Influence of Nb on the Microstructure and Fracture Toughness of (Zr0.76Fe0.24)100−xNbx Nano-Eutectic Composites

The present study demonstrates the evolution of eutectic microstructure in arc-melted (Zr0.76Fe0.24)100−xNbx (0 ≤ x ≤ 10 atom %) composites containing α-Zr//FeZr2 nano-lamellae phases along with pro-eutectic Zr-rich intermetallic phase. The effects of Nb addition on the microstructural evolution and mechanical properties under compression, bulk hardness, elastic modulus, and indentation fracture toughness (IFT) were investigated. The Zr–Fe–(Nb) eutectic composites (ECs) exhibited excellent fracture strength up to ~1800 MPa. Microstructural characterization revealed that the addition of Nb promotes the formation of intermetallic Zr54Fe37Nb9. The IFT (KIC) increases from 3.0 ± 0.5 MPa√m (x = 0) to 4.7 ± 1.0 MPa√m (x = 2) at 49 N, which even further increases from 5.1 ± 0.5 MPa√m (x = 0) and up to 5.9 ± 1.0 MPa√m (x = 2) at higher loads. The results suggest that mutual interaction between nano-lamellar α-Zr//FeZr2 phases is responsible for enhanced fracture resistance and high fracture strength.

Considering a critical survey of the current state of understanding, further exploration in the broad field of the mechanical properties of NECs, particularly in the context of processing, as well as the structure-property relationship seem to be essential. On the other hand, Zr-based alloys possess high-temperature properties, good mechanical and radiation damage resistance, low thermal neutron capture cross section, and excellent corrosion resistance, which makes them useful in nuclear power plant applications and chemical processing plants [17][18][19]. Zr-Fe eutectic composites are very attractive because of their high abundance of natural resources and corrosion-resistant properties [17][18][19]. However, very few studies have been reported on the structure-property relationship and phase formation, the deformation mechanism, and the fracture behavior of the Zr-base lamellar eutectic composites [20,21]. The present work attempts to reveal the microscopic deformation behavior of the Zr-Fe-based NECs. The effect of Nb addition to eutectic Zr 76 Fe 24 on the compressive mechanical properties and the deformation behavior have been evaluated using the indentation fracture toughness method at various loads.

Materials and Methods
A series of (Zr 0.76 Fe 0.24 ) 100−x Nb x (x = 0, 2, 4, 6, and 10 atom %) alloy ingots were prepared by arc-melting process in an Ar atmosphere. The arc-melted ingots (AMIs) were re-melted repeatedly at least three times for homogenization. Parallelepiped specimens were cut from the AMIs using electro-discharge machining (EDM). The constituent phases and their structure were identified using a Philips PW3373 PANalytical high-resolution X-ray diffraction unit (XRD, Cu-K α radiation, Philips, Kassel, Germany). The Vickers macro-hardness (H) of the specimens were measured using Leco LV-700, USA Vickers hardness tester (LECO, Saint Joseph, MO, USA) according to ASTM E-384 standard for a dwell time of 15 s. Indentations at each test load of P max = 49 N up to P max = 294 N were conducted for an average hardness H [4,8]. The measurement of IFT is sensitive to surface preparation; therefore, the samples were polished carefully to eliminate the residual stress zones on the specimens' surface. The IFT values denoted as K IC was measured on highly polished specimen surfaces, which were free from any pre-cracks, using a Vickers diamond pyramid indenter at P max values of 49 to 294 N and the Vickers hardness tester mentioned above. K IC deals with the critical value of stress intensity factor K I in crack opening mode when fracture initiates and an unstable crack propagates. The K IC values of Zr-Fe-(Nb) eutectic composites alloys were calculated using an equation proposed by Niihara et al. [22,23]: where H is the macrohardness in GPa, E is Young's modulus in GPa, P is the applied indentation load (P max ), a is half of the indentation diagonal length, and l is the Palmqvist crack length, i.e., the extent of the cracks that emerge from the edges of the indentations only. A Leica DM 2500M optical microscope (OM) and a SUPRA 40 field emission scanning electron microscope (FESEM, Carl Zeiss SMT AG, Oberkochen, Germany) equipped with an Oxford ISIS300 energy dispersive X-ray spectrometer (EDS) (Oxford Instruments plc, Oxfordshire, UK) were used to investigate the geometry of the indentation impressions, the median, and Palmqvist crack lengths. The volume fraction of the phases were calculated from the microscopy images. At least five images were used to obtain average values. Compression tests (CTs) were performed at room temperature using a TINIUS Olsen H50KS universal testing machine (TINIUS Olsen, Kolkata, India) at an initial strain rate of 8 × 10 −4 s −1 . A detailed microstructural investigation was performed using a JEOL JEM-2100 transmission electron microscope (TEM) (JEOL, Tokyo, Japan). Thin TEM samples were prepared by mechanical polishing followed by ion-beam milling in liquid N 2 using Gatan PIPS691 precision ion polishing system. A 35 DLP Olympus Panametric ultrasonic pulser receiver was used to measure the elastic properties.

