift up to 269 nm of the Cu NCs makes it actually applicable with very low background and light scattering interference, which is ideal for bioimaging and biosensing.

Synthesis and Characterization of Cu NCs@ESM Using NH 2 OH·HCl
In the above case, the fluorescent Cu NCs were successfully in situ generated in ESM by externally introduced N 2 H 4 ·H 2 O as the reducer. In order to develop diverse synthetic routes, other reducing agents, NaBH 4 and NH 2 OH·HCl were also tried to prepare fluorescent Cu NCs@ESM employing the similar synthetic route. However, very weakly red emitting Cu NCs could be obtained via NaBH 4 reduction. In particular, the reaction condition was relatively harsh, and it seemed very difficult to control a good nucleation and growth of copper clusters due to the strong reducing capacity and instability of NaBH4 itself ( Figure S8). Meanwhile, no fluorescent CuNCs could be generated by NH 2 OH·HCl reduction in the case. One possible reason is that, comparable to NaBH 4 and N 2 H 4 ·H 2 O, the lower reducibility of NH 2 OH·HCl was uncapable of converting Cu(II) to Cu(0) effectively.
Intriguingly, it was found that the Cu 2+ /ESM treated subsequently with strong alkaline solution before throwing into NH 2 OH·HCl could be reduced to obtain red fluorescent Cu NCs effectively. In the typical procedure, ESM was briefly incubated in a CuSO 4 solution (1 mL, 50 mM) for 10 min, and then the ESM immobilized with Cu 2+ was soaked in a NaOH solution of 10 M for 30 min during which the membrane color changed to purplish red from blue indicating the formation of ESM-Cu complex [20,47], and finally transferred into 1 M NH 2 OH·HCl to initiate the reduction. As the reaction proceeded for 1 h, the color of the membrane changed from purplish red to yellow, suggesting the formation of Cu NCs embedded in ESM. Figure  capacity and instability of NaBH4 itself ( Figure S8). Meanwhile, no fluorescent CuNCs could be generated by NH2OH·HCl reduction in the case. One possible reason is that, comparable to NaBH4 and N2H4·H2O, the lower reducibility of NH2OH·HCl was uncapable of converting Cu(II) to Cu(0) effectively. Intriguingly, it was found that the Cu 2+ /ESM treated subsequently with strong alkaline solution before throwing into NH2OH·HCl could be reduced to obtain red fluorescent Cu NCs effectively. In the typical procedure, ESM was briefly incubated in a CuSO4 solution (1 mL, 50 mΜ) for 10 min, and then the ESM immobilized with Cu 2+ was soaked in a NaOH solution of 10 M for 30 min during which the membrane color changed to purplish red from blue indicating the formation of ESM-Cu complex [20,47], and finally transferred into 1 M NH2OH·HCl to initiate the reduction. As the reaction proceeded for 1 h, the color of the membrane changed from purplish red to yellow, suggesting the formation of Cu NCs embedded in ESM. Figure   As shown in Figure S10, weakly red emitting Cu NCs were generated after reaction in NH2OH·HCl solutions for 1~6 h, when the Cu 2+ /ESMs were treated subsequently with 500 mM~5 M NaOH aqueous solution before throwing into 1 M NH2OH·HCl, respectively. Even more, no fluorescence was observed during the whole reaction with a NaOH concentration lower than 500 mM. However, when the concentrations of NaOH solution reached 10~12 M, the visible red emitting Cu NCs could be in situ generated within 30 min, and the fluorescence strength reached a maximum after 5 h. Obviously, in the procedure employing NH2OH·HCl as reductant, the strong alkaline condition was essential for the generation of red fluorescent Cu NCs. First, in acid and neutral aqueous solution, free carboxyl and amino groups in ESM were partly dissociated into negatively As shown in Figure S10, weakly red emitting Cu NCs were generated after reaction in NH 2 OH·HCl solutions for 1~6 h, when the Cu 2+ /ESMs were treated subsequently with 500 mM~5 M NaOH aqueous solution before throwing into 1 M NH 2 OH·HCl, respectively. Even more, no fluorescence was observed during the whole reaction with a NaOH concentration lower than 500 mM. However, when the concentrations of NaOH solution reached 10~12 M, the visible red emitting Cu NCs could be in situ generated within 30 min, and the fluorescence strength reached a maximum after 5 h. Obviously, in the procedure employing NH 2 OH·HCl as reductant, the strong alkaline condition was essential for the generation of red fluorescent Cu NCs. First, in acid and neutral aqueous solution, free carboxyl and amino groups in ESM were partly dissociated into negatively charged species, incubating ESM with Cu 2+ immediately produced Cu 2+ /ESM association by their electrostatic attraction and coordination. Subsequently, the acidity of solution was adjusted to more than pH 12 by adding NaOH and this resulted in an increase in the degree of exposure of free amino groups which could combine with Cu 2+ easily to form a stable complex. Second, the reducing capability of tyrosine residues can be greatly improved by adjusting the reaction pH above the pKa of Tyr (~10). Hence, the reducing capability of ESM itself was not unexpected since it contains Tyr residues and possibly other residues with reduction functionality. Third, Kodali et al. reported the presence of considerable amount of cysteine-rich ESM proteins with multiple disulfide crosslink [48]. The disulfide bonds could be cleaved into free -SH under alkaline environment. And the -SH can easily combine to form stable Cu-S bond, which can stabilize the nucleated clusters. The influences of other process parameters, such as incubation time, the concentrations of CuSO 4 precursor and NH 2 OH·HCl were also investigated systematically, which were shown in Figure S11-S13.

