A Critical Review on Recycling Composite Waste Using Pyrolysis for Sustainable Development

: The rising usage of carbon and glass ﬁbers has raised awareness of scrap management options. Every year, tons of composite scrap containing precious carbon and glass ﬁbers accumulate from numerous sectors. It is necessary to recycle them efﬁciently, without harming the environment. Pyrolysis seems to be a realistic and promising approach, not only for efﬁcient recovery, but also for high-quality ﬁber production. In this paper, the essential characteristics of the pyrolysis process, their inﬂuence on ﬁber characteristics, and the use of recovered ﬁbers in the creation of a new composite are highlighted. Pyrolysis, like any other recycling process, has several drawbacks, the most problematic of which is the probability of char development on the resultant ﬁber surface. Due to the char, the mechanical characteristics of the recovered ﬁbers may decrease substantially. Chemically treating and post-heating the ﬁbers both help to reduce char formation, but only to a limited degree. Thus, it was important to identify the material cost reductions that may be achieved using recovered carbon ﬁbers as structural reinforcement, as well as the manufacture of high-value products using recycled carbon ﬁbers on a large scale. Recycled ﬁbers are cheaper than virgin ﬁbers, but they inherently vary from them as well. This has hampered the entry of recycled ﬁber into the virgin ﬁber industry. Based on cost and performance, the task of the current study was to modify the material in such a way that virgin ﬁber was replaced with recycled ﬁber. In order to successfully modify the recycling process, a regulated optimum temperature and residence duration in post-pyrolysis were advantageous.


Introduction
Composite materials are composed of two or more different materials having considerably different physical and/or chemical characteristics that, when merged, produce a material with attributes that differ from the separate elements. Composite materials are extensively utilized in the automobile, construction, transportation, aerospace, and renewable energy applications due to their durability, high strength, great quality, minimal maintenance, and low weight [1][2][3].
In recent years, a few significant occurrences occurred that significantly increased the sociotechnical push for long-term composite recycling, particularly: 1.
The increased utilization of composites in mass-production automobiles resulting from the development of high-volume thermoplastic composite-based technologies [3].
1. The increased utilization of composites in mass-production automobiles resulting from the development of high-volume thermoplastic composite-based technologies [3]. 2. The first significant group of wind turbines made of composite materials approaching their End-of-Life (EOL) in 2019-2020 and preparing to be dismantled [1]. 3. A global prohibition on composite landfilling in several countries [1,4]. 4. The COVID-19 epidemic hastening the retirement of airplanes (airplane mass decommissioning is predicted in the 2020s) [5].
According to Stella Job, the absence of recycling facilities is an obstacle to the expanded usage of glass fiber reinforced composite (GFRC) and carbon fiber-reinforced composite (CFRC) composites [6]. Therefore, the growing usage of these significant materials-along with landfilling limits and prohibitions-necessitated the development of viable composite recycling methods [7]. As the EU moves closer to eliminating landfill alternatives, it is reasonable to predict that such sociotechnical stress will surely increase in the near future [4], It is also worth noting the ever-increasing number of wind turbines that have reached the end of their useful life and are ready to be burned or recycled, as well as the expansion of composite markets and increased composite manufacturing and installation rates (As presented in Figure 1). Additionally, decommissioning will continue to increase the number of installed wind turbines, year after year, as it has in the past [4]. As a result, the motivation to create the most sustainable composite recycling technologies is undoubtedly critical to the composite industry's preservation and success. It has been predicted that this trend will become increasingly significant in the 2020s. The use of composites is most prevalent in the wind energy, marine, aerospace, and automotive industries. In these cases, recent advancements have led to a greater emphasis on material EOL management [9]. The use of composites is most prevalent in the wind energy, marine, aerospace, and automotive industries. In these cases, recent advancements have led to a greater emphasis on material EOL management [9]. Over the next ten years, the International Air Transport Association (IATA) estimates that 11,000 aircraft will be retired [5]. The COVID-19 pandemic has severely curtailed aviation travel, and this is likely to hasten the decommissioning of these planes, emphasizing the importance of recycling. Moreover, composite utilization in airplanes has increased dramatically, as is clear in the commercial aircraft produced by Airbus and Boeing. Take, for example, the usage of composites in the Airbus commercial aircraft A300 (4.5 wt%,   and B787 (50 wt%, 2007-present) [10]. By weight, the B787 body is 50% composites, 10% steel, 15% titanium, 20% aluminum (Al), and 5% other. Meanwhile, the composite material in B787 consists mainly of carbon sandwich structures, CFRP laminates, and fiberglass [1]. In the aircraft sector, Al has long been one of the most utilized materials. However, its utilization rate has dropped from 50% in the Boeing B777 to barely 20% in the Boeing B787 [11]. Comparisons of tensile modulus and strength characteristics of E-glass fibers (72 GPa, 3.5 GPa) against Al (68.9 GPa, 0.31 GPa) offer another explanation for the tendency toward composites [11].

Automotive
Because their light weight allows for the maximum possible performance, composites have been utilized in sports vehicles. Electric propulsion and self-guiding technologies have been made possible by recent advancements in mobility. These vehicles require lightweight materials to achieve higher ranges between recharging (i.e., electric automobiles), which has driven the need for high-volume composite manufacturing and EoL disposal. Another driving force behind the push for recycling is the fact that the automobile and aerospace industries, which produce large quantities of carbon fiber parts, also waste large percentages of the raw materials used (sometimes as much as 20-40%). One of the goals of the automobile industry is to have vehicles that are both fuel-efficient and lightweight. The use of CFRC in automotive components decreases the weight of a typical vehicle by 30% [2]. The importance of environmental stewardship cannot be overstated. EU law in the automobile sector mandates that 85% of a car can be recycled. CF scrap may be collected and transformed into new components with less than 10% of the energies used to manufacture virgin carbon fiber (CF), meeting legal and environmental goals [2]. CFRC help to reduce greenhouse gas emissions by reducing fuel usage, since they are utilized to make lighter automobile and airplane bodies [2]. Cost reduction is a significant motivator in the composites field [12].