Results and Discussion
3.1. X-ray Diffraction and Phase Analysis of As-Solidified Composites Figure 1 shows the XRD patterns for the Zr-Fe-(Nb) with varying Nb content up to x = 10 atom %. The XRD pattern of x = 0 shows sharp diffraction peaks of hcp α-Zr, bcc FeZr 2 ; however, additional reflections of intermetallic Zr 54 Fe 37 Nb 9 (JCPDS #00-046-1095) has been observed from x = 2 [24]. It has been observed that the peak intensity of FeZr 2 phase gradually decreases with the addition of Nb content, whereas the peak intensities of intermetallic Zr 54 Fe 37 Nb 9 phase increases with the increase in the amount of Nb. This indicates that the phase fraction of intermetallic Zr 54 Fe 37 Nb 9 is higher in the alloys with higher Nb content. Therefore, it may be concluded that the addition of Nb assists in the formation and stabilization of the intermetallic phase Zr 54 Fe 37 Nb 9 .
Materials 2018, 11, 113 3 of 9 indentation impressions, the median, and Palmqvist crack lengths. The volume fraction of the phases were calculated from the microscopy images. At least five images were used to obtain average values. Compression tests (CTs) were performed at room temperature using a TINIUS Olsen H50KS universal testing machine (TINIUS Olsen, Kolkata, India) at an initial strain rate of 8 × 10 −4 s −1 . A detailed microstructural investigation was performed using a JEOL JEM-2100 transmission electron microscope (TEM) (JEOL, Tokyo, Japan). Thin TEM samples were prepared by mechanical polishing followed by ion-beam milling in liquid N2 using Gatan PIPS691 precision ion polishing system. A 35 DLP Olympus Panametric ultrasonic pulser receiver was used to measure the elastic properties. Figure 1 shows the XRD patterns for the Zr-Fe-(Nb) with varying Nb content up to x = 10 atom %. The XRD pattern of x = 0 shows sharp diffraction peaks of hcp α-Zr, bcc FeZr2; however, additional reflections of intermetallic Zr54Fe37Nb9 (JCPDS #00-046-1095) has been observed from x = 2 [24]. It has been observed that the peak intensity of FeZr2 phase gradually decreases with the addition of Nb content, whereas the peak intensities of intermetallic Zr54Fe37Nb9 phase increases with the increase in the amount of Nb. This indicates that the phase fraction of intermetallic Zr54Fe37Nb9 is higher in the alloys with higher Nb content. Therefore, it may be concluded that the addition of Nb assists in the formation and stabilization of the intermetallic phase Zr54Fe37Nb9.   Figure 2b,c, respectively. Table 1 summarizes the constituent phases in different Nb containing composites, as identified using XRD and EDS analyses. A new phase with chemical composition Zr54Fe37Nb9, (atom %) evolved in the x = 4 sample, and the morphology was modified from the lamellar eutectic to a complex heterogeneous microstructure, consisting of mainly α-Zr and Zr54Fe37Nb9, as also observed in x = 6 ( Figure 2d) and x = 10 ( Figure 2e).   Figure 2b,c, respectively. Table 1 summarizes the constituent phases in different Nb containing composites, as identified using XRD and EDS analyses. A new phase with chemical composition Zr 54 Fe 37 Nb 9 , (atom %) evolved in the x = 4 sample, and the morphology was modified from the lamellar eutectic to a complex heterogeneous microstructure, consisting of mainly α-Zr and Zr 54 Fe 37 Nb 9 , as also observed in x = 6 ( Figure 2d) and x = 10 ( Figure 2e). The volume fraction (vol %) of the phases present in these samples are shown in Table 1. The amount of α-Zr phase remained constant around 69-74 vol % when the Nb content varied from 0 to 6 atom %. The α-Zr showed a decrease when Nb content increased to 10 vol %. On the other hand, the amount of FeZr 2 phase decreased from 31 vol % in the x = 0 sample to 12 vol % in the x = 4 sample and finally disappeared when Nb content increased to 6 atom %. The ternary intermetallic phase is not observed in the sample without Nb content. With the addition of Nb (x = 2), the ternary intermetallic phases form and its fraction increased from 8 to 39 vol % when the Nb content increased from 2 to 10 atom %, respectively. Therefore, the addition of Nb helped to destabilize the FeZr 2 phase and promoted the formation of the Zr 54 Fe 37 Nb 9 intermetallic compound, as corroborated by the XRD data.