Synthesis and Characterization of Cu NCs@ESM Using VC
VC is one mild and environmentally friendly reagent, which was often used in the nanomaterials preparation instead of some severe or toxic reductants. Herein, VC was also employed to generate fluorescent Cu NCs embedded in ESM. Excitedly, it was found that VC could in situ reduce Cu 2+ loaded on ESM into fluorescent Cu NCs under alkaline solution. The obtained Cu NCs@ESM had a yellowish color and emitted strong red fluorescence centered at 643 nm under 365 nm UV irradiation with interwoven fibrous structure (Figure 3a,b). The Cu NCs@ESM had a maximum excitation at 375 nm and the maximum emission wavelength was almost invariable when the excitation wavelengths changed from 340 to 570 nm indicating the uniform size distribution of generated NCs (Figures S14 and 3c). It noteworthy that different orange and red fluorescence were observed in the developed three synthetic routes, which was confirmed by the excitation and emission spectra of Cu NCs@ESM composites fabricated by employing different reducing reagents ( Figures S4, S9 and S14). Although the exact size determination of the Cu NCs embedded in the ESM was difficult, the different size of clusters could be expected in different synthetic routes due to the different clustering process of Cu atoms under different reaction environment and the size-dependent fluorescence could be achieved by varying the synthetic routes [17]. The content of copper in the obtained Cu NCs@ESM was determined to be 1.6% by ICP-AES. The generation of Cu(0) on the ESM platform was further demonstrated by the Cu2P 3/2 and Cu2P 1/2 peaks centered at 931.6 and 951.3 eV, respectively (Figure 3d). The time-resolved fluorescence decay of the obtained Cu NCs@ESM was simultaneously investigated by time correlated single photon counting (TCSPC) technique, and the average lifetime of generated Cu NCs was calculated to be 2.84 ns ( Figure S15). In the typical alkaline condition, when the concentrations of CuSO 4 precursor was more than 10 mM and concentrations of VC was more than 1 M, the red fluorescent Cu NCs were generated in a few minutes and reached the strongest fluorescence about 5 h (Figures S16 and S17). It has to be noted that the strong alkaline environment plays a key role in the synthetic route. When the ESM was pre-incubated in 1 mL CuSO 4 (50 mM) for 10 min, then treated with NaOH aqueous solution of concentrations lower than 0.1 M, and finally transferred to 2 M VC solution, no fluorescent Cu NCs could be generated even with a prolonged reaction ( Figure S18). This may be due to the reducing capability of ESM itself and VC was initiated effectively in strong alkaline condition to generate metal nucleation and fluorescent clusters as expected.