Marine
Composites have proven to be a game-changer in the offshore business. At present, glass fiber (GF) and carbon fiber (CF) composite materials play a huge role in marine energy development, shipbuilding, and marine engineering repair. Composite materials have slowly and steadily replaced upper metal (above water level) in more and more marine installations, whether new installations or in renovations of existing structures. Carbon fiber has several advantages in marine engineering construction [13][14][15][16][17], including lighter weight, high strength, and wear resistance. Most installations use structural parts to replace traditional building materials, reducing the high freight weight, seawater corrosion, and the problems arising from rebar materials [18,19]. The following are the primary advantages of GRP for maritime applications: environmental resistance, durability, costeffectiveness, the ability to mold complex, seamless objects, the ability to adjust strength to load circumstances, excellent strength-to-weight ratio, light weight (about half that of similar steel constructions), low maintenance/repairability, and excellent long-term durability [18,19].

Wind Energy
Composites are used in wind turbines because of their high specific strength. According to the GWEC, the total number of utility-scale wind turbines installed throughout the world has surpassed 330,000, most of which are projected to last 20-25 years. The first significant group of wind turbines made of composite materials will approach their EOL in the 2020s [20]. As a result of the approaching challenge of recycling wind turbine blades, roughly two gigawatts are expected to be replaced in 2019 and 2020 [21]. Denmark, for example, was a significant participant in the initial implementation of wind turbines, and has now become one of the first countries to tackle the mass disposal problem [20]. Some EU nations have prohibited the disposal of composite blades in landfills for environmental  [4], necessitating the development of novel EOL solutions for composites in this industry. The used scrap blade materials are anticipated to double in the next decade, from 1,000,000 t in 2020 to 2,000,000 t in 2030 [22]. An estimated 25% of all EOL trash will be generated in the EU, according to estimates [12].
The majority of turbine rotors feature three blades, with sizes ranging from 12 m to 80 m or more. Several of these blades are expected to be phased out shortly [20]. Siemens Gamesa Renewable Energy (SGRE) has a capacity of 14 MW wind turbines with Integral Blades that are 108 m long. The radius of the rotor is 111 m. As we enter the 2020s, recycling will become increasingly important. Nowadays, about 90% of the entire mass of wind turbines is recyclable, and the wind energy sector uses about 2.5 million tons of composite material worldwide [4]. Furthermore, by 2023, about 14,000 blades (weighing 40,000-60,000 tons) will be decommissioned. The wind industry prioritizes the recycling of these obsolete blades [4]. For disassembly, collecting, transportation, waste disposal, and restructuring of composite materials into production chains, this challenge requires both logistical and technical solutions [4].

Construction and Infrastructure
Perhaps the most intriguing application of sophisticated composite materials so far is a functional bridge on the state highway system. Hollow carbon composite tubes and lightweight concrete were employed in its construction. ACMs are excellent for seismic retrofitting because of their flexibility and ease of application. They are now a valuable resource for retrofitting and improving processes in forensic engineering. Glass and carbon fibers are most commonly used in epoxy resin matrixes [23].
Additionally, after wind turbines, WPCBs are one of the fastest-growing worldwide waste sources, accounting for a major portion of overall electronic waste and containing 27.4-45.55 wt% GF. Owing to the existence of hazardous metals and organic substances, as well as GFs, the recovery of WPCBs to retrieve GFs is a difficult procedure [7,22].
Composite material recycling will become more important in the 2020s and beyond as efforts are made to cut down on pollution and fulfill demand. Figure 2 shows the global composite materials' market size distribution by application in 2020. Among composite materials, fiber-reinforced composites (FRC) are the most widely utilized [24][25][26][27][28]. The remarkable material characteristics of CFRC and GFRC make them particularly useful in this regard [29][30][31][32]. FRC materials are attractive as a replacement for steel and other materials due to their low weight, high strength, durability, and form flexibility. CF and GF, with polyester matrix resin as components, were used to create modern  Among composite materials, fiber-reinforced composites (FRC) are the most widely utilized [24][25][26][27][28]. The remarkable material characteristics of CFRC and GFRC make them particularly useful in this regard [29][30][31][32]. FRC materials are attractive as a replacement for steel and other materials due to their low weight, high strength, durability, and form flexibility. CF and GF, with polyester matrix resin as components, were used to create modern FRC materials in the early 1950s. They're commonly utilized in the construction of boats, automobiles, and storage tanks [30]. The international market for composite materials is growing and is estimated to exceed $96 billion in 2020, up 40% from 2014. Carbon and glass fibers are the most common materials; CFRC and GFRC products account for $57 billion and $30 billion, respectively, of the $96 billion [2].
The FRC industry's expansion has boosted both productivity and consumption. However, it has also resulted in a large number of EOL materials. The struggle to preserve and recycle EOL scrap FRC has become a major barrier to the sustainability of a circular economy. In the past, the industry rushed to use these materials without understanding how to properly dispose of them. For decades, the two most common disposal techniques used by the composite industry were landfill and incineration. The drawbacks of these techniques have led to increased environmental awareness, resulting in the search for sustainable disposal methods and strategies to avoid trash accumulation [33][34][35][36][37][38][39].
Over the past few years, several studies have analyzed market demand for various composites, as well as the associated quantity of accumulating waste, in order to minimize the unavoidable negative effects. The market for fiber-reinforced polymer composites (FRPC) in the United States was about $12 billion in 2020, with a yearly growth rate of 6.6% [40,41]. To meet such a high need for virgin carbon fiber (vCF) and virgin glass fiber (vGF), the accumulating CFRC and GFRC waste must be recycled effectively, to minimize environmental consequences while also meeting the demand [42]. However, converting CFRP and GFRP into useful resources is a difficult problem that threatens the future of the fiber-based industry [43][44][45][46].
As a result, the treatment and recycling of FRC materials such as CFRC/GFRC within environmental constraints, government regulations, manufacturing costs, resource management, and economic opportunity are all critical worldwide problems. The present research demonstrated the influence of the pyrolysis technique as a rising and feasible technology for FRC recycling. This research will help to systematize technological knowledge of CFRC/GFRC recycling processes such as pyrolysis.
Several researchers have dealt with the topic of recycling FRC materials. Krauklis et al. tried to create clear standards for economically and ecologically viable EOL solutions and fiber-reinforced composite material recycling [1]. Oliveux et al. examined the life cycle assessment of composite materials, as well as the economic and environmental implications of recycling them [25]. Naqvi et al. presented the strong link between recycling and reusability of fibers, which helped to illustrate the idea of the circular economy and cradle-to-cradle strategies [40]. Gharde et al. listed mechanical, thermal, and chemical recycling methods, as well as their efficacy in degrading large amounts of FRP materials [3]. Moreover, Liu et al. devised a technique for deconstructing, recycling, and remanufacturing composite materials that are both sustainable and cost-effective [7]. Pickering et al. examined thermoset composite recycling systems and detailed some of the major work in the fields of mechanical and thermal recycling [46]. According to Job et al., GF/CF plastics (GRP and CFRP) offer outstanding characteristics, but they also found that a lack of recycling programs was a barrier to their wider usage [6].
The conventional narrative review structure was used in this study. The Scopus database was primarily used for a complex literature search, with three other databases (Web of Science, Science Direct, and Research Gate) serving as supplementary support platforms. The search was restricted to the previous 20 years, with a focus on recent papers (the last ten years). Keywords used in searches included "carbon fiber", "glass fiber", "pyrolysis", "CFRC", "CFRP", "FRC", "GFRC", "GFRP", "composite recycling", "waste composite", and "thermal recycling". Finally, suitable papers were carefully chosen Furthermore, utilizing Microsoft Excel, all of the related papers on the recycling of CFRC waste (410 papers) and GFRC waste (120 papers) were evaluated and organized into a private database. The selection was further refined based on the following criteria: a focus on thermal recycling technologies, particularly Pyrolysis techniques; and the impact on the environment, economic valuation, recycled fiber quality, and industrial reusability. Publications that did not meet the outlined selection criteria were removed. Consequently, the scope of this literature analysis was restricted to include just the most important pyrolysis-based approaches for recycling CFRC and GFRC waste. The necessity to replace virgin fibers with recycled fibers was also supported by emphasizing the associated process parameters and the characteristics of the resulting fibers. The final reference list included 114 publications.
This review provided a summary article detailing known ways for recycling accumulating composite scraps, comprising carbon and glass fiber. The focus was on the use of thermal recycling technologies, particularly Pyrolysis techniques, for recovering fibers and determining their preserved characteristics. Pyrolysis approaches were prioritized in the study on the basis of the following criteria: the impact on the environment, economic valuation, recycled fiber quality, and industrial reusability. The research also emphasized the accompanying process parameters and the properties of the resultant fibers in order to support the need to replace virgin fibers with recycled fibers. Additionally, the current study revealed gaps and recommened possible solutions.
This work is well-structured and separated into sections as follows. An overview of the various recycling options can be found in Section 2. Section 3 shows how to recover CFRC/GFRC using the pyrolysis technique. Pyrolysis products and their reuse are described in Section 4. The research gaps are then explored in Section 5, reviewing the current study effort on recycling CFRC/GFRC, utilizing the promised approach of pyrolysis. Finally, in Section 6, the article ends with the authors' conclusions.