Microstructural Characterization of the As-Solidified Composites
The volume fraction (vol %) of the phases present in these samples are shown in Table 1. The amount of α-Zr phase remained constant around 69-74 vol % when the Nb content varied from 0 to 6 atom %. The α-Zr showed a decrease when Nb content increased to 10 vol %. On the other hand, the amount of FeZr2 phase decreased from 31 vol % in the x = 0 sample to 12 vol % in the x = 4 sample and finally disappeared when Nb content increased to 6 atom %. The ternary intermetallic phase is not observed in the sample without Nb content. With the addition of Nb (x = 2), the ternary intermetallic phases form and its fraction increased from 8 to 39 vol % when the Nb content increased from 2 to 10 atom %, respectively. Therefore, the addition of Nb helped to destabilize the FeZr2 phase and promoted the formation of the Zr54Fe37Nb9 intermetallic compound, as corroborated by the XRD data.   Figure 3 shows bright field (BF) TEM images of the x = 0 and x = 2 samples, respectively. Figure 3a shows the alternating two-phase lamellar eutectic structure of the x = 0 sample. The darker lamellae were identified as hcp α-Zr, and the brighter lamellae as tetragonal FeZr2, as deduced from SAED patterns. Similarly, a eutectic microstructure is revealed in Figure 3b for the x = 2 sample. The interlamellar spacing (λ = (λα-Zr + λFeZr2)/2) was determined by measuring the lowest possible λ values at 10 different locations. The lowest values of λ were measured to be 120 nm, 135 nm, and 300 nm in the x = 0, x = 2, and x = 6 samples, respectively. Therefore, the addition of Nb increases the λ value and causes a coarsening of the microstructure.   Figure 3 shows bright field (BF) TEM images of the x = 0 and x = 2 samples, respectively. Figure 3a shows the alternating two-phase lamellar eutectic structure of the x = 0 sample. The darker lamellae were identified as hcp α-Zr, and the brighter lamellae as tetragonal FeZr 2 , as deduced from SAED patterns. Similarly, a eutectic microstructure is revealed in Figure 3b for the x = 2 sample. The interlamellar spacing (λ = (λ α-Zr + λ FeZr2 )/2) was determined by measuring the lowest possible λ values at 10 different locations. The lowest values of λ were measured to be 120 nm, 135 nm, and 300 nm in the x = 0, x = 2, and x = 6 samples, respectively. Therefore, the addition of Nb increases the λ value and causes a coarsening of the microstructure. Materials 2018, 11, 113 5 of 9