To test the effect of copper precursors on the fluorescence of Cu NCs@ESM in the developed strategies, various copper precursors such as CuCl 2 , Cu(NO 3 ) 2 , Cu(CH 3 COO) 2 , CuSO 4 were employed in the three routes reduced by N 2 H 4 ·H 2 O, NH 2 OH·HCl and VC, respectively. The results show that brightly orange and red emitting Cu NCs could be generated no matter what kind of the above four copper precursors was employed ( Figure S19). Interestingly, the ESM platform, even if boiled in water, was almost equally efficient in the proposed methods for generating fluorescent Cu NCs@ESM ( Figure S20). In addition, UV-Vis DRS measurement was conducted to further confirm the successful formation of Cu NCs on the ESM substrate [44]. As shown in Figure 4, there were no characteristic surface plasmon resonance (SPR) absorption of Cu nanoparticles (Cu NPs) located at~560 nm in the spectra of Cu NCs@ESM fabricated by the three different routes, indicating the in situ generation of ultra-small Cu NCs rather than the large-sized Cu NPs [31]. spectra of Cu NCs@ESM fabricated by the three different routes, indicating the in situ generation of ultra-small Cu NCs rather than the large-sized Cu NPs [31].  It is noteworthy that the blue fluorescence was also dramatically suppressed after the generation of Cu NCs compared with the ESM itself in the NH2OH·HCl and VC reduction routes ( Figure S21). According to the excitation spectra of the fabricated composites ( Figures S9 and S14)    It is noteworthy that the blue fluorescence was also dramatically suppressed after the generation of Cu NCs compared with the ESM itself in the NH2OH·HCl and VC reduction routes ( Figure S21). According to the excitation spectra of the fabricated composites ( Figures S9 and S14)  It is noteworthy that the blue fluorescence was also dramatically suppressed after the generation of Cu NCs compared with the ESM itself in the NH 2 OH·HCl and VC reduction routes ( Figure S21). According to the excitation spectra of the fabricated composites ( Figures S9 and S14), one possible reason was that an efficient fluorescence resonance energy transfer (FRET) could happen between the ESM protein and Cu NCs, indicating a spatial proximity between the formed Cu NCs and the protein fluorophores inside the ESM, and the excellent stability of the obtained monolithic Cu NCs@ESM could be expected. On the other hand, the contribution of the oxidation or reduction of some components in the natural ESM substrate during the reaction process was not unexpected. As shown in Figure S22, the red fluorescence intensity of monolithic Cu NCs@ESM was still strong stored in wet form (dipped in water) for around 15 days and even more than a month in dried form at 4 • C in the refrigerator. Moreover, photobleaching was not observed even when the product had been continuously irradiated under 365 nm UV light for 12 h ( Figure S23). Attractively, the fluorescence intensity could be maintained without any weakening even under high ionic strength conditions (1 M NaCl solution, Figure S24) for a long period of time. In addition, the Cu NCs@ESM remained very stable in the majority of organic solvents while immediate fluorescence quenching occurred in ethanol as shown in Figure 5a, and the fluorescence intensity decreased continuously with increasing volume fractions of ethanol (vol %, ethanol:H 2 O). It should be noted that a low volume fraction of 0.05% could result in an obviously distinguishable response from the background quickly (Figure 5b). The effective response of Cu NCs@ESM to ethanol content indicates the promise to develop visual sensing strips for ethanol solution and vapor conveniently based on the monolithic products. Herein, the fluorescent stability of Cu NCs embedded in ESM substrate was contributed to the protection of fibrous ESM structure and rich functional groups in the natural ESM acting as nucleation template and capping stabilizer, which avoids the aggregation and oxidation induced fluorescence quenching. In the presence of ethanol, ESM substrate was denatured mainly due to the destroy of hydrogen bonds and hydrophobicity of the composed proteins, and a looser structure was expected. Thus, the protection of ESM with Cu NCs was correspondingly weakened and the surface chemical environment of the clusters exhibited a significant change, resulting in easy oxidation of Cu NCs and fluorescence quenching of Cu NCs@ESM composite. In addition, the yellow color of the fabricated composite, which was the characteristic color of formed ultralfine Cu NCs, was found to fade obviously in the presence of ethanol ( Figure S25a). Fascinatingly, the red fluorescence could be recovered when the quenched composite was replaced in a reducing agent solution such as sodium borohydride (NaBH 4 ), and the yellow color reappeared, which showed the promise of the recycled ethanol sensing application ( Figure S25b). ESM protein and Cu NCs, indicating a spatial proximity between the formed Cu NCs and the protein fluorophores inside the ESM, and the excellent stability of the obtained monolithic Cu NCs@ESM could be expected. On the other hand, the contribution of the oxidation or reduction of some components in the natural ESM substrate during the reaction process was not unexpected. As shown in Figure S22, the red fluorescence intensity of monolithic Cu NCs@ESM was still strong stored in wet form (dipped in water) for around 15 days and even more