Review of Recycling Technologies
Several publications have documented several techniques of CFRC/GFRC for prospective industries over the last 10 years. The most common ways of recycling composite material are mechanical, thermal, and chemical recycling [25]. Thermal recycling methods were detailed in depth in this study along with the economic potential and environmental effects of the techniques.
Heat is utilized to break down scrap composite during thermal recycling. The minor volatile elements are likely burned away due to the increased working temperature (450-700 • C), leaving only the valued fibers. The temperature is usually determined by the kind of resin used in the waste composite. An inappropriate temperature might result in char on the fiber (undercooking) or a decrease in the thickness of the fibers (overcooking) [25,45]. As illustrated in Figure 3, thermal recycling may be divided into three categories [46].
The underlying idea for utilizing heat to decompose scrap composite remains the same; however, the outcomes vary depending on the method. Due to the calorific values of polymeric compounds, electricity may be produced by turning scrap composites into heat [24,25]. On the other hand, the ash byproduct of the combustion (incineration) process is a significant disadvantage, since it can only be landfilled as inert waste, at a cost that varies from country to country. In France, for example, its cost is about 92 €/ton. This complexity stymies the circular economy's growth. Furthermore, while converting heat to electricity, no more than a 35% efficiency rate is attainable. Generally, burning coal rather than incinerating CFRP is a far superior alternative. Complete fiber recovery utilizing thermal techniques-such as the fluidized-bed process (FBP) or pyrolysis-have been the subject of recent research [47]. Heat is utilized to break down scrap composite during thermal recycling. The minor volatile elements are likely burned away due to the increased working temperature (450-700 °C), leaving only the valued fibers. The temperature is usually determined by the kind of resin used in the waste composite. An inappropriate temperature might result in char on the fiber (undercooking) or a decrease in the thickness of the fibers (overcooking) [25,45]. As illustrated in Figure 3, thermal recycling may be divided into three categories [46]. The underlying idea for utilizing heat to decompose scrap composite remains the same; however, the outcomes vary depending on the method. Due to the calorific values of polymeric compounds, electricity may be produced by turning scrap composites into heat [24,25]. On the other hand, the ash byproduct of the combustion (incineration) process is a significant disadvantage, since it can only be landfilled as inert waste, at a cost that varies from country to country. In France, for example, its cost is about 92 €/ton. This complexity stymies the circular economy's growth. Furthermore, while converting heat to electricity, no more than a 35% efficiency rate is attainable. Generally, burning coal rather than incinerating CFRP is a far superior alternative. Complete fiber recovery utilizing thermal techniques-such as the fluidized-bed process (FBP) or pyrolysis-have been the subject of recent research [47].
Rather than complete incineration of CFRC, management of resin breakdown, at the right temperature, would yield CF with minimal surface harm. Rodrigues et al. thermally decomposed resins for two hours at a temperature of 450 °C and recovered the CF without significantly compromising their surface properties [45]. Because of its cross-linked construction, degraded epoxy resin is difficult to recycle. As a result, recycling with minimal surface damage is a preferable alternative to fully landfilling. Although resin decomposition utilizing thermal techniques is not as suitable for GF as it is for CF, chemical treatment of rGF aids in the recovery of characteristics, to an extent [48]. When GF is thermally recycled at high temperatures (300-600 °C), it loses up to 80% of its strength, making it hard to recover because of its poor reinforcing potential [49,50]. Yang et al. explored chemical etching and post-sanitation to treat degraded GF. In rGF, the chemical treatment restored 30-70% of the loss of the mechanical characteristic [49]. By soaking the GF in a NaOH for 10 min at 90 °C, and then neutralizing it with HLC, Thomason et al. were able to restore 75% of the strength loss. The procedure used in their study is called short-hot sodium hydroxide solution therapy [48]. Pender and Yang [51] used catalysts such as CuO and Rather than complete incineration of CFRC, management of resin breakdown, at the right temperature, would yield CF with minimal surface harm. Rodrigues et al. thermally decomposed resins for two hours at a temperature of 450 • C and recovered the CF without significantly compromising their surface properties [45]. Because of its cross-linked construction, degraded epoxy resin is difficult to recycle. As a result, recycling with minimal surface damage is a preferable alternative to fully landfilling. Although resin decomposition utilizing thermal techniques is not as suitable for GF as it is for CF, chemical treatment of rGF aids in the recovery of characteristics, to an extent [48]. When GF is thermally recycled at high temperatures (300-600 • C), it loses up to 80% of its strength, making it hard to recover because of its poor reinforcing potential [49,50]. Yang et al. explored chemical etching and post-sanitation to treat degraded GF. In rGF, the chemical treatment restored 30-70% of the loss of the mechanical characteristic [49]. By soaking the GF in a NaOH for 10 min at 90 • C, and then neutralizing it with HLC, Thomason et al. were able to restore 75% of the strength loss. The procedure used in their study is called short-hot sodium hydroxide solution therapy [48]. Pender and Yang [51] used catalysts such as CuO and CeO 2 to speed up the breakdown of resin. Consequently, the process duration was cut by 20 min, and energy usage was lowered by 40%. The most efficient method used CuO at 375 • C to remove resins, whereas CuO and CeO 2 improved the strength retention of GF by 20%.