Compressive Deformation Behavior
The compressive engineering stress-strain plots of Zr-Fe-(Nb) NECs as obtained during the uniaxial compression tests (CT) under constrained geometry at room temperature are plotted in

Elastic Modulus Measurement
The density of Zr-Fe-(Nb) composites were measured by the Archimedes principle and are listed in Table 2. Nb addition increased the density (ρ) of the composites from 6.74 g/cc (x = 0) to 7.03 g/cc (x = 10). The estimated Poisson's ratio ν, Young's modulus E, bulk modulus G, and shear modulus K is summarized in Table 2. The addition of Nb gradually increased the Young's modulus E from 68 (x = 0) to 101 GPa (x = 6), the shear modulus K from 25 (x = 0) to 38 GPa (x = 6), and the bulk

Compressive Deformation Behavior
The compressive engineering stress-strain plots of Zr-Fe-(Nb) NECs as obtained during the uniaxial compression tests (CT) under constrained geometry at room temperature are plotted in Figure 4. The yield strength (σ y ), fracture strength (σ f ), and fracture strain (ε f ) of the investigated NECs are measured and summarized in Table 1. The sample without Nb had a high value of σ y = 1015 MPa and σ f = 1025 MPa, with a low fracture strain of ε f = 2.1%. The stress-strain curves of the investigated NECs show primarily elastic deformation with very limited plastic strain, as evident in Figure 4. Therefore, their σ y values of all the NECs are close to their σ f values. The compression test revealed an increase in fracture strength σ f for the composites with an increase in Nb content. In the x = 2, x = 4 and x = 6 NECs, the measured σ f was found to be increased up to 1060 MPa, 1510 MPa, and 1800 MPa, respectively. The fracture strain ε f gradually increased from 2.1% up to 3.7% upon the addition of Nb. A sudden drop in σ f was observed in the x = 10 NEC, which had a low fracture strength of σ f = 1025 MPa with a reduced strain of ε f = 1.8%. The presence of the eutectic microstructure and an increase in the volume fraction of the ternary intermetallic phase improved the mechanical properties of these samples (with increasing addition of Nb). The best mechanical properties were obtained in the x = 6 condition, where there was an optimum mix of α-Zr and Zr 54 Fe 37 Nb 9 phases. Further increase in the amount of brittle Zr 54 Fe 37 Nb 9 phase degraded the properties of these (Zr 0.76 Fe 0.24 ) 100−x Nb x composites.

Compressive Deformation Behavior
The compressive engineering stress-strain plots of Zr-Fe-(Nb) NECs as obtained during the uniaxial compression tests (CT) under constrained geometry at room temperature are plotted in Figure 4. The yield strength (σy), fracture strength (σf), and fracture strain (εf) of the investigated NECs are measured and summarized in Table 1. The sample without Nb had a high value of σy = 1015 MPa and σf = 1025 MPa, with a low fracture strain of εf = 2.1%. The stress-strain curves of the investigated NECs show primarily elastic deformation with very limited plastic strain, as evident in Figure 4. Therefore, their σy values of all the NECs are close to their σf values. The compression test revealed an increase in fracture strength σf for the composites with an increase in Nb content. In the x = 2, x = 4 and x = 6 NECs, the measured σf was found to be increased up to 1060 MPa, 1510 MPa, and 1800 MPa, respectively. The fracture strain εf gradually increased from 2.1% up to 3.7% upon the addition of Nb. A sudden drop in σf was observed in the x = 10 NEC, which had a low fracture strength of σf = 1025 MPa with a reduced strain of εf = 1.8%. The presence of the eutectic microstructure and an increase in the volume fraction of the ternary intermetallic phase improved the mechanical properties of these samples (with increasing addition of Nb). The best mechanical properties were obtained in the x = 6 condition, where there was an optimum mix of α-Zr and Zr54Fe37Nb9 phases. Further increase in the amount of brittle Zr54Fe37Nb9 phase degraded the properties of these (Zr0.76Fe0.24)100−xNbx composites.