than a month in dried form at 4 °C in the refrigerator. Moreover, photobleaching was not observed even when the product had been continuously irradiated under 365 nm UV light for 12 h ( Figure S23). Attractively, the fluorescence intensity could be maintained without any weakening even under high ionic strength conditions (1 M NaCl solution, Figure S24) for a long period of time. In addition, the Cu NCs@ESM remained very stable in the majority of organic solvents while immediate fluorescence quenching occurred in ethanol as shown in Figure 5a, and the fluorescence intensity decreased continuously with increasing volume fractions of ethanol (vol %, ethanol:H2O). It should be noted that a low volume fraction of 0.05% could result in an obviously distinguishable response from the background quickly ( Figure  5b). The effective response of Cu NCs@ESM to ethanol content indicates the promise to develop visual sensing strips for ethanol solution and vapor conveniently based on the monolithic products. Herein, the fluorescent stability of Cu NCs embedded in ESM substrate was contributed to the protection of fibrous ESM structure and rich functional groups in the natural ESM acting as nucleation template and capping stabilizer, which avoids the aggregation and oxidation induced fluorescence quenching. In the presence of ethanol, ESM substrate was denatured mainly due to the destroy of hydrogen bonds and hydrophobicity of the composed proteins, and a looser structure was expected. Thus, the protection of ESM with Cu NCs was correspondingly weakened and the surface chemical environment of the clusters exhibited a significant change, resulting in easy oxidation of Cu NCs and fluorescence quenching of Cu NCs@ESM composite. In addition, the yellow color of the fabricated composite, which was the characteristic color of formed ultralfine Cu NCs, was found to fade obviously in the presence of ethanol ( Figure S25a). Fascinatingly, the red fluorescence could be recovered when the quenched composite was replaced in a reducing agent solution such as sodium borohydride (NaBH4), and the yellow color reappeared, which showed the promise of the recycled ethanol sensing application ( Figure S25b).

Surface Patterning on ESM Substrate
Due to the excellent stability and strong fluorescence of the prepared monolithic Cu NCs@ESM in dried form, it was possible to create fluorescent patterns on the surface of ESM employing the proposed facile and green route employing VC as the reducing reagent. For example, a red

Surface Patterning on ESM Substrate
Due to the excellent stability and strong fluorescence of the prepared monolithic Cu NCs@ESM in dried form, it was possible to create fluorescent patterns on the surface of ESM employing the proposed facile and green route employing VC as the reducing reagent. For example, a red fluorescent smiling face and "Cu-N-C-s" letters were obtained by simply painting them on a piece of ESM substrate with CuSO 4 solution as "ink" followed by VC incubation under alkaline condition ( Figure 6). More importantly, this work could be employed for "hidden" writing and anti-counterfeiting applications.
Materials 2018, 11, x FOR PEER REVIEW 10 of 16 fluorescent smiling face and "Cu-N-C-s" letters were obtained by simply painting them on a piece of ESM substrate with CuSO4 solution as "ink" followed by VC incubation under alkaline condition ( Figure 6). More importantly, this work could be employed for "hidden" writing and anticounterfeiting applications.

Monolithic Cu NCs@ESM Composite as Hg 2+ Responsive Strips
Developing solid state fluorescent materials for sensing purposes (a good example is pH testing paper) is of great significance with the advantages of reducing liquid handling operations (such as accurate volume measurements) and greatly lowered detection costs, which is especially useful in circumstances of in-field or POC quantitative or semi-quantitative tests. Mercury is a highly toxic heavy metal element that is widely distributed in the environment. There is a strong demand to develop low-cost and efficient techniques for Hg 2+ detection. As a proof-of-concept demonstration, the as-prepared Cu NCs@ESM was used as visible "turn-off" strip sensor for Hg 2+ with satisfactory sensitivity and selectivity. As shown in Figure 7b, the fluorescence of Cu NCs@ESM was quenched completely by dipping the strip in an Hg 2+ solution for 1 h, while the fluorescence intensity was almost unchanged when incubated with other metal ions (Mn 2+ , Co 2+ , Cd 2+ , Ba 2+ , Zn 2+ , Pb 2+ , Al 3+ , Fe 3+ , Cu 2+ , K + , Na + ) at the concentration of 500 μM. The current results show that the concentration of Hg 2+ as low to 50 μM could be visibly recognized by distinguishable fluorescence quenching from the background easily (Figure 7a). The possible quenching mechanism is attributed to the high-affinity metallophilic interactions between the d 10 centers of Hg 2+ (5d 10 ) and d 10 centers of Cu + (3d 10 ) in the Cu NCs embedded in ESM. In addition, the formation of certain complexes by coordination and electrostatic attractions between Hg 2+ and the rich functional groups (e.g., hydroxyl, carboxyl, amino and thiol) in the ESM platform was not unexpected. Overall, the surface capping-ligands and charge states of these Cu NCs were greatly changed in the presence of Hg 2+ ions mainly due to the aforementioned interactions, which leads to the effective fluorescence quenching [49].