Fast, hot air was conducted across the conventional fluidized bed process (FBP). Typically, a bed of 0.85-mm-sized silica sand is utilized, which is subsequently transformed into a fluidized bed by flowing air at 0.4-1.0 m/s. The waste composite divides into fibers and fillers (volatile chemicals) inside a fluidized bed, which are transported out as individual particles by the air stream [46,52]. Furthermore, using a high-temperature (1000 • C) secondary chamber causes the volatile chemicals to be oxidized, leaving the fibers alone [46,52]. The method can recover both CF and GF, and it's very good for recycling EOL waste composites [25]. However, constraints, such as fiber strength and length deterioration, were apparent throughout the process's early development. In addition, the fibers obtained using this method are puffy [29].
Pickering et al. [52] demonstrated the limits when they studied the capacity of FBP to recover GF and obtained 67% fiber output. Moreover, the procedure only kept 50% of the rGF's tensile strength, compared to vGF. The research also added a financial estimation for commercializing the method, which predicted a net yearly profit of 0.002 million dollars for 9000 t per year. In contrary to Pickering et al. [52], Zheng et al. [53] reported having developed a unique FBP method for recycling WPCBs, claiming to have achieved a 94.8 wt% and 95.4 wt% GF recovery and purity rate, respectively. Other than the fact that, in their method, the WPCB were coarsely chopped, rather than standard cutting size (25 mm), the recycling technique appeared to be almost the same. However, SEM image observations were used to confirm the findings. Furthermore, no information about the rGFs' strength was provided. Pender and Yang [54] utilized CuO to increase the production of rGF, with the yield increasing from 59 to 70%. Yip et al. [55] conducted research identical to Pickering et al. [52], using CF instead of GF. When compared to GF recycling, the data revealed that recycling CF under the same circumstances was significantly more effective. The length of the rCF was determined by the initial length of the CF waste, according to the research and, given the non-uniform orientation, a fiber length of 5.9-9.5 mm could be recovered. Pickering et al. [56] built a commercial-scale FBP, in line with prior research. The rCF only lost 18.2% of its tensile strength and had no tensile modulus loss. According to the research, when compared to any other rCF utilizing FBP, this design showed the greatest efficiency. Furthermore, the energy required to obtain CF from FBP was approximately 5-10% of the energy required to produce vCF.
Other researchers [25,29,46] thoroughly described and analyzed the technical comparability and reuse applications of three recycling techniques. Their findings indicated that the thermochemical technique was suitable for CFRC recycling, due to the rising cost of CF for high-grade applications like aerospace and structure industries. The mechanical method was suggested as a preferable method for GFRC due to the low cost of vGF [25,57]. Wong et al. [58] compared the power consumption of the chemical, thermochemical (incineration and pyrolysis), and mechanical techniques. The power consumed during pyrolysis (30 MJ/kg) was reasonable, as shown by this study, when compared to other frequently used industrial applications. Mechanical separation, incineration, gasification, and slower pyrolysis (i.e., in a kiln), on the other hand, were either costly or yielded low characteristic fibers. Pyrolysis seemed, thus, to be a realistic and promising approach for efficient recovery and high characteristic fiber production. The essential pyrolysis technique variables, their influence on fiber characteristics, and the utilization of recovered fiber were highlighted in this paper. The present study identified gaps, and a proposal was presented.
The University of Nottingham in the United Kingdom devised a low-temperature (450 • C) incineration method in an FBP for the recycling of FRC [46,52,53]. This method recovered fibers while also generating gas for energy recovery. Mixed and polluted materials can be treated in fluidized-bed reactors. This technique, conversely, necessitated large quantities of high-temperature air and resulted in a decrease in fiber characteristics (particularly for GF) due to mechanical activity in the bubbling sand bed. The value of recovered fibers is an essential consideration in this procedure. Fiber has a high intrinsic value owing to its large price as a virgin substance, but the high labor costs involved and the large quantity of energy required undermine the economic case for recycling operations utilizing a low-temperature incineration FBP. In aeronautical applications, a combination thermolysis and gasification method for recovering scrap CFRC was employed [59]. However, the gasification period was too lengthy, resulting in unfavorable changes in the atomic composition of the CF. The most researched thermal technique for recovering CF/GF composite waste is pyrolysis in an inert environment [60][61][62]. To guarantee effective and maximal recovery of fiber and fuels, as well as chemical synthesis, pyrolysis processes (slow or rapid) need optimum conditions [63][64][65][66]. According to the authors' knowledge, no detailed study of carbon/glass fiber recovery utilizing the pyrolysis technique has yet been published. The current research not only covered the essential elements of the pyrolysis technique but also emphasized the influence of technique variables on fiber recovery and fuel generation.