Elastic Modulus Measurement
The density of Zr-Fe-(Nb) composites were measured by the Archimedes principle and are listed in Table 2. Nb addition increased the density (ρ) of the composites from 6.74 g/cc (x = 0) to 7.03 g/cc (x = 10). The estimated Poisson's ratio ν, Young's modulus E, bulk modulus G, and shear modulus K is summarized in Table 2. The addition of Nb gradually increased the Young's modulus E from 68 (x = 0) to 101 GPa (x = 6), the shear modulus K from 25 (x = 0) to 38 GPa (x = 6), and the bulk

Elastic Modulus Measurement
The density of Zr-Fe-(Nb) composites were measured by the Archimedes principle and are listed in Table 2. Nb addition increased the density (ρ) of the composites from 6.74 g/cc (x = 0) to 7.03 g/cc (x = 10). The estimated Poisson's ratio ν, Young's modulus E, bulk modulus G, and shear modulus K is summarized in Table 2. The addition of Nb gradually increased the Young's modulus E from 68 (x = 0) to 101 GPa (x = 6), the shear modulus K from 25 (x = 0) to 38 GPa (x = 6), and the bulk modulus K from 94 (x = 0) to 105 GPa (x = 6), respectively. However, E = 96 GPa and K = 36 GPa was observed in x = 10. Nb addition increased the density of the composites and caused significant changes in their elastic moduli due to the alteration in the phase constituents and subsequently the microstructure.

Vickers Bulk Hardness
The macro-hardness (H) data at different load P max values is summarized in Table 3. Figure 5 shows the variation of H with the addition of Nb. A high value of H = 3.82 ± 0.17 GPa was obtained in the x = 0 sample at P max = 49 N. However, H further increased up to 5.20 ± 0.05 GPa at P max = 49 N in x = 6. Thus, H gradually increased upon the addition of Nb, which suggests an increase in composite strength. However, a sudden drop in hardness of 5.06 ± 0.05 GPa was observed in the x = 6 sample at P max = 49 N, and the intermetallic Zr 54 Fe 37 Nb 9 phase had a big impact on the higher hardness values. The high volume fraction of Zr 54 Fe 37 Nb 9 was present in the x = 10 sample, as revealed in XRD analysis and SEM micrographs, lowering the H values. Therefore, the H of the investigated NECs depended on the relative volume fraction of α-Zr, FeZr 2 , and Zr 54 Fe 37 Nb 9 , as shown in Table 3.

Indentation Fracture Toughness
The Vickers IFT measurements refer to a complex state of three-dimensional crack system with significant deformation residual stress and damage around the cracks. In this investigation, l/a data was considered to be in the range of 0.25-2.5. The values of calculated KIC of the investigated NECs are summarized in Table 3. The length of the cracks extending from the four corners (l) and the size of the indentation diagonal (d) was measured for the desired Palmqvist crack lengths and the size of indentation with an standard error in the range of 2-10%. The IFT measurements were performed at various Pmax values within a range between 49 and 294 N in order to study the effect of load variation and Nb content on the KIC in Zr-Fe-(Nb) NECs. Figure 6 shows the variation of the estimated KIC measured at different Pmax values. KIC gradually increased from 3.0 ± 0.5 in the x = 0 sample at Pmax = 49 N to 4.2 ± 1 MPa√m in the x = 6 sample at Pmax = 49 N; thereafter, it dropped down to 3.6 ± 0.8 MPa√m at x = 10 at Pmax = 49 N. In addition, the estimated KIC gradually increased with the increase in applied indentation load Pmax. Such as in case of the x = 0 AMI, KIC increased from 3.0 ± 0.5 √m at Pmax = 49 N up to 5.1 ± 0.5 MPa√m at Pmax = 294 N. Therefore, the fracture resistance of the investigated composites increased with the increase in Nb content in the NECs up to x = 2. The evolution of intermetallic Zr54Fe37Nb9 decreased the IFT values. By increasing the Nb up to x = 6 atom %, the fracture strength was enhanced due to the presence of nanolamellar α-Zr and FeZr2 phases and solid-solution strengthening. However, the presence of homogeneous NECs (x = 0 and 2) with a higher volume fraction of FeZr2 phase led to IFT values higher than the other Nb-containing specimens.