Monolithic Cu NCs@ESM Composite as Hg 2+ Responsive Strips
Developing solid state fluorescent materials for sensing purposes (a good example is pH testing paper) is of great significance with the advantages of reducing liquid handling operations (such as accurate volume measurements) and greatly lowered detection costs, which is especially useful in circumstances of in-field or POC quantitative or semi-quantitative tests. Mercury is a highly toxic heavy metal element that is widely distributed in the environment. There is a strong demand to develop low-cost and efficient techniques for Hg 2+ detection. As a proof-of-concept demonstration, the as-prepared Cu NCs@ESM was used as visible "turn-off" strip sensor for Hg 2+ with satisfactory sensitivity and selectivity. As shown in Figure 7b, the fluorescence of Cu NCs@ESM was quenched completely by dipping the strip in an Hg 2+ solution for 1 h, while the fluorescence intensity was almost unchanged when incubated with other metal ions (Mn 2+ , Co 2+ , Cd 2+ , Ba 2+ , Zn 2+ , Pb 2+ , Al 3+ , Fe 3+ , Cu 2+ , K + , Na + ) at the concentration of 500 µM. The current results show that the concentration of Hg 2+ as low to 50 µM could be visibly recognized by distinguishable fluorescence quenching from the background easily (Figure 7a). The possible quenching mechanism is attributed to the high-affinity metallophilic interactions between the d 10 centers of Hg 2+ (5d 10 ) and d 10 centers of Cu + (3d 10 ) in the Cu NCs embedded in ESM. In addition, the formation of certain complexes by coordination and electrostatic attractions between Hg 2+ and the rich functional groups (e.g., hydroxyl, carboxyl, amino and thiol) in the ESM platform was not unexpected. Overall, the surface capping-ligands and charge states of these Cu NCs were greatly changed in the presence of Hg 2+ ions mainly due to the aforementioned interactions, which leads to the effective fluorescence quenching [49].

Catalytic Activity of Cu NCs@ESM for MB Reduction
Because of a greater proportion of high energy orbitals, ultrasmall metal NCs with usual core sizes smaller than 2 nm have been considered as active catalysts different from cousin nanoparticles and bulks [18]. Theoretical and experimental studies have shown that Cu NCs possess unique catalysis properties, and the catalytic performance of the clusters has been found strongly dependent on clusters size, composition and cluster-support interactions [1,14]. With the attractive features of the in situ generated Cu NCs@ESM nanocomposite, such as monolith, convenient operation, good stability, easy storage and transport, their potential utility as low-cost and recyclable catalyst was expected. Specifically, to examine the catalytic activity of the product, the reduction degradation of methylene blue (MB) dye was investigated as model reaction [14,18,39,50]. As shown by the inset in Figure 8, the original blue color of MB solution immediately faded after the monolithic Cu NCs@ESM was thrown into the solution due to the formation of colorless product, leucomethylene blue (LMB). However, the blue color was almost unchanged when the serial ESM controls without Cu NCs incorporated were added into the MB solutions and incubated even for a longer time, indicating that the observed catalytic performance of Cu NCs@ESM nanocomposite was really contributed to the incorporated Cu NCs, similar to that of reported Cu NCs prepared by wet chemistry methods ( Figure  S26a). The UV-vis spectrometer was used to optically monitor the catalyzed process. The featured maximum absorption peak at 662 nm of original MB dye was found to be quickly and dramatically decreased within 2 min, which suggests that the Cu NCs@ESM could serve as an efficient catalyst for the reduction degradation of MB without the need of either additional reducing agents or UV irradiation. Significantly, the strong fluorescence of Cu NCs@ESM was still maintained after the reduction degradation (inset in Figures 8 and S26b), and the catalytic reaction could be cycled 4~5 times just by removing out and throwing into facilely, benefiting from the rigid solid monolithic characteristics of the ESM platform.