Recovery of CFRC/GFRC Utilizing Pyrolysis
Both CF and GF may be recycled efficaciously using this method [40]. The scrap composites are heated in the absence of air, unlike previous thermal recycling methods. The disintegrating matrix generates oil and gas, as well as fibers and fillers (solid products) [25,46]. The working temperature for a typical FRC varies between 400 and 700 • C, depending on the composition of the waste composite [24,29]. The oil that results is aromatic and has a heating value of 37 MJ/kg, which is comparable to fuels. The pyrolysis reactor may be renewed with the gas produced. The liquid and gas generated can be used as a chemical feedstock in a variety of processes. Despite all of this, the technique can preserve fibers with superior mechanical characteristics [24,29]. Pyrolysis is the best researched thermal recycling method [25], and a flowchart of the process is shown in Figure 4.

Recovery of CFRC/GFRC Utilizing Pyrolysis
Both CF and GF may be recycled efficaciously using this method [40]. The scrap composites are heated in the absence of air, unlike previous thermal recycling methods. The disintegrating matrix generates oil and gas, as well as fibers and fillers (solid products) [25,46]. The working temperature for a typical FRC varies between 400 and 700 °C, depending on the composition of the waste composite [24,29]. The oil that results is aromatic and has a heating value of 37 MJ/kg, which is comparable to fuels. The pyrolysis reactor may be renewed with the gas produced. The liquid and gas generated can be used as a chemical feedstock in a variety of processes. Despite all of this, the technique can preserve fibers with superior mechanical characteristics [24,29]. Pyrolysis is the best researched thermal recycling method [25], and a flowchart of the process is shown in Figure 4. Pyrolysis, like any other recycling process, has several drawbacks, the most problematic of which is the probability of char development on the resultant fiber surface [29]. Due to the char, the mechanical characteristics of the recovered fibers can be substantially decreased. Chemical treatment [27,28] and post-heating treatment of the fibers both help to reduce char formation, but only to a limited extent [67,68]. Carbon dioxide (CO2) and water vapors have been utilized to eliminate char formation from CFRC in recent research [69]. Additionally, oxidizing the fiber surface results in the development of a surface with high levels of oxygen, which improves the fiber's adhesiveness with resins [70]. Pyrolysis, like any other recycling process, has several drawbacks, the most problematic of which is the probability of char development on the resultant fiber surface [29]. Due to the char, the mechanical characteristics of the recovered fibers can be substantially decreased. Chemical treatment [27,28] and post-heating treatment of the fibers both help to reduce char formation, but only to a limited extent [67,68]. Carbon dioxide (CO 2 ) and water vapors have been utilized to eliminate char formation from CFRC in recent research [69]. Additionally, oxidizing the fiber surface results in the development of a surface with high levels of oxygen, which improves the fiber's adhesiveness with resins [70].
The UK milled carbon group was successful in building and executing a commercialscale furnace with a controlled environment that can totally eliminate char development on the rCF [29,62]. Additionally, a German company (CFK) currently employs a continuous pyrolysis reactor. Both businesses recycle CFRC trash in different forms. They may also recover longer and cleaner CFs, thanks to the large furnaces and continuous flow [29]. Meyer et al. [60] demonstrated this phenomenon in previous research by recycling aircraft CFRC scrap, in which lab-scale pyrolysis was scaled up to industrial pyrolysis. Using a larger oven, the scientists were able to recreate industrial plant operations with rCF, preserving 96% of its initial tensile strength. Although the rCF was sufficient to replace vCF, a supplementary combustion chamber was developed to remove the leftover char. Overall, the process results could be influenced by a regulated environment in the pyrolysis reactor.

Pyrolysis: Controlled Atmospheres
To extract fibers from solid pyrolysis products, sophisticated, regulated air conditions were introduced with the development of pyrolysis technologies. Evidence of such approaches were shown in several works in the literature released since 2010. Pyrolysis' basic principle remained unchanged. Air conditions inside pyrolysis reactors, on the other hand, have been continually changing to achieve greater yields. In pyrolysis, typical atmospheric conditions include nitrogen, vacuum, and superheated steam.

Vacuum Atmosphere
Organic vapors' residential period within a vacuum pyrolysis reactor is reduced because of the low degradation temperature that is adequate to recover GF without disrupting surface quality [71,72]. VP was evaluated as a replacement for the mechanical technique by Zhou and Qiu, and used to recycle WPCBs [71]. vacuum pyrolysis (VP) was judged as an alternative approach to mechanical recycling. The liquid and gas products (can be used as chemical feedstock) along with solid products (GF and metal components) were found to increase the interests of researchers when compared to mechanical recycling [71][72][73]. The researchers used a two-step pyrolysis technique to extract GF from WPCBs, using VP and VCS. Long et al. [73] utilized VP to separate the GF from metal portions, utilizing GS and nonmetal portions and a calcination procedure. There was no examination of the mechanical characteristics of rGF in that research, which focused on recycling WPCBs in a vacuum environment. Table 1 lists the process' yields. Due to the lack of relevant research on CF, this procedure was confined to GF alone.

Nitrogen Atmosphere
Pyrolysis in a nitrogen environment-unlike vacuum pyrolysis-may recycle both CFRC and GFRC [62]. Until Zhou et al. [72] published their work in 2010, the most common pyrolysis technique used to recycle WPCBs was pyrolysis under nitrogen atmosphere (NA). WPCBs were recycled via vacuum pyrolysis, resulting in a maximal rGF. After studying the benefits of NA, Onwudili et al. [74] improved the method and succeeded in recycling CFRC scrap, recovering 98% of rCF. According to the study, a rise in reaction time may have resulted in a reduction in the mechanical characteristics of rCF. The inadequate reaction time may also have resulted in the formation of char on the fibers. Table 1 shows the yield from the procedure.
In 2016, Onwudili et al. [62] used NA with a semi-batch reactor to investigate the mechanical characteristics of both recycled CFRC and GFRC waste. Chemical alterations of the surface of rCF and rGF fibers may have improved fiber characteristics, according to the study. Secondary combustion (SC) was also utilized in both experiments [62,74] to oxidize the char on the pyrolyzed fibers. When analyzing the findings, it was discovered that oxidized fibers preserved the highest mechanical characteristics, compared to nonoxidized fibers.

Superheated Steam Atmosphere
In most cases, the steam is created by heating saturated steam at a steady pressure. To attain superheated levels, the steam is heated many times over its saturation point during the transition period. In pyrolysis, using a superheated steam atmosphere improves heat transmission, which accelerates the thermal breakdown and supports the removal of oxygen from the pyrolysis reactor [75]. In comparison to other pyrolysis atmospheres, recycling CFRC with superheated steam leads to high retention of CF mechanical characteristics [76][77][78][79]. Chemical treatments can also decrease a considerable percentage of char development on the resultant rCF and rGF [68].
Shi et al. [76] discovered that the rCF had a major quantity of char on its surface, which rendered the fibers unusable. According to the study, the higher the quality of rCF, the lower the pyrolysis temperature. Shi et al. [68] expanded their earlier study to CFRC and GFRC, eradicating char on rCF and rGF utilizing chemical treatment. Using NMP, the bending strength rose from 49-78% for rCF and 26-94% for rGF. Using fast pyrolysis, Jeong et al. reported that 66% of the strength and 100% of the tensile modulus were retained after recycling CF [78].
Ye et al. [79] combined VP and mild gasification for recycling CFRC scrap to maintain maximal tensile strength (TS) for rCF. In both laboratory and semi-industrial sizes, the method preserved 90% of its TS. According to the study, an increase in degradation in the polymer matrix resulted in a drop in the TS of the fibers. Kim et al. [77] used an FBP at 550 • C for 60 min and preserved 90.42% of the TS. According to the study, increasing the steam temperature improved the elimination of char. Kim et al. [80] utilized superheated steam to eliminate minor resins with CO 2 , maintaining more than 80% of TS.