Fractrographic Investigation
To understand the IFT behavior of the NECs with the nanolamellar phases, the indented and fractured NECs were further investigated in detail. Figure 7 shows the SEM images of the lateral surfaces of the indented and fractured specimens. Palmqvist cracks were observed emerging from the edges of the indentation impressions. The geometry of Palmqvist cracks at the edges of the indentations at an operating load of 49 N is shown in Figure 7, which shows the SEM micrograph of

Indentation Fracture Toughness
The Vickers IFT measurements refer to a complex state of three-dimensional crack system with significant deformation residual stress and damage around the cracks. In this investigation, l/a data was considered to be in the range of 0.25-2.5. The values of calculated K IC of the investigated NECs are summarized in Table 3. The length of the cracks extending from the four corners (l) and the size of the indentation diagonal (d) was measured for the desired Palmqvist crack lengths and the size of indentation with an standard error in the range of 2-10%. The IFT measurements were performed at various P max values within a range between 49 and 294 N in order to study the effect of load variation and Nb content on the K IC in Zr-Fe-(Nb) NECs. Figure 6 shows the variation of the estimated K IC measured at different P max values. K IC gradually increased from 3.0 ± 0.5 in the x = 0 sample at P max = 49 N to 4.2 ± 1 MPa √ m in the x = 6 sample at P max = 49 N; thereafter, it dropped down to 3.6 ± 0.8 MPa √ m at x = 10 at P max = 49 N. In addition, the estimated K IC gradually increased with the increase in applied indentation load P max . Such as in case of the x = 0 AMI, K IC increased from 3.0 ± 0.5 √ m at P max = 49 N up to 5.1 ± 0.5 MPa √ m at P max = 294 N. Therefore, the fracture resistance of the investigated composites increased with the increase in Nb content in the NECs up to x = 2. The evolution of intermetallic Zr 54 Fe 37 Nb 9 decreased the IFT values. By increasing the Nb up to x = 6 atom %, the fracture strength was enhanced due to the presence of nanolamellar α-Zr and FeZr 2 phases and solid-solution strengthening. However, the presence of homogeneous NECs (x = 0 and 2) with a higher volume fraction of FeZr 2 phase led to IFT values higher than the other Nb-containing specimens.

Indentation Fracture Toughness
The Vickers IFT measurements refer to a complex state of three-dimensional crack system with significant deformation residual stress and damage around the cracks. In this investigation, l/a data was considered to be in the range of 0.25-2.5. The values of calculated KIC of the investigated NECs are summarized in Table 3. The length of the cracks extending from the four corners (l) and the size of the indentation diagonal (d) was measured for the desired Palmqvist crack lengths and the size of indentation with an standard error in the range of 2-10%. The IFT measurements were performed at various Pmax values within a range between 49 and 294 N in order to study the effect of load variation and Nb content on the KIC in Zr-Fe-(Nb) NECs. Figure 6 shows the variation of the estimated KIC measured at different Pmax values. KIC gradually increased from 3.0 ± 0.5 in the x = 0 sample at Pmax = 49 N to 4.2 ± 1 MPa√m in the x = 6 sample at Pmax = 49 N; thereafter, it dropped down to 3.6 ± 0.8 MPa√m at x = 10 at Pmax = 49 N. In addition, the estimated KIC gradually increased with the increase in applied indentation load Pmax. Such as in case of the x = 0 AMI, KIC increased from 3.0 ± 0.5 √m at Pmax = 49 N up to 5.1 ± 0.5 MPa√m at Pmax = 294 N. Therefore, the fracture resistance of the investigated composites increased with the increase in Nb content in the NECs up to x = 2. The evolution of intermetallic Zr54Fe37Nb9 decreased the IFT values. By increasing the Nb up to x = 6 atom %, the fracture strength was enhanced due to the presence of nanolamellar α-Zr and FeZr2 phases and solid-solution strengthening. However, the presence of homogeneous NECs (x = 0 and 2) with a higher volume fraction of FeZr2 phase led to IFT values higher than the other Nb-containing specimens.