Catalytic Activity of Cu NCs@ESM for MB Reduction
Because of a greater proportion of high energy orbitals, ultrasmall metal NCs with usual core sizes smaller than 2 nm have been considered as active catalysts different from cousin nanoparticles and bulks [18]. Theoretical and experimental studies have shown that Cu NCs possess unique catalysis properties, and the catalytic performance of the clusters has been found strongly dependent on clusters size, composition and cluster-support interactions [1,14]. With the attractive features of the in situ generated Cu NCs@ESM nanocomposite, such as monolith, convenient operation, good stability, easy storage and transport, their potential utility as low-cost and recyclable catalyst was expected. Specifically, to examine the catalytic activity of the product, the reduction degradation of methylene blue (MB) dye was investigated as model reaction [14,18,39,50]. As shown by the inset in Figure 8, the original blue color of MB solution immediately faded after the monolithic Cu NCs@ESM was thrown into the solution due to the formation of colorless product, leucomethylene blue (LMB). However, the blue color was almost unchanged when the serial ESM controls without Cu NCs incorporated were added into the MB solutions and incubated even for a longer time, indicating that the observed catalytic performance of Cu NCs@ESM nanocomposite was really contributed to the incorporated Cu NCs, similar to that of reported Cu NCs prepared by wet chemistry methods ( Figure S26a). The UV-vis spectrometer was used to optically monitor the catalyzed process. The featured maximum absorption peak at 662 nm of original MB dye was found to be quickly and dramatically decreased within 2 min, which suggests that the Cu NCs@ESM could serve as an efficient catalyst for the reduction degradation of MB without the need of either additional reducing agents or UV irradiation. Significantly, the strong fluorescence of Cu NCs@ESM was still maintained after the reduction degradation (inset in Figures 8 and S26b), and the catalytic reaction could be cycled 4~5 times just by removing out and throwing into facilely, benefiting from the rigid solid monolithic characteristics of the ESM platform.

Conclusions
In summary, in situ generation of orange/red emitting copper nanoclusters embedded in monolithic eggshell membrane (Cu NCs@ESM) was successfully demonstrated in this work. To the best of our knowledge, this is the first report on the fabrication of fluorescent Cu NCs employing natural ESM as a platform, and three different synthetic routes were developed using various reducing reagents, including N2H4·H2O, NH2OH·HCl and Vitamin C (VC) under different reaction conditions. The obtained Cu NCs@ESM nanocomposites show excellent photo and chemical stability. Significantly, the routes are extremely low cost, green, facile, and versatile. Syntheses of other monolithic nanoclusters, nanoparticles and quantum dots are going on well in our laboratory employing the similar strategy based on ESM or even silkworm cocoon as the solid platforms. In addition, the selective fluorescence quenching response of Cu NCs@ESM to Hg 2+ ions and its good catalytic activity for MB reduction degradation makes it ideal as an inexpensive sensing strip and recyclable catalyst. We believe that it would serve as a general strategy for the fabrication of various monolithic nanomaterials with potential applications in the fields of chemical sensing, heterogeneous catalysis, antibacterial nanomaterial, surface enhanced Raman scattering interface, fluorescent surface patterning, nanodevices and so on.

Conclusions
In summary, in situ generation of orange/red emitting copper nanoclusters embedded in monolithic eggshell membrane (Cu NCs@ESM) was successfully demonstrated in this work. To the best of our knowledge, this is the first report on the fabrication of fluorescent Cu NCs employing natural ESM as a platform, and three different synthetic routes were developed using various reducing reagents, including N 2 H 4 ·H 2 O, NH 2 OH·HCl and Vitamin C (VC) under different reaction conditions. The obtained Cu NCs@ESM nanocomposites show excellent photo and chemical stability. Significantly, the routes are extremely low cost, green, facile, and versatile. Syntheses of other monolithic nanoclusters, nanoparticles and quantum dots are going on well in our laboratory employing the similar strategy based on ESM or even silkworm cocoon as the solid platforms. In addition, the selective fluorescence quenching response of Cu NCs@ESM to Hg 2+ ions and its good catalytic activity for MB reduction degradation makes it ideal as an inexpensive sensing strip and recyclable catalyst. We believe that it would serve as a general strategy for the fabrication of various monolithic nanomaterials with potential applications in the fields of chemical sensing, heterogeneous catalysis, antibacterial nanomaterial, surface enhanced Raman scattering interface, fluorescent surface patterning, nanodevices and so on.