Microwave Pyrolysis
Microwave radiation is used to replace the traditional heating source in microwaveassisted pyrolysis. This modification enhances the heat transfer while consuming a minimum quantity of energy, without conflicting with the basics of pyrolysis. The method may recycle both CFRC and GFRC fibers while preserving greater mechanical character- istics [66]. Obunai et al. [81] removed all the resin after 300 sec utilizing a 700 W with 2.5 L/min argon environment. Tensile strength in the rCF was just 0.7% lower than in the vCF. Similarly, Jiang et al. [82] recycled CFRC for 30 min at 500 • C using a 0.70 m 3 /min N 2 . The rCF had a clean fiber surface and mechanical characteristics similar to vCF.

Pyrolysis on Wind Turbine
Pyrolysis was commonly favored in studies concentrating on GF recovery from wind turbines [83][84][85][86]. Aside from basic GF recycling, research has concentrated on maintaining mechanical characteristics to utilize them in a variety of different applications [26].
Several researchers were successful in preserving 75% of rGF TS by employing the microwave method in NA [85][86][87][88]. Their research claimed that a reduction in TS could be compensated by recycling it as a hybrid composite, mixing rGF and vGF.
Other researchers emphasized limitations, stating that rGF from wind blades was discontinuous, thin, and randomly directed. Furthermore, the TS of rGF was lower than that of vGF [83,84]. Furthermore, other studies concluded that the wind blades would be useful for both energy and material recovery [26]. Current studies also emphasized that chemical recycling could be more efficient for the recovery of GF and CF from wind blades [34].

Pyrolysis Products and Their Reuse
As previously stated, the compromised fiber surface with char poses a challenge for reuse. To separate the fiber, low-temperature combustion and gasification procedures employ a considerable volume of hot air to eliminate the char. A post-pyrolysis treatment is required to purify the surface of the recovered fiber before it can be recombined to create a new composite. The treatment is accomplished by oxidization, carried out at a regulated temperature and residence duration. The optimum temperature and residence time are significant issues.
XPS is utilized to assess the surface properties of recovered fibers [88]. Surface characteristics may have an effect on interfacial bonding performance. Both the oxidizing (air) and thermal (N 2 ) atmospheres are important in determining surface properties. Surface defects have been discovered in oxidizing atmospheres, resulting in a decrease in TS and crystallite size. As a result, in order to allow a successful recycling process, a regulated and optimum temperature and residence duration in post-pyrolysis is advantageous [89].
Recycling CFRC/GFRC by pyrolysis has great potential, since it recovers the precious fibers and produces both gas and liquid products. A gas analyzer can be utilized to evaluate the gas mixture produced by the pyrolysis process. Because of the significant secondary cracking, the produced gas may be composed of, according to the literature, H 2 , CH 4 , CO, and CO 2 . The quantity of these gases is mostly determined by the pyrolysis mode (slow or rapid), temperature, and residence duration. Additionally, researchers discovered that the breakdown of oxygen-rich components contained in the resin formulation produce carbon oxides in greater concentrations at higher temperatures. The produced liquid is mostly aromatic. The major components of the organic fraction were detected by GC-MS as ethylbenzene, benzene, styrene, toluene, and p-xylene. Aside from aromatics, pyrolysis oil contains oxygenated species [88][89][90][91][92]. The major gaseous and oil components are summarized in Figure 5. TGA was frequently utilized to evaluate breakdown behavior [90]. TG and DTG graphs demonstrated the mass loss of the resin with increasing temperatures. According to published research, the breakdown temperature of the resin was complete between 450-500 °C in the case of GRFC [91,92], while CFRC breakdown temperatures were between 450-600 °C depending on kind and whether the materials were cured or uncured [77,93]. For post-pyrolysis in air atmosphere, 500-600 °C was found to be the optimal temperature for oxidizing char and cleaning the fiber surface. [59,77]. In comparison to virgin material, attenuated total reflection, combined with FTIR, proved to be a reliable technique for identifying functional groups existing on recovered fibers [94]. To maximize the effect of the recycling process, mechanical characteristics were measured [95][96][97]. SEM, Raman, and XPS studies were used to examine the morphology of the retrieved fibers. Image analyses for fiber length [10] and micro-bond testing for interfacial adhesion among various pyrolysis parameters for recovered fibers and polymers [73] were used for additional studies. Table 2 summarizes the characterization methodologies used to investigate thermal, mechanical, and morphological evaluations of fibers. Table 2. Characterization methods used in CFRC/GFRC recycling processes [40]. Recycling choices have a major influence on the assessment of mechanical characteristics of recovered fibers (CF/GF). Poor adherence (to recycled fibers and epoxy resins) has an impact on mechanical characteristics. Pyrolysis is the only technique that generates higher mechanical characteristics for recycled fibers and permits commercial-scale use, according to several studies [24,25,29]. To solve mechanical property concerns, pyrolysis should be controlled using a regulated temperature with quick heating rates, adequate residence duration, and appropriate raw material length (Table 3). TGA was frequently utilized to evaluate breakdown behavior [90]. TG and DTG graphs demonstrated the mass loss of the resin with increasing temperatures. According to published research, the breakdown temperature of the resin was complete between 450-500 • C in the case of GRFC [91,92], while CFRC breakdown temperatures were between 450-600 • C depending on kind and whether the materials were cured or uncured [77,93]. For post-pyrolysis in air atmosphere, 500-600 • C was found to be the optimal temperature for oxidizing char and cleaning the fiber surface [59,77]. In comparison to virgin material, attenuated total reflection, combined with FTIR, proved to be a reliable technique for identifying functional groups existing on recovered fibers [94]. To maximize the effect of the recycling process, mechanical characteristics were measured [95][96][97]. SEM, Raman, and XPS studies were used to examine the morphology of the retrieved fibers. Image analyses for fiber length [10] and micro-bond testing for interfacial adhesion among various pyrolysis parameters for recovered fibers and polymers [73] were used for additional studies. Table 1 shows the yield from the procedure. (1) Thermoset polyester/styrene resin with GF (12%) (2) Thermoset polyester/styrene resin with GF (30%) (3) Phenolic resin with GF (31%) (4) Phenolic resin with CF (5) Epoxy resin with GF and CF (45%) (6) Polypropylene resin with GF tape (75%) (7) Vinylester resin with GF woven (70%)   Table 2 summarizes the characterization methodologies used to investigate thermal, mechanical, and morphological evaluations of fibers. Table 2. Characterization methods used in CFRC/GFRC recycling processes [40]. Recycling choices have a major influence on the assessment of mechanical characteristics of recovered fibers (CF/GF). Poor adherence (to recycled fibers and epoxy resins) has an impact on mechanical characteristics. Pyrolysis is the only technique that generates higher mechanical characteristics for recycled fibers and permits commercial-scale use, according to several studies [24,25,29]. To solve mechanical property concerns, pyrolysis should be controlled using a regulated temperature with quick heating rates, adequate residence duration, and appropriate raw material length (Table 3). The poor market potential of recovered GF makes it unsuitable for high-value industries. Pyrolysis reduced the TS of the recovered CF by 5-10% as compared to combustion (18%). However, additional study is needed to fully comprehend the mechanisms involved.

