Magnetostrictive Properties of Mn0.70Zn0.24Fe2.06O4 Ferrite

Institute of Metrology and Biomedical Engineering, Warsaw University of Technology, 02-525 Warsaw, Poland
Author to whom correspondence should be addressed.
Materials 2018, 11(10), 1894;
Received: 18 September 2018 / Revised: 30 September 2018 / Accepted: 1 October 2018 / Published: 3 October 2018
This paper presents the results of measurements of magnetostrictive properties of Mn0.70Zn0.24Fe2.06O4 ferrite for power applications. Frame-shaped samples were used for measurements to guarantee a uniform magnetizing field and magnetostrictive strain distribution. Magnetostrictive hysteresis loops were measured by semiconductor strain gauges. The results indicate that the magnetostrictive characteristic of Mn0.70Zn0.24Fe2.06O4 ferrite is non-monotonic and magnetostriction changes have opposite signs for higher values of the magnetizing field. View Full-Text
Keywords: power ferrites; Mn-Zn ferrites; magnetostriction power ferrites; Mn-Zn ferrites; magnetostriction
Show Figures

Figure 1

MDPI and ACS Style

Bieńkowski, A.; Szewczyk, R. Magnetostrictive Properties of Mn0.70Zn0.24Fe2.06O4 Ferrite. Materials 2018, 11, 1894.

Show more citation formats Show less citations formats
Note that from the first issue of 2016, MDPI journals use article numbers instead of page numbers. See further details here.

Article Access Map by Country/Region

Back to TopTop