Fractrographic Investigation
To understand the IFT behavior of the NECs with the nanolamellar phases, the indented and fractured NECs were further investigated in detail. Figure 7 shows the SEM images of the lateral surfaces of the indented and fractured specimens. Palmqvist cracks were observed emerging from the edges of the indentation impressions. The geometry of Palmqvist cracks at the edges of the indentations at an operating load of 49 N is shown in Figure 7, which shows the SEM micrograph of

Fractrographic Investigation
To understand the IFT behavior of the NECs with the nanolamellar phases, the indented and fractured NECs were further investigated in detail. Figure 7 shows the SEM images of the lateral surfaces of the indented and fractured specimens. Palmqvist cracks were observed emerging from the edges of the indentation impressions. The geometry of Palmqvist cracks at the edges of the indentations at an operating load of 49 N is shown in Figure 7, which shows the SEM micrograph of the indented impression along with the Palmqvist cracks emerged from the edge of the indentation diagonals in the x = 0 and x = 6 NECs. It is interesting to note that the plastic flow lines in the α-Zr phase were observed near the vicinity of the indented plastic zone in the x = 6 samples, while the other phases do not show plastic flow lines. These results suggest that the mutual interaction between lamellar FeZr 2 //α-Zr phases is responsible for an enhanced fracture strength and fracture toughness. the indented impression along with the Palmqvist cracks emerged from the edge of the indentation diagonals in the x = 0 and x = 6 NECs. It is interesting to note that the plastic flow lines in the α-Zr phase were observed near the vicinity of the indented plastic zone in the x = 6 samples, while the other phases do not show plastic flow lines. These results suggest that the mutual interaction between lamellar FeZr2//α-Zr phases is responsible for an enhanced fracture strength and fracture toughness.

Summary
A series of eutectic nano-lamellar α-Zr//FeZr2 eutectic composites was developed in Zr-Fe-(Nb) at low cooling rates (10 K/s). Nb addition resulted in the formation of intermetallic Zr54Fe37Nb9 and destabilized the FeZr2 phase. Even though Nb addition coarsened the interlamellar spacing λ, a compressive fracture strength up to 1800 MPa was achieved. On the other hand, Nb addition increased the density, the Young's modulus, and the hardness of the composite. The fracture resistance of the NECs increased with the increase in Nb from 3.1 ± 0.5 (x = 0) up to 4.7 ± 1.0 MPa√m (x = 2) at Pmax = 49 N. These results suggest that the mutual interaction between nanolamellar FeZr2//α-Zr phases is responsible for an enhanced IFT and a high fracture strength, whereas a higher volume fraction of Zr54Fe37Nb9 intermetallic phase in x = 10 is responsible for reduced IFT values.

Summary
A series of eutectic nano-lamellar α-Zr//FeZr 2 eutectic composites was developed in Zr-Fe-(Nb) at low cooling rates (10 K/s). Nb addition resulted in the formation of intermetallic Zr 54 Fe 37 Nb 9 and destabilized the FeZr 2 phase. Even though Nb addition coarsened the interlamellar spacing λ, a compressive fracture strength up to 1800 MPa was achieved. On the other hand, Nb addition increased the density, the Young's modulus, and the hardness of the composite. The fracture resistance of the NECs increased with the increase in Nb from 3.1 ± 0.5 (x = 0) up to 4.7 ± 1.0 MPa √ m (x = 2) at P max = 49 N. These results suggest that the mutual interaction between nanolamellar FeZr 2 //α-Zr phases is responsible for an enhanced IFT and a high fracture strength, whereas a higher volume fraction of Zr 54 Fe 37 Nb 9 intermetallic phase in x = 10 is responsible for reduced IFT values.