Thermal Analysis
It is important to identify the material cost reductions that may be achieved by using rCF. rCFv are indeed cheaper than virgin fibers, but they are also inherently different from vCF, which has restricted the entry of rCF into the vCF. Based on cost and performance, the task was to modify the material in such a way that virgin fiber can be replaced with recycled fiber.
In the case of carbon fiber composite materials, pyrolysis can result in fibers that are thin, discontinuous, and short in length. There were certain advantages to using these fibers; they were cost-effective, lightweight, with 3-dimensional complexity in the panels, and a secondary structure for airplane interiors [25]. Thermochemically converted recycled fibers demonstrated good mechanical characteristics compared to virgin fibers. When using the pyrolysis method, fiber strength was reduced by 10%, compared to the combustion procedure, which resulted in a greater loss of strength at 50%. The electrical conductivity of pyrolyzed recycled fiber was identical to that of vCF [109][110][111]. Some oxygenated species could still be found on the surface after recovery by pyrolysis, and fibers have been shown to bind effectively to epoxy resin [89] in terms of structure-property connection.
Reinventing composite constructions relies heavily on the fiber reclamation process for performance. A combination of resin and recovered fiber are compressed into pellets using direct-or injection-molding techniques. Nonwoven mats for lightweight composite manufacturing were made from milled fiber by ELG Carbon fiber in the United Kingdom [9]. Recycled carbon fiber products in automobile applications deliver lighter and stronger components at high volume manufacturing rates, while also allowing considerable cost savings. Nonaligned and short fibers tend to generate excellent quality, 3D complex, and lightweight constructions for components and panels with complex forms [112]. Recently, General Electric (GE) launched a bracket competition to enhance the extremely efficient bracket design [113,114]. The recovered nonaligned fibers have the potential to be part of improved lightweight products. For recycled fibers, there exists a broad variety of possible applications.
There are also myriad possibilities for market growth, e.g., nonwoven mats made from recycled carbon fibers, recycled carbon fibers mixed with thermoplastic fibers, chopped tow, and milled fiber. As part of a circular economy, carbon fibers are reused for as long as feasible and recovered for new composites and promising materials for practical uses.
It is the fiber reclamation process, which can supply high-quality fiber to produce new composites for intermediate commodities, that drives the usage of recovered fibers in a circular system. In contrast to low-value end-use, high-value end-use encourages the development of a sustainable supply chain for recovered fiber. With their 3D complex forms and discontinuous fibers, nonwoven mats with high fiber volume fractions in composites and minimal fiber breaking during molding can attain exceptional mechanical characteristics. While rCF may not be able to compete with vCF in terms of performance, competition is feasible in terms of weight reduction, cost reduction, and the ability to synthesize complicated shapes acceptable to certain automobile and parts sectors. The development of an efficient recovery process that can create high-quality fibers under moderate circumstances and reuse them in new composites is still in progress. Fibers produced using the pyrolysis process consist of short, discontinuous, fluffy fibers that have undergone a variety of procedures. Pimenta and Pinho introduced remanufacturing techniques [29]. The recovered fibers could be reused in different ways, based on their physical structure and mechanical characteristics, among other factors. Fiber alignment, fiber content, and fiber breakage reduction during processing still required technical development. A suitable, effective and low cost fiber recovery process in combination with suitable re-manufacturing process should be developed to reach the properties and performance of vCF. For technological demonstrations, Pimenta and Pinho emphasized, discontinuous, 3D-oriented fiber had the capacity to create secondary components for the automobile sector, as well as aircraft interiors and tools. When the residual char was removed from the recycled fibers, their mechanical characteristics were comparable to virgin substance, notably in the case of rCF [93].
Technical improvements in remanufacturing procedures are needed, notably in fiber alignment and fiber composition of new composites. The mechanical characteristics of recovered fibers-mixed with polymers to create new composites with qualities equivalent to the original CFRC-play a major role in efficient recycling processes.

Discussion
Mechanical separation, incineration, gasification, and slower pyrolysis in a kiln, are costly or yield low characteristic fibers. Pyrolysis seems to be a realistic and promising approach because it is efficient in recovery and produces high characteristic fibers. The essential pyrolysis variables, their influence on fiber characteristics, and the reuse of recycled fiber for a new composite were highlighted in this paper.
Industrial uses employing recycled fibers or resin, according to Oliveux et al., are uncommon. The authors claimed that this was due to a lack of trust in the quality of recycled fibers, as well as the fact that each batch of recycled composites comes from a variety of manufacturers and typically contains various fiber grades. This makes it difficult to manage the length, length uniformity, surface quality, and source of fibers. However, this does not rule out the possibility of other uses for recycled fiber [25]. In the same way, the current study (based on the literature) concluded that there are currently no commercially viable products created from short, thin, and nonaligned recovered fibers obtained by pyrolysis. More study on the use of recovered fibers is needed. On the other hand, according to Naqvi et al. (2018), recycled fibers may be used in a variety of ways other than competing with virgin materials, such as accessing new markets or creating new materials. Pickering et al. came to the conclusion that a rCF/rGF's worth may be increased by utilizing its unique features. The course rGF composites, for example, can be utilized as a core material because of their greater permeability, which acts as a flow channel [46]. However, based on the literature researched, it is important to identify the material cost reductions that may be achieved by using rCF. While rCF are indeed cheaper than virgin fibers, they are inherently different from them, which has restricted their entry into the market. Based on cost and performance, the task was to modify the material in such a way that virgin fiber could be replaced with recycled fiber. Similarly, Job et al. found that because of the reduction in the quality of rCF/rGF, these fibers could only compete with lower-value materials like aluminum or cheaper virgin material composites. Additionally, quantity is critical, as economically viable processes need high throughputs. Market development is required to utilize large quantities of rCF/rGF. This means that either the rCF/cost must decrease to allow the rCF/rGF to penetrate new markets, or the rCF/rGF must seek out higher-value end markets [6].
According to Liu et al., optimization strategies may be discovered at all stages of the composite recycling and remanufacturing process. However, given the potential for optimization, these applications are still uncommon. Meanwhile, the majority of the strategies used to adjust parameters are a design of experiments strategies [7]. This is consistent with what was stated in the research: that there are currently no commercially viable products created from recovered fibers and that more studies and experiments on the use of recovered fibers are needed. According to Krauklis et al., pyrolysis is presently the most prevalent technique for recycling FRCs in the industry. Thermal recycling allows rCF to be recovered while retaining much of their reinforcing potential, whereas rGF is severely destroyed [1]. Similarly, this study concluded that pyrolysis seemed to be a realistic and promising approach because it was efficient in recovery and produced high characteristic fibers. On the other hand, Gharde et al. stated that recycling procedures should be chosen based on the kinds of composite materials and their ability to be reused in future applications. Every recycling process has its own set of benefits and drawbacks [3].
Pyrolysis, like any other recycling process, has several drawbacks, the most problematic of which is the probability of char development on the resultant fiber surface. Due to the char, the mechanical characteristics of the recovered fibers can be substantially decreased. Chemical treatment and post-heating the fibers both help to reduce char formation, but only to a limited extent.
A successful commercial-scale pyrolysis program was implemented in Germany and the United Kingdom. As a result of recycled fibers and other products like gas and oil, which may be utilized as feedstocks, the process has had a green impact. It is difficult to avoid char development in rGFs. It is also difficult to maintain the full mechanical characteristics of both CF and GF. A further heat/chemical treatment is required to remove small resin contaminants from the recovered fibers.
Both the oxidizing (air) and thermal (N 2 ) atmospheres were important in determining surface properties. Surface defects were discovered in an oxidizing atmosphere, resulting in a decrease in TS and crystallite size. As a result, for the recycling process to be successful, a regulated and optimum temperature and residence duration in post-pyrolysis is advantageous.
It is critical to figure out how to save money on materials by employing recovered carbon fibers as structural reinforcement, as well as how to find large-scale high-value applications for recovered carbon fibers. Although recycled fibers are less expensive than virgin fibers, they are fundamentally different, and this distinction has hampered their introduction into the virgin fiber market. The aim has thus been to alter the material such that virgin fiber is replaced with recycled fiber, based on cost and performance.
Pyrolysis can result in fibers that are short and discontinuous in carbon fiber composite materials. The use of these fibers has several advantages; cost-effectiveness, lightness, 3dimensional complexity in the panels, and a secondary framework for airplane interiors.
In comparison to virgin fibers, thermochemically transformed recycled fibers showed superior mechanical properties. Moreover, recycled carbon fiber products in automotive applications deliver lighter and stronger components at high volume manufacturing rates, while also allowing considerable cost savings. For components and panels with complex shapes, discontinuous and thin fibers tend to produce excellent characteristics and 3D, intricate, low-weight structures.
For recycling CFRC/GFRC, pyrolysis has been classified as the most feasible and sustainable method for conserving resources and providing efficient recycling. However, the current study may be used to generate a variety of research topics. The following perspectives can be used to plan and solve future improvements in pyrolysis for the recovery of CF/GF:

1.
In an appropriate experimental facility, how well does pyrolysis perform for mixed and polluted scrape? In the majority of the work in the literature, there has been no mention of an FBR or any other reactor capable of processing mixed and polluted wastes.

2.
Determination of the optimal variables of pyrolysis and post-pyrolysis are necessary in order to better comprehend the impact of pyrolysis. For further enhancement of the quality of the recovered fibers, research on the optimum variables of pyrolysis is needed. 3.
In the literature, there is a gap in the examination of financial and energy-based evaluation of pyrolysis. The data will show that recycled fibers are better for the environment than EOL landfilling. Mathematical modeling may be built to show how pyrolysis and post-pyrolysis processing changes-as well as other important parameters-affect the cost and environmental effect.

4.
There are currently no commercially viable products created from short, thin, and nonaligned recovered fibers obtained by pyrolysis. More study on the use of recovered fibers is needed.

5.
When pyrolyzing a recycled composite, there is no information on fiber grading and fractionation to remove short fibers and retain excellent purity and strength without losing part of the fiber. 6.
How can the original fiber length and strength be preserved following pyrolysis? The longer the starting fiber, the longer the recovered fiber-although better understanding of the effects of thermal and oxidation treatment is needed to enhance product quality and lower costs. 7.
The lack of sizing on recycled fiber surfaces is a key study topic. This might result in inadequate adhesion among the polymer and recovered fibers, resulting in poor mechanical characteristics. The mechanical characteristics of recycled fibers might be significantly improved by pyrolysis resizing. 8.
Pyrolysis improved the mechanical characteristics of recovered fibers when contrasted with incineration, gasification, mechanical, and chemical techniques. On the other hand, an inappropriate set of pyrolysis conditions has a detrimental impact on these characteristics (such as poor heating rates and high residence time). This compromise will not be accepted if the recovered fibers are to be used in a high-grade composite application. 9.
It is unclear what effect fiber reclamation has on the performance of composites when compared to virgin and recovered composites with similar structures.

Conclusions and Future Research
The primary objectives of this research were to identify alternative pyrolysis recycling processes for CFRC and GFRC waste and prioritize the most sustainable techniques, with respect to financial and environmental considerations. Presently, the fate of waste CFRC and GFRC is mainly to be landfilled or incinerated, as these are the methods used by traditional waste disposal companies. However, many waste disposal businesses have switched to total fiber recovery technologies, considering concerns like sustainable